WO2010059834A2 - Système et procédé de moulage de coquilles molles pour implants remplis de fluide - Google Patents
Système et procédé de moulage de coquilles molles pour implants remplis de fluide Download PDFInfo
- Publication number
- WO2010059834A2 WO2010059834A2 PCT/US2009/065159 US2009065159W WO2010059834A2 WO 2010059834 A2 WO2010059834 A2 WO 2010059834A2 US 2009065159 W US2009065159 W US 2009065159W WO 2010059834 A2 WO2010059834 A2 WO 2010059834A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mandrel
- spray
- dispersion
- chamber
- mandrels
- Prior art date
Abstract
Priority Applications (7)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP09756390A EP2379298B1 (fr) | 2008-11-20 | 2009-11-19 | Système et procédé de moulage de coquilles molles pour implants remplis de fluide |
AU2009316547A AU2009316547A1 (en) | 2008-11-20 | 2009-11-19 | System and method for molding soft fluid-filled implant shells |
CN2009801514692A CN102256762A (zh) | 2008-11-20 | 2009-11-19 | 用于模制软流体填充的植入体壳的系统和方法 |
ES09756390T ES2397688T3 (es) | 2008-11-20 | 2009-11-19 | Sistema y método para moldear capsulas de implantes blandas llenas de fluido |
RU2011124178/05A RU2011124178A (ru) | 2008-11-20 | 2009-11-19 | Способ формования мягкой оболочки для заполняемого текучей средой имплантата и соответствующая установка |
BRPI0921104A BRPI0921104A2 (pt) | 2008-11-20 | 2009-11-19 | sistema e método para a moldagem de envoltórios de implante moles recheados de fluido |
CA2744062A CA2744062A1 (fr) | 2008-11-20 | 2009-11-19 | Systeme et procede de moulage de coquilles molles pour implants remplis de fluide |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11640608P | 2008-11-20 | 2008-11-20 | |
US61/116,406 | 2008-11-20 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2010059834A2 true WO2010059834A2 (fr) | 2010-05-27 |
WO2010059834A3 WO2010059834A3 (fr) | 2010-11-25 |
Family
ID=42133787
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2009/065159 WO2010059834A2 (fr) | 2008-11-20 | 2009-11-19 | Système et procédé de moulage de coquilles molles pour implants remplis de fluide |
Country Status (11)
Country | Link |
---|---|
US (3) | US8431179B2 (fr) |
EP (2) | EP2511062A1 (fr) |
KR (1) | KR20110103964A (fr) |
CN (1) | CN102256762A (fr) |
AR (1) | AR075357A1 (fr) |
AU (1) | AU2009316547A1 (fr) |
BR (1) | BRPI0921104A2 (fr) |
CA (1) | CA2744062A1 (fr) |
ES (1) | ES2397688T3 (fr) |
RU (1) | RU2011124178A (fr) |
WO (1) | WO2010059834A2 (fr) |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2012043997A2 (fr) * | 2010-09-28 | 2012-04-05 | Yu Won-Seok | Prothèse en silicone ronde ou anatomique dotée d'une enveloppe présentant des caractéristiques améliorées de durabilité et son procédé de fabrication |
CN103998360A (zh) * | 2011-05-26 | 2014-08-20 | 阿德文尼拉企业有限公司 | 用于涂覆物体的系统和方法 |
ITPI20130015A1 (it) * | 2013-03-07 | 2014-09-08 | S M Scienzia Machinale S R L | Apparecchiatura e metodo per la produzione di un oggetto tridimensionale biocompatibile |
EP2990174A1 (fr) * | 2014-08-21 | 2016-03-02 | Applied Silicone Company LLC | Système et procédé d'enveloppe de prothèse automatisée |
WO2017042627A1 (fr) | 2015-09-11 | 2017-03-16 | S.M. Scienzia Machinale S.R.L. | Appareil et procédé permettant de fabriquer un objet tridimensionnel biocompatible |
Families Citing this family (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2333522A1 (fr) | 2001-04-30 | 2011-06-15 | The General Hospital Corporation | Procédé et appareil permettant d'améliorer la clarté et la sensibilité de l'image en tomographie à cohérence optique au moyen d'une interaction permettant de contrôler les propriétés focales et la synchronisation de cohérence |
WO2010059834A2 (fr) * | 2008-11-20 | 2010-05-27 | Allergan, Inc. | Système et procédé de moulage de coquilles molles pour implants remplis de fluide |
EP2605732B1 (fr) * | 2010-08-18 | 2018-02-14 | Christopher Burnside Gordon | Article orthétique moulé in situ et procédé pour sa fabrication |
US10722997B2 (en) * | 2012-04-02 | 2020-07-28 | Thomas West, Inc. | Multilayer polishing pads made by the methods for centrifugal casting of polymer polish pads |
KR102100654B1 (ko) | 2012-04-02 | 2020-04-14 | 토마스 웨스트 인코포레이티드 | 폴리머 연마패드의 원심주조를 위한 방법 및 시스템 및 상기 방법으로 만들어진 연마패드 |
US10022842B2 (en) | 2012-04-02 | 2018-07-17 | Thomas West, Inc. | Method and systems to control optical transmissivity of a polish pad material |
US10820984B2 (en) | 2012-11-14 | 2020-11-03 | ImplantADJUST, LLC | Implant with elastomeric membrane and methods of fabrication thereof |
US9351824B2 (en) | 2012-11-14 | 2016-05-31 | ImplantADJUST, LLC | Adjustable implant with self-sealing elastomeric membrane and methods of fabrication thereof |
EP2962662A1 (fr) * | 2012-12-13 | 2016-01-06 | Allergan, Inc. | Implant mammaire de surface variable |
US20160130690A1 (en) * | 2014-11-12 | 2016-05-12 | Applied Silicone Corporation | Immersion Curing Process |
WO2020214328A2 (fr) * | 2019-03-19 | 2020-10-22 | University Of Pittsburgh - Of The Commonwealth System Of Higher Education | Mécanisme d'automatisation pour la production pré-clinique de guides nerveux résorbables |
KR102580385B1 (ko) * | 2021-02-25 | 2023-09-21 | 오스템임플란트 주식회사 | 인공유방 보형물 제조방법 |
KR102580384B1 (ko) * | 2021-02-25 | 2023-09-21 | 오스템임플란트 주식회사 | 인공유방 보형물 제조방법 |
US11357614B1 (en) | 2021-06-11 | 2022-06-14 | Marcel Malek | Breast implant |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2128827A (en) * | 1938-03-09 | 1938-08-30 | Frank B Killian | Method and apparatus for manufacturing thin rubber articles |
EP0416846A2 (fr) * | 1989-09-05 | 1991-03-13 | Dow Corning Wright Corporation | Procédé pour la fabrication d'un article implantable comportant une structure en forme de petites colonnes sur la surface |
US5935164A (en) * | 1997-02-25 | 1999-08-10 | Pmt Corporaton | Laminated prosthesis and method of manufacture |
US20040032056A1 (en) * | 2002-08-15 | 2004-02-19 | Koua Vang | Drip retainer |
EP1398131A1 (fr) * | 2002-09-12 | 2004-03-17 | Polyzen, Inc. | Dispositifs médicaux polymères moulé par trempage avec un gradient d'épaisseur de paroi inverse et procédé de moulage par trempage |
Family Cites Families (73)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2469892A (en) | 1947-09-10 | 1949-05-10 | Rempel Entpr | Hollow article and method and apparatus for producing the same |
GB702146A (en) | 1950-11-10 | 1954-01-13 | Chad Valley Company Ltd | A new or improved process for the production of dolls and other toys |
US2804643A (en) | 1955-03-21 | 1957-09-03 | Theodore A Miller | Vacuum extractor apparatus for removing hollow flexible molded articles from reentrant mold cavities |
US3652748A (en) | 1965-05-14 | 1972-03-28 | Arthur H Roberts | Process for preparing molded hollow articles |
US3439079A (en) | 1966-05-16 | 1969-04-15 | Gen Electric | Molding hollow articles |
GB1192360A (en) | 1966-09-28 | 1970-05-20 | Courtaulds Ltd | The Centrifugal Casting of Rollers |
GB1206110A (en) | 1966-12-19 | 1970-09-23 | Courtaulds Ltd | Cast wheels |
US4043721A (en) | 1968-07-11 | 1977-08-23 | Lemelson Jerome H | Composite body molding apparatus |
GB1306541A (en) | 1969-01-20 | 1973-02-14 | Ceskoslovenska Akademie Ved | Method of manufacturing tubes by centrifugal casting |
US3652368A (en) | 1969-12-17 | 1972-03-28 | Plastics Inc | Apparatus for rotational molding of laminated hollow structures |
US3584105A (en) | 1970-01-14 | 1971-06-08 | Pekor Iron Works | Method of centrifugally forming hollow articles |
BE757080A (fr) | 1970-04-03 | 1971-03-16 | Giehler Herbert | Procede et dispositif pour la fabrication de pieces creuses en matieresthermoplastiques par moulage par rotation a l'etat fondu |
US3683062A (en) | 1970-08-20 | 1972-08-08 | Essex International Inc | Rotational casting method |
US3788382A (en) | 1970-11-25 | 1974-01-29 | J Richey | Vacuum metal casting apparatus |
DE2160124A1 (de) | 1971-01-08 | 1972-08-24 | Monster Molding Ltd | Verfahren zum Rotationspressen von Formkörpern bei Raumtemperatur |
US3925530A (en) | 1971-02-08 | 1975-12-09 | Phillips Petroleum Co | Release coating for molds |
GB1434345A (en) | 1972-04-26 | 1976-05-05 | Quraishi A H | Rotational moulding |
US3883902A (en) | 1972-08-16 | 1975-05-20 | Medical Eng Corp | Variable volume prosthetic assembly |
US3850368A (en) | 1973-02-12 | 1974-11-26 | Kennametal Inc | Apparatus for centrifugal compaction |
DE2530211C2 (de) | 1975-07-07 | 1983-12-01 | Elkamet-Werk Lahn-Kunststoff Gmbh, 3560 Biedenkopf | Verfahren und Vorrichtung zum Herstellen von Hohlkörpern aus thermoplastischem Kunststoff durch Rotationsschmelzen |
FR2397931A1 (fr) | 1977-07-22 | 1979-02-16 | Thomson Brandt | Procede de reproduction de disque support d'information et disque obtenu par un tel procede |
US4285903A (en) | 1977-08-29 | 1981-08-25 | Lemelson Jerome H | Molding system |
DE2756384C3 (de) | 1977-12-17 | 1981-09-10 | Reitberger, Ernst, 7030 Böblingen | Vorrichtung zum Herstellen von Hohlkörpern aus thermoplastischem Kunststoff |
JPS6015454B2 (ja) | 1980-10-29 | 1985-04-19 | 北辰工業株式会社 | 薄肉エンドレスベルトの製造法 |
EP0054197B1 (fr) | 1980-12-12 | 1985-06-26 | Beiersdorf Aktiengesellschaft | Prothèse mammaire |
US4416841A (en) | 1981-03-11 | 1983-11-22 | Corea John E | Method for centrifugal casting of thermosetting plastics |
US4624818A (en) | 1982-03-25 | 1986-11-25 | Allied Corporation | Rotational molding process using abrasive-resistant nylon composition |
US4548779A (en) | 1982-11-15 | 1985-10-22 | Allied Corporation | Rotational molding multilayered articles |
US4836963A (en) | 1984-05-01 | 1989-06-06 | Old Town Canoe Company | Rotational molding method |
US4956133A (en) | 1985-08-19 | 1990-09-11 | Le Roy Payne | Continuous molding apparatus and method |
US6030557A (en) | 1985-08-19 | 2000-02-29 | Payne; Leroy | Multiaxis rotational molding method, apparatus and structure |
US5188845A (en) | 1985-08-19 | 1993-02-23 | Payne Leroy | Multiaxis rotational molding apparatus |
US5316701A (en) | 1985-08-19 | 1994-05-31 | Payne Leroy | Multiaxis rotational molding process |
US6511619B1 (en) | 1985-08-19 | 2003-01-28 | Payne Leroy | Multiaxis rotational molding apparatus and method |
FR2590836B1 (fr) | 1985-12-02 | 1988-04-15 | Luchaire Sa | Procede et machine de fabrication de pieces creuses en matiere plastique, par roulage par rotation |
US4865787A (en) | 1986-07-17 | 1989-09-12 | General Electric Company | Method for the impregnation of filament wound structures with thermoplastic binders |
US4796686A (en) | 1986-08-20 | 1989-01-10 | Gayso Donald W | Centrifugal casting machine with venturi actuated vacuum venting |
US4960425A (en) | 1987-05-27 | 1990-10-02 | Mentor Corporation | Textured surface frosthesis implants |
US4990299A (en) | 1987-11-02 | 1991-02-05 | Primtec | Multi-parting molding system with clamping means |
GB8820945D0 (en) | 1988-09-07 | 1988-10-05 | Smith & Nephew | Medical articles |
US4882107A (en) | 1988-11-23 | 1989-11-21 | Union Carbide Chemicals And Plastics Company Inc. | Mold release coating process and apparatus using a supercritical fluid |
US4992312A (en) | 1989-03-13 | 1991-02-12 | Dow Corning Wright Corporation | Methods of forming permeation-resistant, silicone elastomer-containing composite laminates and devices produced thereby |
US5035601A (en) | 1990-02-21 | 1991-07-30 | Lin Chao Tung | Hollow forming machine capable of rotating mould in both horizontal and vertical direction |
US5091445A (en) | 1990-05-04 | 1992-02-25 | Dow Corning Corporation | Silicone sealants |
US5346660A (en) | 1990-09-07 | 1994-09-13 | Toto Ltd. | Method of manufacturing powder molding |
US5096627A (en) | 1990-09-17 | 1992-03-17 | Minnesota Mining And Manufacturing Company | Method of molding optical recording drums |
US5156818A (en) | 1990-11-16 | 1992-10-20 | Alternative Technologies For Waste, Inc. | Biaxial casting apparatus for isolating radioactive waste |
US5795325A (en) | 1991-07-16 | 1998-08-18 | Heartport, Inc. | Methods and apparatus for anchoring an occluding member |
US5376117A (en) | 1991-10-25 | 1994-12-27 | Corvita Corporation | Breast prostheses |
AU657180B2 (en) | 1991-11-15 | 1995-03-02 | Lucite International Uk Limited | Polymerisable compositions |
JP2969311B2 (ja) | 1992-08-31 | 1999-11-02 | タキロン株式会社 | ゲル状弾性体 |
US5356589A (en) | 1993-03-09 | 1994-10-18 | Essef Corporation | Method and apparatus for forming rotationally cast tank liner having an end fitting |
US5519082A (en) | 1994-04-13 | 1996-05-21 | Shin-Etsu Chemical Co., Ltd. | Curable silicone rubber composition and method for preparing silicone rubber |
DE4413076A1 (de) | 1994-04-15 | 1995-10-19 | Amoena Med Orthopaedie Tech | Verfahren zur Herstellung von Brustprothesen |
US5525274A (en) | 1994-06-29 | 1996-06-11 | Davidson Textron Inc. | Process for manufacturing plastic microspheres |
JP3761222B2 (ja) | 1994-08-05 | 2006-03-29 | エルカメート・クンストシユトッフテヒニック・ゲゼルシヤフト・ミト・ベシユレンクテル・ハフツング | 流動性の乾燥した熱可塑性合成樹脂から回転溶融により中空体を造るための装置 |
WO1997008238A1 (fr) | 1995-08-29 | 1997-03-06 | Exxon Chemical Patents Inc. | Polypropylene supportant les rayonnements et articles utiles realises a partir de cette matiere |
US5665069A (en) | 1996-07-19 | 1997-09-09 | Cumer; Patricia Lynn | Pressure-directed peribulbar anesthesia delivery device |
US5705110A (en) | 1996-09-09 | 1998-01-06 | Centro Incorporated | Process for reducing cross link vapors from rotomolded products made of cross link polyethlylene |
US6180203B1 (en) | 1997-04-09 | 2001-01-30 | Peter J. Unkles | Rotational moulding process |
JP3743787B2 (ja) | 1997-09-03 | 2006-02-08 | 東ソー株式会社 | 高純度薬品容器用ポリエチレン樹脂及びそれよりなる高純度薬品容器 |
US6177034B1 (en) | 1998-04-03 | 2001-01-23 | A-Pear Biometric Replications Inc. | Methods for making prosthetic surfaces |
US6214272B1 (en) | 1998-07-14 | 2001-04-10 | Brunswick Corporation | Rotational molding process |
US6329444B1 (en) | 1998-10-14 | 2001-12-11 | Apex Medical Technologies, Inc. | Dip-molded medical devices from cis-1,4-polyisoprene |
US6231547B1 (en) | 1999-02-18 | 2001-05-15 | Abbott Laboratories | External retaining device for a catheter and catheter assembly and method using same |
JP2001029475A (ja) | 1999-07-23 | 2001-02-06 | Kanegafuchi Chem Ind Co Ltd | 血液灌流バルーンカテーテル |
US6409954B1 (en) | 1999-10-05 | 2002-06-25 | Roto Plastics, Inc. | Method of making a rotary molded plastic member with variable wall thickness |
US6692527B1 (en) * | 1999-12-01 | 2004-02-17 | Howard T. Bellin | Non-rotating breast implant |
US6291543B1 (en) | 2000-05-24 | 2001-09-18 | Polyzen, Inc. | Surfacially cross-linked elastoplastic articles, and method of making the same |
US6602452B2 (en) | 2001-07-18 | 2003-08-05 | Mcghan Medical Corporation | Rotational molding of medical articles |
NL1019023C2 (nl) * | 2001-09-24 | 2003-03-25 | Mentor Medical Systems B V | Inrichting en werkwijze voor het vervaardigen van een siliconen omhulsel voor een borstimplantaat. |
US7758788B2 (en) | 2004-08-13 | 2010-07-20 | Mentor Worldwide Llc | Spray method for forming shells for prostheses |
WO2010059834A2 (fr) * | 2008-11-20 | 2010-05-27 | Allergan, Inc. | Système et procédé de moulage de coquilles molles pour implants remplis de fluide |
-
2009
- 2009-11-19 WO PCT/US2009/065159 patent/WO2010059834A2/fr active Application Filing
- 2009-11-19 AU AU2009316547A patent/AU2009316547A1/en not_active Abandoned
- 2009-11-19 EP EP12176367A patent/EP2511062A1/fr not_active Withdrawn
- 2009-11-19 CA CA2744062A patent/CA2744062A1/fr not_active Abandoned
- 2009-11-19 RU RU2011124178/05A patent/RU2011124178A/ru unknown
- 2009-11-19 US US12/621,700 patent/US8431179B2/en active Active
- 2009-11-19 KR KR1020117014140A patent/KR20110103964A/ko not_active Application Discontinuation
- 2009-11-19 BR BRPI0921104A patent/BRPI0921104A2/pt not_active Application Discontinuation
- 2009-11-19 EP EP09756390A patent/EP2379298B1/fr not_active Not-in-force
- 2009-11-19 CN CN2009801514692A patent/CN102256762A/zh active Pending
- 2009-11-19 ES ES09756390T patent/ES2397688T3/es active Active
- 2009-11-20 AR ARP090104497A patent/AR075357A1/es unknown
-
2013
- 2013-04-22 US US13/867,821 patent/US8703230B2/en active Active
-
2014
- 2014-03-24 US US14/223,875 patent/US20140203478A1/en not_active Abandoned
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2128827A (en) * | 1938-03-09 | 1938-08-30 | Frank B Killian | Method and apparatus for manufacturing thin rubber articles |
EP0416846A2 (fr) * | 1989-09-05 | 1991-03-13 | Dow Corning Wright Corporation | Procédé pour la fabrication d'un article implantable comportant une structure en forme de petites colonnes sur la surface |
US5935164A (en) * | 1997-02-25 | 1999-08-10 | Pmt Corporaton | Laminated prosthesis and method of manufacture |
US20040032056A1 (en) * | 2002-08-15 | 2004-02-19 | Koua Vang | Drip retainer |
EP1398131A1 (fr) * | 2002-09-12 | 2004-03-17 | Polyzen, Inc. | Dispositifs médicaux polymères moulé par trempage avec un gradient d'épaisseur de paroi inverse et procédé de moulage par trempage |
Cited By (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9408692B2 (en) | 2010-09-28 | 2016-08-09 | Won Seok Yu | Round or anatomical type silicone prosthesis having shell with enhanced durability and method for manufacturing same |
WO2012043997A3 (fr) * | 2010-09-28 | 2012-06-21 | Yu Won-Seok | Prothèse en silicone ronde ou anatomique dotée d'une enveloppe présentant des caractéristiques améliorées de durabilité et son procédé de fabrication |
CN103124569A (zh) * | 2010-09-28 | 2013-05-29 | 刘源硕 | 具有耐用性增强的外壳的圆型或解剖型硅胶假体及其制造方法 |
KR101288117B1 (ko) * | 2010-09-28 | 2013-07-19 | 유원석 | 내구성이 향상된 쉘을 갖는 라운드형 또는 아나토미칼형 실리콘 보형물 및 그 제조방법 |
JP2013537059A (ja) * | 2010-09-28 | 2013-09-30 | ウォン ソク ユ | 耐久性が向上したシェルを有するラウンド型またはアナトミカル型のシリコンバッグ及びその製造方法 |
WO2012043997A2 (fr) * | 2010-09-28 | 2012-04-05 | Yu Won-Seok | Prothèse en silicone ronde ou anatomique dotée d'une enveloppe présentant des caractéristiques améliorées de durabilité et son procédé de fabrication |
EP2623131A4 (fr) * | 2010-09-28 | 2017-07-26 | Won-Seok Yu | Prothèse en silicone ronde ou anatomique dotée d'une enveloppe présentant des caractéristiques améliorées de durabilité et son procédé de fabrication |
CN103998360A (zh) * | 2011-05-26 | 2014-08-20 | 阿德文尼拉企业有限公司 | 用于涂覆物体的系统和方法 |
ITPI20130015A1 (it) * | 2013-03-07 | 2014-09-08 | S M Scienzia Machinale S R L | Apparecchiatura e metodo per la produzione di un oggetto tridimensionale biocompatibile |
WO2014136021A1 (fr) | 2013-03-07 | 2014-09-12 | S.M. Scienzia Machinale S.R.L. | Appareil et procédé pour produire un objet tridimensionnel biocompatible |
US11260563B2 (en) | 2013-03-07 | 2022-03-01 | S.M. Scienzia Machinale Srl | Apparatus and method for producing a biocompatible three-dimensional object |
CN105382985A (zh) * | 2014-08-21 | 2016-03-09 | 应用硅树脂责任有限公司 | 安装系统和制造假体外壳的自动化方法 |
EP2990174A1 (fr) * | 2014-08-21 | 2016-03-02 | Applied Silicone Company LLC | Système et procédé d'enveloppe de prothèse automatisée |
CN105382985B (zh) * | 2014-08-21 | 2019-02-15 | 应用硅树脂责任有限公司 | 安装系统和制造假体外壳的自动化方法 |
WO2017042627A1 (fr) | 2015-09-11 | 2017-03-16 | S.M. Scienzia Machinale S.R.L. | Appareil et procédé permettant de fabriquer un objet tridimensionnel biocompatible |
Also Published As
Publication number | Publication date |
---|---|
KR20110103964A (ko) | 2011-09-21 |
ES2397688T3 (es) | 2013-03-08 |
BRPI0921104A2 (pt) | 2016-02-16 |
US20100178414A1 (en) | 2010-07-15 |
CN102256762A (zh) | 2011-11-23 |
RU2011124178A (ru) | 2012-12-27 |
CA2744062A1 (fr) | 2010-05-27 |
US8431179B2 (en) | 2013-04-30 |
AR075357A1 (es) | 2011-03-30 |
US8703230B2 (en) | 2014-04-22 |
WO2010059834A3 (fr) | 2010-11-25 |
EP2511062A1 (fr) | 2012-10-17 |
EP2379298A2 (fr) | 2011-10-26 |
US20140203478A1 (en) | 2014-07-24 |
AU2009316547A1 (en) | 2010-05-27 |
US20130234365A1 (en) | 2013-09-12 |
EP2379298B1 (fr) | 2012-10-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US8703230B2 (en) | System and method for molding soft fluid-filled implant shells | |
JP5666448B2 (ja) | 分離固定面を備えた軟質充填プロテーゼシェル | |
JP6053874B2 (ja) | 分離固定面を備えた軟質充填プロテーゼシェル | |
AU617667B2 (en) | Open-cell, silicone-elastomer medical implant and method for making | |
AU2015258842B2 (en) | Soft filled prosthesis shell with variable texture | |
US5674285A (en) | Mammary implant having shell with unitary rough-textured outer layer | |
EP1796595B1 (fr) | Procédé de pulvérisation pour la formation d'enveloppes pour prothèses | |
KR20120032392A (ko) | 내구성이 향상된 쉘을 갖는 실리콘 보형물 제조방법 | |
KR101021668B1 (ko) | 응력 집중을 최소화한 인공 유방 보형물 제조 방법 | |
EP3142602B1 (fr) | Coque souple de prothèse remplie à texture variable | |
AU2015205876A1 (en) | Soft filled prosthesis shell with discrete fixation surfaces |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 200980151469.2 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 09756390 Country of ref document: EP Kind code of ref document: A2 |
|
DPE1 | Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101) | ||
WWE | Wipo information: entry into national phase |
Ref document number: 2744062 Country of ref document: CA |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2009316547 Country of ref document: AU |
|
WWE | Wipo information: entry into national phase |
Ref document number: 4230/DELNP/2011 Country of ref document: IN |
|
ENP | Entry into the national phase |
Ref document number: 2009316547 Country of ref document: AU Date of ref document: 20091119 Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2009756390 Country of ref document: EP |
|
ENP | Entry into the national phase |
Ref document number: 20117014140 Country of ref document: KR Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2011124178 Country of ref document: RU |
|
ENP | Entry into the national phase |
Ref document number: PI0921104 Country of ref document: BR Kind code of ref document: A2 Effective date: 20110520 |