WO2010057907A2 - Multiple-junction photoelectric device and its production process - Google Patents
Multiple-junction photoelectric device and its production process Download PDFInfo
- Publication number
- WO2010057907A2 WO2010057907A2 PCT/EP2009/065369 EP2009065369W WO2010057907A2 WO 2010057907 A2 WO2010057907 A2 WO 2010057907A2 EP 2009065369 W EP2009065369 W EP 2009065369W WO 2010057907 A2 WO2010057907 A2 WO 2010057907A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- intermediate layer
- elementary
- bottom face
- angle
- layer
- Prior art date
Abstract
Description
Claims