WO2010046537A1 - Rouleau pour une section de séchage de machine de nappe de fibres et procédé de fabrication d'un rouleau de section de séchage de machine de nappe de fibres - Google Patents

Rouleau pour une section de séchage de machine de nappe de fibres et procédé de fabrication d'un rouleau de section de séchage de machine de nappe de fibres Download PDF

Info

Publication number
WO2010046537A1
WO2010046537A1 PCT/FI2009/050848 FI2009050848W WO2010046537A1 WO 2010046537 A1 WO2010046537 A1 WO 2010046537A1 FI 2009050848 W FI2009050848 W FI 2009050848W WO 2010046537 A1 WO2010046537 A1 WO 2010046537A1
Authority
WO
WIPO (PCT)
Prior art keywords
roll
fibre
surface structure
ribs
web machine
Prior art date
Application number
PCT/FI2009/050848
Other languages
English (en)
Inventor
Juha ISOMETSÄ
Original Assignee
Metso Paper, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Metso Paper, Inc. filed Critical Metso Paper, Inc.
Publication of WO2010046537A1 publication Critical patent/WO2010046537A1/fr

Abstract

La présente invention se rapporte à un rouleau (10) pour une machine de nappe de fibres comprenant un corps de rouleau (15), au moyen duquel le rouleau peut être fixé pour tourner dans la machine de nappe de fibres, une structure de surface (60) disposée en association avec le corps et présentant une pluralité de nervures (50) espacées à distance les unes des autres et s'étendant autour du corps du rouleau, formant ainsi une surface (55) qui est ouverte d'une manière du type fente. Les nervures (50) et la sous-structure (60') de la structure de surface (60) à l'intérieur de celles-ci dans le sens radial du rouleau forment une structure sensiblement uniforme. L'invention concerne également un procédé de fabrication d'un rouleau pour une machine de nappe de fibres et des outils d'usinage permettant de pratiquer des rainures adjacentes (52) dans la structure de surface (60) du rouleau de machine de nappe de fibres (10).
PCT/FI2009/050848 2008-10-23 2009-10-21 Rouleau pour une section de séchage de machine de nappe de fibres et procédé de fabrication d'un rouleau de section de séchage de machine de nappe de fibres WO2010046537A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
FI20086005A FI20086005L (fi) 2008-10-23 2008-10-23 Kuiturainakoneen tela ja menetelmä kuiturainakoneen telan valmistamiseksi
FI20086005 2008-10-23

Publications (1)

Publication Number Publication Date
WO2010046537A1 true WO2010046537A1 (fr) 2010-04-29

Family

ID=39924644

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/FI2009/050848 WO2010046537A1 (fr) 2008-10-23 2009-10-21 Rouleau pour une section de séchage de machine de nappe de fibres et procédé de fabrication d'un rouleau de section de séchage de machine de nappe de fibres

Country Status (2)

Country Link
FI (1) FI20086005L (fr)
WO (1) WO2010046537A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3599306A (en) * 1969-06-13 1971-08-17 Beloit Corp Roll composition
FI50159B (fr) * 1968-12-18 1975-09-01 Beloit Corp
FI56251B (fi) * 1970-10-28 1979-08-31 Beloit Corp Med ett kombinationsmaterial belagd vals, saerskilt en pappersmaskinsvals
DE3829648A1 (de) * 1988-06-14 1989-12-21 Ravensburg Maschf Verfahren zur herstellung von nuten in zylindrischen walzen und schleifmaschine zur durchfuehrung des verfahrens
EP0655561A1 (fr) * 1993-11-30 1995-05-31 Sgl Technik Gmbh Rouleau en matière plastique renforcée de fibres à surface rainurée en losanges

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FI50159B (fr) * 1968-12-18 1975-09-01 Beloit Corp
US3599306A (en) * 1969-06-13 1971-08-17 Beloit Corp Roll composition
FI56251B (fi) * 1970-10-28 1979-08-31 Beloit Corp Med ett kombinationsmaterial belagd vals, saerskilt en pappersmaskinsvals
DE3829648A1 (de) * 1988-06-14 1989-12-21 Ravensburg Maschf Verfahren zur herstellung von nuten in zylindrischen walzen und schleifmaschine zur durchfuehrung des verfahrens
EP0655561A1 (fr) * 1993-11-30 1995-05-31 Sgl Technik Gmbh Rouleau en matière plastique renforcée de fibres à surface rainurée en losanges

Also Published As

Publication number Publication date
FI20086005L (fi) 2010-04-24
FI20086005A0 (fi) 2008-10-23

Similar Documents

Publication Publication Date Title
RU2587172C2 (ru) Устройство уплотнения для машины для намотки волокнистой текстуры на оправку для пропитки
CN1543523A (zh) 纤维结构的干燥方法
CN107638998A (zh) 一种玻璃纤维布成卷生产装置
KR20160036567A (ko) 섬유 재료의 웹을 생산하기 위한 장치 및 방법
RU2015121726A (ru) Устройство и способ для изготовления заготовок для роторных лопастей ветроэнергетических установок, а также роторная лопасть и ветроэнергетическая установка с такой роторной лопастью
JP4924202B2 (ja) 繊維束の樹脂含浸方法および繊維束樹脂含浸装置
CN101831756B (zh) 一种双轴向经编机
US11571866B2 (en) Manufacturing process for papermaking endless belts using 3D printing technology
CN109968691A (zh) 一种纤维热塑性流延震动浸润预浸机
CN1275754C (zh) 织物帘布和钢丝帘布双面涂覆橡胶层用的联合轧光机
WO2010046537A1 (fr) Rouleau pour une section de séchage de machine de nappe de fibres et procédé de fabrication d'un rouleau de section de séchage de machine de nappe de fibres
CN116853882B (zh) 一种具有加热功能的纺织面料牵引设备
CN107416582A (zh) 一种碳纤维预浸丝束背衬纸剥离方法和装置
JP2018510795A (ja) 予成形品の作製方法および作製装置
CN114770980A (zh) 可生产变曲率型材的拉挤型材装置
KR100813863B1 (ko) 제지 기계의 에너지 재생을 위한 장치 및 방법
CN203174343U (zh) 小型簇绒地毯多功能整理轧水烘干装置
EP3601659B1 (fr) Machine de traitement de textiles
CN207987450U (zh) 一种改进的碳纤维编织用碳素箭头装置
CN208082800U (zh) 一种玻璃纤维布成卷生产装置
CN202626745U (zh) 纤维幅材机的刮刀设备及用于纤维幅材机刮刀设备的刮片
CN221263601U (zh) 电机绕组端箍的浸胶设备
EP2513361B1 (fr) Dispositif de formation de nappe comportant une courroie
CN206735457U (zh) 预缩机的平幅落布装置
CN220812947U (zh) 一种涤纶面料阻燃整理装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09821651

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09821651

Country of ref document: EP

Kind code of ref document: A1