WO2009158030A1 - Composite membrane and moisture adjustment module using the same - Google Patents
Composite membrane and moisture adjustment module using the same Download PDFInfo
- Publication number
- WO2009158030A1 WO2009158030A1 PCT/US2009/003832 US2009003832W WO2009158030A1 WO 2009158030 A1 WO2009158030 A1 WO 2009158030A1 US 2009003832 W US2009003832 W US 2009003832W WO 2009158030 A1 WO2009158030 A1 WO 2009158030A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composite membrane
- moisture
- membrane
- composite
- porous
- Prior art date
Abstract
Description
Claims