WO2009027686A1 - Améliorations concernant le revêtement des conduites - Google Patents

Améliorations concernant le revêtement des conduites Download PDF

Info

Publication number
WO2009027686A1
WO2009027686A1 PCT/GB2008/002927 GB2008002927W WO2009027686A1 WO 2009027686 A1 WO2009027686 A1 WO 2009027686A1 GB 2008002927 W GB2008002927 W GB 2008002927W WO 2009027686 A1 WO2009027686 A1 WO 2009027686A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
field joint
pipe
coating material
layer
Prior art date
Application number
PCT/GB2008/002927
Other languages
English (en)
Inventor
Damian Daykin
David Jackson
Original Assignee
Pipeline Induction Heat Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pipeline Induction Heat Limited filed Critical Pipeline Induction Heat Limited
Publication of WO2009027686A1 publication Critical patent/WO2009027686A1/fr

Abstract

Cette invention concerne un procédé de revêtement d'un joint de chantier d'un pipeline entre deux longueurs de conduite raccordées (1a, 1b), chaque longueur étant revêtue le long d'une partie de sa longueur. Le procédé comprend les étapes consistant à appliquer une couche (5) d'un premier matériau de revêtement sur le joint de chantier de sorte qu'il entre en contact avec le revêtement de conduite (9, 10, 11, 12) de chacune des deux longueurs de conduite et qu'il s'étende entre celles-ci, et appliquer ensuite une couche d'un second matériau de revêtement sur le joint de chantier. Le premier matériau de revêtement est apte à se lier à au moins un composant du revêtement de conduite (9, 10, 11, 12) et le second matériau de revêtement est un matériau polymérisable. Le premier matériau de revêtement peut être une polyoléfine telle que le polypropylène et le second matériau de revêtement peut comprendre une matière chimique à base d'uréthanne qui forme du polyuréthanne suite à son durcissement.
PCT/GB2008/002927 2007-08-29 2008-08-29 Améliorations concernant le revêtement des conduites WO2009027686A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB0716750.5 2007-08-29
GB0716750A GB0716750D0 (en) 2007-08-29 2007-08-29 Improvements in coating pipes

Publications (1)

Publication Number Publication Date
WO2009027686A1 true WO2009027686A1 (fr) 2009-03-05

Family

ID=38616893

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2008/002927 WO2009027686A1 (fr) 2007-08-29 2008-08-29 Améliorations concernant le revêtement des conduites

Country Status (2)

Country Link
GB (1) GB0716750D0 (fr)
WO (1) WO2009027686A1 (fr)

Cited By (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ITMI20110053A1 (it) * 2011-01-20 2012-07-21 Saipem Spa Metodo di giunzione di spezzoni di tubo per realizzare tubazioni per idrocarburi, in particolare tubazioni sottomarine
GB2490153A (en) * 2010-07-05 2012-10-24 Acergy France Sa Coating a joint of a pipe during fabrication of the pipe from pipe sections
NL2007692C2 (en) * 2011-11-01 2013-05-07 Heerema Marine Contractors Nl Pipeline unit.
NL2007693C2 (en) * 2011-11-01 2013-05-07 Heerema Marine Contractors Nl Pipeline unit.
US8857700B2 (en) 2010-06-04 2014-10-14 Shawcor Ltd. Low temperature method for forming field joints on undersea pipelines
GB2516981A (en) * 2013-08-09 2015-02-11 Pipeline Induction Heat Ltd Mould equipment for pipeline section coating and methods for coating of pipeline sections with moulds
WO2015017938A1 (fr) * 2013-08-09 2015-02-12 Shawcor Ltd. Raccords à haute température
CN104500917A (zh) * 2014-12-17 2015-04-08 四川金发科技发展有限公司 一种管道补口方法
CN104500918A (zh) * 2014-12-17 2015-04-08 四川金发科技发展有限公司 一种管道补口方法
CN104500916A (zh) * 2014-12-17 2015-04-08 四川金发科技发展有限公司 一种管道补口
CN104500920A (zh) * 2014-12-17 2015-04-08 四川金发科技发展有限公司 一种补口机具及施工方法
CN104633392A (zh) * 2014-12-17 2015-05-20 四川金发科技发展有限公司 一种补口方法
CN104633391A (zh) * 2014-12-17 2015-05-20 四川金发科技发展有限公司 一种补口方法
WO2016095766A1 (fr) * 2014-12-17 2016-06-23 四川金发科技发展有限公司 Machine de revêtement de joint de pipeline, procédé de construction et nouvelle structure de revêtement de joint de pipeline
WO2017123915A1 (fr) * 2016-01-15 2017-07-20 Basf Se Article composite
EP3247543A4 (fr) * 2015-01-23 2018-10-17 Shawcor Ltd. Raccord bicouche de champ moulé par injection pour pipeline
US10309162B2 (en) 2010-07-05 2019-06-04 Acergy France SAS Techniques for coating pipes
US10450470B2 (en) 2013-11-26 2019-10-22 Basf Se Polyurethane elastomeric composition and method of preparing the same
CN111344366A (zh) * 2017-11-16 2020-06-26 陶氏环球技术有限责任公司 用于涂覆管道现场接头的方法
US10711090B2 (en) 2013-06-24 2020-07-14 Materia, Inc. Thermal insulation
US11034124B2 (en) 2015-11-02 2021-06-15 Agc Chemicals Americas, Inc. Insulated conduit including a fluoropolymer composition for use as a thermal insulation layer

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0309597A1 (fr) * 1987-09-29 1989-04-05 Blome GmbH & Co. Kommanditgesellschaft Revêtement de la zone de raccordement de tuyaux en acier soudés l'un à l'autre
WO1996003222A1 (fr) * 1994-07-28 1996-02-08 Isotub Coating Procede, dispositif et installation pour revetir un tube notamment un tube de pipeline
GB2307192A (en) * 1995-11-14 1997-05-21 Wood Limited E Pipe-coating method and product
US5662974A (en) * 1994-06-17 1997-09-02 Shaw Industries Ltd. Superimposed coverings having increased stability
WO2002011972A1 (fr) * 2000-08-03 2002-02-14 Pipeline Induction Heat Ltd Appareil et procede de revetement de conduites
WO2003095887A1 (fr) * 2002-05-08 2003-11-20 Socotherm S.P.A. Procede d'isolation de champ de raccords pour des canalisations de transport de fluides

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0309597A1 (fr) * 1987-09-29 1989-04-05 Blome GmbH & Co. Kommanditgesellschaft Revêtement de la zone de raccordement de tuyaux en acier soudés l'un à l'autre
US5662974A (en) * 1994-06-17 1997-09-02 Shaw Industries Ltd. Superimposed coverings having increased stability
WO1996003222A1 (fr) * 1994-07-28 1996-02-08 Isotub Coating Procede, dispositif et installation pour revetir un tube notamment un tube de pipeline
GB2307192A (en) * 1995-11-14 1997-05-21 Wood Limited E Pipe-coating method and product
WO2002011972A1 (fr) * 2000-08-03 2002-02-14 Pipeline Induction Heat Ltd Appareil et procede de revetement de conduites
WO2003095887A1 (fr) * 2002-05-08 2003-11-20 Socotherm S.P.A. Procede d'isolation de champ de raccords pour des canalisations de transport de fluides

Cited By (47)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8857700B2 (en) 2010-06-04 2014-10-14 Shawcor Ltd. Low temperature method for forming field joints on undersea pipelines
GB2490153A (en) * 2010-07-05 2012-10-24 Acergy France Sa Coating a joint of a pipe during fabrication of the pipe from pipe sections
US10309162B2 (en) 2010-07-05 2019-06-04 Acergy France SAS Techniques for coating pipes
US10160147B2 (en) 2010-07-05 2018-12-25 Acergy France SAS Techniques for coating pipes
GB2490153B (en) * 2010-07-05 2013-10-02 Acergy France Sa Techniques for coating pipes
WO2012098528A1 (fr) * 2011-01-20 2012-07-26 Saipem S.P.A. Procédé de jonction de conduites pour la construction de canalisations d'hydrocarbures, en particulier, des canalisations sous-marines
US10527206B2 (en) 2011-01-20 2020-01-07 Saipem S.P.A. Pipe-joining method for building hydrocarbon pipelines, in particular, underwater pipelines
ITMI20110053A1 (it) * 2011-01-20 2012-07-21 Saipem Spa Metodo di giunzione di spezzoni di tubo per realizzare tubazioni per idrocarburi, in particolare tubazioni sottomarine
CN103328872A (zh) * 2011-01-20 2013-09-25 塞彭公司 构造碳氢化合物管线且尤其是水下管线的管道连接方法
GB2509477B (en) * 2011-10-31 2016-09-14 Heerema Marine Contractors Nl Pipeline unit
WO2013066170A1 (fr) * 2011-10-31 2013-05-10 Heerema Marine Contractors Nederland B.V. Unité de canalisation
GB2509477A (en) * 2011-10-31 2014-07-02 Heerema Marine Contractors Nl Pipeline unit
GB2509678B (en) * 2011-10-31 2018-07-25 Heerema Marine Contractors Nl Pipeline unit
US9657872B2 (en) 2011-10-31 2017-05-23 Heerema Marine Contractors Nederland Se Pipeline unit
AU2012331694B2 (en) * 2011-10-31 2017-02-02 Heerema Marine Contractors Nederland Se Pipeline unit
AU2012331693B2 (en) * 2011-10-31 2016-10-06 Heerema Marine Contractors Nederland Se Pipeline unit
US9322494B2 (en) 2011-10-31 2016-04-26 Heerema Marine Contractors Nederland Se Pipeline unit
GB2509678A (en) * 2011-10-31 2014-07-09 Heerema Marine Contractors Nl Pipeline unit
WO2013066169A1 (fr) * 2011-10-31 2013-05-10 Heerema Marine Contractors Nederland B.V. Unité de canalisation
NL2007693C2 (en) * 2011-11-01 2013-05-07 Heerema Marine Contractors Nl Pipeline unit.
NL2007692C2 (en) * 2011-11-01 2013-05-07 Heerema Marine Contractors Nl Pipeline unit.
US10711090B2 (en) 2013-06-24 2020-07-14 Materia, Inc. Thermal insulation
US10161556B2 (en) 2013-08-09 2018-12-25 Shawcor, Ltd. High temperature insulated pipelines
US9791091B2 (en) 2013-08-09 2017-10-17 Agc Chemicals Americas, Inc. High temperature field joints
WO2015017938A1 (fr) * 2013-08-09 2015-02-12 Shawcor Ltd. Raccords à haute température
GB2516981A (en) * 2013-08-09 2015-02-11 Pipeline Induction Heat Ltd Mould equipment for pipeline section coating and methods for coating of pipeline sections with moulds
US9810366B2 (en) 2013-08-09 2017-11-07 Shawcor Ltd. High temperature field joints
US10450470B2 (en) 2013-11-26 2019-10-22 Basf Se Polyurethane elastomeric composition and method of preparing the same
CN104633391A (zh) * 2014-12-17 2015-05-20 四川金发科技发展有限公司 一种补口方法
CN104500917A (zh) * 2014-12-17 2015-04-08 四川金发科技发展有限公司 一种管道补口方法
CN104500918A (zh) * 2014-12-17 2015-04-08 四川金发科技发展有限公司 一种管道补口方法
CN104500916A (zh) * 2014-12-17 2015-04-08 四川金发科技发展有限公司 一种管道补口
CN104500920A (zh) * 2014-12-17 2015-04-08 四川金发科技发展有限公司 一种补口机具及施工方法
CN104633392A (zh) * 2014-12-17 2015-05-20 四川金发科技发展有限公司 一种补口方法
WO2016095766A1 (fr) * 2014-12-17 2016-06-23 四川金发科技发展有限公司 Machine de revêtement de joint de pipeline, procédé de construction et nouvelle structure de revêtement de joint de pipeline
US10105885B2 (en) 2015-01-23 2018-10-23 Shawcor Ltd. Two-layered injection molded field joint for pipeline applications
EP3247543A4 (fr) * 2015-01-23 2018-10-17 Shawcor Ltd. Raccord bicouche de champ moulé par injection pour pipeline
US11034124B2 (en) 2015-11-02 2021-06-15 Agc Chemicals Americas, Inc. Insulated conduit including a fluoropolymer composition for use as a thermal insulation layer
WO2017123915A1 (fr) * 2016-01-15 2017-07-20 Basf Se Article composite
WO2017123974A1 (fr) * 2016-01-15 2017-07-20 Basf Se Article composite
WO2017123885A1 (fr) * 2016-01-15 2017-07-20 Basf Se Article composite
WO2017123953A1 (fr) * 2016-01-15 2017-07-20 Basf Se Article composite
US10816130B2 (en) 2016-01-15 2020-10-27 Basf Se Composite article
US10830387B2 (en) 2016-01-15 2020-11-10 Basf Se Composite article
US10837591B2 (en) 2016-01-15 2020-11-17 Basf Se Composite article
US10895342B2 (en) 2016-01-15 2021-01-19 Basf Se Composite article
CN111344366A (zh) * 2017-11-16 2020-06-26 陶氏环球技术有限责任公司 用于涂覆管道现场接头的方法

Also Published As

Publication number Publication date
GB0716750D0 (en) 2007-10-10

Similar Documents

Publication Publication Date Title
WO2009027686A1 (fr) Améliorations concernant le revêtement des conduites
CA2800370C (fr) Procede et systeme basse pression permettant de former des joints de montage sur des conduites sous-marines
US11168827B2 (en) Method of and system for coating a field joint of a pipe
EP1504214B1 (fr) Procede d'isolation de champ de raccords pour des canalisations de transport de fluides
US10641429B2 (en) Techniques for protecting pipe coatings
AU2017270651B2 (en) Method for connecting two unitary elements of a conduit for transporting fluids by means of a sleeve
EP3717821B1 (fr) Canalisation revêtue
JP5783089B2 (ja) 鋼材溶接継手部の防食被覆方法及び装置
US20240026993A1 (en) Pipeline junction coating
JP3072554B2 (ja) 水道用保温管の接合方法及び接合部の保温方法及び末端処理方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 08788474

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 08788474

Country of ref document: EP

Kind code of ref document: A1