WO2008097013A1 - Organic/inorganic composite separator having porous active coating layer and electrochemical device containing the same - Google Patents
Organic/inorganic composite separator having porous active coating layer and electrochemical device containing the same Download PDFInfo
- Publication number
- WO2008097013A1 WO2008097013A1 PCT/KR2008/000706 KR2008000706W WO2008097013A1 WO 2008097013 A1 WO2008097013 A1 WO 2008097013A1 KR 2008000706 W KR2008000706 W KR 2008000706W WO 2008097013 A1 WO2008097013 A1 WO 2008097013A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- organic
- inorganic
- composite separator
- inorganic composite
- separator according
- Prior art date
Abstract
Description
Claims