Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
  • C08G63/88—Post-polymerisation treatment
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
  • C08G63/02—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds
  • C08G63/06—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds derived from hydroxycarboxylic acids
  • C08G63/08—Lactones or lactides
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J3/00—Processes of treating or compounding macromolecular substances
  • C08J3/12—Powdering or granulating

Definitions

• the present invention relates to lactide particles, more specifically to lactide particles which are stable enough to be stored and transported at room temperature and which have a quality high enough for use as starting material for polylactic acid.
• lactic acid exists in two forms which are optical enantiomers, designated as D-lactic acid and L- lactic acid.
• D-lactic acid, L-lactic acid, or mixtures thereof may be polymerized to form an intermediate molecular weight polylactic acid which, after the ring-closure reaction, generates lactide as earlier disclosed.
• the lactide (sometimes also referred to as dilactide), or the cyclic dimer of lactic acid, may have one of three types of stereochemical configurations depending on whether it is derived from two L- lactic acid molecules, two D-lactic acid molecules or an L- lactic acid molecule and a D-lactic acid molecule.
• L-lactide L-lactide
• D-lactide D-lactide
• meso-lactide meso-lactide
• a 50/50 mixture of L-lactide and D- lactide with a melting point of about 126°C is often referred to in the literature as D, L-lactide.
• the optical activity of either lactic acid or lactide is known to alter under certain conditions, with a tendency toward equilibrium at optical inactivity, where equal amounts of the D and L enantiomers are present.
• Relative concentrations of D and L enantiomers in the starting materials, the presence of impurities or catalysts, varying temperatures, residence times, and pressures are known to affect the rate of such racemization.
• the optical purity of the lactic acid or the lactide is decisive for the stereochemistry of the polylactic acid obtained upon ring- opening polymerization of the lactide.
• stereochemistry, and molecular weight are the key parameters for polymer quality.
• crystalline powdery lactide is used as the starting material. These crystals, which are commercially available for over 30 years now, are highly hygroscopic and are packed under inert atmosphere in damp- and air-tight packages and stored in freezers (temperature below 12 0 C) . It will be clear that these precautions cannot be taken when polylactic acid is used for bulk applications because it would render the product too expensive.
• the present invention is directed to a method for the manufacture of stable, high-quality lactide particles, said method comprising subjecting molten lactide to a flaking process that effectively transforms the liquid lactide melt to a coarse solid granulate.
• lactide particles also referred to as flakes
• stable lactide particles is meant that when storing the lactide particles having an initial free acid content of at most 5 meq/kg at 20 degrees Celcius in air, the free acid content will still be below 2000 after 10 weeks of storage.
• the flaking method or process according to the present invention is a rapid, cheap and surprisingly efficient method for producing stable lactide particles.
• the powdery crystalline lactides used in the medical industry are known to be manufactured via solvent crystallization as this is a technique with which the high chemical purity, that is required in medical applications, can be achieved.
• Solvent crystallization is however a very expensive, not environmentally friendly and a complex process due to the solvents that are used.
• the flaking process according to the present invention does not have these disadvantages .
• the present flaking process does also not include lengthy processing times and additional extensive drying steps as is the case in for example when a prilling process is used to manufacture lactide particles. And further, problems such as racemization, hydrolysis and oxidation are prevented in using the flaking process according to the present invention, which therefore results in lactide particles of high quality, significantly higher than for example lactide particles made via prilling.
• the flaking process according to the present invention for example, a production rate could be obtained, depending on cooling temperature and drum rotational speed, which was minimally two to three times higher compared to an alternative process used for making lactide pastilles. Furthermore, the resulting lactide flakes exhibit favorable properties making them very suitable for further processing. We found for example that the lactide flakes of the present invention can be relatively rapidly and easy processed further in a subsequent melting step leading to short residence times in this melting step. These short, residence times offer the advantage that the risk of side reactions occurring, leading to for example the formation of lactic acid, lactoyllactic acid and water, is significantly reduced and thus the purity of the high quality lactide is preserved.
• the temperature of the melting process can be lowered which also is positive as above-mentioned side reactions are less likely to occur.
• the lactide particles made via the present flaking process are easy to disperse and thus less mechanical input is required for said homogenization process. This also reduces the risk of any side reactions occurring.
• the lactide used in the flaking process according to the present invention is in the molten form, meaning that all lactide entering the solidification process is at a temperature above the melting point of the lactide.
• the flaking process comprises contacting a continuous flow of molten lactide with a surface with a temperature lower than the melting point of the lactide, allowing the lactide melt to solidify on said surface, and removing the solid lactide from that surface.
• Said surface may be cooled internally or externally and this can be done by various means as known to the skilled person.
• the solidified lactide falls off of the surface under the influence of gravity and is thus removed from the surface.
• the solidified lactide on the surface is brought in contact with a means that removes or scrapes off the solidified lactide from said surface for product collection.
• the apparatus used for the flaking process preferably are prepared from corrosion-resistant material such as stainless steel. Further, to avoid water uptake of the lactide particles, the flaking process is preferably conducted under inert gas or dry atmosphere such as under nitrogen or dry air.
• the flaking process according to the present invention may be performed with the conventional drum flaker apparatus used in the various thermal processes in chemical and food industries.
• molten lactide solidifies on the surface of the drum, after which it is removed from said surface either by means of gravity or by means of some type of scraping-device.
• drum flakers Various types of drum flakers are possible. Some examples hereof are rotating drum flakers wherein the rotating drum runs through a lactide melt in a dip pan underneath the drum, or rotating drum flakers wherein the lactide melt is "spread" over the rotating drum by means of for example an overhead applicator roll. It is of course also possible to apply the lactide melt on said rotating drum by other means well-known to the person skilled in the art.
• An example may be the spraying or dripping of lactide melt onto the surface of the drum.
• Another example of a suited means for use in the flaking process is a belt flaker.
• the lactide melt can be applied on a cooled and moving belt instead of a rotating drum.
• the lactide solidifies after which it is removed either by means of gravity or by means of some type of scraping device.
• a sieving step may be performed after the flaking process to avoid dusting during transport and during further processing to form polylactide.
• Stable lactide particles can be made having a various surface area per unit of volume. Particles can be obtained with a surface area per unit of volume of between 1000 to 3000 m "1 but also up to 10000 irf 1 . It was found that lactide particles having a surface area per unit of volume of from 3000 to 10000 irf 1 showed the most ideal chemical stability for transport and storage and for further processing in the subsequent melting step or other processing steps.
• the optical purity of the lactide is very important for the stereochemistry of the polylactic acid that is obtained. Therefore, it is preferred that the lactide present in the particles according to the invention contains more than 95% by weight D- or L-lactide, preferably more than 98.5% by weight D- or L-lactide, most preferably more than 99.5% D-or L-lactide by weight.
• the water content of the lactide is also an important factor for the stability of the lactide particles.
• Contamination by water ultimately hydrolyzes the lactide to lactic acid It was found that if the water content is below 200 ppm, the stability of the lactide particles when stored at ambient temperature in airtight and vapor-tight packages is ensured for several months. Preferably, the water content is below 100 ppm because it further increases the stability and thus shelf life of the lactide.
• the water content of the lactide can be measured by means of a Karl-Fisher titration as will be known by the artisan.
• the free acid content of the lactide is important for the stability and quality of the lactide.
• the presence of lactic acid and or lactoyl lactic acid in the lactide monomer will result in reduced rates of polymerization in the further manufacture of polylactic acid and in polylactic acid polymers of limited molecular weight.
• the free acid content is below 50 inilli-equivalents per Kg lactide (meq.Kg "1 ) the stability of the lactide particles when stored at ambient temperature in air-tight and vapor-tight packages is ensured for several months.
• the acid content is below 20 meq.Kg "1 because it further increases the stability of the lactide.
• the acid content is between 0 and 10 meq.Kg "1 and most preferably, the free acid content is less than 5 meq.Kg "1 .
• the free acid content can be measured by means of titration using for instance sodium methylate or potassium methylate in water-free methanol, as will be clear for the artisan.
• the lactide used as starting material for the shaping process may have been prepared by any conventional lactide process such as water removal from a lactic acid solution or condensation reaction of lactate esters, followed by a ring- closure reaction in a lactide reactor with the help of a catalyst.
• the crude lactide is further purified by for instance distillation and/or crystallization prior to the shaping process.
• the lactide reactor can be of any suitable type that is designed for heat sensitive materials.
• a reactor that can maintain a uniform film thickness, such as a falling film or agitated thin-film evaporator is most preferred, because film formation increases the rate of mass transfer.
• lactide can quickly form and vaporize, and as lactide vaporizes, more lactide is produced as dictated by the polylactic acid/lactide equilibrium reaction.
• these lactide reactors are operated under reduced pressure such as between about 1 mmHg and 100 mmHg.
• the temperature of the lactide formation is kept between 150 0 C and 250 0 C.
• Many suitable catalysts are known, such as metal oxides, metal halides, metal dusts, anionic clay, and organic metal compounds derived from carboxylic acids or the like. Normally a tin (II) catalyst is used for lactide formation.
• Stabilizers may also be added to the lactide reactor in order to facilitate lactide formation and discourage degenerative lactic acid and lactide reactions.
• Stabilizers such as antioxidants, either manufactured or naturally occurring, can be used to reduce the number of degradation reactions that occur during the process of polylactic acid and lactide production. Stabilizers may also reduce the rate of lactide formation during this process. Therefore, efficient production of lactide requires proper reactor design for minimal thermal severity and a proper balance between the catalyst and any use of process stabilizers.
• the stabilizing agent may include primary antioxidants and/or secondary antioxidants.
• Primary antioxidants are those which inhibit free radical propagation reactions, such as and not limited to alkylidene bisphenols, alkyl phenols, aromatic amines, aromatic nitro and nitroso compounds, and quinones.
• secondary antioxidants break down hydroperoxides.
• Some non-limiting examples of secondary antioxidants include: phosphites, organic sulfides, thioethers, dithiocarbamates, and dithiophosphates .
• Antioxidants include such compounds as trialkyl phosphites, mixed alkyl/aryl phosphites, alkylated aryl phosphites, sterically hindered aryl phosphites, aliphatic spirocyclic phosphites, sterically hindered phenyl spirocyclics, sterically hindered bisphosphonites, hydroxyphenyl propionates, hydroxy benzyls, alkylidene bisphenols, alkyl phenols, aromatic amines, thioethers, hindered amines, hydroquinones, and mixtures thereof.
• phosphite-containing compounds Preferably, phosphite-containing compounds, hindered phenolic compounds, or other phenolic compounds are used as process stabilizing antioxidants. Most preferably, phosphite- containing compounds are used.
• the amount of process stabilizer used can vary depending upon the optical purity desired of the resulting lactide, the amount and type of catalyst used, and the conditions inside of the lactide reactor. Normally amounts varying from 0.01 to 0.3 wt . % process stabilizer can be used.
• dehydration or anti- hydrolysis agents may be used. These dehydration agents favor the formation of lactide. Further, they may be used in a later stage of the manufacturing process for polylactic acid as well as for preventing chain scission by water. Compounds based on peroxide may be used for this purpose but preferred are compounds containing the carbodiimide functionality.
• the carbodiimide compound is a compound having one or more carbodiimide groups in a molecule and also includes a polycarbodiimide compound.
• dicyclohexyl carbodiimide diisopropyl carbodiimide, dimethyl carbodiimide, diisobutyl carbodiimide, dioctyl carbodiimide, diphenyl carbodiimide, naphthyl carbodiimide, etc.
• industrially easily available compounds such as dicyclohexyl carbodiimide, diisopropyl carbodiimide or products like Stabaxol® by Rheinchemie are used.
• the lactide particle usually comprises more than 95% by weight lactide, preferably more than 98.5% by weight lactide, most preferably more than 99.5% by weight.
• the flaking process according to the present invention can either be combined with the preparation and/or purification, or not.
• the lactide is obtained form distillation, it makes sense to directly couple a flaking machine to the distillation column because the lactide is already in its melted form.
• the final purification step of the lactide comprises melt- crystallization, a flaking machine can be directly coupled to the melt crystallisator .
• Flaking of L-lactide using a lab-scale rotating drum flaker Fresh L-lactide ex. Purac® ⁇ 5 meq/Kg free lactic acid) was molten using a stirred, oil-heated vessel. Subsequently, the liquid with a temperature of between 105-120 0 C was metered during flaking into the dip pan underneath a rotating drum flaker having a surface area of 0.75 m 2 . The liquid lactide was dosed at such a rate that the level of the liquid remained constant in the dip pan. Due to the internal cooling of the drum, the lactide solidifies on the drum surface. The cooling water for the rotating drum was kept at a temperature between 10 and 35 0 C and the rotational speed at between 5 and 15rpm. Further, the dipping depth of the drum into the molten lactide was varied and tests were done at a dipping depth of 20 mm and 50 mm.
• the flakes produced have an average height of between 0.3 and 0.7 mm, a width of 1 to 3mm and a length of 3 to 10mm.
• the surface area per unit of volume varied between 4000 and 10000 rrf 1 .
• the bulk density was between 500 and 600 kg/rrf 3 .

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Polyesters Or Polycarbonates (AREA)
• Processes Of Treating Macromolecular Substances (AREA)
• Processing And Handling Of Plastics And Other Materials For Molding In General (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
• Medicinal Preparation (AREA)
• Heterocyclic Compounds That Contain Two Or More Ring Oxygen Atoms (AREA)
• Biological Depolymerization Polymers (AREA)

Priority Applications (10)

Applications Claiming Priority (4)

Publications (1)

Family

ID=38973061

Family Applications (2)

Family Applications After (1)

Country Status (12)

Cited By (2)

Families Citing this family (8)

Citations (2)

Family Cites Families (21)

• 2007
  • 2007-11-28 JP JP2009537660A patent/JP2010510975A/ja active Pending
  • 2007-11-28 CA CA2670934A patent/CA2670934C/en active Active
  • 2007-11-28 AU AU2007327594A patent/AU2007327594B2/en active Active
  • 2007-11-28 KR KR1020097013184A patent/KR101469574B1/ko active Active
  • 2007-11-28 MX MX2009005581A patent/MX2009005581A/es active IP Right Grant
  • 2007-11-28 ES ES07847442T patent/ES2429291T3/es active Active
  • 2007-11-28 EP EP07847444.2A patent/EP2097469B1/en active Active
  • 2007-11-28 BR BRPI0719152-9A patent/BRPI0719152B1/pt active IP Right Grant
  • 2007-11-28 EP EP07847442.6A patent/EP2084207B1/en active Active
  • 2007-11-28 PL PL07847442T patent/PL2084207T3/pl unknown
  • 2007-11-28 MX MX2009005580A patent/MX2009005580A/es active IP Right Grant
  • 2007-11-28 BR BRPI0719591-5A patent/BRPI0719591B1/pt active IP Right Grant
  • 2007-11-28 JP JP2009537661A patent/JP5489720B2/ja active Active
  • 2007-11-28 AU AU2007327592A patent/AU2007327592B9/en active Active
  • 2007-11-28 RU RU2009118566/04A patent/RU2451695C2/ru active
  • 2007-11-28 DK DK07847444.2T patent/DK2097469T3/da active
  • 2007-11-28 DK DK07847442.6T patent/DK2084207T3/da active
  • 2007-11-28 PL PL07847444T patent/PL2097469T3/pl unknown
  • 2007-11-28 KR KR1020097013083A patent/KR101469573B1/ko active Active
  • 2007-11-28 ES ES07847444T patent/ES2430063T3/es active Active
  • 2007-11-28 CA CA2670931A patent/CA2670931C/en active Active
  • 2007-11-28 WO PCT/EP2007/062917 patent/WO2008065130A1/en not_active Ceased
  • 2007-11-28 RU RU2009119292/04A patent/RU2454437C2/ru active
  • 2007-11-28 WO PCT/EP2007/062919 patent/WO2008065132A1/en not_active Ceased

Patent Citations (2)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events