WO2008046877A2 - Feuille de verre mate - Google Patents
Feuille de verre mate Download PDFInfo
- Publication number
- WO2008046877A2 WO2008046877A2 PCT/EP2007/061126 EP2007061126W WO2008046877A2 WO 2008046877 A2 WO2008046877 A2 WO 2008046877A2 EP 2007061126 W EP2007061126 W EP 2007061126W WO 2008046877 A2 WO2008046877 A2 WO 2008046877A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- glass sheet
- acid
- less
- etched
- glass
- Prior art date
Abstract
Selon l'invention, des feuilles de verre mates, attaquées par un acide, présentent une surface attaquée par un acide dont la rugosité de surface est définie par : Rz supérieur à 12 et inférieur à 22, et Rz/RSm supérieur à 0,18 et inférieur à 0,30, mesurée sur une longueur d'échantillon de 20 mm avec une coupure utilisant toute la longueur de données sélectionnées, un filtre à faible portée de 0,008 mm et un filtre à longue portée de 0,8 mm. De telles feuilles de verre peuvent présenter des propriétés antidérapantes et servir avantageusement de revêtement de sol.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP07821491A EP2074072A2 (fr) | 2006-10-18 | 2007-10-18 | Feuille de verre mate |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP06122490 | 2006-10-18 | ||
EP06122490.3 | 2006-10-18 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2008046877A2 true WO2008046877A2 (fr) | 2008-04-24 |
WO2008046877A3 WO2008046877A3 (fr) | 2008-06-12 |
Family
ID=37814236
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2007/061126 WO2008046877A2 (fr) | 2006-10-18 | 2007-10-18 | Feuille de verre mate |
Country Status (2)
Country | Link |
---|---|
EP (1) | EP2074072A2 (fr) |
WO (1) | WO2008046877A2 (fr) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2287120A1 (fr) * | 2009-07-16 | 2011-02-23 | AGC Glass Europe | Article de verre décoratif |
WO2011036155A3 (fr) * | 2009-09-25 | 2012-01-19 | Agc Glass Europe | Article de décoration en verre |
WO2013013900A1 (fr) | 2011-07-28 | 2013-01-31 | Agc Glass Europe | Procede de fabrication d'une feuille de verre antiderapante |
WO2013079263A1 (fr) | 2011-11-29 | 2013-06-06 | Agc Glass Europe | Plaque de verre présentant des propriétés non glissantes |
WO2014012809A1 (fr) * | 2012-07-18 | 2014-01-23 | Agc Glass Europe | Feuille de verre dépolie |
RU2635312C2 (ru) * | 2011-06-30 | 2017-11-10 | Гардиан Индастриз Корп. | Способ изготовления термически обработанного и подвергнутого травлению/фрезерованию ионным пучком покрытого изделия с использованием защитной пленки из алмазоподобного углерода (dlc) |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6553788B1 (en) * | 1999-02-23 | 2003-04-29 | Nippon Sheet Glass Co., Ltd. | Glass substrate for magnetic disk and method for manufacturing |
DE20207373U1 (de) * | 2002-05-10 | 2003-06-12 | Toepfer Ct Essen Gmbh | Chemische Zusammensetzung zur Oberflächenbehandlung |
US20030170459A1 (en) * | 2002-03-05 | 2003-09-11 | Zuel Company, Inc. | Anti-reflective glass surface with improved cleanability |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5014717A (fr) * | 1973-06-08 | 1975-02-17 |
-
2007
- 2007-10-18 EP EP07821491A patent/EP2074072A2/fr not_active Withdrawn
- 2007-10-18 WO PCT/EP2007/061126 patent/WO2008046877A2/fr active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6553788B1 (en) * | 1999-02-23 | 2003-04-29 | Nippon Sheet Glass Co., Ltd. | Glass substrate for magnetic disk and method for manufacturing |
US20030170459A1 (en) * | 2002-03-05 | 2003-09-11 | Zuel Company, Inc. | Anti-reflective glass surface with improved cleanability |
DE20207373U1 (de) * | 2002-05-10 | 2003-06-12 | Toepfer Ct Essen Gmbh | Chemische Zusammensetzung zur Oberflächenbehandlung |
Non-Patent Citations (1)
Title |
---|
DATABASE WPI Week 197629 Derwent Publications Ltd., London, GB; AN 1976-54716X XP002424506 & JP 50 014717 A (MATSUSHITA ELECTRIC WORKS LTD) 17 February 1975 (1975-02-17) * |
Cited By (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2287120A1 (fr) * | 2009-07-16 | 2011-02-23 | AGC Glass Europe | Article de verre décoratif |
WO2011006883A3 (fr) * | 2009-07-16 | 2011-06-23 | Agc Glass Europe | Article de décoration en verre |
WO2011036155A3 (fr) * | 2009-09-25 | 2012-01-19 | Agc Glass Europe | Article de décoration en verre |
RU2635312C2 (ru) * | 2011-06-30 | 2017-11-10 | Гардиан Индастриз Корп. | Способ изготовления термически обработанного и подвергнутого травлению/фрезерованию ионным пучком покрытого изделия с использованием защитной пленки из алмазоподобного углерода (dlc) |
WO2013013900A1 (fr) | 2011-07-28 | 2013-01-31 | Agc Glass Europe | Procede de fabrication d'une feuille de verre antiderapante |
BE1020126A3 (fr) * | 2011-07-28 | 2013-05-07 | Agc Glass Europe | Procede de fabrication d'une feuille de verre antiderapante. |
JP2014523850A (ja) * | 2011-07-28 | 2014-09-18 | エージーシー グラス ユーロップ | 滑り止めガラス板を製造するための方法 |
EA023520B1 (ru) * | 2011-07-28 | 2016-06-30 | Агк Гласс Юроп | Способ изготовления нескользящего стеклянного листа |
WO2013079263A1 (fr) | 2011-11-29 | 2013-06-06 | Agc Glass Europe | Plaque de verre présentant des propriétés non glissantes |
WO2014012809A1 (fr) * | 2012-07-18 | 2014-01-23 | Agc Glass Europe | Feuille de verre dépolie |
BE1020793A3 (fr) * | 2012-07-18 | 2014-05-06 | Agc Glass Europe | Feuille de verre depolie. |
Also Published As
Publication number | Publication date |
---|---|
EP2074072A2 (fr) | 2009-07-01 |
WO2008046877A3 (fr) | 2008-06-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2008046877A2 (fr) | Feuille de verre mate | |
CN105874356B (zh) | 具有保留的光学性质的耐划痕制品 | |
DE102009050568A1 (de) | Einrichtung mit verminderten Reibeigenschaften | |
EP2454207B1 (fr) | Article de verre décoratif | |
CN104136391A (zh) | 夹层玻璃及安装有该夹层玻璃的安装结构体 | |
JP2003535216A (ja) | 低光散乱超疎性表面を有する基材およびその製造方法 | |
WO2012163946A1 (fr) | Élément substrat pour l'application d'un revêtement facile à nettoyer | |
PT1981822E (pt) | Substratos revestidos que têm camadas internas de revestimento que exibem actividade fotocatalítica melhorada | |
CN109895472B (zh) | 一种自沉式塑胶地板及其制备方法 | |
US10590030B2 (en) | Glass plate, touch pad, and touch panel | |
CA2998262C (fr) | Panneau acoustique | |
US20240158293A1 (en) | Glass, glass-ceramic and ceramic articles with graded protective coatings having hardness and strength | |
KR102515679B1 (ko) | 향상된 표면파형을 갖는 라미네이티드 글라스 구조물 | |
JP2003247085A (ja) | 耐食、耐摩耗性装飾コーティング | |
EP1856004A1 (fr) | Substrat pour revêtement hydrophobe | |
CN102242560A (zh) | 磨砂面铝塑复合板 | |
CN105008584A (zh) | 装饰性深黑色涂层 | |
CN109811986A (zh) | 一种人造瓷砖及其制备方法和应用 | |
KR20180105149A (ko) | 샤워, 욕실 또는 욕실 스크린 물품 | |
CN205742861U (zh) | 一种隔音复合竹地板 | |
CN210105205U (zh) | 一种人造瓷砖 | |
BR112019015934A2 (pt) | Vidraça revestida, método de fabricação de uma vidraça revestida, e uso da vidraça revestida | |
KR102668321B1 (ko) | 경도 및 강도를 갖는 등급이 매겨진 보호 코팅 유리, 유리-세라믹 및 세라믹 제품 | |
CN210288966U (zh) | 一种富有光泽的石材涂料 | |
BRPI0417912A (pt) | método para produzir um revestimento de óxido de ferro sobre um artigo de vidro em um processo on-line de "float glass" à pressão atmosférica, e artigo de vidro revestido |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 07821491 Country of ref document: EP Kind code of ref document: A2 |
|
REEP | Request for entry into the european phase |
Ref document number: 2007821491 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2007821491 Country of ref document: EP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |