WO2007147811A2 - Verfahren zur herstellung dünner schichten eines silikons und dünnes silikon - Google Patents
Verfahren zur herstellung dünner schichten eines silikons und dünnes silikon Download PDFInfo
- Publication number
- WO2007147811A2 WO2007147811A2 PCT/EP2007/056040 EP2007056040W WO2007147811A2 WO 2007147811 A2 WO2007147811 A2 WO 2007147811A2 EP 2007056040 W EP2007056040 W EP 2007056040W WO 2007147811 A2 WO2007147811 A2 WO 2007147811A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicone
- layer
- thin
- cover layer
- extruded
- Prior art date
Abstract
Description
Claims