Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
  • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
  • B29C70/28—Shaping operations therefor
  • B29C70/30—Shaping by lay-up, i.e. applying fibres, tape or broadsheet on a mould, former or core; Shaping by spray-up, i.e. spraying of fibres on a mould, former or core
  • B29C70/32—Shaping by lay-up, i.e. applying fibres, tape or broadsheet on a mould, former or core; Shaping by spray-up, i.e. spraying of fibres on a mould, former or core on a rotating mould, former or core
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
  • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
  • B29C70/28—Shaping operations therefor
  • B29C70/40—Shaping or impregnating by compression not applied
  • B29C70/50—Shaping or impregnating by compression not applied for producing articles of indefinite length, e.g. prepregs, sheet moulding compounds [SMC] or cross moulding compounds [XMC]
  • B29C70/52—Pultrusion, i.e. forming and compressing by continuously pulling through a die
  • B29C70/521—Pultrusion, i.e. forming and compressing by continuously pulling through a die and impregnating the reinforcement before the die
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
  • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
  • B29C70/28—Shaping operations therefor
  • B29C70/40—Shaping or impregnating by compression not applied
  • B29C70/50—Shaping or impregnating by compression not applied for producing articles of indefinite length, e.g. prepregs, sheet moulding compounds [SMC] or cross moulding compounds [XMC]
  • B29C70/52—Pultrusion, i.e. forming and compressing by continuously pulling through a die
  • B29C70/525—Component parts, details or accessories; Auxiliary operations
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B60—VEHICLES IN GENERAL
  • B60C—VEHICLE TYRES; TYRE INFLATION; TYRE CHANGING; CONNECTING VALVES TO INFLATABLE ELASTIC BODIES IN GENERAL; DEVICES OR ARRANGEMENTS RELATED TO TYRES
  • B60C7/00—Non-inflatable or solid tyres
  • B60C7/10—Non-inflatable or solid tyres characterised by means for increasing resiliency
  • B60C7/14—Non-inflatable or solid tyres characterised by means for increasing resiliency using springs
  • B60C7/143—Non-inflatable or solid tyres characterised by means for increasing resiliency using springs having a lateral extension disposed in a plane parallel to the wheel axis
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B60—VEHICLES IN GENERAL
  • B60C—VEHICLE TYRES; TYRE INFLATION; TYRE CHANGING; CONNECTING VALVES TO INFLATABLE ELASTIC BODIES IN GENERAL; DEVICES OR ARRANGEMENTS RELATED TO TYRES
  • B60C7/00—Non-inflatable or solid tyres
  • B60C7/10—Non-inflatable or solid tyres characterised by means for increasing resiliency
  • B60C7/14—Non-inflatable or solid tyres characterised by means for increasing resiliency using springs
  • B60C7/16—Non-inflatable or solid tyres characterised by means for increasing resiliency using springs of helical or flat coil form
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
  • B29B15/00—Pretreatment of the material to be shaped, not covered by groups B29B7/00 - B29B13/00
  • B29B15/08—Pretreatment of the material to be shaped, not covered by groups B29B7/00 - B29B13/00 of reinforcements or fillers
  • B29B15/10—Coating or impregnating independently of the moulding or shaping step
  • B29B15/12—Coating or impregnating independently of the moulding or shaping step of reinforcements of indefinite length
  • B29B15/122—Coating or impregnating independently of the moulding or shaping step of reinforcements of indefinite length with a matrix in liquid form, e.g. as melt, solution or latex
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C2791/00—Shaping characteristics in general
  • B29C2791/001—Shaping in several steps
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2031/00—Use of polyvinylesters or derivatives thereof as moulding material
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2067/00—Use of polyesters or derivatives thereof, as moulding material
  • B29K2067/06—Unsaturated polyesters
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
  • B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
  • B29K2105/08—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of continuous length, e.g. cords, rovings, mats, fabrics, strands or yarns
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
  • B29L2030/00—Pneumatic or solid tyres or parts thereof
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/13—Hollow or container type article [e.g., tube, vase, etc.]
  • Y10T428/1352—Polymer or resin containing [i.e., natural or synthetic]
  • Y10T428/1372—Randomly noninterengaged or randomly contacting fibers, filaments, particles, or flakes

Definitions

• the present invention relates to composite materials based on fibers and curable resin, to composite parts made from such materials and to processes and devices for manufacturing such materials or composite parts.
• EP-AI 074 369 discloses a method of manufacturing a composite part of given thickness, of convex shape, comprising reinforcing fibers parallel to at least a preferred reinforcing direction, said fibers being embedded in a matrix based on a composition comprising an ionizing radiation-curable resin, the process comprising the following steps:
• a disadvantage, however, of this method is that it requires, after solidification of the resin-based matrix, first of all to cut the solid precomposite into elementary sections, then to superpose, to the desired final shape, the constrained elementary sections, as many successive manipulations that are penalizing from the industrial and antinomic point of view of the search for high production rates.
• Patent Application EP-A-174,250 (or US Pat. No. B2-6,926,853) has proposed:
• stabilization chamber comprising a series of irradiation tubes (referenced for example respectively 131 and 231 in Figures 1 and 4) emitting in the UV-visible spectrum; finally, winding said solid (stabilized) wire or ribbon over a large-diameter receiving coil (referenced, for example, 141 in Fig. 1), for intermediate storage.
• Composite parts may then be prepared by unwinding and then rewinding in solid layers of said wire or ribbon, on any support of appropriate shape.
• the high-pressure mold-baking operation has, in a known manner, its own disadvantages, among which a high cost of the molds, the need to check the tightness, a homogeneous distribution of pressures, which are responsible for high final industrial cost.
• a high cost of the molds the need to check the tightness, a homogeneous distribution of pressures, which are responsible for high final industrial cost.
• to have a uniform cooking pressure at very high pressures of the order of 50 bar it is necessary to use flexible cooking membranes whose life is limited.
• the Applicant has found a new method that allows to prepare a composite part of very high quality, in the form of a continuous ring, while overcoming the major drawbacks mentioned above, that is to say by removing from one part cutting operations and reassembly by superposition, avoiding the other part of the mold baking under high pressure.
• the present invention relates to a method of manufacturing a closed geometry composite block in the form of a continuous ring, based on fibers and a crosslinkable resin, by continuous winding and superposition in several layers a ribbon of reinforcing fibers embedded in a matrix based on a composition comprising a crosslinkable resin, said process comprising, from upstream to downstream, at least the following steps:
• Nc a predetermined number denoted "Nc" of layers of said ribbon for direct formation of said continuous ring on said support, Nc being less than 15;
• a major advantage of the process of the invention is that it allows the pure and simple removal of the stabilization chamber and its series of UV irradiation tubes as described in EPA-I 174 250 above, which significantly simplifies the manufacturing process and device, thereby substantially reducing the final industrial cost of the composite blocks concerned.
• the invention also relates to a device suitable for implementing the method according to the invention, such a device comprising at least upstream downstream (with reference to FIGS. 1 and 2):
• a vacuum chamber 13, 13a, 13b
• an impregnation chamber 14, 15, 16, 17, 18
• calibrating means (19, 20) comprising at least one calibration die (20) for forming a ribbon (21) comprising the fibers (11) and the resin (17) in the liquid state;
• a support or mandrel (23) of closed form for receiving said ribbon (21) for forming, by superposition of layers of said ribbon, a composite ring (30) on said support;
• the invention also relates in itself to a continuous composite ring, of monolithic structure, comprising unidirectional reinforcing fibers embedded in a matrix based on a crosslinkable resin that can be obtained according to the process of the invention.
• FIG. 1 a composite block (continuous elementary ring) obtainable according to the process of the invention (Fig. 2), as well as an example of an assembly of several composite blocks (Fig. 3) may constitute a reinforcing structure for a non-pneumatic elastic bandage ( Figure 4).
• the first three stages (arrangement, degassing and impregnation) of the process of the invention are steps known to those skilled in the art, as well as the materials (fibers and resin compositions) used; they have, for example, been described in one and / or both of the above-mentioned applications EP-A-I 074 369 and EP-A-I 174 250.
• any type of reinforcing fiber is usable as long as the latter is compatible with its crosslinkable resin matrix.
• a fiber is for example chosen from the group consisting of polyacrylic fibers, polyacrylonitrile, polyvinyl alcohol, aromatic polyamide (or “aramid”), polyamide-imide, polyimide, chlorofibers, polyester fibers, aromatic polyester, polyethylene, polypropylene, cellulose fibers, rayon, viscose, polyphenylene benzobisoxazole (or "PBO”), polyethylene naphthenate (“PEN”), glass, carbon, silica fibers, ceramic fibers, and mixtures of such fibers.
• high tenacity fibers particularly fibers selected from the group consisting of glass fibers, carbon fibers and mixtures of such fibers.
• an essential step of degassing of the fiber arrangement by the action of the vacuum must be carried out, in particular in order to reinforce the effectiveness of the impregnation and especially to guarantee the absence of bubbles at the same time. inside the final composite ring.
• Such a degassing step has been described in detail in the aforementioned EP-AI 174 250.
• the resin composition used is for example a curable resin (ie, hardenable) by ionizing radiation, such as for example an ultraviolet-visible radiation emitting preferably in the spectrum of at least 300 nm to 450 nm, a beam of accelerated electrons or X-rays. It is also possible to choose a composition comprising a resin which can be hardened with a peroxide, the subsequent crosslinking can then be carried out, when the time comes, by means of a supply of calories, for example by the action of micro -ondes.
• a composition of the ionizing radiation curable type is used, the final polymerization being able to be triggered and easily controlled by means of an ionizing treatment, for example of UV or UV-visible type.
• polyester resin As a crosslinkable resin, a polyester or vinylester resin is preferably used.
• polyester resin By “polyester” resin is meant in known manner an unsaturated polyester resin.
• Vinylester resins are well known in the field of composite materials.
• the vinylester resin is preferably of the epoxyvinylester type. It is more preferable to use a vinylester resin, in particular of the epoxide type, which is at least partly based (that is to say grafted on a structure of the type) novolac (also called phenoplast) and / or bisphenol, or preferably a vinylester resin containing novolac, bisphenolic, or novolak and bisphenol.
• a vinylester resin in particular of the epoxide type, which is at least partly based (that is to say grafted on a structure of the type) novolac (also called phenoplast) and / or bisphenol, or preferably a vinylester resin containing novolac, bisphenolic, or novolak and bisphenol.
• a novolac-based epoxyvinylester resin (part in square brackets in formula I below), for example, corresponds, in a known manner, to the following formula (I):
• a bisphenol A epoxyvinylester resin (part in square brackets of the formula (II) below) for example meets the formula (the "A” recalling that the product is manufactured using acetone):
• An epoxyvinylester resin of novolac and bisphenolic type has shown excellent results.
• Such epoxyvinylester resins are available from other manufacturers such as Reichhold, Cray Valley, UCB.
• the so-called “calibration" die makes it possible, by virtue of a cross-section of determined dimensions, generally and preferably rectangular, to adjust the proportion of resin with respect to the reinforcing fibers while imposing on the impregnated form and thickness aimed for the ribbon.
• the fiber ribbon thus formed through the calibration die then arrives continuously on a support or mandrel of suitable shape on which it is then wound directly, unidirectionally, by superposition of the predetermined number Nc of layers.
• a closed and continuous ring is thus formed whose cross section is essentially rectangular, this being achieved let us recall it before any stabilization, even partial polymerization of the resin.
• the tension stress experienced by the reinforcing fibers in the ribbon being moved is between 0.2 and 5 cN / tex. (centinewton per tex); it is therefore the voltage measured between the calibration die and the input of the support or mandrel dictating the shape of the final composite block. It was found that outside this preferred tension range, there was a risk of deformation or at least loss of regularity of shape of the tape, which could be detrimental to the quality and endurance of the final composite block. For this reason, said tension stress is more preferably between 0.5 and 2.5 cN / tex.
• the operation of winding the ribbon on said mandrel is preferably done by rotating the mandrel itself in a fixed plane and tangential to the arrival plane of the ribbon on the mandrel. turning. The winding operation is stopped once the Nc ribbon layers are wound on themselves.
• each layer of order N can be mechanically pressed at the entrance of the support or mandrel, for example by rolling with the aid of a wheel of the same width as the ribbon, so as to compact slightly together, to guarantee an excellent adhesion between the successive layers, to distribute the fibers in a homogeneous way laterally.
• the reinforcing fibers are substantially unidirectional, distributed in a manner homogeneous throughout the volume and in a matrix (ie, resin composition) which is still in the liquid state.
• the particular geometry of the ring thus formed is of course dictated by that of the support or mandrel on which the ribbon "liquid" has been wound.
• the support or mandrel for example metal, is provided with a flat-bottomed reception groove conforming to the shape of the ribbon, of suitable depth to receive and geometrically stabilize the Nc superimposed ribbon layers.
• the liquid resin is subjected to at least partial polymerization, for example using UV or a heat treatment, to stabilize, at least partially solidify said ring before separating it from its support.
• said support is advantageously constructed of two removable parts, symmetrical or not, which can be easily separated mechanically.
• the composite block thus stabilized in which the resin composition is then at least partly in the solid phase, can then be easily handled, stored as is or treated immediately in order to finish polymerizing the resin (final baking or crosslinking).
• the final firing operation can be carried out under simple atmospheric pressure, "outside the mold” (or “open mold” according to a recognized terminology), by any known means of skilled in the art.
• a simple thermal oven is used at the appropriate temperature, at atmospheric pressure or under low pressure, or a UV chamber.
• An alternative embodiment is to completely cook the composite block on its support or receiving chuck, and to extract the latter after complete cooking.
• the thickness of the final composite ring is preferably between 0.5 and 5.0 mm (millimeters), more preferably in a range of 1 to 2 mm. Its width is preferably less than 25 mm, more preferably in a range of 5 to 20 mm.
• its largest dimension is typically of the order from a few cm (centimeters) to a few tens of cm.
• Two essential characteristics of the process of the invention are, on the one hand, the maximum thickness of the strip at the outlet of the calibration die, which must be less than 0.5 mm, and secondly the maximum number of layers which are wound for formation of the composite ring, which must be less than 15. It turned out that if these two characteristics are not verified, the shape and regularity of the ribbon as those of the final composite are no longer under control, resulting in a crippling degradation of the endurance in flexion-compression of the final composite ring. Furthermore, a thickness of less than 0.05 mm (or 50 microns) may be difficult to cope with industrial constraints.
• the thickness of the strip at the outlet of the die is preferably chosen between 0.05 and 0.35 mm, more preferably between 0.10 and 0.30 mm; the number of layers Nc is in turn preferably less than 10, more preferably between 5 and 10.
• the present invention covers the cases where one or more steps other than the steps described above (fiber arrangement, degassing, impregnation, calibration, unidirectional winding on support, at least partial stabilization) are added to the process of the invention.
• the method of the invention may be implemented using a device (1) itself subject of the invention comprising at least, from upstream to downstream (with reference to FIGS. 1 and 2):
• Figure 1 attached schematically shows an example of such a device 1 (for a part in perspective to illustrate the birth of the tape 21 after passing through the calibration means 19, 20).
• the coil is unwound continuously by driving, so as to achieve a rectilinear arrangement 12 of these fibers 11.
• This arrangement 12 then passes through a vacuum chamber 13 (connected to a vacuum pump not shown), disposed between an inlet pipe 13a and an outlet pipe 13b opening to the impregnation chamber 14, the two preferably rigid walled tubings having for example a minimum upper section (typically twice as much) to the total fiber section and a much greater length (typically 50 times more) to said section minimal.
• the use of rigid wall pipes, both for the inlet in the vacuum chamber and the outlet of the vacuum chamber and the transfer from the vacuum chamber to the impregnation chamber is compatible both with high rates of passage of fibers through the orifices without breaking the fibers, but also ensures a sufficient seal. It suffices, if necessary experimentally, to search for the largest section of passage, taking into account the total section of the fibers to be treated, again making it possible to provide sufficient sealing, taking into account the speed of advance of the fibers and the length tubing.
• the vacuum inside the chamber 13 is for example of the order of 0.1 bar.
• the arrangement 12 of fibers 11 passes through an impregnation chamber 14 comprising a feed tank 15 (connected to a metering pump not shown) and an impregnation tank 16 sealed completely filled with impregnating composition 17 based on a vinylester-type curable resin (eg, "ATLAC 590" from DSM).
• the composition further comprises (at a weight ratio of 1 to 2%) a photoinitiator agent suitable for the UV and / or UV-visible radiation by which the composition will subsequently be treated, for example the bis (2,4,6-trimethylbenzoyl) phenylphosphine oxide ("Irgacure 819" from Ciba).
• the impregnating composition 17 is in the liquid state.
• an impregnated material comprising for example (% by weight) from 50 to 75% of solid fibers 11, the remainder consisting of the liquid impregnation matrix 17.
• the impregnated material then passes through calibration means 19 comprising at least one calibration die 20 whose channel (not shown here), for example of rectangular or conical shape, is adapted to the particular conditions of production.
• this channel has a minimum rectangular cross-section whose downstream orifice has dimensions (for example 5.3 mm by 0.25 mm or 10.6 mm by 0.25 mm) slightly greater than the target ribbon.
• the die has a length that is typically greater than at least 100 times the minimum dimension of the minimum section. Its function is to ensure a high dimensional accuracy to the finished product, it can also play a role of dosing the fiber ratio with respect to the resin.
• the die 20 can be directly integrated into the impregnation chamber 14, which avoids, for example, the use of the outlet pipe 18. Thanks to the calibration means (19, 20) is obtained at this stage a "liquid" composite tape 21 (liquid in the sense that its impregnating resin is always liquid) whose shape of the cross section is essentially rectangular (for example 5 mm by 0.2 mm or 10 mm by 0.2 mm, respectively).
• the rotating mandrel 23 is preferably provided with a receiving groove 24 matching the shape and width of the ribbon 21 and thus facilitating the winding of the ribbon on itself in its different layers Nc superimposed.
• the "liquid" composite block thus obtained is partially polymerized by means of the polymerization means 25 disposed facing the mandrel 23 (for example a few seconds under UV radiation), directly on said mandrel, before extracting the latter mechanically (separation into two parts ).
• the ribbon thus stabilized can be handled easily, for example it is treated for 5 min in a UV oven ("UVAprint” lamp from the company Dr. Honle, wavelength 200 to 600 nm) before final baking in a simple oven by example under atmospheric pressure and high temperature (for example at 230 ° C. for 5 to 6 min) if a high value of Tg (glass transition temperature) is desired on the final composite.
• UVAprint lamp from the company Dr. Honle, wavelength 200 to 600 nm
• Tg glass transition temperature
• the entire cooking operation could be performed under UV radiation, entirely or not on the receiving mandrel.
• a composite block is obtained in the form of a closed continuous ring whose reinforcing fibers are distributed homogeneously throughout the volume.
• this composite ring is new in that it has a true monolithic structure; by this is meant a homogeneous structure, that is to say in which no stratum (or elementary layer of ribbon) is visible in cross-section, particularly if said section is observed under optical microscope, nor can it be revealed to use. It is endowed with excellent mechanical properties, with in particular a very high endurance in bending and in shear, at least as good as, if not greater than that observed on these composite rings of the prior art requiring a very high pressure during their final cooking.
• Such an example of composite block 30 has been reproduced schematically in Figure 2 attached, it was obtained by winding on a convex mandrel of elliptical shape. It consists of a continuous closed flat ring whose rectangular cross section has dimensions of 10 mm by 1.4 mm. As seen in Figure 2, the shape or geometry of the ring is substantially elliptical with internal longitudinal dimensions (denoted A in Figure 2) of the order of 15 cm and transverse (denoted B in FIG. 2) of the order of 6 cm.
• the invention thus offers the possibility of manufacturing a composite block in very small sections that can have many industrial applications, whether used individually or associated with other composite blocks for forming more complex structures.
• Such structures may serve in particular reinforcing reinforcement to any system of ground connection of motor vehicles, such as non-pneumatic tire, tire, internal safety support for tire, wheel, other suspension element and anti-vibration.
• the latter can be advantageously nested within each other , then stapled mechanically or "chemically” thanks for example to the use of a filling polymer for filling all the interstices present between the elementary rings.
• This filling polymer must of course be compatible with the resin of the composite ring and capable of good adhesion with the latter, if necessary by means of an appropriate adhesive composition as described for example in the application WO 2004/058909 (or US2006 / 0047050).
• This polymer is for example a diene elastomer or a polyurethane.
• the reinforcement 40 may comprise mechanical connection means 42 (for example a staple) intended to ensure the subsequent connection to the rigid part of a wheel as explained below.
• This composite reinforcing reinforcement may form a radial reinforcing arch of a non-pneumatic tire carcass as described, for example, in patents or patent applications WO 00/37269 (or US Pat. No. 6,640,859) and EP 1,359. 028 (or US-B2-6,994,135).
• FIG. 4 shows a partial perspective of such a non-pneumatic flexible tire 50.
• a tire when it is associated with any other rigid mechanical element intended to ensure the connection between the flexible tire and the hub, replaces the assembly. constituted by the tire and the wheel as known on most current road vehicles.
• the bandage profile delimits a toroidal internal cavity of ovoid section.
• the tire 50 comprises an attachment zone 51 (comprising the connecting means 42 illustrated in FIG. 3), two sidewalls 52 and a tread 53.
• the attachment zone is intended to be rigidly connected to a wheel hub by the intermediate of a mechanical element such as a wheel disk or wheel (not shown here).
• the tread 53 has several circumferential ribs, but this aspect of course has no limiting character.
• the flanks 52 are rounded and occupy most of the radial height of the tire 50.
• the supporting structure comprises a plurality of support members constituted by the composite reinforcing plates 40 illustrated in Figure 3 above.
• the support members 40 are circumferentially adjacent and each extends substantially radially outwardly from the attachment zone 51.
• FIG. 4 also shows a principle of this type of non-pneumatic tire according to which it is the flexion of the support elements that can carry the load.
• the tire comprises one hundred support elements 40. This number may of course be very different depending, for example, on the type of vehicle and the type of use for which it is intended and the characteristics of the support elements. .
• the number of elements may thus vary, for example, from 30 to 300.
• an interconnection structure disposed radially under the tread 53 which is relatively rigid in longitudinal traction-compression, connects circumferentially all of the support elements 40. .
• Such a non-pneumatic tire is likely to equip any type of motor vehicle, for example of tourism type, two wheels (including motorcycles, scooters), aircraft, such as industrial vehicles chosen from vans, "heavy-weight" - it that is, metros, buses, road transport vehicles (trucks, tractors, trailers), off-road vehicles such as agricultural or civil engineering vehicles, other transport or handling vehicles.
• motor vehicle for example of tourism type, two wheels (including motorcycles, scooters), aircraft, such as industrial vehicles chosen from vans, "heavy-weight" - it that is, metros, buses, road transport vehicles (trucks, tractors, trailers), off-road vehicles such as agricultural or civil engineering vehicles, other transport or handling vehicles.

Landscapes

• Engineering & Computer Science (AREA)
• Mechanical Engineering (AREA)
• Chemical & Material Sciences (AREA)
• Composite Materials (AREA)
• Reinforced Plastic Materials (AREA)
• Moulding By Coating Moulds (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=36607387

Family Applications (1)

Country Status (6)

Cited By (15)

Families Citing this family (12)

Citations (8)

Family Cites Families (10)

• 2007
  • 2007-01-23 AT AT07702951T patent/ATE552957T1/de active
  • 2007-01-23 WO PCT/EP2007/000541 patent/WO2007085414A1/fr not_active Ceased
  • 2007-01-23 CN CN2007800028132A patent/CN101370644B/zh not_active Expired - Fee Related
  • 2007-01-23 EP EP07702951A patent/EP1981700B1/fr not_active Not-in-force
  • 2007-01-23 JP JP2008551713A patent/JP2009524536A/ja not_active Ceased
  • 2007-01-23 US US12/223,341 patent/US8585947B2/en active Active

Patent Citations (8)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events