WO2007070934A1 - Composition explosive - Google Patents

Composition explosive Download PDF

Info

Publication number
WO2007070934A1
WO2007070934A1 PCT/AU2006/001923 AU2006001923W WO2007070934A1 WO 2007070934 A1 WO2007070934 A1 WO 2007070934A1 AU 2006001923 W AU2006001923 W AU 2006001923W WO 2007070934 A1 WO2007070934 A1 WO 2007070934A1
Authority
WO
WIPO (PCT)
Prior art keywords
particles
composition
energetic material
shock
liquid oxidant
Prior art date
Application number
PCT/AU2006/001923
Other languages
English (en)
Inventor
Vladamir Sujansky
Original Assignee
Orica Explosives Technology Pty Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from AU2005907351A external-priority patent/AU2005907351A0/en
Application filed by Orica Explosives Technology Pty Ltd filed Critical Orica Explosives Technology Pty Ltd
Publication of WO2007070934A1 publication Critical patent/WO2007070934A1/fr

Abstract

L’invention concerne une composition explosive comprenant : un oxydant liquide ; un combustible comprenant des particules d'un matériau énergétique distribuées de manière homogène dans l'oxydant liquide, ledit matériau énergétique étant capable de réagir avec l'oxydant liquide à une température élevée pour libérer de l’énergie et lesdites particules de matériau énergétique comprenant des particules sensibles aux chocs pour lesquelles la réaction entre le matériau énergétique et l’oxydant liquide peut être amorcée par un choc et des particules d’amorce secondaire pour lesquelles la réaction entre le matériau énergétique et l’oxydant liquide peut être amorcée par l’énergie libérée par la réaction des particules sensibles aux chocs et de l’oxydant liquide.
PCT/AU2006/001923 2005-12-22 2006-12-18 Composition explosive WO2007070934A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
AU2005907351A AU2005907351A0 (en) 2005-12-22 Explosive Composition
AU2005907351 2005-12-22

Publications (1)

Publication Number Publication Date
WO2007070934A1 true WO2007070934A1 (fr) 2007-06-28

Family

ID=38188144

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/AU2006/001923 WO2007070934A1 (fr) 2005-12-22 2006-12-18 Composition explosive

Country Status (1)

Country Link
WO (1) WO2007070934A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114410147A (zh) * 2021-12-26 2022-04-29 南京理工大学 一种纳米铝热剂含能油墨的制备方法

Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1043534A (en) * 1961-10-27 1966-09-21 Secr Aviation Improvements in or relating to gas-producing compositions
GB1384870A (en) * 1964-01-15 1975-02-26 Atlantic Res Corp Propellant compositions
AU7371074A (en) * 1974-09-25 1976-04-01 Ici Australia Ltd Explosive composition
US3956039A (en) * 1956-01-13 1976-05-11 The United States Of America As Represented By The United States Energy Research And Development Administration High explosive compound
US4183775A (en) * 1977-10-14 1980-01-15 Aeci Limited Explosive containing polyvinyl chloride and aluminum as sensitizer
US4330346A (en) * 1979-06-01 1982-05-18 Dyno Industrier A.S. Cap-sensitive powdered explosive composition
US5034073A (en) * 1990-10-09 1991-07-23 Aerojet General Corporation Insensitive high explosive
US5074938A (en) * 1990-05-25 1991-12-24 Thiokol Corporation Low pressure exponent propellants containing boron
US20030051786A1 (en) * 2000-10-26 2003-03-20 Verity Dennis Gordon Metal and metal oxide granules and forming process
WO2004023062A1 (fr) * 2002-09-05 2004-03-18 Baker Hughes Incorporated Explosif a charge creuse desensibilisee
US6846372B1 (en) * 2003-03-31 2005-01-25 The United States Of America As Represented By The Secretary Of The Navy Reactively induced fragmentating explosives
FR2868774A1 (fr) * 2004-04-07 2005-10-14 Giat Ind Sa Composition explosive

Patent Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3956039A (en) * 1956-01-13 1976-05-11 The United States Of America As Represented By The United States Energy Research And Development Administration High explosive compound
GB1043534A (en) * 1961-10-27 1966-09-21 Secr Aviation Improvements in or relating to gas-producing compositions
GB1384870A (en) * 1964-01-15 1975-02-26 Atlantic Res Corp Propellant compositions
AU7371074A (en) * 1974-09-25 1976-04-01 Ici Australia Ltd Explosive composition
US4183775A (en) * 1977-10-14 1980-01-15 Aeci Limited Explosive containing polyvinyl chloride and aluminum as sensitizer
US4330346A (en) * 1979-06-01 1982-05-18 Dyno Industrier A.S. Cap-sensitive powdered explosive composition
US5074938A (en) * 1990-05-25 1991-12-24 Thiokol Corporation Low pressure exponent propellants containing boron
US5034073A (en) * 1990-10-09 1991-07-23 Aerojet General Corporation Insensitive high explosive
US20030051786A1 (en) * 2000-10-26 2003-03-20 Verity Dennis Gordon Metal and metal oxide granules and forming process
WO2004023062A1 (fr) * 2002-09-05 2004-03-18 Baker Hughes Incorporated Explosif a charge creuse desensibilisee
US6846372B1 (en) * 2003-03-31 2005-01-25 The United States Of America As Represented By The Secretary Of The Navy Reactively induced fragmentating explosives
FR2868774A1 (fr) * 2004-04-07 2005-10-14 Giat Ind Sa Composition explosive

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114410147A (zh) * 2021-12-26 2022-04-29 南京理工大学 一种纳米铝热剂含能油墨的制备方法

Similar Documents

Publication Publication Date Title
US3770522A (en) Emulsion type explosive composition containing ammonium stearate or alkali metal stearate
JP2942266B2 (ja) 有機微小球体を含有するエマルジョン爆薬
AU2012286593B2 (en) Improved explosive composition
CA2965705C (fr) Composition explosive pour sol mou et humide et procede de mise en place
US3249474A (en) Explosive composition containing inorganic salts and coated metal
EP3551597A1 (fr) Composition explosive améliorée
JP2942265B2 (ja) フェノール系乳化剤誘導体を含有するエマルジョン爆薬
CA2024611C (fr) Composition explosive sensible au detonateur contenant de 20 a 40% de particules de nitrate d'ammonium solide
US3297502A (en) Explosive composition containing coated metallic fuel
EP0648199A1 (fr) Utilisation avantageuse de rebuts contenant de l'energie
US4780156A (en) Water resistant sensitizing additive for ammonium nitrate blasting agents
WO2007070934A1 (fr) Composition explosive
KR20080083920A (ko) 유중수적형 에멀젼폭약
CA1110852A (fr) Compositions explosives en bouillie
KR101060523B1 (ko) 친환경적인 고위력 유중수적형 에멀젼 폭약 조성물
JP3984383B2 (ja) 油中水滴型エマルション爆薬組成物の製造方法
WO2002090296A2 (fr) Explosif a particules a ecoulement libre
JP3874739B2 (ja) 粒子性添加物を含む高エネルギー爆薬
US3444014A (en) Gelled aqueous nitric acid composition and method of making same
CA1101675A (fr) Traduction non-disponible
CA3217755A1 (fr) Composition de formation d'un explosif a emulsion a base de peroxyde d'hydrogene
CA3217786A1 (fr) Composition sensibilisante pour emulsions de peroxyde d'hydrogene energetiques
CA3217779A1 (fr) Composition de formation d'un explosif comprenant une emulsion de peroxyde d'hydrogene et un carburant de type huile
JP2001172096A (ja) 固形エマルション爆薬組成物及びその製造方法
JP2003201193A (ja) 爆薬組成物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 06828030

Country of ref document: EP

Kind code of ref document: A1