WO2006083206A1 - Iron-based powder combination - Google Patents
Iron-based powder combination Download PDFInfo
- Publication number
- WO2006083206A1 WO2006083206A1 PCT/SE2006/000080 SE2006000080W WO2006083206A1 WO 2006083206 A1 WO2006083206 A1 WO 2006083206A1 SE 2006000080 W SE2006000080 W SE 2006000080W WO 2006083206 A1 WO2006083206 A1 WO 2006083206A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- powder
- iron
- weight
- alloyed
- molybdenum
- Prior art date
Abstract
Description
Claims