WO2006017074A2 - Low-doped semi-insulating sic crystals and method - Google Patents
Low-doped semi-insulating sic crystals and method Download PDFInfo
- Publication number
- WO2006017074A2 WO2006017074A2 PCT/US2005/023796 US2005023796W WO2006017074A2 WO 2006017074 A2 WO2006017074 A2 WO 2006017074A2 US 2005023796 W US2005023796 W US 2005023796W WO 2006017074 A2 WO2006017074 A2 WO 2006017074A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- deep level
- concentration
- crystal
- matter
- shallow
- Prior art date
Abstract
Description
Claims