WO2006013809A1 - 吸水性不織布及び貼付材 - Google Patents

吸水性不織布及び貼付材 Download PDF

Info

Publication number
WO2006013809A1
WO2006013809A1 PCT/JP2005/014017 JP2005014017W WO2006013809A1 WO 2006013809 A1 WO2006013809 A1 WO 2006013809A1 JP 2005014017 W JP2005014017 W JP 2005014017W WO 2006013809 A1 WO2006013809 A1 WO 2006013809A1
Authority
WO
WIPO (PCT)
Prior art keywords
nonwoven fabric
water
skin
fiber nonwoven
fiber
Prior art date
Application number
PCT/JP2005/014017
Other languages
English (en)
French (fr)
Inventor
Atsunori Maeda
Original Assignee
Toyo Boseki Kabushiki Kaisha
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toyo Boseki Kabushiki Kaisha filed Critical Toyo Boseki Kabushiki Kaisha
Publication of WO2006013809A1 publication Critical patent/WO2006013809A1/ja

Description

明 細 書
吸水性不織布及び貼付材
技術分野
[0001] 本発明は、吸水性に優れた不織布及び貼付材に関する。更に詳しくは、水膨潤時 に、人体に対する密着性に優れ、かつ人体に与える物理的刺激が少なぐ人体に接 する用途に用 、て好適な吸水性不織布及び貼付材に関する。
背景技術
[0002] 従来より、吸水性繊維は、止水材、建材等の他、衛材、貼付材等、多くの分野に展 開されている。このような用途の中で、衛材、貼付材等の人体に用いる用途において は、特に吸水性繊維の特性を利用して、汗等による蒸れを防止するため用いる (例え ば特許文献 1参照）、あるいは吸血材として用いることが知られて 、る（例えば特許文 献 2参照)。これらの衛材、貼付材は、人体力 流出する体液を吸収するために吸水 性繊維を利用しており、肌へ水分、薬効成分を供給するものではないため、粘着層 やメッシュシートを介して人体に用いるのが一般的である。そのため、吸水性繊維が 肌へ及ぼす刺激や、肌への密着性について特に問題となることはな力つた。
特許文献 1：特開平 6 - 207358号公報
特許文献 2：特開 2001— 120588号公報
[0003] 一方、吸水性繊維に水分は薬効成分を含ませて肌に接触させ、積極的に肌に有 効成分を供給するものとして、吸水性繊維と低温収縮性繊維とを含む不織布を用い た湿布材が開示されている（例えば特許文献 3参照)。カゝかる湿布材は粘着剤を必要 とせず、皮膚かぶれを防止し、効果的に有効成分を肌に供給するものである。しかし ながら、水分を含んだ吸水性繊維からなる短繊維不織布を直接肌に密着させるとす ると、繊維端が肌を刺激し、強い不快感を与え、更には肌を傷つけ、敏感な箇所での 使用に問題が生じる。更に膨潤した吸水性不織布は肌への密着性が悪ぐ凹凸が大 き 、箇所や動きが激 、箇所に用いた場合、部分的に肌から剥離しやす!、と 、う問 題を有する。また、水分を含んだ吸水性繊維は、肌に密着し易いことから、不織布を 肌力 剥がした場合、多くの繊維片が不織布力 脱離し、肌に残るということも問題と なる。
特許文献 3：特開平 7— 32640号公報
発明の開示
発明が解決しょうとする課題
[0004] 本発明は、水分や薬効成分を含ませて直接肌に接触させても、肌への刺激が小さ ぐかつ人体への密着性に優れ、更には破断し難い吸水性短繊維不織布を提供す ることを目的とする。
課題を解決するための手段
[0005] 本発明は、力かる問題を解決するために以下の手段を採用するものである。
すなわち、（1) (A)繊度が 0. 5〜2. 7dtexである接着性繊維を 5%〜60%と、吸水 率 200%〜30000%の吸水性繊維を 40%〜95%含むことを特徴とする短繊維不 織布（2) (B)目付が 5〜： LOOgZm2であることを特徴とする (A)記載
の短繊維不織布， (3) (C)熱ローラーで表面を加熱処理することを特徴とする (A)〜 (C)何れか〖こ記載の短繊維不織布、（4) (D)人体に接触する部材に用いることを特 徴とする (A)〜（D)記載の短繊維不織布、 (5) (A)〜（D)記載の短繊維不織布を用 V、ることを特徴とする貼付材である。
発明の効果
[0006] 本発明による吸水性短繊維不織布は、水分を含んだ状態で肌への刺激力 、さぐ かつ人体への密着性に優れるため、敏感な箇所、凹凸が大きい箇所、動きが激しい 箇所でも粘着剤等を用いずに肌に接触させることができ、水分 ·薬効成分を直接か つ有効に肌に供給することができ、更には使用後きれいに短繊維不織布を肌から剥 がせるという効果を有する。
発明を実施するための最良の形態
[0007] 以下に本発明を詳細に説明する。
本発明に用いる接着性繊維は、 0. 5〜2. 7dtexであることが好ましい。 2. 7dtex 以上であれば、繊維端が肌を強く刺激して使用者に不快感を与え、更には肌を傷つ ける場合もある力 である。一方、 0. 5dtex未満であれば貼付材として使用し、動い た場合等に部分的に繊維が破断し、肌力 剥がした時に、不織布片ゃ繊維片が肌 に残る等の不具合を生じるからである。更に好ましくは 0. 8〜2. 5dtex、最も好ましく は 1. 0〜2. Odtexである。
[0008] また本発明に用いる吸水性繊維は、吸水率 200%以上であることが好ま 、。この ような範囲であれば、水分や薬効成分を十分に含有させることができ、また肌への密 着性を長時間保持することができるからである。特に好ましくは 1000%以上、更に好 ましくは 10000%以上である。
[0009] なお本発明でいう薬効成分は、肩こりや捻挫を治癒する等の健康の回復作用を有 するものの他、肌を健やかに保つこと等、美容に用いるものも含むものである。
[0010] 本願発明に用いる吸水性繊維は、上述の繊度及び吸水率を満たせば特に限定さ れるものではないが、吸水性繊維としては COOX(X:アルカリ金属または NH )基を
4 有するアクリロニトリル系繊維が特に好ましい。かかる繊維は、 pHを弱酸性に保つ機 能があり、肌を健やかに保つ機能を繊維自身が有するからである。
[0011] 本発明にカゝかる吸水性短繊維不織布は、吸水性繊維を 40重量％〜95重量％含 むことが好ましい。 40重量％未満であれば、水分、薬効成分を十分に保持すること ができず、更には肌への密着性が不十分となり、剥離しやすくなるからである。また 9 5重量％以上であれば、不織布の強度を保持することが困難になり、使用時に動い た場合に不織布が破断し、剥離時に不織布片が肌に残る等の不具合が生じるから である。
更に好ま 、吸水性繊維の含有量は 60重量％〜80重量％であり、最も好ましくは 65重量％〜75重量％である。
[0012] 本発明に力かる吸水性短繊維不織布は、水分を含有させる前の目付が 5〜： LOOg Zm2であることが好ましい。目付が 5gZm2未満であれば、水分'薬効成分を十分に 保持することができない。また目付が lOOgZm2以上とすると肌への密着性が低下し 、凹凸の大きな箇所や動きが激しい箇所に用いることが困難となるからである。更に 好ましい目付は 10〜50gZm2、最も好ましくは 15〜35gZm2である。
[0013] 本願発明にカゝかる吸水性短繊維不織布は、接着性繊維を含むことが好ま ヽ。吸 水性繊維カゝらなる短繊維不織布は膨潤すると破断し易くなり、ニードルパンチ法等に よる繊維交絡によると、使用した状態で運動等すると破断して不織布'繊維が破片と なって肌に付着し、除去することが困難となる等の不具合が生じるからである。特に 肌への密着性を向上させるために目付を下げる場合に、接着性繊維を含有させる必 要性が高くなる。接着性繊維の含有量は好ましくは 5〜60重量％、更に好ましくは 1 0〜50重量％、最も好ましくは 25〜35重量％である。 5重量％未満であれば十分な 効果が発揮できず、吸水時の破断が生じ易くなり、他方 60重量％以上であれば短繊 維不織布の十分な吸水性を確保できないからである。
[0014] 本発明に用いる接着性繊維は、 PETZPP、 PPZPE、 PET/PE, PET/PET, PEZPE、 PPZPP等の複合繊維 (シースコア構造等）を有する繊維であってもよ ヽ。 特にポリオレフイン系繊維は柔軟性が高ぐ繊維端が肌に与える刺激力 S小さく好まし い。
[0015] 更に本発明は、熱ローラーで少なくとも片面を加熱処理することが好ましい。かかる 処理により効果的に強度を向上し、水分を含んだ吸水性単繊維不織布を肌に接触さ せて剥がした後に繊維片が肌に残ることを防止することができ、また毛羽立ちを抑制 し、肌への刺激を低減できるからである。
[0016] 熱ローラーのエンボスパターンや条件等は特に限定するものではないが、エンボス 面積率が 20%〜100%であることが好まし!/、。エンボス面積が 20%未満であれば、 肌にのこる繊維片が多くなる力もである。更に好ましくは 50%以上、最も好ましくは 1 00% (フラットローラー）である。
[0017] また、熱ローラーでの加熱条件は、接着性繊維 (低融点成分)の融点より 10°C〜20 °C高い温度で、線圧 10〜150kg/2. 5mでカ卩ェすることが推奨される。線圧が 10k g/2. 5m未満であれば、水を含んだ短繊維不織布は使用時に運動等して外的作 用が加わると、分解し易くなつてバラける、あるいは繊維片が肌に付着する、という不 具合が生じるからである。また、通常の短繊維不織布は、線圧が高すぎると、風合い が硬くなる、ペーパーライクになる等の不具合が生じる力 吸水性繊維を含む短繊維 不織布は、膨潤させた状態での線圧が風合いに与える影響は小さぐ特に上限は問 題とならないが、 150kgZ2. 5mを超えると繊維にダメージを与えるため好ましくない 。特【こ好まし ヽ範囲 ίま、 20〜140kg/2. 5m、更【こ好ましく ίま 30〜120kg/2. 5m 、最も好ましくは 40〜： L00kgZ2. 5mである。
[0018] 本願発明にかかる短繊維不織布は、人体に接触する用途に用いて特に効果を発 揮するものであり、貼付材、湿布材、美容材等に用いることができる。
実施例
[0019] 以下に本発明を実施例及び比較例を用いて、本発明を具体的に説明する。なお、 評価は以下の方法により測定した値を採用した。
[0020] (吸水率）
(吸水率） 300mlビーカーに試料 0. 4〜0. 42g (W2)を精秤し、これに純水 300ml を入れ、 30分後、試料をナイロン濾布（200メッシュ）に包み、遠心脱水機（160G X 5分、但し Gは重力加速度。 )により繊維間の水を除去する。この方法で調整した試料 の重量を測定する (Wig)。以上の測定結果から、次式によって算出する。
吸水率（％) = ( (Wl -W2) /W2) X 100
(皮膚への刺激性）
女性モニター 5名を選出し、サンプル 15cm X 15cmに化粧水を十分に膨潤させて、 腰部に装着し、 1時間放置した。その間の刺激性につき以下の基準でアンケートをと り、 5名の平均点を評価した。
0点:使用に耐えないほど、不快である
3点:健康や肌に有効であれば使用する意欲はある力 不快感はある
5点：湿布しても不快感はな!/、。
(密着性）
女性モニター 5名を選出し、サンプル 15cm X 15cmに化粧水を十分に膨潤させて、 腰部に装着し、 1時間放置した後の密着性につき以下の基準で目視評価し、 5名の 平均点を評価した。
0点:使用中の運動等により、サンプルが剥離した。
3点：サンプルの完全な剥離は生じな力つたが、部分的に肌に密着して!/、な 、箇所 が見られた。
5点：サンプルの剥離は見られな力つた。
(不織布破断） 女性モニター 5名を選出し、サンプル 15cm X 15cmに化粧水を十分に膨潤させて、 腰部に装着し、 1時間放置した後、サンプルを剥がして肌の上に残った不織布片 (ゲ ル状物）を観察し、以下の基準で評価した。
0点：サンプル湿布箇所全面に、不織布片が残留して!/ヽた。
3点：サンプル不織布片の残留が目立った。
5点：サンプル不織布片は見当たらな力つた。
[0021] (実施例 1)
2. 9dtex X 38mmの吸水性繊維 (東洋紡社製：製品名ランシール）を 70重量部、 1 . 7dtexX 5 lmmのポリオレフイン系熱溶融接着性繊維 (チッソ株式会社製、製品名 ESCスフ） 30重量部を混綿、カーデングし、 20gZm2のウェブシートを形成し、 150 °Cに加熱されたステンレス製フラットローラー 2本の間を線圧 50kg/2. 5mで通して 、不織布シートを得た。評価結果を表 1に示す。
[0022] (実施例 2)
2. 9dtex X 38mmの吸水性繊維 (東洋紡社製：製品名ランシール）を 65重量部、 1 . ldtex X 5 lmmのポリオレフイン系熱溶融接着性繊維 (チッソ株式会社製:製品名 ESCスフ） 35重量部を混綿、カーデングし、 20gZm2のウェブシートを形成し、 150 °Cに加熱されたステンレス製フラットローラー 2本の間を線圧 50kg/2. 5mで通して 、不織布シートを得た。評価結果を表 1に示す。
[0023] (実施例 3)
2. 9dtex X 38mmの吸水性繊維 (東洋紡社製：製品名ランシール）を 70重量部、 1 . 7dtexX 5 lmmのポリオレフイン系熱溶融接着性繊維 (チッソ株式会社製、製品名 ESCスフ） 30重量部を混綿、カーデングし、 30gZm2のウェブシートを形成し、 150 °Cに加熱されたステンレス製フラットローラー 2本の間を線圧 50kg/2. 5mで通して 、不織布シートを得た。評価結果を表 1に示す。
[0024] (比較例 1)
2. 9dtex X 38mmの吸水性繊維 (東洋紡社製：製品名ランシール）を 30重量部、 3 . 3dtexX 5 lmmのポリオレフイン系熱溶融接着性繊維 (チッソ株式会社製、製品名 ESCスフ） 70重量部を混綿、カーデングし、 20gZm2のウェブシートを形 成し、 150°Cに加熱されたステンレス製フラットローラー 2本の間を線圧 50kg/2. 5 mで通して、不織布シートを得た。評価結果を表 1に示す。
[0025] (比較例 2)
2. 9dtex X 38mmの吸水性繊維 (東洋紡社製：製品名ランシール）を 100重量部を カーデングし、 20gZm2のウェブシートを形成し、 150°Cに加熱されたステン レス製フラットローラー 2本の間を線圧 50kg/2. 5mで通して、不織布シートを得た。 評価結果を表 1に示す。
[0026] (比較例 3)
2. 9dtex X 38mmの吸水性繊維 (東洋紡社製：製品名ランシール）を 70重量部 、 1. 7dtex X 5 lmmのポリオレフイン系熱溶融接着性繊維 (チッソ株式会社製、製品 名 ESCスフ） 30重量部を混綿、カーデングし、 120gZm2のウェブシートを形成し、 1 50°Cに加熱されたステンレス製フラットローラー 2本の間を線圧 50kgZ2. 5mで通し て、不織布シートを得た。評価結果を表 1に示す。
[表 1]
実讓 1 実脑 2 実施例 3 比較例 1 比翻 2 比棚 3 繊度 (dtex) 2.9 2.9 2.9 2.9 2.9 2.9 吸水性繊維 吸水率 % 15000 15000 15000 15000 15000 15000
含有量 重量％ 70 65 70 100 30 70 繊度 (dtex) 1.7 1 1.7 ― 3.3 1.7 含有量 重量％ 30 35 30 0 70 30 表難讓 i温度 (°c) 一 150 150 150 150 150 150 目付 g/m 20 20 30 20 20 120 趙繊 - 5 5 5 5 0 5 評価 密着'生 - 5 5 5 5 0 0
不織布断 - 5 5 5 0 5 5
7] 本願発明にかかる吸水性短繊維不織布 （実施例 1〜2 ) は、 皮膚刺激性が小さく、 か つ密着性に優れ、 更には短繊維片が肌に残留し難い、 吸水性繊維であった。 他方、 本発明の範囲外の吸水性短繊維不織布は、 皮膚刺激性が大きい、 密着性が悪い、 あるいは短繊維片が肌に残留する等の不具合が生じ、 実用には困難なものであつた。 産業上の利用可能性
差替え用紙 （規則 26) 本発明は、水分や薬効成分を含ませて直接肌に接触させても、肌への刺激が小さ ぐかつ人体への密着性に優れ、更には不織布が破断分離することがなく使用するこ とができるため、関節、足の裏、顔等人体の場所を選ばず貼付材、湿布材、美容材 等に用いることができ、産業界に寄与すること大である。

Claims

請求の範囲
[1] 繊度が 0. 5〜2. 7dtexである接着性繊維を 5%〜60%と、吸水率 200%〜30000
%の吸水性繊維を 40%〜95%含むことを特徴とする短繊維不織布。
[2] 目付が 5〜： LOOgZm2であることを特徴とする請求項 1記載の短繊維不織布。
[3] 熱ローラーで表面を加熱処理することを特徴とする請求項 1〜3記載の短繊維不織 布。
[4] 人体に接触する部材に用いることを特徴とする請求項 1〜4記載の短繊維不織布。
[5] 請求項 1〜4記載の短繊維不織布を用いることを特徴とする貼付材。
PCT/JP2005/014017 2004-08-06 2005-08-01 吸水性不織布及び貼付材 WO2006013809A1 (ja)