WO2006008385A1 - Procede de fabrication selective de nanotubes de carbone ordonne - Google Patents
Procede de fabrication selective de nanotubes de carbone ordonne Download PDFInfo
- Publication number
- WO2006008385A1 WO2006008385A1 PCT/FR2005/001542 FR2005001542W WO2006008385A1 WO 2006008385 A1 WO2006008385 A1 WO 2006008385A1 FR 2005001542 W FR2005001542 W FR 2005001542W WO 2006008385 A1 WO2006008385 A1 WO 2006008385A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- ferrous metal
- metal deposition
- grains
- microns
- Prior art date
Abstract
Description
Claims