WO2005065177A2 - Process for preparing bitumen compositions with reduced hydrogen sulfide emission - Google Patents
Process for preparing bitumen compositions with reduced hydrogen sulfide emission Download PDFInfo
- Publication number
- WO2005065177A2 WO2005065177A2 PCT/US2004/042005 US2004042005W WO2005065177A2 WO 2005065177 A2 WO2005065177 A2 WO 2005065177A2 US 2004042005 W US2004042005 W US 2004042005W WO 2005065177 A2 WO2005065177 A2 WO 2005065177A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- asphalt
- inorganic
- scavenger
- metal salt
- mixtures
- Prior art date
Abstract
Description
Claims