Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/86—Inert electrodes with catalytic activity, e.g. for fuel cells
  • H01M4/8605—Porous electrodes
  • H01M4/8626—Porous electrodes characterised by the form
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0202—Collectors; Separators, e.g. bipolar separators; Interconnectors
  • H01M8/023—Porous and characterised by the material
  • H01M8/0236—Glass; Ceramics; Cermets
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0202—Collectors; Separators, e.g. bipolar separators; Interconnectors
  • H01M8/023—Porous and characterised by the material
  • H01M8/0239—Organic resins; Organic polymers
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0202—Collectors; Separators, e.g. bipolar separators; Interconnectors
  • H01M8/023—Porous and characterised by the material
  • H01M8/0241—Composites
  • H01M8/0243—Composites in the form of mixtures
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/02—Details
  • H01M8/0271—Sealing or supporting means around electrodes, matrices or membranes
  • H01M8/0273—Sealing or supporting means around electrodes, matrices or membranes with sealing or supporting means in the form of a frame
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/10—Fuel cells with solid electrolytes
  • H01M8/1004—Fuel cells with solid electrolytes characterised by membrane-electrode assemblies [MEA]
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/10—Fuel cells with solid electrolytes
  • H01M8/1097—Fuel cells applied on a support, e.g. miniature fuel cells deposited on silica supports
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/2404—Processes or apparatus for grouping fuel cells
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/241—Grouping of fuel cells, e.g. stacking of fuel cells with solid or matrix-supported electrolytes
  • H01M8/2418—Grouping by arranging unit cells in a plane
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M8/00—Fuel cells; Manufacture thereof
  • H01M8/24—Grouping of fuel cells, e.g. stacking of fuel cells
  • H01M8/241—Grouping of fuel cells, e.g. stacking of fuel cells with solid or matrix-supported electrolytes
  • H01M8/242—Grouping of fuel cells, e.g. stacking of fuel cells with solid or matrix-supported electrolytes comprising framed electrodes or intermediary frame-like gaskets
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
  • Y02E60/30—Hydrogen technology
  • Y02E60/50—Fuel cells
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
  • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
  • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T29/00—Metal working
  • Y10T29/49—Method of mechanical manufacture
  • Y10T29/49002—Electrical device making
  • Y10T29/49108—Electric battery cell making
  • Y10T29/4911—Electric battery cell making including sealing

Definitions

• Electrochemical cells generally include an anode and a cathode separated by an electrolyte.
• a well-known use of electrochemical cells is in a fuel cell (a cell that converts fuel and oxidants to electrical energy) that uses a proton exchange membrane (hereafter "PEM”) as the electrolyte, for example direct methanol fuel cells.
• PEM proton exchange membrane
• a reactant or reducing fluid such as methanol is supplied to the anode, and an oxidant such as oxygen is supplied to the cathode.
• the methanol electrochemically reacts at a surface of the anode to produce hydrogen ions and electrons.
• the electrons are conducted to an external load circuit and then returned to the cathode, while hydrogen ions transfer through the electrolyte to the cathode, where they react with the oxidant and electrons to produce water and release thermal energy.
• the membrane electrode assembly (MEA).
• MEA membrane electrode assembly
• the process of making an MEA is well established, such that individual MEA's are produced manually or by automated processes. In the manual processes, each gas diffusion electrode and/or gas diffusion layer is individually applied for each element of the array.
• the disadvantage of such processes include, inter alia, a great degree of difficulty in aligning the elements by hand, which makes the process very time consuming and very expensive to implement.
• the invention provides a process of forming at least one framed membrane electrode sub-assembly comprising: a.) at least one framed membrane electrode assembly component comprising an external frame having a plurality of bridges, and at least one element having a plurality of outer edges, wherein the at least one element is connected to the external frame via the plurality of bridges, thereby forming a unitary structure; b.) a carrier material having a plurality of apertures defined by a plurality of inner edges; c.) securing the carrier material to the at least one framed membrane electrode assembly component, wherein the external frame, and plurality of outer edges of the at least one element are supported by the carrier material, thereby forming at least one framed membrane electrode sub-assembly.
• the framed MEA component may be selected from the group consisting of a gas diffusion layer (GDL), a gas diffusion electrode (GDE), a catalyst coated membrane (CCM), and a proton exchange membrane (PEM).
• steps a.) to c.) may be repeated at least once to form additional framed membrane electrode sub-assemblies.
• the invention provides a process for making a framed membrane electrode assembly array, wherein the above identified process further comprises: d.) separating the at least one element from the external frame, wherein the bridges and attached material are removed; and e.) contacting the framed membrane electrode sub-assembly formed in the above process with additional components.
• the framed membrane electrode sub- assembly formed in step (c) is placed on either side of a catalyst-coated membrane followed by pressing to form the framed membrane electrode assembly array.
• the framed membrane electrode assembly array is prepared by pressing together the sandwich formed by the framed membrane electrode sub-assemblies formed in step (c) and the ion-exchange membrane disposed there between.
• the framed membrane electrode assembly component comprises a catalyst coated membrane
• step (e) precedes step (d)
• framed membrane electrode assembly components each comprising a gas diffusion layer are placed on either side of the framed membrane electrode sub-assembly formed in step (c), and pressed to form the framed membrane electrode assembly array.
• step (e) precedes step (d)
• framed membrane electrode assembly components each comprising a gas diffusion electrode are placed on either side of the framed membrane electrode sub-assembly formed in step (c), and pressed to form a framed membrane electrode assembly array.
• the invention provides a framed membrane electrode sub-assembly formed using the above process.
• the invention provides a framed membrane electrode assembly array comprising a framed membrane electrode sub- assembly formed using the above process.
• the invention provides a fuel cell comprising a framed membrane electrode assembly array, wherein the framed membrane electrode sub-assembly is formed using the above process.
• Figure 1 depicts a top view of a planar-framed membrane electrode assembly component produced according to the present invention by die cutting a sheet of GDL, GDE, CCM or a PEM.
• Figure 2 depicts a carrier material configuration in accordance with the present invention.
• Figure 3 depicts the placement and attachment of the framed membrane electrode assembly component on top of the carrier material.
• FIG 4 depicts a catalyst-coated membrane (CCM) with selectively coated electrodes on a proton exchange membrane.
• CCM catalyst-coated membrane
• Figure 5 depicts an exploded view of a framed membrane electrode assembly array comprising a CCM sandwiched between two framed membrane electrode sub-assemblies with bridges removed.
• Figure 6 depicts a plurality of framed MEA components.
• Fuel cells are electrochemical devices that convert the chemical energy of a fuel, such as methanol or a hydrogen gas, and an oxidant into electrical energy.
• Typical fuel cells comprise an anode (a negatively charged electrode), a cathode (a positively charged electrode) separated by an electrolyte that are formed as assemblages of membrane electrode assemblies (MEA).
• the present invention is intended for use in the production of membrane electrode assemblies for use in fuel cells utilizing prot-on- exchange membranes (also known as "PEM"), for example direct methanol fuel cells, hydrogen fuel cells, reformed hydrogen fuel cells, as well as other liquid feed fuel cells (e.g. those utilizing feed fuels of ethanol, propanol, formic acid and the like), however the present invention is preferably used for the production of MEA's utilized in direct methanol fuel cells.
• PEM prot-on- exchange membranes
• the present invention allows for the production of MEA's having a variety of applications utilizing micro-portable technology, for example, micro-portable direct methanol fuel cells, which can be packaged having a substantially flat geometry for use in consumer electronics such as, for example, laptop computers, cell phones, PDA's and other portable electronic devices.
• planar means that each MEA element in the framed membrane electrode assembly component is arranged such that its largest surface lies in substantially the same plane as the equivalent surfaces of adjacent or neighboring MEA's.
• complementary framed membrane sub-assembly means a sub-assembly that complements the first formed sub-assembly, e.g.
• the present invention generally relates to a process of forming a framed membrane electrode assembly array (1), as shown in Figure 5, comprising the following steps, wherein steps a.) and b.) may be performed in any order.
• step (a) at least one framed membrane electrode assembly component (2), shown in Figure 1 , is formed.
• the framed membrane electrode assembly component (2) comprises an external frame (3) having a plurality of bridges or tabs (4), and at least one element (5) having outer edges, wherein the at least one element is connected to the external frame via the plurality of bridges, thereby forming a unitary structure.
• a carrier material (6) shown in Figure 2, having a plurality of apertures defined by a plurality of inner edges (11) is formed.
• the carrier material (6) is secured to the at least one framed membrane electrode assembly component (2), wherein the external frame and the plurality of outer edges (7) of the at least one element are supported by the carrier material as shown in Figure 3, thereby forming an framed membrane electrode sub-assembly.
• step (d) the at least one element is separated or electrically isolated from the external frame by removing the bridges and the material attached to said bridges (14).
• the framed membrane electrode component is a gas diffusion electrode or a catalyst coated membrane
• either an anode side (8) or cathode side (9), as seen in Figure 5 may be formed.
• steps (a) to (c) may be repeated at least once to make additional framed membrane electrode subassemblies that complement the sub-assembly formed in step (c), e.g., if a cathode side sub-assembly is formed in step (c), the steps are repeated to form an anode side sub- assembly.
• a framed membrane electrode assembly array may be formed by contacting the framed membrane electrode sub-assembly formed in the above process with additional components.
• the framed membrane electrode assembly component comprises a gas diffusion layer
• the framed membrane electrode sub- assembly formed in step (c) is placed on either side of a catalyst-coated membrane followed by pressing to form the framed membrane electrode assembly array.
• the framed membrane electrode assembly array is prepared by pressing together the sandwich formed by the framed membrane electrode sub-assemblies formed in step (c) and the ion-exchange membrane disposed there between.
• step (e) precedes step (d)
• additional framed membrane electrode assembly components each comprising a gas diffusion layer are placed on either side of the framed membrane electrode sub-assembly formed in step (c), and pressed to form the framed membrane electrode assembly array.
• step (e) precedes step (d)
• additional framed membrane electrode assembly components each comprising a gas diffusion electrode are placed on either side of the framed membrane electrode sub-assembly formed in step (c), and pressed to form a framed membrane electrode assembly array.
• Figure 4 shows a catalyst-coated membrane having selectively coated electrodes (12) on a PEM (13).
• the electrodes may be an anode with cathode on the other side or a cathode with anode on the other side.
• the process according to the present invention is scalable meaning it is a process that allows for the production of as few as one framed membrane electrode assembly component and any number of the same. This is determined by the size of the framed membrane electrode sub- assembly and the size and type of equipment used to make it. A plurality of framed MEA components is shown in Figure 6.
• the forming of the at least one framed membrane electrode assembly component (2), shown in Figure 1 typically occurs using cutting means, such as by die cutting a sheet CCM or GDL, PEM and/or GDE to have a single or multiple element geometry using a steel rule die for forming the required shape
• Cutting dies typically include features providing for aligning of the elements such as, for example, spring pins or visual registration marks so that the cut outline is properly positioned with respect to the part.
• the sheet In forming the framed membrane electrode assembly component from a sheet of CCM or GDE, the sheet may be selectively coated to resemble the form of the at least one element so that when the die cutting occurs, valuable catalyst (typically comprising platinum) may be conserved.
• the framed membrane electrode assembly component (2) formed in step a.) generally comprises at least one element (5) having outer edges, an external frame (3), a plurality of bridges (4) connecting the at least one element to the external frame, and a plurality of voids (10) defined by these components as shown in Figure 1 , wherein the framed membrane electrode assembly component is a CCM, GDL PEM and/or GDE.
• the bridges (4) act to stabilize the at least one element (5), so that the element(s) have the necessary alignment during the remainder of the process according to the present invention.
• the voids (10) allow for the electrical isolation of the at least one element(s) from the other elements in the array.
• the required alignment can be provided by the presence of alignment holes in the GDL or GDE.
• the at least one element typically forms either the anode or the cathode.
• the at least one element (5) may be of any shape, such as rectangular, circular, elliptical and the like, as well as a variety of shapes within the same framed membrane electrode assembly component. The shape of the element is dictated more by customer needs rather than fabrication process requirements. Typically, the at least one element has a rectangular shape.
• the framed membrane electrode assembly component, and thereby the at least one element, plurality of bridges and external frame form a substantially unitary structure all formed from the same material.
• the framed membrane electrode assembly component and thereby the at least one element, plurality of bridges and external frame form a substantially unitary structure all formed from the same material.
• the framed membrane electrode assembly component and thereby the at least one element, plurality of bridges and external frame form a substantially unitary structure all formed from the same material.
• the framed membrane electrode assembly component and thereby the at least one element, plurality of bridges and external frame
• the framed membrane electrode assembly component (2) may have a thickness ranging from about 100 to about 1000 microns.
• the thickness is in the range of about 100 to about 800 microns, more typically from about 150 to about 400 microns, most typically from about 200 to about 300 microns.
• the thickness is in the range of about 25 to about 375 microns, more typically from about 50 to about 250 microns, most typically from about 75 to about 200 microns.
• the framed membrane electrode assembly component (2) of the present invention may comprise any conventionally known proton exchange membrane (which acts as the electrolyte (ion-exchanger) as well a gas diffusion layer (a barrier film which separates the gases in the anode and cathode compartments of the fuel cell or a porous, conductive sheet material), each of which may have a catalyst coated thereon, thereby forming a catalyst-coated membrane (CCM) and/or a gas diffusion electrode (GDE) respectively.
• the gas diffusion layer can be coated on one or both surfaces with a thin porous layer usually referred to as the gas diffusion layer, typically comprising a film of carbon support particles and a binder, for example, fluoropolymers such as PTFE.
• the gas diffusion layer is a woven or non-woven carbon fiber substrate; more preferably, carbon- based papers or cloths that can optionally be treated to exhibit hydrophilic or hydrophobic behavior.
• a variety of techniques are known for the manufacture of a catalyst- coated membrane. Typical manufacturing techniques involve the application of a catalyst coating composition onto substrates such as the proton exchange polymer membrane. Methods for applying the catalyst onto the substrate include spraying, painting, patch coating, flexographic printing and screen-printing.
• the proton exchange membrane for use in preparing a catalyst- coated membrane (CCM) can be a membrane of the same ion exchange polymers used in the electrocatalyst coating compositions.
• the membranes can be made by known extrusion or casting techniques and have thicknesses that can vary depending upon the intended application.
• the membranes typically have a thickness of 350 ⁇ m or less, although recently membranes that are quite thin, i.e., 50 ⁇ m or less, more typically 25 ⁇ m or less, are being employed.
• the polymer can be in alkali metal or ammonium salt form, it is typical for the polymer in the membrane to be in acid form to avoid post treatment acid exchange steps.
• Suitable perfluorinated sulfonic acid polymer membranes in acid form are available under the trademark National® by E.I. du Pont de Nemours and Company. Reinforced perfluorinated ion exchange polymer membranes can also be utilized in CCM manufacture.
• Reinforced membranes can be made by impregnating porous, expanded PTFE (ePTFE) with ion exchange polymer.
• ePTFE porous, expanded PTFE
• ion exchange polymer ePTFE is available under the tradename "Goretex” from W. L. Gore and Associates, Inc., Elkton, MD, and under the tradename “Tetratex” from Tetratec, Feasterville, PA. Impregnation of ePTFE with perfluorinated sulfonic acid polymer is disclosed in U.S. Patents 5,547,551 and 6,110,333 both of which are incorporated herein by reference.
• the proton exchange membrane can be a porous support. A porous support may improve mechanical properties for some applications and/or decrease costs.
• the porous support can be made from a wide range of components, including hydrocarbons and polyolefins, e.g., polyethylene, polypropylene, polybutylene, copolymers including polyolefins, and the like. Perhalogenated polymers such as polychlorotrifluoroethylene can also be used.
• the membrane can also be made from a polybenzimadazole polymer, for example, by casting a solution of polybenzimadazole in phosphoric acid (H 3 PO 4 ) doped with trifluoroacetic acid (TFA) as described in U.S. Patent Nos. 5,525,436, 5,716,727, 6,025,085 and 6,099,988.
• Ion exchange polymers suitable for use in making the proton exchange membrane or catalyst coated membranes according to the present invention include, but are not limited to, highly fluorinated ion- exchange polymers. "Highly fluorinated” means that at least 90% of the total number of univalent atoms in the polymer are fluorine atoms. Most typically, the polymer is perfluorinated. It is typical for polymers used in fuel cells to have sulfonate ion exchange groups.
• sulfonate ion exchange groups as used herein means either sulfonic acid groups or salts of sulfonic acid groups, typically alkali metal or ammonium salts.
• the sulfonic acid form of the polymer is typical. If the polymer in the electrocatalyst coating composition is not in sulfonic acid form when used, a post treatment acid exchange step can be used to convert the polymer to acid form prior to use.
• the ion exchange polymer employed comprises a polymer backbone with recurring side chains attached to the backbone with the side chains carrying the ion exchange groups. Homopolymers or copolymers can be used.
• Copolymers are typically formed from one monomer that is a nonfunctional monomer and that provides carbon atoms for the polymer backbone, and a second monomer that provides carbon atoms for the polymer backbone and also contributes a side chain carrying a cation exchange group or its precursor, e.g., a sulfonyl halide group such a sulfonyl fluoride (-SO F), which can be subsequently hydrolyzed to a sulfonate ion exchange group.
• a sulfonyl halide group such a sulfonyl fluoride (-SO F)
• -SO F sulfonyl fluoride
• copolymers of a first fluorinated vinyl monomer together with a second fluorinated vinyl monomer having a sulfonyl fluoride group (-SO 2 F) can be used.
• Exemplary first fluorinated vinyl monomers include tetrafluoroethylene (TFE), hexafluoropropylene, vinyl fluoride, vinylidine fluoride, trifluoroethylene, chlorotrifluoroethylene, perfluoro (alkyl vinyl ether), and mixtures of two or more thereof.
• Exemplary second monomers include fluorinated vinyl ethers with sulfonate ion exchange groups or precursor groups that can provide the desired side chain in the polymer.
• the first monomer can also have a side chain that does not interfere with the ion exchange function of the sulfonate ion exchange group. Additional monomers can also be incorporated into the polymers if desired.
• suitable polymers include those disclosed in U.S. Patents 3,282,875; 4,358,545; and 4,940,525.
• One exemplary polymer comprises a perfluorocarbon backbone and a side chain represented by the formula -O-CF 2 CF(CF3)-O-CF 2 CF2SO3H.
• TFE tetrafluoroethylene
• PMMAF perfluoro(3,6-dioxa- 4-methyl-7-octenesulfonyl fluor
• An exemplary polymer of the type disclosed in U.S. Patents 4,358,545 and 4,940,525 has a side chain -O-CF 2 CF 2 SO 3 H.
• TFE tetrafluoroethylene
• POPF perfluoro(3-oxa-4-pentenesulfonyl fluoride)
• hydrolysis and acid exchange perfluorinated polymers of the type described hereinabove
• IXR ion exchange ratio
• Ion exchange ratio is the number of carbon atoms in the polymer backbone in relation to the ion exchange groups.
• IXR values for the polymer are possible. Typically, however, the IXR range for perfluorinated sulfonate polymers is from about 7 to about 33.
• EW equivalent weight
• the equivalent weight range corresponding to an IXR of about 7 to about 33 is about 700 EW to about 2000 EW.
• a preferred range for IXR for such a polymer is from about 8 to about 23 (750 to 1500 EW), and a more preferred range is from about 9 to about 15 (800 to 1100 EW).
• Any liquid medium compatible with the process for creating the proton exchange membrane, or for coating the catalyst onto the membrane can be used.
• the medium can be selected to minimize process risks associated with such constituents, as the medium is in contact with the catalyst during use.
• the medium is also sufficiently stable in the presence of the ion exchange polymer that, in the acid form, has strong acidic activity.
• the liquid medium is typically polar for compatibility with the ion exchange polymer, and is preferably able to wet the membrane. While it is possible for water to be used as the liquid medium, the medium is preferably such that the ion exchange polymer coalesces upon drying and does not require post treatment steps such as heating to form a stable electrode layer.
• a wide variety of polar organic liquids or mixtures thereof can serve as suitable liquid media for the electrocatalyst coating composition.
• Water in minor quantity can be present in the medium if it does not interfere with the coating process. Although some polar organic liquids can swell the membrane when present in sufficiently large quantity, the amount of liquid used in the electrocatalyst coating is preferably small enough that the adverse effects from swelling during the process are minor or undetectable. It is believed that solvents able to swell the proton exchange membrane can provide better contact and more secure application of the electrode to the membrane. A variety of alcohols are well suited for use as the liquid medium.
• Typical liquid media include suitable C 4 to C 8 alkyl alcohols such as n-, iso-, sec- and tert-butyl alcohols; the isomeric 5-carbon alcohols such as 1 , 2- and 3-pentanol, 2-methyl-1-butanol, 3-methyl, 1-butanol, etc.; the isomeric 6-carbon alcohols, such as 1-, 2-, and 3-hexanol, 2-methyl-1- pentanol, 3-methyl- 1-pentanol, 2-methyl-1-pentanol, 3-methyl, 1-pentanol, 4-methyl-1-pentanol, etc.; the isomeric C 7 alcohols and the isomeric Cg alcohols. Cyclic alcohols are also suitable.
• Preferred alcohols are n- butanol and n-hexanol, and n-hexanol is more preferred.
• the amount of liquid medium in the anode electrocatalyst varies and is determined by the type of medium employed, the constituents of the electrocatalyst, the type of coating equipment employed, desired electrode thickness, process speeds etc.
• the preferred ion exchange polymer is the commercially available dispersion of the acid form of the perfluorinated sulfonic acid polymer, sold by E.I. du Pont de Nemours and Company under the trademark Nation®, in a water/alcohol dispersion. Any conventionally known catalyst utilized with fuel cell technology may be used in conjunction with the present invention.
• Suitable catalysts for fuel cells typically depend upon the reactants selected. Suitable catalysts for use with the proton exchange membrane and gas diffusion electrode generally depend upon the reactants selected. However, typical catalyst matrials for oxidation of hydrogen or methanol fuels include metals such as for example, Pd, Pt, Ru, Rh and alloys thereof. Commonly use catalysts include platinum supported on carbon particles. Different catalysts may be preferred for use in different types of fuel cells and electrochemical reactors.
• the carrier material (6) as shown in Figure 2, is formed using a die cutting process similar to that used to form the framed membrane electrode assembly component. The carrier material is also a substantailly unitary structure having at least one aperture that is defined by the inner edges of the carrier material.
• the size of the apertures in the carrier material may vary widely and are dependent upon the size of the at least one element of the framed membrane electrode assembly component in order to ensure proper adhesion between materials.
• the carrier material (6) is configured such that the holes in the carrier material are slightly smaller than the element(s) (5) of the framed membrane electrode assembly component (2), such that only a small portion of the outer edge of the element is secured to the carrier material, where the outer edges of the at least one element overlap with the inner edges of the carrier naterial, thereby providing stability for the at least one element after the bridges have been removed.
• the carrier material (6) suitable for use with the present invention may comprise a thermoplastic material or a composite of thermoplastic materials.
• thermoplastic materials for use with the present invention include, but are not limited to, melt -processible fluoropolymers (i.e., Teflon® FEP 100 and Teflon® PFA 340-both available from E.I. du Pont de Nemours and Co., Wilmington DE); partially fluorinated polymers such as, for example, polyvinylidene fluoride (specific examples being Kynar® 710 and Kynar Flex® 2801 manufactured by Atofina Chemicals, King of Prussia, PA); thermoplastic fluoroelastomers (i.e., Kalrez® and Viton®, manufactured by E. I.
• aromatic condensation polymers such as polyaryl(ether ketone)'s (i.e., polyaryl(ether ketone) manufactured by Victrex Manufacturing Limited, Lancashire, Great Britain); modified polyethylene and modified polypropylene (i.e., Bynel® 4105 and Bynel® 50E561 respectively, both manufactured by E.I.
• thermoplastic material comprises Bynel® 4105.
• thermoplastic material should preferably be higher than the maximum temperature attainable in the fuel cells (i.e., about 95°C for a direct methanol fuel cell) and should be lower than the temperature that the polymeric electrolyte membrane can withstand (i.e., about 150°C for National®).
• the material should adhere well to various GDL's and polymeric electrolyte membranes by hot pressing.
• Suitable thermoplastic composite materials include, but are not limited to those thermoplastic materials noted above, which encapsulate inert fillers or a reinforcing layer comprising a material such as, for example, fiber glass, glass cloth, Kevlar® paper, Kapton® films, (the Kevlar and Kapton both being availbable from E.I.
• the reinforcing layer should be capable of withstanding higher temperatures than the melting point of the thermoplastic material in order to provide dimensional stability and, if necessary, electric insulation to finished parts.
• the carrier material (6) typically has a thickness ranging from about 25 microns to a maximum thickness of GDL material under compressive force used in the fuel cell applications. Preferably the carrier material has a thickness of about 10 microns to about 125 microns, more typically about 25 microns to about 100 microns and most preferably the thickness is about 50 microns. Securing the carrier material (6) to the framed membrane electrode assembly component (2) and the edges (7) of the element(s) (5) typically occurs through bonding methods, including adhesive and mechanical bonding.
• An adhesive bond may be achieved by pressing the parts together, and optionally, applying heat if necessary to activate the adhesive.
• the parts may be pressed together between optionally heated platens of a hydraulic or pneumatic press, between optionally heated rolls of a laminator, or while being conveyed between the belts of a belt press, wherein the belts pass through optional heating and cooling zones.
• a typical hot pressing operation for example, can be done in a 100 Ton press (manufactured by PHI, City of Industry, CA).
• Variables in the above- described processes include pressure, time and temperature, wherein one skilled in the art will recognize and understand the adjustments and appropriate values for each depending upon the materials used in the process.
• the adhesion between the framed membrane electrode assembly component and the carrier material is sufficient to withstand the subsequent process steps without damaging the integrity of the carrier material or framed membrane electrode assembly component.
• the outer edges of the at least one element overlap to some degree with the inner edges of the carrier material.
• Separating or electrically isolating the at least one elements (5) from the remainder of elements, if present, is typically performed using a cutting means, such as a die punch, where the plurality of bridges, and the carrier material secured thereto, are removed from the framed membrane electrode sub-assembly (3) to form openings (14), as shown in Figure 5.
• a cutting means such as a die punch
• the carrier material, as well as the framed membrane electrode assembly component may have perforations allowing for the removal of the bridges.
• the carrier material remains adhered or bonded to the framed membrane electrode assembly component where the inner edges of the carrier material overlap with the outer edges of the at least one element.
• This step is utilized for making both the cathode side (9) and anode side (8) of the framed MEA array shown in Fig 5.
• the size of holes cut in the carrier material and framed membrane electrode assembly component is not critical, so long as the at least one element is electrically isolated and the framed membrane electrode assembly component maintains its shape, while the external frame and at least a portion of the element(s) remain adhered or bonded to the carrier material.
• a framed MEA array can be converted into a fuel cell assembly by a.) trimming away the external frames (3) shown in Figure 5, b.) applying a gasket, for example silicone rubber (Furan® - Type 1007, obtained from Stockwell Rubber Company) cut to shape to cover the exposed area of the membrane of the MEA, by placing it on either side of the framed MEA Array (taking care to avoid overlapping of each element (5) and the gasket material), c.) sandwiching the gasketed framed MEA Array between anode and cathode flow field plates which may be equipped with anode inlet, anode outlet, catholyte gas inlet, catholyte gas outlet, end blocks, tied together with tie rods, or electrically insulating adhesive layers, and metal current collectors.
• a gasket for example silicone rubber (Furan® - Type 1007, obtained from Stockwell Rubber Company) cut to shape to cover the exposed area of the membrane of the MEA, by placing it on either side of the framed MEA Array
• the elements (5) of the framed MEA Array may be connected electrically in series or parallel based on the power output of the target application.
• the fuel cell assembly is typically connected to a fuel cell system (not shown).
• the fuel cell system typically comprises of a supply of air for use as catholyte gas, a load box to regulate the power output from the fuel cell, a fuel, e.g. methanol, solution tank to hold the feed anolyte solution, a liquid pump to feed the anolyte solution to the fuel cell at the desired flow rate, an exhaust container to collect the spent anolyte solution, and a power switch.
• the stack/plates were placed in a hydraulic press preheated to 130°C.
• the stack/plates were placed in a hydraulic press preheated to 130°C.
• the stack/plates were placed in a hydraulic press preheated to 165°C.

Landscapes

• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Electrochemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Life Sciences & Earth Sciences (AREA)
• Manufacturing & Machinery (AREA)
• Sustainable Development (AREA)
• Sustainable Energy (AREA)
• Composite Materials (AREA)
• Ceramic Engineering (AREA)
• Fuel Cell (AREA)

Priority Applications (3)

Applications Claiming Priority (2)

Publications (1)

Family

ID=34102852

Family Applications (1)

Country Status (5)

Cited By (5)

Families Citing this family (8)

Citations (2)

Family Cites Families (14)

• 2004
  • 2004-07-22 TW TW093121906A patent/TW200509447A/zh unknown
  • 2004-07-22 DE DE112004001357T patent/DE112004001357T5/de not_active Withdrawn
  • 2004-07-22 WO PCT/US2004/023667 patent/WO2005011041A1/en not_active Ceased
  • 2004-07-22 JP JP2006521252A patent/JP2006528414A/ja not_active Ceased
  • 2004-07-22 US US10/563,460 patent/US7416804B2/en not_active Expired - Fee Related

Patent Citations (2)

Also Published As

Similar Documents

Legal Events