WO2004096713A1 - Process for preparing zirconium oxides and zirconium-based mixed oxides - Google Patents
Process for preparing zirconium oxides and zirconium-based mixed oxides Download PDFInfo
- Publication number
- WO2004096713A1 WO2004096713A1 PCT/GB2004/001840 GB2004001840W WO2004096713A1 WO 2004096713 A1 WO2004096713 A1 WO 2004096713A1 GB 2004001840 W GB2004001840 W GB 2004001840W WO 2004096713 A1 WO2004096713 A1 WO 2004096713A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- zirconium
- oxide
- aqueous solution
- weight
- hydroxide
- Prior art date
Abstract
Description
Claims