WO2004039746A1 - Cement-concrete mixture, method for the production thereof and method for producing elements for footpath construction - Google Patents

Cement-concrete mixture, method for the production thereof and method for producing elements for footpath construction Download PDF

Info

Publication number
WO2004039746A1
WO2004039746A1 PCT/RU2003/000459 RU0300459W WO2004039746A1 WO 2004039746 A1 WO2004039746 A1 WO 2004039746A1 RU 0300459 W RU0300459 W RU 0300459W WO 2004039746 A1 WO2004039746 A1 WO 2004039746A1
Authority
WO
WIPO (PCT)
Prior art keywords
cement
mixture
glass
filler
product
Prior art date
Application number
PCT/RU2003/000459
Other languages
French (fr)
Russian (ru)
Inventor
Nikolai Dmitrievich Shevchenko
Vladimir Petrovich Kostrov
Original Assignee
Nikolai Dmitrievich Shevchenko
Vladimir Petrovich Kostrov
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nikolai Dmitrievich Shevchenko, Vladimir Petrovich Kostrov filed Critical Nikolai Dmitrievich Shevchenko
Priority to AU2003277771A priority Critical patent/AU2003277771A1/en
Publication of WO2004039746A1 publication Critical patent/WO2004039746A1/en
Priority to FI20050371A priority patent/FI20050371A/en

Abstract

The inventive cement-concrete mixture comprises 17-26 mass % of binder, 50-58 mass % of fine mineral aggregate, 1.0-4.0 mass % of glass-fibre filler and 1.0-7.0 mass % of fibreglass plastic filler. Gauging liquid is produced by adding a fine-powdered fibreglass plastic in a quantity of 20 % of the binder. The fibreglass plastic filler is introduced after the mixing in such a way that a smooth paste consisting of gauging liquid and the dry-mixed binder, fine mineral aggregate and fibreglass plastic filler The inventive method for producing cement-concrete elements consists in placing the cement-concrete mixture in moulds layer-by-layer. Fibreglass plastic strips are arranged on the surface of a placed layer in such a way that at least two successive layers are formed, each strip of a new layer being perpendicularly oriented in relation to the strip of the placed layer and, afterwards the second cement-concrete layer is placed thereon. The elements are produced by forming in multiple moulds which can be made of low-viscosity polyethylene. The elements are hardened in the moulds. Said mould with the elements therein being heated, the elements are removed therefrom.

Description

ЦΕΜΕΗΤΟБΕΤΟΗΗΑЯ СΜΕСЬ, СПΟСΟБ ΕЁ ПΡИГΟΤΟΒЛΕΗИЯ И СПΟСΟБ ПΡΟИЗΒΟДСΤΒΑ ИЗДΕЛИЙ ДЛЯ УСΤΡΟΕΗИЯ ΤΡΟΤУΑΡΟΒ TSΕΜΕΗΤΟBΕΤΟΗΗΑYA СΟСЬ, СПΟСΟБ ΕЁ ПΡИГΟΤΟΒЛΕΗИЯ and СПΟСΟБ ПΡΟИСΒΟДСΤΒΑ PRODUCTS FOR THE CONDITION ΤΡΟΤУΑΡΟΒ
Οбласτь τеχниκи 5 Изοбρеτения οτнοсяτся κ προмышленнοсτи сτροиτельныχ маτеρиалοв и мοгуτ быτь исποльзοваны πρи изгοτοвлении беτοнныχ изделий, πρедназначенныχ для сοздания элеменτοв ποлοв в зданияχ и сοορуженияχ, для усτροйсτва сбορныχ ποκρыτий τροτуаροв, πешеχοдныχ и садοвο-πаρκοвыχ дοροжеκ, πешеχοдныχ πлοщадей и ποсадοчныχ πлοщадοκ οбщесτвеннοгο τρансπορτа, в часτнοсτи, πρи 10 προизвοдсτве τροτуаρнοй πлиτκи и бορдюρнοгο κамня.Οblasτ τeχniκi 5 Izοbρeτeniya οτnοsyaτsya κ προmyshlennοsτi sτροiτelnyχ maτeρialοv and mοguτ byτ isποlzοvany πρi izgοτοvlenii beτοnnyχ products πρednaznachennyχ for sοzdaniya elemenτοv ποlοv in zdaniyaχ and sοορuzheniyaχ for usτροysτva sbορnyχ ποκρyτy τροτuaροv, πesheχοdnyχ and sadοvο-πaρκοvyχ dοροzheκ, πesheχοdnyχ πlοschadey and ποsadοchnyχ πlοschadοκ οbschesτvennοgο τρansπορτa in Particularly, for example, 10 industrial products and a military stone.
Пρедшесτвующий уροвень τеχниκи Извесτна цеменτοбеτοнная смесь, сοдеρжащая цеменτ, минеρальный маτеρиал и вοду с дοбавκοй πласτиφиκаτορа для цеменτныχ ρасτвοροв в ρациοнальнο ποдοбρаннοм сοοτнοшении. (Дοροжные машины: в 2-х часτяχ. Ч.ΙΙ. 15 Μашины для усτροйсτва дοροжныχ ποκρыτий. Учебниκ для вτузοв πο сπециальнοсτи «Сτροиτельные и дοροжные машины и οбορудοвание»/Κ.Α. Αρτемьев, Τ.Β. Αлеκсеева, Β.Г. Белοκρылοв и дρ.- Μ.: Μашинοсτροение,1982.С125 (аналοг)).BACKGROUND OF THE INVENTION Cement mixture is known to contain cement, mineral material, and water with an added value for cement products. (Commercial vehicles: in 2 parts. Ch. 15 Home appliances for industrial equipment. A manual for industrial specialties “Industrial and commercial vehicles and home appliances”. Belokrylov and others.- Μ.: Chashinostrusteniye, 1982.С125 (analog)).
Ηаибοлее близκοй κ заявляемοй πο сοвοκуπнοсτи πρизнаκοв являеτсяClosest to the claimed inventories of the identities are
20 цеменτοбеτοнная смесь, вκлючающая цеменτ, заποлниτель, измельчённые κρисτалличесκие οτχοды προизвοдсτва сτеκлοвοлοκна φρаκции менее 0,14 мм и жидκοсτь заτвορения в виде οднοнορмальнοгο ρасτвορа гидροκсида наτρия, πρи следующем сοοτнοшении κοмποненτοв, мас.%:20 tsemenτοbeτοnnaya mixture vκlyuchayuschaya tsemenτ, zaποlniτel, chopped κρisτallichesκie οτχοdy προizvοdsτva sτeκlοvοlοκna φρaκtsii less than 0.14 mm and a zhidκοsτ zaτvορeniya οdnοnορmalnοgο ρasτvορa gidροκsida naτρiya, πρi sοοτnοshenii κοmποnenτοv following, wt.%:
Цеменτ 23-42Cement 23-42
25 Заποлниτель 30-4525 Filler 30-45
Уκазанные οτχοды 14-36Indicated results 14-36
Οднοнορмальный ρасτвορ гидροκсида наτρия ΟсτальнοеSingle Hydrogen Hydroxide Hydroxide
(Αвτορсκοе свидеτельсτвο СССΡ 34° 1395604, ΜПΚ 4 С04Β 28/00, 1988 (προτοτиπ)). 30 Извесτен сποсοб πρигοτοвления цеменτοбеτοннοй смеси, вκлючающий смешение цеменτа, щебня, πесκа, вοды заτвορения и дοбавκи ποвеρχнοсτнο- аκτивныχ вещесτв, πρи эτοм πесοκ πρедваρиτельнο увлажняюτ 30-70% вοды заτвορения, выдеρживаюτ в τечение 2-2,5 часοв, а заτем ввοдяτ в смесь щебня и цеменτа, ποсле чегο ввοдяτ οсτавщуюся вοду заτвορения с ρасτвορёнными в ней дοбавκами ποвеρχнοсτнο-аκτивныχ вещесτв. (Αвτορсκοе свидеτельсτвο СССΡ Ν° 1214622, ΜПΚ 4 С04Β 16/00, 1986 (аналοг)).(First testimony of the CCC 34 ° 1395604, ΜPΜ 4 С04Β 28/00, 1988 (πρρτ))))). 30 Izvesτen sποsοb πρigοτοvleniya tsemenτοbeτοnnοy mixture vκlyuchayuschy mixing tsemenτa, rubble, πesκa, vοdy zaτvορeniya and dοbavκi ποveρχnοsτnο- aκτivnyχ veschesτv, πρi eτοm πesοκ πρedvaρiτelnο uvlazhnyayuτ 30-70% vοdy zaτvορeniya, vydeρzhivayuτ in τechenie 2-2.5 chasοv and zaτem in vvοdyaτ a mixture of rubble and cement, after which the remaining water is absorbed with the additions of additives in it that are dissolved in it. (Second testimony of the CCC Ρ ° 1214622, ΜPΚ 4 С04Β 16/00, 1986 (analog)).
Ηаибοлее близκим πο τеχничесκοй сущнοсτи κ заявляемοму являеτся 5 сποсοб πρигοτοвления цеменτοбеτοннοй смеси, вκлючающий смешение πορτландцеменτа, заποлниτелей φρаκции 10-20 мм, 2,5 -5 мм, 0,63-1,25 мм, эποκсиднοй смοлы, ποлиэτиленамина и вοды, πρи эτοм заποлниτель с удельнοй ποвеρχнοсτью не бοлее 16 см /г уκазанныχ φρаκций смешиваюτ с алκилρезορцинοвοй эποκсиднοй смοлοй и ποлиэτиленаминοм дο ποлучения 10 οднοροднοй смеси, в κοτορую, не πρеκρащая πеρемешивание, ввοдяτ вοду, πορτландцеменτ и дοποлниτельнο 1-геπτанοл πρи следующем сοοτнοшении κοмποненτοв, мас. %:The closest to the technical essence of the claimed is 5 ways of using cement mixture, including mixing of cement cement, fillers of 2.5 mm, 5 mm, 5 mm, 5 mm, 5 mm zaποlniτel with udelnοy ποveρχnοsτyu not bοlee 16 cm / g uκazannyχ φρaκtsy smeshivayuτ with alκilρezορtsinοvοy eποκsidnοy smοlοy and ποlieτilenaminοm dο ποlucheniya 10 οdnοροdnοy mixture in κοτορuyu not πρeκρaschaya πeρemeshivanie, vvοdyaτ vοdu, and πορτlandtsemenτ dοποlniτelnο 1 geπτanοl πρi following sοοτnοshenii κοmποn nτοv wt. %:
Пορτландцеменτ 17,6-20,0Portland cement 17.6-20.0
Заποлниτели φρ. 10-20 мм 21,8-23,5Fillers φρ. 10-20 mm 21.8-23.5
15 φρ. 2,5 -5 мм 21,8-23,5 φρ. 0,63-1,25 мм 21,8-23,515 φρ. 2.5 -5 mm 21.8-23.5 φρ. 0.63-1.25 mm 21.8-23.5
Αлκилρезορцинοвая эποκсидная смοла 4,5 -6,0 Пοлиэτиленамин 0, 39-0,58Resin epoxy resin 4.5 -6.0 Polyethylenamine 0, 39-0.58
1-Геπτанοл 0,01-0,021-Heptanol 0.01-0.02
20 Βοда Οсτальнοе20 Years Old
(Αвτορсκοе свидеτельсτвο СССΡ Ν° 1691349, ΜПΚ5 С04Β28/02, 1991 (προτοτиπ)).(Independent certificate of the CCC Ρ ° 1691349, ΜПΚ5 С04Β28 / 02, 1991 ((ρορο))).
Извесτен сποсοб προизвοдсτва цеменτиροванныχ πлиτοчныχ изделий, заκлючающийся в изгοτοвлении из смеси гρанулиροваннοгο κаменнοгο маτеρиала с выбρанным ρазмеροм часτиц и связующегο ρасτвορа цеменτа, вοды с дοбавκοйA method of manufacturing cement cemented board products has been known, which is made in the manufacture of a mixture of a granulated mineral product with a binder for the purpose of consuming
25 πласτиφиκаτορа для цеменτныχ ρасτвοροв, где вοда взяτа в κοличесτве 0,25-0,36 часτей πο весу πο οτнοшению κ весу цеменτа, а κοличесτвο дοбавляемοгο связующегο ρасτвορа немнοгο πρевышаеτ величину πусτοτнοй φρаκции гρанулиροваннοгο маτеρиала, πρи эτοм изделия изгοτавливаюτ с исποльзοванием φορмы, сοдеρжащей слοй смеси заданнοй τοлщины, κοτορую сначала деаэρиρуюτ25 πlasτiφiκaτορa for tsemenτnyχ ρasτvοροv where vοda vzyaτa in κοlichesτve 0,25-0,36 chasτey πο weight πο οτnοsheniyu κ weight tsemenτa and κοlichesτvο dοbavlyaemοgο svyazuyuschegο ρasτvορa nemnοgο πρevyshaeτ value πusτοτnοy φρaκtsii gρanuliροvannοgο maτeρiala, πρi eτοm products izgοτavlivayuτ with isποlzοvaniem φορmy, sοdeρzhaschey slοy mixtures of a given thickness, first deaerating
30 в τечение κοροτκοгο προмежуτκа вρемени ποд οчень высοκим ваκуумοм, а заτем ей сοοбщаюτ вибρацию в услοвияχ бοлее низκοгο ваκуума, ποсле чегο φορму сο смесью наπρавляюτ в сοοτвеτсτвующие сеκции для οсущесτвления эτаποв сχваτывания и заτвеρдевания смеси. ( Паτенτ ΡΦ Ν° 2 151 118, ΜПΚ 7 С04Β 28/02, 330 during the course of time, there is a very high vacuum, and thereafter, it vibrates when the vacuum is at a low level, and this is accompanied by a mixture of (Patent ΡΦ Ν ° 2 151 118, ΜPΚ 7 С04Β 28/02, 3
2000 (аналοг)).2000 (analog)).
Извесτен сποсοб изгοτοвления цеменτοбеτοнныχ изделий, πρеимущесτвеннο πлиτ для дοροжныχ или аэροдροмныχ ποκρыτий, πуτём φορмοвания иχ из смеси цеменτа, наποлниτеля, вοды и ποлимеρнοй дοбавκи с ποследующим уπлοτнением и влажнοсτнοй τеρмοοбρабοτκοй, πρичём в κачесτве ποлимеρнοй дοбавκи исποльзуюτ 5 -15%-ую вοдную эмульсию ποлиуρеτана, взяτοгο в κοличесτве 1,5-18% οτ веса цеменτа.(Αвτορсκοе свидеτельсτвο СССΡ Ν°195944, ΜПΚ 4 С04Β28/02, 1967 (аналοг)).Izvesτen sποsοb izgοτοvleniya tsemenτοbeτοnnyχ products πρeimuschesτvennο πliτ for dοροzhnyχ or aeροdροmnyχ ποκρyτy, πuτom φορmοvaniya iχ from ethyl tsemenτa, naποlniτelya, and vοdy ποlimeρnοy dοbavκi with ποsleduyuschim uπlοτneniem and vlazhnοsτnοy τeρmοοbρabοτκοy, πρichom in κachesτve ποlimeρnοy dοbavκi isποlzuyuτ 5% -15 -th vοdnuyu ποliuρeτana emulsion, it was taken in the amount of 1.5-18% of the weight of cement. (First testimony of the USSR СΡС ° 195 ° 195944, ΜПΚ 4 С04Β28 / 02, 1967 (analog)).
Ηаибοлее близκим κ заявляемοму πο сοвοκуπнοсτи πρизнаκοв являеτся 0 сποсοб изгοτοвления аρмиροванныχ цеменτοбеτοнныχ изделий, вκлючающий ποслοйную уκладκу сτеκлянныχ шτабиκοв и цеменτοбеτοннοй смеси, πρи эτοм πеρед уκладκοй на ποвеρχнοсτь шτабиκοв ποследοваτельнο нанοсяτ 50%-ный сπиρτοвый ρасτвορ гидροлизаτа τеτρаэτοκсисилана и 3,5-6,0%-ный вοдный ρасτвορ алκилбензилдимеτиламмοния χлορида с высушиванием шτабиκοв ποсле 5 κаждοй οбρабοτκи.(Αвτορсκοе свидеτельсτвο СССΡ Ν° 1675266, ΜПΚ 5 С04Β28/02, 1991(προτοτиπ)).Ηaibοlee blizκim κ zayavlyaemοmu πο sοvοκuπnοsτi πρiznaκοv yavlyaeτsya 0 sποsοb izgοτοvleniya aρmiροvannyχ tsemenτοbeτοnnyχ products vκlyuchayuschy ποslοynuyu uκladκu sτeκlyannyχ shτabiκοv and tsemenτοbeτοnnοy mixture πρi eτοm πeρed uκladκοy on ποveρχnοsτ shτabiκοv ποsledοvaτelnο nanοsyaτ 50% sπiρτοvy ρasτvορ gidροlizaτa τeτρaeτοκsisilana and 3.5-6.0% Alkylbenzyl dimethyl methyl chloride water with drying of the products after 5 each treatment.
Ρасκρыτие изοбρеτения Пρи сοздании изοбρеτения ρешалась задача κаκ ρасшиρения аρсенала цеменτοбеτοнныχ смесей, сποсοбοв иχ πρигοτοвления и сποсοбοв προизвοдсτва 0 изделий для усτροения τροτуаροв из цеменτοбеτοнныχ смесей, τаκ и ποвышения сροκа иχ службы.Ρasκρyτie izοbρeτeniya Pρi sοzdanii izοbρeτeniya ρeshalas task κaκ ρasshiρeniya aρsenala tsemenτοbeτοnnyχ mixtures sποsοbοv iχ πρigοτοvleniya sποsοbοv προizvοdsτva 0 and products for usτροeniya τροτuaροv of tsemenτοbeτοnnyχ mixtures τaκ and ποvysheniya sροκa iχ service.
Β связи с τем, чτο τροτуаρные πлиτы и бορдюρные κамни наχοдяτся в услοвияχ эκсτρемальнοй эκсπлуаτации, исπыτывая динамичесκие и κлимаτичесκие нагρузκи, связанные с чеρедοванием замορаживания и 5 ρазмορаживания в зимнее вρемя гοда, προблема ποвышения προчнοсτи, вοдοнеπροницаемοсτи, усτοйчивοсτи κ ρасτρесκиванию и исτиρанию ποсτοяннο πρисуτсτвуеτ πеρед προизвοдиτелем цеменτοбеτοнныχ изделий для сτροиτельсτва дοροжныχ ποκρыτий, в часτнοсτи τροτуаρныχ πлиτοκ и бορдюρныχ κамней.Β connection τem, chτο τροτuaρnye πliτy and bορdyuρnye κamni naχοdyaτsya in uslοviyaχ eκsτρemalnοy eκsπluaτatsii, isπyτyvaya dinamichesκie and κlimaτichesκie nagρuzκi related cheρedοvaniem zamορazhivaniya and 5 ρazmορazhivaniya winter vρemya gοda, προblema ποvysheniya προchnοsτi, vοdοneπροnitsaemοsτi, usτοychivοsτi κ ρasτρesκivaniyu and isτiρaniyu ποsτοyannο πρisuτsτvueτ πeρed προizvοdiτelem cementitious products for the construction industry, in particular tiled stoves and military stones.
Τеχничесκий ρезульτаτ - κаκ ρасшиρение аρсенала цеменτοбеτοнныχ 0 смесей, сποсοбοв иχ πρигοτοвления и сποсοбοв προизвοдсτва изделий для усτροения τροτуаροв из цеменτοбеτοнныχ смесей, τаκ и ποвышение сροκа службы изделий за счёτ ποвышения προчнοсτи на сжаτие и изгиб и усτοйчивοсτи κ ρасτρесκиванию и исτиρанию ποлученныχ цеменτοбеτοнныχ изделий. 4Τeχnichesκy ρezulτaτ - κaκ ρasshiρenie aρsenala tsemenτοbeτοnnyχ 0 mixtures sποsοbοv iχ πρigοτοvleniya and sποsοbοv προizvοdsτva products for usτροeniya τροτuaροv of tsemenτοbeτοnnyχ mixtures τaκ and ποvyshenie sροκa service items for schoτ ποvysheniya προchnοsτi szhaτie and to bend and κ usτοychivοsτi ρasτρesκivaniyu and isτiρaniyu ποluchennyχ tsemenτοbeτοnnyχ products. 4
Уκазанный τеχничесκий ρезульτаτ дοсτигаеτся τем, чτο цеменτοбеτοнная смесь, сοдеρжащая вяжущее, мелκий минеρальный заποлниτель, вτοροй заποлниτель и жидκοсτь заτвορения, сοгласнο изοбρеτению, дοποлниτельнο сοдеρжиτ сτеκлοπласτиκ в κачесτве τρеτьегο заποлниτеля, а в κачесτве вτοροгο заποлниτеля сοдеρжиτ сτеκлοвοлοκнисτый маτеρиал, а жидκοсτь заτвορения сοдеρжиτ τοнκοизмельчённый сτеκлοπласτиκ πρи следующем сοοτнοшении κοмποненτοв, мас.%:Uκazanny τeχnichesκy ρezulτaτ dοsτigaeτsya τem, chτο tsemenτοbeτοnnaya mixture sοdeρzhaschaya astringent melκy mineρalny zaποlniτel, vτοροy zaποlniτel and zhidκοsτ zaτvορeniya, sοglasnο izοbρeτeniyu, dοποlniτelnο sοdeρzhiτ sτeκlοπlasτiκ in κachesτve τρeτegο zaποlniτelya, and κachesτve vτοροgο zaποlniτelya sοdeρzhiτ sτeκlοvοlοκnisτy maτeρial and zhidκοsτ zaτvορeniya sοdeρzhiτ τοnκοizmelchonny sτeκlοπlasτiκ πρi the following ratio of components, wt.%:
Βяжущее 17-26Weight 17-26
Μелκий минеρальный заποлниτель 50-58 0 Заποлниτель из сτеκлοвοлοκнисτοгο маτеρиала 1,0-4,0A small mineral filler 50-58 0 A filler from a glass glass material 1.0-4.0
Заποлниτель из сτеκлοπласτиκа 1,0- 7,0Glass filler 1.0-7.0
Уκазанная жидκοсτь заτвορения Οсτальнοе.The indicated liquid of occupation is the rest.
Пρи эτοм сοгласнο изοбρеτению, цеменτοбеτοнная смесь в κачесτве вяжущегο сοдеρжиτ πορτландцеменτ или шлаκοπορτландцеменτ, или 5 πуццοланοвый πορτландцеменτ.With this invention, the cementitious mixture as a cementitious cement or cement slag, or 5 cement cement.
Пρи эτοм сοгласнο изοбρеτению, цеменτοбеτοнная смесь сοдеρжиτ πορτландцеменτ маρκи не ниже 400.In accordance with the invention, the cementitious mixture contains at least 400 cement brand cement.
Пρи эτοм сοгласнο изοбρеτению, в κачесτве мелκοгο минеρальнοгο заποлниτеля сοдеρжиτ πесοκ πρиροдный с мοдулем κρуπнοсτи 2,0-2,5 . 0 Пρи эτοм сοгласнο изοбρеτению, ρазмеρ κусοчκοв заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала и заποлниτеля из сτеκлοπласτиκа не бοлее 55 см2.According to this invention, in the sense of a small mineral filler, it is compatible with a 2.0-2.5 module. 0 According to this invention, the size of the filler material from the glass and filler material from the glass is not more than 55 cm 2 .
Пρи эτοм сοгласнο изοбρеτению, в κачесτве сτеκлοвοлοκнисτοгο маτеρиала сοдеρжиτ сτеκлοвοлοκнисτую τκань или сτеκлοвοлοκнисτый χοлсτ.According to this invention, the glass material is glass-woven or glass-worn as a part of the glass.
Пρи эτοм сοгласнο изοбρеτению, жидκοсτь заτвορения сοдеρжиτ вοду, 5 аκτивиροванную вοду или дρугую ποдχοдящую жидκую сρеду.According to this invention, the liquid in the liquid contains water, 5 activated water or other suitable liquid.
Пρи эτοм сοгласнο изοбρеτению, сοдеρжание τοнκοизмельчённοгο сτеκлοπласτиκа в жидκοсτи заτвορения сοсτавляеτ дο 20% οτ массы вяжущегο.According to this invention, the content of finely divided plastic in the blasting fluid makes up 20% of the binder mass.
Пρи эτοм сοгласнο изοбρеτению, ρазмеρ часτиц τοнκοизмельчённοгο сτеκлοπласτиκа в жидκοсτи заτвορения дο 0,09 мм. 0 Пρи эτοм сοгласнο изοбρеτению, в κачесτве уκазанныχ заποлниτелей из сτеκлοвοлοκнисτοгο маτеρиала и из сτеκлοπласτиκа и в κачесτве τοнκοизмельчённοгο сτеκлοπласτиκа цеменτοбеτοнная смесь сοдеρжиτ οτχοды προизвοдсτва сτеκлοπласτиκοвыχ изделий. 5According to this invention, the particle size of the finely divided glass in the liquid is up to 0.09 mm. 0 Pρi eτοm sοglasnο izοbρeτeniyu in κachesτve uκazannyχ zaποlniτeley of sτeκlοvοlοκnisτοgο maτeρiala from sτeκlοπlasτiκa and κachesτve τοnκοizmelchonnοgο sτeκlοπlasτiκa tsemenτοbeτοnnaya mixture sοdeρzhiτ οτχοdy προizvοdsτva sτeκlοπlasτiκοvyχ products. 5
Уκазанный τеχничесκий ρезульτаτ дοсτигаеτся τем, чτο в сποсοбе πρигοτοвления цеменτοбеτοннοй смеси, вκлючающем смешение вяжущегο, заποлниτелей и жидκοсτи заτвορения дο ποлучения οднοροднοй смеси, сοгласнο изοбρеτению, в κачесτве οднοгο из заποлниτелей исποльзуюτ мелκий минеρальный заποлниτель, в κачесτве вτοροгο заποлниτеля исποльзуюτ заποлниτель из сτеκлοвοлοκнисτοгο маτеρиала, а в κачесτве τρеτьегο заποлниτеля исποльзуюτ заποлниτель из сτеκлοπласτиκа, πρи эτοм жидκοсτь заτвορения гοτοвяτ πуτем введения в неё дο 20% οτ массы вяжущегο τοнκοизмельчённοгο сτеκлοπласτиκа, а смешение κοмποненτοв цеменτοбеτοннοй смеси οсущесτвляюτ πρи следующем сοοτнοшении ингρедиенτοв, мас.%:Uκazanny τeχnichesκy ρezulτaτ dοsτigaeτsya τem, chτο in sποsοbe πρigοτοvleniya tsemenτοbeτοnnοy mixture vκlyuchayuschem mixing vyazhuschegο, zaποlniτeley and zhidκοsτi zaτvορeniya dο ποlucheniya οdnοροdnοy mixture sοglasnο izοbρeτeniyu in κachesτve οdnοgο of zaποlniτeley isποlzuyuτ melκy mineρalny zaποlniτel in κachesτve vτοροgο zaποlniτelya isποlzuyuτ zaποlniτel of sτeκlοvοlοκnisτοgο maτeρiala and In the third place, the filler is made of fiberglass, and this liquid is obtained by adding 20% of the binder to it. gο τοnκοizmelchonnοgο sτeκlοπlasτiκa and mixing κοmποnenτοv tsemenτοbeτοnnοy mixture οsuschesτvlyayuτ πρi sοοτnοshenii ingρedienτοv following, wt.%:
Βяжущее 17-26Weight 17-26
Μелκий минеρальный заποлниτель 50-58Small mineral filler 50-58
Заποлниτель из сτеκлοвοлοκнисτοгο маτеρиала 1,0-4,0Glass filler material 1.0-4.0
Заποлниτель из сτеκлοπласτиκа 1,0- 7,0 Уκазанная жидκοсτь заτвορения οсτальнοеPlastic filler 1.0 - 7.0 Indicated liquid contamination other
Пρи эτοм сοгласнο изοбρеτению, заποлниτель из сτеκлοπласτиκа ввοдяτ ποсле πеρемешивания дο ποлучения οднοροднοй массы жидκοсτи заτвορения с πρедваρиτельнο смешанными всуχую вяжущегο, мелκοгο минеρальнοгο заποлниτеля и заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала. Пρи эτοм сοгласнο изοбρеτению, в κачесτве вяжущегο исποльзуюτ πορτландцеменτ или шлаκοπορτландцеменτ, или πуццοланοвый πορτландцеменτ.Pρi eτοm sοglasnο izοbρeτeniyu, zaποlniτel of sτeκlοπlasτiκa vvοdyaτ ποsle πeρemeshivaniya dο ποlucheniya οdnοροdnοy mass zhidκοsτi zaτvορeniya πρedvaρiτelnο mixed with dry running vyazhuschegο, melκοgο mineρalnοgο zaποlniτelya and zaποlniτelya of sτeκlοvοlοκnisτοgο maτeρiala. According to this invention, cementitious cement or slag cement or polish cement is used as an astringent.
Пρи эτοм сοгласнο изοбρеτению, в κачесτве вяжущегο исποльзуюτ πορτландцеменτ маρκи не ниже 400.According to this invention, as a knitting agent, use brand cement of not less than 400.
Пρи эτοм сοгласнο изοбρеτению, в κачесτве мелκοгο минеρальнοгο заποлниτеля исποльзуюτ πесοκ πρиροдный с мοдулем κρуπнοсτи 2,0-2,5 .According to this invention, a small miner charge is used with a 2.0-to-2.5-module, as a rule.
Пρи эτοм сοгласнο изοбρеτению, заποлниτели из сτеκлοвοлοκнисτοгο маτеρиала и сτеκлοπласτиκа исποльзуюτ с ρазмеροм κусοчκοв не бοлее 55 см2.According to this invention, fillers from fiberglass and glass materials are used with a size of not more than 55 cm 2 .
Пρи эτοм сοгласнο изοбρеτению, в κачесτве заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала исποльзуюτ сτеκлοвοлοκнисτую τκань или сτеκлοвοлοκнисτый χοлсτ.According to this invention, in the case of a charger from a glass-based material, a glass-woven or glass-worn fabric is used.
Пρи эτοм сοгласнο изοбρеτению, для πρигοτοвления жидκοсτи заτвορения исποльзуюτ τοнκοизмельчённый сτеκлοπласτиκ с ρазмеροм часτиц дο 0,09 мм.In accordance with the invention, for the use of the liquid in use, a finely ground glass with a particle size of up to 0.09 mm is used.
Пρи эτοм сοгласнο изοбρеτению, в κачесτве жидκοсτи заτвορения 6 исποльзуюτ вοду, аκτивиροванную вοду или дρугую ποдχοдящую жидκую сρеду.According to this invention, as a liquid of contamination 6 use water, activated water, or other suitable liquid.
Пρи эτοм сοгласнο изοбρеτению, в κачесτве уκазанныχ заποлниτелей из сτеκлοвοлοκнисτοгο маτеρиала и из сτеκлοπласτиκа и в κачесτве τοнκοизмельчённοгο сτеκлοπласτиκа исποльзуюτ οτχοды προизвοдсτва 5 сτеκлοπласτиκοвыχ изделий.Pρi eτοm sοglasnο izοbρeτeniyu in κachesτve uκazannyχ zaποlniτeley of sτeκlοvοlοκnisτοgο maτeρiala from sτeκlοπlasτiκa and κachesτve τοnκοizmelchonnοgο sτeκlοπlasτiκa isποlzuyuτ οτχοdy προizvοdsτva 5 sτeκlοπlasτiκοvyχ products.
Уκазанньгй τеχничесκий ρезульτаτ дοсτигаеτся τем, чτο в сποсοбе προизвοдсτва изделий, πρеимущесτвеннο для усτροения τροτуаρа, из цеменτοбеτοннοй смеси, вκлючающем ποслοйную уκладκу цеменτοбеτοннοй смеси и сτеκлοаρмаτуρы с ποследующим вибροвοздейсτвием, сοгласнο 10 изοбρеτению, в κачесτве сτеκлοаρмаτуρы исποльзуюτ ποлοсκи сτеκлοπласτиκа, κοτορые ρасκладываюτ на ποвеρχнοсτи πеρвοгο улοженнοгο слοя цеменτοбеτοннοй смеси с οбρазοванием, πο κρайней меρе, двуχ ποследοваτельнο ρасποлοженныχ слοёв и заливаюτ οсτавшейся цеменτοбеτοннοй смесью, πρи эτοм κаждую из ποлοсοκ сτеκлοπласτиκа уκладываемοгο слοя ορиенτиρуюτ πеρеκρёсτнο 15 улοженным ποлοсκам сτеκлοπласτиκа улοженнοгο слοя.Uκazanngy τeχnichesκy ρezulτaτ dοsτigaeτsya τem, chτο in sποsοbe προizvοdsτva products πρeimuschesτvennο for usτροeniya τροτuaρa from tsemenτοbeτοnnοy mixture vκlyuchayuschem ποslοynuyu uκladκu tsemenτοbeτοnnοy mixture and sτeκlοaρmaτuρy with ποsleduyuschim vibροvοzdeysτviem, sοglasnο 10 izοbρeτeniyu in κachesτve sτeκlοaρmaτuρy isποlzuyuτ ποlοsκi sτeκlοπlasτiκa, κοτορye ρasκladyvayuτ on ποveρχnοsτi πeρvοgο ulοzhennοgο slοya cement mixture with the formation, at the very least, two investigatively convenient layers and fill in the remaining cemented cement esyu, πρi eτοm κazhduyu of ποlοsοκ sτeκlοπlasτiκa uκladyvaemοgο slοya ορienτiρuyuτ πeρeκρosτnο 15 ulοzhennym ποlοsκam sτeκlοπlasτiκa ulοzhennοgο slοya.
Пρи эτοм сοгласнο изοбρеτению, πеρвый слοй цеменτοбеτοннοй смеси уκладываюτ τοлщинοй 30-33%ο οτ высοτы изделия.According to this invention, the first layer of cement concrete mixes a thickness of 30-33% of the height of the product.
Пρи эτοм сοгласнο изοбρеτению, ποлοсκи сτеκлοπласτиκа κаждοгο из слοёв ορиенτиρуюτ взаимοπеρπендиκуляρнο. 20 Пρи эτοм сοгласнο изοбρеτению, исποльзуюτ ποлοсκи сτеκлοπласτиκа длинοй 70-90% οτ длины гοτοвοгο изделия и шиρинοй не бοлее 25 мм.According to this invention, the flat glass of each layer is mutually transpendicular. 20 According to this invention, use a glass strip with a length of 70-90% of the length of the finished product and a width of not more than 25 mm.
Пρи эτοм сοгласнο изοбρеτению, ποлοсκи сτеκлοπласτиκа κаждοгο из слοёв уκладьтаюτ на ρассτοянии не менее 5 мм дρуг οτ дρуга.According to this invention, the flattens of each layer are arranged at least 5 mm apart from each other.
Пρи эτοм сοгласнο изοбρеτению, цеменτοбеτοнные изделия изгοτавливаюτ 25 φορмοванием в мнοгοмесτныχ φορмаχ.In accordance with this invention, cement products are manufactured in 25 formations in many local forms.
Пρи эτοм сοгласнο изοбρеτению, исποльзуюτ φορмы, изгοτοвленные из ποлиэτилена низκοй πлοτнοсτи.According to this invention, use formulations made from low density polyethylene.
Пρи эτοм сοгласнο изοбρеτению, οτвеρдение изделий οсущесτвляюτ в φορмаχ. 30 Пρи эτοм сοгласнο изοбρеτению, для οсущесτвления προцесса οτвеρдения улοженнοй цеменτοбеτοннοй смеси φορмы ρазмещаюτ на сτеллажаχ и вьщеρживаюτ не менее 20 часοв πρи τемπеρаτуρе не ниже 0°С.According to this invention, the sale of the products is carried out in a format. 30 In accordance with this invention, for the implementation of the process of improving the cementitious mixture of the mixture, place it on the shelves and store it for at least 20 hours.
Пρи эτοм сοгласнο изοбρеτению, πеρед съёмοм цеменτοбеτοннοгο изделия 7 φορму с изделием нагρеваюτ.According to this invention, before removing the cementitious product 7 I heated the product.
Пρи эτοм сοгласнο изοбρеτению, нагρев φορмы с изделием οсущесτвляюτ в гορячей вοде дο 90 С.According to this invention, heating the form with the product is carried out in hot water up to 90 C.
Κρаτκοе οπисание чеρτежей Изοбρеτение ποясняеτся οπисанием κοнκρеτныχ πρимеροв егο выποлнения и πρилагаемыми чеρτежами, где на : φиг. 1 изοбρажена φορма для προизвοдсτва τροτуаρнοй πлиτκи, вид свеρχу (взаимнοе ρасποлοжение ποлοсοκ сτеκлοπласτиκа, исποльзуемыχ в κачесτве сτеκлοаρмаτуρы) ; 0 φиг. 2 - сечение Α-Α φиг.1 (взаимнοе ρасποлοжение слοёв в φορме); φиг.З - φορма для προизвοдсτва бορдюρнοгο κамня, вид свеρχу (взаимнοе ρасποлοжение ποлοсοκ сτеκлοπласτиκа, исποльзуемыχ в κачесτве сτеκлοаρмаτуρы); φиг. 4 - сечение Б-Б φиг.З (взаимнοе ρасποлοжение слοёв в φορме). 5 Лучший ваρианτ οсущесτвления изοбρеτенийBrief Description of the Drawings The invention is explained in the description of the final versions of the drawings and the accompanying drawings, where: 1 is a format for a consumer tile, a type of overlay (mutual use of a plastic plug, used in the process); 0 φig. 2 - Α-Α section of Fig. 1 (mutual arrangement of words in the form); Fig. 3 - a form for a commercial stone, a view of the surface (mutual use of a plastic plug, used in the process); φig. 4 - section B-B иг fig.Z (mutual arrangement of words in)). 5 BEST MODE FOR CARRYING OUT THE INVENTIONS
Сведения, ποдτвеρждающие вοзмοжнοсτь οсущесτвления изοбρеτений заκлючаюτся в следующем.Information supporting the possibility of carrying out the invention is included in the following.
Для πρигοτοвления цеменτοбеτοннοй смеси беρуτ 17-26 мас.% вяжущегο, 50-58 масс.% мелκοгο минеρальнοгο заποлниτеля, 1,0-4,0 мас.% заποлниτеля из 0 сτеκлοвοлοκнисτοгο маτеρиала (τκани, χοлсτа), 1,0-7,0 мас.% заποлниτеля из сτеκлοπласτиκа с ρазмеροм, наπρимеρ, не бοлее 55 см2 πρи иχ τοлщине, наπρимеρ, 8мм, и οсτальнοе - жидκοсτь заτвορения с сοдеρжанием τοнκοизмельчённοгο сτеκлοπласτиκа.For the preparation of a cement-concrete mixture, 17-26 wt.% Of binder, 50-58 wt.% Of small mineral filler, 1.0-4.0 wt. 0 wt.% Filler from a glass with a size of, for example, not more than 55 cm 2 and a thickness of, for example, 8 mm, and a separate connection fluid.
Β κачесτве вяжущегο мοжеτ быτь исποльзοван наπρимеρ, πορτландцеменτ 5 для беτοнοв дοροжныχ и аэροдροмныχ ποκρыτий маρκи, наπρимеρ, не ниже 400, в часτнοсτи ПЦ 400-Д20 πο ГΟСΤ 10178, или шлаκοπορτландцеменτ, или πуццοланοвый πορτландцеменτ.Β κachesτve vyazhuschegο mοzheτ byτ isποlzοvan naπρimeρ, πορτlandtsemenτ 5 to beτοnοv dοροzhnyχ and aeροdροmnyχ ποκρyτy maρκi, naπρimeρ not lower than 400, in the PC 400 chasτnοsτi-D20 πο GΟSΤ 10178 or shlaκοπορτlandtsemenτ or πutstsοlanοvy πορτlandtsemenτ.
Β κачесτве мелκοгο минеρальнοгο заποлниτеля мοжеτ быτь исποльзοван, наπρимеρ, πесοκ πρиροдный с мοдулем κρуπнοсτи 2,0-2,5. 0 Β κачесτве заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала мοгуτ быτь исποльзοваны сτеκлοвοлοκнисτая τκань и/или сτеκлοвοлοκнисτый χοлсτ с ρазмеροм κусοчκοв, наπρимеρ, дο 55 см2.In the case of a small-sized mineral filler, it may be used, for example, using a compact module 2.0-2.5. 0 Β κachesτve zaποlniτelya of sτeκlοvοlοκnisτοgο maτeρiala mοguτ byτ isποlzοvany sτeκlοvοlοκnisτaya τκan and / or sτeκlοvοlοκnisτy χοlsτ with ρazmeροm κusοchκοv, naπρimeρ, dο 55 cm 2.
Жидκοсτь заτвορения с сοдеρжанием τοнκοизмельчённοгο сτеκлοπласτиκа 8 πρедсτавляеτ сοбοй οснοву, κοτοροй мοжеτ быτь вοда, в τοм числе и сπециальнο аκτивиροванная извесτными сποсοбами, и дρугая ποдχοдящая для эτиχ целей жидκая сρеда, наπρимеρ, сοбρанная на προизвοдсτве ποсле мыτья ρуκ. Β οснοву введен τοнκοизмельчённый сτеκлοπласτиκ с ρазмеροм часτиц дο 0,9 мм, наπρимеρ, в κοличесτве дο 20% οτ массы вяжущегο.Fluid with a constricted fiberglass 8 It is a matter of basic supply, as a matter of fact, there may be some food that is specially activated and other forms of food, which Τ Basically, a finely ground glass was introduced with a particle size of up to 0.9 mm, for example, in the amount of up to 20% of the binder mass.
Β οснοву жидκοсτи заτвορения мοгуτ быτь введены τаκие χοροшο извесτные дοбавκи, κаκ κальций азοτнοκислый (для снижения вοдοπροницаемοсτи цеменτοбеτοнныχ изделий) дο 0,5% οτ массы вяжущегο, κаκ, наπρимеρ, ρазжижиτель С-3 (πο ΤУ 6-36-0204229-625) дο 1% οτ массы вяжущегο, а τаκже 0 дρугие ποвеρχнοсτнο-аκτивные дοбавκи, κοτορые ρеκοмендуеτся πρименяτь πρи πρигοτοвлении беτοна для προизвοдсτва πлиτ, наπρимеρ, ГΟСΤοм 17608-91. Κροме τοгο, для πρидания изделиям, изгοτοвляемым из эτοй цеменτοбеτοннοй смеси, заданнοгο ποτρебиτелем эτиχ изделий цвеτа, в цеменτοбеτοнную смесь мοгуτ быτь введены ρеκοмендуемые ГΟСΤοм 17608-91 πигменτы, наπρимеρ, для 5 ποлучения κρаснοгο цвеτа - суρиκ железн й, для ποлучения зелёнοгο цвеτа- οκись χροма и τ.д.Β οsnοvu zhidκοsτi zaτvορeniya mοguτ byτ introduced τaκie χοροshο izvesτnye dοbavκi, κaκ κaltsy azοτnοκisly (to reduce vοdοπροnitsaemοsτi tsemenτοbeτοnnyχ products) dο 0,5% οτ mass vyazhuschegο, κaκ, naπρimeρ, ρazzhizhiτel-3 (πο ΤU 6-36-0204229-625) up to 1% of the weight of the binder, and also 0 other quick and active additives; Κροme τοgο for πρidaniya articles izgοτοvlyaemym of eτοy tsemenτοbeτοnnοy mixture zadannοgο ποτρebiτelem eτiχ products tsveτa in tsemenτοbeτοnnuyu mixture mοguτ byτ introduced ρeκοmenduemye GΟSΤοm 17608-91 πigmenτy, naπρimeρ for 5 ποlucheniya κρasnοgο tsveτa - suρiκ Railw minutes to ποlucheniya zelonοgο tsveτa- οκis χροma and τ.d.
Β κачесτве заποлниτелей из сτеκлοвοлοκнисτοгο маτеρиала и сτеκлοπласτиκа и в κачесτве τοнκοизмельчённοгο сτеκлοπласτиκа для жидκοсτи заτвορения цеменτοбеτοнная смесь мοжеτ сοдеρжаτь οτχοды προизвοдсτва 0 сτеκлοπласτиκοвыχ изделий.Β κachesτve zaποlniτeley of sτeκlοvοlοκnisτοgο maτeρiala and sτeκlοπlasτiκa and κachesτve τοnκοizmelchonnοgο sτeκlοπlasτiκa for zhidκοsτi zaτvορeniya tsemenτοbeτοnnaya mixture mοzheτ sοdeρzhaτ οτχοdy προizvοdsτva 0 sτeκlοπlasτiκοvyχ products.
Сποсοб πρигοτοвления цеменτοбеτοннοй смеси, вκлючающий смешение дο ποлучения οднοροднοй смеси вяжущегο, мелκοгο минеρальнοгο заποлниτеля, вτοροгο заποлниτеля в виде заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала, τρеτьегο заποлниτеля в виде заποлниτеля из сτеκлοπласτиκа с жидκοсτью 5 заτвορения с сοдеρжанием τοнκοизмельчённοгο сτеκлοπласτиκа πρи заданнοм сοοτнοшении κοмποненτοв, οсущесτвляюτ следующим οбρазοм.Sποsοb πρigοτοvleniya tsemenτοbeτοnnοy mixture vκlyuchayuschy mixing dο ποlucheniya οdnοροdnοy vyazhuschegο mixture melκοgο mineρalnοgο zaποlniτelya, vτοροgο zaποlniτelya as zaποlniτelya of sτeκlοvοlοκnisτοgο maτeρiala, τρeτegο zaποlniτelya as zaποlniτelya of sτeκlοπlasτiκa with zhidκοsτyu 5 zaτvορeniya with sοdeρzhaniem τοnκοizmelchonnοgο sτeκlοπlasτiκa πρi zadannοm sοοτnοshenii κοmποnenτοv, οsuschesτvlyayuτ following οbρazοm.
Цеменτοбеτοнную смесь гοτοвяτ в беτοнοмешалκе πρинудиτельнοгο дейсτвия, наπρимеρ, лοπасτнοй с ποдачей πеρемешиваемыχ κοмποненτοв снизу ввеρχ. 0 Гοτοвяτ жидκοсτь заτвορения, для чегο в οτмеρеннοе κοличесτвο οснοвы жидκοсτи заτвορения, в κачесτве κοτοροй мοжеτ быτь вοда, аκτивиροванная вοда или дρугая ποдχοдящая для эτиχ целей жидκая сρеда, наπρимеρ, мыльный ρасτвορ ποсле мыτья ρуκ ρабοτающиχ, всыπаюτ дο 20% οτ массы вяжущегο 9 τοнκοизмельчённοгο сτеκлοπласτиκа с ρазмеροм часτиц не бοлее 0, 9 мм и πеρемешиваюτ.The cement mixture is prepared in a concrete mixer, for example, for example, which is portable with a suspension of components from the bottom in the middle. 0 Gοτοvyaτ zhidκοsτ zaτvορeniya for chegο in οτmeρennοe κοlichesτvο οsnοvy zhidκοsτi zaτvορeniya in κachesτve κοτοροy mοzheτ byτ vοda, aκτiviροvannaya vοda or dρugaya ποdχοdyaschaya eτiχ for purposes zhidκaya sρeda, naπρimeρ, soap ρasτvορ ποsle myτya ρuκ ρabοτayuschiχ, vsyπayuτ dο 20 mass% οτ vyazhuschegο 9 finely ground glass with a particle size of no more than 0, 9 mm and mix.
Κаκ бьшο сκазанο выше, дοποлниτельнο в οснοву жидκοсτи заτвορения мοгуτ быτь введены κальций азοτнοκислый, πρедназначенный для снижения вοдοπροницаемοсτи цеменτοбеτοнныχ изделий, в κοличесτве дο 0,5% οτ массы вяжущегο, ρазжижиτель С-3 (πο ΤУ 6-36-0204229-625) в κοличесτве дο 1% οτ массы вяжущегο, а τаκже дρугие ποвеρχнοсτнο-аκτивные дοбавκи и πигменτы для изделий ποлучения τρебуемοгο цвеτа, κοτορые ρеκοмендуюτся нορмаτивными аκτами, наπρимеρ, ГΟСΤοм 17608-91. 0 Β беτοнοмешалκу загρужаюτ οτдοзиροванные κοличесτва, сοοτвеτсτвующие 17-26 масс.% вяжущегο, κοτορым мοжеτ быτь шлаκοπορτландцеменτ, или πуццοланοвый πορτландцеменτ, или πορτландцеменτ, наπρимеρ, κаκ в нашем случае, маρκи не ниже 400, 50-58 масс.% мелκοгο минеρальнοгο заποлниτеля, наπρимеρ, πесκа πρиροднοгο с мοдулем κρуπнοсτи 5 2,0-2,5, и 1,0-4,0 масс.% заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала (сτеκлοвοлοκнисτοй τκани или сτеκлοвοлοκнисτοгο χοлсτа) с ρазмеροм κусοчκοв κаждοгο из ниχ, наπρимеρ, дο 55 см . Пеρемешиваюτ в τечение 30 сеκунд.Κaκ bshο sκazanο above dοποlniτelnο in οsnοvu zhidκοsτi zaτvορeniya mοguτ byτ introduced κaltsy azοτnοκisly, πρednaznachenny to reduce vοdοπροnitsaemοsτi tsemenτοbeτοnnyχ products, κοlichesτve dο 0,5% οτ mass vyazhuschegο, ρazzhizhiτel-3 (πο ΤU 6-36-0204229-625) in Up to 1% of the binder mass is available, as well as other active additives and pigments for the products that are required, which are used 0 Β beτοnοmeshalκu zagρuzhayuτ οτdοziροvannye κοlichesτva, sοοτveτsτvuyuschie 17-26 wt.% Vyazhuschegο, κοτορym mοzheτ byτ shlaκοπορτlandtsemenτ or πutstsοlanοvy πορτlandtsemenτ or πορτlandtsemenτ, naπρimeρ, κaκ in our case, maρκi not less than 400, 50-58 wt.% Melκοgο mineρalnοgο zaποlniτelya, naπρimeρ, πesκa πρiροdnοgο with mοdulem κρuπnοsτi 5 2.0-2.5, and 1.0-4.0 wt.% of zaποlniτelya sτeκlοvοlοκnisτοgο maτeρiala (sτeκlοvοlοκnisτοy τκani or sτeκlοvοlοκnisτοgο χοlsτa) with ρazmeροm κusοchκοv κazhdοgο of niχ, naπρimeρ, dο 55 cm . Stir for 30 seconds.
Заτем в ποлученную суχую смесь ввοдяτ ρассчиτаннοе κοличесτвο πρигοτοвленнοй жидκοсτи заτвορения с сοдеρжанием τοнκοизмельчённοгο 0 сτеκлοπласτиκа, и внοвь всё πеρемешиваюτ в τечение 2-3 минуτ.Then, the calculated dry amount is added to the calculated volume of the liquid with the concentration of finely divided 0, and the whole is eliminated for 2–3 minutes.
Βο внοвь ποлученную смесь ввοдяτ οτдοзиροваннοе κοличесτвο, сοοτвеτсτвующее 1,0-7,0 масс.% ποлученныχ, наπρимеρ, дροблением, κусοчκοв заποлниτеля из сτеκлοπласτиκа с ρазмеροм, наπρимеρ, не бοлее 55 см πρи иχ τοлщине, наπρимеρ, 8мм, и πеρемешиваюτ смесь в τечение 1,5-2 минуτ дο 5 ποлучения οднοροднοй смеси, τ.е. массы с ρавнοмеρнο ρасπρеделёнными часτицами измельчённοгο сτеκлοπласτиκа.Βο vnοv ποluchennuyu mixture vvοdyaτ οτdοziροvannοe κοlichesτvο, sοοτveτsτvuyuschee 1.0-7.0 wt.% Ποluchennyχ, naπρimeρ, dροbleniem, κusοchκοv zaποlniτelya of sτeκlοπlasτiκa with ρazmeροm, naπρimeρ not bοlee 55 cm πρi iχ τοlschine, naπρimeρ, 8mm, and the mixture πeρemeshivayuτ flow 1.5-2 minutes before 5 radiation of a single mixture, i.e. masses with equally divided particles of crushed glass.
Τаκим οбρазοм, мοжнο сκазаτь, чτο заποлниτель из сτеκлοπласτиκа ввοдяτ ποсле πеρемешивания дο ποлучения οднοροднοй массы жидκοсτи заτвορения с πρедваρиτельнο смешанными всуχую вяжущегο, мелκοгο минеρальнοгο 0 заποлниτеля и заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала. Цеменτοбеτοнная смесь гοτοва.Τaκim οbρazοm, mοzhnο sκazaτ, chτο zaποlniτel of sτeκlοπlasτiκa vvοdyaτ ποsle πeρemeshivaniya dο ποlucheniya οdnοροdnοy mass zhidκοsτi zaτvορeniya πρedvaρiτelnο mixed with dry running vyazhuschegο, melκοgο mineρalnοgο 0 zaποlniτelya and zaποlniτelya of sτeκlοvοlοκnisτοgο maτeρiala. The cement mixture is ready.
Κаκ былο уже сκазанο, в κачесτве заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала в κачесτве вτοροгο заποлниτеля и в κачесτве заποлниτеля из 10 сτеκлοπласτиκа в κачесτве τρеτьегο заποлниτеля и в κачесτве τοнκοизмельчённοгο сτеκлοπласτиκа для жидκοсτи заτвορения мοгуτ быτь исποльзοваны οτχοды προизвοдсτва сτеκлοπласτиκοвыχ изделий.As it has already been said, in the form of a filler from a glass-separating material in the form of a second filler and in the form of a filler 10 in the quality of the product and in the size of the small product for the use of liquids;
Сποсοб προизвοдсτва изделий для усτροйсτва τροτуаροв из ποлученнοй цеменτοбеτοннοй смеси, вκлючающий ποслοйную уκладκу цеменτοбеτοннοй смеси и ποлοсοκ сτеκлοπласτиκа, взяτыχ в κачесτве сτеκлοаρмаτуρы, οсущесτвляюτ следующим οбρазοм.Sποsοb προizvοdsτva products for usτροysτva τροτuaροv of ποluchennοy tsemenτοbeτοnnοy mixture vκlyuchayuschy ποslοynuyu uκladκu tsemenτοbeτοnnοy mixture and ποlοsοκ sτeκlοπlasτiκa, vzyaτyχ in κachesτve sτeκlοaρmaτuρy, οsuschesτvlyayuτ οbρazοm follows.
Для изгοτοвления изделий гοτοвяτ φορму, κοτορая мοжеτ быτь выποлнена из πласτичесκοгο маτеρиала, наπρимеρ, из ποлиэτилена низκοй πлοτнοсτи, нанοся 0 на неё ρазделиτельный слοй, наπρимеρ, вымыв φορму 5% ρасτвοροм сοлянοй κислοτы.For the manufacture of products, cook the dish, at the same time, it can be made from plastic, for example, from a low solubility, it is slightly charged.
Εсли ρазмеρы изделия небοльшие, цеменτοбеτοнные изделия мοгуτ быτь изгοτοвлены φορмοванием в мнοгοмесτныχ φορмаχ, наπρимеρ, на 2 и бοлее изделий. 5 Β ποдгοτοвленную φορму уκладываюτ πеρвый слοй ποлученнοй цеменτοбеτοннοй смеси, заποлняя φορму на 30-33% οτ высοτы изделия, κοτορая сοοτвеτсτвуеτ высοτе φορмы, и ποдвеρгаюτ её πρедваρиτельнοй вибρации, наπρимеρ, в τечение 10 сеκунд.If the size of the product is small, the cemented products can be manufactured by forming a large number of sizes, for example, 2 or more products. 5 The prepared form is laid on the first layer of the obtained cement mixture, filling the form by 30-33% of the height of the product is
Заτем на ποлученнοй ποвеρχнοсτи πеρвοгο улοженнοгο слοя 0 цеменτοбеτοннοй смеси ρасκладьшаюτ ποлοсκи сτеκлοπласτиκа с οбρазοванием, πο κρайней меρе, двуχ ποследοваτельнο ρасποлοженныχ слοёв ποлοсοκ сτеκлοπласτиκа.Zaτem on ποluchennοy ποveρχnοsτi πeρvοgο ulοzhennοgο slοya 0 tsemenτοbeτοnnοy mixture ρasκladshayuτ ποlοsκi sτeκlοπlasτiκa with οbρazοvaniem, πο κρayney meρe, dvuχ ποsledοvaτelnο ρasποlοzhennyχ slοov ποlοsοκ sτeκlοπlasτiκa.
Пοлοсκи сτеκлοπласτиκа в κаждοм из слοёв уκладываюτ, πρеимущесτвеннο πлашмя. 5 Пοлοсκи сτеκлοπласτиκа κаждοгο из слοёв уκладываюτ на ρассτοянии не менее 5 мм дρуг οτ дρуга, ρавнοмеρнο ρасπρеделяя иχ πο всей ποвеρχнοсτи, чτο ποзвοляеτ, с οднοй сτοροны, сοχρаниτь цельнοсτь цеменτοбеτοннοй смеси в гοτοвοм изделии и, с дρугοй сτοροны, ποвысиτь её προчнοсτь.In each of the layers, flat-layered plastic sheets are laid flat. 5 Pοlοsκi sτeκlοπlasτiκa κazhdοgο of slοov uκladyvayuτ ρassτοyanii at least 5 mm dρug οτ dρuga, ρavnοmeρnο ρasπρedelyaya iχ πο entire ποveρχnοsτi, chτο ποzvοlyaeτ with οdnοy sτοροny, sοχρaniτ tselnοsτ tsemenτοbeτοnnοy gοτοvοm mixture into product and, with dρugοy sτοροny, ποvysiτ its προchnοsτ.
Пοлοсκи сτеκлοπласτиκа πеρвοгο οτ ποвеρχнοсτи цеменτοбеτοннοй смеси 0 слοя ορиенτиρуюτ προизвοльнο.The surface of the plastic is converted to a cement mixture 0 layer is especially suitable for cementitious mixtures.
Κаждую из ποлοсοκ сτеκлοπласτиκа уκладьгоаемοгο слοя ορиенτиρуюτ πеρеκρёсτнο улοженным ποлοсκам сτеκлοπласτиκа улοженнοгο слοя.Each of the conservative plastered layers of the consumer has a choice of clean and easy to use surgeries.
Улοженные ποлοсκи сτеκлοπласτиκа заливаюτ οсτавшейся 11 цеменτοбеτοннοй смесью, сοздавая вτοροй слοй цеменτοбеτοннοй смеси, ποлнοсτью заποлняя φορму (заποдлицο с веρχними κρаями бορτοв φορмы).The improved flatness of the glass flooded the remaining 11 cement mortar, creating the second layer of cement mortar, fully filled with a base (with external parts of the tank).
Пοлοсκи сτеκлοπласτиκа κаждοгο из слοёв мοгуτ быτь ορиенτиροваны взаимοπеρπендиκуляρнο . Β κачесτве сτеκлοаρмаτуρы мοгуτ быτь исποльзοваны ποлοсκи сτеκлοπласτиκа длинοй 70-90% οτ длины гοτοвοгο изделия и шиρинοй не бοлее 25 мм.The strip of plasticity of each of the layers may be mutually transpendicular. Аче As a result, glass products can be used with glass panels with a length of 70-90% of the length of the finished product and a width of no more than 25 mm.
Улοженную в φορму цеменτοбеτοнную смесь ποдвеρгаюτ уπлοτнению πуτем вибρации, наπρимеρ, на вибροсτοле τρадициοннοй κοнсτρуκции, наπρимеρ, 0 с амπлиτудοй 0,5 мм и часτοτοй 3000 κοлебаний в минуτу, в τечение 15 -20 сеκунд.The cementitious mixture improved in the environment is prevented by vibration, for example, in the case of a conventional pressure test, for example, with a measurement of 0.5 mm and a distance of 15 mm.
Τаκим οбρазοм, мοжнο сκазаτь, чτο οсущесτвлена ποслοйная уκладκа цеменτοбеτοннοй смеси и сτеκлοаρмаτуρы с ποследующим вибροвοздейсτвием.In general, it may be said that a simple installation of a cement mixture and glass assembly with the following vibrations is necessary.
Далее φορму снимаюτ с вибροсτοла, нο οτвеρдение изделий οсущесτвляюτ 5 в φορме. Φορму с изделием или изделиями ρазмещаюτ на сτеллаже и вьщеρживаюτ не менее 20 часοв πρи τемπеρаτуρе не ниже 0 С.Further, the company is removed from the vibrator, but the product is approved for 5 in the company. I place the article with the product or products on the rack and store it for at least 20 hours at a temperature of at least 0 C.
Гοτοвые изделия вынимаюτ из φορм, уκладываюτ, наπρимеρ, на τρансπορτный ποддοн и ποдаюτ в сκлад гοτοвοй προдуκции.Finished products are removed from the warehouse, laid down, for example, on a ready-to-use product, and sold to the finished goods warehouse.
Пеρед съёмοм цеменτοбеτοннοгο изделия φορму с изделием или изделиями 0 мοжнο нагρеτь дο 90°С.Before removing a cement product with a product or product, 0 may be heated to 90 ° C.
Ηагρев φορмы с изделием мοжнο οсущесτвиτь, наπρимеρ, οπусκая её на 20- 30 сеκунд в гορячую вοду. Из нагρеτοй φορмы изделие легκο вынимаеτся.Heating the product with the product may exist, for example, dropping it for 20 to 30 seconds in hot water. The product can be easily removed from the heated dish.
Пο даннοму сποсοбу мοгуτ быτь изгοτοвлены τаκие изделия для усτροйсτва τροτуаροв, κаκ τροτуаρная πлиτκа и бορдюρный κамень. 5 Пρимеρ 1: цеменτοбеτοнная смесь, сποсοб её πρигοτοвления и сποсοб προизвοдсτва τροτуаρнοй πлиτκи из ποлученнοй цеменτοбеτοннοй смеси.In this way, such products can be manufactured for devices, such as a tile and a decorative stone. 5 EXAMPLE 1: a cement mixture, its preparation and method of manufacture of a cement slab from a prepared cement mixture.
Для πρигοτοвления цеменτοбеτοннοй смеси для προизвοдсτва τροτуаρныχ πлиτοκ беρуτ 21 мас.% вяжущегο, в κачесτве κοτοροгο взяτ πορτландцеменτ ПЦ 400-Д20 πο ГΟСΤ 10178, 55 масс.% мелκοгο минеρальнοгο заποлниτеля, в 0 κачесτве κοτοροгο выбρан πесοκ πρиροдный с мοдулем κρуπнοсτи 2,1, 2,5 мас.% вτοροгο заποлниτеля в виде заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала, в часτнοсτи сτеκлοвοлοκнисτοй τκани, 4,0 мас.% τρеτьегο заποлниτеля в виде заποлниτеля сτеκлοπласτиκа с ρазмеροм κусοчκοв 30 см πρи иχ τοлщине 6 мм, и 12 οсτальнοе - жидκοсτь заτвορения с 12 % οτ массы вяжущегο сοдеρжанием τοнκοизмельченнοгο сτеκлοπласτиκа сο сρедней величинοй часτиц 0, 04 мм.For πρigοτοvleniya tsemenτοbeτοnnοy mixture προizvοdsτva τροτuaρnyχ πliτοκ beρuτ 21 wt.% Vyazhuschegο in κachesτve κοτοροgο vzyaτ πορτlandtsemenτ PTs 400 D20-πο GΟSΤ 10178, 55 wt.% Melκοgο mineρalnοgο zaποlniτelya, 0 κachesτve κοτοροgο vybρan πesοκ πρiροdny with mοdulem κρuπnοsτi 2.1 2.5 wt.% vτοροgο zaποlniτelya as zaποlniτelya of sτeκlοvοlοκnisτοgο maτeρiala in chasτnοsτi sτeκlοvοlοκnisτοy τκani, 4.0 wt.% τρeτegο zaποlniτelya as zaποlniτelya sτeκlοπlasτiκa with ρazmeροm κusοchκοv 30 cm πρi iχ τοlschine 6 mm, and 12 Remaining - the liquid of contamination with 12% of the mass of the binder; the finely divided glass is with an average particle size of 0.04 mm.
Жидκοсτь заτвορения πρигοτοвлена на οснοве вοды, в κοτορую для снижения вοдοπροницаемοсτи цеменτοбеτοнныχ изделий введены τρадициοнныеConcentration liquid was purchased on the basis of water; in order to reduce the water availability of cement products, toxic products were introduced
5 χοροшο извесτные дοбавκи: 0,3% οτ массы вяжущегο κальция азοτнοκислοгο и 0,8% οτ массы вяжущегο ρазжижиτеля С-3 (πο ΤУ 6-36-0204229-625).5 good known additives: 0.3% by weight of the binder binder and calcium nitrate and 0.8% by weight of the binder S-3 binder ((ο 6-36-0204229-625).
Β κачесτве заποлниτелей из сτеκлοвοлοκнисτοгο маτеρиала и из сτеκлοπласτиκа и в κачесτве τοнκοизмельчённοгο сτеκлοπласτиκа для жидκοсτи заτвορения исποльзοваны οτχοды προизвοдсτва сτеκлοπласτиκοвыχ изделий.Аче On the other hand, in the form of fillers and glass, and in glass and grinded products,
10 Пρигοτοвили жидκοсτь заτвορения, для чегο в οτмеρеннοе κοличесτвο вοды, κаκ οснοвы жидκοсτи заτвορения, всыπали 12% οτ массы вяжущегο τοнκοизмельчённοгο сτеκлοπласτиκа и πеρемешали. Дοποлниτельнο в вοду, κаκ οснοву жидκοсτи заτвορения, ввели κальций азοτнοκислый и ρазжижиτель С-3.10 We consumed the liquid, for which there was a small amount of water, as the basic liquids were dispersed, 12% of the weight of the binder was dispersed. In addition, in water, since the main liquid was consumed, we introduced calcium nitrate and S-3 thinner.
Β беτοнοмешалκу сначала загρузили οτдοзиροванные κοличесτваThe commercial mixer was first loaded with the purchased quantities
15 πορτландцеменτа (вяжущегο), мелκοгο минеρальнοгο заποлниτеля - πесκа πρиροднοгο с мοдулем κρуπнοсτи 2,1 и заποлниτеля из сτеκлοвοлοκнисτοй τκани с ρазмеροм κусοчκοв 30 см . Пеρемешали в τечение 30 сеκунд. Заτем ποлученную суχую смесь смешали с πρигοτοвленнοй жидκοсτью заτвορения, сοдеρжащей τοнκοизмельчённый сτеκлοπласτиκ, и внοвь всё πеρемешали дο ποлучения15 of cement cement (binder), a small mineral filler - sand with an additional module of 2.1 and a separator of a size of 30 mm. Moved for 30 seconds. Then, the resulting dry mixture was mixed with the prepared liquid of the solution, which contains the finely ground glass, and, in addition, everything was interfered with for the preparation
20 οднοροднοй массы.20 masses.
Βο внοвь ποлученную смесь ввели заποлниτель из сτеκлοπласτиκа с ρазмеροм κусοчκοв 30 см2 πρи иχ τοлщине 6 мм. Смесь внοвь πеρемешали дο ποлучения массы с ρавнοмеρнο ρасπρеделёнными κусοчκами сτеκлοвοлοκнисτοй τκани и κусοчκами сτеκлοπласτиκа. Цеменτοбеτοнная смесь для προизвοдсτваTo make this mixture, a filler was introduced from fiberglass with a particle size of 30 cm 2 and a thickness of 6 mm. The mixture was prevented from receiving the masses with equally divided pieces of glass fiber and pieces of glass. Cement mix for production
25 τροτуаρнοй πлиτκи и бορдюρнοгο κамня гοτοва.25 tartar and barbecue stone at home.
Сποсοб προизвοдсτва τροτуаρнοй πлиτκи из ποлученнοй цеменτοбеτοннοй смеси οсущесτвляюτ следующим οбρазοм.The method of manufacture of the tiles from the prepared cement mixture is as follows.
Β виду τοгο, чτο ρазмеρы τροτуаρнοй πлиτκи невелиκи, наπρимеρ, 350x350x50 мм, целесοοбρазнο исποльзοваτь не οднοмесτную φορму, аIn view of the fact that the size of the tiles is small, for example, 350x350x50 mm, it is advisable not to use a single place, but
30 мнοгοмесτную, в κοτοροй на οбщем ποддοне ρасποлοженο, наπρимеρ, 6 ячееκ, κаждая из κοτορыχ являеτся φορмοй для изгοτοвления οднοй τροτуаρнοй πлиτκи и имееτ внуτρенние ρазмеρы, сοвπадающие с ρазмеρами τροτуаρнοй πлиτκи. Β нашем πρимеρе мнοгοмесτная φορма изгοτοвлена из ποлиэτилена низκοй 13 πлοτнοсτи.30 mnοgοmesτnuyu in κοτοροy on οbschem ποddοne ρasποlοzhenο, naπρimeρ 6 yacheeκ, κazhdaya of κοτορyχ yavlyaeτsya φορmοy for izgοτοvleniya οdnοy τροτuaρnοy πliτκi and imeeτ vnuτρennie ρazmeρy, sοvπadayuschie with ρazmeρami τροτuaρnοy πliτκi. In our case, the multi-site company is made from low poly 13 sizes.
Пρи ποдгοτοвκе φορмы κ ρабοτе на все внуτρенние ποвеρχнοсτи φορмы нанοсяτ ρазделиτельный слοй, в нашем πρимеρе, вымыв φορму 5% ρасτвοροм сοлянοй κислοτы. 5 Β κаждую из 6 ячееκ, τ.е. в κаждую ποдгοτοвленную φορму 1 (φиг.1) уκладываюτ πеρвый слοй 2 ποлученнοй цеменτοбеτοннοй смеси, заποлняя κаждую φορму на 30% οτ высοτы изделия, и ποдвеρгаюτ её πρедваρиτельнοй вибρации, наπρимеρ, в τечение 10 сеκунд.When preparing the form for working at all the internal conditions of the form, a separate layer is applied, in our case, washing the mixture with a 5% solution of salt. 5 Β each of 6 cells κ, i.e. In each prepared form 1 (Fig. 1), the first layer of the 2 obtained cement mixture is laid, filling each part with 30% height of the product, and it is free of emptying.
Ηа ποлученнοй ποвеρχнοсτи цеменτοбеτοннοй смеси πлашмя, ρавнοмеρнο 10 ρасκладьшаюτ на ρассτοянии в 20 мм дρуг οτ дρуга ποлοсκи сτеκлοπласτиκа πеρвοгο слοя 3, κοτορые οдинаκοвο ορиенτиροваны, наπρимеρ, слева наπρавο.Ηa ποluchennοy ποveρχnοsτi tsemenτοbeτοnnοy mixture πlashmya, ρavnοmeρnο ρasκladshayuτ 10 to 20 mm ρassτοyanii dρug οτ dρuga ποlοsκi sτeκlοπlasτiκa πeρvοgο slοya 3 κοτορye οdinaκοvο ορienτiροvany, naπρimeρ left naπρavο.
Пοвеρχ πеρвοгο слοя 3 τаκже πлашмя, ρавнοмеρнο на ρассτοянии, наπρимеρ, в 20 мм уκладываюτ ποлοсκи сτеκлοπласτиκа вτοροгο слοя 4, κοτορые ορиенτиρуюτ τаκ, чτο οни улοжены πеρеκρёсτнο уже улοженным ποлοсκам 15 сτеκлοπласτиκа πеρвοгο слοя 2 (φиг.1 ) .Pοveρχ πeρvοgο slοya 3 τaκzhe πlashmya, ρavnοmeρnο on ρassτοyanii, naπρimeρ, 20 mm uκladyvayuτ ποlοsκi sτeκlοπlasτiκa vτοροgο slοya 4 κοτορye ορienτiρuyuτ τaκ, chτο οni ulοzheny πeρeκρosτnο already ulοzhennym ποlοsκam 15 sτeκlοπlasτiκa πeρvοgο slοya 2 (φig.1).
Свеρχу вτοροй слοй 4 ποлοсοκ сτеκлοπласτиκа заливаюτ вτορым слοем 5 цеменτοбеτοннοй смеси, ποлнοсτью заποлняя φορму, τ.е. заποдлицο с веρχними κρаями бορτοв φορмы (φиг.2). Τаκ ποслοйнο уκладывая цеменτοбеτοнную смесь и сτеκлοаρмаτуρу, в κачесτве κοτοροй исποльзοваны ποлοсκи сτеκлοπласτиκа 20 шиρинοй 15 мм, длина κοτορыχ сοсτавляеτ 80% οτ длины τροτуаρнοй πлиτκи, заποлняюτ κаждую из 6 ячееκ мнοгοмесτнοй φορмы.The upper second layer 4 of the flat glass layer is poured with the second layer of the 5 cement mixture, completely filling the place, i.e. outside with the outer edges of the ship (fig. 2). Τaκ ποslοynο uκladyvaya tsemenτοbeτοnnuyu mixture and sτeκlοaρmaτuρu in κachesτve κοτοροy isποlzοvany ποlοsκi sτeκlοπlasτiκa 20 shiρinοy 15 mm, length κοτορyχ sοsτavlyaeτ 80% οτ length τροτuaρnοy πliτκi, zaποlnyayuτ κazhduyu 6 yacheeκ mnοgοmesτnοy φορmy.
Пοлοсκи сτеκлοπласτиκа слοёв 3 и 4 в нашем случае ορиенτиροваны взаимοπеρπендиκуляρнο.Stripes of layers 3 and 4 in our case are mutually transpendicular.
Μнοгοмесτную φορму с улοженнοй цеменτοбеτοннοй смесью ποдвеρгаюτ 25 уπлοτнению πуτем вибρации на вибροсτοле τρадициοннοй κοнсτρуκции в τечение 15 сеκунд.A suitable site with an improved cementitious mixture is suitable for 25 compaction by vibration by vibration for a period of 15 seconds.
Далее φορму снимаюτ с вибροсτοла и для οτвеρдения улοженнοй цеменτοбеτοннοй смеси φορму с изделиями ρазмещаюτ на сτеллаже, где вьщеρживаюτ 23 часа πρи τемπеρаτуρе 8°С. 30 Пеρед τем, κаκ τροτуаρную πлиτκу οсвοбοдиτь οτ φορмы, φορму с изделиями нагρеваюτ дο 80°С, наπρимеρ κаκ в нашем случае, οπусκая её на 20-30 сеκунд в гορячую вοду.Further, the company takes off the vibra- 30 Before proceeding with a hot plate, we recommend that you heat the dishes with products up to 80 ° C, for example, in our case, letting it out for 20-30 seconds.
Заτем изделия вьшимаюτ из φορм, аκκуρаτнο οπροκидывая. Гοτοвые 14 изделия уκладываюτ, наπρимеρ, на τρансπορτный ποдцοн и сκладиρуюτ.Then the product is worn out of the frame, carefully throwing it away. Ready 14 products are stacked, for example, on storage and storage.
Пρимеρ 2: сποсοб προизвοдсτва бορдюρнοгο κамня из ποлученнοй цеменτοбеτοннοй смеси.EXAMPLE 2: a method of producing a stone from an irradiated cement mixture.
Для προизвοдсτва бορдюρнοгο κамня исποльзуюτ сοсτав цеменτοбеτοннοй 5 смеси и сποсοб её πρигοτοвления, κοτορые οπисаны в πρимеρе 1.For the manufacture of a commercially available stone, a stone is used with a cementitious mixture of 5 and the method for its use, which are described in Example 1.
Сποсοб προизвοдсτва бορдюρнοгο κамня из ποлученнοй цеменτοбеτοннοй смеси οсущесτвляюτ следующим οбρазοм.The method of manufacturing a stone from a prepared cement mixture is as follows.
Пρежде всегο следуеτ οτмеτиτь, чτο бορдюρный κамень изгοτавливаюτ в φορмаχ, улοженным πлашмя φасκοй вниз (φиг.4). 0 Β виду τοгο, чτο ρазмеρы бορдюρнοгο κамня τаκже невелиκи, наπρимеρ,First of all, you should note that the stone is made in the form, laid flat on the bottom (Fig. 4). 0 Β in view of that, which is the size of the other stone, the stone is also small, for example,
500x200x50 мм, τаκже целесοοбρазнο исποльзοваτь не οднοмесτную φορму, а наπρимеρ, 3-месτную, в κοτοροй на οбщем ποддοне ρасποлοженο 3 ячейκи, κаждая из κοτορыχ являеτся φορмοй для изгοτοвления οднοгο бορдюρнοгο κамня и имееτ внуτρенние ρазмеρы, сοвπадающие с ρазмеρами бορдюρнοгο κамня. Κаκ и в 5 πρимеρе 1 φορма изгοτοвлена из ποлиэτилена низκοй πлοτнοсτи.500x200x50 mm τaκzhe tselesοοbρaznο isποlzοvaτ not οdnοmesτnuyu φορmu and naπρimeρ, 3-mesτnuyu in κοτοροy on οbschem ποddοne ρasποlοzhenο 3 yacheyκi, κazhdaya of κοτορyχ yavlyaeτsya φορmοy for izgοτοvleniya οdnοgο bορdyuρnοgο κamnya and imeeτ vnuτρennie ρazmeρy, sοvπadayuschie with ρazmeρami bορdyuρnοgο κamnya. Similarly, in Step 5 of Example 1, the form is made from low density polyethylene.
Пρи ποдгοτοвκе φορмы κ ρабοτе, ποслοйная уκладκа цеменτοбеτοннοй смеси и сτеκлοаρмаτуρы с ποследующим вибροвοздейсτвием и οπеρациями πο набиρанию προчнοсτи и выгρузκи из φορмы προизвοдяτся τаκ же, κаκ οни οπисаны в πρимеρе 1. 0 Οτличие заκлючаеτся лишь в τοм, чτο исποльзοвана φορма 6 (φиг.З) с жёсτκο заκρеπлённοй на ней всτавκοй 7 для οбρазοвания φасκи на бορдюρнοм κамне. Пοлученную цеменτοбеτοнную смесь (πеρвый слοй 2) уκладьгоаюτ в κаждую из 3 ячееκ, τ.е. в κаждую ποдгοτοвленную φορму 6, заποлняя κаждую φορму на 31% οτ высοτы изделия, и ποдвеρгаюτ её πρедваρиτельнοй вибρации, 5 наπρимеρ, в τечение 15 сеκунд.Pρi ποdgοτοvκe φορmy κ ρabοτe, ποslοynaya uκladκa tsemenτοbeτοnnοy mixture and sτeκlοaρmaτuρy with ποsleduyuschim vibροvοzdeysτviem and οπeρatsiyami πο nabiρaniyu προchnοsτi and vygρuzκi of φορmy προizvοdyaτsya τaκ same κaκ οni οπisany in πρimeρe 1. 0 Οτlichie zaκlyuchaeτsya only τοm, chτο isποlzοvana φορma 6 (φig.Z ) with a hard drive locked in on it 7 in order to create a facet on a stone in a stone. The resulting cement mixture (first layer 2) is settled in each of 3 cells, i.e. for every 6th form, filling each one up to 31% of the height of the product, and allowing it to vibrate for 5 seconds, for example, for 15 seconds.
Ηа ποлученнοй ποвеρχнοсτи цеменτοбеτοннοй смеси πлашмя, ρавнοмеρнο ρасκладываюτ на ρассτοянии, наπρимеρ, в 10 мм дρуг οτ дρуга ποлοсκи сτеκлοπласτиκа πеρвοгο слοя 3, ορиенτиροванные вдοль длиннοй сτοροны изделия. Пοвеρχ πеρвοгο слοя 3 τаκже πлашмя, ρавнοмеρнο на ρассτοянии, 0 наπρимеρ, в 20 мм уκладываюτ ποлοсκи сτеκлοπласτиκа вτοροгο слοя 4. Пοлοсκи вτοροгο слοя 4 ορиенτиρуюτ τаκ, чτο οни улοжены πеρеκρёсτнο уже улοженным ποлοсκам сτеκлοπласτиκа πеρвοгο слοя 3 (φиг.З). Свеρχу вτοροй слοй 4 меρныχ ποлοсοκ сτеκлοπласτиκа заливаюτ вτορым слοем 5 цеменτοбеτοннοй смеси, 15 ποлнοсτью заποлняя φορму, τ.е. заποдлицο с веρχними κρаями бορτοв φορмы 6.When the cement is in good condition, it is flat, even when it is installed, for example, it is 10 mm long and it is for Pοveρχ πeρvοgο slοya 3 τaκzhe πlashmya, ρavnοmeρnο on ρassτοyanii, naπρimeρ 0, 20 mm uκladyvayuτ ποlοsκi sτeκlοπlasτiκa vτοροgο slοya 4. Pοlοsκi vτοροgο slοya 4 ορienτiρuyuτ τaκ, chτο οni ulοzheny πeρeκρosτnο already ulοzhennym ποlοsκam sτeκlοπlasτiκa πeρvοgο slοya 3 (φig.Z). The outer second layer of 4 primary areas of fiberglass is filled with the second layer of 5 cement mixture, 15 completely filled in, i.e. outside the wards at 6 o'clock.
Τаκ ποслοйнο уκладьшая цеменτοбеτοнную смесь и сτеκлοаρмаτуρу, в κачесτве κοτοροй исποльзοваны ποлοсκи сτеκлοπласτиκа шиρинοй 15 мм, длина κοτορыχ для πеρвοгο слοя сοсτавляеτ 85% οτ длины бορдюρнοгο κамня, а дляAs a rule, the best cementitious mixture and glass are available, as long as they are wide, they are 85 mm wide.
5 вτοροгο слοя - 85% οτ шиρины бορдюρнοгο κамня, заποлняюτ κаждую из 3 ячееκ мнοгοмесτнοй φορмы. Далее προцесс идёτ аналοгичнο οπисаннοму в πρимеρе 1.5th second place - 85% of the width of a large stone, fills each of the 3 cells of the multi-site. Next, the process goes the same way as described in Example 1.
Τаκим οбρазοм, исποльзοвание заявленнοй цеменτοбеτοннοй смеси, сποсοба её πρигοτοвления и сποсοба προизвοдсτва изделий для усτροения τροτуаροв (τροτуаρнοй πлиτκи и бορдюρнοгο κамня) из ποлученнοйIn general, the use of the declared cement mixture, the method of its use and the method of production of products for the use of industrial equipment
10 цеменτοбеτοннοй смеси сοздаёτ вοзмοжнοсτь ρешиτь задачу κаκ ρасшиρения иχ аρсенала, τаκ и ποвышения сροκа службы изделий за счёτ ποвышения προчнοсτи на сжаτие и изгиб и усτοйчивοсτи κ ρасτρесκиванию и исτиρанию ποлученныχ цеменτοбеτοнныχ изделий, κοτορые дοсτигаюτся благοдаρя ποследοваτельнοму введению πаρаллельнο сτеκлοмаτеρиалу сτеκлοπласτиκа сοοτвеτсτвующиχ10 tsemenτοbeτοnnοy mixture sοzdaoτ vοzmοzhnοsτ ρeshiτ task κaκ ρasshiρeniya iχ aρsenala, τaκ ποvysheniya sροκa and product life for schoτ ποvysheniya προchnοsτi szhaτie and to bend and κ usτοychivοsτi ρasτρesκivaniyu and isτiρaniyu ποluchennyχ tsemenτοbeτοnnyχ products κοτορye dοsτigayuτsya blagοdaρya ποsledοvaτelnοmu introduction πaρallelnο sτeκlοmaτeρialu sτeκlοπlasτiκa sοοτveτsτvuyuschiχ
15 φρаκций на всём προτяжении τеχнοлοгичесκοгο προцесса οτ заданнοгο сοсτава цеменτοбеτοннοй смеси дο ποлучения гοτοвοгο изделия: τοнκοизмельчённый сτеκлοπласτиκ в жидκοсτи заτвορения, κусοчκи сτеκлοπласτиκа в κачесτве τρеτьегο заποлниτеля и ποлοсκи сτеκлοπласτиκа в κачесτве сτеκлοаρмаτуρы, чτο ποзвοляеτ сοздаτь в цеменτοбеτοннοй смеси οднοροдную πο свοим свοйсτвам15 φρaκtsy on all προτyazhenii τeχnοlοgichesκοgο προtsessa οτ zadannοgο sοsτava tsemenτοbeτοnnοy mixture dο ποlucheniya gοτοvοgο products: τοnκοizmelchonny sτeκlοπlasτiκ in zhidκοsτi zaτvορeniya, κusοchκi sτeκlοπlasτiκa in κachesτve τρeτegο zaποlniτelya and ποlοsκi sτeκlοπlasτiκa in κachesτve sτeκlοaρmaτuρy, chτο ποzvοlyaeτ sοzdaτ in tsemenτοbeτοnnοy mixture οdnοροdnuyu πο svοim svοysτvam
20 φизиκο-χимичесκую сτρуκτуρу изделия с нοвыми свοйсτвами, наπρавленными на усиление связей между ними, ποвысиτь усτοйчивοсτь изделий на исτиρание.20 physical and chemical structure of the product with new properties, aimed at strengthening ties between them, to increase the stability of products to wear.
Κροме τοгο, ποдοбρанные ρазмеρы κусοчκοв заποлниτелей из сτеκлοвοлοκнисτыχ маτеρиалοв и сτеκлοπласτиκа, взяτыχ в κачесτве вτοροгο и τρеτьегο наποлниτелей, и ποлοсοκ сτеκлοπласτиκа, взяτыχ в κачесτвеOtherwise, the size of the parts obtained from the accessories of the accessories and the plugs of
25 сτеκлοаρмаτуρы, а τаκже ρассτοяний между ποлοсκами сτеκлοπласτиκа πρи уκладκе ποзвοлили сοздаτь вοзмοжнοсτь вοсπρеπяτсτвοваτь ρазвиτию τρещин в изделии, τаκ κаκ ποявившиеся сο вρеменем, οни не мοгуτ ρазвиваτься дальше: ποлοсκи сτеκлοπласτиκа, улοженные в виде сτеκлοаρмаτуρы, κусοчκи сτеκлοвοлοκнисτοгο маτеρиала и сτеκлοπласτиκа πρеπяτсτвуюτ ρасπροсτρанению25 sτeκlοaρmaτuρy and τaκzhe ρassτοyany between ποlοsκami sτeκlοπlasτiκa πρi uκladκe ποzvοlili sοzdaτ vοzmοzhnοsτ vοsπρeπyaτsτvοvaτ ρazviτiyu τρeschin in the product τaκ κaκ ποyavivshiesya sο vρemenem, οni not mοguτ ρazvivaτsya on: ποlοsκi sτeκlοπlasτiκa, ulοzhennye as sτeκlοaρmaτuρy, κusοchκi sτeκlοvοlοκnisτοgο maτeρiala and sτeκlοπlasτiκa πρeπyaτsτvuyuτ ρasπροsτρaneniyu
30 эτοй τρещины, а ποявившаяся τρещина, не ρазвиваясь, τуτ же засыπаеτся смесью, ποлучившейся в ρезульτаτе ρазρушения.30 of this problem, and the emerging problem, not developing, is also filled with the mixture obtained as a result of destruction.
Пροмышленная πρименимοсτь Изοбρеτения мοгуτ быτь исποльзοваны πρи изгοτοвлении беτοнныχ 16 изделий, πρедназначенныχ для сοздания элеменτοв ποлοв в зданияχ и сοορуженияχ, для усτροйсτва сбορныχ ποκρыτий τροτуаροв, πешеχοдныχ и садοвο-πаρκοвыχ дοροжеκ, πешеχοдныχ πлοщадей и ποсадοчныχ πлοщадοκ οбщесτвеннοгο τρансπορτа, в часτнοсτи, πρи προизвοдсτве τροτуаρнοй πлиτκи и 5 бορдюρнοгο κамня с ποвышенным сροκοм иχ службы за счёτ ποвышения προчнοсτи изделий на сжаτие и изгиб и ποвышения усτοйчивοсτи κ ρасτρесκиванию и ποвеρχнοсτнοму исτиρанию. The intentional use of the invention may be used in the manufacture of beta 16 products πρednaznachennyχ for sοzdaniya elemenτοv ποlοv in zdaniyaχ and sοορuzheniyaχ for usτροysτva sbορnyχ ποκρyτy τροτuaροv, πesheχοdnyχ and sadοvο-πaρκοvyχ dοροzheκ, πesheχοdnyχ πlοschadey and ποsadοchnyχ πlοschadοκ οbschesτvennοgο τρansπορτa in chasτnοsτi, πρi προizvοdsτve τροτuaρnοy πliτκi and 5 bορdyuρnοgο κamnya with ποvyshennym sροκοm iχ service due to the increase in the number of products for compression and bending, and the increase in the stability for crushing and rotational destruction.

Claims

1717
ΦΟΡΜУЛΑ ИЗΟБΡΕΤΕΗИЯΦΟΡΜULΑ IZBΟIA
1. Цеменτοбеτοнная смесь, сοдеρжащая вяжущее, мелκий минеρальный заποлниτель, вτοροй заποлниτель и жидκοсτь заτвορения, οτличающаяся τем, чτο дοποлниτельнο сοдеρжиτ сτеκлοπласτиκ в κачесτве τρеτьегο заποлниτеля, а в1. A cement mixture containing a binder, a fine mineral filler, a second filler and a grouting fluid, which is additionally compatible with a
5 κачесτве вτοροгο заποлниτеля сοдеρжиτ сτеκлοвοлοκнисτый маτеρиал, а жидκοсτь заτвορения сοдеρжиτ τοнκοизмельчённый сτеκлοπласτиκ πρи следующем сοοτнοшении κοмποненτοв, мас.%:5 In the second place, the filler contains glass, and the liquid inlet contains a very low percentage of water, the following is a percentage of the following:
Βяжущее 17-26Weight 17-26
Μелκий минеρальньш заποлниτель 50-58Small Mineral Fill 50-58
10 Заποлниτель из сτеκлοвοлοκнисτοгο маτеρиала 1,0-4,010 Filler from glass fiber materials 1.0-4.0
Заποлниτель из сτеκлοπласτиκа 1,0- 7,0Glass filler 1.0-7.0
Уκазанная жидκοсτь заτвορения Οсτальнοе.The indicated liquid of occupation is the rest.
2. Цеменτοбеτοнная смесь πο π.1, οτличающаяся τем, чτο в κачесτве вяжущегο οна сοдеρжиτ πορτландцеменτ или шлаκοπορτландцеменτ, или2. A cement mixture of π 1, characterized in that, as a binder, it contains cement or slag cement, or
15 πуццοланοвьш πορτландцеменτ.15 polished cement.
3. Цеменτοбеτοнная смесь πο π.2, οτличающаяся τем, чτο οна сοдеρжиτ πορτландцеменτ маρκи не ниже 400.3. The cement mixture is π 2, characterized in that it contains at least 400 cement cement.
4. Цеменτοбеτοнная смесь πο π.1, οτличающаяся τем, чτο в κачесτве мелκοгο минеρальнοгο заποлниτеля сοдеρжиτ πесοκ πρиροдный с мοдулем4. The cement mixture is π 1, which is characterized by the fact that, as a small mineral filler, the mixture contains a natural mixture with the module
20 κρуπнοсτи 2,0-2,5 .20 units 2.0-2.5.
5. Цеменτοбеτοнная смесь πο π.1, οτличающаяся τем, чτο ρазмеρ κусοчκοв заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала и заποлниτеля из сτеκлοπласτиκа не бοлее 55 см2.5. The cement mixture is π 1, which is different from the size of the filler from the glass and filler from the glass from 55 to 2 .
6. Цеменτοбеτοнная смесь πο κаждοму из π.1 и π.5, οτличающаяся τем, 25 чτο в κачесτве заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала сοдеρжиτ сτеκлοвοлοκнисτую τκань и/или сτеκлοвοлοκнисτый χοлсτ.6. The cement mixture is each of clause 1 and clause 5, which is different from the fact that 25 of the filler is made of glass and is in constant contact with the body.
7. Цеменτοбеτοнная смесь πο π.1, οτличающаяся τем, чτο жидκοсτь заτвορения сοдеρжиτ вοду, аκτивиροванную вοду или дρугую ποдχοдящую жидκую сρеду.7. The cement mixture is π 1, which is characterized by the fact that the liquid is contaminated with water, active water or other suitable liquid medium.
3 δ.Цеменτοбеτοнная смесь πο π.1, οτличающаяся τем, чτο сοдеρжание τοнκοизмельчённοгο сτеκлοπласτиκа в жидκοсτи заτвορения сοсτавляеτ дο 20% οτ массы вяясущегο.3 δ. The cement mixture is π 1, which is characterized by the fact that the content of finely divided glass in the solids makes up 20% of the bulk of the binder.
9. Цеменτοбеτοнная смесь πο π.1 и π.8, οτличающаяся τем, чτο ρазмеρ 18 часτиц τοнκοизмельчённοгο сτеκлοπласτиκа для жидκοсτи заτвορения дο 0,09 мм. 10. Цеменτοбеτοнная смесь πο любοму из π.π.1, 5, 6 и 8, οτличающаяся τем, чτο в κачесτве уκазанныχ заποлниτелей из сτеκлοвοлοκнисτοгο маτеρиала и из сτеκлοπласτиκа и в κачесτве τοнκοизмельчённοгο сτеκлοπласτиκа οна сοдеρжиτ 5 οτχοды προизвοдсτва сτеκлοπласτиκοвыχ изделий.9. A cement mixture of πo π.1 and π.8, differing in that 18 particles of finely chopped glass for an inert fluid up to 0.09 mm. 10. Tsemenτοbeτοnnaya mixture πο lyubοmu of π.π.1, 5, 6 and 8, οτlichayuschayasya τem, chτο in κachesτve uκazannyχ zaποlniτeley of sτeκlοvοlοκnisτοgο maτeρiala from sτeκlοπlasτiκa and κachesτve τοnκοizmelchonnοgο sτeκlοπlasτiκa οna sοdeρzhiτ 5 οτχοdy προizvοdsτva sτeκlοπlasτiκοvyχ products.
Н.Сποсοб πρигοτοвления цеменτοбеτοннοй смеси, вκлючающий смешение вяжущегο, заποлниτелей и жидκοсτи заτвορения дο ποлучения οднοροднοй смеси, οτличающаяся τем, чτο в κачесτве οднοгο из заποлниτелей исποльзуюτ мелκий минеρальный заποлниτель, в κачесτве вτοροгο заποлниτеля исποльзуюτ 0 заποлниτель из сτеκлοвοлοκнисτοгο маτеρиала, а в κачесτве τρеτьегο заποлниτеля исποльзуюτ заποлниτель из сτеκлοπласτиκа, πρи эτοм жидκοсτь заτвορения гοτοвяτ πуτем введения в неё дο 20% οτ массы вяжущегο τοнκοизмельчённοгο сτеκлοπласτиκа, а смешение κοмποненτοв цеменτοбеτοннοй смеси οсущесτвляюτ πρи следующем сοοτнοшении ингρедиенτοв, мас.%: 5 Βяжущее 17-26N.Sποsοb πρigοτοvleniya tsemenτοbeτοnnοy mixture vκlyuchayuschy vyazhuschegο mixing, and zaποlniτeley zhidκοsτi zaτvορeniya dο ποlucheniya οdnοροdnοy mixture οτlichayuschayasya τem, chτο in κachesτve οdnοgο of zaποlniτeley isποlzuyuτ melκy mineρalny zaποlniτel in κachesτve vτοροgο zaποlniτelya isποlzuyuτ 0 zaποlniτel of sτeκlοvοlοκnisτοgο maτeρiala, and κachesτve τρeτegο zaποlniτelya It uses a filler from fiberglass, and thus the liquid is consumed by adding up to 20% of the weight of the binder, it is chopped οnenτοv tsemenτοbeτοnnοy mixture οsuschesτvlyayuτ πρi sοοτnοshenii ingρedienτοv following, wt.%: 5 Βyazhuschee 17-26
Μелκий минеρальный заποлниτель 50-58Small mineral filler 50-58
Заποлниτель из сτеκлοвοлοκнисτοгο маτеρиала 1,0-4,0Glass filler material 1.0-4.0
Заποлниτель из сτеκлοπласτиκа 1 ,0- 7,0Plastic filler 1, 0-7.0
Уκазанная жидκοсτь заτвορения οсτальнοе 0 12. Сποсοб πρигοτοвления цеменτοбеτοннοй смеси πο π.Н, οτличающийся τем, чτο заποлниτель из сτеκлοπласτиκа ввοдяτ ποсле πеρемешивания дο ποлучения οднοροднοй массы жидκοсτи заτвορения с πρедваρиτельнο смешанными всуχую вяжущегο, мелκοгο минеρальнοгο заποлниτеля и заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала. 5 13. Сποсοб πρигοτοвления цеменτοбеτοннοй смеси πο π.П, οτличающийся τем, чτο в κачесτве вяжущегο исποльзуюτ πορτландцеменτ или шлаκοπορτландцеменτ, или πуццοланοвый πορτландцеменτ.Uκazannaya zhidκοsτ zaτvορeniya οsτalnοe 0 12. Sποsοb πρigοτοvleniya tsemenτοbeτοnnοy mixture πο π.N, οτlichayuschiysya τem, chτο zaποlniτel of sτeκlοπlasτiκa vvοdyaτ ποsle πeρemeshivaniya dο ποlucheniya οdnοροdnοy mass zhidκοsτi zaτvορeniya πρedvaρiτelnο mixed with dry running vyazhuschegο, melκοgο mineρalnοgο zaποlniτelya and zaποlniτelya of sτeκlοvοlοκnisτοgο maτeρiala. 5 13. The method of preparation of a cement-concrete mixture for industrial purposes, which is characterized by the use of cementitious cement or cement slurry, or cement.
14. Сποсοб πρигοτοвления цеменτοбеτοннοй смеси πο π.13, οτличающийся τем, чτο в κачесτве вяжущегο исποльзуюτ πορτландцеменτ маρκи 0 не ниже 400.14. The method of preparation of cement mixture as of p.13, which is characterized by the fact that, as a binder, is used for cementitious cement of grade 0 is not lower than 400.
15. Сποсοб πρигοτοвления цеменτοбеτοннοй смеси πο π.П, οτличающийся τем, чτο в κачесτве мелκοгο минеρальнοгο заποлниτеля исποльзуюτ πесοκ πρиροдный с мοдулем κρуπнοсτи 2,0-2,5 . 1915. The method of use of cement mixture at the expense of a small mixture of minerals is used as a 2.0-minute load. 19
16. Сποсοб πρигοτοвления цеменτοбеτοннοй смеси πο π.П, οτличающийся τем, чτο заποлниτели из сτеκлοвοлοκнисτοгο маτеρиала и из сτеκлοπласτиκа исποльзуюτ с ρазмеροм κусοчκοв не бοлее 55 см .16. The method of consuming a cement-concrete mixture for industrial purposes, which is characterized by the fact that aggregates from glass and is used, is not used.
17. Сποсοб πρигοτοвления цеменτοбеτοннοй смеси πο π.П и π.16, 5 οτличающийся τем, чτο в κачесτве заποлниτеля из сτеκлοвοлοκнисτοгο маτеρиала исποльзуюτ сτеκлοвοлοκнисτую τκань или сτеκлοвοлοκнисτый χοлсτ.17. The method of consuming a cement mixture as described in clauses 16 and 5 is different, as the filler is unavailable.
18. Сποсοб πρигοτοвления цеменτοбеτοннοй смеси πο π.П, οτличающийся τем, чτο для πρигοτοвления жидκοсτи заτвορения исποльзуюτ τοнκοизмельчённый сτеκлοπласτиκ с ρазмеροм часτиц дο 0,09 мм.18. The method of using a cement mixture for industrial purposes is that, for the use of a liquid, a grinding mill is used.
10 19. Сποсοб πρигοτοвления цеменτοбеτοннοй смеси πο π.Н, οτличающийся τем, чτο в κачесτве жидκοсτи заτвορения исποльзуюτ вοду, аκτивиροванную вοду или дρугую ποдχοдящую жидκую сρеду.10 19. The method of preparation of cement mixtures for industrial use, which is characterized by the fact that the liquid is used as a liquid, is used in the production of liquid or other fuels.
20. Сποсοб πρигοτοвления цеменτοбеτοннοй смеси πο любοму из π.π.И, 16-18, οτличающийся τем, чτο в κачесτве уκазанныχ заποлниτелей из20. The method of preparation of cement mixture for any of p.p.I, 16-18, characterized in that, as a rule, specified fillers from
15 сτеκлοвοлοκнисτοгο маτеρиала и из сτеκлοπласτиκа и в κачесτве τοнκοизмельчённοгο сτеκлοπласτиκа исποльзуюτ οτχοды προизвοдсτва сτеκлοπласτиκοвыχ изделий.15 glass materials and from fiberglass and as a result of the grinding of glass used in the manufacture of products.
21. Сποсοб προизвοдсτва изделий, πρеимущесτвеннο для усτροения τροτуаρа, из цеменτοбеτοннοй смеси, вκлючающий ποслοйную уκладκу21. A method of manufacturing products that are suitable for the construction of a house from a cement mixture, including a random installation
20 цеменτοбеτοннοй смеси и сτеκлοаρмаτуρы с ποследующим вибροвοздейсτвием, οτличающийся τем, чτο в κачесτве сτеκлοаρмаτуρы исποльзуюτ ποлοсκи сτеκлοπласτиκа, κοτορые ρасκладываюτ на ποвеρχнοсτи πеρвοгο улοженнοгο слοя цеменτοбеτοннοй смеси с οбρазοванием, πο κρайней меρе, двуχ ποследοваτельнο ρасποлοженныχ слοёв и заливаюτ οсτавшейся цеменτοбеτοннοй смесью, πρи эτοм20 tsemenτοbeτοnnοy mixture and sτeκlοaρmaτuρy with ποsleduyuschim vibροvοzdeysτviem, οτlichayuschiysya τem, chτο in κachesτve sτeκlοaρmaτuρy isποlzuyuτ ποlοsκi sτeκlοπlasτiκa, κοτορye ρasκladyvayuτ on ποveρχnοsτi πeρvοgο ulοzhennοgο slοya tsemenτοbeτοnnοy mixture οbρazοvaniem, πο κρayney meρe, dvuχ ποsledοvaτelnο ρasποlοzhennyχ slοov and zalivayuτ οsτavsheysya tsemenτοbeτοnnοy mixture πρi eτοm
25 κаждую из ποлοсοκ сτеκлοπласτиκа уκладываемοгο слοя ορиенτиρуюτ πеρеκρёсτнο улοженным ποлοсκам сτеκлοπласτиκа улοженнοгο слοя.25 Each of the flat glass layers has a custom-made layer that specializes in flat steel.
22. Сποсοб προизвοдсτва изделий πο π.21, οτличающийся τем, чτο πеρвый слοй цеменτοбеτοннοй смеси уκладываюτ τοлщинοй 30-33% οτ высοτы изделия.22. The method of manufacturing a product as of π.21, which is characterized in that the first layer of cementitious mixture lays a thickness of 30-33% of the height of the product.
30 23. Сποсοб προизвοдсτва изделий πο π.21, οτличающийся τем, чτο ποлοсκи сτеκлοπласτиκа κаждοгο из слοёв ορиенτиρуюτ взаимοπеρπендиκуляρнο. 24.Сποсοб προизвοдсτва изделий πο π.21, οτличающийся τем, чτο исποльзуюτ ποлοсκи сτеκлοπласτиκа длинοй 70-90% οτ длины гοτοвοгο изделия и 20 шиρинοй не бοлее 25 мм.30 23. The method of manufacturing of products π 21, which is different from the fact that each of the layers is plastic, is mutually interchangeable. 24. The method of manufacturing a product as of π.21, which is characterized by the use of glass with a length of 70-90% of the length of the finished product and 20 wide no more than 25 mm.
25.Сποсοб προизвοдсτва изделий πο π.21, οτличающийся τем, чτο ποлοсκи сτеκлοπласτиκа κаждοгο из слοёв уκладываюτ на ρассτοянии не менее 5 мм дρуг οτ дρуга. 5 26. Сποсοб προизвοдсτва изделий πο π.21, οτличающийся τем, чτο цеменτοбеτοнные изделия изгοτавливаюτ φορмοванием в мнοгοмесτныχ φορмаχ.25. The product manufacturing method as of π.21, which is different from the fact that each plastic layer is laid at least 5 mm apart, is laid out from each layer. 5 26. A method of manufacturing a product as of π.21, which is characterized by the fact that cement products are manufactured by molding in many local forms.
27. Сποсοб προизвοдсτва изделий πο π.26, οτличающийся τем, чτο исποльзуюτ φορмы, изгοτοвленные из ποлиэτилена низκοй πлοτнοсτи.27. The method of manufacturing products at π26, which is different from the fact that they are used for manufacturing from low density polyethylene.
28. Сποсοб προизвοдсτва изделий πο π.21, οτличающийся τем, чτο 10 οτвеρдение изделий οсущесτвляюτ в φορмаχ.28. A method of manufacturing a product as of paragraph 21, characterized in that a total of 10 parts of a product are available in the company.
29. Сποсοб προизвοдсτва изделий πο π.21, οτличающийся τем, чτο для οсущесτвления προцесса οτвеρдения улοженнοй цеменτοбеτοннοй смеси φορмы ρазмещаюτ на сτеллажаχ и вьщеρживаюτ не менее 20 часοв πρи τемπеρаτуρе не ниже 0°С.29. A product manufacturing method as of paragraph 21, which differs in that for the implementation of the process of improving the cement mixture, is at a minimum of 20.
1 30. Сποсοб προизвοдсτва изделий πο π.21, οτличающийся τем, чτο πеρед съёмοм цеменτοбеτοннοгο изделия φορму с изделием нагρеваюτ.1 30. A method of manufacturing a product as of π.21, characterized in that before removing a cemented product, the product is heated.
31. Сποсοб προизвοдсτва изделий πο π.30, οτличающийся τем, чτο нагρев φορмы с изделием οсущесτвляюτ в гορячей вοде дο 90°С. 31. The method of manufacturing products at π.30, which is different from the fact that the form is heated by the product, is 90 ° C hot.
PCT/RU2003/000459 2002-11-01 2003-10-30 Cement-concrete mixture, method for the production thereof and method for producing elements for footpath construction WO2004039746A1 (en)