WO2004000529A1 - Verfahren zur herstellung von bauteilen aus hochgradig lignocellulosefaser-gefüllten thermoplasten - Google Patents
Verfahren zur herstellung von bauteilen aus hochgradig lignocellulosefaser-gefüllten thermoplasten Download PDFInfo
- Publication number
- WO2004000529A1 WO2004000529A1 PCT/EP2003/006595 EP0306595W WO2004000529A1 WO 2004000529 A1 WO2004000529 A1 WO 2004000529A1 EP 0306595 W EP0306595 W EP 0306595W WO 2004000529 A1 WO2004000529 A1 WO 2004000529A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fibers
- filled
- thermoplastic
- lignocellulose
- fiber
- Prior art date
Abstract
Description
Claims