WO2002077307A1 - Dc cast ai alloy - Google Patents
Dc cast ai alloy Download PDFInfo
- Publication number
- WO2002077307A1 WO2002077307A1 PCT/GB2002/001275 GB0201275W WO02077307A1 WO 2002077307 A1 WO2002077307 A1 WO 2002077307A1 GB 0201275 W GB0201275 W GB 0201275W WO 02077307 A1 WO02077307 A1 WO 02077307A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alloy
- heating
- present
- interannealing
- ingot
- Prior art date
Abstract
Description
Claims