WO2002060267A1 - Fünfschichtige, biaxial erstreckte, siegelfähige schlauchfolie zur verpackung und umhüllung von pastösen lebensmitteln, fleisch und fleisch mit knochen und ihre verwendung - Google Patents
Fünfschichtige, biaxial erstreckte, siegelfähige schlauchfolie zur verpackung und umhüllung von pastösen lebensmitteln, fleisch und fleisch mit knochen und ihre verwendung Download PDFInfo
- Publication number
- WO2002060267A1 WO2002060267A1 PCT/EP2001/001068 EP0101068W WO02060267A1 WO 2002060267 A1 WO2002060267 A1 WO 2002060267A1 EP 0101068 W EP0101068 W EP 0101068W WO 02060267 A1 WO02060267 A1 WO 02060267A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acid
- tubular film
- film according
- ethylene
- layer
- Prior art date
Abstract
Description
Claims