WO2002038313A1 - Systeme et procede d'injecteur de metal fondu a filtrage - Google Patents

Systeme et procede d'injecteur de metal fondu a filtrage Download PDF

Info

Publication number
WO2002038313A1
WO2002038313A1 PCT/US2000/042121 US0042121W WO0238313A1 WO 2002038313 A1 WO2002038313 A1 WO 2002038313A1 US 0042121 W US0042121 W US 0042121W WO 0238313 A1 WO0238313 A1 WO 0238313A1
Authority
WO
WIPO (PCT)
Prior art keywords
molten metal
piston
injector
cylinder
cavity
Prior art date
Application number
PCT/US2000/042121
Other languages
English (en)
Inventor
Thomas N. Meyer
Michael J. Kinosz
Nicolas Bigler
Guy Arnaud
David R. Trudel
Original Assignee
Alcoa Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Alcoa Inc. filed Critical Alcoa Inc.
Priority to PCT/US2000/042121 priority Critical patent/WO2002038313A1/fr
Priority to AU2001236434A priority patent/AU2001236434A1/en
Publication of WO2002038313A1 publication Critical patent/WO2002038313A1/fr

Abstract

L'invention concerne un système d'injecteur de métal fondu à filtrage (10) composé d'un four support (12), d'un moule de coulée (16) logé sur le four support, et d'au moins un injecteur de métal fondu (18) logé sur le fond du moule de coulée. Ledit four support contient du métal fondu alimenté (14). Ledit moule définit une cavité de moule (34) destinée à recevoir un métal fondu provenant du four support. Ledit injecteur de métal fondu fait saillie dans le four support, et comporte un cylindre (46) définissant une chemise de cavité de piston (48), et un piston alternatif (60) destiné à pomper le métal fondu vers le haut, du four support vers la cavité de moule. Le cylindre et le piston sont au moins partiellement immergés dans le métal fondu lorsque le four support contient le métal fondu. Le cylindre ou le piston comporte une admission de métal fondu (75, 84, 86, 88) destinée à recevoir le métal fondu dans la cavité de piston lorsque le four support contient du métal fondu. Un conduit (50) relie la cavité de piston à la cavité de moule. Un filtre de métal fondu (80) est logé dans le conduit lors du mouvement alternatif du piston. L'admission de métal fondu peut être une soupape reliée au cylindre, un espace formé entre le piston et une extrémité ouverte du cylindre, une ouverture définie dans la paroi latérale du cylindre, ou un clapet de retenue à bille intégré dans le piston. Un deuxième filtre de métal fondu (82) couvre de préférence l'admission de métal fondu dans l'injecteur.
PCT/US2000/042121 2000-11-09 2000-11-09 Systeme et procede d'injecteur de metal fondu a filtrage WO2002038313A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
PCT/US2000/042121 WO2002038313A1 (fr) 2000-11-09 2000-11-09 Systeme et procede d'injecteur de metal fondu a filtrage
AU2001236434A AU2001236434A1 (en) 2000-11-09 2000-11-09 Filtering molten metal injector system and method

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2000/042121 WO2002038313A1 (fr) 2000-11-09 2000-11-09 Systeme et procede d'injecteur de metal fondu a filtrage

Publications (1)

Publication Number Publication Date
WO2002038313A1 true WO2002038313A1 (fr) 2002-05-16

Family

ID=21742201

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2000/042121 WO2002038313A1 (fr) 2000-11-09 2000-11-09 Systeme et procede d'injecteur de metal fondu a filtrage

Country Status (2)

Country Link
AU (1) AU2001236434A1 (fr)
WO (1) WO2002038313A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1511866A1 (fr) * 2002-06-13 2005-03-09 Alotech Ltd Llc Appareil et procede de distribution
EP2319638A2 (fr) 2009-11-04 2011-05-11 Heinrich G. Baumgartner Machine de moulage sous pression de métal

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0381486A2 (fr) * 1989-02-01 1990-08-08 Fry's Metals Limited Dispositif et procédé de coulée
US4991641A (en) * 1990-05-07 1991-02-12 Electrovert Ltd. Method of and apparatus for metal casting
US5181551A (en) * 1991-09-25 1993-01-26 Electrovert Ltd. Double acting cylinder for filling dies with molten metal
JPH07284904A (ja) * 1994-04-21 1995-10-31 Hitachi Metals Ltd 差圧鋳造用ストーク
US5657812A (en) * 1994-11-15 1997-08-19 Bachmann Giesserei Und Formenbau Gmbh & Co. Kg Metal-casting apparatus and method

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0381486A2 (fr) * 1989-02-01 1990-08-08 Fry's Metals Limited Dispositif et procédé de coulée
US4991641A (en) * 1990-05-07 1991-02-12 Electrovert Ltd. Method of and apparatus for metal casting
US5181551A (en) * 1991-09-25 1993-01-26 Electrovert Ltd. Double acting cylinder for filling dies with molten metal
JPH07284904A (ja) * 1994-04-21 1995-10-31 Hitachi Metals Ltd 差圧鋳造用ストーク
US5657812A (en) * 1994-11-15 1997-08-19 Bachmann Giesserei Und Formenbau Gmbh & Co. Kg Metal-casting apparatus and method

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 1996, no. 02 29 February 1996 (1996-02-29) *

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1511866A1 (fr) * 2002-06-13 2005-03-09 Alotech Ltd Llc Appareil et procede de distribution
EP1511866A4 (fr) * 2002-06-13 2005-11-30 Alotech Ltd Llc Appareil et procede de distribution
EP2319638A2 (fr) 2009-11-04 2011-05-11 Heinrich G. Baumgartner Machine de moulage sous pression de métal
DE102009051879B3 (de) * 2009-11-04 2011-06-01 Baumgartner, Heinrich G. Metall-Druckgussmaschine
EP2319638A3 (fr) * 2009-11-04 2012-01-18 Heinrich G. Baumgartner Machine de moulage sous pression de métal

Also Published As

Publication number Publication date
AU2001236434A1 (en) 2002-05-21

Similar Documents

Publication Publication Date Title
EP1486276B1 (fr) Procédé et dispositif pour fabriquer des objets métalliques par coulée sous pression
US6293759B1 (en) Die casting pump
US5244033A (en) Diecasting apparatus
EP1797977A2 (fr) Coulée sous pression dans un moule de précision
EP0632244A2 (fr) Appareil pour pomper et couler des bains de fusion
EP0406559A2 (fr) Procédé et appareil de coulée par contre gravité comportant une vanne actionnée magnétiquement pour éviter tout débordement de mÀ©tal liquide
CN204700275U (zh) 建筑升降机减速机箱体低压铸造模具
JPH05505145A (ja) 低い溶融温度を有する金属合金をキャスティングするためのバルブメカニズム
US3874440A (en) Moulds for producing light alloy and other castings
KR101854968B1 (ko) 알루미늄 합금용 핫 챔버 주조기
US6578620B1 (en) Filtering molten metal injector system and method
CN113751696A (zh) 用于压铸机的铸造单元
WO2002038313A1 (fr) Systeme et procede d'injecteur de metal fondu a filtrage
US6540008B1 (en) Molten metal injector system and method
CN109290545A (zh) 一种避免铸件产生气泡的卧式压铸机
US20020121355A1 (en) Molten metal injector system and method
EP0368573B1 (fr) Méthode et appareillage pour couler des alliages métalliques à bas point de fusion
JPH0245940B2 (fr)
US20020084054A1 (en) Ball check valve molten metal injector
JPH06509512A (ja) ダイカスト機の操作方法
EP1479464A2 (fr) Machine de moulage à injection verticale à trois compartiments
WO2002038312A1 (fr) Systeme et procede d'injection de metal en fusion
CN1232370C (zh) 压铸装置
JP2002514508A (ja) 注入カップ貯蔵部を使用したインベストメント鋳造装置及びその鋳造方法
JPH06285616A (ja) 自動注湯方法及びその装置

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ CZ DE DE DK DK DM DZ EE EE ES FI FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase