WO2002016447A1 - Procede de production de polymere d'hydrocarbure alicyclique vinylique et objet moule - Google Patents

Procede de production de polymere d'hydrocarbure alicyclique vinylique et objet moule Download PDF

Info

Publication number
WO2002016447A1
WO2002016447A1 PCT/JP2001/007273 JP0107273W WO0216447A1 WO 2002016447 A1 WO2002016447 A1 WO 2002016447A1 JP 0107273 W JP0107273 W JP 0107273W WO 0216447 A1 WO0216447 A1 WO 0216447A1
Authority
WO
WIPO (PCT)
Prior art keywords
alicyclic hydrocarbon
reaction solution
polymer
hydrocarbon polymer
vinyl
Prior art date
Application number
PCT/JP2001/007273
Other languages
English (en)
Japanese (ja)
Inventor
Tsutomu Nagamune
Original Assignee
Nippon Zeon Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Zeon Co., Ltd. filed Critical Nippon Zeon Co., Ltd.
Publication of WO2002016447A1 publication Critical patent/WO2002016447A1/fr

Abstract

L'invention concerne un procédé de production d'un polymère d'hydrocarbure alicyclique vinylique consistant à chauffer une solution réactionnelle contenant un polymère d'hydrocarbure alicyclique vinylique à une pression non supérieure à la pression atmosphérique afin d'éliminer des matières volatiles par évaporation et de récupérer le polymère. Grâce à ce procédé, on peut réduire la teneur du polymère en ingrédients volatils résiduels et empêcher le polymère de subir une diminution de poids moléculaire.
PCT/JP2001/007273 2000-08-25 2001-08-24 Procede de production de polymere d'hydrocarbure alicyclique vinylique et objet moule WO2002016447A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2000255661 2000-08-25
JP2000-255661 2000-08-25

Publications (1)

Publication Number Publication Date
WO2002016447A1 true WO2002016447A1 (fr) 2002-02-28

Family

ID=18744402

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2001/007273 WO2002016447A1 (fr) 2000-08-25 2001-08-24 Procede de production de polymere d'hydrocarbure alicyclique vinylique et objet moule

Country Status (1)

Country Link
WO (1) WO2002016447A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012043708A1 (fr) 2010-09-29 2012-04-05 日本ゼオン株式会社 Copolymère bloc hydrogéné comprenant un groupe alcoxysilyle et son utilisation
JP2020117651A (ja) * 2019-01-28 2020-08-06 Ｍｃｐｐイノベーション合同会社 ミリ波モジュール及びその構成部品

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000034340A1 (fr) * 1998-12-04 2000-06-15 Nippon Zeon Co., Ltd. Polymeres hydrogenes, composition a base de resine, et procede de production d'un substrat destine a un support d'enregistrement de donnees
JP2001272534A (ja) * 2000-03-24 2001-10-05 Mitsui Chemicals Inc 偏光板用保護膜及びそれを用いてなる偏光板

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000034340A1 (fr) * 1998-12-04 2000-06-15 Nippon Zeon Co., Ltd. Polymeres hydrogenes, composition a base de resine, et procede de production d'un substrat destine a un support d'enregistrement de donnees
JP2001272534A (ja) * 2000-03-24 2001-10-05 Mitsui Chemicals Inc 偏光板用保護膜及びそれを用いてなる偏光板

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012043708A1 (fr) 2010-09-29 2012-04-05 日本ゼオン株式会社 Copolymère bloc hydrogéné comprenant un groupe alcoxysilyle et son utilisation
JP2020117651A (ja) * 2019-01-28 2020-08-06 Ｍｃｐｐイノベーション合同会社 ミリ波モジュール及びその構成部品

Similar Documents

Publication Publication Date Title
AU752141B2 (en) Vinylcyclohexane-based block copolymers
WO1996010596A1 (fr) Polymere a ouverture de cycle hydrogene
WO2004081062A1 (fr) Procede de production d'une solution de polyolefine modifiee
EP0713893A1 (fr) Polymere hydrogene a ouverture de cycle et a base de norbornene, son procede de production et son utilisation
EP2264078B1 (fr) Polymère hydrogéné à base de beta-pinène et article moulé le contenant
JPWO2003018656A1 (ja) ブロック共重合体、その製造方法、および成形体
JP3360335B2 (ja) ビニル化環状炭化水素系重合体から成る成形材料
US20090292088A1 (en) Process for production of cyclic olefin addition polymer
WO2002016447A1 (fr) Procede de production de polymere d'hydrocarbure alicyclique vinylique et objet moule
JPH06136057A (ja) 水素添加シクロペンタジエン系樹脂、その製造方法、それからなる光学材料、医療用器材、電気絶縁材料、および電子部品処理用器材
JP5682321B2 (ja) ノルボルネン系開環共重合体水素化物及びその利用
JP4447224B2 (ja) 光学材料および光学製品
TW200948835A (en) β-pipene based copolymer and producing method thereof
JPH0892357A (ja) 変性ノルボルネン系樹脂の製造方法
JP4288991B2 (ja) 重合体の精製方法
JP3277568B2 (ja) ビニル化環状炭化水素系共重合体、その水素添加物、水素添加物からなる光学材料、医療用器材、電気絶縁材料、および電子部品処理用器材
JP2010007006A (ja) ビニル脂環式炭化水素重合体の製造方法
JP2002003524A (ja) 芳香族ビニル重合体水素添加物またはシクロアルケンビニル重合体水素添加物の製造方法
JP2002003506A (ja) 芳香族ビニル重合体水素添加物またはシクロアルケンビニル重合体水素添加物の製造方法およびその原料単量体
JP2010254910A (ja) 環状オレフィン付加重合体の製造方法
JP2003082113A (ja) 非汚染性軟質樹脂成形体
JP2013048560A (ja) 培養用容器
JP2004244594A (ja) 環状共役ジエン系共重合体
JP4214686B2 (ja) 樹脂積層体及びその製造方法
JP2005290232A (ja) 開環共重合体水素化物、その製造方法および成形材料

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): JP US

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
ENP Entry into the national phase

Ref country code: JP

Ref document number: 2002 521542

Kind code of ref document: A

Format of ref document f/p: F