WO2001098018A1 - Verbindungstechnik zwischen formgedächtnis-material und stahl- oder kupfermaterial - Google Patents
Verbindungstechnik zwischen formgedächtnis-material und stahl- oder kupfermaterial Download PDFInfo
- Publication number
- WO2001098018A1 WO2001098018A1 PCT/DE2001/002154 DE0102154W WO0198018A1 WO 2001098018 A1 WO2001098018 A1 WO 2001098018A1 DE 0102154 W DE0102154 W DE 0102154W WO 0198018 A1 WO0198018 A1 WO 0198018A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alloy
- copper
- over
- mpa
- component made
- Prior art date
Abstract
Description
Claims