WO2001022779A1 - Gel utilisable au four a micro-onde contenant une matiere a changement de phase microencapsulee - Google Patents

Gel utilisable au four a micro-onde contenant une matiere a changement de phase microencapsulee Download PDF

Info

Publication number
WO2001022779A1
WO2001022779A1 PCT/US2000/040974 US0040974W WO0122779A1 WO 2001022779 A1 WO2001022779 A1 WO 2001022779A1 US 0040974 W US0040974 W US 0040974W WO 0122779 A1 WO0122779 A1 WO 0122779A1
Authority
WO
WIPO (PCT)
Prior art keywords
thermal storage
storage device
phase change
gel
gelled
Prior art date
Application number
PCT/US2000/040974
Other languages
English (en)
Inventor
Matthew T. Maguire
Original Assignee
Frisby Technologies, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Frisby Technologies, Inc. filed Critical Frisby Technologies, Inc.
Priority to AU13664/01A priority Critical patent/AU1366401A/en
Publication of WO2001022779A1 publication Critical patent/WO2001022779A1/fr

Abstract

L'invention concerne un dispositif de stockage thermique pouvant être utilisé pour chauffer ou refroidir, qui comprend un réservoir étanche aux liquides contenant une matière gélifiée, une matière contenant hydroxy, et une matière à changement de phase. La matière à changement de phase peut être microencapsulée et conférer un pouvoir de libération prolongée ou d'absorption de la chaleur. Le dispositif de stockage thermique peut être chauffé au moyen d'une source à micro-onde.
PCT/US2000/040974 1999-09-22 2000-09-22 Gel utilisable au four a micro-onde contenant une matiere a changement de phase microencapsulee WO2001022779A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU13664/01A AU1366401A (en) 1999-09-22 2000-09-22 Microwavable gel containing microencapsulated phase change material

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US40117099A 1999-09-22 1999-09-22
US09/401,170 1999-09-22

Publications (1)

Publication Number Publication Date
WO2001022779A1 true WO2001022779A1 (fr) 2001-03-29

Family

ID=23586620

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2000/040974 WO2001022779A1 (fr) 1999-09-22 2000-09-22 Gel utilisable au four a micro-onde contenant une matiere a changement de phase microencapsulee

Country Status (2)

Country Link
AU (1) AU1366401A (fr)
WO (1) WO2001022779A1 (fr)

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002076851A1 (fr) * 2001-03-27 2002-10-03 Atmosphere Controle Dispositif generateur de vapeur d'eau pour le chauffage de denrees dans un four a micro-ondes
FR2822933A1 (fr) * 2001-03-27 2002-10-04 Atmosphere Controle Dispositif generateur de vapeur d'eau apte a etre introduit dans un conditionnement pour le chauffage de denrees notamment aux micro-ondes et conditionnement renfermant un tel dispositif
FR2825631A1 (fr) * 2001-12-04 2002-12-13 Oreal Hydrogels contenant des microcapsules thermostabilisatrices
WO2003002424A2 (fr) * 2001-06-29 2003-01-09 Thermotic Developments Limited Materiau de regulation thermique
EP1492629A1 (fr) * 2002-01-23 2005-01-05 Barbara Pause Materiaux de caoutchouc silicone, leur procede de production, et leurs applications
WO2008072169A2 (fr) * 2006-12-12 2008-06-19 Koninklijke Philips Electronics N.V. Dispositif pouvant être chauffé par infrarouge, et systèmes et procédés de chauffage par infrarouge
WO2014052409A3 (fr) * 2012-09-25 2014-06-12 Cold Chain Technologies, Inc. Gel comprenant un matériau à changement de phase, procédé de préparation du gel, et équipement à échange thermique comprenant le gel
CN104069087A (zh) * 2014-07-15 2014-10-01 中国科学院理化技术研究所 一种用于微波肿瘤增敏治疗的微胶囊及其制备方法和应用
DE102013215255A1 (de) * 2013-08-02 2015-02-05 Siemens Aktiengesellschaft Elektronisches oder elektrisches Bauteil mit PCM-haltiger Kühlung
EP2806777A4 (fr) * 2012-01-25 2015-10-14 Powell Kym Dispositif de réchauffage de lingettes
GB2532269A (en) * 2014-11-14 2016-05-18 Ure Sami Phase change material filled cooking apparatus
US9598622B2 (en) 2012-09-25 2017-03-21 Cold Chain Technologies, Inc. Gel comprising a phase-change material, method of preparing the gel, thermal exchange implement comprising the gel, and method of preparing the thermal exchange implement
CN113173739A (zh) * 2020-05-09 2021-07-27 中国科学院青海盐湖研究所 一种相变混凝土及其制备方法
CN113173740A (zh) * 2020-05-09 2021-07-27 中国科学院青海盐湖研究所 一种相变保温砂浆及其制备方法
CN114634798A (zh) * 2022-01-25 2022-06-17 武汉科技大学 一种具有晶须/纤维包覆层的高温相变储热微胶囊及其制备方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5424519A (en) * 1993-09-21 1995-06-13 Battelle Memorial Institute Microwaved-activated thermal storage material; and method
US5478988A (en) * 1994-01-28 1995-12-26 Thermionics Corporation Thermal exchange composition and articles for use thereof
US5565132A (en) * 1995-06-06 1996-10-15 The University Of Dayton Thermoplastic, moldable, non-exuding phase change materials
US5722482A (en) * 1992-07-14 1998-03-03 Buckley; Theresa M. Phase change thermal control materials, method and apparatus
US5804266A (en) * 1996-03-28 1998-09-08 The University Of Dayton Microwavable thermal energy storage material

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5722482A (en) * 1992-07-14 1998-03-03 Buckley; Theresa M. Phase change thermal control materials, method and apparatus
US5424519A (en) * 1993-09-21 1995-06-13 Battelle Memorial Institute Microwaved-activated thermal storage material; and method
US5478988A (en) * 1994-01-28 1995-12-26 Thermionics Corporation Thermal exchange composition and articles for use thereof
US5565132A (en) * 1995-06-06 1996-10-15 The University Of Dayton Thermoplastic, moldable, non-exuding phase change materials
US5804266A (en) * 1996-03-28 1998-09-08 The University Of Dayton Microwavable thermal energy storage material

Cited By (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002076851A1 (fr) * 2001-03-27 2002-10-03 Atmosphere Controle Dispositif generateur de vapeur d'eau pour le chauffage de denrees dans un four a micro-ondes
FR2822933A1 (fr) * 2001-03-27 2002-10-04 Atmosphere Controle Dispositif generateur de vapeur d'eau apte a etre introduit dans un conditionnement pour le chauffage de denrees notamment aux micro-ondes et conditionnement renfermant un tel dispositif
WO2003002424A3 (fr) * 2001-06-29 2003-03-06 Thermotic Dev Ltd Materiau de regulation thermique
WO2003002424A2 (fr) * 2001-06-29 2003-01-09 Thermotic Developments Limited Materiau de regulation thermique
FR2825631A1 (fr) * 2001-12-04 2002-12-13 Oreal Hydrogels contenant des microcapsules thermostabilisatrices
EP1492629A4 (fr) * 2002-01-23 2006-02-22 Barbara Pause Materiaux de caoutchouc silicone, leur procede de production, et leurs applications
EP1492629A1 (fr) * 2002-01-23 2005-01-05 Barbara Pause Materiaux de caoutchouc silicone, leur procede de production, et leurs applications
US7488773B2 (en) 2002-01-23 2009-02-10 Barbara Hildegard Pause Material made from a silicone rubber, production process, and application
WO2008072169A2 (fr) * 2006-12-12 2008-06-19 Koninklijke Philips Electronics N.V. Dispositif pouvant être chauffé par infrarouge, et systèmes et procédés de chauffage par infrarouge
WO2008072169A3 (fr) * 2006-12-12 2008-11-27 Koninkl Philips Electronics Nv Dispositif pouvant être chauffé par infrarouge, et systèmes et procédés de chauffage par infrarouge
EP2806777A4 (fr) * 2012-01-25 2015-10-14 Powell Kym Dispositif de réchauffage de lingettes
WO2014052409A3 (fr) * 2012-09-25 2014-06-12 Cold Chain Technologies, Inc. Gel comprenant un matériau à changement de phase, procédé de préparation du gel, et équipement à échange thermique comprenant le gel
US11739244B2 (en) 2012-09-25 2023-08-29 Cold Chain Technologies, Llc Gel comprising a phase-change material, method of preparing the gel, thermal exchange implement comprising the gel, and method of preparing the thermal exchange implement
US9598622B2 (en) 2012-09-25 2017-03-21 Cold Chain Technologies, Inc. Gel comprising a phase-change material, method of preparing the gel, thermal exchange implement comprising the gel, and method of preparing the thermal exchange implement
US10829675B2 (en) 2012-09-25 2020-11-10 Cold Chain Technologies, Llc Gel comprising a phase-change material, method of preparing the gel, thermal exchange implement comprising the gel, and method of preparing the thermal exchange implement
US9556373B2 (en) 2012-09-25 2017-01-31 Cold Chain Technologies, Inc. Gel comprising a phase-change material, method of preparing the gel, and thermal exchange implement comprising the gel
DE102013215255A1 (de) * 2013-08-02 2015-02-05 Siemens Aktiengesellschaft Elektronisches oder elektrisches Bauteil mit PCM-haltiger Kühlung
CN104069087A (zh) * 2014-07-15 2014-10-01 中国科学院理化技术研究所 一种用于微波肿瘤增敏治疗的微胶囊及其制备方法和应用
GB2532269A (en) * 2014-11-14 2016-05-18 Ure Sami Phase change material filled cooking apparatus
CN113173739A (zh) * 2020-05-09 2021-07-27 中国科学院青海盐湖研究所 一种相变混凝土及其制备方法
CN113173740A (zh) * 2020-05-09 2021-07-27 中国科学院青海盐湖研究所 一种相变保温砂浆及其制备方法
CN113173739B (zh) * 2020-05-09 2022-12-06 中国科学院青海盐湖研究所 一种相变混凝土及其制备方法
CN113173740B (zh) * 2020-05-09 2022-12-13 中国科学院青海盐湖研究所 一种相变保温砂浆及其制备方法
CN114634798A (zh) * 2022-01-25 2022-06-17 武汉科技大学 一种具有晶须/纤维包覆层的高温相变储热微胶囊及其制备方法
CN114634798B (zh) * 2022-01-25 2023-06-06 武汉科技大学 一种具有晶须/纤维包覆层的高温相变储热微胶囊及其制备方法

Also Published As

Publication number Publication date
AU1366401A (en) 2001-04-24

Similar Documents

Publication Publication Date Title
CA2338509C (fr) Compresse froide gelifiante
WO2001022779A1 (fr) Gel utilisable au four a micro-onde contenant une matiere a changement de phase microencapsulee
US6079404A (en) Article for thermal energy storage
US5423996A (en) Compositions for thermal energy storage or thermal energy generation
US5630961A (en) Microwave-activated mixed-powder thermal storage material; and method
CA2124216C (fr) Agent de rechauffage/refroidissement granulaires
Mishra et al. Latent heat storage through phase change materials
US5534020A (en) Instant reusable compress
US9605874B2 (en) Phase change heat packs
PT983474E (pt) Corpo de calor latente
US5513629A (en) Microwavable heat releasing and absorbing composition and container
AU4196799A (en) Self-regulating heat pack
US5494598A (en) Heat exchange medium and articles for use thereof
GB2233081A (en) Heating or cooling device
US5245938A (en) Solid, pliable organic compound for hot/cold thermal padding material
WO1990005508A1 (fr) Ameliorations relatives a des dispositifs chauffants
US20130204333A1 (en) Powdered mix for use in therapy packs
WO1992020755A1 (fr) Support d'echange thermique et articles fabriques avec ce dernier
CA2082972A1 (fr) Reservoir thermique en materiau composite, constitue d'un compose organique pliable, plein
WO1996036199A1 (fr) Composition de poudre de chauffage par accumulation activee par micro-ondes et procede de fabrication
CA2251839C (fr) Ensemble chauffant
JPH07330038A (ja) 薬剤包装体および薬剤包装方法
CA2013097A1 (fr) Produit comprime a chaud ou a froid presentant un centre sec
JPH0480595A (ja) 蓄熱システム
CZ6826U1 (cs) Zdravotní a potravinářský obklad

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP