Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
• • A—HUMAN NECESSITIES
  • A46—BRUSHWARE
  • A46B—BRUSHES
  • A46B5/00—Brush bodies; Handles integral with brushware
  • A46B5/002—Brush bodies; Handles integral with brushware having articulations, joints or flexible portions
  • A46B5/0054—Brush bodies; Handles integral with brushware having articulations, joints or flexible portions designed to allow relative positioning of the head to body
  • A46B5/0062—Brush bodies; Handles integral with brushware having articulations, joints or flexible portions designed to allow relative positioning of the head to body being flexible or resilient during use
• • A—HUMAN NECESSITIES
  • A46—BRUSHWARE
  • A46B—BRUSHES
  • A46B5/00—Brush bodies; Handles integral with brushware
  • A46B5/02—Brush bodies; Handles integral with brushware specially shaped for holding by the hand
• • A—HUMAN NECESSITIES
  • A46—BRUSHWARE
  • A46D—MANUFACTURE OF BRUSHES
  • A46D3/00—Preparing, i.e. Manufacturing brush bodies
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
  • B29C45/14—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor incorporating preformed parts or layers, e.g. injection moulding around inserts or for coating articles
  • B29C45/14336—Coating a portion of the article, e.g. the edge of the article
  • B29C45/14385—Coating a portion of a bundle of inserts, e.g. making brushes
• • A—HUMAN NECESSITIES
  • A46—BRUSHWARE
  • A46B—BRUSHES
  • A46B2200/00—Brushes characterized by their functions, uses or applications
  • A46B2200/10—For human or animal care
  • A46B2200/1066—Toothbrush for cleaning the teeth or dentures
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
  • B29L2031/00—Other particular articles
  • B29L2031/42—Brushes
  • B29L2031/425—Toothbrush

Definitions

• a toothbrush generally includes a body having a handle portion, a head portion and bristles extending from the head portion.
• the bristles can be arranged in the form of tufts.
• a toothbrush is constructed to withstand the normal pressures exerted upon the brush during brushing of teeth and other surfaces of the oral cavity.
• Toothbrushes have been manufactured by injecting a liquid polymeric composition, e.g., polypropylene, into a mold cavity that defines a toothbrush body, whereupon the polymer composition hardens (i.e., freezes) in the form of the body of the toothbrush, e.g., the handle and head of the brush.
• a liquid polymeric composition e.g., polypropylene
• the body of the toothbrush is then transferred to a second mold cavity and a second liquid polymer composition, e.g., an elastomer, is injected into the second mold cavity to form a second portion of the brush body, e.g., the gripping member.
• the amount of time that it takes the liquid polymer composition to harden in the mold cavity is referred to as the "set time”.
• the “set time” influences the rate toothbrushes can be manufactured.
• the invention features an oral brush that includes a body that includes a) a polymer composition that includes polypropylene and that has a melt flow rate of at least about 10 g/10 min, and b) a bristle extending from the body.
• the body has a tensile strength of at least about 3100 psi.
• the body has a tensile strength of at least about 3700 psi.
• the body can have a tensile strength of from about 3700 psi to about 6,000 psi.
• the body defines a shape that includes a handle and a head extending from said handle, where the handle includes a thumb grip having a cross-sectional area no greater than about 1.8 cm 2 . In other embodiments, the body defines a shape that includes a handle and a head extending from said handle, said handle having a cross-sectional area no greater than about 1 cm 2 .
• the polymer composition has a melt flow rate of from about 10 g/10 min to about 40 g/10 min. In some embodiments, the polymer composition has a melt flow rate of from about 15 g/10 min to about 30 g/10 min. In still other embodiments, the polypropylene has a melt flow rate of in the range of from about 30 g/10 min to about 40 g/10 min.
• the polypropylene has a tensile strength of from about 4000 psi to about 6000 psi.
• the polymer composition further includes a plastomer.
• the plastomer has a melt flow rate of from about 1.3 g/10 min to about 5.2 g/10 min.
• the plastomer can have a tensile strength of from about 1500 to about 3100 psi.
• the plastomer includes a copolymer that includes ethylene and a polyalpha-olefin.
• the polymer composition can include from about 2% by weight to about 30% by weight plastomer.
• the polymer composition includes from about 10% by weight to about 20% by weight plastomer.
• the polymer composition includes from about 75% by weight to about 90% by weight polypropylene, and from about 10% by weight to about 25% by weight of plastomer.
• the invention features a process of manufacturing an oral brush body that includes injecting a polymer composition having a melt flow rate of at least 10 g/10 min into a mold cavity to form a body of the oral brush.
• the polymer composition includes polypropylene.
• the polymer composition includes a plastomer.
• the polymer composition further includes at least about 10% by weight of a plastomer.
• the polymer composition includes polypropylene and a plastomer.
• the process further includes preparing the polymer composition by combining from about 75% by weight to about 90% by weight plastomer and from about 10% by weight to about 25% by weight polypropylene.
• the invention features a process of manufacturing an oral brush that includes injecting a polymer composition having a melt flow rate of at least about 10 g/10 min into a mold cavity defining at least a portion of an oral brush body, the mold cavity that includes a plurality of bristles.
• the oral brushes of the present invention are flexible and do not break when brushing forces are exerted on the head portion of the brush.
• the oral brushes do not break when flexed in a forward direction or a reverse direction.
• the brushes can also be returned to their original form after having been bent with this force.
• the present invention enables the manufacture of brush bodies having relatively narrow regions that exhibit excellent resistance to breakage and remain flexible, yet are sufficiently rigid so as to provide a structure suitable for its intended purpose.
• the brush bodies can be molded rapidly due to the minimal set time in the injection molding operation, excellent rates of production and manufacturing efficiencies are achieved.
• FIG. 1 is a side view of a toothbrush.
• Fig. 2 is a top view of the toothbrush of Fig. 1.
• Fig. 3 is a photograph of a toothbrush positioned in a test fixture of an Instron test apparatus taken from the front side of the Instron test apparatus.
• Fig. 4 is a photograph of the front of the Instron test apparatus of Fig. 3.
• toothbrush 10 includes a body 12 that includes a handle 14, a head 16, a neck 18 between the handle and the head 16 and a thumb grip 19.
• Tufts 20, which include at least one bristle 22, extend from head 16 of body 12.
• the body can include a base, e.g., made from a relatively harder, more rigid plastic such as polypropylene, and a grip, e.g., made from a relatively rubbery material such as, e.g., styrene-ethylene-butadiene-styrene block copolymer.
• the toothbrush body exhibits a tensile strength of at least about 3100 psi, more preferably from about 3700 psi to about 6000 psi as measured according to ASTM D638.
• At least a portion of the toothbrush body (e.g., the base) includes a polymer composition that exhibits a melt flow rate of at least about 10 g/10 min, preferably from about 10 g/10 min to about 40 g/10 min, more preferably from about 12 g/10 min to about 35 g/10 min, most preferably from about 15 g/10 min to about 30 g/10 min as measured according to ASTM D1238-95.
• the toothbrush body includes a polymer composition that exhibits a melt flow rate of from about 30 g/10 min to about 40 g/10 min.
• the toothbrush body is sufficiently stiff such that it can be bent without breaking. A number of properties of the brush, when taken in combination, provide a picture of the ability of the brush body to bend, yet resist breakage.
• the maximum displacement is the maximum distance the specimen deflected during the test.
• the brush body exhibits a forward maximum displacement of at least 3 inch, and a reverse maximum displacement of at least about 2.7 in. when measured according to the Maximum Displacement Test Method below.
• a second property is the stiffness of the brush body, which can be measured by the amount of forward and reverse maximum load a brush body can withstand.
• the forward maximum load refers to the maximum amount of force applied to the brush body from the bristle surface of the brush body.
• the brush exhibits a forward maximum load to break of at least about 8.0 lbs of force, more preferably from about 9.0 lbs of force to about 12.0 lbs of force, and a reverse maximum load to break of at least about 8.0 lbs of force, more preferably from about 8.0 lbs of force to about 11.0 lbs of force when measured according to the Maximum Load Test Method below.
• a third property of the brush is energy to break the brush body as tested in forward and reverse directions.
• the brush body exhibits a forward maximum energy to break of at least about 21 lbs-in, more preferably at least about 23 lbs-in, and a reverse maximum energy to break of at least about 23 lbs-in, when measured according to the Energy to Break Test Method set forth below.
• a fourth property is the toughness of the brush body in the forward and reverse directions.
• the brush body exhibits a toughness of at least about 40 in-lbs/in 3 , more preferably at least about 44 in-lbs/in 3 , in the forward direction and a toughness of at least about 40 in-lbs/in 3 , more preferably at least about 45 in-lbs/in 3 , in the reverse direction when calculated according to the Toughness Test Method set forth below.
• the above properties preferably exist in toothbrush bodies in which the thumb grip region of the toothbrush body has a cross-sectional area no greater than 1.8 cm, preferably no greater than 1.1 cm, most preferably no greater than 1 cm.
• the polymer composition of the toothbrush body includes polypropylene.
• Polypropylene exists in a variety of forms, each of which exhibits a variety of properties.
• the body includes a polypropylene known as a controlled rheology polypropylene, and has a melt flow rate of no greater than 40 g/10 min, more preferably no greater than 30 g/10 min, and a tensile strength of at least about 3100 psi, more preferably from about 4,000 psi and 6,000 psi, most preferably at least about 4,700 psi.
• the polypropylene is formulated to harden rapidly after being injected into a mold cavity.
• the ability to harden is referred to as "set time.”
• the set time is sufficiently short so as to permit maximum utilization of the injection molding equipment.
• Preferred polypropylene is at least about 97% isotactic polypropylene.
• Suitable polypropylene is available under the trade designations FINA 3824 and FINA 3825 from Fina Oil and Chemical Company (Dallas, Texas), and PP1105 from Exxon Chemical (Houston, Texas).
• the polymer composition can include up to 100% by weight polypropylene.
• the polypropylene is present in the polymer composition in an amount of from about 75% by weight to about 90% by weight, most preferably about 85% by weight.
• the polypropylene preferably has a narrow molecular weight range.
• the polypropylene also includes a catalyst that controls the length of the polymer chain so as to produce a narrow molecular weight range of polymer. This is referred to as a controlled rheology polypropylene. Preferred catalysts also promote rapid hardening of the polypropylene after it has been injected into a mold cavity. Examples of useful catalysts include Ziegler-Natta catalysts, and Ziegler-Natta-type catalysts.
• the polymer composition of the toothbrush body can also include a plastomer. Plastomers have properties that are generally intermediate to those of thermoplastic materials and elastomeric materials. Preferably the plastomer modifies the impact properties (i.e., the reaction to a force) of the polypropylene and toothbrush bodies made therefrom.
• Preferred plastomers exhibit a melt flow rate of from about 1 g/10 min to about 5 g/10 min, more preferably from about 1.3 g/10 min to about 5.2 g/10 min, and a tensile strength of from about 1500 psi to about 3000 psi, more preferably about 2500 psi.
• useful plastomers include copolymers of ethylene and alpha-olefins, e.g., C 3 to C 20 alpha-olefin. Suitable commercial plastomers are available under the trade designation Exact 4033 from Exxon Chemical.
• plastomer When plastomer is present in the polymer composition of the toothbrush body, it is present in an amount of at least about 2% by weight, preferably from about 2% by weight to about 30% by weight, more preferably from about 10%) by weight to about 25% by weight, most preferably about 15% by weight based on the weight of the polymer composition.
• the polymer composition of the toothbrush body may also include an ethylene-alpha olefin interpolymer.
• Preferred ethylene-alpha olefin interpolymers exhibit a melt flow rate of from about 1 g/10 min to about 5 g/10 min, more preferably about 5 g/10 min, and a tensile strength of from about 1500 psi to about 3000 psi, more preferably about 1700 psi.
• Examples of commercially available ethylene-alpha olefin interpolymers are available under the FLEXOMER trade designation from Union Carbide (Danbury, Connecticut), e.g., FLEXOMER POLYOLEFLN DFDB-1085 Natural.
• an ethylene-alpha olefin interpolymer is present in the polymer composition of the toothbrush body, it is present in an amount of at least about 2% by weight, preferably from about 2% by weight to about 30% by weight, more preferably from about 10% by weight to about 25% by weight, most preferably about 15%o by weight based on the weight of the polymer composition.
• the portion of the toothbrush body that includes the polymer composition is stable to ultraviolet (UV) light such that the body is free from discoloration due UV light over the useful life of the toothbrush.
• the polymer composition of the toothbrush body can also include a variety of other components including calcium carbonate, antioxidant, pigment (e.g., titanium dioxide), dye, UV brighteners, and combinations thereof.
• Test procedures used in the examples include the following. Maximum Displacement Maximum displacement in the forward and reverse direction is determined as follows.
• the width and thickness of the brush body at the thumb grip of the brush body is measured and recorded.
• the thumb grip is the fulcrum, or point about which the free portion of the brush body rotates when a force is applied to the brush body by the Instron test apparatus.
• the width of the brush body (the width as determined from the top view (i.e., bristle surface) see Fig. 2) at the fulcrum of the brush body (e.g., along line A- A') is measured and recorded.
• the thickness of the brush body as viewed from the side of the brush body is measured at the fulcrum (e.g., along line B-B') and recorded.
• the width and thickness values are input into an Instron Model 4301 test apparatus (Instron, Canton, Massachusetts).
• the handle of the brush body is inserted in the Instron test fixture, which is attached to the Instron test apparatus, as shown in Figs. 3 and 4.
• To measure maximum displacement in the forward direction the handle is inserted into the test fixture such that the bristles face upward in the direction of the load to be applied.
• To measure maximum displacement in the reverse direction the handle is inserted into the test fixture such that the bristles face downward, away from the load to be applied.
• the handle backstop is adjusted such that the distance from the front edge of the test fixture to the tip of the brush head is 61 mm.
• the tip of the brush body is centered directly beneath the load cell, as shown in Fig. 3.
• a force is applied in a perpendicular direction to the longitudinal direction of the brush body at a cross-head speed of 0.5 in/min.
• the initial settings on the Instron test apparatus are as followings: initial load -0.5 lbs and initial extension
• the Instron test cycle is then run. A force is applied to the brush body until the brush body either breaks or reaches a bend angle of 90°. The distance the grip of the Instron test apparatus travels in the vertical direction to achieve a 90° bend in the brush body is read from the display of the Instron test apparatus and is recorded as the maximum displacement (in).
• the maximum load exerted on the brush body when bent to 90° is read from the display of the Instron test apparatus and recorded. This value is recorded as the maximum load (in lbs).
• Energy to break (E b ) of the brush body in the forward and reverse direction is determined by calculating the area under the force vs. displacement curve. The energy to break is read from the display of the Instron test apparatus and is recorded in lbs-in.
• Fina 3824 controlled rheology polypropylene (FINA-PP) (Fina Oil &
• a polymer composition was prepared according to Example 1 with the exception that the ratio FINA-PP/EXXON-PP1 was 75/25.
• EXAMPLE 3 FINA-PP and EXACT 4033 ethylene-based plastomer (EXACT 4033) (Exxon Chemical) having a melt flow rate of 1.3 g/10 min and a tensile strength of 2500 were mixed together to form a polymer composition that included 85% by weight FINA-PP and 15% by weight EXACT 4033.
• Example 4 75/25 (Example 5); 85/15 (Example 6); 80/20 (Example 7); 75/25 (Example 8).
• EXAMPLE 9 FLNA-PP, EXACT 4033, and calcium carbonate, were mixed together to form a polymer composition that included 85% by weight FLNA-PP, 15% by weight EXACT 4033, and 10% by weight calcium carbonate.
• EXAMPLE 11 A polymer composition was prepared according to Example 10 with the exception that the ratio of F NA-PP/FLEXOMER was 75/25.
• the polymer compositions of Examples 1-11 were injection molded into a into a mold cavity at 200°C.
• the mold cavity defined a toothbrush body having a thumb grip having a cross-sectional area of 1 cm.
• a reciprocating screw injection molding machine having a shot capacity of 150 grams injected the materials at temperatures between 190°C and 250°C.

Landscapes

• Engineering & Computer Science (AREA)
• Manufacturing & Machinery (AREA)
• Mechanical Engineering (AREA)
• Brushes (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Cosmetics (AREA)

Priority Applications (8)

Applications Claiming Priority (2)

Publications (1)

Family

ID=23521997

Family Applications (1)

Country Status (14)

Cited By (12)

Families Citing this family (46)

Citations (5)

Family Cites Families (24)

• 1999
  • 1999-08-31 US US09/385,578 patent/US6397425B1/en not_active Expired - Lifetime
• 2000
  • 2000-08-22 CN CNB008123128A patent/CN100396209C/zh not_active Expired - Lifetime
  • 2000-08-22 EP EP00955819A patent/EP1211961B1/en not_active Expired - Lifetime
  • 2000-08-22 AT AT00955819T patent/ATE272338T1/de not_active IP Right Cessation
  • 2000-08-22 BR BRPI0013626-3A patent/BR0013626B1/pt not_active IP Right Cessation
  • 2000-08-22 RU RU2002107995/12A patent/RU2246887C2/ru active
  • 2000-08-22 ES ES00955819T patent/ES2226904T3/es not_active Expired - Lifetime
  • 2000-08-22 WO PCT/US2000/022997 patent/WO2001015567A1/en not_active Ceased
  • 2000-08-22 DE DE60012756T patent/DE60012756T2/de not_active Expired - Lifetime
  • 2000-08-22 AU AU67959/00A patent/AU769355B2/en not_active Expired
  • 2000-08-22 MX MXPA02002147A patent/MXPA02002147A/es active IP Right Grant
  • 2000-08-22 JP JP2001519792A patent/JP2003508099A/ja active Pending
  • 2000-08-22 CA CA002381538A patent/CA2381538C/en not_active Expired - Lifetime
• 2002
  • 2002-02-06 ZA ZA200201052A patent/ZA200201052B/xx unknown

Patent Citations (5)

Also Published As

Similar Documents

Legal Events