Classifications

• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K6/00—Preparations for dentistry
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F8/00—Chemical modification by after-treatment
  • C08F8/30—Introducing nitrogen atoms or nitrogen-containing groups
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K6/00—Preparations for dentistry
  • A61K6/60—Preparations for dentistry comprising organic or organo-metallic additives
  • A61K6/65—Dyes
  • A61K6/66—Photochromic dyes
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K6/00—Preparations for dentistry
  • A61K6/60—Preparations for dentistry comprising organic or organo-metallic additives
  • A61K6/69—Medicaments
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J135/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical, and containing at least another carboxyl radical in the molecule, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Adhesives based on derivatives of such polymers
  • C09J135/08—Copolymers with vinyl ethers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2666/00—Composition of polymers characterized by a further compound in the blend, being organic macromolecular compounds, natural resins, waxes or and bituminous materials, non-macromolecular organic substances, inorganic substances or characterized by their function in the composition
  • C08L2666/28—Non-macromolecular organic substances
  • C08L2666/36—Nitrogen-containing compounds

Definitions

• the invention relates to denture adhesives and to processes for making and using denture adhesives.
• Dentures are substitutes for missing teeth and serve as a replacement for all or some of the teeth found in the oral cavity. Despite diligent efforts by dental professionals and designers of dental prostheses, dentures do not always fit perfectly. Over time, even well-fitting dentures can become ill-fitting due to natural shrinkage and changes in the gum or mucous tissues. Therefore, adherent creams, liquids or powders are often used to secure or temporarily fix dentures within the mouth.
• the denture adhesive should develop a high degree of tack upon contact with saliva so that the dentures can be held in place as soon as they are seated in the mouth. It is also highly desirable that the saliva hydrated adhesive be spread over the denture-mucosa interface in order to seal the denture in place effectively.
• the mucilage should possess sufficient cohesive strength to withstand the stresses of mastication, which may rupture the seal and thus dislodge the denture.
• the denture adhesive must also exhibit sufficient resistance to degradation under the extreme environmental changes that can occur in the oral cavity during such common actions as drinking hot or cold beverages. Of course, the adhesive must also be releasable so that the denture wearer may remove the dentures for cleaning and maintenance. Denture adhesives are generally sold as a cream, liner or strip, liquid or powder, and many examples are well known in the art.
• a popular current choice for a polymeric denture adhesive comprises a methyl vinyl ether/maleic anhydride copolymer known as "Gantrez®.” This polymer is combined with a number of other ingredients to form the final denture adhesive.
• Polymers of course, have been known for many years and have been used for many different purposes. Depending on the monomer or monomers selected, a polymer may have a vast array of properties and be useful for a number of different purposes. Once the basic constituents of the polymer or copolymer have been selected, any number of modifications may be made to affect various properties of the final polymer or copolymer.
• the chain length of the polymer may be regulated to be short or long, and, in the case of copolymers of two or more chemically distinct monomers, the order of the monomers may be regulated to form a block copolymer or an alternating copolymer or anything in between.
• the properties of the polymer or copolymer may still be modified significantly by various chemical or physical methods.
• One method of modifying the properties of a polymer or copolymer is to modify various ligands that may be present on the polymer chain.
• the anhydride group may be hydrolyzed to the corresponding dicarboxylic acid.
• the carboxylic acid in turn, may be fully or partially neutralized to form a salt or the carboxylic acid may be fully or partially esterified with various groups.
• the modification of the carboxylic acid leads to a change in the properties of the copolymer.
• the copolymer may be plasticized or otherwise modified by the addition of a cation or covalently bound ligand.
• ionic or covalent bonds may lead to crosslinking of the copolymer chains.
• a salt is formed with a divalent cation, the cation may form an ionic "cross-link" between two copolymer chains.
• Such a cross-link may be very easily dissociated in the presence of water.
• a compound contains two or more groups capable of forming an ester with a carboxylic acid ligand, then covalent cross-links may be formed between adjacent copolymer chains. These covalent cross-links may have more or less resistance to hydrolysis depending on the ligand chosen.
• Anhydride copolymers may also be used in hair spray or cosmetics; as thickening agents; and as anti-static agents for flammable liquids.
• U.S. Patent No. 5,753,215 discloses MVE/MA copolymers monoesterified with butanol and neutralized by diamines or polyvalent metal salts.
• the diamines include lysine, arginine and cystine
• the polyvalent metal salts include bromides, chlorides, nitrates, acetates, carbonates and sulphates of calcium, zinc, magnesium, barium, aluminum and zirconium.
• Anhydride copolymers have been used to support biological molecules in U.S. Patent No. 5,760,166.
• Anhydride copolymers have also been used to precipitate proteins from aqueous media in U.S. Patent Nos. 5,534,597 and 5,294,681.
• a gel-forming system useful in wound dressings contains a mixture of polymers as discussed in U.S. Patent No. 5,578,661. Another gel is discussed in U.S. Patent No. 5,521,256.
• Sodium hydroxide is added to a crosslinked MVE/MA copolymer, thereby forming a gel solution.
• Denture adhesives are not the only adhesive materials that contain anhydride copolymers.
• U.S. Patent No. 5,298,56 is directed to an adhesive useful in recycling of corrugated paper.
• Another adhesive used to help bond polymers such as ethylene or vinyl alcohol copolymers to polyolefins and polyamides, is discussed in U.S. Patent No. 5,115,033.
• An anhydride polymer is part of an electrically conductive gel composition for use in establishing a low resistance contact between an electrode and a biological body in U.S. Patent No. 5,178,143. While this gel is not, strictly speaking, an adhesive, it is made from a crosslinked, neutralized copolymer of maleic anhydride and vinyl ether.
• denture adhesive copolymers particularly MVE/MA copolymers
• covalent cross-linking is not an attractive approach to fine-tuning the desired properties of the denture adhesive.
• Covalent cross-linking can reduce the affinity of the copolymer for water, which can have an adverse effect on the properties of the copolymer for some important applications.
• Cross-linking agents have been tried with denture adhesives, including propylene glycol and glycerin in U.S. Patent No. 5,696,181.
• U.S. Patent No. 5,066,709 is directed to a bioadhesive composition comprising a MNE/MA copolymer monofunctional lactam side groups.
• a denture adhesive must consider organoleptic properties in addition to the functional aspects of a cross-linking agent.
• a certain amount of a cross-linking agent can be expected to hydrolyze in an aqueous environment such as the oral cavity, especially if the covalent cross-link is accomplished through an ester linkage.
• the cross-linking agent itself must be nontoxic at a minimum and should also not provide an unpleasant taste, texture or other sensation to the user.
• the inventors have found by raising the molecular weight of the copolymer in the denture adhesive with a cross-linked polymer or polymer salt, the denture adhesive of the present invention has improved holding performance over currently marketed denture adhesives without adversely affecting the organoleptic qualities.
• the amide linkages between the cross-linking compound and the copolymer of the present invention appear to hydrolyze relatively slowly, allowing for improved hold over a long period of time.
• the invention provides A denture adhesive comprising a safe and effective amount of a cross-linked partial copolymer salt, wherein the copolymer salt is at least partially cross-linked by amide linkages through a cross-linking agent selected from the group consisting of lysine, histidine, arginine, derivatives or family members of lysine, histidine or arginine and mixtures thereof.
• a cross-linking agent selected from the group consisting of lysine, histidine, arginine, derivatives or family members of lysine, histidine or arginine and mixtures thereof.
• the invention further provides a method of making a copolymer salt comprising the steps of cross-linking an alkyl vinyl ether/polymerizable anhydride copolymer with lysine, histidine, arginine, derivatives or family members of lysine, histidine or arginine and mixtures thereof; at least partially hydrolyzing the anhydride to form the acid and neutralizing the acid to form a salt thereof.
• a denture adhesive in accordance with the invention begins with the polymer or copolymer to be used.
• Polymers or copolymers containing acid anhydride groups are capable of forming cross-links with lysine, histidine, arginine, derivatives or family members of lysine, histidine or arginine and mixtures thereof and are within the scope of the invention to the extent that such polymers or copolymers are useful as ingredients in denture adhesives.
• a preferred embodiment of the invention uses a copolymer of an acid anhydride.
• a more preferred embodiment of the invention uses a copolymer of an alkyl vinyl ether with an unsaturated acid anhydride, and a highly preferred embodiment of the invention uses a methyl vinyl ether/maleic anhydride copolymer.
• Gantrez® methyl vinyl ether/maleic acid or anhydride copolymers
• Preferred Gantrez polymers include the Gantrez AN series of the anhydride form of the polymer, commercially available from International Specialty Products of Wayne, New Jersey, U.S.A.
• the polymer has a specific viscosity of at least about 1.0 and preferably from about 2.5 to about 6.0. Specific viscosity is measured as a solution of lg of copolymer in 100 ml of methyl-ethyl ketone (MEK) at 25°C. Higher and lower specific viscosities are within the scope of the invention, but lower than 2.5 specific viscosity polymers are not preferred because these polymers can have poor cohesive properties in denture adhesive formulations.
• MK methyl-ethyl ketone
• Partial salts of the copolymers must be used, including mixed partial salts of different cations.
• Preferred cations include, but are not limited to, calcium, magnesium, strontium, ferrous iron, sodium, potassium, zirconium oxy, zinc, and other non-toxic cations.
• the acid groups are not entirely cross-linked and neutralized.
• a 1% solution of the copolymer in deionized water should have a pH of from about 4 to about 8, preferably from about 4.5 to about 7.5, and most preferably from about 5 to about
• the cross-linking agent of the invention includes the naturally occurring amino acids lysine, histidine, arginine, derivatives or family members of lysine, histidine or arginine and mixtures thereof.
• the preferred amino acid, lysine (2,6 diaminohexanoic acid) is an amino acid having the structure:
• Derivatives including, but not limited to, acid salts thereof and substituted amines capable of forming cross-links with the acid anhydride groups on the MVE/MA copolymer may be within the scope of the invention as may nontoxic diamino acids with a shorter or longer chain length, side chains or ligands and derivatives thereof.
• the amount of cross-linking in the copolymer needs to be controlled. Excess cross- linking can make a batch of copolymer unsuitable for use.
• the percent substitution of lysine in the polymer is less than about 5% and more than about 0.005%. More preferably, the percent substitution is more than about 0.01% and less than about 1% and most preferably the percent substitution is about 0.05% to 0.5%.
• the copolymer salt may be combined with a hydrophilic polymer to enhance the ability of the denture adhesive to form a swellable, tacky and viscous adhesive material upon contact with saliva in the oral cavity.
• the preferred hydrophilic polymers are selected from the group comprising sodium carboxymethyl cellulose, sodium alginate, polyoxyethylene oxide, karaya gum, hydroxyethyl cellulose, locust bean gum, xanthan gum, carrageenan, methyl cellulose and mixtures thereof.
• the hydrophilic polymer may comprise from about 10 to about 60% by weight of the final denture adhesive, preferably from about 15% to about 55% by weight and most preferably from about 20% to about 50% by weight.
• the cross-linked polymer salt of the invention may be incorporated into the denture adhesive composition in an effective amount as the sole adhesive component or in combination with other water soluble polymers and excipients as is known in the art such as fillers, lubricants, flavors, coloring agents, preservatives and the like.
• mineral oil, vegetable oil, petrolatum, preservatives, such as the alkyl parabens, fumed silica and mint flavor are examples of common excipients used in known commercial denture adhesive compositions.
• the crosslinked copolymer salt comprises from about 10% to about 70% by weight of the adhesive compositions, and preferably from about 20% to about 60%.
• the suitable hydrophilic polymers include both natural and synthetic gums, preferably sodium carboxymethyl cellulose, polyethylene oxide and sodium alginate.
• the copolymer and the cross-linking agent are dispersed in water at room temperature (about 10% solids content)and mixed to form the cross-linked polymer.
• the preferred cross-linking agent lysine is very reactive with the anhydride groups in the polymer, and the anhydride groups react with the amino groups in the lysine in preference to hydrolysis in water. Without being limited by theory, we speculate that the amino group immediately adjacent to the carboxyl group in lysine is reacting with the anhydride via a mechanism known as the Dakin-West reaction.
• This bond is a is a true covalent bond and is not vulnerable to hydrolysis when the denture adhesive is placed in an aqueous environment in the mouth.
• the other amino group may then react with an anhydride group in another polymer chain to form a cross-linked polymer system.
• a partial salt is then formed by full or partial hydrolysis of the remaining anhydride groups and partial neutralization of the resulting acid.
• the solution or dispersion is then dried to form a film or a flake of the desired copolymer.
• the dried copolymer partial salt is milled to a suitable particle size material and may then be combined with other ingredients to form a denture adhesive.
• Examples 1-9 A lysine-poly methylvinyl ether/maleic acid was prepared by adding 99.62 g of a methylvinyl ether/maleic anhydride copolymer (GANTREZ AN 169) to 1250 ml. of vigorously mixed deionized water. 0.38 g of L-Lysine monohydrate was added to the mix, and the resulting mixture was held at room temperature for 30 minutes with continuous mixing.
• GANTREZ AN 169 methylvinyl ether/maleic anhydride copolymer
• the mixture was then heated to 85-90°C and held at that temperature for 2 hours with continuous mixing.
• the resulting solution was discharged into trays (while maintaining batch temperature and mixing speed) and dried in an 85°C oven.
• the resulting copolymer was a 0.36% substituted Lysine GANTREZ Acid.
• Examples 10-17 A partial calcium salt of poly methylvinyl ether/ maleic acid was prepared by adding 74.87 g GANTREZ AN 169 to 1250 ml. of vigorously mixed deionized water. Then L-Lysine monohydrate 0.24 g was added to the mixture, and the resulting mixture was held at room temperature for 30 minutes with continuous mixing to form a slurry solution. 24.89 g of calcium hydroxide was added to the slurry solution and the mixture was heated to 85-90°C. The temperature was maintained at 85-90°C for 2 hours with continuous mixing. The solution of the partial salt was discharged into trays (while maintaining batch temperature and mixing speed), and the solution was heated in an 85°C oven until dry.
• the salt was milled and used to make a denture adhesive cream formula.
• This salt is 0.3 Lysine-70 Ca GANTREZ Salt.
• Using different amounts of lysine and metal oxides, different percentages of substitution of Lysine-GANTREZ Salts were prepared and used to make denture adhesive creams by combining 30% of the salt (by weight) with 24% by weight carboxymethyl cellulose, 18% by weight mineral oil and 28% by weight petrolatum.
• a comparative example of a denture adhesive cream was made without lysine.
• the shear strength of the denture adhesive creams were measured and the results are shown in Table 2. The shear strength was measured with an Instron Model 1122. Denture adhesive creams made with lysine cross-linked GANTREZ copolymer partial Ca salts show improved performance.
• Examples 18-19 A 0.5 percent substitution lysine, 40 percent substitution Zinc, 20 percent substitution Magnesium, and 10 percent substitution Sodium methylvinyl ether maleic acid copolymer salt was prepared by adding 75.93 g of GANTREZ AN 169 to 1,000 ml. of vigorously mixed deionized water. Then 0.40 g L-Lysine monohydrate was added to the mixture, and the resulting mixture was held at room temperature for 30 minutes with continuous mixing.
• a solution of 250 ml of deionized water containing 15.85 g zinc oxide, 3.93 g magnesium oxide and 3.90 g sodium hydroxide was added gradually to the lysine GANTREZ AN slurry and the mixture was heated to 85-90°C and held at that temperature for 2 hours with continuous mixing.
• the solution of the partial salt was discharged into trays (while maintaining batch temperature and mixing speed), and the salt was heated at 85°C until dry.
• the dry salt was milled and used to make a denture adhesive cream formula.

Landscapes

• Health & Medical Sciences (AREA)
• Chemical & Material Sciences (AREA)
• Animal Behavior & Ethology (AREA)
• Life Sciences & Earth Sciences (AREA)
• Epidemiology (AREA)
• General Health & Medical Sciences (AREA)
• Public Health (AREA)
• Veterinary Medicine (AREA)
• Oral & Maxillofacial Surgery (AREA)
• Organic Chemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Dental Preparations (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)

Priority Applications (11)

Applications Claiming Priority (2)

Publications (1)

Family

ID=22769991

Family Applications (1)

Country Status (17)

Cited By (11)

Families Citing this family (17)

Citations (4)

Family Cites Families (18)

• 1998
  • 1998-12-08 US US09/207,309 patent/US6166102A/en not_active Expired - Lifetime
• 1999
  • 1999-08-12 UA UA2001074708A patent/UA72485C2/uk unknown
  • 1999-12-08 KR KR1020017007166A patent/KR20010101153A/ko not_active Withdrawn
  • 1999-12-08 WO PCT/GB1999/004122 patent/WO2000033792A1/en not_active Ceased
  • 1999-12-08 HU HU0104744A patent/HUP0104744A2/hu unknown
  • 1999-12-08 CN CN99816076A patent/CN1334714A/zh active Pending
  • 1999-12-08 PL PL99348832A patent/PL348832A1/xx not_active Application Discontinuation
  • 1999-12-08 NZ NZ512746A patent/NZ512746A/en unknown
  • 1999-12-08 MX MXPA01005812A patent/MXPA01005812A/es unknown
  • 1999-12-08 CZ CZ20012040A patent/CZ20012040A3/cs unknown
  • 1999-12-08 BR BR9916070-6A patent/BR9916070A/pt not_active IP Right Cessation
  • 1999-12-08 EP EP99959537A patent/EP1137388A1/en not_active Withdrawn
  • 1999-12-08 HK HK02102562.2A patent/HK1043044A1/zh unknown
  • 1999-12-08 JP JP2000586287A patent/JP2002531475A/ja not_active Withdrawn
  • 1999-12-08 AU AU16678/00A patent/AU1667800A/en not_active Abandoned
  • 1999-12-08 CA CA002354038A patent/CA2354038A1/en not_active Abandoned
• 2001
  • 2001-07-05 ZA ZA200105545A patent/ZA200105545B/xx unknown

Patent Citations (4)

Also Published As

Similar Documents

Legal Events