WO2000007209A1 - Procede de production de dispositifs getter evaporables a pertes de particules reduites - Google Patents

Procede de production de dispositifs getter evaporables a pertes de particules reduites Download PDF

Info

Publication number
WO2000007209A1
WO2000007209A1 PCT/IT1999/000233 IT9900233W WO0007209A1 WO 2000007209 A1 WO2000007209 A1 WO 2000007209A1 IT 9900233 W IT9900233 W IT 9900233W WO 0007209 A1 WO0007209 A1 WO 0007209A1
Authority
WO
WIPO (PCT)
Prior art keywords
solution
precursor
powder
evaporable getter
production
Prior art date
Application number
PCT/IT1999/000233
Other languages
English (en)
Inventor
Corrado Carretti
Marco Guastalla
Original Assignee
Saes Getters S.P.A.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Saes Getters S.P.A. filed Critical Saes Getters S.P.A.
Priority to AU51928/99A priority Critical patent/AU5192899A/en
Publication of WO2000007209A1 publication Critical patent/WO2000007209A1/fr

Abstract

L'invention concerne un procédé de production de dispositifs getter évaporables à base de baryum, à pertes de particules réduites. Ledit procédé consiste à enduire la surface libre (13) du paquet de poudre (12) du dispositif, d'une couche vitreuse (30) obtenue par atomisation ultrasonique d'une solution de précurseurs du verre formant la couche.
PCT/IT1999/000233 1998-07-28 1999-07-23 Procede de production de dispositifs getter evaporables a pertes de particules reduites WO2000007209A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU51928/99A AU5192899A (en) 1998-07-28 1999-07-23 Process for the production of evaporable getter devices with reduced particle loss

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
ITMI98A001742 1998-07-28
IT1998MI001742A IT1301948B1 (it) 1998-07-28 1998-07-28 Processo per la produzione di dispositivi getter evaporabili conridotta perdita di particelle

Publications (1)

Publication Number Publication Date
WO2000007209A1 true WO2000007209A1 (fr) 2000-02-10

Family

ID=11380534

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IT1999/000233 WO2000007209A1 (fr) 1998-07-28 1999-07-23 Procede de production de dispositifs getter evaporables a pertes de particules reduites

Country Status (4)

Country Link
AU (1) AU5192899A (fr)
IT (1) IT1301948B1 (fr)
TW (1) TW434643B (fr)
WO (1) WO2000007209A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002027058A1 (fr) * 2000-09-27 2002-04-04 Saes Getters S.P.A. Dispositifs poreux d'absorption de gaz a perte de particules reduite et leur procede de fabrication
WO2003010790A1 (fr) * 2001-06-26 2003-02-06 Saes Getters S.P.A. Dispositif getter evaporable pour tubes cathodiques
US8815115B2 (en) 2009-03-18 2014-08-26 Saes Getters S.P.A. Method for the removal of hydrogen from a hydrogen sensitive device by means of a non-evaporable yttrium based getter alloy

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1572000A (en) * 1975-12-12 1980-07-23 Getters Spa Getter device
EP0028372A1 (fr) * 1979-10-25 1981-05-13 Kabushiki Kaisha Toshiba Dispositif getter
JPS58111237A (ja) * 1981-12-25 1983-07-02 Toshiba Corp 耐酸化性ゲツタ装置
DE3414245A1 (de) * 1984-04-14 1985-10-17 Battelle-Institut E.V., 6000 Frankfurt Verfahren und vorrichtung zur dichten belegung von festkoerperoberflaechen mit feinen fluessigkeitstroepfchen

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1572000A (en) * 1975-12-12 1980-07-23 Getters Spa Getter device
EP0028372A1 (fr) * 1979-10-25 1981-05-13 Kabushiki Kaisha Toshiba Dispositif getter
JPS58111237A (ja) * 1981-12-25 1983-07-02 Toshiba Corp 耐酸化性ゲツタ装置
DE3414245A1 (de) * 1984-04-14 1985-10-17 Battelle-Institut E.V., 6000 Frankfurt Verfahren und vorrichtung zur dichten belegung von festkoerperoberflaechen mit feinen fluessigkeitstroepfchen

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 007, no. 218 (E - 200) 28 September 1983 (1983-09-28) *

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002027058A1 (fr) * 2000-09-27 2002-04-04 Saes Getters S.P.A. Dispositifs poreux d'absorption de gaz a perte de particules reduite et leur procede de fabrication
US6620297B2 (en) 2000-09-27 2003-09-16 Saes Getters, S.P.A. Porous getter devices with reduced particle loss and method for manufacturing same
US6783696B2 (en) 2000-09-27 2004-08-31 Saes Getters S.P.A. Porous getter devices with reduced particle loss and method for manufacturing same
US7122100B2 (en) 2000-09-27 2006-10-17 Saes Getters S.P.A. Porous getter devices with reduced particle loss and method for manufacturing same
CN1318642C (zh) * 2000-09-27 2007-05-30 工程吸气公司 降低颗粒物损失的多孔吸气剂器件及其制备方法
WO2003010790A1 (fr) * 2001-06-26 2003-02-06 Saes Getters S.P.A. Dispositif getter evaporable pour tubes cathodiques
US6873102B2 (en) 2001-06-26 2005-03-29 Saes Getters S.P.A. Evaporable getter device with metallic nets
US8815115B2 (en) 2009-03-18 2014-08-26 Saes Getters S.P.A. Method for the removal of hydrogen from a hydrogen sensitive device by means of a non-evaporable yttrium based getter alloy

Also Published As

Publication number Publication date
AU5192899A (en) 2000-02-21
ITMI981742A1 (it) 2000-01-28
ITMI981742A0 (it) 1998-07-28
IT1301948B1 (it) 2000-07-20
TW434643B (en) 2001-05-16

Similar Documents

Publication Publication Date Title
US6723435B1 (en) Optical fiber preforms
RU2336944C2 (ru) Композиция и устройство для сорбции газа и способ получения композиции
WO2000007209A1 (fr) Procede de production de dispositifs getter evaporables a pertes de particules reduites
US5885492A (en) Method for preparing spherical phosphor particles
US6873102B2 (en) Evaporable getter device with metallic nets
CN1318038A (zh) 制造用于光导纤维预制品的煤烟的方法以及由其制成的预制品
US20050163930A1 (en) Device and method for producing a calcium-rich getter thin film
US6139768A (en) Nitrogenated evaporable getter devices with high fritting resistance and process for their production
EP0853328B1 (fr) Dispositif dégazeur frittable et évaporable à haut rendement de barium
JPH02119032A (ja) カラー受像管
US3973816A (en) Method of gettering a television display tube
US6395082B2 (en) Coating material for inner surface of cathode-ray tube
CN1149610C (zh) 用于钙蒸发过程的吸气剂
KR20060024891A (ko) 엘씨디 겟터
US6306314B1 (en) Evaporable getter device with reduced activation time
JP2004288454A (ja) Ｆｐｄ用保護膜およびその製造方法ならびにこれを用いたｆｐｄ
KR100309706B1 (ko) 분무열분해법에 의한 알루미네이트 계열 형광체의 제조방법
EP0003148A2 (fr) Méthode de fabrication d'écrans luminescents, écrans luminescents obtenus par cette méthode, et tubes à rayons cathodiques comportant de tels écrans luminescents
CN1041241A (zh) 彩色显象管制造方法
KR20220055074A (ko) 증기 챔버의 제조 방법
JPS63211537A (ja) 蛍光膜の形成方法
CN1215909A (zh) 阴极射线管的阴极
JPH06287026A (ja) 接着用ガラス原料、接着用ガラス、接着用ガラスの製造方法、接着用ガラスを用いた真空気密容器およびその製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SL SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase