WO1999012689A1 - Process of using an active solder alloy - Google Patents
Process of using an active solder alloy Download PDFInfo
- Publication number
- WO1999012689A1 WO1999012689A1 PCT/US1998/019004 US9819004W WO9912689A1 WO 1999012689 A1 WO1999012689 A1 WO 1999012689A1 US 9819004 W US9819004 W US 9819004W WO 9912689 A1 WO9912689 A1 WO 9912689A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- workpieces
- joined
- solder material
- solder
- temperature
- Prior art date
Abstract
Description
Claims