WO1997022470A9 - Films de polyethylene a orientation biaxiale - Google Patents

Films de polyethylene a orientation biaxiale

Info

Publication number
WO1997022470A9
WO1997022470A9 PCT/US1996/020180 US9620180W WO9722470A9 WO 1997022470 A9 WO1997022470 A9 WO 1997022470A9 US 9620180 W US9620180 W US 9620180W WO 9722470 A9 WO9722470 A9 WO 9722470A9
Authority
WO
WIPO (PCT)
Prior art keywords
film
films
ethylene
density
polymer
Prior art date
Application number
PCT/US1996/020180
Other languages
English (en)
Other versions
WO1997022470A1 (fr
Filing date
Publication date
Application filed filed Critical
Priority to AU13369/97A priority Critical patent/AU1336997A/en
Priority to EP96944865A priority patent/EP0876250A4/fr
Priority to BR9612068-1A priority patent/BR9612068A/pt
Priority to IL12459096A priority patent/IL124590A0/xx
Priority to JP52297797A priority patent/JP2002515923A/ja
Priority to HU0001641A priority patent/HUP0001641A1/hu
Priority to KR1019980704592A priority patent/KR20000064446A/ko
Priority to NZ326083A priority patent/NZ326083A/xx
Publication of WO1997022470A1 publication Critical patent/WO1997022470A1/fr
Publication of WO1997022470A9 publication Critical patent/WO1997022470A9/fr
Priority to NO982786A priority patent/NO982786L/no

Abstract

L'invention se rapporte à des articles et à des film obtenus à partir de polymères à base d'éthylène fabriqués au moyen d'un système catalyseur d'alliage organométallique. L'orientation biaxiale améliore spectaculairement la transparence, la rigidité, la résistance au choc au mouton, la résistance au percement, et le rétrécissement. La résistance à la traction et la tension de rupture sont également améliorées. La rigidité du film, telle que mesurée par le module sécant, est augmentée de 300 % sur un film non orienté du même polymère d'éthylène. Ces articles et ces films sont utilisés comme emballages moulants, surenveloppes et dans des applications d'emballage à sec tels que des sandwichs et des céréales ainsi que dans des applications sans emballage telles que des albums photos ou porte-documents.
PCT/US1996/020180 1995-12-18 1996-12-18 Films de polyethylene a orientation biaxiale WO1997022470A1 (fr)

Priority Applications (9)

Application Number Priority Date Filing Date Title
AU13369/97A AU1336997A (en) 1995-12-18 1996-12-18 Biaxially oriented polyethylene films
EP96944865A EP0876250A4 (fr) 1995-12-18 1996-12-18 Films de polyethylene a orientation biaxiale
BR9612068-1A BR9612068A (pt) 1995-12-18 1996-12-18 Pelìculas de polietileno orientadas biaxialmente
IL12459096A IL124590A0 (en) 1995-12-18 1996-12-18 Biaxially oriented polyethylene films
JP52297797A JP2002515923A (ja) 1995-12-18 1996-12-18 二軸配向ポリエチレンフィルム
HU0001641A HUP0001641A1 (hu) 1995-12-18 1996-12-18 Biaxiálisan orientált polietilén filmek
KR1019980704592A KR20000064446A (ko) 1995-12-18 1996-12-18 2축배향폴리에틸렌필름
NZ326083A NZ326083A (en) 1995-12-18 1996-12-18 Biaxially oriented polyethylene films
NO982786A NO982786L (no) 1995-12-18 1998-06-17 Biaksialt orienterte polyetylen filmer

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US877795P 1995-12-18 1995-12-18
US60/008,777 1995-12-18
US75510596A 1996-11-22 1996-11-22
US08/755,105 1996-11-22

Publications (2)

Publication Number Publication Date
WO1997022470A1 WO1997022470A1 (fr) 1997-06-26
WO1997022470A9 true WO1997022470A9 (fr) 1997-09-04

Family

ID=26678610

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1996/020180 WO1997022470A1 (fr) 1995-12-18 1996-12-18 Films de polyethylene a orientation biaxiale

Country Status (12)

Country Link
EP (1) EP0876250A4 (fr)
JP (1) JP2002515923A (fr)
KR (1) KR20000064446A (fr)
AU (1) AU1336997A (fr)
BR (1) BR9612068A (fr)
CA (1) CA2239549A1 (fr)
HU (1) HUP0001641A1 (fr)
IL (1) IL124590A0 (fr)
NO (1) NO982786L (fr)
NZ (1) NZ326083A (fr)
PL (1) PL327143A1 (fr)
WO (1) WO1997022470A1 (fr)

Families Citing this family (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA2245375C (fr) * 1998-08-19 2006-08-15 Nova Chemicals Ltd. Production de polyethylene par un procede a deux reacteurs utilisant un catalyseur de phosphinimine
US6248442B1 (en) 1998-12-31 2001-06-19 Mobil Oil Corporation Easy opening hermetically sealed film
US6800692B2 (en) 2000-06-22 2004-10-05 Exxonmobil Chemical Patents Inc. Metallocene-produced very low density polyethylenes
EP1299470B1 (fr) * 2000-06-22 2007-08-08 Univation Technologies, LLC M lange de poly thyl ne tr s basse densit et de poly thyl ne haute densit
US7135526B2 (en) 2001-06-22 2006-11-14 Univation Technologies, Llc Very low density polyethylene and high density polyethylene blends
AU2003269970A1 (en) 2002-09-05 2004-03-29 Exxonmobil Chemical Patents Inc. Shrink film
CN102417644A (zh) * 2004-03-19 2012-04-18 陶氏环球技术有限责任公司 由聚合物配方制成的薄膜层
WO2007130277A1 (fr) 2006-05-05 2007-11-15 Exxonmobil Chemical Patents Inc. Mélanges de polymères basse densité linéaires et articles fabriqués à partir de ces mélanges
US20080118692A1 (en) * 2006-11-21 2008-05-22 Fina Technology, Inc. Polyethylene useful for producing film and molded articles in a process which uses solid state stretching
US8709610B2 (en) 2008-10-17 2014-04-29 Dow Global Technologies Llc Biaxially oriented film which could be thermally laminated with paper and other substrates
JP2010270227A (ja) * 2009-05-21 2010-12-02 Tohcello Co Ltd 二軸延伸エチレン系共重合体フィルム
WO2014173423A1 (fr) * 2013-04-25 2014-10-30 Huhtamaki Films Germany Gmbh & Co. Kg Feuille multicouche à propagation de déchirement linéaire
EP3335874A1 (fr) 2016-12-15 2018-06-20 Borealis AG Articles à orientation biaxiale comprenant un polymère de polyéthylène multimodal
EP3630449A4 (fr) * 2017-05-23 2021-01-20 Jindal Films Americas LLC Films lldpe métallisés, orientés et minces
US11230049B2 (en) 2019-08-21 2022-01-25 Aerostar International, Inc. Seals for aerial vehicles
CN114901732A (zh) 2019-12-09 2022-08-12 埃克森美孚化学专利公司 纵向取向的聚乙烯薄膜
EP4073154A1 (fr) 2019-12-09 2022-10-19 ExxonMobil Chemical Patents Inc. Films de polyéthylène orientés biaxialement et leur procédé de production
WO2021119155A1 (fr) 2019-12-09 2021-06-17 Exxonmobil Chemical Patents Inc. Films de polyéthylène à orientation biaxiale
CN115594909B (zh) * 2021-06-28 2023-12-22 中国石油化工股份有限公司 冷拉伸套管膜用聚乙烯组合物及其制备方法
NL2029437B1 (en) * 2021-10-15 2023-05-16 Perfo Tec B V Package for preserving respiring produce and method
EP4423152A1 (fr) 2021-10-26 2024-09-04 ExxonMobil Chemical Patents Inc. Films de polyéthylène à basse densité linéaire hautement orientés ayant une aptitude au traitement et des propriétés mécaniques exceptionnelles
WO2024068914A1 (fr) 2022-09-30 2024-04-04 Basell Polyolefine Gmbh Mélange de polymères pour la production d'un film polymère biorienté

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
MX9200724A (es) * 1991-02-22 1993-05-01 Exxon Chemical Patents Inc Mezcla termosellable de polietileno o plastomero de muy baja densidad con polimeros a base de polipropileno y pelicula termosellable asi como articulos hechos con aquellas.
US5562958A (en) * 1991-10-15 1996-10-08 The Dow Chemical Company Packaging and wrapping film
US5283128A (en) * 1992-03-23 1994-02-01 Viskase Corporation Biaxially oriented heat shrinkable film
DE69308153T3 (de) * 1992-09-16 2012-04-05 Exxonmobil Chemical Patents, Inc. (N.D.Ges.D. Staates Delaware) Weiche filme mit verbesserten physikalischen eigenschaften
DE69433089T2 (de) * 1993-06-24 2004-06-17 American National Can Co., Chicago Mehrschichtige strukturen aus single-site katalysierten polymeren

Similar Documents

Publication Publication Date Title
US5591390A (en) Method of manufacturing packaging and wrapping film
WO1997022470A9 (fr) Films de polyethylene a orientation biaxiale
AU1336997A (en) Biaxially oriented polyethylene films
US5629059A (en) Multi-layer packaging film and receptacles made therefrom
CA1147520A (fr) Pellicule multicouche retrecissable en polyester/polyolefine
CA2703193C (fr) Films multicouches
US4640856A (en) Multi-layer packaging film and receptacles made therefrom
US4247584A (en) Composition comprising a blend of EVA polymers having differing VA contents; films and laminates made therefrom by extrusion; and heat-sealed food bags made from the laminates
EP0706455B1 (fr) Structures ameliorees de polymeres produits a l'aide de catalyseurs a site unique
EP0217596B1 (fr) Film orienté barrière d'oxygène
AU3794000A (en) Packaging film and use of the same
AU752296B2 (en) Poultry shrink bags
US7316833B1 (en) Multi-layer thermoplastic films and packages made therefrom
JP2000109570A (ja) レトルト容器、レトルト包装用フィルムおよびレトルト用包材
AU739685C (en) Multilayer thermoplastic films and packages made therefrom
CA2245678C (fr) Film multicouche permeable a l'oxygene et ayant un module eleve, procede d'emballage utilisant ce film, et produit emballe le comprenant
AU681358B2 (en) Formulation of high abuse, high shrink barrier bags for meat packaging
CA1141883A (fr) Pellicules d'eva et methode pour les preparer