WO1997020876A1 - Produit moussant rapidement pour la construction de systemes prefabriques - Google Patents
Produit moussant rapidement pour la construction de systemes prefabriques Download PDFInfo
- Publication number
- WO1997020876A1 WO1997020876A1 PCT/EP1996/005283 EP9605283W WO9720876A1 WO 1997020876 A1 WO1997020876 A1 WO 1997020876A1 EP 9605283 W EP9605283 W EP 9605283W WO 9720876 A1 WO9720876 A1 WO 9720876A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- polyol
- component system
- water
- groups
- Prior art date
Abstract
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU10951/97A AU1095197A (en) | 1995-12-01 | 1996-11-29 | Rapid-foaming foam for prefabricated system building |
EP96941619A EP0863927A1 (fr) | 1995-12-01 | 1996-11-29 | Produit moussant rapidement pour la construction de systemes prefabriques |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DK136295 | 1995-12-01 | ||
DK1362/95 | 1995-12-01 | ||
DK55096 | 1996-05-07 | ||
DK0550/96 | 1996-05-07 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1997020876A1 true WO1997020876A1 (fr) | 1997-06-12 |
Family
ID=26064203
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP1996/005283 WO1997020876A1 (fr) | 1995-12-01 | 1996-11-29 | Produit moussant rapidement pour la construction de systemes prefabriques |
Country Status (4)
Country | Link |
---|---|
EP (1) | EP0863927A1 (fr) |
AU (1) | AU1095197A (fr) |
CA (1) | CA2242672A1 (fr) |
WO (1) | WO1997020876A1 (fr) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2023193882A1 (fr) * | 2022-04-04 | 2023-10-12 | Wacker Chemie Ag | Mousse expansible à base de minéraux |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR1441565A (fr) * | 1964-04-08 | 1966-06-10 | Gen Tire & Rubber Co | Polymères d'isocyanurates et leur préparation |
DE2502260A1 (de) * | 1974-01-30 | 1975-08-07 | Upjohn Co | Cokatalysatorsystem zur trimerisierung eines polyisocyanats und verfahren zur herstellung eines zelligen polymeren mit vornehmlich wiederkehrenden isocyanurateinheiten |
EP0006150A1 (fr) * | 1978-06-10 | 1980-01-09 | BASF Aktiengesellschaft | Procédé de préparation de mousses de polyuréthanne intégrales résistant à la lumière |
US4184022A (en) * | 1978-09-15 | 1980-01-15 | Owens-Corning Fiberglas Corporation | Polyisocyanurate foam comprising reaction product of a polyisocyanate and a polyol mixture comprising a carboxylic ester polyol and a resole polyether polyol using a catalyst comprising dimethylethanolamine and an alkali metal salt of a carboxylic acid |
US4425446A (en) * | 1982-06-23 | 1984-01-10 | Sealed Air Corporation | Urea-modified isocyanurate foam, composition and method |
US5254600A (en) * | 1990-08-17 | 1993-10-19 | Atlas Roofing Corporation | Method of producing rigid foams and products produced therefrom |
-
1996
- 1996-11-29 AU AU10951/97A patent/AU1095197A/en not_active Abandoned
- 1996-11-29 CA CA002242672A patent/CA2242672A1/fr not_active Abandoned
- 1996-11-29 EP EP96941619A patent/EP0863927A1/fr not_active Withdrawn
- 1996-11-29 WO PCT/EP1996/005283 patent/WO1997020876A1/fr not_active Application Discontinuation
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR1441565A (fr) * | 1964-04-08 | 1966-06-10 | Gen Tire & Rubber Co | Polymères d'isocyanurates et leur préparation |
DE2502260A1 (de) * | 1974-01-30 | 1975-08-07 | Upjohn Co | Cokatalysatorsystem zur trimerisierung eines polyisocyanats und verfahren zur herstellung eines zelligen polymeren mit vornehmlich wiederkehrenden isocyanurateinheiten |
EP0006150A1 (fr) * | 1978-06-10 | 1980-01-09 | BASF Aktiengesellschaft | Procédé de préparation de mousses de polyuréthanne intégrales résistant à la lumière |
US4184022A (en) * | 1978-09-15 | 1980-01-15 | Owens-Corning Fiberglas Corporation | Polyisocyanurate foam comprising reaction product of a polyisocyanate and a polyol mixture comprising a carboxylic ester polyol and a resole polyether polyol using a catalyst comprising dimethylethanolamine and an alkali metal salt of a carboxylic acid |
US4425446A (en) * | 1982-06-23 | 1984-01-10 | Sealed Air Corporation | Urea-modified isocyanurate foam, composition and method |
US5254600A (en) * | 1990-08-17 | 1993-10-19 | Atlas Roofing Corporation | Method of producing rigid foams and products produced therefrom |
Also Published As
Publication number | Publication date |
---|---|
AU1095197A (en) | 1997-06-27 |
EP0863927A1 (fr) | 1998-09-16 |
CA2242672A1 (fr) | 1997-06-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1127908B1 (fr) | Système moussant local à deux composants et son utilisation pour le remplissage de cavités en vue de la protection Antiincendie | |
EP1924356B1 (fr) | Procede de production de mousse de polyisocyanurate rigide | |
EP0043952B1 (fr) | Masses intumescentes éventuellement mousseuses | |
EP0683805B1 (fr) | Composition prepolymere pour mousses isolantes | |
EP1302492A1 (fr) | Système moussant local à plusieurs composants et son utilisation | |
EP0120253A1 (fr) | Masses intumescentes éventuellement mousseuses et objets obtenus par moulage préparés à partir de celles-ci | |
EP1469059A2 (fr) | Mousses expansibles en cas d'incendie | |
EP2091992A1 (fr) | Polyphénylène polyméthylène polyisocyanate et son utilisation pour la fabrication de mousses en polyuréthanne | |
EP0061058B1 (fr) | Solutions d'oligouréthane-éthers dans des polyéther-polyols et leur utilisation dans un procédé de préparation de mousses de polyuréthane ayant une bonne aptitude au soudage à haute fréquence et au doublage à la flamme | |
DE19860339C2 (de) | Reaktive Zweikomponenten-Polyurethanschäummasse und Verfahren zur Brandschutzabdichtung | |
DE3001966A1 (de) | Starre isocyanuratpolyurethanschaeume und verfahren zu ihrer herstellung | |
WO1997020876A1 (fr) | Produit moussant rapidement pour la construction de systemes prefabriques | |
DE2251889C2 (de) | Verfahren zur Herstellung von harten Polyurethanschaumstoffen in situ auf einer Oberfläche | |
DE4416838A1 (de) | Polyester auf Basis oleochemischer Polyole zur Herstellung von Polyurethan-Schaumstoffen | |
US4430840A (en) | Foam, composition and method useful for retrofit insulation | |
US4401769A (en) | Foam, composition and method useful for retrofit insulation | |
DE19744364A1 (de) | Bindemittel-Zusammensetzung | |
EP0465922B1 (fr) | Procédé pour préparer des mousses à base d'isocyanates | |
DE10108445A1 (de) | Druckbehälter enthaltend Umsetzungsprodukt zur Herstellung eines elastischen Schaumstoffes | |
DE10347659B4 (de) | Prepolymere, insbesondere für Einkomponentenschaum | |
EP0398162A2 (fr) | Procédé de préparation de mousse de polyuréthane | |
DE10108443A1 (de) | Druckbehälter enthaltend Umsetzungsprodukt zur Herstellung eines elastischen Schaumstoffes | |
DE10152310A1 (de) | Verfahren zur Herstellung von harten Polyurethanen | |
EP1894954A1 (fr) | Composant d'isocyanate et prépolymère fabriqué à partir de celui-ci ainsi que polyuréthane et mousses constituées d'un ou de deux composants de polyuréthane fabriqués à partir de celui-ci | |
DE4441570A1 (de) | Schaumkunststoff aus Einweg-Druckbehältern |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AU CA JP US |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
WWE | Wipo information: entry into national phase |
Ref document number: 1996941619 Country of ref document: EP |
|
ENP | Entry into the national phase |
Ref document number: 2242672 Country of ref document: CA Ref country code: CA Ref document number: 2242672 Kind code of ref document: A Format of ref document f/p: F |
|
NENP | Non-entry into the national phase |
Ref country code: JP Ref document number: 97520959 Format of ref document f/p: F |
|
WWP | Wipo information: published in national office |
Ref document number: 1996941619 Country of ref document: EP |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1996941619 Country of ref document: EP |