WO1997015846A1 - Formulation de fibre optique polymere, procede de fabrication et utilisation associes - Google Patents

Formulation de fibre optique polymere, procede de fabrication et utilisation associes Download PDF

Info

Publication number
WO1997015846A1
WO1997015846A1 PCT/US1996/014314 US9614314W WO9715846A1 WO 1997015846 A1 WO1997015846 A1 WO 1997015846A1 US 9614314 W US9614314 W US 9614314W WO 9715846 A1 WO9715846 A1 WO 9715846A1
Authority
WO
WIPO (PCT)
Prior art keywords
parts
ofthe
temperature
container
mixture
Prior art date
Application number
PCT/US1996/014314
Other languages
English (en)
Inventor
Jerry W. Williams
James R. Zarian
Gerald L. Uhl
Jeanne M. Goetzke
Original Assignee
Minnesota Mining And Manufacturing Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Minnesota Mining And Manufacturing Company filed Critical Minnesota Mining And Manufacturing Company
Priority to AU69161/96A priority Critical patent/AU6916196A/en
Publication of WO1997015846A1 publication Critical patent/WO1997015846A1/fr

Abstract

Une fibre optique polymère est le produit de réaction de 100 à 80 parties environ d'au moins un monomère méthacrylique dérivé de l'estérification de l'acide méthacrylique par un alcool possédant au moins 4 atomes de carbone, et de 0 à 20 parties environ d'au moins un agent de réticulation éthyléniquement insaturé pouvant subir une polymérisation radicalaire. La fibre optique polymère conforme à l'invention transmet la lumière pour une plage de température comprise entre -40 °C et 125 °C environ, et présente en outre une stabilité thermique et une flexibilité à long terme (de l'ordre de plusieurs semaines) lors du vieillissement à des températures allant jusqu'à 125 °C environ, sans perte de ses propriétés physiques et optiques.
PCT/US1996/014314 1995-10-24 1996-09-06 Formulation de fibre optique polymere, procede de fabrication et utilisation associes WO1997015846A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU69161/96A AU6916196A (en) 1995-10-24 1996-09-06 Polymeric optical fiber formulation, method of fabrication, and uses therefor

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US604095P 1995-10-24 1995-10-24
US60/006,040 1995-10-24
US58093595A 1995-12-29 1995-12-29
US08/580,935 1995-12-29
US60583096A 1996-02-23 1996-02-23
US08/605,830 1996-02-23

Publications (1)

Publication Number Publication Date
WO1997015846A1 true WO1997015846A1 (fr) 1997-05-01

Family

ID=27358026

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1996/014314 WO1997015846A1 (fr) 1995-10-24 1996-09-06 Formulation de fibre optique polymere, procede de fabrication et utilisation associes

Country Status (2)

Country Link
AU (1) AU6916196A (fr)
WO (1) WO1997015846A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0849315A1 (fr) * 1996-12-17 1998-06-24 Rohm And Haas Company Guide de lumière acrylique flexible à stabilité photo-thermique améliorée
US6535667B1 (en) 2001-12-31 2003-03-18 3M Innovative Properties Company Light fiber comprising continuous outer cladding and method of making
US6799880B2 (en) 2001-12-31 2004-10-05 3M Innovative Properties Company Illumination device

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0097325A2 (fr) * 1982-06-17 1984-01-04 Sumitomo Chemical Company, Limited Fibre optique
EP0229202A1 (fr) * 1984-07-10 1987-07-22 Sumitomo Electric Industries Limited Guide d'ondes optique et son procédé de fabrication
JPS62288801A (ja) * 1986-06-06 1987-12-15 Sumitomo Electric Ind Ltd プラスチツク光フアイバ−
US4828359A (en) * 1986-01-09 1989-05-09 Sumitomo Electric Industries, Ltd. Alkyl methacrylate homo - or copolymer optical waveguide for illumination and production of the same
US5298327A (en) * 1986-07-08 1994-03-29 Lumenyte International Corporation High temperature plastic light conduit and composition of matter therefor
EP0629493A1 (fr) * 1993-06-15 1994-12-21 Rohm And Haas Company Matériau composite réticulé et son procédé de fabrication

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0097325A2 (fr) * 1982-06-17 1984-01-04 Sumitomo Chemical Company, Limited Fibre optique
EP0229202A1 (fr) * 1984-07-10 1987-07-22 Sumitomo Electric Industries Limited Guide d'ondes optique et son procédé de fabrication
US4828359A (en) * 1986-01-09 1989-05-09 Sumitomo Electric Industries, Ltd. Alkyl methacrylate homo - or copolymer optical waveguide for illumination and production of the same
JPS62288801A (ja) * 1986-06-06 1987-12-15 Sumitomo Electric Ind Ltd プラスチツク光フアイバ−
US5298327A (en) * 1986-07-08 1994-03-29 Lumenyte International Corporation High temperature plastic light conduit and composition of matter therefor
EP0629493A1 (fr) * 1993-06-15 1994-12-21 Rohm And Haas Company Matériau composite réticulé et son procédé de fabrication

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
DATABASE WPI Derwent World Patents Index; AN 88-026414, XP002022263 *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0849315A1 (fr) * 1996-12-17 1998-06-24 Rohm And Haas Company Guide de lumière acrylique flexible à stabilité photo-thermique améliorée
US6207747B1 (en) 1996-12-17 2001-03-27 Fiberstors Incorporated Acrylic flexible light pipe of improved photo-thermal stability
US6535667B1 (en) 2001-12-31 2003-03-18 3M Innovative Properties Company Light fiber comprising continuous outer cladding and method of making
US6799880B2 (en) 2001-12-31 2004-10-05 3M Innovative Properties Company Illumination device

Also Published As

Publication number Publication date
AU6916196A (en) 1997-05-15

Similar Documents

Publication Publication Date Title
EP0098578B1 (fr) Fibres optiques en matière plastique
EP0253515B1 (fr) Lentille de contact souple à base d'un hydrogel fluoré
AU727717B2 (en) Chemical composition and polymers and polymeric materials derived therefrom
KR920001247B1 (ko) 광섬유용 클래딩 물질
CA1270394A (fr) Fibre optique
EP0162472B1 (fr) Fibre optique en matière plastique
GB2161954A (en) Optical fiber having a polymethacrylate core and fluoro-copolymer cladding
CA2113640C (fr) Coeurs de fibres optiques en plastique renfermant du fluor
WO1997015846A1 (fr) Formulation de fibre optique polymere, procede de fabrication et utilisation associes
CA1255939A (fr) Fibre optique
GB2178190A (en) Optical fibers made of copolymers
WO1994015005A1 (fr) Articles formes ayant un indice de refraction variant graduellement
US5239027A (en) Transparent thermoplastic molding composition, process for its preparation and its use
EP0436727B1 (fr) Lentille de contact
KR100191225B1 (ko) 투명한 열가소성 성형화합물을 포함하는 빔도파관 및 이의 제조방법
EP0108420A2 (fr) Bâton à transport d'image en résine synthétique et procédé de fabrication
JP2002501444A (ja) 放射対称屈折率分布形透明製品とその製造方法
US5951920A (en) Process for preparing optical fiber cladding solutions
JP3620613B2 (ja) 含水性眼用レンズ材料
US7343073B2 (en) Optical members and compositions for producing them
US5491770A (en) Copolymers for optical fibers
Koike et al. Graded-index polymer optical fiber by new random copolymerization technique
JPS6337312A (ja) ソフトコンタクトレンズ用材料
JPS61194404A (ja) 光伝送繊維用透明重合体の製造方法
JPH07168138A (ja) コンタクトレンズ

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE HU IL IS JP KE KG KP KR KZ LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK TJ TM TR TT UA UG UZ VN AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): KE LS MW SD SZ UG AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 97516590

Format of ref document f/p: F

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA