WO1996006129A1 - Verfahren zur herstellung von expandierten polyolefin-partikeln - Google Patents
Verfahren zur herstellung von expandierten polyolefin-partikeln Download PDFInfo
- Publication number
- WO1996006129A1 WO1996006129A1 PCT/EP1995/003190 EP9503190W WO9606129A1 WO 1996006129 A1 WO1996006129 A1 WO 1996006129A1 EP 9503190 W EP9503190 W EP 9503190W WO 9606129 A1 WO9606129 A1 WO 9606129A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyolefin
- particles
- blowing agent
- polyolefin particles
- impregnation
- Prior art date
Abstract
Description
Claims