WO1995016522A1 - Composition pour revetements durables, procede de production de revetements antireflechissants durables, et articles revetus - Google Patents

Composition pour revetements durables, procede de production de revetements antireflechissants durables, et articles revetus Download PDF

Info

Publication number
WO1995016522A1
WO1995016522A1 PCT/US1994/014013 US9414013W WO9516522A1 WO 1995016522 A1 WO1995016522 A1 WO 1995016522A1 US 9414013 W US9414013 W US 9414013W WO 9516522 A1 WO9516522 A1 WO 9516522A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
weight percent
amount
coating composition
water
Prior art date
Application number
PCT/US1994/014013
Other languages
English (en)
Inventor
Huawen Li
Bhima R. Vijayendran
Original Assignee
Ppg Industries, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ppg Industries, Inc. filed Critical Ppg Industries, Inc.
Priority to AU13011/95A priority Critical patent/AU1301195A/en
Publication of WO1995016522A1 publication Critical patent/WO1995016522A1/fr

Abstract

Composition pour revêtements, procédé de production de revêtements antiréfléchissants, et articles revêtus. Le procédé de revêtement comprend: (a) le revêtement de la matière support par une composition formée essentiellement de: (1) environ 20 à 70 % en poids d'un mélange de monomères au silane comprenant un glycidoxyalkylalcoxysilane et un ou plusieurs alkylalcoxysilane; (2) environ 0 à 40 % en poids de tétra(C1-C4) alcoxysilane; (3) environ 0 à 10 % en poids de silane(s) fluoré(s); (4) environ 1 à 8 % en poids d'un polymère soluble dans l'eau; (5) une quantité de tensioactif non ionique produisant un nivellement; (6) une quantité d'un alcool aliphatique inférieur produisant une solvatisation; (7) une quantité d'un acide soluble dans l'eau produisant une réaction catalytique; et (8) de l'eau; (b) le durcissement de la matière support revêtue; (c) le traitement du revêtement durci à l'aide d'une solution acide aqueuse; (d) la mise en contact du revêtement traité avec une solution aqueuse de lessivage; et (e) le durcissement du produit mentionné sous (d).
PCT/US1994/014013 1993-12-13 1994-12-05 Composition pour revetements durables, procede de production de revetements antireflechissants durables, et articles revetus WO1995016522A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU13011/95A AU1301195A (en) 1993-12-13 1994-12-05 Durable coating composition, process for producing durable, antireflective coatings, and coated articles

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US16599693A 1993-12-13 1993-12-13
US08/165,996 1993-12-13

Publications (1)

Publication Number Publication Date
WO1995016522A1 true WO1995016522A1 (fr) 1995-06-22

Family

ID=22601355

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1994/014013 WO1995016522A1 (fr) 1993-12-13 1994-12-05 Composition pour revetements durables, procede de production de revetements antireflechissants durables, et articles revetus

Country Status (2)

Country Link
AU (1) AU1301195A (fr)
WO (1) WO1995016522A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5958514A (en) * 1997-04-17 1999-09-28 Sdc Coatings, Inc. Composition for providing an abrasion resistant coating on a substrate
WO1999057375A1 (fr) * 1998-05-04 1999-11-11 3M Innovative Properties Company Articles retroreflechissants avec revetement a base de composite de ceramere durci possedant des caracteristiques de resistance a l'abrasion et aux taches
WO2001090268A1 (fr) * 2000-05-25 2001-11-29 Fraunhofer-Gesellschaft Zur Foerderung Der Angewandten Forschung E.V. Materiau polymere hybride pour revetements photosensibles et articles optiques et vitrages recouverts d'un tel materiau
US6331206B1 (en) 1996-11-22 2001-12-18 U.S. Philips Corporation Lacquer composition
WO2005101063A1 (fr) 2004-04-14 2005-10-27 Lg Chem, Ltd. Composition de revetement antireflet et couche de revetement presentant une excellente resistance aux taches
US7001642B2 (en) 1999-04-23 2006-02-21 Sdc Technologies, Inc. Composition for providing an abrasion resistant coating on a substrate with a matched refractive index and controlled tintability
US7097704B1 (en) 2002-09-16 2006-08-29 Sdc Technologies, Inc. Tintable abrasion resistant coating composition and methods of making and using same

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4174229A (en) * 1978-03-28 1979-11-13 Ppg Industries, Inc. Magnesium oxide cementitious compositions containing hydrolyzable organo-silicon compounds
US4529758A (en) * 1983-05-05 1985-07-16 General Electric Company Water based resin dispersions
US4904525A (en) * 1987-02-13 1990-02-27 Toray Industries, Inc. Anti-reflection optical article and process of producing the same
US4918131A (en) * 1987-08-14 1990-04-17 Wacker-Chemie Gmbh Aqueous silicone dispersions
US4940743A (en) * 1984-04-06 1990-07-10 Bayer Aktiengesellschaft Silicone resin emulsion
US4988759A (en) * 1989-09-26 1991-01-29 E. I. Du Pont De Nemours And Company Coating composition of acrylic polymers containing reactive groups and an epoxy organosilane
JPH0321678A (ja) * 1989-06-19 1991-01-30 Nikon Corp コーティング組成物及びこれが塗布された光学物品
US5104692A (en) * 1990-04-20 1992-04-14 Pilkington Visioncare Holdings, Inc. Two-layer antireflective coating applied in solution
JPH04345841A (ja) * 1991-05-24 1992-12-01 Toru Yamamoto バリアー性積層フィルムおよびその製造方法
US5173368A (en) * 1988-09-14 1992-12-22 Pilkington Visioncare Holdings, Inc. Solution-applied antireflective coatings

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4174229A (en) * 1978-03-28 1979-11-13 Ppg Industries, Inc. Magnesium oxide cementitious compositions containing hydrolyzable organo-silicon compounds
US4529758A (en) * 1983-05-05 1985-07-16 General Electric Company Water based resin dispersions
US4940743A (en) * 1984-04-06 1990-07-10 Bayer Aktiengesellschaft Silicone resin emulsion
US4904525A (en) * 1987-02-13 1990-02-27 Toray Industries, Inc. Anti-reflection optical article and process of producing the same
US4918131A (en) * 1987-08-14 1990-04-17 Wacker-Chemie Gmbh Aqueous silicone dispersions
US5173368A (en) * 1988-09-14 1992-12-22 Pilkington Visioncare Holdings, Inc. Solution-applied antireflective coatings
JPH0321678A (ja) * 1989-06-19 1991-01-30 Nikon Corp コーティング組成物及びこれが塗布された光学物品
US4988759A (en) * 1989-09-26 1991-01-29 E. I. Du Pont De Nemours And Company Coating composition of acrylic polymers containing reactive groups and an epoxy organosilane
US5104692A (en) * 1990-04-20 1992-04-14 Pilkington Visioncare Holdings, Inc. Two-layer antireflective coating applied in solution
JPH04345841A (ja) * 1991-05-24 1992-12-01 Toru Yamamoto バリアー性積層フィルムおよびその製造方法

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6331206B1 (en) 1996-11-22 2001-12-18 U.S. Philips Corporation Lacquer composition
US5958514A (en) * 1997-04-17 1999-09-28 Sdc Coatings, Inc. Composition for providing an abrasion resistant coating on a substrate
US6001163A (en) * 1997-04-17 1999-12-14 Sdc Coatings, Inc. Composition for providing an abrasion resistant coating on a substrate
US6346331B2 (en) 1997-04-17 2002-02-12 Sdc Coatings, Inc. Composition for providing an abrasion resistant coating on a substrate
WO1999057375A1 (fr) * 1998-05-04 1999-11-11 3M Innovative Properties Company Articles retroreflechissants avec revetement a base de composite de ceramere durci possedant des caracteristiques de resistance a l'abrasion et aux taches
US7001642B2 (en) 1999-04-23 2006-02-21 Sdc Technologies, Inc. Composition for providing an abrasion resistant coating on a substrate with a matched refractive index and controlled tintability
US7014918B2 (en) 1999-04-23 2006-03-21 Sdc Technologies, Inc. Composition for providing an abrasion resistant coating on a substrate with a matched refractive index and controlled tintability
US7105598B2 (en) 1999-04-23 2006-09-12 Sdc Technologies, Inc. Composition for providing an abrasion resistant coating on a substrate with a matched refractive index and controlled tintability
WO2001090268A1 (fr) * 2000-05-25 2001-11-29 Fraunhofer-Gesellschaft Zur Foerderung Der Angewandten Forschung E.V. Materiau polymere hybride pour revetements photosensibles et articles optiques et vitrages recouverts d'un tel materiau
US7097704B1 (en) 2002-09-16 2006-08-29 Sdc Technologies, Inc. Tintable abrasion resistant coating composition and methods of making and using same
WO2005101063A1 (fr) 2004-04-14 2005-10-27 Lg Chem, Ltd. Composition de revetement antireflet et couche de revetement presentant une excellente resistance aux taches
EP1735645B1 (fr) * 2004-04-14 2012-08-15 LG Chem, Ltd. Composition de revetement antireflet et couche de revetement presentant une excellente resistance aux taches

Also Published As

Publication number Publication date
AU1301195A (en) 1995-07-03

Similar Documents

Publication Publication Date Title
US20010031811A1 (en) Durable coating composition, process for producing durable, antireflective coatings, and coated articles
US5728758A (en) Coating composition and articles having a cured coating
US5744243A (en) Coating composition and articles prepared therewith
EP2001966B1 (fr) Compositions de revetement resistantes a l'abrasion et articles enduits
US8182866B2 (en) Method of producing a substrate which is coated with a mesoporous layer and use thereof in ophthalmic optics
JP6986339B2 (ja) 反射防止膜形成用組成物、反射防止膜およびその形成方法
WO2000010934A1 (fr) Procede de production de surfaces antireflechissantes durables et d'articles antireflechissants
US20020061407A1 (en) Abrasion resistant coating composition and coated articles
KR20140058565A (ko) 반사 방지막 및 반사 방지판
EP2450193B1 (fr) Procédé de coloration d'articles et compositions pouvant être colorées à utiliser dans ce procédé
US6858294B1 (en) Coating fluid for forming hard coating and substrates covered with hard coating
EP3602149B1 (fr) Article optique comprenant un revêtement résistant à l'abrasion et/ou aux rayures et présentant une faible sensibilité aux fissures
WO1995016522A1 (fr) Composition pour revetements durables, procede de production de revetements antireflechissants durables, et articles revetus
CN109963916B (zh) 可热固化的混杂环氧功能组合物和由其制备的透明的热固化的耐腐蚀性涂层
JP3837865B2 (ja) コーティング用組成物及び光学物品
JPH08311408A (ja) コーティング用組成物およびその製造方法および積層体
JPH10292135A (ja) コーティング用組成物、その製造方法および積層体
JPH01275130A (ja) 低反射透明成形体
JPH08311240A (ja) コーティング用組成物および積層体
JPH10324846A (ja) コーティング用組成物、積層体及び眼鏡レンズ
JPH08231807A (ja) プライマー組成物及びプラスチックレンズ
JP3220906B2 (ja) コーティング用組成物
JPH11130982A (ja) コーティング用組成物及びその製造方法並びに積層体
JPH09127301A (ja) プラスチックレンズ
KR20240032538A (ko) 중공실리카 입자, 그의 제조방법 및 중공실리카 분산액

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU BR CA CN JP KR

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE

WR Later publication of a revised version of an international search report
121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
NENP Non-entry into the national phase

Ref country code: CA

122 Ep: pct application non-entry in european phase