USRE34912E - Slag treatment material - Google Patents

Slag treatment material Download PDF

Info

Publication number
USRE34912E
USRE34912E US08/124,802 US12480293A USRE34912E US RE34912 E USRE34912 E US RE34912E US 12480293 A US12480293 A US 12480293A US RE34912 E USRE34912 E US RE34912E
Authority
US
United States
Prior art keywords
slag
sub
test
treatment material
sio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
US08/124,802
Inventor
Kozo Sonobe
Takashi Fukuzawa
Kohsuke Takeuchi
Tatushi Tabata
Hiroshi Fukuoka
Kunio Hisamatsu
Makoto Katamura
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Chemical Industrial Co Ltd
Original Assignee
Nippon Chemical Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP19371887A external-priority patent/JPS6437443A/en
Priority claimed from JP19371287A external-priority patent/JPS6437437A/en
Priority claimed from JP62193717A external-priority patent/JPH062610B2/en
Priority claimed from JP62193716A external-priority patent/JPH062609B2/en
Priority claimed from JP19371387A external-priority patent/JPS6437438A/en
Priority claimed from JP19371187A external-priority patent/JPS6437436A/en
Priority claimed from JP62193714A external-priority patent/JPH062607B2/en
Priority claimed from US07/616,643 external-priority patent/US5187126A/en
Application filed by Nippon Chemical Industrial Co Ltd filed Critical Nippon Chemical Industrial Co Ltd
Priority to US08/124,802 priority Critical patent/USRE34912E/en
Application granted granted Critical
Publication of USRE34912E publication Critical patent/USRE34912E/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

A method for improving the characteristics of fused slag material is disclosed. This improved method results in a fused slag having resistance against pulverization at the cooling process for generation of yellowish turbid water due to contact of slag lumps with rain water, this method characterized by forming a slag treatment material by rough crushing a substantially dehydrated heat-treated material containing boron, and adding that slag treatment material to molten slag.

Description

This is a continuation in part of application Ser. No. 226,278, filed Jul. 29, 1988 now abandoned.
BACKGROUND OF THE INVENTION
1. Industrial Field of the Invention
This invention relates to a slag treatment material for modifying the properties of iron slag and steel slag, and, more particularly, to an improved slag treatment material which can effectively act to prevent, when a cooling process is applied to such iron slag or steel slag as blast furnace slag, the powdering of the slag due to disintegration of the generation of yellowish turbid water when slag lumps come into contact with water.
2. Prior Art
A steel slag, particularly stainless steel slag, which has a basicity (weight ratio CaO/SiO2) of substantially 1.5 or more, has a property whereby the 2CaO.SiO2, phase changes from an α-type phase to an α'-type phase, and then changes to a γ-type phase or β-type phase when the slag is subjected to a cooling process. In many cases, when the slag changes from the α'-type phase to the γ-type phase, a volume expansion of substantially 14% results. As it well known, this causes the slag to powder into fine particles.
This powdering phenomenon worsens the working environment, and disturbs further utilization of slag. Present stainless steel manufacturers are therefore faced with serious problems in regard to the treatment of slag.
It has long been a problem for stainless steel manufacturers to find a method of preventing the powdering of slag and of solidifying it since the discharged slag can be effectively utilized as a secondary material in such applications as engineering aggregates for road construction and so on.
Known methods of preventing the powdering of slag can be exemplified as follows:
1 a method in which slag is made into water-granulated glass when the residue slag is discharged;
2 a method in which slag is modified to form a material which mainly comprises (CaO.SiO2 and has a basicity of 1.5 or less (in practice this can be slightly varied according to the composition of the slag);
3 a method in which the phase change from an α'-type phase to a γ-type which results in a great change in density is controlled and the phase change from an α'-type phase to a β-type phase is activated.
However, in regard to 1, at the time of water granulation, a phreatic explosion can occur due to the presence of molten metals carried at the time of discharge of the slag, and since water granulated glass is a soft material, it does not have sufficient strength to serve as an engineering aggregate. Therefore, this method 1 has not yet been put into practical use although it has been partially tested.
In regard to 2, although some additives designed to modify the properties of the SiO2 containing material have already been placed on the market, they require the installation of supplying facilities and stirring facilities since a large quantity of SiO2 needs to be employed equivalent to substantially 20% of the molten slag. Furthermore, the slag viscosity is increased according to the drop in temperature of the molten slag following the addition, and this is not suitable from the viewpoint of workability and total cost.
The method 3, that is, bringing about a phase change from an α'-type phase to a β-type phase has been studied for many years and a variety of methods have been disclosed. One of these methods, which is the most effective and assured method available at present. [see Japanese Patent Laid-Open No.43690/1978 and the Kawatetsu Engineering Report Vol. 18, No. 1 (1986) 20 to 24] is one in which Si4+ ions are replaced by B3+ ions having a smaller diameter than that of the Si4+ ions contained in the slag.
However, the above-described conventional boron type of slag powdering preventing material is in the form of fine powder and a dehydration/vaporization reaction occurs at the time of contact with the molten slag since the boronic slag powdering preventing material is one containing water. As a result of this, a blowing phenomenon of the slag powdering preventing material is generated, causing the working environment to become excessively worsened and sometimes dangerous. Therefore operation of the work is very difficult.
Furthermore, since the conventional boron type of slag powdering preventing material differs significantly in the chemical composition and properties from slag, differences in viscosity and density from the fused slag can be easily generated, that is, the so-called affinity between the slag and the slag powdering preventing material is not sufficient and thereby the diffusing/mixing performance is insufficient. As a result of such disadvantages, the boron type of slag powdering preventing material cannot be put into practical use although there have been some proposals therefor.
A second problem arises in such iron or steel slag as blast furnace slag in that so-called "yellowish turbid water" is generated when the slag comes into contact with water such as rain or gutter water.
As is well known, blast furnace slag is widely used as various aggregates, particularly as road beds. However, it has been confirmed that if the percentage of sulfur contained in the slag is high, a mistake in the conditions or methods for use will cause yellowish turbid water and hydrogen sulfide smells to be generated due to rain water or gutter water which has been brought into contact with the slag. Particularly in order to ensure that the slag quality for road construction is free from such problems, it is a rule that such slag should not generate any yellowish turbid water or hydrogen sulfide smells. In order to evaluate this fact, a color identification test is employed, and slag should satisfy this test (JIS A 5015 made public on Nov. 1).
The phenomenon of generation of yellowish turbid water is caused from the elution of sulfur (S) contained in the form of calcium sulfide (CaS) which is contained, as a major part, in slag, and is due to generation of yellow polysulfide (such as CaSx) after being applied to a hydrolysis process. Known methods of preventing generation of yellowish turbid water can be exemplified as follows:
1 a method where slag is subjected to aging in which it is oxidized by water and air until it is stabilized;
2 a method in which an oxidant is added to molten slag;
3 a method in which slag is treated with CO2 so that the surface of the slag is stabilized; and
4 a method in which the cooling speed of slag is raised.
In regard to 1, aging treatment takes almost one to three months to be completed, requiring the use of a very broad space (slag yard) for storage.
In regard to 2, several methods can be exemplified such as a method in which a high degree of ferrous oxide is added or a method in which a gas containing oxygen, such as air, is added. However, this method is not preferable since poisonous SO2 gas is generated due to the reaction. Furthermore, with this method, the generation of the yellowish turbid water cannot be sufficiently prevented.
In regard to 3, although the surface of slag can be stabilized, when it is used as ballast this method is disadvantageous in that fused sulfides can again overflow from the fractured surface when it is crushed.
The method 4 is a method in which glass is prepared by degrading, diffusing and rapidly cooling down fused slag so that the included sulfur component is prevented from oozing out. However, this involves such problems as a deterioration in strength and necessitates granulation to below a specific viscosity to form the glass, allowing it to be used as a material for thin aggregates, but making it very difficult to be used as rough aggregates.
Although other methods have been disclosed in which iron, manganese or zinc is, as an effective component, added so that sulfides are fixed, these methods have not been put into practical use due to high costs and insufficient effects.
Therefore, at present, the method 1 in which slag is subjected to aging is the only available method for preventing generation of yellowish turbid water from slag.
Problems to be Solved by the Invention
As can be clearly seen from the above description, this invention is intended to overcome the long time problems of powdering and generation of yellowish turbid water from iron and steel slag by means of an industrially low-cost and convenient slag treatment material.
Therefore, an object of the present invention is collectively to overcome the problems by improving the conventional boron type of powdering prevention material so that the reaction in which Si4+ is replaced by B3+ is further effectively accelerated for the purpose of modifying the properties of slag.
SUMMARY OF THE INVENTION
The inventors of the present invention therefore have investigated improving boron type of slag powdering prevention materials to complete the present invention.
That is, this invention relates to a slag treatment material which modifies properties of iron slag that has resistance against slag powdering during the process of cooling molten slag and against generation of yellowish turbid water when slag is brought into contact with rain water. The treatment material for improving the properties of iron slab is characterized in that it comprises a material obtained by coarsely crushing a substantially dehydrated heat-treated material containing boron.
DETAILED DESCRIPTION OF THE INVENTION Operation
The operation of the present invention will now be described.
The characteristics of the slag treatment material according to the present invention, different from conventionally known crystal hydrated borate powders used to prevent powdering in steel and iron slag, lie in that it comprises a material which is obtained by coarsely crushing a substantially dehydrated heat-treated material (hereinafter referred to as "heat-treated material containing boron"). The affinity of the heat-treated material containing boron of the present invention to molten slag mainly composed of basic calcium silicate (simply termed "slag" hereinafter) occurring in steel or iron making or the like, is superior to a material containing crystal hydrated borate, the precursor of the former. The result in uniformity with slag favorably surpassed the expectations of the inventors of the present invention.
In this case, the heat-treated material containing boron preferably contains a relatively high percentage of boron, it being contained, in many cases, at about 10 wt % or more B2 O3 m preferably about 20 wt % or more.
As a material of the type described above, the following material which has been heat treated can be exemplified:
materials mainly containing two-component type borates such as natural or synthetic alkali borate, alkaline earth metal borate, borosilicate;
materials mainly containing three-component type borosilicates such as alkali borosilicate, alkaline earth metal borosilicate;
materials mainly containing alumino-borosilicates; or
materials mainly containing the four components of boron, silicone, an alkali metal and an alkaline earth metal.
Heat-treated material containing boron refers to material containing at least 80 wt % of the above-described main component, in which case the above-described main component contains at least 10 wt % as B2 O3, or preferably 20 wt % as the effective component.
Therefore, remaining components may comprise at most 20 wt %, such components being exemplified by materials unavoidably involved in mixing during the preparation of the heat-treated material, materials for adjusting properties such as melting points, softening points, viscosities, surface tensions, or materials which can be fixed as sulfides.
Such components can be exemplified by Na2 O, K2 O, Li2 O, CaO, MgO, BaO, SiO2, Fe2 O3, Al2 O3, MnO2, ZnO, P2 O5, CaF2 or materials containing these components.
In the above-described materials those containing alkali metal borates as the major component, are from a practical view point preferably represented by the following general formula: Me2 O.nB2 O3 (wherein Me represents one or two or more types of alkali metal elements selected from Li, K and Na, and n represents the range of the number of moles between 1 and 10). Those containing alkaline earth metal borates as the major component are preferably represented by the following formula: MeO.nB2 O3 (wherein Me represents one or two or more alkaline earth metal elements, n represents the range of the number of moles between 1 and 5). Those containing borosilicates are preferably represented by the following general formula: SiO2.nB2 O3 (wherein n represents the number of moles between 1 and 9). Those containing borosilicates are preferably in the range where B2 O3 : 10 to 80 wt %, SiO2 : 5 to 70 wt %, Me2 O:2 to 50 wt % (however, B2 O3 +SiO2 +Me2 O≧80 wt %) and the others: 0 to 20 wt %. Those containing alkaline earth metal borosilicates are preferably in the range where B2 O3 :20 to 80 wt %, SiO: 10 to 60 wt %, Me2 O:5 to 40 wt % (however B2 O3 +SiO2 +Me2 O≧80 wt. %) and the others: 0 to 20 wt %. Those containing alumino-borosilicates are preferably in the range where B2 O:20 to 60 wt %, SiO2 :5 to 50 wt %, Al2 O3 :2 to 20 wt %, Me2 O:5 to 50 wt % (wherein Me represents an alkali metal or alkaline earth metal, and n represents the valence), (however B2 O3+ SiO2 +Al2 O3 +Me2/n O≧80 wt %) and the others: 0 to 20 wt %. Those containing a material containing boron as the major component of the four component type preferably are in the range where B2 O3 :20 to 60 wt %, Si2 :10 to 50 wt %, Me2 O:3 to 20 wt %, and MeO: 5 to 35 wt %.
The reason for the above lies in that all of the above-described materials containing boron can be easily melted and diffused at the temperature of the molten slag since then the melting points and softening points are in the range of about 1100° C. or less, preferably in the range of 700° to 1050° C. so that the need for the heat treated material containing boron to be quickly melted and diffused in the molten slag can be satisfied due to its composition.
Heat-treated material containing boron here refers to a substantially dehydrated heat treated material which is obtained by sintering or vitrifying a material containing a boron component as the major component. Therefore, sintered materials, glass materials and their mixtures can be included in the heat-treated material containing boron and glass materials are particularly preferable for use in the present invention. Vitrification here refers to materials made amorphous to a degree where they cannot be clearly defined with a specific strength of analyzing rays when X-ray analysis is conducted.
The heat-treated material containing boron according to the present invention is crushed for use, however, this needs to be a material which has been coarsely crushed.
Therefore, although in many cases, the particle size distribution will range from 0.1 mm or larger to fist sized lumps or cullets, a particle distribution where 0.1 to 50 mm particles are 90% or more of the distribution is preferable.
The reason why coarsely crushed treatment material is required according to the present invention lies in that if particle size is 0.1 mm or less, condensation occurs between fine particles, preventing the material from being smoothly melted in the molten slag although this depends upon how it is added to the molten slag. Furthermore, non-melted lumps will sometimes be generated, or a dust phenomenon will occur at the time of addition in the furnace.
On the other hand, although large coarsely crushed treatment material is preferable, in view of uniformly improved properties of slag arising from the stirrings effect caused by the addition thereof to molten slag, if the lumps or cullets exceed fist size then unmelted portions will be generated, a situation that needs to be avoided.
Therefore, a supplement can be, if necessary, mixed with the above-described slag treatment material in order to improve the effects for quickly melting, diffusing and mixing with the molten slag after the slag treatment material has been added.
Such a supplement may be a powder in which dehydrating and/or decarbonizing reactions are generated by applying heat. Powders of the type described above can be exemplified by one or more of materials selected from: aluminosilicates such as clay, activated clay, diatomaceous earth; other aluminosilicates such as bentonite, perlite and zeolite; carbonates or bicarbonates such as limestone, sodium, potassium, calcium, magnesium or barium carbonate; or borates such as borax, kernite, ulexite or colemanite.
Although the mount of addition of the above-described supplement differs according to type, method of adding the slag powdering prevention agent properties and state of the molten slag, it may be up to 30 wt % with respect to the slag powdering prevention agent, and is preferably in the range of from 5 to 15 wt %.
The particle size of this supplement is preferably smaller than that of the slag powdering prevention agent and its mean particle size is preferably smaller than the lower limit of the slag powdering prevention agent.
The slag treatment material according to the present invention can be prepared by mixing a starting material which contains a boron component as the effective component, and heating the thus-mixed material so as to sinter or melt it, followed by cooling and crushing.
The boron type starting material can be exemplified by artificial materials such as boric acid, sodium borate, natural materials such as borax colemanite (Ca2 B6 O11.5-H2 O), ulexite (NaCaB5 O5 O9.8H2 O), tincal (Na2 B4 O7.10-H2 O), and kernite (Na2 B4 O7.4H2 O). The alkaline material can be exemplified by caustic alkali, alkali carbonate and alkali bicarbonate and so on. The alkali earth metallic material can be exemplified by carbonate, hydroxide, and oxides of alkaline earth metal. The silicon material can be exemplified by silica sand quartz sand, diatom, synthetic silica, slag, clay and the like. Other materials can be exemplified by Fe2 O3, Al2 O3, MnO2, P2 O5, fluoride, or materials containing these materials.
The above-described starting materials are properly selected, mixed to achieve the above-described ratio, and supplied to a required fusing furnace or a calcining furnace so as to be heated/fused or calcined. Next, the thus heat-treated material is subjected to particle size adjustment after it has been cooled down whereby a desired product can be obtained.
Although there is no reason for limiting the heating conditions, temperatures must be those at which water of crystallization or adhered water can be, of course, substantially dehydrated, at which the particles of the material can be calcined with each other, and at which they can be fused. Since this temperature differs in accordance with the composition of the material, it may be determined so as to correspond to the specific heat treatment apparatus.
When vitrification is conducted, the most practical and therefore preferable, method of cooling down the fused liquid is tapping the fused liquid while applying pressured water to granulate the slag, and recovering it as sand-like glass. Another method is one in which the fused liquid to be tapped is placed on a belt conveyer and cooled by water or air to be recovered as cullets.
Next, particle size is adjusted after conducting drying so as to remove adhered water. However, in the case of water-granulated material, particle size adjustment by crushing and screening is not necessarily required since dried material per se can be made into product. Therefore, the particle size adjustment need only be conducted if necessary. Sintered material is subjected to particle size adjustment with a conventional crusher.
In this case, the above-described supplement can be mixed in if desired.
Slags to which the present invention is directed ar slags mainly containing basic type calcium silicates that tend to disintegrate or powder when being cooled or subjected to aging, or types that tend to generate yellowish turbid water when brought into contact with water. Such slags generally have a basicity (weight ratio CaO/SiO2) of at least 1.3, preferably within the range between 1.5 and 3.5 and can be exemplified by blast furnace slag, steel slag for such as stainless steel, or converter slag etc.
Although the amount of slag treatment material to be added with respect to the amount of slag differs in accordance with its composition and properties and the composition etc. of the slag it must be at least about 0.15 wt % as B2 O3 for the purpose of either preventing slag powdering or preventing generation of yellowish turbid water, and be preferably 0.3 wt % or more in consideration of durability of modified slag.
The reason for this lies in that, if it is less than about 0.15 wt %, it is not sufficient to prevent generation of yellowish turbid water and occurrence of powdering. On the other hand, there is no reason to define an upper limit. In many oases, it is naturally limited from the viewpoint of economy or affect on molten metal. Therefore, the preferable range from the viewpoint of practical use is from 0.3 wt % to 1.5 wt %.
Slag can be improved by using the slag treatment material according to the present invention without any particular change in the operating conditions of conventional blast furnaces and steel furnaces, and the slag treatment material can be added to molten slag in the presence or non-presence of molten metal it can be understood that this will be very advantageous.
Therefore, when molten iron is delivered from a blast furnace together with a slag through gutters the slag treatment material may be added into a slag accumulated on iron by a dam disposed in the gutter through supplying port being disposed at the desired position on the gutter. Alternatively, it may be added at the time of delivery together with molten slag.
In the case of manufacturing stainless steel or the like, the slag treatment material is added, similar to the above description, during the time the stainless steel is delivered from an electric fusing furnace to a ladle o during time the molten slag is tapped into a slag pot from the ladle.
In this case, the manner of adding the slag treatment material to molten slag is not particularly limited and need only satisfy the necessity that the slag treatment material should be quickly melted and diffused into the molten slag.
For example, a method in which the slag treatment material is added as it is to molten slag in the presence or non presence of molten metal, is a method in which the same is added under air pressure, a method in which it is supplied as bagged or a method in which molten slag is supplied to a place where the slag treatment material has been previously supplied can be employed.
If the slag treatment material is added in the presence of molten metal, the degree of affect on the mixture of boron into the molten metal, etc. can be substantially neglected. This makes application of the slag treatment material according to the present invention particularly advantageous.
Therefore, the slag treatment material is added only into a slag tapped in a slag pot when the above-described affect of boron is expected, but in other cases, it is practical to add it to the slag in the presence of molten metal which has been maintained at high temperature since the viscosity of the molten slag is relatively small, allowing the melting and diffusion of the slag treatment material to be conducted quickly, as a result of which, the improvement in properties of the slag can be uniformly conducted.
If there is a fear of the slag treatment material insufficiently melting or diffusing due to an increase in the viscosity of the molten slag when it is added to a slag pot, re-heating of the slag or addition of the above-described supplement is, if necessary, required for the purpose of assisting diffusion of the slag treatment material.
Therefore, it is substantially unnecessary to provide any special diffusion means for rapidly melting or diffusion of the slag treatment material after it has been added to the molten slag.
As a result, slag whose properties have been improved can be obtained by gradual or rapid cooling in a normal way after the above-described addition has been conducted.
Embodiments
The present invention will now be described with reference to the following embodiments.
EXAMPLE 1 1 Preparation of slag treatment material sample
The material mixture whose composition (by weight) is as follows (Table 1) was melted in an electric furnace, the thus-obtained molten glass was rappidly charged into water, and the thus-obtained glass material was coarsely crushed. The coarsely crushed glass showed a particle size distribution without exception where particle sizes of 5 to 30 mm were 90% or more of the product.
                                  TABLE 1                                 
__________________________________________________________________________
Sample        Boric                Quartz                                 
No. Colemanite                                                            
          Borax                                                           
              acid                                                        
                  K.sub.2 CO.sub.3                                        
                      Li.sub.2 CO.sub.3                                   
                          Mg(OH).sub.2                                    
                               BaCO.sub.3                                 
                                   sand                                   
                                       Alumina                            
__________________________________________________________________________
1         100 72.3                                                        
2             100 49.7                                                    
3             100     26.4                                                
4   100       79.3        84                                              
5             100              94.3                                       
6             100                                                         
7             100                  12.6                                   
8             100                  9.8                                    
9         100                      7                                      
10            100 88               41                                     
11            100     71           160                                    
12  100       4.2                  4.4                                    
13            100         92       19                                     
14            100              64  17                                     
15  100       13.3                 62.6                                   
                                       16.8                               
16            100 32.6    80.4     34.0                                   
                                       11.2                               
17            100              43  79.4                                   
                                       11.2                               
__________________________________________________________________________
Note: Boric acid used was an anhydride. Potassium carbonate, lithium carbonate, magnesium hydroxide, barium carbonate and alumina used were industrial chemical grade. Colemanite was constituted by 45%-B2 O3, 25%-CAO, 4%-SIO2, 24%-Ignition loss and 2%-balance. Borax was constituted by 21.43%- Na2 O, 48.21%-B2 O3 and 29.96%-Ignition loss, both the colemanite and borax being made in Turkey. Quartz sand used was dried 98%-pure SiO2 from Africa.
The major compositions of samples Nos. 1 to 8 are shown in the following table 2.
              TABLE 2                                                     
______________________________________                                    
Sample No.         Glass composition                                      
______________________________________                                    
1                  Na.sub.2 O.5B.sub.2 O.sub.3                            
2                  K.sub.2 O.4B.sub.2 O.sub.3                             
3                  Li.sub.2 O.4B.sub.2 O.sub.3                            
4                  CaO.4B.sub.2 O.sub.3                                   
5                  MgO.B.sub.2 O.sub.3                                    
6                  BaO.3B.sub.2 O.sub.3                                   
7                  SiO.sub.2.7B.sub.2 O.sub.3                             
8                  SiO.sub.2.9B.sub.2 O.sub.3                             
______________________________________
The outline of the chemical compositions (weight %) of samples Nos. 9 to 17 obtained similarly are as follows:
                                  TABLE 3                                 
__________________________________________________________________________
Chemical analysis of Glass Samples Nos. 9 to 17 (weight %)                
Sample No.                                                                
      B.sub.2 O.sub.3                                                     
         Na.sub.2 O                                                       
             K.sub.2 O                                                    
                Li.sub.2 O                                                
                   CaO                                                    
                      MgO                                                 
                         BaO                                              
                            SiO.sub.2                                     
                               Al.sub.2 O.sub.3                           
                                   Residue                                
__________________________________________________________________________
 9    63 28                  9                                            
10    50     30             20                                            
11    35        10          55                                            
12    59           29       10     2                                      
13    55              35    10                                            
14    60                 30 10                                            
15    35           15       39 10  1                                      
16    45     10       25    15 5                                          
17    45                 15 35 5                                          
__________________________________________________________________________
2 Slag modification test
When slag having basicity (CaO/SiO2 =2.10) which is the first molten slag tapped from an electric furnace for manufacturing stainless steel (capacity: 30 tons) was removed i.e., tapped from a ladle to a slag pot, 30 Kg of each of the above slag treatment material test samples were simultaneously supplied in 10 Kg vinyl bags. Next, after the thus-supplied slag was solidified by allowing it to stand at low temperature, the state of the slags were observed until the temperature reached room temperature.
The test conditions are as follows:
              TABLE 4                                                     
______________________________________                                    
                               B.sub.2 O.sub.3                            
     Sam-   Amount of Amount of                                           
                               contained                                  
                                      Temperature                         
Test ple    tapping   sample added                                        
                               in slag                                    
                                      at tapping                          
No.  No.    (t)       (kg/t slag)                                         
                               (wt %) (°C.)                        
______________________________________                                    
 1    1     4.99      6.01     0.51   1443                                
 2    2     4.77      6.29     0.47   1421                                
 3    3     5.76      5.20     0.47   1420                                
 4    4     5.00      6.00     0.50   1407                                
 5    5     3.65      8.21     0.52   1432                                
 6    6     3.68      8.16     0.47   1422                                
 7    7     5.56      5.39     0.48   1442                                
 8    8     5.48      5.48     0.50   1449                                
 9    9     3.71      8.10     0.51   1432                                
10   10     3.26      9.20     0.46   1411                                
11   11     2.23      13.43    0.47   1418                                
12   12     3.38      8.87     0.52   1444                                
13   13     3.37      8.91     0.49   1406                                
14   14     3.46      8.67     0.52   1428                                
15   15     2.21      13.58    0.47   1430                                
16   16     2.81      10.67    0.48   1430                                
17   17     2.65      11.33    0.51   1441                                
18   --     4.12      0        0      1431                                
19   --     4.07      0        0      1406                                
20   --     3.99      0        0      1413                                
______________________________________
After addition of each slag treatment test sample, no dust or gases were generated in any test, such that such addition of slag treatment test sample could be conducted safely. When molten slag was supplied i.e., tapped to the slag pot, excellent diffusion and mixing of the slag treatment test samples were observed.
After allowing each test amount of slag to stand at room temperature for cooling after addition of slag treatment test samples, the state of the slags were observed. Test Nos. 1 to 17 showed no powdering or degradation.
On the other hand, conventional slags of test nos. 18-20 to which no slag treatment materials were added decayed and powdered after being cooled.
The outline of the analyzed value (weight %) of slag used in the test is as follows:
______________________________________                                    
Test No.  CaO      SiO.sub.2  MgO   Al.sub.2 O.sub.3                      
______________________________________                                    
1 to 20   48 to 55 22 to 28   9 to 13                                     
                                    9 to 15                               
______________________________________
In none of the tests, was dust generation observed due to supply of the test samples, and the test samples instantaneously splashed and flowed on the molten slag. The state of the slags were observed after each slag had been allowed to stand and cool to room temperature. No decay or powdering phenomenon were observed it was found that an excellent effect can be obtained by using 0.46 to 0.53 wt % of B2 O3.
EXAMPLE 2 1 Preparation of slag treatment material sample
A fused liquid having the same glass composition as those used as samples Nos. 1, 2 and 4 according to Example 1 was granulated with pressured water, and the resultant crushed glass product was dried. Then the slag treatment materials shown in Table 5 were prepared.
              TABLE 5                                                     
______________________________________                                    
Slag treatment                                                            
            Glass                                                         
material    composition Particle size                                     
______________________________________                                    
18          Na.sub.2 O.5B.sub.2 O.sub.3                                   
                        In all of the samples,                            
19          Li.sub.2 O.4B.sub.2 O.sub.3                                   
                        particles sized from 0.1                          
20          K.sub.2 O.4B.sub.2 O.sub.3                                    
                        to 5 mm shared 90%                                
______________________________________
2 Slag modification test
When slag having basicity (CaO/SiO2 =2.02) which is the first molten slag tapped from an electric furnace for manufacturing stainless steel (capacity: 30 tons) was removed from a ladle to a slag pot, 30 Kg of each of the above slag treatment material test samples were simultaneously supplied in 10 Kg vinyl bags. Next, after the thus-supplied slag was solidified by allowing it to stand at low temperature, the state of the slags were observed until the temperature reached room temperature.
The test conditions are as follows:
              TABLE 6                                                     
______________________________________                                    
                               B.sub.2 O.sub.3                            
     Sam-   Amount of Amount of                                           
                               contained                                  
                                      Temperature                         
Test ple    tapping   sample added                                        
                               in slag                                    
                                      at tapping                          
No.  No.    (t)       (kg/t slag)                                         
                               (wt %) (°C.)                        
______________________________________                                    
21   18     5.20      16.3     0.49   1436                                
22   19     5.53      16.3     0.49   1404                                
23   20     4.39      17.0     0.51   1419                                
24   --     5.49      --       --     1420                                
______________________________________
After addition of each test sample, no dust or gases were generated in any test, and addition work could be conducted safely. When molten slag was supplied to the slag pot, excellent diffusion and mixing were observed.
After allowing each slag to stand at room temperature for cooling after being tested, the state of the slags were observed. Test Nos. 21 to 23 did not show any decay or powdering.
After allowing these slag lumps to stand outdoors for three months, no change was observed.
On the other hand, the conventional slag of test No. 24 to which no slag treatment material was added decayed and powdered when it was cooled.
Comparative Example
In Example 2, borax (Na2 B4 O7.10H2)(B2 O3 :37.00 wt %, Na2 O:16.5 wt %)(particles sized from 0.2 to 0.4. mm comprising 55%) of 12 kg/ton slag was supplied in separate vinyl bags. Intense splash and blow resulted and un-dissolved lumps were generated, causing the supply to be stopped.
EXAMPLE 3 1 Preparation of slag treatment material sample
A fused liquid having the same composition as those used in the test samples 4, 5 and 6 according to Example 1 was granulated with pressured water, and the resultant crushed vitrified product was dried. Then, the slag treatment materials shown in Table 7 were prepared.
              TABLE 7                                                     
______________________________________                                    
Sample   Glass                                                            
No.      composition Particle size                                        
______________________________________                                    
21       MgO.B.sub.2 O.sub.3                                              
                     In all of the samples, particles                     
22       CaO.4B.sub.2 O.sub.3                                             
                     sized from 0.1 to 5 mm shared                        
23       BaO.3B.sub.2 O.sub.3                                             
                     90%                                                  
______________________________________
2 Slag modification test
When slag having basicity (CaO/SiO2 =2.06) which is the first molten slag tapped from an electric furnace for manufacturing stainless steel (capacity: 30 tons) was removed from a ladle to a slag pot, 40 Kg of each of the above slag treatment material test samples were simultaneously supplied in 10 Kg vinyl bags. Next, after the thus-supplied slag was solidified by allowing it to stand at low temperature, the state of the slags were observed until the temperature reached room temperature.
The test conditions are as follows:
              TABLE 8                                                     
______________________________________                                    
                               B.sub.2 O.sub.3                            
     Sam-   Amount of Amount of                                           
                               contained                                  
                                      Temperature                         
Test ple    tapping   sample added                                        
                               in slag                                    
                                      at tapping                          
No.  No.    (t)       (kg/t slag)                                         
                               (wt %) (°C.)                        
______________________________________                                    
25   21     5.28      7.58     0.48   1421                                
26   22     6.80      5.88     0.49   1441                                
27   23     4.91      8.15     0.47   1418                                
28   --     5.54      0        0      1427                                
______________________________________
After addition of each test sample, no dust or gases were generated in any test, and additional work could be conducted safely. When molten slag was supplied to the slag pot, excellent diffusion and mixing were observed.
After allowing each slag to stand at room temperature for cooling after being tested, the state of the slags were observed. Test Nos. 25 to 27 did not show any decay or powdering.
After allowing these slag lumps to stand outdoors for three months, no change was observed.
On the other hand, the conventional slag of test No. 28 to which no slag treatment material was added decayed and powdered when it was cooled.
EXAMPLE 4 1 Preparation to slag treatment material sample
A fused liquid having the same composition as those used in the test samples 7 and 8 according to the Example 1 was granulated with pressured water, and the resultant crushed glass product was dried. Then, the slag treatment materials shown in Table 9 were prepared.
              TABLE 9                                                     
______________________________________                                    
Sample Glass                                                              
No.    composition                                                        
                  Particle size                                           
______________________________________                                    
24     SiO.sub.2.7B.sub.2 O.sub.3                                         
                  In all of the samples, particles                        
25     SiO.sub.2.9B.sub.2 O.sub.3                                         
                  sized from 0.1 mm to 5 mm shared 90%                    
______________________________________
2 Slag modification test
When slag having basicity (CaO/SiO2 =2.13) which is the first molten slag tapped from an electric furnace for manufacturing stainless steel (capacity: 30 tons) was removed from a ladle to a slag pot, 30 Kg of each of the above slag treatment material test samples were simultaneously supplied in 10 Kg vinyl bags. Next, after the thus-supplied slag was solidified by allowing it to stand at low temperature, the state of the slags were observed until the temperature reached room temperature.
The test conditions are as follows
              TABLE 10                                                    
______________________________________                                    
                               B.sub.2 O.sub.3                            
     Sam-   Amount of Amount of                                           
                               contained                                  
                                      Temperature                         
Test ple    tapping   sample added                                        
                               in slag                                    
                                      at tapping                          
No.  No.    (t)       (kg/t slag)                                         
                               (wt %) (°C.)                        
______________________________________                                    
29   24     5.68      5.28     0.47   1415                                
30   25     5.37      5.59     0.51   1445                                
31   --     5.20      0        0      1432                                
______________________________________
After addition of each test sample, no dust or gases were generated in any test, and additional work could be conducted safely. When molten slag was supplied to the slag pot, excellent diffusion and mixing were observed. After allowing each slag to stand at room temperature for cooling after being tested, the state of the slags were observed. Test Nos. 29 to 30 showed no powdering or degradation.
After allowing these slag lumps to stand outdoor for three months, no change was observed.
On the other hand, the conventional slag of Test No. 31 to which no slag treatment material was added decayed and powdered when it was cooled.
EXAMPLE 5 1 Preparation of slag treatment material sample
A fused liquid having the same composition as those used in that according to the Example 1 was fused in an electric furnace, granulated with pressured water, and the resultant slag treatment material shown in Table 11 was prepared.
              TABLE 11                                                    
______________________________________                                    
Sample  Composition (wt %)                                                
No.     B.sub.2 O.sub.3                                                   
                  Li.sub.2 O                                              
                         Na.sub.2 O                                       
                                  K.sub.2 O                               
                                       SiO.sub.2                          
______________________________________                                    
26      34               15            51                                 
27      63               28             9                                 
28      30                        15   55                                 
29      50                        30   20                                 
30      35        10                   55                                 
______________________________________
2 Slag modification test
When slag having basicity (CaO/SiO2 =2.15) which is the first molten slag tapped from an electric furnace for manufacturing stainless steel (capacity: 30 tons) was removed from a ladle to a slag pot, 50 Kg of each of the above slag treatment material test samples were simultaneously supplied in 10 Kg vinyl bags. Next, after the thus-supplied slag was solidified by allowing it to stand at low temperature, the state of the slag were observed until the temperature reached room temperature.
The test conditions are as follows:
              TABLE 12                                                    
______________________________________                                    
                               B.sub.2 O.sub.3                            
     Sam-   Amount of Amount of                                           
                               contained                                  
                                      Temperature                         
Test ple    tapping   sample added                                        
                               in slag                                    
                                      at tapping                          
No.  No.    (t)       (kg/t slag)                                         
                               (wt %) (°C.)                        
______________________________________                                    
32   26     3.27      15.29    0.52   1407                                
33   27     6.30      7.94     0.50   1432                                
34   28     3.19      15.67    0.47   1423                                
35   29     4.90      10.20    0.51   1416                                
36   30     3.65      13.70    0.48   1440                                
37   --     5.22      0        0      1431                                
______________________________________
After addition of each test sample, no dust or gases were generated in any test and additional work could be conducted safely. When molten slag was supplied to the slag pot, excellent diffusion and mixing were observed.
After allowing each slag to stand at room temperature for cooling after being tested, the state of the slags were observed. Test No. 32 to 36 showed no powdering or degradation.
After allowing these slag lumps to stand outdoor for three months, no change was observed.
On the other hand the conventional slag to which no slag treatment material was added decayed and powdered when it was cooled.
EXAMPLE 6 1 Preparation of slag treatment material sample
A fused liquid having the same composition as that used in Example 1 was fused in an electric furnace, granulated with water, and the resultant slag treatment material shown in Table 13 was prepared.
              TABLE 13                                                    
______________________________________                                    
Sample  Composition (wt %)                                                
No.     B.sub.2 O.sub.3                                                   
               CaO      MgO  BaO    SiO.sub.2                             
                                         Na.sub.2 O                       
______________________________________                                    
31      59     29                   10                                    
32      40     30                   25   5                                
33      55              30          10                                    
34      30              15          50   5                                
35      60                   30     10                                    
36      25                   20     44   11                               
______________________________________
2 Slag modification test
When slag having basicity (CaO/SiO2 =2.10) which is the first molten slag tapped from an electric furnace for manufacturing stainless steel (capacity: 30 tons) was removed from a ladle to a slag pot, 40 Kg of each of the above slag treatment material test samples were simultaneously supplied in 10 Kg vinyl bags. Next after the thus-supplied slag was solidified by allowing it to stand at low temperature, state of the slags were observed until the temperature reached room temperature.
The test conditions are a follows:
              TABLE 14                                                    
______________________________________                                    
                               B.sub.2 O.sub.3                            
     Sam-   Amount of Amount of                                           
                               contained                                  
                                      Temperature                         
Test ple    tapping   sample added                                        
                               in slag                                    
                                      at tapping                          
No.  No.    (t)       (kg/t slag)                                         
                               (wt %) (°C.)                        
______________________________________                                    
38   31     4.78      8.37     0.49   1415                                
39   32     3.40      11.76    0.47   1442                                
40   33     4.31      9.28     0.51   1430                                
41   34     2.61      15.33    0.46   1431                                
42   35     4.90      8.16     0.49   1439                                
43   36     2.22      18.02    0.45   1420                                
44   --     3.38      0        0      1443                                
______________________________________
After addition of each test sample, no dust or gases were generated in any test and additional work could be conducted safely. When molten slag was supplied to the slag pot, excellent diffusion and mixing were observed.
After allowing each slag to stand at room temperature for cooling after being tested, the state of the slags were observed. Test Nos. 38 to 43 showed no powdering or degradation.
After allowing these slag lumps to stand outdoors for three months, no change was observed.
On the other hand, the conventional slag of test No. 44 to which no slag treatment material was added decayed and powdered when it was cooled.
EXAMPLE 7 1 Preparation of a sample of slag treatment material
A material whose composition (weight) is as shown below was heated and sintered at a predetermined temperature for 20 minutes in an electric furnace. After this sintering had been completed, the material heated was cooled below 100.C and crushed to prepare a slag treatment material in which particles of from 0.1 to 0.5 mm comprised 90% or more of the material.
                                  TABLE 15                                
__________________________________________________________________________
Sample No. 37 38 39 40 41 42 43 44 45 46                                  
__________________________________________________________________________
Boric acid anhydride                                                      
                 100      100   100   100                                 
Borax anhydride                                                           
           100                                                            
              100   100                                                   
                       100         100                                    
Colemanite(anhydride)                                                     
                     76                                                   
                        76   100                                          
Rare lime  10.4  56.1      50                                             
                              13                                          
                                 80                                       
                                    40                                    
Magnesium oxide                                                           
              5.1                      20                                 
Quartz sand          30                30                                 
Kaolin                 100                                                
                          100       40                                    
Sodium fluoride               39    40                                    
Fluorite                         40    30                                 
Calcining  700                                                            
              700                                                         
                 400                                                      
                    700                                                   
                       700                                                
                          400                                             
                             650                                          
                                400                                       
                                   650                                    
                                      500                                 
Temperature                                                               
__________________________________________________________________________
The materials used were crushed as necessary, and the resultant particle sizes were adjusted to pass through a 16-mesh Tyler reference screen and fit in a 100-mesh screen. As a result, the mixed starting materials shown in Table 15 were prepared to be used as the material for the sintering test. The chemical composition (weight %) of each slag treatment material was as follows:
                                  TABLE 16                                
__________________________________________________________________________
Boric              Quick                                                  
                       Magnesium                                          
                             Quartz  Sodium                               
acid     Borax                                                            
             Colemanite                                                   
                   lime                                                   
                       oxide sand                                         
                                 Kaolin                                   
                                     fluoride                             
                                          Fluorite                        
__________________________________________________________________________
B.sub.2 O.sub.3                                                           
     99.8                                                                 
         69.2                                                             
             60.8                                                         
Na.sub.2 O                                                                
         30.8                        73.8                                 
CaO          33.8  96                     57                              
MgO                    98                                                 
Al.sub.2 O.sub.3                 44.2     0.5                             
SiO.sub.2     5.4            98  54.8     12                              
F                                    45.6 36                              
Residue       2.7  2                      6.7                             
Ig loss            2    2     2  1        3                               
__________________________________________________________________________
Colemanite was made a test sample after it had been completely dehydrated at 600° C.
The compositions of the thus-obtained slag treatment materials were as shown in Table 17, they being strong sintered material.
              TABLE 17                                                    
______________________________________                                    
Composition (wt %)                                                        
Sample                                          Resi-                     
No.   B.sub.2 O.sub.3                                                     
             Na.sub.2 O                                                   
                     CaO  MgO   Al.sub.2 O.sub.3                          
                                      SiO.sub.2                           
                                           F    due                       
______________________________________                                    
37    63     28      9                                                    
38    66     29           5                                               
39    65             35                                                   
40    56.1   15.1    12.3             16.4                                
41    42.5   11.4    9.3        16.7  20.0                                
42    40.5           19.4       18.2  21.9                                
43    37.7   18.6    29.0             3.35 11.1                           
44    45.6           45.5                  14.4 5                         
45    30.5   26.6    17.3       8.0   9.5  8.0                            
46    55.6           9.5  10.9        16.4 7.6                            
______________________________________
2 Slag modification test
When slag having basicity (CaO/SiO2 =2.11) which is the first molten slag tapped from an electric furnace for manufacturing stainless steel (capacity: 30 tons) was removed from a ladle to a slag pot, 40 Kg of each of the above slag treatment material test samples were simultaneously supplied in 5 Kg vinyl bags. Next, after the thus-supplied slag was solidified by allowing it to stand at low temperature, the state of the slags were observed until the temperature reached room temperature.
The test conditions are as follows:
              TABLE 18                                                    
______________________________________                                    
                               B.sub.2 O.sub.3                            
     Sam-   Amount of Amount of                                           
                               contained                                  
                                      Temperature                         
Test ple    tapping   sample added                                        
                               in slag                                    
                                      at tapping                          
No.  No.    (t)       (kg/t slag)                                         
                               (wt %) (°C.)                        
______________________________________                                    
45   37     4.85      8.25     0.52   1412                                
46   38     5.39      7.42     0.49   1437                                
47   39     5.20      7.69     0.50   1429                                
48   40     4.88      8.20     0.46   1442                                
49   41     3.62      11.06    0.47   1437                                
50   42     3.18      12.59    0.51   1441                                
51   43     3.02      13.26    0.50   1423                                
52   44     4.15      9.65     0.44   1416                                
53   45     2.65      15.08    0.46   1429                                
54   46     4.54      8.81     0.49   1428                                
55   --     --        --       --     1435                                
______________________________________
After addition of each test sample, no dust or gases were generated in any test, and additional work could be conducted safely. When molten slag was supplied to the slag pot, excellent diffusion and mixing were observed.
After allowing each slag to stand at room temperature for cooling after being tested, the state of the slags were observed. Test Nos. 45 to 54 showed no powdering or degradation.
After allowing these slag lumps to stand outdoor for three months, no change was observed.
On the other hand the conventional slag of test No. 55 to which no slag treatment material was added decayed and powdered when it was cooled.
Analyzed values of the slag for test (weight %) were as follows:
______________________________________                                    
Test No. CaO      SiO.sub.2  MgO    Al.sub.2 O.sub.3                      
______________________________________                                    
45 to 55 49 to 56 22 to 26   10 to 13                                     
                                    11 to 12                              
______________________________________
EXAMPLE 8
A predetermined amount of slag treatment sample 9 identical to that used in Example 1 was added as packed in plastics film bags to fused slag occurring during tapping from an electric furnace when the slag was being removed from a ladle to a slag pot. After treatment, The slag was made into ballast by adjusting its particle size to a range equivalent to MS-25 after normal cooling by standing.
The presence of yellowish turbid water from the ballast was measured in accordance with the following evaluation method. The results of measurement and the chemical composition (weight %) are shown in Table 19.
              TABLE 19                                                    
______________________________________                                    
Test No.     56      57      58    59    60                               
______________________________________                                    
Amount of slag                                                            
             3.0     3.0     3.0   3.0   3.0                              
(t/ch)                                                                    
Amount of addition                                                        
             --      5       10    15    25                               
(kg/ch)                                                                   
Rate of                                                                   
addition                                                                  
wt %         0       0.17    0.34  0.50  0.83                             
Conversion by B.sub.2 O.sub.3                                             
             0       0.11    0.21  0.32  0.52                             
Chemical composition                                                      
of slag (wt %)                                                            
CaO          27.1    26.5    27.1  24.3  25.6                             
SiO.sub.2    20.6    20.2    20.5  21.1  20.3                             
MgO          15.6    11.0    16.8  15.4  19.7                             
Al.sub.2 O.sub.3                                                          
             28.5    27.3    25.7  25.4  26.1                             
MnO          1.2     1.2     1.1   0.8   1.3                              
TiO.sub.2    0.7     0.8     0.5   0.5   0.6                              
FeO          2.2     0.9     2.6   1.1   2.3                              
S            1.9     2.2     2.3   2.6   2.0                              
P            0.005   0.005   0.005 0.005 0.005                            
Color Identification                                                      
             5.0     0.5     0     0     0                                
Test (yellow index)                                                       
Remarks      Cont.   Comp.   E     E     E                                
______________________________________                                    
 (Cont: Contrast example, Comp: Comparison example, E: Example)
Method of evaluating yellowish turbid water
The thus-obtained 500 g of sample ballast was weighed, placed in 1500 ml of pure water, and boiled for 45 minutes in accordance with a color identification test per JIS A5015. The filtered eluate was put in a color comparing tube so as to be visually tested with reference to a potassium bichromate color reference liquid upon the presence of color. In order to numerize the degree of darkness or lightness of the color of the eluate, that is the degree of the hue of the eluate, the absorbance of the reference liquid and the eluate were measured with a spectraphotometer. The results were evaluated with the thus obtained yellow index as shown in Table 20.
              TABLE 20                                                    
______________________________________                                    
                             Concentration of                             
         Yellow   Absorbance potassium bichromate                         
Hue      Index    (-log T)   reference (g/l)                              
______________________________________                                    
colorless                                                                 
         0        0.022 or less                                           
                             0.002 or less                                
almost   0.5      0.022 to 0.064                                          
                             0.002 to 0.006                               
colorless                                                                 
extremely                                                                 
         1.0      0.064 to 0.113                                          
                             0.006 to 0.011                               
light yellow                                                              
very light                                                                
         1.5      0.113 to 0.181                                          
                             0.011 to 0.018                               
yellow                                                                    
slightly 2.0      0.181 to 0.30                                           
                             0.018 to 0.032                               
light yellow                                                              
light yellow                                                              
         2.5      0.30 to 0.46                                            
                             0.032 to 0.052                               
yellow   3.0      0.46 to 0.80                                            
                             0.052 to 0.10                                
slightly 3.5      0.80 to 1.02                                            
                             0.10 to 0.17                                 
dark yellow                                                               
dark yellow                                                               
         4.0      1.02 to 1.09                                            
                             0.17 to 0.30                                 
very dark                                                                 
         4.5      1.09 to 1.16                                            
                             0.30 to 0.45                                 
yellow                                                                    
brown    5.0      1.16 or more                                            
                             0.45 or more                                 
______________________________________
EXAMPLE 9
Each of slag treatment materials Sample Nos. 1, 3, 12, 15, 18, 25, 26, 27, 28, 29, 30 and 40, each being packed in plastics film bags were added to a fused slag tapped from an electric furnace to comprise 0.40 wt % B2 O3 at the time of being taken out from a ladle to a slag pot. After treatment the respective slags were made into ballast by adjusting particle size to range corresponding to MS-25 after normal cooling by standing.
The ballasts thus-obtained for each treatment material were tested for the generation of yellowish turbid water similar to the above description, with none of them generating yellowish turbid water.
Effect of the Invention
1 Since the slag treatment material according to the present invention comprises coarsely crushed substantially dehydrated heat treated material, especially, vitrified material, it will not generate degassing reactions such as degassing carbon dioxide gas or steam. As a result of this, working environments will not be deteriorated due to blowing or splashing.
2 For similar reasons, there is substantially endothermic heat arising from the fusion of the material heat of vaporation, heat of transition etc. Therefore, the coarsely crushed vitrified material ca be quickly melted into molten slag.
3 Diffusion after being melted into molten slag can be optionally adjusted by using a supplement.
4 The slag treatment material according to the present invention can prevent slag powdering during cooling and substantially prevent generation of yellowish turbid water.
5 The method according to the present invention is very advantageous from a industrial viewpoint since the slag treatment material can be supplied as it is packed in such as a polyvinyl chloride or polyethylene resin bag, that is so-called polybags without requiring any changes in conventional processes.

Claims (1)

What is claimed is:
1. A slag treatment material comprising a material for improving molten slag in such a manner that the resulting fused slag is made resistant against powdering in a cooling process or against generation of yellowish turbid water which is caused when said slag is contacted with rain water, characterized in that: said slag treatment material is formed by coarsely crushing a substantially dehydrated heat treated material containing boron, having a particulate size distribution ranged from 0.1 mm to a first sized mass and melting point below 1,100° C., wherein 90 wt % or more of the particles fall within a range of from 0.1 to 50 mm, and having a melting or softening point ranging from 700° C. to 1050° C., said substantially dehydrated heat treated material being a vitrified material, sintered material or a mixture thereof and consisting essentially of the following components represented by, as oxide form, B2 O3 :20 to 50 wt %, Me2 1 O:3 to 20 wt %, Me2 O:10 to 35 wt %, SiO2 : 20 to 50 wt % (wherein Me1 represents an alkali metal and Me2 represents alkaline earth metal); and the balance (unavoidable contaminants): 0 to 10 wt %;
and that said material when added to a slag and made into a ballast having a range equivalent to MS-25 and eluated in accordance with JIS A5015, provide a spectorphotometric index of less than about 1.0.
US08/124,802 1987-08-04 1993-09-21 Slag treatment material Expired - Lifetime USRE34912E (en)