US20190381208A1 - Removable Film Forming Gel Compositions Featuring Adhesion Promoters - Google Patents

Removable Film Forming Gel Compositions Featuring Adhesion Promoters Download PDF

Info

Publication number
US20190381208A1
US20190381208A1 US16/341,637 US201716341637A US2019381208A1 US 20190381208 A1 US20190381208 A1 US 20190381208A1 US 201716341637 A US201716341637 A US 201716341637A US 2019381208 A1 US2019381208 A1 US 2019381208A1
Authority
US
United States
Prior art keywords
film
gel composition
gel
amine
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/341,637
Other languages
English (en)
Inventor
Katie F. Wlaschin
George W. Griesgraber
Alexi J. Young
Semra Colak Atan
Delony L. Langer-Anderson
Junia M. Pereira
Michael J. Solberg
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Priority to US16/341,637 priority Critical patent/US20190381208A1/en
Assigned to 3M INNOVATIVE PROPERTIES COMPANY reassignment 3M INNOVATIVE PROPERTIES COMPANY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: LANGER-ANDERSON, Delony L., WLASCHIN, KATIE F., COLAK ATAN, SEMRA, YOUNG, Alexi J., GRIESGRABER, GEORGE W., SOLBERG, Michael J., PEREIRA, Junia M.
Publication of US20190381208A1 publication Critical patent/US20190381208A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L26/00—Chemical aspects of, or use of materials for, wound dressings or bandages in liquid, gel or powder form
    • A61L26/0009—Chemical aspects of, or use of materials for, wound dressings or bandages in liquid, gel or powder form containing macromolecular materials
    • A61L26/0019—Chemical aspects of, or use of materials for, wound dressings or bandages in liquid, gel or powder form containing macromolecular materials obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/34—Silicon-containing compounds
    • C08K3/346—Clay
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/34—Silicon-containing compounds
    • C08K3/36—Silica
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/16—Nitrogen-containing compounds
    • C08K5/17—Amines; Quaternary ammonium compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L83/00—Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon only; Compositions of derivatives of such polymers
    • C08L83/04—Polysiloxanes
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2203/00—Applications
    • C08L2203/02—Applications for biomedical use
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2203/00—Applications
    • C08L2203/16—Applications used for films

Definitions

  • the present disclosure provides easy to apply gel compositions that dry to form durable film bandages and other tissues protectants.
  • the film-forming, gel compositions of the present disclosure can be flexible, breathable, waterproof, non-stinging, gentle to skin, and easy to remove by peeling or other wearer generated force.
  • the gel compositions when dried, possess enhanced cohesion and integrity. If desired, the gel compositions are capable of absorbing moisture and wound exudate, particularly blood. Accordingly, the film-forming compositions are particularly well suited for use as a liquid bandage or skin protectant.
  • the gel compositions are useful for protecting or treating skin, tissues, organs, nails, hydrated tissues and mucous membranes, e.g., bleeding injuries, surgical site, skin ulcers, cold sores, cuts, rashes, abrasions, incisions and blisters, abraded gums and other oral surfaces, hemorrhoids and abraded body areas, and other mucosal membrane incisions and wounds.
  • neither the gel composition nor the subsequently-formed films irritate the skin and other tissue during application, drying, or during use after drying.
  • the bandages created are desirably substantially painless while worn and can be easily removed by peeling, if desired, substantially without pain or disturbance of the wound site.
  • the dried bandages formed can exhibit high water vapor transmission throughout.
  • the gel composition when applied over surfaces moist with blood or body fluids, can form a tough, lightly adherent film that can, in certain circumstances, absorb and retain volumes of exudate.
  • the gel compositions of the present disclosure can dry to a relatively thick, flexible film with the desirable wound healing properties (e.g., breathable, flexible, non-stinging) in a single application.
  • a gel composition applied at a 50-120 mil coating thickness to skin at room temperature an adherent film can form having a thickness of at least 2 mils, at least 3 mils, at least 4 mils, at least 5 mils, or at least 6 mils.
  • the gel compositions exhibit a 180 degree peel adhesion from human skin of no greater than 900 grams per square inch according to a Skin Adhesion Test and a keratin removal level of no greater than 40% according to a Skin Removal Test. Accordingly, the dried films can be removed by application of force without substantial damage to the underlying skin or wound site.
  • the gel composition includes a film-forming polymer, a compatible tackifier, an antiseptic, a volatile solvent, and optionally at least one of a cationic polymer acting as a coagulant and an amine-rich adhesion promoter. At least the film-forming polymer and the tackifier are typically soluble in the solvent.
  • the gel composition may be silicone-based, in that the film-forming material includes a silicone-containing polymer.
  • the film-forming polymer may be composed of segmented siloxane copolymers, including silicone polyurea block copolymers and polydiorganosiloxane polyoxamide block copolymers.
  • polymeric materials are typically non-adhesive materials, often having release properties, and can be formulated with silicate tackifying resins (such as MQ resins), amine-rich adhesion promoters, or certain coagulants.
  • silicate tackifying resins such as MQ resins
  • amine-rich adhesion promoters or certain coagulants.
  • a particularly suitable film-forming polymer is a polydiorganosiloxane polyoxamide.
  • the present disclosure provides a film-forming gel composition for use as a conformable film bandage, the composition including a silicone-containing, film-forming polymer; an amine-rich adhesion promoter, and a volatile solvent.
  • a film cast from the composition is self-supporting on a biological substrate and can be peeled off the substrate without substantially compromising the integrity of the film such that at least a portion of the film is removable in a single continuous layer.
  • the present disclosure provides a film useful as a conformable bandage, wherein the film exhibits an upright MVTR of at least 300 g/m 2 /24 hours, a Skin Adhesion of at least 50 g/inch and no greater than 900 g/inch, an elongation of at least 100%, and an ultimate tensile strength of at least 0.3 MPa. At least a portion of the film has a thickness of at least 2 mils and no greater than 20 mils, and the film is self-supporting and consists of a single layer.
  • the film can include: (a) (a) 50-75 wt. % film-forming polymer, (b) 0.1-30 wt. % filler, and
  • compositions comprising “a” cationic antimicrobial agent can be interpreted as a gel composition comprising “one or more” cationic antimicrobial agents.
  • the term “generally”, unless otherwise specifically defined, means that the property or attribute would be readily recognizable by a person of ordinary skill but without requiring absolute precision or a perfect match (e.g., within +/ ⁇ 20% for quantifiable properties).
  • the term “substantially”, unless otherwise specifically defined, means to a high degree of approximation (e.g., within +/ ⁇ 10% for quantifiable properties) but again without requiring absolute precision or a perfect match. Terms such as same, equal, uniform, constant, strictly, and the like, are understood to be within the usual tolerances or measuring error applicable to the particular circumstance rather than requiring absolute precision or a perfect match.
  • polydiorganosiloxane refers to a divalent segment of formula
  • each R 1 is independently an alkyl, haloalkyl, aralkyl, alkenyl, aryl, or aryl substituted with an alkyl, alkoxy, or halo; each Y is independently an alkylene, aralkylene, or a combination thereof;
  • n is independently an integer of 0 to 1500.
  • film-forming refers to a composition when allowed to dry under ambient conditions (e.g., 23° C. and 50% relative humidity (RH)) on skin or mucosal tissue forms a continuous layer that does not flake off after simple flexing of the tissue.
  • ambient conditions e.g., 23° C. and 50% relative humidity (RH)
  • moisture vapor transmission rate also referred to as “water vapor transmission rate” (WVTR)
  • WVTR water vapor transmission rate
  • ready to use refers to the composition intended to be applied (e.g., to skin or mucosal tissue) without dilution. It should be understood that (unless otherwise specified) the listed amounts of all identified components are for “ready to use” gel compositions.
  • active kill means to render a microorganism ineffective by killing (e.g., bacteria and fungi) or otherwise rendering inactive (e.g., viruses) and may be distinguished from disrupting microorganism adhesion or mere bacteriostatic activity.
  • an active kill results in at least a 0.5 log reduction using the Antimicrobial Efficacy Test described herein, and is desirably at least a 1 log reduction, more preferably at least a 2 log reduction, even more preferably at least a 3 log reduction.
  • the concentrations or amounts of the components when considered separately, may not kill to an acceptable level, or may not kill as broad a spectrum of undesired microorganisms, or may not kill as fast; however, when used together such components provide an enhanced (preferably synergistic) antimicrobial activity (as compared to the same components used alone under the same conditions).
  • FIG. 1 is a flow chart of a method of applying a gel composition of the present disclosure to a target site
  • FIG. 2 is a flow chart of another method of applying a gel composition of the present disclosure to a target site
  • FIG. 3 is a flow chart of another method of applying a gel composition of the present disclosure to a target site
  • FIG. 4 is an isometric view of an applicator tip suitable for dispensing gel compositions according to methods of the present disclosure
  • FIG. 5 is an isometric view of another applicator tip suitable for dispensing gel compositions according to methods of the present disclosure
  • FIG. 6 is a flow chart of another method of applying a gel composition of the present disclosure to a target site
  • the present disclosure provides myriad flexible, breathable, non-stinging, gentle to skin, self-supporting, and film-forming compositions.
  • the gel composition used in forming a bandage or other protectant typically includes a silicone-containing, film-forming polymer, a tackifier, a coagulant, an antiseptic, and a volatile solvent. Other compositions may exclude antiseptic, coagulant, or both.
  • the gel compositions of the present disclosure may also include fillers, antibiotics, surfactants, and other additives to enhance user comfort or treatment (e.g., release agents to the underlying area of covered tissue). It is a particular feature of the disclosure that the gel materials can act at room temperature (20° C.) when applied to tissues of a user to form films in minutes or less.
  • the films are conformable, comfortable and can be elastic and flexible.
  • the films do not significantly irritate the skin and mucous membrane when deposited during application and in use after drying.
  • the dried films are substantially painless and can be removed substantially without pain.
  • the dried bandages formed are substantially non-water sensitive and have high moisture vapor transmission therethrough.
  • the bandages can form when applied over surfaces wet with water, blood or body fluids, in short times at standard room temperature and reasonable variants thereof.
  • the use of gel compositions over certain bleeding or exudating wounds provides a stark advantage over previously available compositions, which rely on the maintenance of dry or drier target surfaces.
  • the compositions of the present disclosure also tend to be easier to coat in relatively thicker applications, which are more visible to the user and consequently easier to remove.
  • the combination of features allows the compositions of the present disclosure to cover and protect myriad open wounds.
  • Protectable wounds include, but are not limited to, abrasions, lacerations, scrapes, punctures, burns
  • Certain gel compositions of the present disclosure include one or more of the following characteristics: relatively high levels of bacterial kill if an antimicrobial agent is present (or if the composition is inherently antimicrobial); relatively short dry times; generally clear viewing of the underlying tissue; good adhesion to the skin when dry; little or no tack when dry; capable of releasing an active agent such as an antimicrobial agent or a coagulant; and can be removed relatively easily in a single continuous film, preferably without the need for organic solvent-based removers or other dissolution.
  • the gel compositions may be used to secure medical articles to the skin or other tissue.
  • Useful medical articles that can be secured by dried films resulting from such gel compositions include, but are not limited to: nasal gastric tubes, blood stream catheters, dialysis catheters and tubing stents, surgical tools, tympanoplasty tubes, shunts including shunts for hydrocephalus, post-surgical drain tubes and drain devices, urinary catheters, endotraecheal tubes, other implantable devices, and other indwelling devices.
  • Dry times of the film of the present disclosure are preferably no greater than about 5 minutes, more preferably no greater than about 3 minutes, even more preferably no greater than about 2 minutes, and most preferably no greater than about 1.5 minutes on skin measured at 23° C. at 45-55% relative humidity. Dry time can be considered as the minimum time for a composition applied at a defined coat weight to be visibly dry, demonstrate no transfer of the composition to a latex gloved covered hand, and have a minimum level of tack. Dry time of a given composition can be measured under ASTM D 5895-13, particularly with a circular time drying recorder (Test Method B). Dry time measured under this method may be longer than those experienced on skin.
  • composition may be tack free (in that no composition transfers to a gloved hand) and yet still be not completely dry. Accordingly, tack free times are preferably no greater than about 2 minutes, no greater than about 1 minutes, and in some implementations no greater than about 30 seconds.
  • the desired specific viscosity of the gel composition depends, in part, on the intended application. For example, where application is to be made to a specific position on the skin (e.g., elbow surfaces, knee surfaces and the like), higher viscosity compositions are preferred to prevent “running” of the compositions to unintended locations. Preferred compositions, in present circumstances, of the present disclosure also possess viscosities that ensure the applied gel easily conforms to tissues while drying, does not run, and forms a relatively thick film. For conformable films the viscosity of a gel composition is at least 20,000 Centipoise (cps), at least 50,000 cps, at least 60,000 cps and in yet other embodiments at least 70,000 cps.
  • cps Centipoise
  • the viscosity is no greater than about 1,100,000 cps, no greater than about 800,000 cps, no greater than about 600,000 cps, no greater than about 400,000 cps and in yet other implementations no greater than about 250,000 cps when measured at 23° C. using a Brookfield LVT viscometer and the procedure described in the Examples Section.
  • This viscosity range can, in certain circumstances, ensure that the compositions can be applied to the skin in a uniform film that will dry rapidly and maintain structural integrity throughout wear.
  • compositions may benefit from higher viscosities as applied, in that (along with other variables) the higher viscosity composition may exhibit less settling (i.e., fewer constituents settling out of an otherwise dissolved or dispersed composition).
  • Applicants have found that certain gel compositions with specific viscosity in the range of 200,000 to 500,000 cps (and particularly 250,000 to 400,000 cps) can be easier to apply, position, and dry while still resulting in a protective covering film exhibiting the characteristics and benefits described below.
  • the dried films of compositions of the present disclosure are generally flexible and durable, and relatively lightly adherent. That is, they do not crack or flake off as brittle films might do and they remain on skin without needing desquamation for removal.
  • the film-forming polymer and compatible tackifier contribute to achieving a delicate balance between low tack, breathability, and flexibility.
  • the composition are accordingly useful on surface areas exposed to high levels of movement, e.g., knuckles, knees, elbows, feet and the like.
  • a film of dried gel composition can have a thickness of at least 1, at least 1.5, 2, 4, 8 mils and typically no greater than 25, 20, 15 mils, and 10 mils.
  • the term “mil” refers to 0.001 inch and 1 mil is equal to about 0.0025 centimeters or about 0.025 millimeters or about 25 micrometers. While the gel compositions of the present disclosure can be coated in such a manner as to form a film having a uniform or substantially uniform thickness, variations in, for example, the pressure applied or the applicator used can result in variable thickness throughout the film layer. In presently preferred implementations, the thickness of the film over the target (e.g., wound or skin lesion) is at least 2 mils thick, while areas of the film surrounding the target (e.g., unblemished tissue) may exhibit a relatively thinner film thickness. Certain methods of application, including those described below, can assist in providing a more uniform thickness to normalize dry time and enhance protection.
  • the conformability and durability properties of the dried films can be determined in part by standard tensile and elongation testing.
  • the elongation of the dried film can range from 50, 75, or 100% to 1400%. In some embodiments, the elongation is at least 100% and no greater than 600%.
  • the ultimate tensile strength is typically at least 0.2, 0.3, or 0.4 MPa and is typically no greater than 2 MPa. In some embodiments, the ultimate tensile strength is no greater than 2, 1.5, or 1 MPa.
  • the Young's elastic modulus is typically at least 0.5, 0.6, 0.7, 0.8, 0.9 or 1 MPa and is typically no greater than about 2 MPa. In some embodiments, the Young's elastic modulus of a tested film is at least 0.7 MPa and typically no greater than 1.5 MPa.
  • Such tensile and elongation properties can be measured, for example, by the methods outlined in ASTM D882-12.
  • the dried films of compositions of the present disclosure are also relatively lightly adherent.
  • Suitable films typically exhibit a peel adhesion to skin according to the Skin Adhesion Test, described below, of at least 25 g/inch, in some embodiments at least 50 g/inch, and in some embodiments at least 75 g/inch.
  • Suitable dried films typically exhibit a peel adhesion according to the Skin Adhesion Test of no greater than 1000 g/inch, in some embodiments no greater than 900 g/inch, in some embodiments no greater than 600 g/inch.
  • a relatively light adherent film within the above range is typically capable of remaining on the surface to which is applied during desired wear period and is advantageously also capable of being pulled away (e.g., with user applied force) without causing rupture or tearing of the surface: for biological surfaces such as skin, without removing portions of the epidermis or damaging skin, scars or tissue underneath the film.
  • This can be a significant advantage over silicone-containing liquid bandages of the prior art, which often rely on the normal desquamation at the applied site for adequate removal (see e.g., U.S. Pat. No. 8,197,803 (Salamone et al.)).
  • the dried films cast from the gel compositions of the present disclosure can exhibit moisture vapor transmission rates of at least 300 g/m 2 /24, thus both preventing dehydration of the wounded area and promoting moist wound healing.
  • dry MVTR or upright MVTR
  • dry MVTR or inverted MVTR
  • ASTM E-96-80 at 40° C. and 20% relative humidity using an upright cup method.
  • Wet MVTR or inverted MVTR
  • Factors influencing the MVTR of a dried film from the inventive gel compositions include, but are not limited to, the thickness of the film layer on the tissue, relative amount of solids in the gel composition before application, the formulation of the gel composition, the viscosity of the gel composition, and the coating structure (i.e., continuous film, or pattern) of the gel.
  • the dried films cast from the gel compositions of the present disclosure exhibit a dry MVTR of at least 300 g/m 2 /24 hours, more preferably at least 500 g/m 2 /24 hours, even more preferably at least 1000 g/m 2 /24 hours, and even more preferably at least 1500 g/m 2 /24 hours.
  • the dried films preferably have a wet MVTR of at least 500 g/m2/24 hours, more preferably at least 900 g/m2/24 hours, even more preferably at least 1000 g/m2/24 hours, and even more preferably at least 1300 g/m2/24 hours.
  • Different regions of the film may include different dry and/or wet MVTR values.
  • the gel compositions exhibit the above, enhanced MVTRs even when applied at the greater coating weight with higher percent solids (and having resultant greater film thickness) than common liquid bandages. Thanks in part to this breathability and other components, the dried films of the present composition can enhance wound healing by increasing the rate of wound reepithelization.
  • the gel compositions of this disclosure may be applied to the skin, mucous membranes, etc. in liquid form by utilization of a brush, rod, finger, sponge, cloth, dropper, etc.; in spray or mist form; or any other usable technique for applying a liquid to a surface such as a wipe, swab or solid paddle applicator.
  • the compositions are applied at a wet coat thickness between 25 mils and 150 mils, and in certain implementations between 40 mils and 100 mils. It is typically preferred, after drying, that the resultant films have a thickness of from about 2 to about 20 mils. A relatively thicker film can be advantageous for site protection and ease of removal, but will typically require a longer dry time than relatively thinner films of the same composition.
  • the total solids content of the gel composition is at least 15 wt. %, and in one embodiment is at least 20% wt., and in one embodiment is less than 35% wt. of the total gel composition.
  • the dried films of the present disclosure are self-supporting after a single application of gel composition.
  • a “self-supporting” film exhibits the desired combination of breathability, durability, and flexibility in a single strata and without the application of additional layers of gel composition on an outer surface of a dried film.
  • a “self-supporting” film does not require an additional, flexible backing for continued wear (i.e., at least 8 hours of continuous existence on the skin or other target tissues).
  • One presently desirable film exhibits an upright MVTR of at least 300 g/m 2 /24 hours, a film thickness of at least 2 mils and no greater than 20 mils, a skin adhesion of no greater than 900 g/inch, an elongation of at least 100%, and an ultimate tensile strength of at least 0.4 MPa.
  • Typical gel compositions can comprise (a) 10-15 wt. % film-forming polymer, (b) 3-5 wt. % tackifier (c) 0-0.3 wt. % antiseptic, (d) 0-3% filler, (e) 60-80 wt. % solvent, (0-5 wt. % cationic polymer, and optionally (g) 0.1-2 wt. % silicone surfactant, based on the total weight of the gel composition.
  • Dried films of the present disclosure typically comprise (a) 50-75% film-forming polymer, (b) 15-30 wt. % tackifier (c) 0.1-0.5 wt. % antiseptic, (d) 0-12 wt. % filler, and (e) 0-20 wt. % cationic polymer and optionally (f) 0.5-15 wt. % silicone surfactant, based on the total weight of the dried film.
  • the gel compositions of the present disclosure include a film-forming polymer which is capable of forming a substantially continuous layer upon drying.
  • Suitable film-forming polymers are at least partially soluble in a volatile solvent, and include silicone-containing polymers.
  • Particularly suitable silicone containing polymers include polysiloxane polyamides, silicone polyureas, and silicone polyamines.
  • the film-forming polymer is typically soluble in the solvent system used in the gel composition.
  • a polymer is “soluble” or “solubilized” if the amount of polymer present in the solvent system is completely dissolved in the solvent system without the polymer forming a precipitate or visible, swollen gel particles in solution.
  • the term “solubility limit” is the maximum amount, measured as a percentage of the total weight of the solution, of a given polymer that can be dissolved in a given solvent system.
  • the film-forming polymer can have a solubility limit of at least 5
  • wt. % at least 10 wt. %, at least 15 wt. %, at least 20 wt. %, in the hexamethyldisiloxane (HMDS), isooctane or any other solvent system described herein, based on the total weight of the gel composition.
  • HMDS hexamethyldisiloxane
  • Silicone-containing polymers useful for practicing the present disclosure may have an intrinsic viscosity (“IV”) of at least 0.9, at least 1.45, at least 1.68, or at least 1.8.
  • the silicone containing polymer typically has an intrinsic viscosity less than 3, as polymers having an intrinsic viscosity above 3 can be difficult to solubilize in certain circumstances.
  • Lower IV polymers have notably higher solubility in the solvents and solvent systems and hence, while they can be film formers, they can be slower to dry and remain tacky after application.
  • the IV of the polymers may be controlled by varying initiator, initiator concentration, reaction temperature, reaction solvent, reaction method, and other parameters known to those skilled in the art.
  • Siloxane polymers have unique properties derived mainly from the physical and chemical characteristics of the siloxane bond. These properties include low glass transition temperature, thermal and oxidative stability, resistance to ultraviolet radiation, low surface energy and hydrophobicity.
  • the siloxane polymers often lack tensile strength.
  • the low tensile strength of the siloxane polymers can be improved by forming block copolymers.
  • Some block copolymers contain a “soft” siloxane polymeric block or segment and any of a variety of “hard” blocks or segments.
  • Particularly suitable elastomeric siloxane-based elastomeric polymers are the segmented polymers of Formula 1 and Formula 2 below.
  • the silicone-containing polymer is a linear polydiorganosiloxane, a linear polydiorganosiloxane polyamide block copolymer or a polydiorganosiloxane urethane-containing copolymer, but other silicone-containing polymers may be useful.
  • a polydiorganosiloxane can have a variety of organic substituents on the silicon carbon atoms of the polysiloxane.
  • each organic substituent can be is independently an alkyl, haloalkyl, arylalkylenyl, alkylarylenyl, alkenyl, aryl, or aryl substituted with an alkyl, alkoxy, or halo.
  • the polydiorganosiloxane may have repeating units of the general formula (Si(R 7 ) 2 O—) wherein R 7 is as defined below for any of the embodiments of R 7 in Formula I. Examples include dimethylsilicones, diethylsilicones, and diphenylsilicones.
  • At least 40 percent, and in some embodiments at least 50 percent, at least 60 percent, at least 70 percent, at least 80 percent, at least 90 percent, at least 95 percent, at least 98 percent, or at least 99 percent of the R 7 groups can be phenyl, methyl, or combinations thereof. In some embodiments, at least 40 percent, at least 50 percent, at least 60 percent, at least 70 percent, at least 80 percent, at least 90 percent, at least 95 percent, at least 98 percent, or at least 99 percent of the R 7 groups are methyl.
  • High molecular weight polydimethylsiloxane (PDMS) is commercially available, for example, from Dow Corning Corporation, Midland, Mich.
  • a linear, polydiorganosiloxane polyamide block copolymer useful for practicing the present disclosure contains at least two repeat units of Formula I:
  • each R 7 is independently an alkyl, haloalkyl, arylalkylenyl, alkylarylenyl, alkenyl, aryl, or aryl substituted with an alkyl, alkoxy, or halo.
  • Each Y is independently an alkylene, arylalkylene, alkylarylene, or a combination thereof.
  • Subscript n is independently in a range from 0 to 1500 and subscript p is in a range from 1 to 10.
  • Each group B is independently a covalent bond, an alkylene, an arylalkylene, an alkylarylene, an arylene, or a combination thereof. When each group B is a covalent bond, the polydiorganosiloxane polyamide block copolymer of Formula I is referred to as a polydiorganosiloxane polyoxamide block copolymer.
  • Group G is a divalent group that is the residue unit that is equal to a diamine of formula
  • Group R 8 is hydrogen or alkyl (e.g., an alkyl having 1 to 10, 1 to 6, or 1 to 4 carbon atoms) or R 8 taken together with G and with the nitrogen to which they are both attached forms a heterocyclic group.
  • Each asterisk (*) indicates a site of attachment of the repeat unit to another group in the copolymer such as, for example, another repeat unit of Formula I.
  • Suitable alkyl groups for R 7 in Formula I typically have 1 to 10, 1 to 6, or 1 to 4 carbon atoms.
  • useful alkyl groups include methyl, ethyl, isopropyl, n-propyl, n-butyl, and iso-butyl.
  • Suitable haloalkyl groups for R 7 often have only a portion of the hydrogen atoms of the corresponding alkyl group replaced with a halogen.
  • Examples of haloalkyl groups include chloroalkyl and fluoroalkyl groups with 1 to 3 halo atoms and 3 to 10 carbon atoms.
  • Suitable alkenyl groups for R 7 often have 2 to 10 carbon atoms.
  • alkenyl groups often have 2 to 8, 2 to 6, or 2 to 4 carbon atoms such as ethenyl, n-propenyl, and n-butenyl.
  • Suitable aryl groups for R 7 often have 6 to 12 carbon atoms.
  • Phenyl is an example of an aryl group.
  • the aryl group can be unsubstituted or substituted with an alkyl (i.e., it may be an alklyarylenyl group) (the alkyl group may be, e.g., an alkyl having 1 to 10 carbon atoms, 1 to 6 carbon atoms, or 1 to 4 carbon atoms), an alkoxy (e.g., an alkoxy having 1 to 10 carbon atoms, 1 to 6 carbon atoms, or 1 to 4 carbon atoms), or halo (e.g., chloro, bromo, or fluoro).
  • an alkyl i.e., it may be an alklyarylenyl group
  • the alkyl group may be, e.g., an alkyl having 1 to 10 carbon atoms, 1 to 6 carbon atoms, or 1 to 4 carbon atoms
  • an alkoxy e.g., an alkoxy having 1 to 10 carbon atoms, 1 to 6 carbon atoms, or 1 to
  • Suitable arylalkylenyl and alkylarylenyl groups for R 7 usually have an alkylene group with 1 to 10 carbon atoms and an aryl group with 6 to 12 carbon atoms.
  • the aryl group is phenyl and the alkylene group has 1 to 10 carbon atoms, 1 to 6 carbon atoms, or 1 to 4 carbon atom.
  • R 7 may be an arylalkylenyl group where any of these alkylene groups is bonded to a phenyl group.
  • At least 40 percent, and in some embodiments at least 50 percent, of the R 7 groups are phenyl, methyl, or combinations thereof.
  • at least 60 percent, at least 70 percent, at least 80 percent, at least 90 percent, at least 95 percent, at least 98 percent, or at least 99 percent of the R 7 groups can be phenyl, methyl, or combinations thereof.
  • at least 40 percent, and in some embodiments at least 50 percent, of the R 7 groups are methyl.
  • at least 60 percent, at least 70 percent, at least 80 percent, at least 90 percent, at least 95 percent, at least 98 percent, or at least 99 percent of the R 7 groups can be methyl.
  • the remaining R 7 groups can be selected from an alkyl having at least two carbon atoms, haloalkyl, arylalkylenyl, alkylarylenyl, alkenyl, aryl, or aryl substituted with an alkyl, alkoxy, or halo.
  • Each Y in Formula I is independently an alkylene, arylalkylene, alkylarylene, or a combination thereof.
  • Suitable alkylene groups typically have up to 10 carbon atoms, up to 8 carbon atoms, up to 6 carbon atoms, or up to 4 carbon atoms. Examples of alkylene groups include methylene, ethylene, propylene, butylene, and the like.
  • Suitable arylalkylene and alkylarylene groups usually have an arylene group with 6 to 12 carbon atoms bonded to an alkylene group with 1 to 10 carbon atoms. In some arylalkylene and alkylarylene groups, the arylene portion is phenylene.
  • the divalent arylalkylene or alkylarylene group has phenylene bonded to an alkylene having 1 to 10, 1 to 8, 1 to 6, or 1 to 4 carbon atoms.
  • group Y “a combination thereof” refers to a combination of two or more groups selected from an alkylene and arylalkylene or alkylarylene group.
  • a combination can be, for example, a single alkylarylene bonded to a single alkylene (e.g., alkylene-arylene-alkylene).
  • the arylene is phenylene and each alkylene has 1 to 10, 1 to 6, or 1 to 4 carbon atoms.
  • Each subscript n in Formula I is independently in a range from 0 to 1500.
  • subscript n can be up to 1000, up to 500, up to 400, up to 300, up to 200, up to 100, up to 80, up to 60, up to 40, up to 20, or up to 10.
  • the value of n is often at least 1, at least 2, at least 3, at least 5, at least 10, at least 20, or at least 40.
  • subscript n can be in the range of 40 to 1500, 0 to 1000, 40 to 1000, 0 to 500, 1 to 500, 40 to 500, 1 to 400, 1 to 300, 1 to 200, 1 to 100, 1 to 80, 1 to 40, or 1 to 20.
  • the subscript p is in a range from 1 to 10.
  • the value of p is often an integer up to 9, up to 8, up to 7, up to 6, up to 5, up to 4, up to 3, or up to 2.
  • the value of p can be in the range of 1 to 8, 1 to 6, or 1 to 4.
  • Group G in Formula I is a residual unit that is equal to a diamine compound of formula
  • R 8 HN-G-NHR 8 minus the two amino groups (i.e., —NHR 8 groups).
  • the diamine can have primary or secondary amino groups.
  • Group R 8 is hydrogen or alkyl (e.g., an alkyl having 1 to 10, 1 to 6, or 1 to 4 carbon atoms) or R 8 taken together with G and with the nitrogen to which they are both attached forms a heterocyclic group (e.g., a 5- to 7-membered ring).
  • R 8 HN-G-NHR 8 is piperazine.
  • R 8 is hydrogen or an alkyl.
  • both of the amino groups of the diamine are primary amino groups (i.e., both R 8 groups are hydrogen) and the diamine is represented by formula H 2 N-G-NH 2 .
  • G is an alkylene, heteroalkylene, polydiorganosiloxane, arylene, arylalkylene, alkylarylene, or a combination thereof.
  • Suitable alkylenes often have 2 to 10, 2 to 6, or 2 to 4 carbon atoms.
  • alkylene groups include ethylene, propylene, and butylene.
  • Suitable heteroalkylenes are often polyoxyalkylenes such as polyoxyethylene having at least 2 ethylene units, polyoxypropylene having at least 2 propylene units, or copolymers thereof.
  • polydiorganosiloxanes include polydimethylsiloxanes with alkylene terminal groups.
  • Suitable arylalkylene groups usually contain an arylene group having 6 to 12 carbon atoms bonded to an alkylene group having 1 to 10 carbon atoms.
  • arylalkylene groups are phenylene-alkylene where the phenylene is bonded to an alkylene having 1 to 10 carbon atoms, 1 to 8 carbon atoms, 1 to 6 carbon atoms, or 1 to 4 carbon atoms.
  • alkylarylene groups are alkylene-phenylene where the alkylene having 1 to 10 carbon atoms, 1 to 8 carbon atoms, 1 to 6 carbon atoms, or 1 to 4 carbon atoms is bonded to a phenylene.
  • a combination thereof refers to a combination of two or more groups selected from an alkylene, heteroalkylene, polydiorganosiloxane, arylene, arylalkylene, and alkylarylene.
  • a combination can be, for example, an arylalkylene bonded to an alkylene (e.g., alkylene-arylene-alkylene).
  • the arylene is phenylene and each alkylene has 1 to 10, 1 to 6, or 1 to 4 carbon atoms.
  • the polydiorganosiloxane polyamide is a polydiorganosiloxane polyoxamide.
  • the polydiorganosiloxane polyoxamide tends to be free of groups having a formula
  • any carbonyl group along the backbone of the copolymeric material is bonded to another carbonyl group and is part of an oxalyl group.
  • the polydiorganosiloxane polyoxamide has a plurality of aminoxalylamino groups.
  • the polydiorganosiloxane polyamide is a block copolymer and can be an elastomeric material. Unlike many of the known polydiorganosiloxane polyamides that are generally formulated as brittle solids or hard plastics, the polydiorganosiloxane polyamides can be formulated to include greater than 50 weight percent polydiorganosiloxane segments based on the weight of the copolymer.
  • the weight percent of the diorganosiloxane in the polydiorganosiloxane polyamides can be increased by using higher molecular weight polydiorganosiloxanes segments to provide greater than 60 weight percent, greater than 70 weight percent, greater than 80 weight percent, greater than 90 weight percent, greater than 95 weight percent, or greater than 98 weight percent of the polydiorganosiloxane segments in the polydiorganosiloxane polyamides. Higher amounts of the polydiorganosiloxane can be used to prepare elastomeric materials with lower modulus while maintaining reasonable strength.
  • Some of the polydiorganosiloxane polyamides can be heated to a temperature up to 200° C., up to 225° C., up to 250° C., up to 275° C., or up to 300° C. without noticeable degradation of the material.
  • the copolymers when heated in a thermogravimetric analyzer in the presence of air, the copolymers often have less than a 10 percent weight loss when scanned at a rate 50° C. per minute in the range of 20° C. to 350° C.
  • the copolymers can often be heated at a temperature such as 250° C. for 1 hour in air without apparent degradation as determined by no detectable loss of mechanical strength upon cooling.
  • linear block copolymers having repeat units of Formula I can be prepared, for example by reaction of at least one polydiorganosiloxane-containing precursor with at least one diamine as described in U.S. Pat. No. 7,371,464; incorporated herein by reference.
  • the diamines are sometimes classified as organic diamines or polydiorganosiloxane diamines with the organic diamines including, for example, those selected from alkylene diamines, heteroalkylene diamines (such as polyoxyalkylene diamines), arylene diamines, aralkylene diamines, or alkylene-aralkylene diamines.
  • the diamine has only two amino groups so that the resulting polydiorganosiloxane polyoxamides are linear block copolymers that are often elastomeric, hot melt processable (e.g., the copolymers can be processed at elevated temperatures such as up to 250° C. or higher without apparent degradation of the composition), and soluble in some common organic solvents.
  • the diamine is free of a polyamine having more than two primary or secondary amino groups. Tertiary amines that do not react with the polydiorganosiloxane-containing precursor of can also be present. Additionally, the diamines utilized in the reaction are free of any carbonylamino group. That is, the diamine is not an amide.
  • Preferred alkylene diamines include, but are not limited to, ethylene diamine, propylene diamine, butylene diamine, hexamethylene diamine, 2-methylpentamethylene 1,5-diamine (i.e., commercially available from DuPont, Wilmington, Del.
  • DYTEK A 1,3-pentane diamine (commercially available from DuPont under the trade designation DYTEK EP), 1,4-cyclohexane diamine, 1,2-cyclohexane diamine (commercially available from DuPont under the trade designation DHC-99), 4,4′-bis(aminocyclohexyl)methane, and 3-aminomethyl-3,5,5-trimethylcyclohexylamine.
  • the polydiorganosiloxane polyoxamide copolymer can be produced using a plurality of polydiorganosiloxane precursors, a plurality of diamines, or a combination thereof.
  • a plurality of precursors having different average molecular weights can be combined under reaction conditions with a single diamine or with multiple diamines.
  • the precursor of may include a mixture of materials with different values of n, different values of p, or different values of both n and p.
  • the multiple diamines can include, for example, a first diamine that is an organic diamine and a second diamine that is a polydiorganosiloxane diamine.
  • a single precursor can be combined under reaction conditions with multiple diamines.
  • Any suitable reactor or process can be used to prepare the polydiorganosiloxane polyamide copolymer material.
  • the reaction can be conducted using a batch process, semi-batch process, or a continuous process.
  • Exemplary batch processes can be conducted in a reaction vessel equipped with a mechanical stirrer such as a Brabender mixer, provided the product of the reaction is in a molten state has a sufficiently low viscosity to be drained from the reactor.
  • Exemplary semi-batch process can be conducted in a continuously stirred tube, tank, or fluidized bed.
  • Exemplary continuous processes can be conducted in a single screw or twin screw extruder such as a wiped surface counter-rotating or co-rotating twin screw extruder.
  • the polydiorganosiloxane-containing precursor can be prepared by any known method.
  • this precursor is prepared according to the following reaction scheme, as described in previously cited U.S. Pat. No. 7,371,464 (Sherman et al.).
  • the polydiorganosiloxane diamine can be prepared by any known method and can have any suitable molecular weight.
  • polydiorganosiloxane polyamides including polydiorganosiloxane diamines and particularly polydiorganosiloxane polyoxamide
  • suitable polydiorganosiloxane polyamides including polydiorganosiloxane diamines and particularly polydiorganosiloxane polyoxamide
  • U.S. Pat. No. 8,586,668 Leir et al
  • U.S. Pat. No. 5,214,119 Leir et al.
  • U.S. Pat. No. 5,461,134 Leir et al.
  • U.S. Pat. No. 5,512,650 Leir et al.
  • U.S. Pat. No. 7,371,464 Sherman et al.
  • silicone elastomers include polydiorganosiloxane polyuria. copolymers and blends thereof, such as those described in U.S. Pat. Nos. 5,461,134 and 6,007,914 (Joseph et al.).
  • Silicone-polyurethane copolymers (SPU) useful as film-forming polymers in the compositions and methods according to the present disclosure include block copolymers comprising silicone blocks and secondblocks derived from a multifunctional isocyanate. At points herein the term silicone-polyurea may be used interchangeable with silicone-polyurethane.
  • Useful silicone polyurea block copolymers are disclosed in, e.g., U.S. Pat. Nos.
  • Blocks derived from an isocyanate may have two functional groups (e.g., —NHCONH— or —NHC(O)O—) attached to a divalent organic radical (such as alkyl groups, cycloalkyl groups, and aryl groups, containing from 1 to 30 carbon atoms).
  • a divalent organic radical such as alkyl groups, cycloalkyl groups, and aryl groups, containing from 1 to 30 carbon atoms.
  • Examples of useful diisocyanate compounds from which second blocks may be derived are ethylene diisocyanate, 1,6-hexylene diisocyanate, 1,12-dodecylene diisocyanate, 4,4′-diphenylmethane diisocyanate, 3,3′-dimethoxy-4,4′-diphenylmethane diisocyanate, 3,3′-dimethyl-4,4′-diphenylmethane diisocyanate, 4,4′-diphenyl diisocyanate, toluene-2,6,-diisocyanate, mixtures of toluene-2,6-diisocyanate and toluene-2,4-diisocyanate, 1,4-cyclohexylene diisocyanate, 4,4′-dicyclohexylmethane diisocyanate, 3,3′-diphenyl-4,4′-biphenylene diisocyanate, 4,4′-bipheny
  • Silicone blocks include those having the general formula (Si(R 7 ) 2 O—) wherein R 7 is as defined above for any of the embodiments of R 7 in Formula I.
  • Non-limiting examples include dimethylsilicones, diethylsilicones, and diphenylsilicones.
  • Polydiorganosiloxane urethane-containing copolymers (a subset of the class of SPU materials) useful in compositions of the present disclosure contain soft polydiorganosiloxane units, hard polyisocyanate residue units, terminal groups and optionally soft and/or hard organic polyamine residue units.
  • Some polydiorganosiloxane urea-containing copolymers are commercially available under the trade designation “GENIOMER 140” available from Wacker Chemie AG, Germany.
  • the polyisocyanate residue is the polyisocyanate minus the —NCO groups
  • the organic polyamine residue is the organic polyamine minus the —NH groups
  • the polyisocyanate residue is connected to the polydiorganosiloxane units or organic polyamine residues by urea linkages.
  • the terminal groups may be non-functional groups or functional groups depending on the purpose of the polydiorganosiloxane urea segmented copolymer.
  • the polydiorganosiloxane urethane containing copolymers useful as polymer processing additives contain at least two repeat units of Formula II
  • each R 9 is a moiety that independently is an alkyl, cycloalkyl, aryl, perfluoroalkyl, or a perfluoroether group.
  • alkyl has about 1 to 12 carbon atoms and may be substituted with, for example, trifluoroalkyl, vinyl, a vinyl radical or higher alkenyl represented by the formula —R 10 (CH 2 ) a CH ⁇ CH 2 wherein R′° is —(CH 2 ) b — or —(CH 2 ) c CH ⁇ CH— and a is 1, 2 or 3; b is 0, 3 or 6; and c is 3, 4 or 5.
  • cycloalkyl has about 6 to 12 carbon atoms and may be substituted with one or more alkyl, fluoroalkyl, or vinyl groups.
  • aryl has about 6 to 20 carbon atoms and may be substituted with, for example, alkyl, cycloalkyl, fluoroalkyl and vinyl groups.
  • the perfluoroalkyl group is as described in U.S. Pat. No. 5,028,679, wherein such description is incorporated herein by reference, and the perfluoroether-containing group is as described in U.S. Pat. Nos.
  • R 9 is a fluorine-containing group is as described in U.S. Pat. No. 5,236,997, wherein such description is incorporated herein by reference.
  • at least 50% of the R 9 moieties are methyl radicals with the balance being monovalent alkyl or substituted alkyl radicals having 1 to 12 carbon atoms, alkenylene radicals, phenyl radicals, or substituted phenyl radicals.
  • each Z′ is arylene, arylalkylene, alkylene, or cycloalkylene.
  • the arylene or arylalkylene has from about 6 to 20 carbon atoms.
  • alkylene or cycloalkylene radical has from about 6 to 20 carbon atoms.
  • Z′ is 2,6-tolylene, 4,4′-methylenediphenylene, 3,3′-dimethoxy-4,4′-biphenylene, tetramethyl-m-xylylene, 4,4′-methylenedicyclohexylene, 3,5,5-trimethyl-3-methylenecyclohexylene, 1,6-hexamethylene, 1,4-cyclohexylene, 2,2,4-trimethylhexylene, or mixtures thereof.
  • each Y′ is independently alkylene, arylalkylene, alkylarylene, or arylene.
  • alkylene has from 1 to 10 carbon atoms.
  • the arylalkylene, alkylarylene, or arylene has from 6 to 20 carbon atoms.
  • each D is independently hydrogen, an alkyl radical having 1 to 10 carbon atoms, phenyl, or a radical that completes a ring structure including B′ or Y′ to form a heterocycle.
  • B is a polyvalent radical selected from the group consisting of alkylene, arylalkylene, alkylarylene, cycloalkylene, phenylene, polyalkylene oxide (e.g., polyethylene oxide, polypropylene oxide, polytetramethylene oxide, and copolymers and mixtures thereof).
  • polyalkylene oxide e.g., polyethylene oxide, polypropylene oxide, polytetramethylene oxide, and copolymers and mixtures thereof.
  • “s” is a number that is 0 to about 1000
  • “r” is a number that is equal to or greater than 1
  • “q” is a number that is about 5 or larger, in some embodiments about 15 to 2000, and in some embodiments about 30 to 1500.
  • linear block copolymers having repeat units of Formula I and polymdiorganolsiloxane urea containing polymers of Formula II can be prepared, for example, as discussed in U.S. Pat. No. 8,552,136 (Papp et al.).
  • silicone containing polymers include those formed from silanols, silicone hydrides, siloxanes, epoxides, and (meth)acrylates.
  • the film-forming polymer is prepared from (meth)acrylate-functional siloxanes, the polymer is sometimes referred to as a siloxane (meth)acrylate.
  • other amphiphilic siloxy-containing polymers have been reported as useful in gel compositions (U.S. Pat. No. 7,795,326 (Salamone et al.)), wherein the hydrophobic siloxysilane monomer is copolymerized with a hydrophilic nitrogen-containing monomer.
  • siloxy-containing polymers include block copolymers of polydimethylsiloxane and polyurethane, and block copolymers of polydimethylsiloxane and poly(ethylene glycol).
  • other potentially viable film-forming polymers include block copolymers of polystyrene and ethylene/butylene, block copolymers of polystyrene and polyisobutylene, block copolymers of polystyrene and polyisoprene, block copolymers of polystyrene and polybutadiene, block copolymers of polydimethylsiloxane and polyurethanes, polymers of C4-C18 acrylates and methacrylates, butyl rubber, polyisobutylene, and combinations thereof.
  • TRIS 3-methacryloyloxypropyltris(trimethylsiloxy)silane
  • TRIS can be used in combination with both hydrophilic comonomers, such as N-isopropylacrylamide (NIPAM), or hydrophobic comonomers, such as methyl methacrylate, such that the resulting copolymers are soluble in a volatile solvent.
  • hydrophilic comonomers such as N-isopropylacrylamide (NIPAM)
  • hydrophobic comonomers such as methyl methacrylate
  • the film-forming polymer is typically present in quantities of at least 5 wt. % and no greater than 30 wt. %, based on the total weight of the gel composition, or any amount within that range. In certain implementations, it may be preferred that the film-forming polymer is present at a concentration of at least 12 wt. % and no greater than 25 wt. %, based on the total weight of the gel composition.
  • a dried film cast form the gel composition may include an amount of film-forming polymer in a range from 50 wt. % to 70 or 75 wt. % relative to a total weight of the dried film, or any amount within that range.
  • gel compositions may feature polymerizable cyanoacrylate monomers as the primary film-forming polymer.
  • Cyanoacrylate monomers that may be used include readily polymerizable alpha-cyanoacrylates, including alkyl cyanoacrylates, aryl cyanoacrylates, alkoxyalkyl cyanoacrylates, such as butyl cyanoacrylate and n-butyl cyanoacrylate in particular, octyl cyanoacrylate and 2-octyl cyanoacrylate in particular, ethyl cyanoacrylate, methyl cyanoacrylate, n-dodecyl cyanoacrylate, phenyl 2-cyanoacrylate, methoxyethyl 2-cyanoacrylate, and the like.
  • the composition may be composed of one or more polymerizable cyanoacrylate monomers.
  • Film-forming cyanoacrylates are as discussed in U.S. Pat. No. 6,183,593 (Narang et al.) and U.S. Pat. No. 6,143,805 (Hickey et al.).
  • Polymerizable cyanoacrylate esters in particular are described in U.S. Publication No. 2008/0152614 (Dunshee).
  • Further cyanoacrylate compositions are also disclosed by U.S. Pat. No. 5,480,935 (Greff et al.).
  • Tackifiers such as silicate tackifying resins can be added to the film-forming polymer to provide or enhance the adhesive properties of the composition.
  • the silicate tackifying resin can influence the physical properties of the resulting gel composition. For example, as silicate tackifying resin content is increased, the glassy to rubbery transition of the gel composition occurs at increasingly higher temperatures.
  • a plurality of silicate tackifying resins can be used to achieve desired performance.
  • Suitable silicate tackifying resins include those resins composed of the following structural units M (i.e., monovalent R′ 3 SiO 1/2 units), D (i.e., divalent R′ 2 SiO 2/2 units), T (i.e., trivalent R′SiO 3/2 units), and Q (i.e., quaternary SiO 4/2 units), and combinations thereof.
  • Typical exemplary silicate resins include MQ silicate tackifying resins, MQD silicate tackifying resins, and MQT silicate tackifying resins. These silicate tackifying resins usually have a number average molecular weight in the range of 100 to 50,000 or in the range of 500 to 15,000 and generally have methyl R′ groups.
  • MQ silicate tackifying resins are particularly suitable for several gel compositions of the present disclosure.
  • MQ silicate tackifying resins are copolymeric resins having R′ 3 SiO 1/2 units (“M” units) and SiO 4/2 units (“Q” units), where the M units are bonded to the Q units, each of which is bonded to at least one other Q unit.
  • Some of the SiO 4/2 units (“Q” units) are bonded to hydroxyl radicals resulting in HOSiO 3/2 units (“T OH ” units), thereby accounting for the silicon-bonded hydroxyl content of the silicate tackifying resin, and some are bonded only to other SiO 4/2 units.
  • MQ silicate tackifying resins can be prepared by the silica hydrosol capping process described in U.S. Pat. No. 2,676,182 (Daudt et al.) as modified according to U.S. Pat. No. 3,627,851 (Brady), and U.S. Pat. No. 3,772,247 (Flannigan). These modified processes often include limiting the concentration of the sodium silicate solution, and/or the silicon-to-sodium ratio in the sodium silicate, and/or the time before capping the neutralized sodium silicate solution to generally lower values than those disclosed by Daudt et al.
  • the neutralized silica hydrosol is often stabilized with an alcohol, such as 2-propanol, and capped with R 3 SiO 1/2 siloxane units as soon as possible after being neutralized.
  • the level of silicon bonded hydroxyl groups (i.e., silanol) on the MQ resin may be reduced to no greater than 1.5 weight percent, no greater than 1.2 weight percent, no greater than 1.0 weight percent, or no greater than 0.8 weight percent based on the weight of the silicate tackifying resin. This may be accomplished, for example, by reacting hexamethyldisilazane with the silicate tackifying resin. Such a reaction may be catalyzed, for example, with trifluoroacetic acid. Alternatively, trimethylchlorosilane or trimethylsilylacetamide may be reacted with the silicate tackifying resin, a catalyst not being necessary in this case.
  • the tackifier is typically added to the composition to at least 2 wt. %, in some embodiments at least 3 wt. %, in some embodiments at least 4 wt. %, in some embodiments at least 5 wt. %, based on the total weight of the gel composition.
  • the tackifier is typically present in composition at no greater than 20 wt. %, more preferably no greater than 15 wt. %, and most preferably no greater than 10 wt. % based on the total weight of the composition.
  • a dried film cast form the gel composition may include an amount of tackifier in a range from 5 wt. % to 25 or 30 wt. % relative to a total weight of the dried film, or any amount within that range.
  • films featuring less than 16 wt. % tackifier exhibit less adhesion to skin or other tissue than may be desired.
  • the gel composition includes a cationic polymer that acts as a coagulant and repository for a certain volume of exudate.
  • This cationic polymer typically comprises a crosslinked, guanidinyl-containing polymer.
  • the base polymer in the guanidinyl-containing polymer typically comprises a polyamine polymer; i.e., a polymer having primary or secondary amino groups that may be pendent or catenary, i.e., in the polymer chain.
  • the aminopolymers contain primary or secondary amine groups and can be prepared by chain growth or step growth polymerization procedures with the corresponding monomers. These monomers can also, if desired, be copolymerized with other monomers.
  • the polymer can also be a synthesized or naturally occurring biopolymer. If any of these polymers, irrespective of source, do not contain primary or secondary amine groups, these functional groups can be added by the appropriate graft chemistry.
  • Useful aminopolymers are water soluble or water-dispersible.
  • water soluble refers to a material that can be dissolved in water. The solubility is typically at least about 0.1 gram per milliliter of water.
  • water dispersible refers to a material that is not water soluble but that can be emulsified or suspended in water.
  • amino polymers suitable for use which are prepared by chain growth polymerization include, but are not limited to: polyvinylamine, poly(N-methylvinylamine), polyallylamine, polyallylmethylamine, polydiallylamine, poly(-aminomethylstyrene), poly(4-aminostyrene), poly(acrylamide-co-methylaminopropylacrylamide), and poly(acrylamide-co-aminoethylmethacrylate).
  • amino polymers suitable for use which are prepared by step growth polymerization include, but are not limited to: polyethylenimine, polypropylenimine, polylysine, polyaminoamides, polydimethylamine-epichlorohydrin-ethylenediamine, and any of a number of polyaminosiloxanes, which can be built from monomers such as aminopropyltriethoxysilane, N-(2-aminoethyl)-3-aminopropyltrimethoxysilane, N-trimethoxysilylpropyl-N-methylamine, and bis(trimethoxysilylpropyl)amine.
  • Useful aminopolymers that have primary or secondary amino end groups include, but are not limited to, those formed from polyamidoamine (PAMAM) and polypropylenimine: e.g., DAB-Am and PAMAM dendrimers (or hyperbranched polymers containing the amine or quaternary nitrogen functional group).
  • PAMAM polyamidoamine
  • PAMAM dendrimers or hyperbranched polymers containing the amine or quaternary nitrogen functional group.
  • Exemplary dendrimeric materials formed from PAMAM are commercially available under the trade designation StarburstTM (PAMAM) dendrimer” (e.g., Generation 0 with 4 primary amino groups, Generation 1 with 8 primary amino groups, Generation 2 with 16 primary amino groups, Generation 3 with 32 primary amino groups, and Generation 4 with 64 primary amino groups) from Aldrich Chemical, Milwaukee, Wis.
  • Dendrimeric materials formed from polypropylenimine is commercially available under the trade designation “DAB-AM” from Aldrich Chemical.
  • DAB-Am-4 is a generation 1 polypropylenimine tetraamine dendrimer with 4 primary amino groups
  • DAB-Am-8 is a generation 2 polypropylenimine octaamine dendrimer with 8 primary amino groups
  • DAB-Am-16 is a generation 3 polypropylenimine hexadecaamine with 16 primary amino groups
  • DAB-Am-32 is a generation 4 polypropylenimine dotriacontaamine dendrimer with 32 primary amino groups
  • DAB-Am-64 is a generation 5 polypropylenimine tetrahexacontaamine dendrimer with 64 primary amino groups.
  • aminopolymers suitable for use which are biopolymers include chitosan, and starch, where the latter is grafted with reagents such as methylaminoethylchloride.
  • aminopolymers suitable for use include polyacrylamide homo- or copolymers with amino monomers including aminoalkyl(meth)acrylate, (meth)acrylamidoalkylamine, and diallylamine.
  • aminopolymers include polyaminoamides, polyethyleneimine, polyvinylamine, polyallylamine, and polydiallylamine.
  • Suitable commercially available aminopolymers include, but are not limited to, polyamidoamines such as ANQUAMINETM360, 401, 419, 456, and 701 (Air Products and Chemicals, Allentown, Pa.); LUPASOLTM polyethylenimine polymers such as FG, PR 8515, Waterfree, P, PS (BASF Corporation, Resselaer, N.Y.); polyethylenimine polymers such as CORCATTM P-600 (EIT Company, Lake Wylie, S.C.); polyoxyalkyleneamines such as JEFFAMINE.TM D-230, D-400, D-2000, HK-511 (XTJ-511), XTJ-510 (D-4000), XTJ-500 (ED-600), XTJ-502 (ED-2003), T-403, XTJ-509 (T-3000), and T-5000 (Huntsman Corporation, Houston, Tex.); and polyamide resins such as the VERSAMID series of resins that are formed
  • the coagulant may be prepared by condensation of the polyamine polymer with a guanylating agent.
  • guanylating agents include: cyanamide; O-alkylisourea salts such as O-methylisourea sulfate, O-methylisourea hydrogen sulfate, O-methylisourea acetate, O-ethylisourea hydrogen sulfate, and O-ethylisourea hydrochloride; chloroformamidine hydrochloride; 1-amidino-1,2,4-triazole hydrochloride; 3,5-dimethylpyrazole-1-carboxamidine nitrate; pyrazole-1-carboxamidine hydrochloride; N-amidinopyrazole-1-carboxamidine hydrochloride; and carbodiimides, such as dicyclohexylcarbodiimide, N-ethyl-N′-(3-dimethylaminopropyl)carbodiimide,
  • the polyamine polymer may also be acylated with guanidino-functional carboxylic acids such as guanidinoacetic acid and 4-guanidinobutyric acid in the presence of activating agents such as EDC (N-[3-(dimethylamino)propyl]-3-ethylcarbodiimide hydrochloride), or EEDQ (2-ethoxy-1-ethoxycarbonyl-1,2-dihydroquinoline).
  • EDC N-[3-(dimethylamino)propyl]-3-ethylcarbodiimide hydrochloride
  • EEDQ 2-ethoxy-1-ethoxycarbonyl-1,2-dihydroquinoline
  • the cationic polymer may be prepared by alkylation with chloroacetone guanyl hydrazone, as described in U.S. Pat. No. 5,712,027.
  • Reagents for the preparation of biguanide-functional polymers include sodium dicyanamide, dicyanodiamide and substituted cyanoguanidines such as N 3 -p-chlorophenyl-NLcyanoguanidine, N 3 -phenyl-N′-cyanoguanidine, N 3 -alpha-naphthyl-N′-cyanoguanidine, N 3 -methyl-N′-cyanoguanidine, N 3 ,N 3 -dimethyl-N′-cyanoguanidine, N 3 -(2-hydroxyethyl)-N′-cyanoguanidine, and N 3 -butyl-M-cyanoguanidine.
  • substituted cyanoguanidines such as N 3 -p-chlorophenyl-NLcyanoguanidine, N 3 -phenyl-N′-cyanoguanidine, N 3 -alpha-naphthyl-N′-cyanoguanidine, N 3 -methyl
  • Alkylene- and arylenebiscyanoguanidines may be utilized to prepare biguanide functional polymers by chain extension reactions.
  • the preparation of cyanoguanidines and biscyanoguanidines is described in detail in Rose, F. L. and Swain, G. J. Chem Soc., 1956, pp. 4422-4425.
  • Other useful guanylating reagents are described by Alan R. Katritzky et al., Comprehensive Organic Functional Group Transformation , Vol. 6, p. 640. Generally, such guanylation reagents are used in amounts sufficient to functionalize 0.5 to 100 mole percent, preferably 2.5 to 50 mole percent, of the available amino groups of the aminopolymer.
  • the resulting polymer will have pendent or catenary guanidinyl groups of the formula III:
  • R 2 is a H, C 1 -C 12 alkyl, C 5 -C 12 (hetero)aryl, or a residue of the polymer chain;
  • each R 3 is independently H, C 1 -C 12 alkyl, or C 5 -C 12 (hetero)aryl,
  • each R 4 is H, C 1 -C 12 alkyl or alkylene, C 5 -C 12 (hetero)aryl or (hetero)arylene, cyano, or —C( ⁇ NH)—N(R 2 )—Polymer, and
  • the guanidinyl-containing polymer can be crosslinked.
  • the amino-containing polymer can be crosslinked prior to reaction with the guanylating agent.
  • the guanidinyl-containing polymer can be crosslined by reaction of a crosslinker with remaining amino groups from the amino-containing polymer precursor or with some of the guanidinyl groups.
  • Suitable crosslinkers include amine-reactive compounds such as bis- and polyaldehydes such as glutaraldehyde, bis- and polygylcidylethers such as butanedioldiglycidylether and ethyleneglycoldiglycidylether, polycarboxylic acids and their derivatives (e.g., acid chlorides), polyisocyanates, formaldehyde-based crosslinkers such as hydroxymethyl and alkoxymethyl functional crosslinkers, such as those derived from urea or melamine, and amine-reactive silanes, such as 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 5,6-epoxyhexyltriethoxysilane, (p-chloromethyl)phenyltrimethoxysilane, chloromethyltriethoxysilane, 3-isocyanatopropyltriethoxysilane, and 3-thiocyanato
  • the gel composition comprises a hemostatic agent, such as a polymerizable cyanoacrylate monomer.
  • a hemostatic agent such as a polymerizable cyanoacrylate monomer.
  • Other coagulants include microfibrillar collagen, chitosan, bone wax, ostene, oxidized cellulose and thrombin.
  • coagulants are typically present in quantities of at least 0.5 wt. % and no greater than 20 wt. %, based on the total weight of the gel composition, or any amount within that range. In certain implementations, it may be preferred that the coagulant is present at a concentration of at least 1 wt. % and no greater than 15 wt. %, and in yet other embodiments at least 1.5 wt. % and no greater than 10 wt. %, based on the total weight of the gel composition, or any amount within that range.
  • a dried film cast form the gel composition may include an amount of coagulant in a range from 5 wt. % to 30 or 35 wt. % relative to a total weight of the dried film, or any amount within that range.
  • the coagulant may remain in the film during treatment, at the surface thereof, may migrate into the wound or target area to assist for localized coagulation, or some combination thereof.
  • the film can act, in these circumstances, as a coagulant delivery system to the underlying target area.
  • Silicone surfactants typically include polydimethylsiloxane (PDMS) fluids and/or organomodified PDMS fluids such as siloxane polyether copolymers.
  • PDMS polydimethylsiloxane
  • organomodified PDMS fluids such as siloxane polyether copolymers.
  • PDMS surfactant is a monocarboyxldecyl terminated polydimethylsiloxane, (available as MCR-B-12 from Gelest LTD, Kent, UK).
  • Other suitable PDMS surfactants include Abil Quat 3272, available from Evonik Goldschmidt, Germany.
  • Another suitable surfactant is dimethoxymethylsilylpropyl-polyethylene Imine—50% in IPA, available from Gelest.
  • the silicone surfactant can improve adhesion of the gel (and the resultant dried film) to tissue.
  • silicone surfactants are typically present in quantities of at least 0.1 wt. % and no greater than 15 wt. %, based on the total weight of the gel composition.
  • a dried film cast from the gel composition may include an amount of silicone surfactant in a range from 1 wt. % to 15 or 20 wt. % relative to a total weight of the dried film, or any amount within that range.
  • silicone surfactant is present in quantities of no greater than 0.25 wt. %, based on the total weight of the gel composition. Applicants have found some evidence that, in contrast to the expected stabilization, the inclusion of greater than 0.25 wt. % can (in certain circumstances) decrease the stability of the composition over an otherwise expected storage life.
  • the gel compositions of the present disclosure may include an amine-rich adhesion promoter.
  • the amine-rich adhesion promoter can, in presently preferred circumstances, be an aminosilicone.
  • Other suitable amine-rich adhesion promoters include polymeric cationic ammonium compounds such as polyhexamethylene biguanide (i.e., polyaminopropyl biguanide) and certain of the aminopolymers described above that serve as the base for guanidynl-containing coagulants.
  • amine number represents the number of milliliters of 0.1N HCl needed to neutralize 10 g of the amine-rich adhesion promoter. Amine number is preferably calculated according to the following equation:
  • the adhesion promoter has an amine number greater than 20, in some embodiments greater than 25, in some embodiments greater than 30, in some embodiments greater than 40, in some embodiments greater than 45, and in some embodiments greater than 50.
  • the amine content of the adhesion promoter appears, among other parameters and characteristics of the promoter, to be directly correlated with improved adhesion to skin. Accordingly, adhesion promoters suitable for use in the gel compositions of the present advantageously typically include a greater number of available amine groups and an attendant, larger amine number.
  • aminosilicone means any amine functionalized silicone; i.e., a silicone containing at least one primary amine, secondary amine, tertiary amine, or a quaternary ammonium group. Typically, these are silicones which have been chemically modified so that some of the pendant groups along the backbone have been replaced with various alkylamine groups (—R—NH2). These amine groups can become positively charged in aqueous solutions because of their electron-donating tendencies, yielding an inorganic, cationic polymer.
  • Useful aminosilicones are typically water soluble or water-dispersible.
  • Exemplary aminosilicones for use in embodiments of the present disclosure can be linear polymers, branched polymers, copolymers, and mixtures thereof.
  • the copolymer is a block copolymer.
  • the aminosilicone has one or more amine groups pendant from the polymer backbone. Examples of such embodiments are illustrated by compounds of formula IV with pendant mono-amines and compounds of Formula VI with pendant di-amines, as shown herein below.
  • the polymer has amine groups at one or more termini of the polymer. Examples of such embodiments are illustrated by compounds of Formula V, as shown herein below.
  • Aminosilicones may further be selected from the group comprising, aminodimethicones, trimethylsilylamodimethicones, aaminoethylaminopropylsiloxane-dimethylsloxane copolymers, and mixtures thereof.
  • an aminosilicone has the structure of Formula IV:
  • R is C 1 -12 (preferably C 1 -6) alkyl, the blocks bearing the subscripts x and y may be randomly mixed, the total value of x is from 10 to 5,000, for example 58 or 100 or 118, and the total value of y is from 2 to 20, preferably 2 to 11, for example 4 or 11.
  • x is 58 and y is 4; x is 100 and y is 4; or x is 118 and y is 11.
  • R is a linear C 3 H 6 group.
  • one or more aminosilicones have the structure of formula V, which features terminal amine groups:
  • R and R′ which may be the same or different, are each saturated, linear or branched alkyl groups of 1 to 12 carbon atoms (in presently preferred circumstances, 1 to 6 carbon atoms), e.g., a linear C 3 H 6 group.
  • R and R′ which may be the same or different, are each saturated, linear or branched alkyl groups of 1 to 12 carbon atoms (preferably 1 to 6), e.g., R is a linear C 3 H 6 group and R′ is a linear C 2 H 4 group.
  • the selected aminosilicone has one or more di- or mono-amine groups pendant from the polymer backbone.
  • compositions of the present invention can comprise at least one silicone quaternary compound selected from silicone quaternium-12 (available, for example, as PECOSIL Calif.-1240, a reaction product of cocamidopropyldimethylamine and Dimethicone PEG-7 acetyl chloride, from Phoenix Chemical, Somerville, N.J.), silicone quaternium-8 (available, for example, as PECOSIL AD-3640 silicone quaternium-19 (available, for example, as ZENESTER Q, a functionalized cationic polymeric silicone polyester made from the reaction of a cationic dimethicone copolyol and a dimer acid, from Zenitech, Ontario, Calif.), silicone quaternium-22 (available as Abil T quat 60), silicone quaternium-80 (available as Abil T Quat 3272), and mixtures thereof.
  • silicone quaternium-12 available, for example, as PECOSIL Calif.-1240, a reaction product of cocamidopropyldimethylamine and Dimethicone
  • Particularly preferred quaternary silicones include those sold as PECOSIL AD-3640 and PECOSIL Calif.-1240, each having the formula:
  • gel compositions of the present disclosure may require relatively more of a given quaternary silicone to achieve the same skin adhesion performance as a suitable aminosilicone, holding other components of the composition constant. Furthermore, such composition may still benefit from the presence of a tackifier.
  • Linear PEIs are commercially available and/or can be made according to known methods.
  • An exemplary branched PEI fragment can be represented by Formula IX, below:
  • branched PEIs typically contain many compounds of this general type as a mixture.
  • Branched PEI can be synthesized by the ring opening polymerization of aziridine. Branched PEIs are commercially available and/or can be made according to known methods.
  • Dendrimeric PEI is a special case of a branched PEI.
  • An exemplary (generation 4) dendrimeric PEI is represented by Formula X, below:
  • the PEI contains only primary and tertiary amino groups.
  • Dendrimeric PEIs are commercially available and/or can be made according to known methods.
  • the amine-rich adhesion promoter may comprise, consist essentially of, or even consist of, a silylated aminopolymer.
  • the silylated aminopolymer may be a polyamine having at least one silane or alkoxysilane moiety attached anywhere within the polyamine.
  • Silylated polyamines can be prepared, for example, by reaction of an amine-reactive organosilane coupling agent with at least some of the primary amines present in an aminopolymer, such as branched PEI.
  • Exemplary amine-reactive organosilane coupling agents include: 3-isocyanatopropyltriethoxysilane; 3-isocyanatopropyltrimethoxysilane; 2-isocyanatoethyltriethoxysilane; 2-isocyanatoethyltrimethoxysilane; 3-acryloxypropyltriethoxysilane; 3-acryloxypropyltrimethoxysilane; 2-acryloxyethyltriethoxysilane; 2-acryloxyethyltrimethoxysilane; 3-glycidoxypropyltriethoxysilane; 3-glycidoxypropyltrimethoxysilane; 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane; and 2-(3,4-epoxycyclohexyl)ethyltriethoxysilane.
  • the silylated polyamine may be, but is not limited to, silylated polyethylenimine (SPEIm), silylated polyvinylpyridine, silylated polydimehtylaminoethylmethacrylate, silyated polyvinylamine, silylated polyallylamine (PAAm) or combinations thereof.
  • the silylated polyamine comprises or is trimethoxysilylpropyl modified polyethylenimine.
  • amine-rich adhesion promotors are typically present in quantities of at least 0.5 wt. % and no greater than 20 wt. %, based on the total weight of the gel composition, or any amount within that range. In certain implementations, it may be preferred that the amine-rich adhesion promoter is present at a concentration of at least 1 wt. % and no greater than 15 wt. %, and in yet other embodiments at least 1.5 wt. % and no greater than 10 wt. %, based on the total weight of the gel composition, or any amount within that range.
  • a dried film cast form the gel composition may include an amount of amine-rich adhesion promoter in a range from 5 wt. % to 30 or 35 wt. % relative to a total weight of the dried film, or any amount within that range.
  • the adhesion promoter is typically added to the composition to at least 2.5 wt. %, in some embodiments at least 4 wt. %, in some embodiments at least 5 wt. %, based on the total weight of the gel composition.
  • the amine-rich adhesion promoter is typically present in composition at no greater than 35 wt. %, more preferably no greater than 25 wt. %, and most preferably no greater than 20 wt. % based on the total weight of the composition.
  • a dried film cast form the gel composition lacking coagulant or tackifier may include an amount of amine-rich adhesion promoter in a range from 10 wt. % to 55 or 60 wt. % relative to a total weight of the dried film, or any amount within that range.
  • the coating gel composition further comprises a volatile solvent.
  • the volatile solvent is selected from the group consisting of volatile linear and cyclic siloxanes, volatile polydimethylsiloxanes, isooctane, octane, and combinations thereof.
  • the solvent is typically at least 40 wt. % of the total gel composition.
  • the solvent is desirably volatile and non-stinging.
  • at least 60 wt. % of the total composition is the solvent.
  • the solvent is present in at least 70 wt. % of the total composition.
  • the solvent system for the gel compositions of the present disclosure can be a non-polar, volatile solvent such as isooctane.
  • Other exemplary volatile solvent systems include a linear siloxane or a cyclic siloxane, such as hexamethyldisiloxane (HMDS), octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, and octamethyltrisiloxane, or a linear, branched or cyclic alkane, such as propane, isobutane, liquid butane (e.g., under pressure), pentane, hexane, heptane, octane, petroleum distillates, cyclohexane, fluorocarbons, such as trichloromonofluoromethane, dichlorodifluoromethane, dichlorotetrafluoroethane, tetrafluoroethane, hepta
  • volatile has its standard meaning, that is, it can evaporate rapidly at normal temperatures and pressure.
  • a solvent can be volatile if one metric drop (1/20 mL, 50 mu L) of the solvent will evaporate completely between 20-25° C. within 5 minutes, or within 4 minutes, or within 3 minutes, or within 2 minutes, or within 1 minute, or within 30 sec, or within 15 sec.
  • non-polar, volatile solvents alone or in combination, as the primary liquid phase of the gel composition can provide a desirable balance between fast drying and reduced skin irritation during application.
  • the solvent is one of HMDS and isooctane.
  • Other, more polar solvents such as ethanol, isopropanol, glycerin, N-methylpyrrolidone, and N,N-dimethylacetamide can be used in other implementations, where a non-stinging gel composition is either unnecessary or undesirable.
  • aprotic solvents have utility including acetates such as methyl and ethyl acetate, propylene glycol diacetate, volatile ketones such as acetone and methyl ethyl ketone, volatile ethers such as diethyl ether, ethyl propyl ether, dipropyl ether and dipropylene glycol dimethyl ether, volatile fluorocarbons, such as pentafluoropropane, perfluoroheptane, perfluoromethylcyclohexane and the like; or a volatile gas, such as carbon dioxide, can also be employed, each with varying degrees of user discomfort.
  • acetates such as methyl and ethyl acetate, propylene glycol diacetate
  • volatile ketones such as acetone and methyl ethyl ketone
  • volatile ethers such as diethyl ether, ethyl propyl ether, dipropyl ether and dipropylene glycol
  • water may be included in a solvent system, which can be useful in solublizing certain active agents and hemostats.
  • a relatively small amount of water is present in the gel composition, such as at least 0.1 wt. %, based on the total weight of the composition.
  • the water content is at least 60 wt. %, based on the total weight of the composition, though such composition may require longer dry times than presently desired.
  • Certain solvent systems including water are exemplified in U.S. Pat. No. 7,651,990 (Asmus), and U.S. Pat. No. 8,338,491 (Asmus et al.).
  • the gel compositions of the present disclosure may include filler.
  • suitable fillers are naturally occurring or synthetic materials including, but not limited to: quartz (i.e., silica, SiO 2 ); nitrides (e.g., silicon nitride); glasses and fillers derived from, for example, Zr, Sr, Ce, Sb, Sn, Ba, Zn, and Al; feldspar; borosilicate glass; kaolin (china clay); talc; zirconia; titania; and submicron silica particles (e.g., pyrogenic silicas such as those available under the trade designations AEROSIL, including “OX 50,” “130,” “150” and “200” silicas from Degussa Corp., Akron, Ohio and CAB-O-SIL M5 and TS-720 silica from Cabot Corp., Tuscola, Ill.).
  • Organic fillers made from polymeric materials are also possible, such as disclosed in PCT Publication No.
  • Clay materials suitable for use in compositions, methods, and articles of the present disclosure can include those in the geological classes of the smectites, the kaolins, the illites, the chlorites, the serpentines, the attapulgites, the palygorskites, the vermiculites, the glauconites, the sepiolites, and the mixed layer clays.
  • Smectites for example, can include montmorillonite, bentonite, pyrophyllite, hectorite, saponite, sauconite, nontronite, talc, beidellite, and volchonskoite.
  • Kaolins can include kaolinite, dickite, nacrite, antigorite, anauxite, halloysite, indellite and chrysotile.
  • Illites for example, include bravaisite, muscovite, paragonite, phlogopite and biotite.
  • Chlorites for example, can include corrensite, penninite, donbassite, sudoite, pennine and clinochlore.
  • Mixed layer clays for example, can include allevardite and vermiculitebiotite. Variants and isomorphic substitutions of these layered clay minerals offer unique applications.
  • a typical gel composition of the present disclosure includes at least one of kaolin and fumed silica.
  • the inclusion of fumed silica can enhance the ability of the gel composition to form a substantially level film surface and ease of removing the dried film by peel.
  • Appropriate amounts of filler will be familiar to those skilled in the art, and will depend upon numerous factors including, for example, the polymer(s) utilized, the type of filler, and the intended treatment area(s) of the gel composition.
  • filler will be added at a level of about 1% to about 20% by weight (preferably, about 3% to about 15% by weight), based upon the total weight of the gel composition, or any amount within that range.
  • a dried film cast form the gel composition may include an amount of filler in a range from 0.1 wt. % to 30 wt. % relative to a total weight of the dried film, or any amount within that range.
  • antiseptic and/or antibiotic agents may be suspended or otherwise dispersed in the gel composition.
  • the antiseptic is a cationic antimicrobial agent including an effective amount of one or more antimicrobial agents selected from the group consisting of biguanides and bisbiguanides such as chlorhexidine, alexidine, and their various salts including but not limited to the digluconate, diacetate, dimethosulfate, and dilactate salts, as well as combinations thereof polymeric cationic ammonium compounds such as polyhexamethylenebiguanide salts; small molecule quaternary ammonium compounds such as benzalkonium halides; cationic antimicrobial dyes; and compatible combinations thereof.
  • biguanides and bisbiguanides such as chlorhexidine, alexidine, and their various salts including but not limited to the digluconate, diacetate, dimethosulfate, and dilactate salts, as well as combinations thereof polymeric cationic ammonium compounds such as polyhexamethylenebiguan
  • Particularly useful cationic antimicrobial agents include benzalkonium chloride, chlorhexidine gluconate, octenidine dihydrochloride, cetyl pyridinium chloride, cetrimonium bromide, benzethonium chloride, polyhexamethylene biguanide salt, methylene blue, toluidiene blue, cationic dyes and compatible combinations thereof. Additional details regarding exemplary cationic antimicrobial agents may be found in International Publication No. WO2014/008264 (Parthasarathy et al.)
  • the antiseptic agent is typically added to the composition at a concentration of at least 0.01 wt. %, in some embodiments at least 0.05 wt. %, in some embodiments at least 0.1 wt. %, in some embodiments at least 0.2 wt. %, in some embodiments at least 0.5 wt. %, in other embodiments at least 0.6 wt. %, in yet other embodiments at least 1.0 wt. % and in yet other implementations at least 1.5 wt. %, in some cases exceeding 2 wt. %., based on the total weight of the gel composition.
  • the composition comprises not greater than 10 wt. %, more preferably no greater than 8 wt.
  • a potential range for antiseptic agent concentration to enhance active kill is at least 0.1 wt. % and no greater than 1.0 wt. %, based on the total weight of the composition.
  • a dried film cast form the gel composition may include an amount of antiseptic agent in a range from 0.1 wt. % to 4 wt. % relative to a total weight of the dried film, or any amount within that range. It should be appreciated that the above concentrations relate to the total amount of cationic agent in the composition, even if a plurality of cationic antimicrobial agents are used.
  • the gel composition can have a synergistic antimicrobial effective amount of an antiseptic surfactants, particularly straight chain 1,2-alkanediols having a chain length in the range of 5 to 10 carbon atoms.
  • an antiseptic surfactants particularly straight chain 1,2-alkanediols having a chain length in the range of 5 to 10 carbon atoms.
  • 1,2-alkanediols include, 1,2-pentanediol, 1,2-hexanediol, 1,2-heptanediol, 1,2-octanediol, 1,2-nonanediol, and 1,2-decanediol, and combinations thereof.
  • One exemplary suitable 1,2-octanediol composition includes 3-[(2-ethylhexyl)oxy]-1,2-propanediol, and is sold as SENSIVA SC-10 by Schülke& Mayr GmbH, Germany.
  • the inclusion of straight chain 1,2-alkanediols can reduce the tendency of certain cationic antimicrobial agents (e.g., benzethonium chloride) to crystallize in a dried film.
  • the straight chain 1,2-alkanediols can prolong the availability of the antimicrobial agent, in that the active kill time is enhanced.
  • a dried film cast form the gel composition may include an amount of antiseptic surfactant in a range from 0.5 wt. % to 2 wt. % relative to a total weight of the dried film, or any amount within that range.
  • a particularly cogent property of certain gel compositions including an antiseptic agent is the ability to reduce the bacterial load on tissue, particularly skin (e.g., to kill the natural skin flora).
  • the dried film achieves at least 1 log reduction of a target microorganism in 2 hours when evaluated by the Antimicrobial Efficacy Test described below.
  • the compositions achieve a 2 log reduction.
  • the compositions achieve a 3 log reduction.
  • the target organisms comprise Pseudomonas aeruginosa, Staphylococcus aureus, Escherichia coli , and methicillin-resistant Staphylococcus aureus .
  • residual antimicrobial efficacy is provided to any surface formed from the dried gel composition.
  • the dried film provides an active kill for an extended period of time during the life of the film.
  • anti-infective agents such as nano-silver particles and silver sulfadiazine, may also be added to gel compositions of the present invention. Such anti-infective agents can be added as suspended solids to the coating polymer in the volatile solvent. Topical antibiotics such as neomycin, polymyxin B, and bacitracin can also be included.
  • anti-itch agents such as chamomile, eucalyptus, camphor, menthol, zinc oxide, talc, and calamine
  • anti-inflammatory agents such as corticosteroids
  • antifungal agents such as terbinafine hydrochloride and miconazole nitrate
  • non-steriodal anti-inflammatory agents such as ibuprofen
  • Essential oils can also be added as flavoring agents, aromatic agents, or antimicrobial agents, including thymol, menthol, sandalwood, cinnamon, jasmine, lavender, pine, lemon, rose, eucalyptus, clove, orange, mint, spearmint, peppermint, lemongrass, bergamot, citronella, cypress, nutmeg, spruce, tea tree, wintergreen, vanilla, and the like.
  • the dried film may contain entrapped active biological or pharmaceutical ingredients for controlled release to a biological surface.
  • antimicrobials agents useful as antiseptics include phenolic antiseptics such as parachlorometaxylenol (PCMX), triclosan, hexachlorophene, and others disclosed in U.S. Pat. No.
  • PCMX parachlorometaxylenol
  • triclosan triclosan
  • hexachlorophene hexachlorophene
  • fatty acid monoesters of glycerin and propylene glycol such as glycerol monolaurate, glycerol monocaprylate, glycerol monocaprate, propylene glycol monolaurate, propylene glycol monocaprylate, propylene glycol moncaprate, C 8 -C 12 alkyl monoethers of glycerin and propylene glycol such as 2-ethylhexyl glycerin ether (available from Schuelke Mayr, Norderstedt, Germany, under the trade designation “SENSIVA SC 50”), natural oil antiseptics; C 6 -C 12 alkyl and aryl carboxylic acids; quaternary silanes, silver, silver salts such as silver chloride, silver oxide silver sulfadiazine, copper, copper salts, and combinations thereof.
  • actives agents or drugs
  • actives agents include those capable of local or systemic effect when administered to the skin.
  • Some examples include buprenorphine, clonidine, diclofenac, estradiol, granisetron, isosorbide dinitrate, levonorgestrel, lidocaine, methylphenidate, nicotine, nitroglycerine, oxybutynin, rivastigmine, rotigotine, scopolamine, selegiline, testosterone, tulobuterol, and fentanyl.
  • antiinflammatory drugs both steroidal (e.g., hydrocortisone, prednisolone, triamcinolone) and nonsteroidal (e.g., naproxen, piroxicam); bacteriostatic agents (e.g., chlorhexidine, hexylresorcinol); antibacterials (e.g., penicillins such as penicillin V, cephalosporins such as cephalexin, erythromycin, tetracycline, gentamycin, sulfathiazole, nitrofurantoin, and quinolones such as norfloxacin, flumequine, and ibafloxacin); antiprotazoals (e.g., metronidazole); antifungals (e.g., nystatin); coronary vasodilators; calcium channel blockers (e.g., nifedipine, diltiazem); bronchodilators
  • bacteriostatic agents e.
  • antimigraine agents e.g., ergotamine, melatonin, sumatriptan, zolmitriptan
  • antiarrhythmic agents e.g., flecainide
  • antiemetics e.g., metaclopromide, ondansetron, granisetron hydrochloride
  • anticancer agents e.g., methotrexate
  • neurologic agents such as anxiolytic drugs; anti-obesity agents; dopamine agonists (e.g., apomorphine); GnRH agonists (e.g., leuprolide, goserelin, nafarelin); fertility hormones (e.g., hCG, hMG, urofollitropin); interferons (e.g., interferon-alpha, interferon-beta, interferon-gamma, pegylated interferon-alpha); and the like, as well as pharmaceutically acceptable salts and
  • compositions may further contain fibrous reinforcement and colorants such as dyes, pigments, and pigment dyes.
  • suitable fibrous reinforcement include PGA microfibrils, collagen microfibrils, and others as described in U.S. Pat. No. 6,183,593.
  • suitable colorants as described in U.S. Pat. No. 5,981,621 include 1-hydroxy-4-[4-methylphenylamino]-9,10-anthracenedione (FD&C violet No. 2); disodium salt of 6-hydroxy-5-[(4-sulfophenyl)oxo]-2-naphthalenesulfonic acid (FD&C Yellow No. 6); 9-(o-carboxyphenyl)-6-hydroxy-2,4,5,7-tetraiodo-3H-xanthen-3-one, disodium salt, monohydrate (FD&C Red No. 3); and the like.
  • florescent dyes and pigments can also be beneficial in enabling the coating to be viewed under black-light.
  • the coating could be substantially clear and transparent under normal lighting so the site can be easily viewed and inspected for changes in the skin.
  • the site can be inspected by the use of a backlight wand or flashlight which reveals the coating by its florescence.
  • a particularly useful hydrocarbon soluble fluorescing dye is 2,5-bis(5-tert-butyl-2-benzoxazolyl) 1 thiophene. Fluorescing dyes, such as rhodamine, may also be bound to cationic polymers and incorporated as part of the coagulant.
  • the gel compositions of the present disclosure may advantageously be provided in a kit.
  • the kit may contain an applicator, a wound cleaning solution, and an absorbent material.
  • the gel composition is arranged in the kit in a vial or other rupturable package separate from the applicator.
  • the applicator is pre-loaded with the gel composition (e.g., in a delivery reservoir).
  • a treatment protocol may involve skin preparation prior to applying the gel compositions of the present disclosure.
  • the target site is preferably dried, e.g., blotted dry, and then a lightly adherent polymeric film is formed over this site by applying the gel composition.
  • the composition Sufficient amounts of the composition are employed to cover (i.e., coat) the entire target site with a layer of the gel composition. It is typically preferred that the resultant dried film have a thickness from about 4 to about 15 mills. The resultant film typically covers at least the entire area of the wound or other target site, but may not under other circumstances. If necessary, excess gel can be removed with a wipe or tissue paper before drying.
  • the gel composition can applied from a single dose product or by use of a multiple use dispenser which governs the amount of material applied onto a unit area.
  • the dispenser described in U.S. Pat. No. 5,558,560 (Benedict) is one example of a dispenser suitable for dispensing a viscous composition through use of a squeeze-tube and applicator tip.
  • the dispenser is suited for dispensing a gel composition having a viscosity of 200,000 to 500,000 cps (particularly 250,000 to 400,000 cps) and a wet coat weight of 50 to 120 mils at a generally uniform thickness.
  • the controlled dispersal of the gel composition include, by way of example, a spray applicator, brush, wipe, swab or solid paddle applicator, applicators for repeated and intermittent use of the gel composition and the like.
  • a spray applicator e.g., those featuring a dispensing tip and a squeeze-tube
  • the gel composition can be conveniently stored at ambient conditions and can be provided in sterile form.
  • One suitable method 10 for applying the gel composition to the wound or other target site is set out in FIG. 1 .
  • At the outset at least the area around the target site is cleaned and dried (Step 20 ). Due to the conformability and breathability of the dried films of the present disclosure, drying the wound itself can be optional, depending on the amount of fluid exiting the wound site. In certain embodiments, a dried film may retain up to 1 mL of blood or exudate without detaching from the body. For moderate to severe bleeding wounds, the site is typically cleaned and dried prior to application.
  • a first quantity of gel composition in an applicator 12 is dispensed at an area proximate the target site 11 and a substantially continuous layer 13 of the gel composition is created by drawing the applicator across the target site 11 while dispensing the composition from the tip 14 (Step 30 ). In certain circumstances, it may be desirable to hold the applicator tip 14 above the target site without making contact with the tissue. Such vertical displacement may not be required for minor scrapes or skin lesions.
  • the applicator is manipulated to sever the connection between the layer 13 and the applicator tip. (Step 40 ). The user may also sever the connection by hand or other tool.
  • the layer 13 possesses dimensions sufficient to entirely cover the target site. Multiple layers, however, may be used for larger wounds or smaller applicator tips.
  • the continuous layer 13 has a substantially continuous thickness of about 100 mil as applied. Once the desired amount of gel is dispensed, the composition is allowed to dry to a film (typically 2-5 minutes).
  • the method 100 of FIG. 2 includes the steps of a) cleaning and dry at least the area around the target site (Step 120 ); dispensing a first quantity of gel composition at an area proximate the target site 110 and creating a substantially continuous layer 113 of the gel composition by drawing the applicator across the target site 110 while dispensing the composition (Step 130 ) and severing the connection between the layer 113 and the applicator tip 114 . (Step 140 ).
  • the user may tap the film around the periphery of the target to effect and enhance a seal around the target. (Step 150 ).
  • the user may wet the finger surface with a topical antiseptic or antibiotic composition for increased protection against infection or contamination.
  • surface depressing tools may be used such as Q-tips, tongue depressors, and foam applicators.
  • the method 200 includes the steps of a) cleaning and dry at least the area around the target site (Step 220 ); dispensing a first quantity of gel composition at an area proximate the target site 210 and creating a substantially continuous layer 213 of the gel composition by drawing an applicator 212 across the target site 210 while dispensing the composition (Step 230 ) and severing the connection between the layer 213 and the applicator tip 214 . (Step 240 ).
  • Applicator tip 214 includes a convex surface 218 adjacent the dispensing slot.
  • the user may tap the film around the periphery using the convex surface 218 of the applicator. (Step 250 ).
  • Using an applicator tip in this fashion may be advantageous for certain users and wound types, as the perceived (or actual) contamination attendant use of one's finger may be eliminated.
  • Each applicator tip 214 includes a generally frustoconical body 215 having a dispensing slot 216 positioned towards the top (as oriented) of the tip 214 .
  • the dispensing slot 216 is dimensioned to dispense a gel composition having a viscosity of 200,000 to 400,000 cps and a wet coat weight of 50 to 120 mils at a generally uniform thickness.
  • the dispensing slot 216 can be disposed at an acute or obtuse angle relative to the plane defined by the bottom-most surfaces of the body 214 .
  • the dispensing slot can be generally parallel to a plane defined by the bottom most surfaces of the body 214 .
  • a ridge 217 projects outwardly from the body 215 , displacing a surface 218 away from the body 215 .
  • the displaced outer surface 218 allows for the applicator tip 214 to be pressed into a gel composition or film without contacting the dispensing slot 215 .
  • the outer surface 218 can include a lens-like, convex structure ( FIG. 4 ) or a rail like, planar structure ( FIG. 5 ).
  • the applicator tip 214 may be supplied with or without a cap 219 used to cover the dispensing slot when the applicator is not in use.
  • FIG. 6 Yet another suitable method 300 for applying a gel composition of the present disclosure to a target site is disclosed in FIG. 6 . While at least the area surrounding the target is again dried, the substantially continuous layer 313 is not drawn over the target. Instead, in Step 330 , a first quantity of gel composition is dispensed at an area proximate the target site 311 and a substantially continuous layer 313 of the gel composition is created by drawing the applicator along the periphery of the target site the target site 311 while dispensing the composition from the tip 314 . After severing the connection between the layer and the applicator (Step 340 ), the resulting layer 313 is drawn across the target site and pressed on the opposite side of the target site from the original location of layer 313 . (Step 350 ). The composition can be drawn by hand (as depicted) or by suitable tool.
  • the gel composition need not be applied in direct contact with the entire target site.
  • the gel composition may be applied over an antiseptic or antimicrobial composition, sutures, gauze, other topical compositions, and combinations thereof.
  • the applied gel compositions of the present disclosure can be removed with relatively little force in a single continuous film without substantial desquamation of the underlying tissue.
  • This desirable property can be enhanced by rolling the edges of the applied film toward the center of the target (or film itself) prior to removal. Rolling can, in certain circumstances, provide a graspable edge for a user or treating professional to engage and remove the film from the skin. For thinner films (e.g., less than 4 mils), it may be sufficient for the film to be removed in multiple pieces.
  • the viscosities of exemplary formulation can be measured using a Brookfield viscometer, model LVT with Brookfield LV spindles (#4). All Examples should be allowed to equilibrate at approximately 22° C. for 24 hours prior to measurement. Preferably the smallest spindle and the lowest speed are chosen such that the viscosity is taken at the lowest speed possible while staying within 10-90% and preferably 20-80% of the viscometer range. In all cases the sample size and container geometry should be chosen to ensure that there were no wall effects. By “wall effects” it is meant the viscosity value is not affected by the container and is essentially equivalent to the viscosity taken in an infinitely large container. For this reason lower viscosity samples require a larger sample size to accommodate the larger spindles. The viscosity of each sample would be taken as the highest relatively stable reading that was achieved.
  • the gel compositions to be tested are applied at a 50 mil wet coat weight to a polycarbonate coupon (LEXAN Clear Polycarbonate available from Sabic Americas, Houston, Tex.).
  • the gel composition samples are applied to a width of 2.54 cm (1.0 in.), a length of 7.62 cm (3 in.), and allowed to dry overnight (about 24 hrs.) at ambient temperature and pressure.
  • Sample materials are laminated to polyester tape (3M 8043, available from 3M Company, St. Paul, Minn.) using a 4 pound roller, and a lead edge of the film tape laminate is then peeled from the LEXAN coupon.
  • the samples are removed at 180 degrees at a rate of 30.5 cm/minute (12 inches per minute). The peel force is then measured with a load cell in units of grams force.
  • the gel compositions to be tested for skin adhesion are applied to the skin of one or more human subjects.
  • the backs of one or more subjects are to be washed using soap (in particular, IVORY SOAP) prior to sample application.
  • the gel composition samples are applied to a width of 2.54 cm (1.0 in.), a length of 7.62 cm (3 in.), and allowed to dry to a film thickness of at least 5 mils.
  • Samples should be placed on the subject's back positioned so that the long axis of each sample was oriented perpendicular to the volunteer's spine.
  • the order of application of sample materials is to be randomized (i.e., rotational placement) on each subject. Sample materials are secured using a 2 kg. (4.5-pound) roller.
  • T-0 An initial set of gel compositions are applied and immediately removed (“T-0”). Another set of samples are applied and allowed to dwell for 24 hours before removal (“T-24”), and another set of samples are applied and allowed to dwell for 48 hours before removal (“T-48”).
  • the gel compositions to be tested are applied to the skin of one or more human subjects.
  • the adhesive samples should have a width of 2.54 cm (1.0 in.) and length of 7.62 cm (3 in.) and a film thickness of at least 5 mils.
  • Samples are to be placed on the subject's back positioned so that the long axis of each sample was oriented perpendicular to the volunteer's spine. 4 hours later, the testing sample is removed at 180 degrees at a rate of 30.5 cm/minute (12 inches per minute) and immediately covered with a fresh liner to prevent the skin facing surface of the film from contamination by hand touch or dirt/dust from environment.
  • the light absorption is measured at a frequency that keratin is known to absorb in (protein) (1539 cm-1, 1630 cm-1) with the absorbance when actual skin is measured being considered 100% and the absorbance of the film alone when not applied to the skin being considered 0%, the absorbance of keratin that adhered to the surface of the adhesive is recorded as a percentage, then an average value is calculated.
  • the samples are then tested again after a 24 hour dwell.
  • the upright MVTR was measured according to ASTM E-96-80.
  • a 3.8 cm diameter sample was placed between adhesive-containing surfaces of two foil adhesive rings, each having a 5.1 cm 2 elliptical opening. The holes of each ring were carefully aligned. Finger pressure was used to form a foil/sample/foil assembly that was flat, wrinkle free, and had no void areas in the exposed sample.
  • a 120-ml glass jar was filled with approximately 50 mL of tap water that contained a couple drops of 0.02% (w/w) aqueous Methylene Blue USP (Basic Blue 9, C.I.52015) solution, unless specifically stated in an example.
  • the jar was fitted with a screw-on cap having a 3.8 inch diameter hole in the center thereof and with a 4.45 cm diameter rubber washer having an approximately 3.6 cm hole in its center The rubber washer was placed on the lip of the jar and foil/sample/foil assembly was placed backing side down on the rubber washer. The lid was then screwed loosely on the jar.
  • the assembly was placed in a chamber at 40° C. and 20% relative humidity for four hours. At the end of four hours, the cap was tightened inside the chamber so that the sample was level with the cap (no bulging) and the rubber washer was in proper seating position.
  • the foil sample assembly was removed from the chamber and weighed immediately to the nearest 0.01 gram for an initial dry weight, W1.
  • the assembly was then returned to the chamber for at least 18 hours, the exposure time T1 in hours, after which it was removed and weighed immediately to the nearest 0.01 g for a final dry weight, W2.
  • the MVTR in grams of water vapor transmitted per square meter of sample area per 24 hours can then be calculated using the following formula.
  • the inverted MVTR was measured using the following test procedure. After obtaining the final “dry” weight, W2, as described for the upright MVTR procedures, the assembly was returned to the chamber for a least 18 additional hours of exposure time, T2, with the jars inverted so that the tap water was in direct contact with the test sample. The sample was then removed from the chamber and weighed to the nearest 0.01 gram for a final wet weight, W3. The inverted wet MVTR in grams of water vapor transmitted per square meter of sample area per 24 hours can then be calculated using the following formula.
  • the Antimicrobial Efficacy Test includes either the Bactericidal Assay, the Bacteriostatic Assay, or both.
  • TAB Tryptic Soy Broth
  • BD Becton, Dickinson and Company
  • D/E Neutralizing Broth available from BD under the tradename DIFCO
  • FBS Fetal Bovine Serum
  • PBS Phosphate Buffer Saline
  • BD Falcon 50 mL Polypropylene Conical Test Tubes available from BD
  • Mini Flip-Top Vial with Butterfields Buffer available from 3M Company of St. Paul, Minn. (USA)
  • PETRIFILM Aerobic Count Plate (AC) 6400/6406/6442 available from 3M Company of St. Paul, Minn. (USA).
  • Antiseptic gel solutions were prepared by diluting the concentrated gel (solids 20%-27%) in 1:1 ratio with the appropriate solvent (isooctane or HMDS) to a final volume of 8 mL.
  • the test solutions were prewarmed to 32° C. in a heating plate while being stirred.
  • 1 mL of serum and 1 mL of appropriate bacterial test culture was pipetted into the 8 mL of test sample.
  • the samples were vortex mixed for 30 seconds, then incubated at 32° C. for 10 min.
  • Duplicates of 1 mL sample aliquots were removed and mixed into 9 mL of D/E neutralizing broth in 50 mL conical tubes that were previously filled. The samples were vortex mixed for 30 seconds at high speed, then placed into an ice bath.
  • the neutralized samples were diluted with a 1:10 serial dilution using the 9 mL Butterfields Buffer test tubes.
  • the dilutions were completed by adding 1 mL of the sample fluid into 9 mL of Butterfields Buffer for the 1:10 dilution.
  • 1 mL from the 1:10 dilution tube was pipetted into 9 mL of Butterfields Buffer to make the 1:100 dilution.
  • pipetted 1 mL from the 1:100 dilution tube into 9 mL of Butterfields Buffer for a 1:1000 dilution.
  • the samples were plated by vortexing the diluted samples and pipetting 1 mL aliquots from these tubes onto the PETRIFILM Aerobic Count Plates. The plating process was completed to negative five ( ⁇ 5) dilutions, which are also notated as 1:1, 1:10, 1:100, 1:1000, 1:10000.
  • the samples were placed in a 37° incubator for 24 hours, then, read with a PETRIFILM PLATE READER (available from 3M Company of St. Paul, Minn.) and the number of colonies recorded and reported as Log(10) Recovery. Log(10) Reduction was also calculated and reported. Log Reduction is calculated by subtracting the log recovered from the control, which in this case is an 8 mL PBS solution inoculated with 1 mL of the same bacterial suspension and 1 mL of FBS.
  • Antiseptic gel solutions were prepared by diluting the concentrated gel (solids 20%-27%) in 1:1 ratio with the appropriate solvent (isooctane or HMDS) to a final volume of 8 mL.
  • the test solutions were prewarmed to 32° C. in a heating plate while being stirred.
  • 1 mL of serum and 1 mL of appropriate bacterial test culture was pipetted into the 8 mL of test sample.
  • 1 mL aliquots were pipetted from this test mixture and placed into duplicate flasks containing 100 mL of TSB without neutralizers and mixed well. These samples were incubated at 37° C. for 48 hours. The samples were then diluted with a 1:10 serial dilution using the Butterfields Buffer test tubes.
  • the dilutions were completed by adding 1 mL of the sample fluid into 9 mL of Butterfields Buffer for the 1:10 dilution. Next, 1 mL from the 1:10 dilution tube was pipetted into 9 mL of Butterfields Buffer to make the 1:100 dilution. Then, pipetted 1 mL from the 1:100 dilution tube into 9 mL of Butterfields Buffer for a 1:1000 dilution. Finally, pipetted 1 mL from the 1:1000 dilution tube into 9 mL of Butterfields Buffer for a 1:10000 dilution.
  • the samples were plated by vortexing the diluted samples and pipetting 1 mL aliquots from these tubes onto the PETRIFILM Aerobic Count Plates. The plating process was completed to negative five ( ⁇ 5) dilutions, which are also notated as 1:1, 1:10, 1:100, 1:1000, 1:10000.
  • the samples were placed in a 37° incubator for 24 hours, then, read with a PETRIFILM PLATE READER (available from 3M Company of St. Paul, Minn.) and the number of colonies recorded and reported as Log(10) Reduction.
  • Log Reduction is calculated by subtracting the log recovered from the input control, which is an 8 mL PBS solution inoculated with 1 mL of the same bacterial suspension and 1 mL of FBS.
  • Source Silicone Poly(diorganosiloxane)-polyoxamide Poly- copolymer made from a diamine of oxamide 25,000 molecular weight (SPOx) as per “Preparatory Example 1” of U.S. Pat. No. 7,947,376.
  • a 12 L 3 neck split top resin flask was charged with 1250 g of aqueous polyethylenimine solution (mw 75,000, 32.6% solids, BASF Lupasol PS) followed by 1279 g of DI water.
  • the flask was equipped with an overhead stirrer and 291.6 g O-methyl isourea hemisulfate was added and the mixture was stirred overnight.
  • An aliquot was taken from the viscous solution and checked by 1H NMR (CD3OD—deuterated methanol) to monitor the disappearance of the O-methyl isourea hemisulfate.
  • the solution was transferred to a polypropylene bottle rinsing with a little water followed by measuring percent solids (21.1% by Ohaus).
  • the dried beads are then jet milled using a 3000 rpm Model 100/20 jet miller.
  • the dried beads are placed in a hopper then feed into an air stream tube.
  • the air stream carries the beads to a splitter where the beads are pushed through two smaller tubes and eventually forced through a cone shaped nozzles (jets).
  • the jets are positioned so the beads colloid into each other, the impact reduces the particle size.
  • the air stream carries the bead particles to a classifier.
  • the classifier depending on its rotational speed will allow small particles to be collected while larger particles are returned to the air stream to be jet milled again. Generally the higher classifier speed results in finer particle size.
  • PDMS was pipetted using a 2 mL pipette into a 125 mL clear glass jar.
  • HMDS was added to the solution jar which was then capped to prevent evaporation.
  • MQ, g-PEI, Sensiva S.C.10, and BZT were subsequently added in that order to the reaction jar.
  • the material was crushed in a weighing dish with a spatula to remove clumps.
  • the mixture solution was placed in an ice bath (4° C.), where the solution was dispersed using a Polytron PT 2500E (available from Kinematica, Inc., Bohemia N.Y.) for 20 minutes at 18.5 ⁇ 1000 RMP. After dispersion, a stir bar was added to the solution jar which was then placed in a hot water bath (66° C.) on a heating and stirring mantle. SPOx was then added immediately and the jar capped. The solution was mixed for 2 hours. After two hours, the jar was sealed with SCOTCH Thread Sealant Tape (available from 3M Company, St. Paul, Minn.) and placed on a roller.
  • SCOTCH Thread Sealant Tape available from 3M Company, St. Paul, Minn.
  • Examples 1-3 were formulated to examine both the Upright and Inverted MVTR of a dried film.
  • the weight percent of components used in the formulations for the gel compositions of Example 1-3 are shown in Table 2A below.
  • the gel composition was applied, using a syringe, to a polyethylene film clamped down to a flat glass panel.
  • the films were dried in a hood for 20 minutes and then die cut to produce circular, 3.8 cm diameter samples.
  • Example 4 is a NEXCARE TEGADERM Waterproof Transparent Dressing, available from 3M Company, St. Paul, Minn.
  • Table 2B MVTR of Examples 1-4 Example 1 2 3 Upright MVTR ( ⁇ 95% 627 ( ⁇ 54) 728 ( ⁇ 72) 783 ( ⁇ 57) confidence) Inverted MVTR (( ⁇ 95% 648 ( ⁇ 115) 956 ( ⁇ 124) 1020 ( ⁇ 163) confidence)
  • Example 4-7 A variety of different coating weights of the formulation of Example 2 were tested to examine the impact of coating weight and film thickness on moisture transmission.
  • the coating weight for each of the sample, as well as the resulting film thickness is Example 4-7 are shown in Table 3 below. Multiple samples of the Examples below were measured for Upright (Dry) and Inverted (Wet) MVTR according to the test methods described above. The average results are reported below, followed by the standard deviation (+/ ⁇ ) of the multiple samples.
  • Examples 8-13 was conducted to evaluate the antimicrobial efficacy of various gel formulations with BZT.
  • the weight percent of components used in the formulations for the gel composition samples of Example 8-13 are shown in Table 4 below.
  • Example 13 is the control Phosphate Buffer Saline (PBS) solution.
  • Examples 14-18 were formulated to examine both the tensile and elongation of dried film generally in accord with ASTM D882-12.
  • the weight percent of components present in the dried films of Example 14-18 are shown in Table 5 below.
  • Gel compositions of the samples were coated on a 1 mil thick NSNF at 50 mils wet (the Gardco Microm II applicator set at 51 mils) and allowed to dry overnight at room temperature and pressure.
  • the dried films were razor cut into 1 ⁇ 2 inches strips and tabs on the strips ends were made using masking tape.
  • the tabs were secured in the grips of a constant rate tensile tester (Zwick/Roell Z005). Gauge length was set at 1′′ and cross-head speed was set at 10′′/min. The grips were drawn apart until the sample ruptured or broke. Each sample was run in triplicate.
  • Examples 19-26 were formulated to examine certain adhesive properties of dried films featuring potential adhesion promoters according to the Polycarbonate Peel Adhesion Test Method.
  • the weight percent of components present in the gel compositions of Example 19-26 are shown in Table 6 below.
  • Gel compositions of the samples were coated on polycarbonate using a Gardco Microm II applicator set at 51 mils, and allowed to dry overnight at ambient temperature and pressure.
  • the sample was peeled from the LEXAN coupon at a platen speed of 305 millimeters/minute (12 inches/minute) over a length of 2.54 centimeters (1 inch) using an IMASS Slip/Peel Tester (Model SP-2000, available from IMASS Incorporated, Accord, Mass.). Each sample was run in duplicate, with the average reported in Table 6 below.
  • Examples 21, 24, 26, 27, and 28 demonstrated improved peel adhesion as compared to Example 19.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Engineering & Computer Science (AREA)
  • Epidemiology (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Animal Behavior & Ethology (AREA)
  • General Health & Medical Sciences (AREA)
  • Public Health (AREA)
  • Veterinary Medicine (AREA)
  • Dispersion Chemistry (AREA)
  • Materials For Medical Uses (AREA)
  • Medicinal Preparation (AREA)
US16/341,637 2016-10-13 2017-10-06 Removable Film Forming Gel Compositions Featuring Adhesion Promoters Abandoned US20190381208A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US16/341,637 US20190381208A1 (en) 2016-10-13 2017-10-06 Removable Film Forming Gel Compositions Featuring Adhesion Promoters

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US201662407922P 2016-10-13 2016-10-13
PCT/US2017/055454 WO2018071278A1 (en) 2016-10-13 2017-10-06 Removable film-forming gel compositions featuring adhesion promoters
US16/341,637 US20190381208A1 (en) 2016-10-13 2017-10-06 Removable Film Forming Gel Compositions Featuring Adhesion Promoters

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2017/055454 A-371-Of-International WO2018071278A1 (en) 2016-10-13 2017-10-06 Removable film-forming gel compositions featuring adhesion promoters

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US17/165,056 Continuation US11497828B2 (en) 2016-10-13 2021-02-02 Removable film forming gel compositions featuring adhesion promoters

Publications (1)

Publication Number Publication Date
US20190381208A1 true US20190381208A1 (en) 2019-12-19

Family

ID=60294394

Family Applications (2)

Application Number Title Priority Date Filing Date
US16/341,637 Abandoned US20190381208A1 (en) 2016-10-13 2017-10-06 Removable Film Forming Gel Compositions Featuring Adhesion Promoters
US17/165,056 Active 2037-10-18 US11497828B2 (en) 2016-10-13 2021-02-02 Removable film forming gel compositions featuring adhesion promoters

Family Applications After (1)

Application Number Title Priority Date Filing Date
US17/165,056 Active 2037-10-18 US11497828B2 (en) 2016-10-13 2021-02-02 Removable film forming gel compositions featuring adhesion promoters

Country Status (3)

Country Link
US (2) US20190381208A1 (zh)
TW (1) TW201829620A (zh)
WO (1) WO2018071278A1 (zh)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11793678B2 (en) 2017-02-14 2023-10-24 3M Innovative Properties Company Bandage composition dispenser
EP3841178A4 (en) * 2018-08-23 2022-06-08 3M Innovative Properties Company TACKED AND FILLED SILICONE ADHESIVE COMPOSITIONS
WO2020243506A1 (en) * 2019-05-31 2020-12-03 Kindeva Drug Delivery Removable film-forming gel compositions featuring adhesion promoters

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20070148475A1 (en) * 2005-12-23 2007-06-28 3M Innovative Properties Company Adhesive compositions
US20070231591A1 (en) * 2004-04-28 2007-10-04 Seiichiro Tsuru Adhesive Material
US20140031734A1 (en) * 2012-01-04 2014-01-30 Momentive Performance Materials Inc. Silicone adhesive compositions
WO2016164316A1 (en) * 2015-04-06 2016-10-13 3M Innovative Properties Company Removable film forming gel compositions and methods for their application

Family Cites Families (63)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2676182A (en) 1950-09-13 1954-04-20 Dow Corning Copolymeric siloxanes and methods of preparing them
US3627851A (en) 1970-10-23 1971-12-14 Dow Corning Flexible coating composition
BE786656A (fr) 1971-07-30 1973-01-24 Ici Ltd Siloxanes
US5214119A (en) 1986-06-20 1993-05-25 Minnesota Mining And Manufacturing Company Block copolymer, method of making the same, dimaine precursors of the same, method of making such diamines and end products comprising the block copolymer
US5512650A (en) 1986-06-20 1996-04-30 Minnesota Mining And Manufacturing Company Block copolymer, method of making the same, diamine precursors of the same, method of making such diamines and end products comprising the block copolymer
DE3717073A1 (de) 1987-05-21 1988-12-08 Wacker Chemie Gmbh Siliconharzpulver und verfahren zu deren herstellung
JPS6422310A (en) 1987-07-17 1989-01-25 Shinetsu Chemical Co Antifoaming agent
US4869964A (en) 1987-12-14 1989-09-26 The B. F. Goodrich Company Oxidation resistant compositions for use with rare earth magnets
US4988755A (en) 1987-12-14 1991-01-29 The B. F. Goodrich Company Passivated rare earth magnet or magnetic material compositions
US4876305A (en) 1987-12-14 1989-10-24 The B. F. Goodrich Company Oxidation resistant compositions for use with rare earth magnets
JPH0623255B2 (ja) 1988-10-05 1994-03-30 信越化学工業株式会社 パーフルオロアルキル基含有オルガノポリシロキサンの製造方法
US4987893A (en) * 1988-10-12 1991-01-29 Rochal Industries, Inc. Conformable bandage and coating material
US5082706A (en) 1988-11-23 1992-01-21 Dow Corning Corporation Pressure sensitive adhesive/release liner laminate
JPH0618880B2 (ja) 1989-02-21 1994-03-16 信越化学工業株式会社 フルオロオルガノポリシロキサン及びその製造方法
JP2669948B2 (ja) 1991-02-18 1997-10-29 信越化学工業株式会社 硬化性フルオロシリコ−ンポリマ−組成物
US5556616A (en) 1991-06-24 1996-09-17 Helene Curtis, Inc. Stable conditioning shampoo having a high foam level containing a graft copolymers of polyethyleneimine and silicone as a conditioner
US5248739A (en) 1991-10-18 1993-09-28 Dow Corning Corporation Silicone pressure sensitive adhesives having enhanced adhesion to low energy substrates
JP2666661B2 (ja) 1992-06-18 1997-10-22 信越化学工業株式会社 オルガノポリシロキサンパウダーの製造方法
US5319040A (en) 1993-03-12 1994-06-07 General Electric Company Method for making substantially silanol-free silicone resin powder, product and use
US5589269A (en) 1993-03-12 1996-12-31 Minnesota Mining And Manufacturing Company Ink receptive sheet
US5558560A (en) 1994-03-07 1996-09-24 Amada Metrecs Company, Limited Tool grinding machine
US5480935A (en) 1994-09-01 1996-01-02 Medlogic Global Corporation Cyanoacrylate adhesive compositions
WO1996034028A1 (en) 1995-04-25 1996-10-31 Minnesota Mining And Manufacturing Company Tackified polydiorganosiloxane oligourea segmented copolymers and a process for making same
MX9708142A (es) 1995-04-25 1997-12-31 Minnesota Mining & Mfg Copolimeros de oligourea polidiorganosiloxano, segmentados, y proceso para su fabricacion.
WO1996035458A2 (en) 1995-04-25 1996-11-14 Minnesota Mining And Manufacturing Company Tackified polydiorganosiloxane polyurea segmented copolymers and a process for making same
US5981621A (en) 1996-02-29 1999-11-09 Closure Medical Corporation Monomeric compositions effective as wound closure devices
AU6909396A (en) 1996-04-25 1997-11-12 Minnesota Mining And Manufacturing Company Silicone compositions containing a silicone-urea segmented copolymer
US6664359B1 (en) 1996-04-25 2003-12-16 3M Innovative Properties Company Tackified polydiorganosiloxane polyurea segmented copolymers and a process for making same
US6846893B1 (en) 1996-10-23 2005-01-25 Minnesota Mining And Manufacturing Company Polymer mixtures containing polydiorganosiloxane urea-containing components
US6007914A (en) 1997-12-01 1999-12-28 3M Innovative Properties Company Fibers of polydiorganosiloxane polyurea copolymers
US6143805A (en) 1998-02-18 2000-11-07 Closure Medical Corporation Electron beam sterilization of liquid adhesive compositions
US6183593B1 (en) 1999-12-23 2001-02-06 Closure Medical Corporation 1,1-disubstituted ethylene adhesive compositions containing polydimethylsiloxane
US6569521B1 (en) 2000-07-06 2003-05-27 3M Innovative Properties Company Stretch releasing pressure sensitive adhesive tape and articles
ATE507883T1 (de) 2002-06-18 2011-05-15 Procter & Gamble Zusammensetzungen aus kationischen polymeren mit hoher ladungsdichte und konditionierungsmittel
GB0216427D0 (en) * 2002-07-16 2002-08-21 Advanced Biotechnologies Inter Wound dressing
WO2004041983A1 (en) 2002-11-04 2004-05-21 The Procter & Gamble Company Liquid laundry detergent
US8198326B2 (en) 2004-09-07 2012-06-12 3M Innovative Properties Company Phenolic antiseptic compositions and methods of use
US20060127345A1 (en) 2004-12-10 2006-06-15 Hilvert Jennifer E Conditioning shampoo containing stabilized silicone particles
US7651990B2 (en) 2005-06-13 2010-01-26 3M Innovative Properties Company Foamable alcohol compositions comprising alcohol and a silicone surfactant, systems and methods of use
US20070041929A1 (en) 2005-06-16 2007-02-22 Torgerson Peter M Hair conditioning composition comprising silicone polymers containing quaternary groups
MX2008002336A (es) 2005-08-17 2009-11-10 Aan Beal Salamone Material de vendaje y recubrimientop basado en un solvente consistente.
NZ568883A (en) 2005-12-07 2010-10-29 Rochal Ind Llp Liquid polymer-containing material which forms a coating on a surface such as skin
US7501184B2 (en) 2005-12-23 2009-03-10 3M Innovative Properties Company Polydiorganosiloxane polyoxamide copolymers
DE102005062268A1 (de) 2005-12-24 2007-08-02 Henkel Kgaa Pulverförmige Stylingmittel und deren Spendersysteme
CA2667307C (en) 2006-10-27 2015-12-01 3M Innovative Properties Company Antimicrobial compositions comprising a c2-c5 lower alcohol, a cationic antimicrobial agent, and a fatty component containing free hydroxyl groups
MX2009006532A (es) 2006-12-21 2009-06-26 Procter & Gamble Composicion para el cuidado personal que comprende aminosilicona y polimeros cationicos derivados de forma natural.
US20080152614A1 (en) 2006-12-22 2008-06-26 3M Innovative Properties Company Method and kit for skin lesion prevention and/or protection
US7705101B2 (en) 2007-06-22 2010-04-27 3M Innovative Properties Company Branched polydiorganosiloxane polyamide copolymers
US20090000727A1 (en) 2007-06-29 2009-01-01 Kanta Kumar Hardcoat layers on release liners
EP2022478A1 (en) 2007-08-07 2009-02-11 KPSS-Kao Professional Salon Services GmbH Conditioning composition for hair
US20110229838A1 (en) 2007-10-01 2011-09-22 Kalgutkar Rajdeep S Orthodontic composition with polymeric fillers
US8431671B2 (en) 2008-03-26 2013-04-30 3M Innovative Properties Company Structured polydiorganosiloxane polyamide containing devices and methods
EP2370505B1 (en) 2008-12-17 2016-09-28 3M Innovative Properties Company Thermoplastic silicone-based polymer process additives for injection molding applications
DE102009017822A1 (de) * 2009-04-20 2010-10-21 Evonik Degussa Gmbh Wässrige Silansysteme basierend auf Tris(alkoxysilylalkyl)aminen und deren Verwendung
EP2422763A1 (en) 2010-08-27 2012-02-29 Colomer Beauty and Professional Products, S.L. Process and kit for treating hair
US8647412B2 (en) 2011-02-28 2014-02-11 Corning Incorporated Sorbent articles for CO2 capture
DE102011079666A1 (de) 2011-07-22 2012-04-26 Henkel Kgaa Kosmetische Zusammensetzung enthaltend Öl aus den Samen der Kapkastanie
US8623454B2 (en) 2011-11-09 2014-01-07 Illinois Tool Works, Inc. Tire dressing paste composition
JP6445430B2 (ja) 2012-07-05 2018-12-26 スリーエム イノベイティブ プロパティズ カンパニー 硬化性抗菌性組成物
US8816019B2 (en) 2013-01-07 2014-08-26 Sabic Global Technologies B.V. Thermoplastic compositions for laser direct structuring and methods for the manufacture and use thereof
WO2014151720A1 (en) 2013-03-15 2014-09-25 Avon Products, Inc Compositions containing titanate silicone networks
US9566780B2 (en) 2013-09-11 2017-02-14 Landa Corporation Ltd. Treatment of release layer
GB201415197D0 (en) 2014-08-28 2014-10-15 Reckitt Benckiser Inc Hair treatment compositions comprising ternary systems of quaternized hydroxyethylcellulose, amine functionalized silicone compounds and cationic guar

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20070231591A1 (en) * 2004-04-28 2007-10-04 Seiichiro Tsuru Adhesive Material
US20070148475A1 (en) * 2005-12-23 2007-06-28 3M Innovative Properties Company Adhesive compositions
US20140031734A1 (en) * 2012-01-04 2014-01-30 Momentive Performance Materials Inc. Silicone adhesive compositions
WO2016164316A1 (en) * 2015-04-06 2016-10-13 3M Innovative Properties Company Removable film forming gel compositions and methods for their application
WO2016164315A1 (en) * 2015-04-06 2016-10-13 3M Innovative Properties Company Removable film forming gel compositions and methods for their application
US10603405B2 (en) * 2015-04-06 2020-03-31 3M Innovative Properties Company Removable film forming gel compositions and methods for their application

Also Published As

Publication number Publication date
US20210154357A1 (en) 2021-05-27
WO2018071278A1 (en) 2018-04-19
TW201829620A (zh) 2018-08-16
US11497828B2 (en) 2022-11-15

Similar Documents

Publication Publication Date Title
US20200188552A1 (en) Removable film forming gel compositions and methods for their application
US11497828B2 (en) Removable film forming gel compositions featuring adhesion promoters
JP4987211B2 (ja) 速硬性皮膜形成調合物
US9096721B2 (en) Film forming, silicone containing compositions
US20090258058A1 (en) Novel silicone film former for delivery of actives
US20070212314A1 (en) Silicone Adhesive Formulation Containing An Antiperspirant
US20070202245A1 (en) Silicone Skin Adhesive Gels With Enhanced Adhesion To Plastic
US20110046242A1 (en) Film Forming, Silicone Containing Compositions
CN105007954B (zh) 硅氧烷膜
US20220241458A1 (en) Removable Film-Forming Gel Compositions Featuring Adhesion Promoters
CN117750951A (zh) 包含水杨酸的成膜组合物和使用方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: 3M INNOVATIVE PROPERTIES COMPANY, MINNESOTA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:WLASCHIN, KATIE F.;GRIESGRABER, GEORGE W.;YOUNG, ALEXI J.;AND OTHERS;SIGNING DATES FROM 20191111 TO 20191115;REEL/FRAME:051020/0841

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION