US20190010348A1 - Pretreat compositions - Google Patents

Pretreat compositions Download PDF

Info

Publication number
US20190010348A1
US20190010348A1 US16/064,492 US201616064492A US2019010348A1 US 20190010348 A1 US20190010348 A1 US 20190010348A1 US 201616064492 A US201616064492 A US 201616064492A US 2019010348 A1 US2019010348 A1 US 2019010348A1
Authority
US
United States
Prior art keywords
ink
fusing
transition metal
particles
conductive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/064,492
Other languages
English (en)
Inventor
Sterling Chaffins
Kevin P. DeKam
Michael G. Monroe
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hewlett Packard Development Co LP
International Wheel and Tire Inc
Original Assignee
Hewlett Packard Development Co LP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hewlett Packard Development Co LP filed Critical Hewlett Packard Development Co LP
Assigned to HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P. reassignment HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CHAFFINS, STERLING, DEKAM, KEVIN P., MONROE, MICHAEL G.
Publication of US20190010348A1 publication Critical patent/US20190010348A1/en
Assigned to INTERNATIONAL WHEEL AND TIRE, INC. reassignment INTERNATIONAL WHEEL AND TIRE, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ARKK ENGINEERING INCORPORATED
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D11/00—Inks
    • C09D11/54—Inks based on two liquids, one liquid being the ink, the other liquid being a reaction solution, a fixer or a treatment solution for the ink
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/10—Processes of additive manufacturing
    • B29C64/106—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material
    • B29C64/112—Processes of additive manufacturing using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material using individual droplets, e.g. from jetting heads
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/10—Processes of additive manufacturing
    • B29C64/165—Processes of additive manufacturing using a combination of solid and fluid materials, e.g. a powder selectively bound by a liquid binder, catalyst, inhibitor or energy absorber
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
    • B29C64/20—Apparatus for additive manufacturing; Details thereof or accessories therefor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y30/00—Apparatus for additive manufacturing; Details thereof or accessories therefor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y40/00—Auxiliary operations or equipment, e.g. for material handling
    • B33Y40/10—Pre-treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y70/00—Materials specially adapted for additive manufacturing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y70/00—Materials specially adapted for additive manufacturing
    • B33Y70/10—Composites of different types of material, e.g. mixtures of ceramics and polymers or mixtures of metals and biomaterials
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D11/00—Inks
    • C09D11/02—Printing inks
    • C09D11/03—Printing inks characterised by features other than the chemical nature of the binder
    • C09D11/037—Printing inks characterised by features other than the chemical nature of the binder characterised by the pigment
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D11/00—Inks
    • C09D11/30—Inkjet printing inks
    • C09D11/32—Inkjet printing inks characterised by colouring agents
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D11/00—Inks
    • C09D11/30—Inkjet printing inks
    • C09D11/32—Inkjet printing inks characterised by colouring agents
    • C09D11/322—Pigment inks
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D11/00—Inks
    • C09D11/30—Inkjet printing inks
    • C09D11/40—Ink-sets specially adapted for multi-colour inkjet printing
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D11/00—Inks
    • C09D11/52—Electrically conductive inks
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2101/00—Use of unspecified macromolecular compounds as moulding material
    • B29K2101/12—Thermoplastic materials
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/25—Solid
    • B29K2105/251—Particles, powder or granules
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01C—RESISTORS
    • H01C17/00—Apparatus or processes specially adapted for manufacturing resistors
    • H01C17/06—Apparatus or processes specially adapted for manufacturing resistors adapted for coating resistive material on a base
    • H01C17/065—Apparatus or processes specially adapted for manufacturing resistors adapted for coating resistive material on a base by thick film techniques, e.g. serigraphy
    • H01C17/06506—Precursor compositions therefor, e.g. pastes, inks, glass frits
    • H01C17/06513—Precursor compositions therefor, e.g. pastes, inks, glass frits characterised by the resistive component
    • H01C17/06526—Precursor compositions therefor, e.g. pastes, inks, glass frits characterised by the resistive component composed of metals
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01C—RESISTORS
    • H01C17/00—Apparatus or processes specially adapted for manufacturing resistors
    • H01C17/06—Apparatus or processes specially adapted for manufacturing resistors adapted for coating resistive material on a base
    • H01C17/065—Apparatus or processes specially adapted for manufacturing resistors adapted for coating resistive material on a base by thick film techniques, e.g. serigraphy
    • H01C17/06506—Precursor compositions therefor, e.g. pastes, inks, glass frits
    • H01C17/06573—Precursor compositions therefor, e.g. pastes, inks, glass frits characterised by the permanent binder
    • H01C17/06586—Precursor compositions therefor, e.g. pastes, inks, glass frits characterised by the permanent binder composed of organic material

Definitions

  • FIG. 1 is a close-up side cross-sectional view of a layer of thermoplastic polymer powder and a pretreat composition in accordance with examples of the present disclosure
  • FIG. 2 is a close-up side cross-sectional view of a layer of thermoplastic polymer powder, a conductive fusing ink, and a second fusing ink in accordance with examples of the present disclosure
  • FIG. 3 is a close-up side cross-sectional view of a layer of thermoplastic polymer powder and transition metal particles in a portion of the layer in accordance with examples of the present disclosure
  • FIG. 4 is a close-up side cross-sectional view of a layer of thermoplastic polymer powder with transition metal particles in a portion of the layer that has been cured to form a matrix of fused thermoplastic polymer particles interlocked with a matrix of sintered transition metal particles in accordance with examples of the present disclosure
  • FIG. 5 is a schematic view of a 3-dimensional printing system in accordance with examples of the present disclosure.
  • the present disclosure is drawn to the area of 3-dimensional printing. More specifically, the present disclosure provides ink sets, material sets, and systems for printing 3-dimensional parts with electrically conductive features.
  • a thin layer of thermoplastic polymer powder is spread on a bed to form a powder bed.
  • a printing head such as an inkjet print head, is then used to print a fusing ink over portions of the powder bed corresponding to a thin layer of the three dimensional object to be formed.
  • the bed is exposed to a light source, e.g., typically the entire bed.
  • the fusing ink absorbs more energy from the light than the unprinted powder.
  • the absorbed light energy is converted to thermal energy, causing the printed portions of the powder to melt and coalesce. This forms a solid layer.
  • a new thin layer of polymer powder is spread over the powder bed and the process is repeated to form additional layers until a complete 3-dimensional part is printed.
  • Such 3-dimensional printing processes can achieve fast throughput with good accuracy.
  • an electrically conductive fusing ink can be printed on a portion of the powder bed to form electrically conductive features in the 3-dimensional printed part.
  • an ink includes a dispersion of silver metal nanoparticles. This type of ink is usually printed on specialty media with a coating that gives the media a smooth surface and also includes chemical components to aid in creating conductive printed elements.
  • such inks can be printed onto a powder bed that has a very rough surface and does not include the chemical components present in such specialty media. Therefore, when conductive inks alone are printed onto the powder bed as a part of the 3-dimensional printing process, the resulting part can sometimes lack electrical conductivity.
  • the present technology provides a pretreat composition that can be applied to the powder bed before the conductive fusing ink.
  • the pretreat composition can include a metal chloride salt such as an alkali metal chloride salt or alkaline earth metal chloride salt.
  • the metal chloride salt in the pretreat composition can be effective to remove dispersing agents from the surfaces of transition metal particles in the conductive fusing ink. This can allow the transition metal particles to sinter together, forming a conductive structure.
  • the pretreat composition can be jetted on portions of the powder bed, followed by the conductive fusing ink to form a conductive portion, and another fusing ink can be jetted on other portions of the powder bed to form insulating portions of the final printed part.
  • the materials, systems, and methods described herein can be used to print parts having a wide variety of electrical configurations, such as embedded electrical elements and surface electrical elements.
  • the present technology can also make it possible to form electrical elements enabled by 3-dimensional printing that are not possible using standard electronics manufacturing techniques, such as embedded coils, diagonal vias, and so on.
  • an ink set can include a pretreat composition including a metal chloride salt, a conductive fusing ink including a transition metal, and a second fusing ink including a fusing agent capable of absorbing electromagnetic radiation to produce heat.
  • the pretreat composition can include a metal chloride salt.
  • the metal chloride salt can be an alkali metal chloride salt or an alkaline earth metal chloride salt.
  • the metal chloride salt can be sodium chloride, potassium chloride, or combinations thereof.
  • Other alkali metal chlorides and alkaline earth metal chlorides can also be used, such as lithium chloride, calcium chloride, magnesium chloride, manganese chloride, or combinations thereof.
  • the metal chloride salt in the pretreat composition can be in the form of an aqueous solution.
  • the pretreat composition can consist essentially of water and the metal chloride salt.
  • the pretreat composition can be a solution of sodium chloride in water, a solution of potassium chloride in water, or a solution of both sodium chloride and potassium chloride in water.
  • Aqueous solutions of other alkali metal chloride salts and alkaline earth metal chloride salts can also be used.
  • aqueous solutions of lithium chloride, calcium chloride, magnesium chloride, manganese chloride, or combinations thereof can be used.
  • the pretreat composition can include other components besides water and the metal chloride salt.
  • the pretreat composition can include an ink vehicle and other ink additives as explained in more detail below.
  • the metal chloride salt can be present in the pretreat composition at a concentration that is effective to aid in forming conductive features using the conductive fusing ink.
  • the concentration of metal chloride salt in the pretreat composition can be from 0.1 wt % to 15 wt %.
  • the concentration can be from 0.5 wt % to 10 wt %.
  • the concentration can be from 1 wt % to 5 wt %.
  • the pretreat composition can consist essentially of water and the metal chloride salt in any of the above listed concentrations.
  • the metal chloride salt can react with dispersing agents at the surfaces of transition metal particles to remove the dispersing agents from the particles. This can increase the sintering between the metal particles and improve the conductivity of the matrix formed of the sintered particles.
  • the pretreat ink can be dispensed onto the powder bed before the conductive fusing ink. When the conductive fusing ink is printed over the pretreat ink, the transition metal particles can come into contact with the chloride salt in the pretreat ink.
  • the polymer powder can be pretreated with a chloride salt before being used in the 3-dimensional printing system. When the conductive fusing ink is printed onto the thermoplastic polymer powder bed, the transition metal particles in the conductive fusing ink can come into contact with the chloride salt already present on the powder.
  • the ink set can also include a conductive fusing ink.
  • the conductive fusing ink can include a transition metal.
  • the conductive fusing ink When the conductive fusing ink is printed onto a layer of the thermoplastic polymer powder, the conductive ink can penetrate into the spaces between powder particles. The layer can then be cured by exposing the layer to electromagnetic radiation. The conductive fusing ink can facilitate fusing of the powder particles by absorbing energy from the electromagnetic radiation and converting the energy to heat. This raises the temperature of the powder above the melting or softening point of the thermoplastic polymer. Additionally, during printing, curing, or both, the transition metal in the conductive ink can form a conductive transition metal matrix that becomes interlocked with the fused thermoplastic polymer particles.
  • the transition metal in the conductive ink can be in the form of elemental transition metal particles.
  • the elemental transition metal particles can include, for example, silver particles, copper particles, gold particles, platinum particles, palladium particles, chromium particles, nickel particles, zinc particles, or combinations thereof.
  • the particles can also include alloys of more than one transition metal, such as Au—Ag, Ag—Cu, Ag—Ni, Au—Cu, Au—Ni, Au—Ag—Cu, or Au—Ag—Pd.
  • non-transition metals can be included in addition to the transition metal.
  • the non-transition metals can include lead, tin, bismuth, indium, gallium, and others.
  • soldering alloys can be included.
  • the soldering alloys can include alloys of lead, tin, bismuth, indium, zinc, gallium, silver, copper, in various combinations.
  • soldering alloys can be printed in locations that are to be used as soldering connections for printed electrical components.
  • the soldering alloys can be formulated to have low melting temperatures useful for soldering, such as less than 230° C.
  • the elemental transition metal particles can be nanoparticles having an average particle size from 10 nm to 200 nm. In more specific examples, the elemental transition metal particles can have an average particle size from 30 nm to 70 nm.
  • the temperature at which the particles are capable of being sintered can also be reduced. Therefore, using elemental transition metal nanoparticles in the conductive fusing ink can allow the particles to sinter and form a conductive matrix of sintered nanoparticles at relatively low temperatures.
  • the elemental transition metal particles in the conductive fusing ink can be capable of being sintered at or below the temperature reached during curing in the 3-dimensional printing process.
  • the particular temperatures used in the process can vary depending on the melt or fusing temperature of the particular polymer powder used.
  • the thermoplastic polymer powder bed can be heated to a preheat temperature during the printing process, and the elemental transition metal particles can be capable of being sintered at or below the preheat temperature.
  • the elemental transition metal particles can be capable of being sintered at a temperature from 20° C. to 350° C.
  • the temperature at which the elemental transition metal particles are capable of being sintered refers to the lowest temperature at which the particles will become sintered together, forming a conductive matrix of sintered particles. It is understood that temperatures above this lowest temperature will also cause the particles to become sintered.
  • the transition metal can be in the form of elemental transition metal particles that are stabilized by a dispersing agent at surfaces of the particles.
  • the dispersing agent can include ligands that passivate the surface of the particles.
  • Suitable ligands can include a moiety that binds to the transition metal. Examples of such moieties can include sulfonic acid, phosphonic acid, carboxylic acid, dithiocarboxylic acid, phosphonate, sulfonate, thiol, carboxylate, dithiocarboxylate, amine, and others.
  • the dispersing agent can contain an alkyl group having from 3-20 carbon atoms, with one of the above moieties at an end of the alkyl chain.
  • the dispersing agent can be an alkylamine, alkylthiol, or combinations thereof.
  • the dispersing agent can be a polymeric dispersing agent, such as polyvinylpyrrolidone (PVP), polyvinylalcohol (PVA), polymethylvinylether, poly(acrylic acid) (PAA), nonionic surfactants, polymeric chelating agents, and others.
  • the dispersing agent can bind to the surfaces of the elemental transition metal particles through chemical and/or physical attachment. Chemical bonding can include a covalent bond, hydrogen bond, coordination complex bond, ionic bond, or combinations thereof. Physical attachment can include attachment through van der Waal's forces, dipole-dipole interactions, or a combination thereof.
  • the conductive fusing ink can be a silver ink that includes silver nanoparticles dispersed by a dispersing agent.
  • examples of commercially available silver inks that can be used in the present ink sets include Mitsubishi® NBSIJ-MU01 available from Mitsubishi Paper Mills Limited, Methode® 9101 available from Methode Electronics, Inc., Methode® 9102 available from Methode Electronics, Inc., NovaCentrixTM JS-B40G available from NovaCentrix, and others.
  • the conductive fusing ink can include a transition metal in the form of a metal salt or metal oxide.
  • a transition metal salt or metal oxide in the conductive ink can form elemental transition metal particles in situ after being printed onto the thermoplastic polymer powder bed. The elemental transition metal particles thus formed can then be sintered together to form a conductive matrix.
  • a reducing agent can be reacted with the metal salt or metal oxide to produce elemental metal particles.
  • a reducing agent can be underprinted onto the powder bed before the conductive fusing ink.
  • a reducing agent can be overprinted over the conductive fusing ink.
  • the reducing agent can be reacted with the metal salt or metal oxide to form elemental metal particles before the thermoplastic polymer particle layer is cured.
  • Suitable reducing agents can include, for example, glucose, fructose, maltose, maltodextrin, trisodium citrate, ascorbic acid, sodium borohydride, ethylene glycol, 1,5-pentanediol, 1,2-propylene glycol, and others.
  • the concentration of transition metal in the conductive fusing ink can vary. However, higher transition metal concentrations can tend to provide better conductivity due to a larger amount of conductive material being deposited on the powder bed.
  • the conductive fusing ink can contain from about 5 wt % to about 50 wt % of the transition metal, with respect to the entire weight of the conductive fusing ink. In further examples, the conductive fusing ink can contain from about 10 wt % to about 30 wt % of the transition metal, with respect to the entire weight of the conductive fusing ink.
  • the conductive fusing ink can be printed from a greater number of slots in an ink jet printer to increase the amount of the transition metal deposited onto the powder bed. Printing multiple passes with the conductive fusing ink can also be used to increase the amount of transition metal deposited onto the powder bed. Additionally, using a higher drop weight in an ink jet printer can increase the amount of transition metal deposited onto the powder bed.
  • Ink sets in accordance with the present technology can also include a second fusing ink.
  • the second fusing ink can be devoid or substantially devoid of the transition metal contained in the conductive fusing ink.
  • the second fusing ink can provide a lower conductivity than the conductive fusing ink when printed on the thermoplastic polymer powder.
  • the second fusing ink can include metal particles that provide a lower conductivity than the transition metal in the conductive fusing ink.
  • the second fusing ink can include metal particles with passivated surfaces that do not sinter together to form a conductive matrix.
  • the second fusing ink can contain another fusing agent that is capable of absorbing electromagnetic radiation to produce heat.
  • the fusing agent can be colored or colorless.
  • the fusing agent can be carbon black, near-infrared absorbing dyes, near-infrared absorbing pigments, tungsten bronzes, molybdenum bronzes, metal nanoparticles, or combinations thereof.
  • near-infrared absorbing dyes include aminium dyes, tetraaryldiamine dyes, cyanine dyes, pthalocyanine dyes, dithiolene dyes, and others.
  • the fusing agent can be a near-infrared absorbing conjugated polymer such as poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS), a polythiophene, poly(p-phenylene sulfide), a polyaniline, a poly(pyrrole), a poly(acetylene), poly(p-phenylene vinylene), polyparaphenylene, or combinations thereof.
  • conjugated refers to alternating double and single bonds between atoms in a molecule.
  • conjugated polymer refers to a polymer that has a backbone with alternating double and single bonds.
  • the fusing agent can have a peak absorption wavelength in the range of 800 nm to 1400 nm.
  • the amount of fusing agent in the second fusing ink can vary depending on the type of fusing agent.
  • the concentration of fusing agent in the second fusing ink can be from 0.1 wt % to 20 wt %.
  • the concentration of fusing agent in the second fusing ink can be from 0.1 wt % to 15 wt %.
  • the concentration can be from 0.1 wt % to 8 wt %.
  • the concentration can be from 0.5 wt % to 2 wt %.
  • the concentration can be from 0.5 wt % to 1.2 wt %.
  • the fusing ink can have a black or gray color due to the use of carbon black as the fusing agent.
  • the fusing ink can be colorless or nearly colorless.
  • the concentration of the fusing agent can be adjusted to provide a fusing ink in which the visible color of the fusing ink is not substantially altered by the fusing agent. Although some of the above described fusing agents have low absorbance in the visible light range, the absorbance is usually greater than zero.
  • the fusing agents can typically absorb some visible light, but their color in the visible spectrum can minimal enough that it does not substantially impact the ink's ability to take on another color when a colorant is added (unlike carbon black which dominates the ink's color with gray or black tones).
  • the fusing agents in concentrated form can have a visible color, but the concentration of the fusing agents in the fusing ink can be adjusted so that the fusing agents are not present in such high amounts that they alter the visible color of the fusing ink.
  • a fusing agent with a very low absorbance of visible light wavelengths can be included in greater concentrations compared to a fusing agent with a relatively higher absorbance of visible light. These concentrations can be adjusted based on a specific application with some experimentation.
  • the concentration of the fusing agent can be high enough that the fusing agent impacts the color of the fusing ink, but low enough that when the ink is printed on the thermoplastic polymer powder, the fusing agent does not impact the color of the powder.
  • the concentration of the fusing agent can be balanced with the amount of fusing ink that is to be printed on the polymer powder so that the total amount of fusing agent that is printed onto the polymer powder is low enough that the visible color of the polymer powder is not impacted.
  • the fusing agent can have a concentration in the fusing ink such that after the fusing ink is printed onto the polymer powder, the amount of fusing agent in the polymer powder is from 0.0003 wt % to 5 wt % with respect to the weight of the polymer powder.
  • the fusing agent can have a temperature boosting capacity sufficient to increase the temperature of the polymer powder above the melting or softening point of the polymer powder.
  • temperature boosting capacity refers to the ability of a fusing agent to convert near-infrared light energy into thermal energy to increase the temperature of the printed polymer powder over and above the temperature of the unprinted portion of the polymer powder.
  • the polymer powder particles can be fused together when the temperature increases to the melting or softening temperature of the polymer.
  • melting point refers to the temperature at which a polymer transitions from a crystalline phase to a pliable, amorphous phase.
  • Some polymers do not have a melting point, but rather have a range of temperatures over which the polymers soften. This range can be segregated into a lower softening range, a middle softening range and an upper softening range. In the lower and middle softening ranges, the particles can coalesce to form a part while the remaining polymer powder remains loose. If the upper softening range is used, the whole powder bed can become a cake.
  • the fusing agent can heat the printed portion to a temperature at or above the melting or softening point, while the unprinted portions of the polymer powder remain below the melting or softening point. This allows the formation of a solid 3D printed part, while the loose powder can be easily separated from the finished printed part.
  • melting point and softening point are often described herein as the temperatures for coalescing the polymer powder, in some cases the polymer particles can coalesce together at temperatures slightly below the melting point or softening point. Therefore, as used herein “melting point” and “softening point” can include temperatures slightly lower, such as up to about 20° C. lower, than the actual melting point or softening point.
  • the fusing agent can have a temperature boosting capacity from about 10° C. to about 70° C. for a polymer with a melting or softening point from about 100° C. to about 350° C. If the powder bed is at a temperature within about 10° C. to about 70° C. of the melting or softening point, then such a fusing agent can boost the temperature of the printed powder up to the melting or softening point, while the unprinted powder remains at a lower temperature. In some examples, the powder bed can be preheated to a temperature from about 10° C. to about 70° C. lower than the melting or softening point of the polymer. The fusing ink can then be printed onto the powder and the powder bed can be irradiated with a near-infrared light to coalesce the printed portion of the powder.
  • the conductive fusing ink and the second fusing ink can be balanced so that thermoplastic polymer powder that is printed with the conductive fusing ink and the second fusing ink reach nearly the same temperature when exposed to light during curing.
  • the type and amount of fusing agent in the second fusing ink can be selected to match the temperature boosting capacity of the transition metal in the conductive fusing ink.
  • the type and amount of transition metal in the conductive fusing ink can also be adjusted to match the temperature boosting capacity of the fusing agent in the second fusing ink.
  • the conductive fusing ink can contain another fusing agent other than the transition metal.
  • the conductive fusing ink and the second fusing ink can raise the temperature of the thermoplastic polymer powder to temperatures within 30° C., within 20° C., or within 10° C. of each other during curing.
  • the ink set can also include colored inks for adding color to the thermoplastic polymer powder. This can allow for printing of full-color 3-dimensional parts.
  • the ink set can include cyan, magenta, yellow, and black inks in addition to the conductive fusing ink, second fusing ink, and pretreat ink if present.
  • Each of the conductive fusing ink, pretreat composition, second fusing ink, and additional colored inks can be formulated for use in an ink jet printer.
  • the transition metal and fusing agents can be stable in an ink jet ink vehicle and the inks can provide good ink jetting performance.
  • the transition metal and fusing agents can be water-soluble, water-dispersible, organic-soluble, or organic-dispersible.
  • the transition metal and fusing agents can also be compatible with the thermoplastic polymer powder so that jetting the inks onto the polymer powder provides adequate coverage and interfiltration of the transition metal and fusing agents into the powder.
  • any of the above described inks can also include a pigment or dye colorant that imparts a visible color to the inks.
  • the colorant can be present in an amount from 0.5 wt % to 10 wt % in the inks. In one example, the colorant can be present in an amount from 1 wt % to 5 wt %. In another example, the colorant can be present in an amount from 5 wt % to 10 wt %. However, the colorant is optional and in some examples the inks can include no additional colorant.
  • the inks can be used to print 3D parts that retain the natural color of the polymer powder. Additionally, the inks can include a white pigment such as titanium dioxide that can also impart a white color to the final printed part. Other inorganic pigments such as alumina or zinc oxide can also be used.
  • the colorant can be a dye.
  • the dye may be nonionic, cationic, anionic, or a mixture of nonionic, cationic, and/or anionic dyes.
  • Specific examples of dyes that may be used include, but are not limited to, Sulforhodamine B, Acid Blue 113, Acid Blue 29, Acid Red 4, Rose Bengal, Acid Yellow 17, Acid Yellow 29, Acid Yellow 42, Acridine Yellow G, Acid Yellow 23, Acid Blue 9, Nitro Blue Tetrazolium Chloride Monohydrate or Nitro BT, Rhodamine 6G, Rhodamine 123, Rhodamine B, Rhodamine B Isocyanate, Safranine O, Azure B, and Azure B Eosinate, which are available from Sigma-Aldrich Chemical Company (St.
  • anionic, water-soluble dyes include, but are not limited to, Direct Yellow 132, Direct Blue 199, Magenta 377 (available from Ilford AG, Switzerland), alone or together with Acid Red 52.
  • water-insoluble dyes include azo, xanthene, methine, polymethine, and anthraquinone dyes.
  • Specific examples of water-insoluble dyes include Orasol® Blue GN, Orasol® Pink, and Orasol® Yellow dyes available from Ciba-Geigy Corp.
  • Black dyes may include, but are not limited to, Direct Black 154, Direct Black 168, Fast Black 2, Direct Black 171, Direct Black 19, Acid Black 1, Acid Black 191, Mobay Black SP, and Acid Black 2.
  • the colorant can be a pigment.
  • the pigment can be self-dispersed with a polymer, oligomer, or small molecule; or can be dispersed with a separate dispersant.
  • Suitable pigments include, but are not limited to, the following pigments available from BASF: Paliogen®) Orange, Heliogen® Blue L 6901F, Heliogen®) Blue NBD 7010, Heliogen® Blue K 7090, Heliogen® Blue L 7101F, Paliogen®) Blue L 6470, Heliogen®) Green K 8683, and Heliogen® Green L 9140.
  • the following pigments are available from Degussa: Printex® U, Printex® V, Printex® 140U, Printex® 140V, Color Black FW 200, Color Black FW 2, Color Black FW 2V, Color Black FW 1, Color Black FW 18, Color Black S 160, Color Black S 170, Special Black 6, Special Black 5, Special Black 4A, and Special Black 4.
  • the following pigment is available from DuPont: Tipure®) R-101.
  • the following pigments are available from Heubach: Dalamar® Yellow YT-858-D and Heucophthal Blue G XBT-583D.
  • the following pigments are available from Clariant: Permanent Yellow GR, Permanent Yellow G, Permanent Yellow DHG, Permanent Yellow NCG-71, Permanent Yellow GG, Hansa Yellow RA, Hansa Brilliant Yellow 5GX-02, Hansa Yellow-X, Novoperm® Yellow HR, Novoperm® Yellow FGL, Hansa Brilliant Yellow 10GX, Permanent Yellow G3R-01, Hostaperm® Yellow H4G, Hostaperm® Yellow H3G, Hostaperm® Orange GR, Hostaperm® Scarlet GO, and Permanent Rubine F6B.
  • the following pigments are available from Mobay: Quindo® Magenta, Indofast® Brilliant Scarlet, Quindo® Red R6700, Quindo® Red R6713, and Indofast® Violet.
  • the following pigments are available from Sun Chemical: L74-1357 Yellow, L75-1331 Yellow, and L75-2577 Yellow.
  • the following pigments are available from Columbian: Raven® 7000, Raven® 5750, Raven® 5250, Raven® 5000, and Raven® 3500.
  • the following pigment is available from Sun Chemical: LHD9303 Black. Any other pigment and/or dye can be used that is useful in modifying the color of the above described inks and/or ultimately, the printed part.
  • the colorant can be included in the conductive fusing ink and/or the second fusing ink to impart color to the printed object when the fusing inks are jetted onto the powder bed.
  • a set of differently colored fusing inks can be used to print multiple colors.
  • a set of fusing inks including any combination of cyan, magenta, yellow (and/or any other colors), colorless, white, and/or black fusing inks can be used to print objects in full color.
  • a colorless fusing ink can be used in conjunction with a set of colored, non-fusing inks to impart color.
  • a colorless fusing ink can be used to coalesce the polymer powder and a separate set of colored or black or white inks not containing a fusing agent can be used to impart color.
  • the inks can be selected to give the inks good ink jetting performance and the ability to color the polymer powder with good optical density.
  • the inks can also include a liquid vehicle.
  • the liquid vehicle formulation can include water and one or more co-solvents present in total at from 1 wt % to 50 wt %, depending on the jetting architecture.
  • one or more non-ionic, cationic, and/or anionic surfactant can optionally be present, ranging from 0.01 wt % to 20 wt %.
  • the surfactant can be present in an amount from 5 wt % to 20 wt %.
  • the liquid vehicle can also include dispersants in an amount from 5 wt % to 20 wt %.
  • the balance of the formulation can be purified water, or other vehicle components such as biocides, viscosity modifiers, materials for pH adjustment, sequestering agents, preservatives, and the like.
  • the liquid vehicle can be predominantly water.
  • a water-dispersible or water-soluble fusing agent can be used with an aqueous vehicle. Because the fusing agent is dispersible or soluble in water, an organic co-solvent is not necessary to solubilize the fusing agent.
  • the inks can be substantially free of organic solvent.
  • a co-solvent can be used to help disperse other dyes or pigments, or improve the jetting properties of the ink.
  • a non-aqueous vehicle can be used with an organic-soluble or organic-dispersible fusing agent.
  • a high boiling point co-solvent can be included in the inks.
  • the high boiling point co-solvent can be an organic co-solvent that boils at a temperature higher than the temperature of the powder bed during printing.
  • the high boiling point co-solvent can have a boiling point above 250° C.
  • the high boiling point co-solvent can be present in the ink at a concentration from about 1 wt % to about 4 wt %.
  • Classes of co-solvents that can be used can include organic co-solvents including aliphatic alcohols, aromatic alcohols, diols, glycol ethers, polyglycol ethers, caprolactams, formamides, acetamides, and long chain alcohols.
  • Examples of such compounds include primary aliphatic alcohols, secondary aliphatic alcohols, 1,2-alcohols, 1,3-alcohols, 1,5-alcohols, ethylene glycol alkyl ethers, propylene glycol alkyl ethers, higher homologs (C 6 -C 12 ) of polyethylene glycol alkyl ethers, N-alkyl caprolactams, unsubstituted caprolactams, both substituted and unsubstituted formamides, both substituted and unsubstituted acetamides, and the like.
  • solvents that can be used include, but are not limited to, 2-pyrrolidinone, N-methylpyrrolidone, 2-hydroxyethyl-2-pyrrolidone, 2-methyl-1,3-propanediol, tetraethylene glycol, 1,6-hexanediol, 1,5-hexanediol and 1,5-pentanediol.
  • One or more surfactants can also be used, such as alkyl polyethylene oxides, alkyl phenyl polyethylene oxides, polyethylene oxide block copolymers, acetylenic polyethylene oxides, polyethylene oxide (di)esters, polyethylene oxide amines, protonated polyethylene oxide amines, protonated polyethylene oxide amides, dimethicone copolyols, substituted amine oxides, and the like.
  • the amount of surfactant added to the formulation of this disclosure may range from 0.01 wt % to 20 wt %.
  • Suitable surfactants can include, but are not limited to, liponic esters such as TergitolTM 15-S-12, TergitolTM 15-S-7 available from Dow Chemical Company, LEG-1 and LEG-7; TritonTM X-100; TritonTM X-405 available from Dow Chemical Company; and sodium dodecylsulfate.
  • liponic esters such as TergitolTM 15-S-12, TergitolTM 15-S-7 available from Dow Chemical Company, LEG-1 and LEG-7; TritonTM X-100; TritonTM X-405 available from Dow Chemical Company; and sodium dodecylsulfate.
  • additives can be employed to optimize the properties of the ink compositions for specific applications.
  • these additives are those added to inhibit the growth of harmful microorganisms.
  • These additives may be biocides, fungicides, and other microbial agents, which are routinely used in ink formulations.
  • suitable microbial agents include, but are not limited to, Nuosept® (Nudex, Inc.), UcarcideTM (Union carbide Corp.), Vancide® (R.T. Vanderbilt Co.), Proxel) (ICI America), and combinations thereof.
  • Sequestering agents such as EDTA (ethylene diamine tetra acetic acid) may be included to eliminate the deleterious effects of heavy metal impurities, and buffer solutions may be used to control the pH of the ink. From 0.01 wt % to 2 wt %, for example, can be used. Viscosity modifiers and buffers may also be present, as well as other additives to modify properties of the ink as desired. Such additives can be present at from 0.01 wt % to 20 wt %.
  • EDTA ethylene diamine tetra acetic acid
  • the liquid vehicle can include the components and amounts as shown in Table 1:
  • liquid vehicle can include the components and amounts as shown in Table 2:
  • liquid vehicle can include the components and amounts as shown in Table 3:
  • liquid vehicle can include the components and amounts as shown in Table 4:
  • liquid vehicle can include the components and amounts as shown in Table 5:
  • liquid vehicle can include the components and amounts shown in Table 6:
  • liquid vehicle formulations of Tables 1 to 6 are provided by example only and other formulations with similar properties can likewise be formulated in accordance with the present technology.
  • a material set such as for 3-dimensional printing, can include a thermoplastic polymer powder, a pretreat composition, a conductive fusing ink, and a second fusing ink.
  • the thermoplastic polymer powder can include powder particles with an average particle size from 20 ⁇ m to 100 ⁇ m.
  • average with respect to properties of particles refers to a number average unless otherwise specified. Accordingly, “average particle size” refers to a number average particle size. Additionally, “particle size” refers to the diameter of spherical particles, or to the longest dimension of non-spherical particles.
  • the polymer particles can have a variety of shapes, such as substantially spherical particles or irregularly-shaped particles.
  • the polymer powder can be capable of being formed into 3D printed parts with a resolution of 20 to 100 microns.
  • “resolution” refers to the size of the smallest feature that can be formed on a 3D printed part.
  • the polymer powder can form layers from about 20 to about 100 microns thick, allowing the fused layers of the printed part to have roughly the same thickness. This can provide a resolution in the z-axis direction of about 20 to about 100 microns.
  • the polymer powder can also have a sufficiently small particle size and sufficiently regular particle shape to provide about 20 to about 100 micron resolution along the x-axis and y-axis.
  • the thermoplastic polymer powder can be colorless.
  • the polymer powder can have a white, translucent, or transparent appearance.
  • a colorless fusing ink such polymer powders can provide a printed part that is white, translucent, or transparent.
  • the polymer powder can be colored for producing colored parts.
  • color when the polymer powder is white, translucent, or transparent, color can be imparted to the part by the fusing ink or another colored ink.
  • the thermoplastic polymer powder can have a melting or softening point from about 70° C. to about 350° C. In further examples, the polymer can have a melting or softening point from about 150° C. to about 200° C.
  • the polymer powder can be selected from the group consisting of nylon 6 powder, nylon 9 powder, nylon 11 powder, nylon 12 powder, nylon 66 powder, nylon 612 powder, polyethylene powder, thermoplastic polyurethane powder, polypropylene powder, polyester powder, polycarbonate powder, polyether ketone powder, polyacrylate powder, polystyrene powder, and mixtures thereof.
  • the polymer powder can be nylon 12, which can have a melting point from about 175° C. to about 200° C.
  • the polymer powder can be thermoplastic polyurethane.
  • the thermoplastic polymer particles can also in some cases be blended with a filler.
  • the filler can include inorganic particles such as alumina, silica, or combinations thereof. When the thermoplastic polymer particles fuse together, the filler particles can become embedded in the polymer, forming a composite material.
  • the filler can include a free-flow agent, anti-caking agent, or the like. Such agents can prevent packing of the powder particles, coat the powder particles and smooth edges to reduce inter-particle friction, and/or absorb moisture.
  • a weight ratio of thermoplastic polymer particles to filler particles can be from 10:1 to 1:2 or from 5:1 to 1:1.
  • the material set can also include the inks as in the ink sets described above.
  • the material set can include a pretreat composition, conductive fusing ink, and another fusing ink as described above. Additional colored inks can also be included in some examples. These inks can have any of the ingredients and properties described above. Additionally, the thermoplastic polymer particles of the material set can have any of the properties described above with respect to thermoplastic polymer powder for printing with the inks.
  • FIG. 1 shows a layer 100 of thermoplastic polymer powder particles 110 .
  • a pretreat composition 120 is dispensed onto a first portion 130 of the layer.
  • a second portion 140 of the layer is not printed with the pretreat composition.
  • FIG. 2 shows the layer 100 of thermoplastic polymer powder particles 110 being printed with a conductive fusing ink 250 in the first portion 130 of the layer, and a second fusing ink 260 in the second portion 140 of the layer.
  • the conductive fusing ink can be printed over the pretreat composition 120 .
  • a metal chloride salt from the pretreat composition can react with dispersing agents on the surfaces of transition metal particles in the conductive fusing ink to remove the dispersing agents.
  • FIG. 3 shows the layer 100 of thermoplastic polymer powder particles 110 after the pretreat composition 120 , conductive fusing ink (shown generally at 250 ), and second fusing ink 260 have been printed onto the layer.
  • the transition metal particles 370 from the conductive fusing ink occupy spaces between the powder particles in the first portion 130 .
  • the second portion 140 includes a fusing agent from the second fusing ink. It should be noted that these figures are not necessarily drawn to scale, and the relative sizes of powder particles and transition metal particles can differ from those shown. For example, in many cases the transition metal particles can be much smaller than the powder particles, such as 2-3 orders of magnitude smaller.
  • FIG. 4 shows the layer 100 after being cured.
  • the transition metal particles in the first portion 130 sinter together to form a matrix of sintered metal particles 480 .
  • the thermoplastic polymer particles 110 fuse together in the second portion 140 , forming a matrix of fused thermoplastic polymer particles 490 .
  • the matrix of sintered metal particles and the fused thermoplastic polymer particles in the first portion are interlocked, forming the conductive composite.
  • FIGS. 1-4 shows only a 2-dimensional cross-section of the conductive composite. Although the sintered metal particles appear to be in isolated locations in the figure, the matrix of sintered metal particles can be a continuously connected matrix in three dimensions. Thus, the conductive composite can have good electrical conductivity through the matrix of sintered transition metal particles.
  • the present technology also encompasses 3-dimensional printing systems that include the material sets.
  • An example of a 3-dimensional printing system 500 is shown in FIG. 5 .
  • the system includes a powder bed 510 including a thermoplastic polymer powder 515 having an average particle size from 20 ⁇ m to 100 ⁇ m.
  • the powder bed has a moveable floor 520 that allows the powder bed to be lowered after each layer of the 3-dimensional part is printed.
  • the 3-dimensional part can include a conductive portion 525 and an insulating portion 527 .
  • the system also includes an inkjet printer 530 that includes a first inkjet pen 535 in communication with a reservoir of a pretreat composition 540 .
  • the first inkjet pen can be configured to print the pretreat composition onto the powder bed.
  • a second inkjet pen 545 is in communication with a reservoir of a conductive fusing ink 550 .
  • the second inkjet pen can be configured to print the conductive fusing ink onto the powder bed.
  • a third inkjet pen 555 is in communication with a reservoir of a second fusing ink 560 .
  • the third inkjet pen can be configured to print the second fusing ink onto the powder bed.
  • a fusing lamp 570 can be used to expose the powder bed to electromagnetic radiation sufficient to fuse the powder that has been printed with the fusing inks.
  • the ink set and/or material set used in the 3-dimensional printing system can include any of the components and ingredients described above.
  • the conductive fusing ink can include elemental transition metal particles that are silver particles, copper particles, gold particles, or combinations thereof.
  • the elemental transition metal particles can have an average particle size from 10 nm to 200 nm.
  • the fusing agent in the second fusing ink can include carbon black, a near-infrared absorbing dye, a near-infrared absorbing pigment, a tungsten bronze, a molybdenum bronze, metal nanoparticles, a conjugated polymer, or combinations thereof.
  • pretreat composition of the 3-dimensional printing system can include a metal chloride salt that includes sodium chloride, potassium chloride, or combinations thereof.
  • the transition metal can be in the form of elemental transition metal particles including a dispersing agent at surfaces of the elemental transition metal particles. The dispersing agent can be capable of being removed from the surfaces by contact with the metal chloride salt.
  • the fusing inks can absorb enough energy to boost the temperature of the thermoplastic polymer powder above the melting or softening point of the polymer, while unprinted portions of the powder bed remain below the melting or softening point.
  • the 3-dimensional printing system can include preheaters for preheating the thermoplastic polymer powder to a temperature near the melting or softening point.
  • the system can include a print bed heater to heat the print bed during printing. The preheat temperature used can depend on the type of thermoplastic polymer used.
  • the print bed heater can heat the print bed to a temperature from 130° C. to 160° C.
  • the system can also include a supply bed, where polymer particles are store before being spread in a layer onto the print bed.
  • the supply bed can have a supply bed heater.
  • the supply bed heater can heat the supply bed to a temperature from 90° C. to 140° C.
  • the pretreat composition can be dried after being dispensed onto the powder bed and before dispensing the conductive fusing ink over the pretreat composition.
  • the pretreat composition is an aqueous solution and the powder bed is preheated to an elevated temperature
  • the water in the pretreat composition can evaporate quickly after printing so that no additional drying time is necessary.
  • Suitable fusing lamps for use in the 3-dimensional printing system can include commercially available infrared lamps and halogen lamps.
  • the fusing lamp can be a stationary lamp or a moving lamp.
  • the lamp can be mounted on a track to move horizontally across the powder bed.
  • Such a fusing lamp can make multiple passes over the bed depending on the amount of exposure needed to coalesce each printed layer.
  • the fusing lamp can be configured to irradiate the entire powder bed with a substantially uniform amount of energy. This can selectively coalesce the printed portions with fusing inks leaving the unprinted portions of the polymer powder below the melting or softening point.
  • the fusing lamp can be matched with the fusing agents in the fusing inks so that the fusing lamp emits wavelengths of light that match the peak absorption wavelengths of the fusing agents.
  • a fusing agent with a narrow peak at a particular near-infrared wavelength can be used with a fusing lamp that emits a narrow range of wavelengths at approximately the peak wavelength of the fusing agent.
  • a fusing agent that absorbs a broad range of near-infrared wavelengths can be used with a fusing lamp that emits a broad range of wavelengths. Matching the fusing agent and the fusing lamp in this way can increase the efficiency of coalescing the polymer particles with the fusing agent printed thereon, while the unprinted polymer particles do not absorb as much light and remain at a lower temperature.
  • an appropriate amount of irradiation can be supplied from the fusing lamp.
  • the fusing lamp can irradiate each layer from about 0.5 to about 10 seconds per pass.
  • the conductive composite can have sufficient electrical conductivity to be used to form electrical components.
  • the resistance of the conductive composite can be tuned in a variety of ways. For example, the resistance can be affected by the type of metal chloride salt in the pretreat composition, the type of transition metal in the conductive fusing ink, the concentration of the transition metal in the conductive fusing ink, the amount of pretreat composition dispensed onto the powder bed, the amount of conductive fusing ink dispensed onto the powder bed, the cross section and length of the conductive portion of the 3-dimensional printed part, and so on.
  • a conductive composite element can have a resistance from 1 ohm to 5 Mega ohms.
  • Sufficient conductivity can be achieved by dispensing a sufficient amount of the transition metal onto the powder bed.
  • a sufficient mass of the transition metal per volume of the conductive composite can be used to achieve conductivity.
  • the mass of transition metal per volume of conductive composite can be greater than 1 mg/cm 3 , greater than 10 mg/cm 3 , greater than 50 mg/cm 3 , or greater than 100 mg/cm 3 .
  • the mass of transition metal per volume of the conductive composite can be greater than 140 mg/cm 3 .
  • the mass of transition metal per volume of conductive composite can be from 1 mg/cm 3 to 1000 mg/cm 3 , from 10 mg/cm 3 to 1000 mg/cm 3 , from 50 mg/cm 3 to 500 mg/cm 3 , or from 100 mg/cm 3 to 500 mg/cm 3 .
  • the amount of pretreat composition dispensed onto the powder bed can affect the conductivity of the printed conductive composite.
  • the mass of metal chloride salt per volume of conductive composite can be greater than 0.2 mg/cm 3 , greater than 3 mg/cm 3 , greater than 10 mg/cm 3 , or greater than 20 mg/cm 3 .
  • the mass of metal chloride salt per volume of the conductive composite can be greater than 28 mg/cm 3 .
  • the mass of metal chloride salt per volume of conductive composite can be from 0.2 mg/cm 3 to 200 mg/cm 3 , from 2 mg/cm 3 to 200 mg/cm 3 , from 10 mg/cm 3 to 100 mg/cm 3 , or from 20 mg/cm 3 to 100 mg/cm 3 .
  • the amount of metal chloride salt or transition metal dispensed onto the powder bed can be adjusted by printing the pretreat composition or conductive fusing ink in multiple passes.
  • a single pass of an inkjet printhead can be sufficient to dispense enough metal chloride salt and/or transition metal to achieve surface conductivity.
  • additional passes can be performed to further increase conductivity.
  • the amount of metal chloride salt and transition metal dispensed can be sufficient to provide bulk conductivity throughout the whole volume of the printed conductive composite, and not along the surface of the layer only.
  • three or more passes can be used to form a conductive composite with bulk conductivity.
  • the amount of metal chloride salt and/or transition metal dispensed can be adjusted by adjusting the drop weight of the inkjet printhead either through resistor design or by changing firing parameters.
  • a greater drop weight a greater amount of the conductive fusing ink can be printed with each drop fired.
  • jetting too large an amount of ink in a single pass can lead to lower print quality because of ink spreading. Therefore, in some examples multiple passes can be used to print more of the conductive fusing ink with better print quality.
  • a 3-dimensional printed part can be formed as follows.
  • An inkjet printer can be used to print a first pass including printing a pretreat composition followed by a conductive fusing ink onto a first portion of the powder bed and printing a second fusing ink onto a second portion of the powder bed.
  • a curing pass can then be performed by passing a fusing lamp over the powder bed to fuse the polymer particles and sinter transition metal particles in the conductive curing ink.
  • one or more additional passes can be performed of printing the pretreat composition and conductive fusing ink onto the first portion of the powder bed to increase the amount of transition metal.
  • Each pass of printing the pretreat composition and conductive fusing ink can be followed by a curing pass with the fusing lamp.
  • the number of passes used can depend on the desired conductivity, the contone level of the printing passes (referring to the density of ink per area deposited on each pass), the type of metal chloride salt, the type of transition metal in the conductive fusing ink, concentration of transition metal in the conductive fusing ink, thickness of the layer of polymer powder being printed, and so on.
  • liquid vehicle or “ink vehicle” refers to a liquid fluid in which additives are placed to form inkjettable fluids, such as inks.
  • liquid vehicles may include a mixture of a variety of different agents, including, surfactants, solvents, co-solvents, anti-kogation agents, buffers, biocides, sequestering agents, viscosity modifiers, surface-active agents, water, etc.
  • the liquid vehicle can carry solid additives such as polymers, latexes, UV curable materials, plasticizers, salts, etc.
  • colorant can include dyes and/or pigments.
  • Dyes refers to compounds or molecules that absorb electromagnetic radiation or certain wavelengths thereof. Dyes can impart a visible color to an ink if the dyes absorb wavelengths in the visible spectrum.
  • pigment generally includes pigment colorants, magnetic particles, aluminas, silicas, and/or other ceramics, organo-metallics or other opaque particles, whether or not such particulates impart color.
  • pigment colorants generally includes pigment colorants, magnetic particles, aluminas, silicas, and/or other ceramics, organo-metallics or other opaque particles, whether or not such particulates impart color.
  • the term “pigment” can be used more generally to describe not only pigment colorants, but other pigments such as organometallics, ferrites, ceramics, etc. In one specific aspect, however, the pigment is a pigment colorant.
  • soluble refers to a solubility percentage of more than 5 wt %.
  • ink jetting or “jetting” refers to compositions that are ejected from jetting architecture, such as ink-jet architecture.
  • Ink-jet architecture can include thermal or piezo architecture. Additionally, such architecture can be configured to print varying drop sizes such as less than 10 picoliters, less than 20 picoliters, less than 30 picoliters, less than 40 picoliters, less than 50 picoliters, etc.
  • the term “substantial” or “substantially” when used in reference to a quantity or amount of a material, or a specific characteristic thereof, refers to an amount that is sufficient to provide an effect that the material or characteristic was intended to provide. The exact degree of deviation allowable may in some cases depend on the specific context.
  • the term “about” is used to provide flexibility to a numerical range endpoint by providing that a given value may be “a little above” or “a little below” the endpoint.
  • the degree of flexibility of this term can be dictated by the particular variable and determined based on the associated description herein.
  • An inkjet printer was used to print conductive traces onto a 1 mm thick nylon coupon that was manufactured from nylon powder (PA12) using a Stratsys® selective laser sintering printer.
  • the inkjet printer printed a pretreat composition and a conductive ink from two separate ink jet pens.
  • the drop weight printed from the ink jet pens was 10 ng.
  • the conductive ink was a silver ink (Mitsubishi NBSIJ-MU01) containing silver nanoparticles.
  • the silver nanoparticles had an average particle size of approximately 20 nm.
  • the pretreat compositions were each a 5 wt % aqueous solution of a chloride compound.
  • the chloride compounds tested included potassium chloride, sodium chloride, lithium chloride, calcium chloride, hydrochloric acid, magnesium chloride, manganese chloride, zinc chloride, nickel chloride, cobalt chloride, and iron chloride.
  • the pretreat composition and conductive ink were printed at a contone level of 255.
  • the resistance of each trace was measured after 1 pass with the inks, after 2 passes with the inks, and after 3 passes with the inks.
  • the amount of solid silver dispensed onto the powder was 47 mg/cm 3 of the powder layer per pass.
  • the mass of chloride dispensed was different for each of the chloride compounds due to their differing molecular weights.
  • the pretreat compositions including potassium chloride and sodium chloride provided the lowest resistance after 3 passes.
  • these pretreat compositions can be especially useful for forming conductive features in 3-dimensional printed parts.
  • Other pretreat compositions can also be useful for applications where a high resistance is desired, such as in 3-dimensional printed resistors.
  • the line widths for all of the metal chloride salts were suitable for 3-dimensional printing using the systems and processes described herein. Line width corresponds generally to print quality. In the application of the present technology, a narrow line width, such as the line widths achieved in this example, allows for printing quality parts with good resolution.
  • the amount of metal chloride salt and conductive ink can be balanced so that not all of the silver particles react and sinter immediately at the surface, but some of the silver particles can penetrate into the powder bed before reacting with the metal chloride salt and sintering together.
  • print quality and penetration of the powder bed layer can be balanced.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Organic Chemistry (AREA)
  • Optics & Photonics (AREA)
  • Mechanical Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Ceramic Engineering (AREA)
  • Civil Engineering (AREA)
  • Composite Materials (AREA)
  • Structural Engineering (AREA)
  • General Chemical & Material Sciences (AREA)
  • Inks, Pencil-Leads, Or Crayons (AREA)
  • Ink Jet (AREA)
US16/064,492 2016-04-15 2016-04-15 Pretreat compositions Abandoned US20190010348A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2016/027966 WO2017180161A1 (en) 2016-04-15 2016-04-15 Pretreat compositions

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2016/027966 A-371-Of-International WO2017180161A1 (en) 2016-04-15 2016-04-15 Pretreat compositions

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US18/327,778 Continuation US20230303884A1 (en) 2016-04-15 2023-06-01 Pretreat compositions

Publications (1)

Publication Number Publication Date
US20190010348A1 true US20190010348A1 (en) 2019-01-10

Family

ID=60042873

Family Applications (2)

Application Number Title Priority Date Filing Date
US16/064,492 Abandoned US20190010348A1 (en) 2016-04-15 2016-04-15 Pretreat compositions
US18/327,778 Pending US20230303884A1 (en) 2016-04-15 2023-06-01 Pretreat compositions

Family Applications After (1)

Application Number Title Priority Date Filing Date
US18/327,778 Pending US20230303884A1 (en) 2016-04-15 2023-06-01 Pretreat compositions

Country Status (4)

Country Link
US (2) US20190010348A1 (zh)
EP (1) EP3443043B1 (zh)
CN (1) CN108603065A (zh)
WO (1) WO2017180161A1 (zh)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11396129B2 (en) * 2017-04-18 2022-07-26 Hewlett-Packard Development Company, L.P. Increasing electrical conductivity at selected locations of a 3D object

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3436236A4 (en) * 2016-07-27 2019-11-27 Hewlett-Packard Development Company, L.P. MANUFACTURE OF THREE-DIMENSIONAL (3D) ELECTRONIC COMPONENTS
EP3533072B1 (en) * 2016-10-25 2022-02-16 Hewlett-Packard Development Company, L.P. 3d-printed part having an integrated temperatur sensor
WO2019152022A1 (en) 2018-01-31 2019-08-08 Hewlett-Packard Development Company, L.P. Additive manufacturing object conductivity
US11772163B2 (en) 2018-02-09 2023-10-03 Hewlett-Packard Development Company, L.P. Three-dimensional printing systems
WO2019212521A1 (en) * 2018-04-30 2019-11-07 Hewlett-Packard Development Company, L.P. Additive manufactured resistivity
US20220001596A1 (en) * 2018-12-14 2022-01-06 Hewlett-Packard Development Company, L.P. Opacifying agent application in three-dimensional printing
CN110142968B (zh) * 2019-06-06 2021-07-06 珠海天威飞马打印耗材有限公司 一种3d打印材料及其制备方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3892635A (en) * 1971-10-28 1975-07-01 Enthone Pre-conditioner and process
US20070238056A1 (en) * 2004-04-27 2007-10-11 Degussa Ag Method and Device for Production of Three-Dimensional Objects by Means of Electromagnetic Radiation of Electromagnetic Radiation and Application of an Absorber by Means of an Ink-Jet Method
WO2014118783A1 (en) * 2013-01-31 2014-08-07 Yissum Research Development Company Of The Hebrew University Of Jerusalem Ltd Three-dimensional conductive patterns and inks for making same
US10926464B2 (en) * 2016-04-15 2021-02-23 Hewlett-Packard Development Company, L.P. Material sets

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI285671B (en) * 1998-10-13 2007-08-21 Orion 21 A D Pty Ltd Luminescent gel coats and moldable resins
CN101451270B (zh) * 2008-12-11 2011-04-13 常振宇 一种大批量制备贵金属纳米线的方法
CN102389949B (zh) * 2011-03-11 2015-09-16 中国科学院福建物质结构研究所 一种海胆状纳米铜颗粒的制备方法
WO2015167530A2 (en) * 2014-04-30 2015-11-05 Hewlett-Packard Development Company, L.P. Three-dimensional (3d) printing method
EP3197669B1 (en) * 2014-09-26 2020-04-01 Hewlett-Packard Development Company, L.P. 3-dimensional printing
JP6472885B2 (ja) 2014-09-30 2019-02-20 ヒューレット−パッカード デベロップメント カンパニー エル．ピー．Ｈｅｗｌｅｔｔ‐Ｐａｃｋａｒｄ Ｄｅｖｅｌｏｐｍｅｎｔ Ｃｏｍｐａｎｙ， Ｌ．Ｐ． 三次元物体の生成

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3892635A (en) * 1971-10-28 1975-07-01 Enthone Pre-conditioner and process
US20070238056A1 (en) * 2004-04-27 2007-10-11 Degussa Ag Method and Device for Production of Three-Dimensional Objects by Means of Electromagnetic Radiation of Electromagnetic Radiation and Application of an Absorber by Means of an Ink-Jet Method
WO2014118783A1 (en) * 2013-01-31 2014-08-07 Yissum Research Development Company Of The Hebrew University Of Jerusalem Ltd Three-dimensional conductive patterns and inks for making same
US10926464B2 (en) * 2016-04-15 2021-02-23 Hewlett-Packard Development Company, L.P. Material sets

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11396129B2 (en) * 2017-04-18 2022-07-26 Hewlett-Packard Development Company, L.P. Increasing electrical conductivity at selected locations of a 3D object
US11840016B2 (en) 2017-04-18 2023-12-12 Hewlett-Packard Development Company, L.P. Increasing electrical conductivity at selected locations of a 3D object

Also Published As

Publication number Publication date
EP3443043B1 (en) 2020-12-09
EP3443043A4 (en) 2019-12-18
US20230303884A1 (en) 2023-09-28
EP3443043A1 (en) 2019-02-20
CN108603065A (zh) 2018-09-28
WO2017180161A1 (en) 2017-10-19

Similar Documents

Publication Publication Date Title
US20230303884A1 (en) Pretreat compositions
US10926464B2 (en) Material sets
CN108699366B (zh) 材料组
US11199456B2 (en) Temperature sensors
US20220388239A1 (en) 3-dimensional printed parts
US11090862B2 (en) Strain sensors
CN108883574B (zh) 材料套装
US11485870B2 (en) Material sets
US11312877B2 (en) Pretreat compositions
US12011874B2 (en) Strain sensors

Legal Events

Date Code Title Description
AS Assignment

Owner name: HEWLETT-PACKARD DEVELOPMENT COMPANY, L.P., TEXAS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:CHAFFINS, STERLING;DEKAM, KEVIN P.;MONROE, MICHAEL G.;REEL/FRAME:046700/0337

Effective date: 20160414

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

AS Assignment

Owner name: INTERNATIONAL WHEEL AND TIRE, INC., MICHIGAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:ARKK ENGINEERING INCORPORATED;REEL/FRAME:050005/0196

Effective date: 20170613

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCV Information on status: appeal procedure

Free format text: APPEAL BRIEF (OR SUPPLEMENTAL BRIEF) ENTERED AND FORWARDED TO EXAMINER

STCV Information on status: appeal procedure

Free format text: EXAMINER'S ANSWER TO APPEAL BRIEF MAILED

STCV Information on status: appeal procedure

Free format text: ON APPEAL -- AWAITING DECISION BY THE BOARD OF APPEALS

STCV Information on status: appeal procedure

Free format text: BOARD OF APPEALS DECISION RENDERED

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION