US20180363177A1 - Patterned nonwoven material - Google Patents

Patterned nonwoven material Download PDF

Info

Publication number
US20180363177A1
US20180363177A1 US16/060,231 US201516060231A US2018363177A1 US 20180363177 A1 US20180363177 A1 US 20180363177A1 US 201516060231 A US201516060231 A US 201516060231A US 2018363177 A1 US2018363177 A1 US 2018363177A1
Authority
US
United States
Prior art keywords
sheet material
imprinted
fibres
pulp
patterned
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/060,231
Other languages
English (en)
Inventor
Mikael Strandqvist
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Essity Hygiene and Health AB
Original Assignee
SCA Hygiene Products AB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SCA Hygiene Products AB filed Critical SCA Hygiene Products AB
Assigned to SCA HYGIENE PRODUCTS AB reassignment SCA HYGIENE PRODUCTS AB ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: STRANDQVIST, MIKAEL
Publication of US20180363177A1 publication Critical patent/US20180363177A1/en
Assigned to ESSITY HYGIENE AND HEALTH AKTIEBOLAG reassignment ESSITY HYGIENE AND HEALTH AKTIEBOLAG CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: SCA HYGIENE PRODUCTS AKTIEBOLAG
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
    • D04H1/425—Cellulose series
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/44—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties the fleeces or layers being consolidated by mechanical means, e.g. by rolling
    • D04H1/46—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties the fleeces or layers being consolidated by mechanical means, e.g. by rolling by needling or like operations to cause entanglement of fibres

Definitions

  • the present disclosure relates to a nonwoven sheet material provided with a visual non-random pattern and to a process for producing such a patterned nonwoven sheet material.
  • Absorbent nonwoven materials are used for wiping various types of spills and dirt in industrial, medical, office and household applications. They typically include a combination of thermoplastic polymers (synthetic fibres) and cellulosic pulp for absorbing water and other hydrophilic substances, as well as hydrophobic substances (oils, fats).
  • the nonwoven wipes of this type in addition to having sufficient absorptive power, are at the same time strong, flexible and soft. They can be produced by various methods, including air-laying, wet-laying and foam-laying of a pulp-containing mixture on a polymer web, followed by dewatering and hydroentangling to anchor the pulp onto the polymer and final drying.
  • Absorbent nonwoven materials of this type and their production processes are disclosed i.a. in WO 2005/042819, WO 2007/108725, WO 2008/066417, and WO 2009/031951.
  • Patterns can be applied by printing; however, printing often results in bleeding of the ink into the nonwoven outside the pattern, e.g. when a wipe or the like is used together with solvents during use of the wipe (wiping), which is clearly undesired.
  • WO 95/09261 discloses nonwoven materials having geometrically repeating patterns that are formed by bonded and unbonded regions on the material.
  • the bonded regions occupy 3-50%, in particular 5-35% of the surface area of the material.
  • the nonwoven materials are three-layered laminates having outer spun-bond thermoplastic layers and an inner melt-blown fibre layer. The laminates are patterned by calendering using heated embossing rolls.
  • a drawback of these materials is that the pattern is connected to bonding of the thermoplast and that, as a consequence, the patterns can only be small and at the same time must occupy a relatively large area of the nonwoven surface. This is particularly disadvantageous for absorbent nonwoven materials, containing cellulose pulp or the like, where bonding reduces the absorptive power and thermo-bonding is therefore avoided.
  • a patterned nonwoven sheet material wherein the patterning does not entail the disadvantages of prior art techniques, such as bleeding of printed patterns, insufficient distinctness of patterns produced by hydroentangling, or stiffness and reduced strength or absorptive capacity of embossing techniques.
  • a hydroentangled, absorbent nonwoven material having a non-random, sharp and distinct visible decorative or identifying pattern on its surface.
  • the visible pattern does not substantially reduce the absorptive power of the material and also ensures maintenance of other product properties, including softness, abrasion resistance, strength etc.
  • the two sides of the material may have different compositions: the lower side may have a relatively high pulp content, whereas the upper side, on which the pattern is provided, may have a relatively low pulp content, or vice versa.
  • FIG. 1 shows a production line for producing sheet material of the present disclosure.
  • FIG. 2 shows a patterned nonwoven according to the present disclosure.
  • sides of the sheet material this means the effective surfaces of the sheet, i.e. the front side and back side (also, interchangeably, referred to as upper and lower surface) of the sheet material.
  • front side and back side also, interchangeably, referred to as upper and lower surface
  • weight ratios or percentages are mentioned herein, these are on dry matter basis (without any water or more volatile substances), unless otherwise specified. Where water weights or percentages are mentioned herein, these are on wet matter basis.
  • the patterned hydroentangled nonwoven sheet material contains cellulosic fibres.
  • the nonwoven sheet material contains at least 25 wt. %, at least 40 wt. %, or at least 50 wt. %.
  • the nonwoven sheet material contains up to 80 wt. %, or between 60 and 75 wt. % of cellulosic fibres.
  • Cellulosic fibres are further defined below and include cellulosic pulp.
  • the sheet material may contain thermoplastic fibres.
  • the sheet material contains at least 10 wt. %, at least 15 wt. %, at least 20 wt. %, or at least 25 wt. %.
  • the sheet material contains up to e.g. 70 wt. %, up to 60 wt. %, up to 50 wt. %, or up to 40 wt. %.
  • the thermoplastic fibres also referred to as (manmade or synthetic) polymer fibres, can include (continuous) filaments and (short) staples or both.
  • the sheet material (combined web) may contain between 6 and 60 wt.
  • the sheet material may contain between 3 and 50 wt. %, between 4 and 30 wt. %, or between 5 and 20 wt. % of the synthetic staple fibres on dry solids basis of the combined web.
  • the sheet material contains both thermoplastic filaments and staple fibres, e.g. in a weight ratio between 9:1 and 1:1, or between 5:1 and 1.5:1. Thermoplastic fibres are further defined and illustrated below.
  • patterned sheet material between 1 and 20% of at least one surface has been imprinted and forms a pattern that is discernible by visual and/or tactile means, e.g. by differences in reflection, brightness, smoothness, etc. between imprinted and non-imprinted part, which can be perceived visually or by touch and feel. These differences are, in particular, differences in height.
  • imprinting is understood to mean exercising mechanical force resulting in some compression of the sheet material, as further defined and illustrated below.
  • the patterns are not exclusively discernible by difference in colour, e.g. resulting from printing, dyeing or inking, or in other differences in material composition.
  • the patterns essentially only result from imprinting.
  • the imprinted part of the sheet material has a thickness which is between 75 and 95% of the thickness of the non-imprinted part.
  • the imprinting action results in a 5-25% reduced thickness.
  • the patterns can be present at either side of the sheet material or on both sides.
  • the patterning i.e. the height differences
  • the front side can have the same or a different material composition as the back side.
  • the sheet material may have a largely homogeneous composition over its thickness.
  • the sheet material may have a gradually changing composition over its thickness, with the two surfaces (front and back) having essentially the same composition (in which case internal areas have a different composition) or a different composition.
  • the sheet material is a layered sheet, with two, three of more layers of different composition, wherein, however, in particular as a result of the hydroentanglement, there are no sharp transitions between adjacent layers.
  • the sheet can be a bilayer sheet, having a relatively high-pulp layer at one side, and a relatively low-pulp layer at the other side.
  • the sheet can also be a three-layer sheet, with adjacent high-pulp, low-pulp and high-pulp layers. Further variants are equally feasible.
  • the sheet material has a high-pulp (front side) surface and an opposite low-pulp (back side) surface, with optionally further layers in between, or without such intermediate layers to form a bilayer sheet.
  • a high-pulp surface may contain at least 60 wt. % of pulp fibres and a low-pulp surface may contain less than 50 wt. % of pulp fibres. Such percentages apply in the outermost regions, e.g. the outermost 5% of the thickness of the sheet.
  • a high-pulp surface may contain less than 30, or less than 15 wt. % of thermoplastic fibres and a low-pulp surface may contain at least 30 wt. %, or more than 50 wt. % of thermoplastic fibres.
  • the thickness of the present sheet materials may vary widely, depending on the intended use.
  • the sheet may have thicknesses (of non-imprinted parts) between 100 and 2000 ⁇ m, 250-1500 ⁇ M, 400-1000 ⁇ m, or 500-800 ⁇ m.
  • the thickness can be measured by the method as further described in the accompanying examples.
  • the height difference between imprinted (pattern) and non-imprinted parts is typically 50-250 ⁇ m, or 75-150 ⁇ m.
  • the height difference can be measured by methods known in the art, e.g. by laser reflection measurement or by white light interference measurement.
  • the patterns can have any form or design. They can be purely decorative or they can have an information or identification function, or both, and are clearly visible to the user or observer. They can include figures, like lines, circles etc. as well as pictures, readable characters (letters, numbers), etc. As a suitable example, a part of the imprinted layer area may form readable characters and/or logotypes. As an even more specific example, between 2 and 15% of the imprinted surface forms readable characters and/or logotypes, and between 0.5 and 3% of the imprinted surface forms other patterns than readable characters or logotypes, in particular geometrical patterns such as straight or curved lines, the percentages being based on the total surface area of the imprinted surface.
  • At least 10% of the total surface area of the imprinted side (or sides) of the sheet material consists of uninterrupted non-imprinted regions of at least 20 cm 2 , or at least 25 cm 2 .
  • at least 20%, or at least 30% of the total surface area of the imprinted side consists of such uninterrupted non-imprinted regions.
  • Such uninterrupted non-imprinted regions may have any form, such as rectangles, polyhedrons, circles, but also more irregular forms.
  • the patterned nonwoven sheet may be of any desired degree of softness, strength, and of any size, and it may be non-coloured (white) or coloured, wherein the colour may be applied before or after the imprinting step.
  • the pattern is stable and resistant to temperature, humidity, UV/vis irradiation and the like, and does not bleed.
  • the present sheet material has excellent absorption performances for both hydrophilic and hydrophobic substances, which are not reduced by the patterns.
  • the water absorption capacity of the final sheet material is at least 5 g of water per g of dry sheet material, or at least 6 g/g (distilled water at 23° C. as reference).
  • a process for producing a patterned nonwoven sheet material as described above includes:
  • the energy to be used for imprinting is especially based on vibrational energy rather than by direct impact or heat.
  • the imprinting action does not comprise embossing or thermo-bonding of thermoplastic fibres to a significant degree. Embossing (with moderately heated rolls) was found to result in less sharp patterns, and thermo-bonding (which implies melting of the thermoplast) reduces the absorptive power of the resulting sheet material.
  • a very useful type of vibrational (oscillating) energy is ultrasound energy.
  • Ultrasound equipment suitable for use in the present process is commonly known in the art.
  • ultrasonic equipment can be purchased e.g. from Herrmann Ultraschall, Karlsbad, DE, or form Branson Ultrasonics, Danbury Conn., USA or Dietzenbach, DE.
  • the imprinting action is a rotatory action using a patterned anvil roll which conveys the sheet material to be imprinted, as shown in accompanying FIG. 1 .
  • the oscillating frequency can be in the upper acoustic range or, in particular embodiments, in the lower ultrasound range, e.g. between 15 and 100 kHz, especially between 18 and 30 kHz.
  • the oscillating power can be in the range of 200-4000 N, or 500-2500 N.
  • the oscillating amplitude will typically be in the range of 10-100 ⁇ m.
  • the distance between the energy transmitter (which is sometimes referred to as sonotrode in an ultrasound equipment) and the anvil can be short and may vary in operation.
  • the clearance between the energy transmitter and protruding parts of the anvil roll has a maximum which is approximately equivalent to or larger than the thickness of the material to be treated and a minimum (imprinting stage) which is somewhat less than the thickness of the material treated.
  • the clearance can be at least 500 ⁇ m, between 600 and 2000 ⁇ m, or between 800 and 1500 ⁇ m.
  • the clearance can be adjustable, so as to allow replacement and processing of sheets of different thicknesses.
  • natural fibres can be used, especially those that have a capacity to absorb water and a tendency to help in creating a coherent sheet.
  • suitable natural fibres there are primarily cellulosic fibres such as seed hair fibres, e g cotton, flax, and pulp.
  • Wood pulp fibres are especially well suited, and both softwood fibres and hardwood fibres are suitable, and also recycled fibres can be used.
  • the pulp fibre lengths can vary from around 3 mm for softwood fibres to around 1.2 mm for hardwood fibres and a mix of these lengths, and even shorter, for recycled fibres.
  • Filaments are fibres that in proportion to their diameter are very long, in principle endless during their production. They can be produced by melting and extruding a thermoplastic polymer through fine nozzles, followed by cooling, for example using an air flow, and solidification into strands that can be treated by drawing, stretching or crimping. Spun-bond filaments are produced in a similar way by stretching the filaments using air to provide an appropriate fibre diameter that is usually above 10 ⁇ m, usually 10-100 ⁇ m. Production of spun-bond filaments is described e.g. in U.S. Pat. Nos. 4,813,864 and 5,545,371. Chemicals for additional functions can be added to the surface of the filaments.
  • Spun-bond and melt-blown filaments as a group are called spun-laid filaments, meaning that they are deposited directly, in situ, on a moving surface to form a web, that is bonded downstream. Controlling the ‘melt flow index’ by the choice of polymers and temperature profile is an essential part of controlling the extrusion and thereby the filament formation.
  • the spun-bond filaments normally are stronger and more even.
  • the filaments are laid lengthwise.
  • thermoplastic polymer that has sufficient coherent properties to allow being cut in the molten state, can in principle be used for producing spun-bond fibres.
  • useful synthetic polymers are polyolefins, such as polyethylene and polypropylene, polyamides such as nylon-6, polyesters such as poly(ethylene terephthalate) and polylactides. Copolymers and mixtures of these polymers may of course also be used, as well as natural polymers with thermoplastic properties.
  • Staple fibres can be produced from the same substances and by the same processes as the filaments described above.
  • Other usable staple fibres are those made from regenerated cellulose such as viscose and lyocell. They can be treated with spin finish and crimped, but this is not necessary for the type of processes used to produce the present nonwoven sheet material.
  • the cutting of the fibre bundle normally is done to result in a single cut length, which can be altered by varying the distances between the knives of the cutting wheel.
  • different fibre lengths are used, between 2 and 50 mm.
  • Wet-laid hydroentangled nonwovens normally use 12-18 mm, or down to 9 mm or less, especially hydroentangled materials produced by wet-laying technology.
  • the strength of the material and its other properties like surface abrasion resistance are increased as a function of the fibre length (for the same thickness and polymer of the fibre). When continuous filaments are used together with staple fibres and pulp, the strength of the material will mostly come from the filaments.
  • Shorter staple fibres can result in an improved material as they have more fibre ends per gram fibre and are easier to move in the Z-direction (perpendicular to the web plane). More fibre ends will project from the surface of the web, thus enhancing the textile feeling. The secure bonding will result in very good resistance to abrasion.
  • the staple fibres can be a mixture of fibres based on different polymers, with different lengths and dtex, and with different colours.
  • the pulp-containing sheet material can be formed from materials that can be applied by various techniques known in the art, including wet-laying, air-laying, dry laying or spun-laying or it can completely or partly be formed from a pre-fabricated sheet, e.g. a tissue sheet.
  • a pre-fabricated sheet e.g. a tissue sheet.
  • the process for producing the patterned nonwoven sheet material of the present disclosure can be as depicted in FIG. 1 .
  • Such a process includes: providing an endless forming fabric 1 , on which the continuous filaments 2 can be laid down as, for example, spun-bond filaments, and excess air can be sucked off through the forming fabric, to form a precursor of a web 3 ; advancing the forming fabric 1 with the continuous filaments to a wet-laying stage and a so-called head box 4 , where an aqueous slurry or an aqueous foam including a mixture 5 of natural fibres and staple fibres is wet-laid on and partly into the precursor web 3 of continuous filaments 2 , and excess water is drained off through the forming fabric 1 , forming a fibrous web 6 ; advancing the fibrous web 6 from the fabric 1 to a second fabric 7 to subject the fibre mixture to a hydroentangling stage 8 , where the filaments 2 and fibres are intermingled intimately and bonded into a nonwoven web 9 by the action of water jets 10 .
  • the web is then advanced to a drying stage 11 where the
  • the continuous filaments 2 which can be made from extruded thermoplastic pellets, can be laid down directly onto a forming fabric 1 where they are allowed to form an unbonded web structure 3 , in which the filaments can move relatively freely from each other. This can be achieved by making the distance between the nozzles and the forming fabric 1 relatively large, so that the filaments are allowed to cool and thus to have reduced stickiness before they land on the forming fabric.
  • cooling of the filaments before they are laid on the forming fabric can be achieved e.g. by air. The air used for cooling, drawing and stretching the filaments is sucked through the forming fabric, to let the filaments follow the air flow into the meshes of the forming fabric to be stayed there. A good vacuum might be needed to suck off the air.
  • the filaments can be cooled by spraying water.
  • the speed of the filaments as they are laid down on the forming fabric may be higher than the speed of the forming fabric, so the filaments can form irregular loops and bends as they are collected on the forming fabric to form a randomized precursor web.
  • the basis weight of the formed filament precursor web 3 can advantageously be between 2 and 50 g/m 2 .
  • the mixture 5 of natural fibres and staple fibres can be wet-laid onto and partly into the precursor web 3 of spun-laid filaments to form a fibrous web 6 .
  • a fibrous web 6 can also be formed from materials applied by various other techniques known in the art.
  • a patterned hydroentangled nonwoven sheet material may also include a material that has been formed of only pulp and thermoplastic fibres that are not filaments, such as staple fibres.
  • a sheet material may be formed by the laying the mixture 5 of pulp and staple fibres directly on the forming web 1 , removing the water, which is followed by hydroentangling, drying and imprinting of the formed web. Further alternatives are also described hereinbelow.
  • the mixture 5 of pulp and staple fibres can be slurried in a conventional way, either mixed together or first separately slurried and then mixed, and conventional papermaking additives such as wet and/or dry strength agents, retention aids, dispersing agents, may be added, to produce a well-mixed slurry of pulp and staple fibres in water.
  • This mixture 5 can, as illustrated in FIG. 1 be pumped out through a wet-laying head box 4 onto moving forming fabric 1 where it is laid down on the unbonded precursor filament web 3 with its freely moving filaments.
  • a particularly advantageous way of depositing the short fibres is by foam formation, which is a variant of wet-laying, in which the cellulosic pulp and staple fibres are mixed with water and air, in the presence of a surfactant, for example between 0.01 and 0.1 wt. % of a non-ionic surfactant so as to form the pulp-containing mixture 5 .
  • the foam may contain between 10 and 90 vol. %, between 15 and 50 vol. %, or between 20 and 40 vol. % of air (or other inert gas). It is transported to the head box 4 where it is laid on top of the filament web 3 and surplus water and air are sucked off.
  • the fibres can be applied by dry-laying (in which fibres are carded and then directly applied on the carrier) or air-laying (in which fibres, which may be short, are fed into an air stream and applied to form a random oriented web).
  • the fibrous web 6 of synthetic fibres such as continuous filaments, and staple fibres and pulp is hydroentangled, while it is supported by the fabric 7 and is intensely mixed and bonded into a composite nonwoven material 9 .
  • An instructive description of the hydroentangling process is given in CA patent no. 841,938.
  • the different fibre types will be entangled by the action of a plurality of thin jets 10 of high-pressure water impinging on the fibres.
  • the fine mobile spun-laid filaments are twisted around and entangled with themselves and with the other fibres, which gives a material with a very high strength in which all fibre types are intimately mixed and integrated.
  • Entangling water is drained off through the forming fabric 7 , and can be recycled, if desired after purification (not shown).
  • the energy supply needed for the hydroentangling is relatively low, i.e. the material is easy to entangle.
  • the energy supply at the hydroentangling can appropriately be in the interval 50-500 kWh/ton.
  • the strength of a hydroentangled material will depend on the amount of entangling points for and thus on the lengths of the fibres, in particular when the material that is hydroentangled is only based on staple and pulp fibres.
  • the strength will be determined mostly on the filaments, and be reached fairly quickly in the entangling. Thus, most of the entangling energy will be spent on mixing filaments and fibres to reach a good integration.
  • the process can include hydroentangling a fibrous web 6 containing a precursor filament web 3 on which a mixture of staple and pulp fibres has been wet-laid or the like.
  • the precursor filament web 3 may be subjected to a prebonding stage, or even be supplied as a prebonded web that can be treated as a normal web by rolling and unrolling operations, even if it still does not have the final strength to its use as a wiping material (not shown).
  • the pulp fibres in mixture 5 can be fairly easily mixed and entangled into and also stuck in such a web of filaments, and/or longer staple fibres.
  • the polymer staple fibres that may be present in mixture 5 can be harder to entangle and to force down into a prebonded filament web, and it is often required to use longer staple fibres such as 12-18 mm to get enough entangling bonding points to catch the polymer fibres securely in the filament web.
  • the precursor filament web 3 may be substantially unbonded prior to the laying of the pulp-containing mixture 5 , i.e. no extensive bonding (e.g. thermal bonding) of the precursor filament web 3 should occur before the pulp-containing mixture 5 (with or without staple fibres) is deposited through head box 4 .
  • the filaments should be largely free to move with respect to each other to the staple and pulp fibres to mix and twirl into the filament web during entangling.
  • Thermal bonding points between filaments in the filament web at this point of the process would act as blockings to stop the staple and pulp fibres to enmesh near these bonding points, as they would keep the filaments immobile in the vicinity of the thermal bonding points.
  • the ‘sieve effect’ of the web would be enhanced and a more two-sided material would be the result.
  • no thermal bondings it is meant that the filaments have not been exposed to excessive heat and pressure, e.g. between heated rollers, which would compress some of the filaments to such extent that they will be softened and/or molten together to deformation in points of contact.
  • Some bond points could result from residual tackiness at the moment of laying-down, especially for melt-blown fibres, but these will be without deformation in the points of contact, and thus without significant negative effect on the properties of the materials.
  • the process as described herein and illustrated in FIG. 1 may result in high flexibility of an unbonded filament web to ease the entraining of polymer staple fibres and thus allows using shorter fibres.
  • the fibres can be in the range of 2 to 8 mm, or 3 to 7 mm, but longer staple fibres can also be used.
  • the entangling stage 8 can include several transverse bars with rows of nozzles from which very fine water jets 10 under very high pressure are directed against the fibrous web to provide an entangling of the fibres.
  • the water jet pressure can then be adapted to have a certain pressure profile with different pressures in the different rows of nozzles.
  • the fibrous web can be transferred to a second entangling fabric before hydroentangling.
  • the web can also, prior to the transfer, be hydroentangled by a first hydroentangling station with one or more bars with rows of nozzles. drying etc.
  • the hydroentangled wet web 9 is then dried, which can be done using a conventional web drying equipment, for example of the types used for tissue drying, such as through-air drying or Yankee drying.
  • the structure of the material can be changed by further processing such as microcreeping, etc.
  • To the material can also be added different additives such as wet strength agents, binder chemicals, latexes, debonders, etc. nonwoven material.
  • a composite patterned nonwoven can be produced with a total basis weight of 20-120 g/m 2 , or 50-80 g/m 2 .
  • FIG. 1 A process and an apparatus for imprinting the nonwoven are represented in FIG. 1 .
  • Wet-laid or foam-laid, hydroentangled semi-finalised sheet material 9 is dried in drier 11 and then conveyed over anvil 20 along guiding rolls 22 to produce imprinted sheet material 23 .
  • the ultrasound anvil roll 20 is activated by driving gear 24 , which in this figure rotates clockwise. Energy is applied by horn 21 provided with sonotrode 25 and oscillation boosters 26 .
  • the anvil roll 20 has suitable dimensions for allowing a continuous sheet to be moved at a significant speed of e.g. 2-10 m/sec, or 3-6 m/sec (180-360 m/min).
  • the anvil roll may have a diameter of e.g. 50-200 cm and a breadth (height of the cylinder) of between 1 and 3 m.
  • the rotating speed is controllable and, for an anvil roll of 1 m diameter, the rotating speed (in radians per s) will be the same as the speed of the passing sheet, i.e. the tangential speed of the rotating roll, corresponding to e.g. 25-60 revolutions per minute (rpm). It is important to ensure that the rotating speed is closely adjusted to the transporting speed of the sheet material, so that the sheet material does not move with respect to the anvil 20 , while it is in contact with the anvil 20 , whereby damage to the sheet material is avoided.
  • Ambient conditions can suitably be applied during the ultrasound treatment.
  • the temperature of the sheet at the imprinting site can be less than 100° C., less than 60° C., or between 30 and 50° C. Further operating conditions for the ultrasound apparatus can be as described above.
  • the structure of the material can be changed by further processing such as microcreeping, etc.
  • To the material can also be added different additives such as wet strength agents, binder chemicals, latexes, debonders, etc. to the nonwoven material.
  • the material After the imprinting step, the material can be wound into mother rolls. The material can then be converted in known ways to suitable formats and packed.
  • a composite patterned nonwoven can be produced with a total basis weight of 20-120 g/m 2 , or 40-80 g/m 2 .
  • FIG. 2 shows an example of a patterned sheet 27 of the present disclosure.
  • the squares 28 as depicted half of which with an internal imprinted FIG. 29 , the other half empty) have unit sizes of about 70 ⁇ 70 mm. It has a relative non-imprinted surface area of about 85% of the total surface and uninterrupted non-imprinted areas of up to 40 cm 2 .
  • the basis weight (grammage) can be determined by a test method following the principles as set forth in the following standard for determining the basis weight: WSP 130.1.R4 (12) (Standard Test Method for Mass per Unit Area). Test pieces of 100 ⁇ 100 mm are punched from the sample sheet. Test pieces are chosen randomly from the entire sample and should be free of folds, wrinkles and any other deviating distortions. The pieces are conditioned at 23° C., 50% RH (Relative Humidity) for at least 4 hours. A pile of ten pieces is weighed on a calibrated balance. The basis weight (grammage) is the weighed mass divided by the total area (0.1 m 2 ), and recorded as mean value with standard deviations.
  • the thickness of a sheet material as described herein can be determined by a test method following the principles of the Standard Test Method for Nonwoven Thickness according to EDANA, WSP 120.6.R4 (12).
  • An apparatus in accordance with the standard is available from IM TEKNIK AB, Sweden, the apparatus having a Micrometer available from Mitutoyo Corp, Japan (model ID U-1025).
  • the sheet of material to be measured is cut into a piece of 200 ⁇ 200 mm and conditioned (23° C., 50% RH, ⁇ 4 hours). During measurement the sheet is placed beneath the pressure foot which is then lowered. The thickness value for the sheet is then read off after the pressure value is stabilised.
  • the measurement is made by a precision micrometer, wherein a distance created by a sample between a fixed reference plate and a parallel pressure foot is measured.
  • the measuring area of the pressure foot is 5 ⁇ 5 cm.
  • the pressure applied during the measurement is 0.5 kPa. Five measurements are performed on different areas of the cut piece to determine the thickness as an average of the five measurements.
  • the amount of water in g that can be held per g by the wipe is determined as follows:
  • the mean water absorption value of the five samples is recorded.
  • the amount of fluid (in % of a given amount) that can be wiped off by the wipe is determined as follows:
  • the wipe sample is planarly placed in center to a circular plastic wiping surface of a circular sample holder of plastic foam (Bulpren R 60 from Recticel), both the surface and the sample holder having a diameter of 113 mm. Excess sample material is folded about the side edge of the sample holder and attached thereto.
  • Water (10 g per 3.6 g sample) is spread as one strand with a length of 200 mm on a steel plate of 500 ⁇ 1200 mm.
  • the sample holder is attached to a robot that is programmed to perform six straight wipes over the steel surface for each sample and one applied water strand, wherein the circular plastic wiping surface of the holder carrying the wipe sample bears on the steel surface at a pressure of 200 g.
  • the robot and control units can be obtained from Thermo CRS.
  • each wipe the robot wipes the steel surface with the wipe sample in a straight direction along and aligned to the water strand at a speed of 80 cm/s, wherein each straight wiping action is 400 mm in length and starts at a point that prior to the first wipe is located 100 mm before the wipe comes in contact with one end of the water strand and the wiping ends 100 mm from the other water strand end that is presented prior to the first wiping.
  • the wipe sample is weighed after each wipe.
  • the amount of absorbed water in % of the amount applied on the plate (10 g per 3.6 g sample) is calculated for each wiping action and sample.
  • the procedure above is repeated for each one of the six samples and the average amount of water for each wiping action is calculated.
  • a tested material has two different sides, three samples are placed with corresponding sides facing towards the sample holder and three samples are placed with the opposite sides facing the sample holder (as were the case in the Examples below).
  • An absorbent sheet material of nonwoven was produced as illustrated in FIG. 1 (items 1 - 11 ) by laying a web of polypropylene filaments on a running conveyor fabric and then applying on the polymer web a pulp dispersion containing a 88:12 weight ratio of wood pulp and polyester staple fibres, and 0.01-0.1 wt. % of a non-ionic surfactant (ethoxylated fatty alcohol) by foam forming in a head box, introducing a total of about 30 vol. % of air (on total foam volume).
  • the weight proportion of the polypropylene filaments was 25 wt. % on dry solids basis of the end product.
  • the amounts were chosen so as to arrive at a basis weight of the end product of 80 g/m 2 .
  • the combined fibre web was then subjected to hydroentanglement using multiple water jets at increasing pressures of 40-100 bar providing a total energy supply at the hydroentangling step of about 180 kWh/ton as measured and calculated as described in CA 841938, pp. 11-12 and subsequently dried.
  • the hydroentangled and dried sheet was then imprinted in an ultrasound apparatus as depicted in FIG. 1 (items 21 - 26 ).
  • the anvil roll had a protruded part of approximately 15% of the surface area, forming lines and text patterns.
  • the imprinted sheet had the pattern as depicted in FIG. 2 .
  • Example 1 The same nonwoven of Example 1 was produced, but it was not imprinted.
  • Example 1 The nonwovens of Example 1 and the Reference Example were analysed and tested according to the Test Methods above. The results are presented in the Table below.
  • test results show that the imprinted nonwoven (Example 1) has at least equal performance to the non-imprinted nonwoven (reference example).

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Nonwoven Fabrics (AREA)
  • Paper (AREA)
  • Laminated Bodies (AREA)
US16/060,231 2015-12-08 2015-12-08 Patterned nonwoven material Abandoned US20180363177A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/EP2015/078983 WO2017097341A1 (en) 2015-12-08 2015-12-08 Patterned nonwoven material

Publications (1)

Publication Number Publication Date
US20180363177A1 true US20180363177A1 (en) 2018-12-20

Family

ID=54979644

Family Applications (1)

Application Number Title Priority Date Filing Date
US16/060,231 Abandoned US20180363177A1 (en) 2015-12-08 2015-12-08 Patterned nonwoven material

Country Status (14)

Country Link
US (1) US20180363177A1 (da)
EP (1) EP3387172B1 (da)
CN (1) CN108291343A (da)
AU (1) AU2015416530B2 (da)
CA (1) CA3007309C (da)
CO (1) CO2018005840A2 (da)
DK (1) DK3387172T3 (da)
ES (1) ES2829877T3 (da)
HK (1) HK1258258A1 (da)
MX (1) MX2018006886A (da)
PL (1) PL3387172T3 (da)
RU (1) RU2717928C2 (da)
WO (1) WO2017097341A1 (da)
ZA (1) ZA201804533B (da)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10435826B2 (en) * 2015-12-01 2019-10-08 Sca Hygiene Products Ab Process for producing nonwoven with improved surface properties
US11015292B2 (en) * 2016-09-01 2021-05-25 Essity Hygiene And Health Aktiebolag Process and apparatus for wetlaying nonwovens
WO2021126034A1 (en) * 2019-12-20 2021-06-24 Essity Hygiene And Health Aktiebolag An absorbent hygienic article for absorbing body fluids
WO2021126035A1 (en) * 2019-12-20 2021-06-24 Essity Hygiene And Health Aktiebolag An absorbent hygienic article for absorbing body fluids
US11371173B2 (en) * 2016-10-21 2022-06-28 Lenzing Ag Process and device for the formation of directly-formed cellulosic webs

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR3092732B1 (fr) * 2019-02-19 2021-06-04 Oreal Procédé de fabrication d’un article cosmétique
CA3143696A1 (en) * 2019-07-18 2021-01-21 Essity Hygiene And Health Aktiebolag Composite nonwoven sheet material
TW202138647A (zh) * 2020-02-24 2021-10-16 奧地利商蘭仁股份有限公司 用於製造紡絲黏合不織布之方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5587225A (en) * 1995-04-27 1996-12-24 Kimberly-Clark Corporation Knit-like nonwoven composite fabric
US6093665A (en) * 1993-09-30 2000-07-25 Kimberly-Clark Worldwide, Inc. Pattern bonded nonwoven fabrics
US20030213108A1 (en) * 2002-03-28 2003-11-20 Sca Hygiene Products Ab Hydraulically entangled nonwoven material and method for making it
US6784126B2 (en) * 1990-12-21 2004-08-31 Kimberly-Clark Worldwide, Inc. High pulp content nonwoven composite fabric
US20080233382A1 (en) * 2007-03-19 2008-09-25 Jared Dean Simmons Nonwoven Fibrous Structure Comprising Compressed Sites and Molded Elements
US20090255640A1 (en) * 2006-07-26 2009-10-15 Sca Hygiene Products Gmbh Multi-ply tissue paper product, paper converting device for a multi-ply tissue paper product and method for producing a multi-ply tissue paper product

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5650217A (en) * 1994-03-15 1997-07-22 Repro-Tronics, Inc. Tactile image enhancer
US20030041953A1 (en) * 2001-08-31 2003-03-06 Bba Nonwovens Simpsonville, Inc. Method of making a bonded nonwoven web
US20060128247A1 (en) * 2004-12-14 2006-06-15 Kimberly-Clark Worldwide, Inc. Embossed nonwoven fabric
WO2010021572A1 (en) * 2008-08-19 2010-02-25 Sca Hygiene Products Ab A tissue paper/nonwoven laminate product
CN102080303A (zh) * 2009-11-30 2011-06-01 苏州美森无纺科技有限公司 具有木浆纤维层的复合水刺布
BR112013000281A2 (pt) * 2010-07-07 2016-05-24 3M Innovative Properties Co mantas fibrosas não tecidas produzidas por deposição a ar (airlaid) dotadas de um padrão e métodos de preparo e uso das mesmas
JP6054866B2 (ja) * 2010-07-07 2016-12-27 スリーエム イノベイティブ プロパティズ カンパニー パターンを付けたエアレイド不織布エレクトレット繊維ウェブ、並びにその製造方法及び使用方法
BR112013016534A2 (pt) * 2010-12-28 2016-09-20 Kimberly Clark Co não tecido formado diretamente, tecido compósito integrado e método para fazer um não tecido formado diretamente
DE202011000582U1 (de) * 2011-03-15 2012-06-21 Mcairlaid's Vliesstoffe Gmbh & Co. Kg Materialbahn
US20140171895A1 (en) * 2012-12-19 2014-06-19 Kimberly-Clark Worldwide, Inc. Laminate and Process For Making Same
CN103417304A (zh) * 2013-08-08 2013-12-04 嘉兴君泰医用辅料有限公司 一种医用手术巾及其制备方法
WO2015047924A1 (en) * 2013-09-24 2015-04-02 The Procter & Gamble Company Nonwoven web with highly detailed and structurally advantageous bond pattern

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6784126B2 (en) * 1990-12-21 2004-08-31 Kimberly-Clark Worldwide, Inc. High pulp content nonwoven composite fabric
US6093665A (en) * 1993-09-30 2000-07-25 Kimberly-Clark Worldwide, Inc. Pattern bonded nonwoven fabrics
US5587225A (en) * 1995-04-27 1996-12-24 Kimberly-Clark Corporation Knit-like nonwoven composite fabric
US20030213108A1 (en) * 2002-03-28 2003-11-20 Sca Hygiene Products Ab Hydraulically entangled nonwoven material and method for making it
US20090255640A1 (en) * 2006-07-26 2009-10-15 Sca Hygiene Products Gmbh Multi-ply tissue paper product, paper converting device for a multi-ply tissue paper product and method for producing a multi-ply tissue paper product
US20080233382A1 (en) * 2007-03-19 2008-09-25 Jared Dean Simmons Nonwoven Fibrous Structure Comprising Compressed Sites and Molded Elements

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10435826B2 (en) * 2015-12-01 2019-10-08 Sca Hygiene Products Ab Process for producing nonwoven with improved surface properties
US11015292B2 (en) * 2016-09-01 2021-05-25 Essity Hygiene And Health Aktiebolag Process and apparatus for wetlaying nonwovens
US20210238804A1 (en) * 2016-09-01 2021-08-05 Essity Hygiene And Health Aktiebolag Process and apparatus for wetlaying nonwovens
US11807986B2 (en) * 2016-09-01 2023-11-07 Essity Hygiene And Health Aktiebolag Process and apparatus for wetlaying nonwovens
US11371173B2 (en) * 2016-10-21 2022-06-28 Lenzing Ag Process and device for the formation of directly-formed cellulosic webs
US20220364282A1 (en) * 2016-10-21 2022-11-17 Lenzing Ag Process and device for the formation of directly-formed cellulosic webs
US11767623B2 (en) * 2016-10-21 2023-09-26 Lenzing Ag Process and device for the formation of directly-formed cellulosic webs
WO2021126034A1 (en) * 2019-12-20 2021-06-24 Essity Hygiene And Health Aktiebolag An absorbent hygienic article for absorbing body fluids
WO2021126035A1 (en) * 2019-12-20 2021-06-24 Essity Hygiene And Health Aktiebolag An absorbent hygienic article for absorbing body fluids
CN114765950A (zh) * 2019-12-20 2022-07-19 易希提卫生与保健公司 用于吸收体液的吸收性卫生物品
US11602466B2 (en) 2019-12-20 2023-03-14 Essity Hygiene And Health Aktiebolag Absorbent hygienic article for absorbing body fluids
US11801173B2 (en) 2019-12-20 2023-10-31 Essity Hygiene And Health Aktiebolag Absorbent hygienic article for absorbing body fluids

Also Published As

Publication number Publication date
HK1258258A1 (zh) 2019-11-08
DK3387172T3 (da) 2020-11-09
ES2829877T3 (es) 2021-06-02
RU2018123573A (ru) 2020-01-09
CO2018005840A2 (es) 2018-06-20
EP3387172A1 (en) 2018-10-17
AU2015416530B2 (en) 2019-05-16
CA3007309A1 (en) 2017-06-15
CA3007309C (en) 2020-08-04
RU2018123573A3 (da) 2020-01-15
EP3387172B1 (en) 2020-10-07
RU2717928C2 (ru) 2020-03-26
MX2018006886A (es) 2018-09-06
CN108291343A (zh) 2018-07-17
AU2015416530A1 (en) 2018-06-28
WO2017097341A1 (en) 2017-06-15
PL3387172T3 (pl) 2021-04-06
ZA201804533B (en) 2019-09-25

Similar Documents

Publication Publication Date Title
AU2015416530B2 (en) Patterned nonwoven material
US8389427B2 (en) Hydroentangled nonwoven material
AU2005331321B2 (en) Hydroentangled integrated composite nonwoven material
US6992028B2 (en) Multi-layer nonwoven fabric
EP1689923B1 (en) A hydroentangled nonwoven material and a method of procuding such a material
EP2913429B1 (en) Hydraulic patterning of a fibrous, sided nonwoven web
KR20130137008A (ko) 재생 셀룰로오스 섬유를 포함하는 부직포 복합체
EP2938770A1 (en) Hydroformed composite nonwoven
US20180363182A1 (en) Process for producing imprinted sheet materials
JP7307632B2 (ja) 複合型不織布の製造方法
NZ758495A (en) Patterned nonwoven material
WO2013095241A1 (en) Method of producing a hydroentangled nonwoven material and a hydroentangled nonwoven material
JP7324014B2 (ja) 複合型不織布とその製造方法
JP2023006231A (ja) 複合型不織布およびその製造方法
JP2022003173A (ja) 複合型不織布およびその製造方法
JP2021172936A (ja) 複合型不織布およびその製造方法
JP2022138533A (ja) 複合型不織布およびその製造方法
JP2023114129A (ja) 複合型不織布およびその製造方法
US20120208423A1 (en) Laminated Nonwoven Fabric

Legal Events

Date Code Title Description
AS Assignment

Owner name: SCA HYGIENE PRODUCTS AB, SWEDEN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:STRANDQVIST, MIKAEL;REEL/FRAME:046016/0323

Effective date: 20180427

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STCT Information on status: administrative procedure adjustment

Free format text: PROSECUTION SUSPENDED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE AFTER FINAL ACTION FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE AFTER FINAL ACTION FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

AS Assignment

Owner name: ESSITY HYGIENE AND HEALTH AKTIEBOLAG, SWEDEN

Free format text: CHANGE OF NAME;ASSIGNOR:SCA HYGIENE PRODUCTS AKTIEBOLAG;REEL/FRAME:057255/0876

Effective date: 20180220

STCV Information on status: appeal procedure

Free format text: NOTICE OF APPEAL FILED

STCV Information on status: appeal procedure

Free format text: APPEAL BRIEF (OR SUPPLEMENTAL BRIEF) ENTERED AND FORWARDED TO EXAMINER

STCV Information on status: appeal procedure

Free format text: EXAMINER'S ANSWER TO APPEAL BRIEF MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION