US20180133834A1 - Splitting of a solid using conversion of material - Google Patents
Splitting of a solid using conversion of material Download PDFInfo
- Publication number
- US20180133834A1 US20180133834A1 US15/544,014 US201515544014A US2018133834A1 US 20180133834 A1 US20180133834 A1 US 20180133834A1 US 201515544014 A US201515544014 A US 201515544014A US 2018133834 A1 US2018133834 A1 US 2018133834A1
- Authority
- US
- United States
- Prior art keywords
- solid
- modifications
- less
- laser
- generated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for creating a detachment zone in a solid is contemplated, such as in order to detach a solid portion, especially a solid layer, from the solid, said solid portion that is to be detached being thinner than the solid from which the solid portion has been removed. The method may comprise at least the steps of: providing a solid which is to be processed and which is made of a chemical compound; providing a LASER light source; and subjecting the solid to LASER radiation from the LASER light source so that the laser beams penetrate into the solid via a surface of the solid portion that is to be cut off; the LASER radiation controlling the temperature of a predefined portion of the solid inside the solid in a defined manner such that a detachment zone or a plurality of partial detachment zones is formed; characterized in that the temperature produced by the laser beams in a predefined portion of the solid is so high that the material forming the predefined portion is subject to modifications in the form of a predetermined conversion of material.
Description
- According to
claim 1, the invention at hand relates to a method for creating a detachment zone in a solid in order to detach a solid portion from the solid and, according to claim 13, to a method for detaching at least one solid portion from a solid. - The splitting of solids, in particular of wafers, is classically effected by means of sawing. This splitting method, however, has a plurality of disadvantages. For instance, chips are always created during sawing, which thus represent destroyed basic material. The thickness fluctuation of the sawed-off disks further also increases when the sawing height increases. In addition, the sawing element has the effect that grooves and surface damages are created on the surfaces of the disks, which are to be separated from one another.
- It can thus be seen that the splitting method “sawing” involves very high material costs and costs for the reworking.
- Publication WO 2013/126927 A2 further discloses a method for cutting off device layers from an original wafer. According to WO 2013/126927 A2, the overall arrangement is thereby heated up very strongly as a result of a laser application. This heating is required in order to reach stresses in the interior of the solid via the different heat expansion coefficients of the solid material and via a “handler”. It can be seen hereby that the thermal stressability of the “handler” must be very high, because very high temperatures appear. According to WO 2013/126927 A2, the laser beams are further always introduced into the solid via a surface, which is not part of the layer to be separated. This also leads to a strong heating of the solid. The high temperatures also have the disadvantage that the solid distorts or expands unintentionally, whereby the generation of crystal lattice modifications is only possible in a highly inaccurate manner.
- According to WO 2013/126927 A2, thick and large solids can thus not be processed.
- It is thus the object of the invention at hand to provide an alternative method for cutting off solid portions, in particular a plurality of solid layers, from a solid. According to the invention, the above-mentioned object is solved by means of a method for creating a detachment zone in a solid in order to detach a solid portion, especially a solid layer, from the solid, wherein the solid portion, which is to be detached, is thinner than the solid, from which the solid portion has been removed. According to the invention, the method comprises at least the steps of providing a solid, which is to be processed, wherein the solid is made of a chemical compound; providing a LASER light source or a laser radiation source, respectively; applying LASER radiation from the LASER light source to the solid, wherein the laser beams penetrate into the solid via a surface of the solid portion, which his to be cut off, wherein the LASER radiation controls the temperature of a predefined portion of the solid inside the solid in a defined manner such that a detachment zone or a plurality of partial detachment zones is formed. Particularly preferably, the temperature produced by the laser beams in the predefined portion of the solid is so high, in particular more than 200° C. or more than 500° C. or more than 800° C. or more than 1000° C. or more than 1500° C. or more than 2000° C., that the material forming the predefined portion is subject to modifications in the form of a predetermined conversion of material.
- This solution is advantageous, because a material conversion or phase conversion, respectively, can preferably be effected without a local destruction of the crystal lattice, whereby a weakening or stability reduction, respectively, can be created in the solid in a highly controlled manner.
- Further preferred embodiments are the subject matter of the subclaims and of the following description parts.
- According to a further preferred embodiment of the invention at hand, the material conversion represents a decomposition of the chemical compound into a plurality or into all individual components or elements, respectively. This embodiment is advantageous, because the material combination, which is most suitable for cutting off the solid portion, can be adjusted in a defined manner by means of the systematic decomposition of the chemical compound of the solid.
- According to the description at hand, a solid starting material is preferably understood as a monocrystalline, polycrystalline or amorphous material. Preferably, monocrystallines comprising a highly anisotropic structure are suitable because of the highly anisotropic atomic binding forces. The solid starting material preferably has a material or a material combination from one of the
main groups subgroup 12 of the periodic table of elements, in particular a combination of elements from the 3., 4., 5. main group and thesubgroup 12, such as, e.g. zinc oxide or cadmium telluride. - In addition to silicon carbide, the semiconductor starting material can for example also consist of silicon, gallium arsenide GaAs, gallium nitride GaN, silicon carbide SiC, indium phosphide InP, zinc oxide, ZnO, aluminum nitride AIN, germanium, gallium(III) oxide Ga2O3, aluminum oxide Al2O3 (sapphire), gallium phosphide GaP, indium arsenide InAs, indium nitride InN, aluminum arsenide AlAs or diamond.
- The solid or the workpiece (e.g. wafer), respectively, preferably has a material or a material combination from one of the
main groups - According to a further preferred embodiment of the invention at hand, the LASER radiation is introduced into the solid with a pulse density of between 100 nJ/μm2 and 10000 nJ/μm2, preferably between 200 nJ/μm2 and 2000 nJ/μm2 and particularly preferably between 500 nJ/μm2 and 1000 nJ/μm2 for controlling the temperature in a defined manner.
- According to a further preferred embodiment of the invention at hand, the receiving layer has a polymer or consists thereof, wherein the polymer is preferably polydimethylsiloxane (PDMS) or an elastomer or an epoxy resin or a combination thereof.
- According to a further preferred embodiment of the invention at hand, the energy of the laser beam of the laser, in particular fs laser (femtosecond laser) is chosen in such a way that the material conversion in the solid or in the crystal, respectively, in at least one direction is smaller or larger than 30-times, or 20-times, or 10-times or 5-times or three-times the Rayleigh length.
- According to a further preferred embodiment of the invention at hand, the wavelength of the laser beam of the laser, in particular of the fs laser, is chosen in such a way that the linear absorption of the solid or of the material, respectively, is less than 10 cm−1 and preferably less than 1 cm−1 and particularly preferably less than 0.1 cm−1.
- According to a further preferred embodiment of the invention at hand, the solid is connected to a cooling device via a solid surface, wherein the solid surface, which is connected to the cooling device, is embodied parallel or substantially parallel to the surface, via which the laser beams penetrate into the solid, wherein the cooling device is operated as a function of the laser application, in particular as a function of the temperature control of the solid, which results from the laser application. Particularly preferably, the surface, via which the solid is connected to the cooling device, is located exactly opposite the surface, via which the laser beams penetrate into the solid. This embodiment is advantageous, because a temperature increase of the solid, which occurs in response to the generation of the modifications, can be limited or reduced. The cooling device is preferably operated in such a way that the heat input introduced into the solid by means of the laser beams is removed from the solid through the cooling device. This is advantageous, because the occurrence of thermally induced stresses or deformations can be reduced significantly through this.
- According to a further preferred embodiment of the invention at hand, the cooling device has at least one sensor device for capturing the temperature of the solid and, as a function of a predefined temperature course, effects a cool-down of the solid. This embodiment is advantageous, because a temperature change of the solid can be captured in a highly accurate manner by means of the sensor device. The change of the temperature is preferably used as data input for controlling the cooling device.
- According to a further preferred embodiment of the invention at hand, the cooling device is coupled to a rotating means and the cooling device comprising the solid arranged thereon is rotated by means of the rotating means during the generation of the modifications, in particular with more than 100 revolutions per minute or with more than 200 revolutions per minute or with more than 500 revolutions.
- According to a further preferred embodiment of the invention at hand, the number of the generated modifications per cm2 is different in at least two different zones of the solid, wherein a first block of modifications is generated in a first zone, wherein the individual modifications per line are preferably generated spaced apart from one another by less than 10 μm, in particular less than 5 μm or less than 3 μm or less than 1 μm or less than 0.5 μm, and the individual lines of the first block are generated spaced apart from one another by less than 20 μm, in particular less than 15 μm or less than 10 μm or less than 5 μm or less than 1 μm, wherein a first partial detachment zone is formed by the first block of modifications and a second block of modification lines is generated in a second zone, wherein the individual modifications per line are preferably generated spaced apart from one another by less than 10 μm, in particular less than 5 μm or less than 3 μm or less than 1 μm, or less than 0.5 μm, and the individual lines of the second block are generated spaced apart from one another by less than 20 μm, in particular less than 15 μm or less than 10 μm or less than 5 μm or less than 1 μm, wherein a second partial detachment zone is formed by the second block of modifications, wherein the first zone and the second zone are spaced apart from one another by a third zone, wherein no modifications or essentially no modifications are generated in the third zone by means of laser beams, and the first zone is spaced apart from the second zone by more than 20 μm, in particular more than 50 μm or more than 100 μm or more than 150 μm or more than 200 μm. This embodiment is advantageous, because mechanical stresses, which are so large that either a local cracking of the solid can take place or that a crack is created in the solid as a result of a further triggering event, such as the thermal application of a receiving layer arranged on the solid, can be created in the solid by means of the local generation of modification blocks. It has been recognized that the modification blocks have the effect that a tear is also guided in a stable manner in a zone between two modification blocks. Thanks to the modification blocks, a controlled and highly accurate crack propagation can be effected by means of fewer modifications. This has significant advantages, because the processing time is shortened, the energy consumption is reduced, and the heating of the solid is reduced.
- The modifications in the first block are preferably generated at pulse intervals of between 0.01 μm and 10 μm and/or line spacings of between 0.01 μm and 20 μm are provided, and/or a pulse repetition frequency of between 16kHz and 20 MHz is provided.
- According to a further aspect of the invention at hand, an optics, by means of which the laser beams are guided from a laser beam source to the solid, is adapted as a function of the location, at which a modification is generated, from which at least one change of the numerical aperture is effected, wherein the numerical aperture at a location in the edge zone of the solid is smaller than at a different location of the solid, which is located closer to the center of the solid. This embodiment is advantageous, because modifications comprising different properties are generated. In particular in the edge zone, i.e. in the zone of up to 10 mm or of up to 5 mm or of up to 1 mm (in radial direction) away from the edge, an optics is preferably used, which is a numerical aperture of between 0.05 and 0.3, in particular of substantially or of exactly 0.1. For the remaining zones, an optics is preferably used, in the case of which the numerical aperture is between 0.2 and 0.6, preferably between 0.3 and 0.5, and particularly preferably is substantially or exactly 0.4.
- According to a further preferred embodiment of the invention at hand, the thermal application of the receiving layer comprises a cool-down of the receiving layer to a temperature of below 20° C., in particular below 10° C. or below 0° C. or below −10° C. or below 100° C. or to or below the glass transition temperature of the material of the receiving layer.
- By means of the temperature control, modifications are or the material conversion is generated by means of LASER, wherein the pulse intervals are provided between 0.01 μm and 10 μm, in particular with 0.2 μm, and/or line spacings of between 0.01 μm and 20 μm, in particular with 3 μm, and/or a pulse repetition frequency of between 16 kHz and 20 MHz, in particular with 128 kHz, is provided, and/or a pulse energy of between 100 nJ and 2000 nJ, in particular with 400 nJ, is provided. Particularly preferably, a pikosecond or femtosecond laser is used for the method according to the invention, in particular when applying silicon carbide, wherein the LASER preferably has a wavelength of between 800 nm and 1200 nm, in particular of 1030 nm or 1060 nm. The pulse duration is preferably between 100 fs and 1000 fs, in particular at 300 fs. Preferably, a lens for focusing the laser beam is furthermore used, wherein the lens preferably effects a 20-100-times reduction, in particular a 50-times reduction or focusing, respectively, of the LASER beam. Preferably, the optics for focusing the laser beam furthermore has a numerical aperture of between 0.1 and 0.9, in particular of 0.65.
- Preferably, every material conversion effected by means of the LASER radiation represents a modification of the material of the solid, wherein the modifications can additionally or in the alternative be understood as destruction of the crystal lattice of the solid, e.g. According to a further preferred embodiment of the invention at hand, the solid is moved with respect to the LASER light source, in particular displaced, in particular rotated. The movement, in particular rotation, of the solid with respect to the LASER light source preferably takes place in a continuous manner. The rotational speeds appearing thereby preferably exceed 1 revolution per second or 5 revolutions per second or 10 revolutions per second or a linear speed of at least 100 mm/s, respectively. For this purpose, the solid is preferably arranged on a rotary table or rotary chuck, respectively, in particular by means of adhesion. The number of modification per cm2 of the solid surface, through which the LASER radiation penetrates into the solid in order to generate the modifications, per rotation is preferably below a predefined maximum number, wherein the maximum number of the modifications per cm2 and per rotation is preferably determined as a function of the solid material and/or of the energy density of the LASER radiation and/or as a function of the duration of the LASER radiation impulses. Preferably, a control device is provided, which determines the maximum number of the modifications to be generated per cm2 per rotation as a function of at least two or three or all of the above-mentioned parameters and preferably of further parameters by means of predefined data and/or functions. This is especially advantageous, because it was recognized that damaging vertical cracks are created, when the damage density is too high, which results from stresses, which are created between the processed zones and the zones, which have not been processed yet.
- In addition or in the alternative, the modifications are generated with different patterns, in particular distances between the individual newly-generated modifications and/or with changed energy input, in particular reduced energy input, in response to consecutive rotations of the solid with respect to the LASER light source. Either the laser or the wafer or solid, respectively, can in particular be displaced in XY direction, wherein the modifications are generated as a function of the translational XY displacement. According to a preferred embodiment, an XY table is used, on which the solid is arranged during the operation of the laser. The optics, by means of which the LASER beams are deflected, is preferably readjusted or newly adjusted, respectively, continuously or in stages, in particular as a function of a movement of the solid, in particular of a rotation of the solid, by means of the already mentioned control device or an alternative control device. Due to the readjustment or new adjustment, respectively, an adjustment of a second LASER beam course preferably takes place with respect to the first LASER beam course, which is adjusted prior to the readjustment or new adjustment, respectively, which differs from the first LASER beam course. As a function of the rotation of the solid, the control device thus preferably adjusts different LASER beam courses. Particularly preferably, the LASER scanning direction is thereby in each case readjusted or newly adjusted, respectively, or changed, respectively. In addition or in the alternative, the control device preferably controls the LASER light source, the optics, in particular the scanners, and/or the device, which displaces the solid, in particular the rotary table or rotary chuck, respectively, in such a way that the energy input per rotation remains the same or decreases, wherein the energy input into the solid preferably decreases continuously, i.e. with each rotation, or decreases in stages, i.e. in each case after a plurality of rotations. Wherein the number of rotations per stage can differ from one another in the case of a gradual decrease of the energy input, a first stage can comprise more than 2 rotations, e.g., and another stage can comprise more or fewer rotations than the first stage. It is furthermore conceivable that the stages in each case comprise the same number of rotations. The stage method can further also be mixed or combined, respectively, with the continuous method.
- According to a preferred embodiment, the laser beam can also repeatedly apply modifications to a line, so that a total modification is generated in a line or row, respectively. According to a further alternative, the lines can cross or overlap one another, respectively, when applying modifications to the laser, wherein the first line of the modifications can in particular intersect one another at a predetermined angle of for example 90°, 45°, 30°, 60° or at another freely selectable angle. The intersecting angles between lines of the laser application for generating modifications can thereby orientate themselves on the crystal orientation of the material of the solid, in order to increase the effectiveness of the added modifications.
- In addition or in the alternative, the LASER light source is embodied as scanner and the generation of the modifications takes place a function of the laser scanning direction, the laser polarization direction and the crystal orientation. The devices required for generating modifications, in particular the LASER light source, the optics, in particular the scanner, and the device, which displaces the solid, in particular the rotary table or rotary chuck, respectively, is preferably controlled by means of the already mentioned control device or by means of an alternative control device, which, as a function of at least two or three of the above-mentioned parameters and preferably further parameters, by means of predefined data and/or functions.
- In addition or in the alternative, the distance between the centers of two modifications, which are generated consecutively in modification generating direction or in circumferential direction of the solid, is less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm.
- In addition or in the alternative, the outer limitations of modifications, which are generated consecutively in modification generating direction or in circumferential direction of the solid, are spaced apart from one another by less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm.
- The invention at hand can further refer to a method for creating a detachment zone in a solid in order to detach a solid portion from the solid, which comprises at least the below-mentioned steps of:
- providing a solid, which is to be processed, providing a LASER light source, applying LASER radiation from the LASER light source to the solid, wherein the LASER radiation generates modifications, in particular crystal lattice defects, in the solid, wherein a control device for controlling the LASER light source and/or a device, which displaces the solid, in particular a rotary table or rotary chuck, respectively, and/or an optics, in particular a scanner, as a function of individual or a plurality of certain parameters or as function of individual or a plurality of these parameters is provided.
- The solid is preferably rotated with respect to the LASER light source and the number of the modifications per cm2 of the solid surface per rotation, through which the LASER radiation penetrates into the solid in order to generate the modifications, is below a predefined maximum number, wherein the maximum number of the modifications per cm2 and per rotation is preferably determined as a function of the solid material and of the energy density of the LASER radiation, and/or the modifications are generated with different patterns, in particular distances between the individual newly generated modifications and/or with changed energy input, in particular reduced energy input, in response to consecutive rotations of the solid with respect to the LASER light source, and/or the LASER light source is embodied as scanner and the generation of the modifications takes place as a function of the laser scanning direction, the laser polarization direction and the crystal orientation, and/or the distance between the centers of two modifications, which are generated consecutively in modification generating direction or in circumferential direction of the solid is less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm,
- and/or the outer limitations of modifications, which are generated consecutively in modification generating direction or in circumferential direction of the solid, are spaced apart from one another by less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm.
- Preferably, the maximally possible number of the modifications, which can be generated in one displacement cycle, in particular one rotation, of the solid with respect to the optics, in particular a scanner, is determined by a plurality of parallel lines, which are in particular spaced apart from one another in radial direction, and the modifications, which can be maximally generated per line. According to a preferred embodiment, the laser beam can be divided into a plurality of laser beams by means of a diffractive optical element, in order to thus simultaneously generate a corresponding number of modifications according to the splitting of the laser beam. The plurality of the lines preferably comprises at least two and preferably at least 10 and particularly preferably up to 50 or up to 100 or up to 200 lines. With regard to the generated patterns, it is conceivable thereby that in the case of a certain number of lines in a first displacement cycle, e.g. only every xth line or every xth and yth line or every xth and every xth minus z line is provided with modifications. Concretely, every 5th line, for example, could be provided with modifications. In the alternative, every 5th and every 7th line could be provided with modifications. In the alternative, e.g., every 5th and every 5th minus 2 could be provided with modifications, which would then result in that the 3rd, 5th, 8th, 10th 13th, 15th, etc. line is provided with modifications. In addition, it is possible that the modifications are generated block by block, that is, that for example a block of 50 consecutive lines includes a modification and the following 50 lines do not include any modifications at all, wherein this block of 50 lines without modification is in turn followed by a block of 50 lines comprising a modification. This means that block by block modifications of a plurality of lines are provided alternately. According to a further embodiment, the width of such alternating blocks can vary according to the distance from the edge of the sample, that is that the blocks have a smaller line number of modifications for example in the area of the edge, and have a higher line number of modifications towards the center of the sample. It is conceivable in addition or in the alternative that the distance between the lines, in which modifications are generated, change as a function of a function. In a second displacement cycle, which preferably appears after the end of the first displacement cycle, in particular after a first rotation, alternative lines, which are preferably spaced apart relative to one another, are preferably written. In the second displacement cycle and in the further displacement cycles, other line numbers can then be provided for the variables x, y, z. More or fewer variables can further be provided. In addition or in the alternative, the distance between the individual modifications of a line can be generated according to a pattern. The modifications in one line are thus preferably generated in a first displacement cycle, in particular a first rotation, e.g. only at every ath point (at which a modification is provided) or at every ath and bth point or at every ath and every ath minus c point. In addition or in the alternative, it is conceivable that the distance between the points, at which modifications are generated, changes as a function of a function. In a second displacement cycle, which preferably appears after the end of the first displacement cycle, in particular after a first rotation, alternative points, which are preferably spaced apart relative to one another, are preferably written. In the second displacement cycle and in the further displacement cycles, other line numbers can then be provided for the variables a, b, c. In addition or in the alternative, it is conceivable that the lines, which are processed, are determined at least as a function of a displacement point or displacement setting, respectively, in particular a rotational position, and the number of rotations and/or the points in a line, which are processed (or at which modifications are generated, respectively) are determined at least as a function of the displacement position or displacement point, in particular a rotational position, and the number of rotations. In particular in the case of linear displacement paths of the solid or of the optics, lines or strips of modifications, which are positioned at an incline to one another, in particular at a right angle, can be generated as well.
- According to a further preferred embodiment, every material conversion, which is effected by means of the LASER radiation, represents a modification of the material of the solid, wherein the solid is moved in a translational manner in XY direction with respect to the LASER light source, and the number of modifications per cm2 of the solid surface, through which the LASER radiation penetrates into the solid in order to generate the modifications, wherein the maximum number of the modifications per cm2 and according to the translational movement in XY direction is preferably determined as a function of the solid material and of the energy density of the LASER radiation and/or the modifications are generated with different patterns, in particular distances between the individual newly generated modifications, and/or with changed energy input, in particular reduced energy input, according to the translational movement in XY direction of the solid with respect to the LASER light source, and/or the LASER light source is embodied as scanner, and the generation of the modifications takes place as a function of the laser scanning direction, the laser polarization direction and the crystal orientation, and/or the distance between the displacements of two modifications, which are generated consecutively in modification generating direction is less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm, and/or the outer limitations of modifications, which are generated consecutively in modification generating direction, are spaced apart from one another by less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm.
- According to a further preferred embodiment, the LASER radiation generates modifications, in particular crystal lattice effects, in the solid, wherein the solid is moved in a translational manner with respect to the LASER light source, and the number of the modifications per cm2 of the solid surface, through which the LASER radiation penetrates into the solid in order to generate the modifications, wherein the maximum number of the modifications per cm2 and according to the translational movement in XY direction is preferably determined as a function of the solid material and of the energy density of the LASER radiation and/or the modifications are generated with different patterns, in particular distances between the individual newly generated modifications, and/or with changed energy input, in particular reduced energy input, according to the translational movement in XY direction of the solid with respect to the LASER light source, and/or the LASER light source is embodied as scanner, and the generation of the modifications takes place as a function of the laser scanning direction, the laser polarization direction and the crystal orientation, and/or the distance between the displacements of two modifications, which are generated consecutively in modification generating direction is less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm, and/or the outer limitations of modifications, which are generated consecutively in modification generating direction, are spaced apart from one another by less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm.
- The control unit controls the generation of the modifications, for example as a function of the number of the displacement cycles and/or of the local heat development, which is preferably captured optically and/or by means of sensors, and/or as a function of the material properties, in particular the density and/or the stability and/or the thermal conductivity of the solid. The invention further relates to a method for cutting off at least one solid portion from a solid, in particular a wafer, at least comprising the steps of: arranging a receiving layer on a solid, which is treated according to a method according to one of
claims 1 to 4, thermal application of the receiving layer for, in particular mechanically, generating crack expansion stresses in the solid, wherein a crack expands in the solid along the detachment zone due to the crack expansion stresses. - Further advantages, goals and characteristics of the invention at hand will be explained by means of the following description of attached drawings, in which the separating method according to the invention is illustrated in an exemplary manner. Components or elements, which are preferably used in the method according to the invention, and/or which at least substantially correspond in the figures with regard to their function, can hereby be identified with the same reference numerals, wherein these components or elements do not need to be numbered or explained in all figures.
-
FIG. 1 shows a schematic illustration of the laser-based generation according to the invention of a detachment layer in a solid; -
FIG. 2 shows a schematic illustration of a preferred cut-off process for cutting off a solid layer from a solid 7; -
FIG. 3 shows two microscopic illustrations of the surfaces, which were created along the detachment zone, of the solid portions, which are cut off from one another; -
FIG. 4 shows an illustration for showing the effect according to the invention; -
FIGS. 5a-5c show three schematic cross sectional illustrations, which in each case show modification blocks in a solid; -
FIGS. 5d-5e show two schematic illustrations, in each case along the detachment zones of split solids, wherein the illustration according toFIG. 5d does not show any modification remainders and the illustration according toFIG. 5e shows modification remainders; -
FIGS. 6a-c show three schematic illustrations of modification blocks and the local solid weakening or local solid cracks created through this; -
FIGS. 7a-c show three schematic illustrations of exemplary crack paths; -
FIGS. 8a-c show the repeated cut-off of solid portions or solid layers, respectively, in particular wafers, from a solid; -
FIGS. 9a-f show a plurality of steps from the provision of the solid to the triggering of the crack as a result of a thermal application of the receiving layer; -
FIG. 10a shows a schematic illustration of the state after the solid portion cut-off; -
FIG. 10b shows a further laser application of the remaining solid for generating modifications for cutting off a further solid layer; -
FIG. 10c shows a schematic illustration of the remaining solid arranged on a cooling device, wherein the cooling device is arranged on a displacement device, in particular a rotary table; -
FIG. 10d shows a schematic illustration of the generation of modifications in the solid; -
FIG. 11 shows a schematic illustration of a cooling device, in particular of a cooling chuck; -
FIG. 12 shows a schematic illustration of a preferably used optics; and -
FIG. 13 shows a schematic illustration of overlapping beams or beam portions, respectively, in response to the generation of a modification in the solid. - In
FIG. 1 ,reference numeral 1 identifies the solid. According to the invention,modifications 9 are generated in the solid 1, in order to form adetachment zone 2, at which or along which, respectively, the solid 1 is separated into at least two components. Themodifications 9 are thereby material conversions or phase conversions, respectively, of the solid material, by means of which thedetachment zone 2 is created. Themodifications 9 are generated by means of at least onelaser beam 4. Thelaser beam 4 penetrates into the preferably at least partially transparent solid 1 via a preferably treated, in particular polished,surface 5. On thesurface 5, the at least one laser beam is preferably broken, which is identified byreference numeral 6. The at least one laser beam then forms afocus 8 for generating the modification. Thepolished surface 5 can also be identified as main surface 18. -
FIG. 2 also shows the treated solid 1, wherein areceiving layer 140 for introducing stresses into the solid 1, is arranged, in particular attached or generated, on at least one surface of the solid 1, in particular partially or completely covering or overlapping thesurface 5. After splitting off the solid layer or the solid portion, respectively, from the solid 1, thereceiving layer 140 initially remains on the split-off solid portion and thus serves to receive it. Thereceiving layer 140 preferably consists of a polymer material or has a polymer material, in particular PDMS. Due to a temperature control, in particular cool-down, of thereceiving layer 140, thereceiving layer 140 contracts and thus introduces stresses into the solid 1, by means of which a crack is triggered and/or is generated and/or guided for cutting off the solid portion from the solid 1. - The LASER application of the solid 1 particularly preferably represents a local temperature control of the solid 1, in particular in the interior of the solid 1. Due to the temperature control, the chemical bond of the solid material changes, whereby a change, in particular reduction, of the strength or stability, respectively, of the solid 1 results in the applied portion. The LASER application preferably takes place in a total plane, which penetrates in the solid 1, wherein it is also conceivable for at least or maximally 30% or 50% or 60% or 70% or 80% or 90% of the plane, which penetrates the solid 1, to experience the modification according to the invention.
-
Reference numeral 10 identifies a first solid portion after cutting through the solid 1, andreference numeral 12 identifies the second solid portion after separating the solid 1.Reference numeral 11 further identifies the surfaces, along which the twosolid portions -
FIG. 3 shows asurface 11 of a firstsolid portion 10 and of a secondsolid portion 12, wherein the firstsolid portion 10 and the secondsolid portion 12 were separated from one another along thesurfaces 11.FIG. 3 furthermore shows anuntreated zone 51 or untreated portion of the solid 1, respectively, and a treatedzone 52 or treated portion of the solid 1, respectively. The treatedportion 52 was created by means of the LASER application according to the invention and shows that the material of the solid 1 changed or was converted, respectively, in this zone. -
FIG. 4 shows a Raman spectrum (reference numeral 53) 6H-SiC with conditioning 1B after cutting off thesolid portion 12.Reference numeral 54 identifies the intensity in % andreference numeral 56 identifies the wave number in cm−1.Reference numeral 61 furthermore identifies the graph for the untreated material portion identified withreference numeral 51 inFIG. 3 andreference numeral 62 identified the graph for the treated material portion identified withreference numeral 52 inFIG. 3 . It can be gathered from theRaman spectrum 53 that the material portions identified byreference numerals - The LASER application according to the invention effects a material-specific, spatially resolved cumulation of the entry input, from which a defined temperature control of the solid 1 results at a defined location or at defined locations and within a defined time. In a concrete application, the solid 1 can consist of silicon carbide, whereby a locally highly limited temperature control of the solid 1 to a temperature of, e.g., more than 2830+/−40° C. is preferably carried out. New materials or phases, in particular crystalline and/or amorphous phases, result from this temperature control, wherein the resulting phases are preferably Si (silicon) and DLC (diamond-like carbon) phases, which are created with significantly reduced stability. The
detachment portion 2 then results from this stability-reduced layer. The laser control preferably takes place by means of spatially resolved sample temperature measurement in order to avoid edge effects in response to the solid or wafer processing, respectively. -
FIG. 5a shows that the number of the generated modifications per cm2 is different in at least two different zones of the solid 1. In a first zone, afirst block 91 is thereby generated at modification lines, wherein theindividual modifications 9 per line are preferably generated spaced apart from one another by less than 10 μm, in particular less than 5 μm or less than 3 μm or less than 1 μm or less than 0.5 μm. The individual lines of thefirst modification block 91 are preferably generated spaced apart from one another by less than 20 μm, in particular less than 15 μm or less than 10 μm or less than 5 μm or less than 1 μm. Mechanical stresses are generated in the solid 1 by means of thefirst block 91 ofmodifications 91. - In a second zone, a
second block 92 of modification lines is generated, wherein theindividual modifications 9 per line are preferably generated spaced apart from one another by less than 10 μm, in particular less than 5 μm or less than 3 μm or less than 1 μm or less than 0.5 μm. The individual lines of thesecond block 92 are preferably generated spaced apart from one another by less than 20 μm, in particular less than 15 μm or less than 10 μm or less than 5 μm or less than 1 μm. Mechanical stresses are generated in the solid 1 by means of thesecond block 92 ofmodifications 92. - The first zone and the second zone are spaced apart from one another by a third zone, wherein no modifications or essentially no
modifications 9 are generated in the third zone by means of laser beams, and the first zone is spaced apart from the second zone by more than 20 μm, in particular more than 50 μm or more than 100 μm or more than 150 μm or more than 200 μm. - The
modifications 9 are hereby preferably introduced into the solid 1 via asurface 5 of the subsequentsolid layer 12. The distance between thesurface 5, via which the laser beams are introduced, to themodifications 9, is preferably less than the distance of themodifications 9 to afurther surface 7 of the solid 1, which is spaced apart from thesurface 5 and which is preferably oriented in parallel. - It can be seen that the
detachment zone 2 according to this illustration is located on one side, in particular below or above allmodifications 9 in solid longitudinal direction, and is preferably spaced apart from themodifications 9. -
FIG. 5b show a similar basic construction. According toFIG. 5b , thedetachment zone 2, however, extends through themodifications 9. -
FIG. 5c further shows that thedetachment zone 2 can also run through the center of themodifications 9. - The course of the
detachment zone 2 can hereby be adjusted via the number of themodifications 9 and/or the size of themodifications 9 and/or the distance of theindividual modifications 9 of ablock -
FIG. 5d shows the remaining solid 1 after the detachment of thesolid layer 12 along thedetachment zone 2 shown inFIG. 5a . Due to the fact that themodifications 9 are completely removed from the remaining solid 1 in this case, the remaining solid 1 does not show any remainders of thesemodifications 9. - In contrast, remainders of the
modifications 9 can be gathered fromFIG. 5e . These modification remainders result, when the solid 1 is cut off along adetachment zone 2, which is shown inFIG. 5b or 5 c. It can further be seen that the modification blocks 91, 92 are preferably spaced apart from one another by cm2 each, preferably by means offields modifications 9 or withfewer modifications 9 can hereby preferably be smaller or larger than the zone, in which the modification blocks 91, 92 are created. At least individual, a plurality or the majority of the zones, in which the modification blocks 91, 92 are generated, are preferably many times larger, in particular at least 1.1-times or 1.5-times or 1.8-times or 2-times or 2.5-times or 3-times or 4-times larger than the zones, in which nomodifications 9 orfewer modifications 9 are generated. -
FIGS. 6a-6c show a further embodiment of the invention at hand. According to these illustrations, the modification blocks 91, 92 serve to create local material weakening or local solid cracks or local stress increases.Reference numeral 25 hereby identifies a first partial detachment zone or crack portion, in which the local material weakening or local solid cracks or local stress increases appear, andreference numeral 27 hereby identifies a second partial detachment zone or crack portion, in which the local material weakening or local solid cracks or local stress increases appear as well. The individual partial detachment zones or crack portions preferably form ends 71, 72, beyond which the respective partial detachment zone or crack portion can be enlarged. The enlargement of the partial detachment zones or crack portions preferably takes place as a result of a force introduction, which is effected by means of the receiving layer 140 (seeFIG. 2 ). -
FIGS. 7a to 7c show embodiments, according to which the course of thedetachment zone 2 is controlled in such a way as a result of the generation of the modification blocks 91, 92, 93 that predetermined patterns or thickness changes are created or compensated. The course of thedetachment zone 2 can hereby be adjusted, e.g., via the number of themodifications 9 and/or the size of the modifications and/or the distance of theindividual modifications 9 of ablock - In
FIG. 7a , thedetachment zone 2 is formed by the below-mentioned components: crack 31 between outer edge andfirst modification block 91, followed by thefirst crack portion 25, which is created directly by means of thefirst block 91 ofmodifications 9, follows bycrack 32 between the twomodification blocks second crack portion 27, which is created directly by means of thesecond block 92 ofmodifications 9, followed by the crack 33 between themodification block 92 and the further outer edge of the solid 1. It can be seen through this that thedetachment zone 2 can be predefined in such a way that a crack for cutting off thesolid layer 12 form the solid 1 can run at different planes in sections. - It can be seen according to
FIG. 7b that thedetachment zone 2 can be chosen in such a way that the course of the crack includes a plurality of geometric turning points. -
FIG. 7c shows a further possible design of thedetachment zone 2 merely in an exemplary manner. - Wit regard to
FIGS. 7a-7c , it is important to note that the formation of wavy courses can offer advantages in response to the further treatment of the exposed surfaces, in particular in the case of subsequent grinding and/or polishing steps. Due to the height of themodifications 9, which is very small in fact, the actual waviness, which is created via this, can only be captured in a high resolution. By means of modification blocks, such as, e.g., theblocks fewer modifications 9 are generated. -
FIGS. 8a-8c show a repeated processing of a solid 1, in particular of an ingot, wherein the solid 1 is in each case thinned by asolid portion 12, especially asolid layer 12. Receivinglayers 140, which may need to be attached, as shown inFIG. 2 , are not shown in these illustrations. In terms of the invention at hand, however, areceiving layer 140 for receiving thesolid portion 12 and for triggering and/or supporting a crack can also be arranged on thesurface -
FIGS. 8a-8c thus in each case show the application of LASER radiation from the LASER light source to the solid, wherein the laser beams penetrate into the solid 1 via asurface solid layer 12, which is to be cut off. The LASER radiation controls the temperature of a predefined portion of the solid 1 inside the solid 1 in a defined manner such that adetachment zone 2 or a plurality of partial detachment zones are formed, the produced temperature in the predefined portion of the solid 1 is thereby preferably so high that the material forming the predefined portion is subject tomodifications 9 in the form of a predetermined material conversion. The number and arrangement of themodifications 9 can thereby be adjusted and is preferably predefined. After cutting off thesolid portion 12, LASER radiation from the LASER source is again applied to the remaining solid 1, wherein the LASER radiation controls the temperature of a predefined portion of the remaining solid 1 inside the remaining solid 1 in a defined manner such that adetachment zone 2 is formed, and the temperature created in the predefined portion of the remaining solid 1, in turn, is so high that the material, which forms the predefined portion, is subjected to a predetermined material conversion.Solid portions 12 of the same, similar or different thickness, e.g., in particularsolid layers 12, in particular wafers, can thus be cut off from a solid 1. The solid 1 preferably has such a length that a plurality, in particular more than 2 or more than 5 or more than 10 or more than 20 or more than 50 or more than 100 or more than 150 or more than 200solid layers 12 comprising a thickness of less than 1000 μm, in particular of less than 800 μm or of less than 500 μm or of less than 300 μm or of less than 200 μm or of less than 150 μm or of less than 110 μm or of less than 75 μm or of less than 50 μm, can be cut off therefrom. A machining of the newly exposedsurface solid layer 12. -
FIGS. 9a-9f show schematic illustrations of different process situations, as they can occur according to the method according to the invention for producingsolid layers 12. -
FIG. 9a shows the provision of the solid 1, in particular of an ingot. - According to
FIG. 9b , the provided solid 1 is arranged on acooling device 3. Thecooing device 3 is preferably a cooling chuck. Particularly preferably, the solid 1 is coupled or adhered, respectively, or welded or screwed or clamped to a tool carrier (chuck), wherein the tool carrier preferably comprises a cooling functionality and thus preferably becomes thecooling device 3. The tool carrier preferably consists of an alloy comprising a composition of 45%-60%, in particular 54% of iron, 20%-40%, in particular 29% of nickel and 10%-30%, in particular 17% of cobalt. The percentages hereby refer to the portion of the total mass. An example for apreferred cooling device 3 is shown inFIG. 11 . The solid 1 and thecooing device 3 preferably have the same or a similar thermal expansion, respectively. Every thermal expansion in response to a temperature increase of 10° C. in a temperature range of between −200° C. and 200° C. is hereby preferably understood as similar thermal expansion, in the case of which the difference of the thermal expansions of the solid 1 and of thecooling device 3 is less than 50%, in particular less than 25% or less than 10% of the thermal expansion of the object (cooling device of ingot), which expands most. The thermal expansion of the solid 1 is preferably less than 10 ppm/K, in particular less than 8 ppm/K or less than 5 ppm/K, such as, e.g., less than 4 ppm/K or substantially 4 ppm/K or exactly 4 ppm/K. - The solid 1 is preferably fixed to the
cooling device 3, in particular adhered, in longitudinal direction with itsunderside 7, which is preferably located in longitudinal direction opposite to thesurface 5. To generate themodifications 9, the laser beams are thus introduced into the solid 1 via thesurface 5, which is part of thesolid layer 12 to be cut off, in the direction of thecooling device 3. -
FIG. 9c shows the generation of themodifications 9 by means of the laser beams in a schematic manner. Thecooling device 3 hereby effects that the energy or heat, respectively, introduced into the solid 1 by means of the laser beams, is at least partially and preferably predominantly discharged from the solid 1. -
FIG. 9d shows a schematic sectional illustration of the solid 1 after the generation of themodifications 9. According to this example, 4 blocks ofmodifications 9 can be seen, which lead to the 4crack portions blocks comprising modifications 9,reference numerals modifications 9, or zones, in whichfewer modifications 9 are generated than in the zones, in which the blocks ofmodifications 9 are generated. -
FIG. 9e shows a state, according to which areceiving layer 140, in particular having a polymer material, is arranged or generated on thesurface 5, via which the laser beams have penetrated into the solid 1. Thereceiving layer 140 has preferably been created as film and has been adhered to thesurface 5 after its creation. It is also possible, however, to embody thereceiving layer 140 by applying a liquid polymer to thesurface 5 and by subsequent solidification. -
FIG. 9f shows a temperature control of thereceiving layer 140 in a schematic manner. The temperature of thereceiving layer 140 is preferably controlled, in particular cooled, to a temperature below the ambient temperature, in particular to a temperature of less than 20° C., or of less than 1° C. or of less than 0° C. or of less than −10° C. or of less than −50° C. or of less than −100° C. Wherein the material of thereceiving layer 140 is subjected to a glass transition as a result of the cool-down. The temperature of thereceiving layer 140 is preferably controlled by means of liquid nitrogen. Due to the temperature control, in particular due to the glass transition, thereceiving layer 140 contracts, whereby mechanical stresses are created in the solid 1. Due to the mechanical stresses, a crack, which connects thecrack portions solid portion 12 is cut off from the solid 1, is triggered. -
FIG. 10a shows an illustration after the temperature control of thereceiving layer 140 shown inFIG. 9f . Thesolid portion 12 is cut off from the solid 1 by means of thereceiving layer 140, which is still arranged thereon. -
FIG. 10b shows a new step of introducingmodifications 9 into the remaining solid 1, which is reduced in its length by at least the already cut-offsolid layer 12. -
FIG. 10c shows a further preferred design in a schematic manner. Thecooling device 3 is hereby coupled to the solid 1 on the one hand and is coupled to adisplacement device 30 on the other hand, in particular an X/Y displacement device or a rotary table. Thedisplacement device 30 effects a movement of the solid 1, whereby the latter can be moved in a defined manner with respect to the surrounding area and a laser optics, in particular a scanner. -
FIG. 10d shows a further detailed schematic illustration ofFIG. 10c . The round arrow inside thedisplacement device 30 identifies that the latter can be rotated. Provision is further made between the solid 1 and thecooling device 3 for a coupling layer, in particular an adhesive layer. Thecoupling layer 30 is hereby preferably embodied in such a way that it withstands a plurality of processing cylinders, in particular more than 200 or more than 300 or more than 500 processing cycles, at high mechanical and thermal stress. It can further be gathered from this illustration that thelaser beam source 401 preferably guides laser beams along a firstlaser beam conductor 402 to anoptics 40, from where the laser beams reach a scanner by means of a furtherlaser beam conductor 403. In the alternative, however, it is also conceivable hereby that at least thelaser beam source 401 and thescanner 400 are provided. -
FIG. 11 shows thecooling device 3. Thecooling device 3 preferably has a conducting-guiding structure, which is preferably formed by means of a tool carrier, in particular a chuck. The conducting-guiding structure preferably has a round basic shape. This is advantageous, because an imbalance can be avoided more easily with regard to spinning processes. The round basic shape is preferably further provided with flattened portions 95-98. These flattened portions are advantageous, because they allow or facilitate, respectively a coarse orientation and/or coffering. - The
cooling device 3, in particular the conducting-guiding structure of thecooling device 3, preferably has a good thermal conductivity. Thecooling device 3 preferably further has anodized aluminum, whereby abrasion particles are reduced or prevented, respectively. This is advantageous, because the clean room compatibility is increased through this. The chuck is preferably further compatible for the detaching process. - Provision is preferably further made for at least two aligning elements 65-68. The aligning elements 65-68 are preferably embodied as alignment holes or slits or pins. The aligning elements 65-68 preferably form actuators for the non-positive and/or positive rotation transfer. The aligning elements 65-68 preferably have steel or ceramic inserts, whereby a high wear resistance is attained. The aligning elements 65-68 preferably serve the purpose of coupling the
cooling device 3 to thedisplacement device 30. - Provision can further be made for aligning pins, they can be embodied as holding-down devices, e.g., whereby e.g. a force and/or positive connection to the conducting-guiding structure can be created.
- Provision is preferably furthermore made for a notch, groove or marking 76 on the
cooling device 3. This feature is advantageous, because the solid orientation, in particular ingot orientation, can be seen through this. The knowledge about the orientation of the solid, in particular of the ingot, can be used in order to be able to adapt themodifications 9, which are generated by means of the laser beams, to the crystallographic orientation. -
Reference numeral 75 identifies an optional data carrier element and/or data transfer element and/or data capturing element in a purely exemplary manner. The element identified withreference numeral 75 is preferably embodied as bar code and/or RFID element and/or SAW sensor. It in particular allows an integration into a manufacturing execution system (MES). - Cooling ducts for guiding a cooling fluid are preferably further provided or embodied, respectively on or in the conducting-guiding structure. The cooling duct or the
cooling ducts 78 can serve the purpose of controlling the temperature of the solid 1, of thecooling device 3 and/or of a machine holder, in particular thedisplacement device 30. Cooling fluid, in particular a liquid, can be supplied into the coolingduct 78 via aninlet 77, and can be removed via anoutlet 79. The boundary surface or the coupling layer, respectively, between solid 1 andcooling device 3 preferably has a high thermal conductivity, in particular according to the thermal conductivity of the solid 1 or of thecooling device 3. In addition or in the alternative, thecooling device 3 can be cooled via the air interface. In the case of high speeds or displacement speeds, respectively, of thedisplacement device 30, the air layer, which forms around thecooling device 3, is very thin, whereby heat can be discharged very well. - An active temperature control is preferably furthermore integrated into the MES. In addition or in the alterative, a process is monitored for different substrate sizes and thicknesses.
- A sealing of the fluid ducts in the case of a fixed storage preferably takes place by means of pressing and, in the case of rotation, by means of a central annular seal, e.g.
-
Reference numeral 69 identifies an optional sensor device, which is preferably embodied as temperature sensor. Preferably, the sensor device is an SAW temperature sensor. -
FIG. 12 shows theoptics modifications 9. The method according to the invention thus preferably also comprises the step of providing anoptics optics 608 preferably has at least two deflectingelements light beam portions laser beam source 401. The method according to the invention further preferably comprises the step of deflecting at least twolight beam portions light beam 606 by means of the deflectingelements light beam portions light beam portions focus 620 inside the solid 1 and thephysical modification 9, in particular in the form of a grid defect, is generated by means of thelight beam portions focus 620, or the step of generating and emitting at least twolight beams 606 by means of the laser beam source orradiation source arrangement 401, respectively. The method according to the invention preferably further comprises the step of deflecting the light beams 606 by means of the deflectingelements light beams 606, which are different from one another, meet in afocus 620 inside the solid 1 and thephysical modification 9, in particular in the form of a grid defect, is generated by means of the light beams (6), which meet in thefocus 620. - It is additionally conceivable that at least two
light beam portions light beam 606, in particular the light beam portions of a plurality of emitted light beams, or the plurality of emittedlight beams 606 are deflected by means of the deflectingelements light beam portions light beam portions focus 620 inside the solid 1, and thephysical modification 9, in particular in the form of a grid defect, is generated by means of thelight beam portions light beams 606, which meet in thefocus 620. - According to the method according to the invention, at least two
light beams 606 and preferably alllight beams 606 can be split intolight beam portions surface portions light beams 606, which are created synchronously, wherein thelight beam portions 616, 186 of a respective light beam are deflected by means of deflectingelements - The
optics 608 preferably has at least one light beam splitting means 633, in particular a half mirror or beam splitter, and at least onelight beam 606 is split into at least twolight beam portions light beam 606 is preferably split into at least twolight beam portions light beam portion 616 is deflected by means of at least two deflectingelements light beam portion 618 on the inside of the solid 1 in order to form afocus 620 for generating thephysical modification 9. Particularly preferably, a plurality ofphysical modifications 9 is generated, wherein thephysical modifications 9 preferably form or describe, respectively, a plane and/or a contour and/or a silhouette and/or the outer shape of a body. - The at least one
light beam 606 emitted by thelaser beam source 401 preferably consists of coherent light and the light waves of thelight beam portions focus 620, preferably have the same phase and the same frequency. - Particularly preferably, at least one
light beam portion light beam 606 is deflected and focused by means of a deflectingelement - The at least one
light beam portion light beam 606 further preferably penetrates a deflectingelement - The
laser beam source 401 preferably generates at least one or exactly two light beams, wherein the light beams 606 are generated as a function of the band gap of the material of the solid 1 with different colors in such a way that themodification 9 is generated by means of a two-photon process. - A first laser field is preferably formed by means of a
first light beam 606, wherein thefirst light beam 606 has photons comprising a first energy, and a second laser field is preferably formed by means of a secondlight beam 606, wherein thesecond laser beam 606 has photons comprising a second energy, wherein the first laser field is weaker than the second laser field and the first energy is larger than the second energy. -
FIG. 13 shows the modification generation by means of two laser beams or two laser beam portions in a schematic illustration. Themodifications 9 hereby preferably have a vertical expansion of less than 50 μm and preferably of less than 30 μm and particularly preferably of less than 20 μm. - The
focus 620 is preferably spaced apart from apenetration surface 626 of the solid 1 by less than 1000 μm and preferably less than 500 μm and particularly preferably less than 200 μm, wherein at least individuallight beam portions penetration surface 626 in order to generate thephysical modification 9. - The
focus 620 is preferably generated in an overlapping portion of at least two intersectinglight beam portions light beam portions light beam portions light beams 606. - What is thus described is a method for creating a detachment zone in a solid in order to detach a solid portion, especially a solid layer, from the solid, wherein the solid portion, which is to be detached, is thinner than the solid, from which the solid portion has been removed. The method according to the invention thereby preferably comprises at least the steps of: providing a solid, which is to be processed, wherein the solid is made of a chemical compound; providing a LASER light source; applying LASER radiation from the LASER light source to the solid, wherein the laser beams penetrate into the solid via a surface of the solid portion, which is to be cut off, wherein the LASER radiation controls the temperature of a predefined portion of the solid inside the solid in a defined manner such that a detachment zone or a plurality of partial detachment zones is formed, characterized in that the temperature produced by the laser beams in a predefined portion of the solid is so high that the material forming the predefined portion is subject to modifications in the form of a predetermined conversion of material.
- What is further described is a method for creating a detachment zone in a solid in order to detach a solid portion from the solid, at least comprising the steps of: providing a solid, which is to be processed, wherein the solid is made of a chemical compound; providing a LASER light source, applying LASER radiation from the LASER light source to the solid, wherein the LASER radiation controls the temperature of a predefined portion of the solid inside the solid in a defined manner such that a detachment zone is formed, wherein the temperature produced in the predefined portion of the solid is so high that the material forming the predefined portion is subject to a predetermined conversion of material.
- 1 solid
- 2 detachment zone
- 4 laser beam
- 5 polished surface
- 6 laser beam in the solid
- 7 underside of the solid
- 8 focus
- 9 modification
- 10 first solid
- 11 solid layer
- 12 second solid
- 17 reference length
- 18 main surface
- 25 first crack portion
- 27 second crack portion
- 28 third crack portion
- 29 fourth crack portion
- 30 rotary table
- 31 crack between outer edge and first modification block
- 32 crack between two Modification blocks
- 33 crack between outer edge and first modification block and further modification block or outer edge
- 34 crack between modification block and outer edge
- 40 optics
- 41 first zone without modification block
- 42 second zone without modification block
- 43 third zone without modification block
- 44 fourth zone without modification block
- 45 fifth zone without modification block
- 51 unchanged material
- 52 unchanged material
- 53 Raman spectrum
- 54 intensity in %
- 56 wavelength in cm−1
- 61 graph relating to unchanged material portion
- 62 graph relating to unchanged material portion
- 65 first aligning element
- 66 second aligning element
- 67 third aligning element
- 68 fourth alignment element
- 69 sensor means
- 75 data carrier element and/o data transfer element
- 76 groove
- 77 fluid inlet
- 78 fluid line
- 79 fluid outlet
- 80 conducting-guiding structure
- 71 first end of a crack portion
- 72 second end of a crack portion
- 91 first block of modifications
- 92 second block of modifications
- 112 second solid layer
- 113 third solid layer
- 140 receiving layer
- 150 temperature control fluid
- 161 deforming direction of the receiving layer
- 300 coupling layer
- 400 scanner
- 401 laser beam source
- 402 laser beam conductor
- 403 further laser beam conductor
- 501 exposed surface of the first solid layer
- 502 laser penetration surface of the second solid layer
- 503 exposed surface of the second solid layer
- 504 laser penetration surface of the third solid layer
- 505 exposed surface of the third solid layer
- 606 light beam
- 608 optics
- 610 first deflecting element
- 612 second deflecting element
- 613 third deflecting element
- 616 first light beam portion
- 618 second light beam portion
- 620 focus
- 622 first surface portion
- 624 second surface portion
- 630 light beam portion
- 632 light beam portion
- 901 first field without modifications
- 902 second field without modifications
- 903 third field without modifications
Claims (15)
1.-15. (canceled)
16. A method for cutting off at least one solid portion from a solid, in particular a wafer, comprising:
providing a solid, which is to be processed, wherein the solid is made of a chemical compound;
providing a LASER light source;
applying LASER radiation from the LASER light source to the solid,
wherein the laser beams penetrate into the solid via a surface of the solid portion, which his to be cut off,
wherein the laser radiation controls the temperature of a predefined portion of the solid inside the solid in a defined manner such that a detachment zone or a plurality of partial detachment zones is formed,
wherein the temperature produced by the laser beams in the predefined portion of the solid is so high that the material forming the predefined portion is subject to modifications in the form of a predetermined conversion of material.
arranging a receiving layer on the treated solid,
thermal application of the receiving layer for, in particular mechanically, generating crack expansion stresses in the solid, wherein a crack expands in the solid along the detachment zone due to the crack expansion stresses.
17. The method according to claim 16 further comprising the solid being of a chemical compound, such as silicon carbide, wherein the chemical compound preferably has a material or a plurality of materials chosen from the third, fourth and/or fifth main group of the periodic table of elements and/or from the 12 th subgroup of the periodic table of elements.
18. The method according to claim 16 further comprising:
the solid being connected to a cooling device via a solid surface, wherein the solid surface, which is connected to the cooling device, is embodied parallel or substantially parallel to the surface, via which the laser beams penetrate into the solid, and
the cooling device being operated as a function of the laser application, in particular as a function of the temperature control of the solid, which results from the laser application.
19. The method according to claim 18 further comprising the cooling device having at least one sensor device for capturing the temperature of the solid and, as a function of a predefined temperature course, effects a cool-down of the solid.
20. The method according to claim 18 further comprising the cooling device being coupled to a rotating means and the cooling device comprising the solid arranged thereon is rotated by means of the rotating means during the generation of the modifications, in particular with more than 100 revolutions per minute or with more than 200 revolutions per minute or with more than 500 revolutions.
21. The method according to claim 16 further comprising every material conversion effected by means of the LASER radiation represents a modification of the material of the solid and wherein:
the solid is rotated with respect to the LASER light source and the number of the modifications per cm2 of the solid surface per rotation, through which the LASER radiation penetrates into the solid in order to generate the modifications, is below a predefined maximum number, wherein the maximum number of the modifications per cm2 and per rotation is preferably determined as a function of the solid material and of the energy density of the LASER radiation, and/or
the modifications are generated with different patterns, in particular distances between the individual newly generated modifications and/or with changed energy input, in particular reduced energy input, in response to consecutive rotations of the solid with respect to the LASER light source, and/or
the LASER light source is embodied as scanner and the generation of the modifications takes place as a function of the laser scanning direction, the laser polarization direction and the crystal orientation, and/or
the distance between the centers of two modifications, which are generated consecutively in modification generating direction or in circumferential direction of the solid is less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm, and/or
the outer limitations of modifications, which are generated consecutively in modification generating direction or in circumferential direction of the solid, are spaced apart from one another by less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm.
22. The method according to claim 16 further comprising the number of the generated modifications per cm2 being different in at least two different zones of the solid and wherein:
a first block of modifications is generated in a first zone, wherein the individual modifications per line are preferably generated spaced apart from one another by less than 10 μm, in particular less than 5 μm or less than 3 μm or less than 1 μm or less than 0.5 μm,
the individual lines of the first block are generated spaced apart from one another by less than 20 μm, in particular less than 15 μm or less than 10 μm or less than 5 μm or less than 1 μm,
a first partial detachment zone is formed by the first block of modifications,
a second block of modification lines is generated in a second zone, wherein the individual modifications per line are preferably generated spaced apart from one another by less than 10 μm, in particular less than 5 μm or less than 3 μm or less than 1 μm, or less than 0.5 μm,
the individual lines of the second block are generated spaced apart from one another by less than 20 μm, in particular less than 15 μm or less than 10 μm or less than 5 μm or less than 1 μm, wherein a second partial detachment zone is formed by the second block of modifications,
the first zone and the second zone are spaced apart from one another by a third zone, wherein no modifications or essentially no modifications or fewer modification as compared to the first or second zone per cm2 are generated in the third zone by means of laser beams, and the first zone is spaced apart from the second zone by more than 20 μm, in particular more than 50 μm or more than 100 μm or more than 150 μm or more than 200 μm.
23. The method according to claim 22 further comprising the modifications at least in the first block and in the second block being generated in pulse intervals of between 0.01 μm and 10 μm and/or line spacings of between 0.01 μm and 20 μm are provided, and/or a pulse repetition frequency of between 16 kHz and 20 MHz is provided.
24. The method according to claim 16 further comprising an optics, by means of which the laser beams are guided from a laser beam source to the solid, being adapted as a function of the location, at which a modification is generated, from which at least one change of the numerical aperture is effected, wherein the numerical aperture at a location in the edge zone of the solid is smaller than at a different location of the solid, which is located closer to the center of the solid.
25. The method according to claim 16 further comprising the LASER radiation generating modifications, in particular crystal lattice defects, in the solid, and wherein:
the solid is rotated with respect to the LASER light source, and
the number of the modifications per cm2 of the solid surface per rotation, through which the LASER radiation penetrates into the solid in order to generate the modifications, is below a predefined maximum number, wherein the maximum number of the modifications per cm2 and per rotation is preferably determined as a function of the solid material and of the energy density of the LASER radiation, and/or
the modifications are generated with different patterns, in particular distances between the individual newly generated modifications and/or with changed energy input, in particular reduced energy input, in response to consecutive rotations of the solid with respect to the LASER light source, and/or
the LASER light source is embodied as scanner and the generation of the modifications takes place as a function of the laser scanning direction, the laser polarization direction and the crystal orientation, and/or
the distance between the centers of two modifications, which are generated consecutively in modification generating direction or in circumferential direction of the solid is less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm, and/or
the outer limitations of modifications, which are generated consecutively in modification generating direction or in circumferential direction of the solid, are spaced apart from one another by less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm.
26. The method according to claim 1 further comprising every material conversion, which is effected by means of the LASER radiation, represents a modification of the material of the solid, and wherein:
the solid is moved in a translational manner in XY direction with respect to the LASER light source, and
the number of modifications per cm2 of the solid surface, through which the LASER radiation penetrates into the solid in order to generate the modifications, wherein the maximum number of the modifications per cm2 and according to the translational movement in XY direction is preferably determined as a function of the solid material and of the energy density of the LASER radiation, and/or
the modifications are generated with different patterns, in particular distances between the individual newly generated modifications, and/or with changed energy input, in particular reduced energy input, according to the translational movement in XY direction of the solid with respect to the LASER light source, and/or
the LASER light source is embodied as scanner, and the generation of the modifications takes place as a function of the laser scanning direction, the laser polarization direction and the crystal orientation, and/or
the distance between the displacements of two modifications, which are generated consecutively in modification generating direction is less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm, and/or
the outer limitations of modifications, which are generated consecutively in modification generating direction, are spaced apart from one another by less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm.
27. The method according to claim 16 further comprising the LASER radiation generating modifications, in particular crystal lattice effects, in the solid, wherein:
the solid is moved in a translational manner with respect to the LASER light source, and
the number of the modifications per cm2 of the solid surface, through which the LASER radiation penetrates into the solid in order to generate the modifications, wherein the maximum number of the modifications per cm2 and according to the translational movement in XY direction is preferably determined as a function of the solid material and of the energy density of the LASER radiation, and/or
the modifications are generated with different patterns, in particular distances between the individual newly generated modifications, and/or with changed energy input, in particular reduced energy input, according to the translational movement in XY direction of the solid with respect to the LASER light source, and/or
the LASER light source is embodied as scanner, and the generation of the modifications takes place as a function of the laser scanning direction, the laser polarization direction and the crystal orientation, and/or
the distance between the displacements of two modifications, which are generated consecutively in modification generating direction is less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm, and/or
the outer limitations of modifications, which are generated consecutively in modification generating direction, are spaced apart from one another by less than 10000 nm, in particular less than 1000 nm, in particular less than 100 nm.
28. The method according to claim 16 further comprising, after cutting off the solid portion, LASER radiation from the LASER source is again applied to the remaining solid, wherein:
the LASER radiation controls the temperature of a predefined portion of the remaining solid inside the remaining solid in a defined manner such that a detachment zone is formed, and
the temperature created in the predefined portion of the solid is so high that the material, which forms the predefined portion, is subjected to a predetermined material conversion.
29. The method according to claim 16 further comprising the thermal application of the receiving layer including a cool-down of the receiving layer to a temperature of below 20° C., in particular below 10° C. or below 0° C. or below −10° C. or below −100° C. or below −125° C. to or below the glass transition temperature of the material of the receiving layer.