US20170283894A1 - Ferritic stainless steel having excellent ductility and method for manufacturing same - Google Patents

Ferritic stainless steel having excellent ductility and method for manufacturing same Download PDF

Info

Publication number
US20170283894A1
US20170283894A1 US15/529,263 US201515529263A US2017283894A1 US 20170283894 A1 US20170283894 A1 US 20170283894A1 US 201515529263 A US201515529263 A US 201515529263A US 2017283894 A1 US2017283894 A1 US 2017283894A1
Authority
US
United States
Prior art keywords
ferritic stainless
stainless steel
less
precipitate
independent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/529,263
Other languages
English (en)
Inventor
Soo-ho Park
Jae-hong Shim
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Posco Holdings Inc
Original Assignee
Posco Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Posco Co Ltd filed Critical Posco Co Ltd
Assigned to POSCO reassignment POSCO ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SHIM, JAE-HONG, PARK, SOO-HO
Publication of US20170283894A1 publication Critical patent/US20170283894A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/0081—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for slabs; for billets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
    • B22D11/001—Continuous casting of metals, i.e. casting in indefinite lengths of specific alloys
    • B22D11/002—Stainless steels
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D27/00—Treating the metal in the mould while it is molten or ductile ; Pressure or vacuum casting
    • B22D27/04—Influencing the temperature of the metal, e.g. by heating or cooling the mould
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/021—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular fabrication or treatment of ingot or slab
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite

Definitions

  • the present disclosure relates to ferritic stainless steel having a high degree of ductility and a method for manufacturing the ferritic stainless steel, and more particularly, to a new kind of ferritic stainless steel provided by improving ferritic stainless steel having poor ductility compared to austenitic stainless steel for use in applications requiring high ductility, and a method for manufacturing the ferritic stainless steel.
  • Ferritic stainless steels have a high degree of corrosion resistance even though the contents of expensive alloying elements in the ferritic stainless steels are low. That is, ferritic stainless steels are more competitive in price than austenitic stainless steels. Ferritic stainless steels are used in applications such as construction materials, transportation vehicles, or kitchen utensils. However, ferrite stainless steels have poor ductility and thus it is difficult to use ferritic stainless steels instead of austenitic stainless steels in many applications. Therefore, many efforts have been made to improve the ductility of ferritic stainless steels and thus to increase the applications of ferritic stainless steels.
  • An aspect of the present disclosure may provide ferritic stainless steel having a high degree of ductility and a method of manufacturing the ferritic stainless steel.
  • ferritic stainless steel may include, by wt %, C: 0.005% to 0.1%, Si: 0.01% to 2.0%, Mn: 0.01% to 1.5%, P: 0.05% or less, S: 0.005% or less, Cr: 10% to 30%, Ti: 0.005% to 0.5%, Al: 0.01% to 0.15%, N: 0.005% to 0.03%, and the balance of Fe and inevitable impurities, wherein the ferritic stainless steel may include 3.5 ⁇ 10 6 or fewer particles of an independent Ti(CN) precipitate per square millimeter (mm 2 ) of ferrite matrix.
  • ferritic stainless steel may include, by wt %, C: 0.005% to 0.1%, Si: 0.01% to 2.0%, Mn: 0.01% to 1.5%, P: 0.05% or less, S: 0.005% or less, Cr: 10% to 30%, Ti: 0.005% to 0.5%, Al: 0.01% to 0.15%, N: 0.005% to 0.03%, and the balance of Fe and inevitable impurities, wherein the ferritic stainless steel may include an independent Ti(CN) precipitate and a dependent Ti(CN) precipitate formed using a TiN inclusion as precipitation nuclei, and the ferritic stainless steel may have a P within a range of 60% or less, the P being defined by Formula 1 below:
  • N S refers to the number of independent Ti(CN) precipitate particles per unit area (mm 2 )
  • N C refers to the number of dependent Ti(CN) precipitate particles per unit area (mm 2 ).
  • the independent Ti(CN) precipitate may have a particle diameter of 0.01 ⁇ m or greater.
  • the independent Ti(CN) precipitate may have an average particle diameter of 0.15 ⁇ m or less.
  • the TiN inclusion may have an average particle diameter of 2 ⁇ m or greater.
  • the ferritic stainless steel may have an elongation of 34% or greater.
  • a method for manufacturing ferritic stainless steel may include casting molten steel as a slab, the molten steel including, by wt %, C: 0.005% to 0.1%, Si: 0.01% to 2.0%, Mn: 0.01% to 1.5%, P: 0.05% or less, S: 0.005% or less, Cr: 10% to 30%, Ti: 0.005% to 0.5%, Al: 0.01% to 0.15%, N: 0.005% to 0.03%, and the balance of Fe and inevitable impurities, wherein in the casting of the molten steel, the slab may be cooled at an average cooling rate of 5° C./sec or less (excluding 0° C./sec) within a temperature range of 1100° C. to 1200° C. based on a surface temperature of the slab.
  • the slab may be cooled at an average cooling rate of 5° C./sec or less (excluding 0° C./sec) within a temperature range of 1000° C. to 1250° C. based on the surface temperature of the slab.
  • the method may further include: obtaining a hot-rolled sheet by performing a hot rolling process on the slab; and performing a hot band annealing process on the hot-rolled sheet within a temperature range of 450° C. to 1080° C. for 1 minute to 60 minutes.
  • the ferritic stainless steel of the present disclosure has a high degree of ductility.
  • FIG. 1 is a scanning electron microscope (SEM) image illustrating the microstructure of a hot-rolled sheet of Inventive Example 1.
  • FIG. 2 is a high magnification SEM image illustrating region A in FIG. 1 .
  • the inventors have reviewed various factors to improve the ductility of ferritic stainless steel and have acquired the following knowledge.
  • Ti titanium
  • Ti(CN) a large amount of Ti(CN) inevitably precipitates in the ferrite matrix of Ti-containing ferritic stainless steel, and the Ti(CN) precipitate becomes the main cause of ductility deterioration.
  • the Ti(CN) precipitate includes a Ti(CN) precipitate independently formed in the ferrite matrix (hereinafter referred to as an “independent Ti(CN) precipitate”) and a Ti(CN) precipitate formed with the help of particles of a TiN inclusion that are crystallized during a steel making process and function as precipitation nuclei (hereinafter referred to as a “dependent Ti(CN) precipitate”).
  • the dependent Ti(CN) precipitate does not have a significant effect on ductility deterioration when compared to the independent Ti(CN) precipitate.
  • ferritic stainless steel having a high degree of ductility will be described in detail according to an aspect of the present disclosure.
  • carbon (C) markedly affects the strength of steel
  • the content of carbon (C) in steel is excessively high, the strength of the steel may increase to an excessive degree, and the ductility of the steel may decrease. Therefore, the content of carbon (C) is limited to 0.1% or less.
  • the lower limit of the content of carbon (C) may be limited to 0.005%.
  • Silicon (Si) is an element added to molten steel during a steel making process to remove oxygen and stabilize ferrite. In the present disclosure, silicon (Si) is added in an amount of 0.01% or greater. However, if the content of silicon (Si) in steel is excessively high, the ductility of the steel may decrease due to hardening. Therefore, the content of silicon (Si) is limited to 2.0% or less.
  • Manganese (Mn) is an element effective in improving the corrosion resistance of steel.
  • manganese (Mn) is added in an amount of 0.01% or greater, more preferably, 0.5% or greater.
  • the content of manganese (Mn) in steel is excessively high, the generation of Mn-containing fumes markedly increases during a welding process, and thus the weldability of the steel decreases.
  • an MnS precipitate may be excessively formed to result in a decrease in the ductility of the steel. Therefore, the content of manganese (Mn) is limited to 1.5% or less, more preferably 1.0% or less.
  • Phosphorus (P) is an impurity inevitably included in steel, causing grain boundary corrosion during a pickling process and deteriorating the hot formability of the steel. Therefore, the content of phosphorus (P) is adjusted as low as possible. In the present disclosure, the upper limit of the content of phosphorus (P) is set to 0.05%.
  • S Sulfur
  • S an impurity inevitably included in steel, segregates along grain boundaries of the steel and deteriorates the hot formability of the steel. Therefore, the content of sulfur (S) is adjusted as low as possible.
  • the upper limit of the content of sulfur (S) is set to be 0.005%.
  • Chromium (Cr) is effective in increasing the corrosion resistance of steel.
  • chromium (Cr) is added in an amount of 10% or greater.
  • the content of chromium (Cr) is limited to 30% or less.
  • Titanium (Ti) fixes carbon (C) and nitrogen (N), thereby decreasing the amounts of carbon (C) and nitrogen (N) dissolved in steel.
  • titanium (Ti) is effective in improving the corrosion resistance of steel.
  • titanium (Ti) is added in an amount of 0.05% or greater, more preferably 0.1% or greater.
  • the content of titanium (Ti) is limited to 0.50% or less, more preferably 0.30% or less.
  • Aluminum (Al) is a powerful deoxidizer used to decrease the oxygen content of molten steel.
  • aluminum (Al) is added in an amount of 0.01% or greater.
  • the content of aluminum (Al) is limited to 0.15% or less, more preferably 0.1% or less.
  • Nitrogen (N) is an element facilitating recrystallization by precipitating austenite during a hot rolling process.
  • nitrogen (N) is added in an amount of 0.005% or greater.
  • the content of nitrogen (N) in steel is excessively high, the ductility of the steel decreases. Therefore, the content of nitrogen (N) is limited to 0.03% or less.
  • the ferritic stainless steel of the present disclosure may include 3.5 ⁇ 10 6 or fewer (excluding zero) independent Ti(CN) precipitate particles per square millimeter (mm 2 ) of ferrite matrix.
  • the Ti(CN) precipitate includes an independent Ti(CN) precipitate and a dependent Ti(CN) precipitate formed using TiN inclusion particles as precipitation nuclei.
  • the dependent Ti(CN) precipitate does not have a significant effect on ductility deterioration when compared to the independent Ti(CN) precipitate. Therefore, only the number of independent Ti(CN) precipitate particles is controlled in the present disclosure. If the number of independent Ti(CN) precipitate particles is outside the above-mentioned range, it may be difficult to obtain a desired degree of ductility.
  • a method of reducing the number of independent Ti(CN) precipitate particles is to increase the amount of Ti(CN) precipitating using TiN inclusion particles as precipitation nuclei.
  • a desired degree of ductility may be obtained by adjusting P defined by Formula 1 below within the range of 60% or less.
  • N S refers to the number of independent Ti(CN) precipitate particles per unit area (mm 2 )
  • N C refers to the number of dependent Ti(CN) precipitate particles per unit area (mm 2 ).
  • the independent Ti(CN) precipitate being the subject of control may be limited to having a particle diameter of 0.01 ⁇ m or greater. Since there is a limit to analyzing and quantifying independent Ti(CN) precipitate having a particle diameter of less than 0.01 ⁇ m, special consideration may not be given thereto.
  • the upper limit of the particle diameter of the independent Ti(CN) precipitate may not be specifically set. However, since it is difficult to form an independent Ti(CN) precipitate having a particle diameter of 2 ⁇ m or greater, the upper limit of the particle diameter of the independent Ti(CN) precipitate may be set to be 2 ⁇ m.
  • the independent Ti(CN) precipitate may have an average particle diameter of 0.15 ⁇ m or less. If the average particle diameter of the independent Ti(CN) precipitate is greater than 0.15 ⁇ m, surface defects may be formed even though the number of independent Ti(CN) precipitate particles is small.
  • the term “average particle diameter” refers to the average of equivalent circular diameters of particles measured by observing a cross-section of steel.
  • the average particle diameter of a TiN inclusion be within the range of 2 ⁇ m or greater.
  • the reason for this is that a relatively coarse TiN inclusion having an average particle diameter of 2 ⁇ m or greater forms nucleus forming sites more efficiently, and thus facilitates the precipitation of Ti(CN).
  • the upper limit of the average particle diameter of the TiN inclusion is not limited. However, if the TiN inclusion is excessively coarse, the total surface area of the TiN inclusion may be excessively small, and thus it may be difficult to increase the number of dependent Ti(CN) precipitate particles. Therefore, the upper limit of the average particle diameter of the TiN inclusion may be set to be 20 ⁇ m.
  • the ferritic stainless steel of the present disclosure has a high degree of ductility. According to an exemplary embodiment of the present disclosure, the ferritic stainless steel may have an elongation of 34% or greater.
  • the ferritic stainless steel of the present disclosure may be manufactured by various methods without limit.
  • the ferritic stainless steel may be manufactured as follows.
  • the method for manufacturing ferritic stainless steel includes casting molten steel having the above-described composition as a slab.
  • One of the technical features of the method is to maximally restrict the formation of an independent Ti(CN) precipitate by facilitating the diffusion of titanium (Ti), carbon (C), and nitrogen (N), and thus inducing the formation of a dependent Ti(CN) precipitate with the help of TiN inclusion particles functioning as precipitation nuclei.
  • a slab produced by casting molten steel is subjected to a cooling process to improve productivity.
  • relatively fine TiN inclusion particles are formed in the slab, and Ti(CN) precipitates randomly in the slab, thereby markedly increasing the number of independent Ti(CN) precipitate particles.
  • relatively rapid cooling of the slab limits the diffusion of alloying elements in the slab, and sufficient nucleus forming energy facilitates the formation of nuclei of a TiN inclusion and a Ti(CN) precipitate simultaneously across the slab.
  • the slab is cooled within the temperature range of 1100° C. to 1200° C. based on the surface temperature of the slab at an average cooling rate of 5° C./sec or less (excluding 0° C./sec), preferably 3° C./sec or less (excluding 0° C./sec), more preferably 2° C./sec (excluding 0° C./sec). That is, the inventors have tried to precipitate as much Ti(CN) as possible using TiN inclusion particles as precipitation nuclei by properly controlling the average cooling rate of a slab within the temperature range of 1100° C. to 1200° C., and thus to decrease the number of independent Ti(CN) precipitate particles.
  • the inventors have found that if a slab is cooled under the conditions described above, the number of independent Ti(CN) precipitate particles is reduced to a target value or less. The reason for this may be that since slow cooling guarantees a sufficient time period for alloying elements to move, large amounts of Ti, C, and N diffuse toward TiN inclusion particles and precipitate in the form of Ti(CN) using the TiN inclusion particles as precipitation nuclei.
  • the average cooling rate of the slab may be controlled using any method or apparatus.
  • a heat insulating material may be disposed around a cast strand.
  • the method of controlling the average cooling rate of the slab is not limited.
  • the slab may be cooled slowly at a constant cooling rate within the above-mentioned temperature range, or the slab may be cooled at a relatively high cooling rate after the slab is constantly maintained at a particular temperature within the temperature range.
  • the temperature range within which the slab is slowly cooled may be widened to a range of 1000° C. to 1250° C. to induce the formation of a coarse TiN inclusion and enable the coarse TiN inclusion to function as nucleus forming sites more effectively for the precipitation of Ti(CN).
  • the method may further include: forming a hot-rolled sheet by performing a finish hot rolling process on the slab; and performing a hot band annealing process on the hot-rolled sheet.
  • Hot band annealing process perform within the range of 450° C. to 1080° C. for 60 minutes or less.
  • the hot band annealing process is performed to improve the ductility of the hot-rolled sheet. Owing to the hot band annealing process, the independent Ti(CN) precipitate may be dissolved again, and dissolved alloying elements may be diffused, thereby further decreasing the number of independent Ti(CN) precipitate particles. To this end, the hot band annealing process may be performed at a temperature of 450° C. or higher. However, if the temperature of the hot band annealing process is higher than 1080° C., or the duration of the band annealing process is longer than minutes, the dependent Ti(CN) precipitate may be dissolved again, and thus the above-mentioned effects may be decreased. The lower limit of the duration of the band annealing process is not limited. For example, it may be preferable that the band annealing process be performed for 1 minute or longer to obtain sufficient effects.
  • the annealed hot-rolled sheet may be subjected to a cold rolling process and a cold rolled sheet annealing process to produce a cold-rolled steel sheet.
  • Molten steels having the compositions shown in Table 1 were prepared and were cast at a constant speed under the conditions shown in Table 2 in order to produce slabs.
  • the slabs were subjected to a hot rolling process and a hot band annealing process to obtain hot-rolled sheets.
  • the slab cooling rate is an average cooling rate measured based on the surface temperature of a slab within the temperature range of 1100° C. to 1200° C.
  • the hot-rolled sheets were photographed using a transmission electron microscope (TEM), and the number and ratio (P) of independent Ti(CN) precipitate particles having a particle diameter of 0.01 ⁇ m or greater were measured using an image analyzer.
  • samples were taken from the hot-rolled sheets based on a direction making an angle of 90° with the rolling direction of the hot-rolled sheets according to JIS 13B, and the elongation of the samples was measured. Results of the measurements are shown in Table 3.
  • FIG. 1 is a scanning electron microscope (SEM) image illustrating the microstructure of a hot-rolled sheet of Inventive Example 1
  • FIG. 2 is a higher magnification SEM image illustrating region A in FIG. 1 .
  • a particle shown in the center of region A in FIG. 1 corresponds to a TiN inclusion particle crystallized during a steel making process.
  • FIG. 2 illustrating region A on an enlarged scale, a large amount of Ti(CN) has precipitated on the TiN inclusion particle functioning as a precipitation nucleus.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Steel (AREA)
  • Continuous Casting (AREA)
US15/529,263 2014-12-26 2015-04-30 Ferritic stainless steel having excellent ductility and method for manufacturing same Abandoned US20170283894A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
KR10-2014-0190545 2014-12-26
KR20140190545 2014-12-26
KR10-2015-0061378 2015-04-30
PCT/KR2015/004410 WO2016104883A1 (fr) 2014-12-26 2015-04-30 Matériau d'acier inoxydable ferritique présentant une excellente ductilité et son procédé de production
KR1020150061378A KR101553607B1 (ko) 2014-12-26 2015-04-30 연성이 우수한 페라이트계 스테인리스 강재 및 그 제조방법

Publications (1)

Publication Number Publication Date
US20170283894A1 true US20170283894A1 (en) 2017-10-05

Family

ID=54248455

Family Applications (1)

Application Number Title Priority Date Filing Date
US15/529,263 Abandoned US20170283894A1 (en) 2014-12-26 2015-04-30 Ferritic stainless steel having excellent ductility and method for manufacturing same

Country Status (7)

Country Link
US (1) US20170283894A1 (fr)
EP (1) EP3239335B1 (fr)
JP (1) JP6605032B2 (fr)
KR (1) KR101553607B1 (fr)
CN (1) CN107109598B (fr)
ES (1) ES2767505T3 (fr)
WO (1) WO2016104883A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20210371962A1 (en) * 2018-10-23 2021-12-02 Posco High-strength ferritic stainless steel for clamp and method for manufacturing same

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6022097B1 (ja) * 2016-03-30 2016-11-09 日新製鋼株式会社 Ｔｉ含有フェライト系ステンレス鋼板および製造方法
KR101835021B1 (ko) * 2016-09-28 2018-03-09 주식회사 포스코 카본 슬러지 흡착이 저감된 배기계 열교환기용 페라이트계 스테인리스강 및 이의 제조 방법
KR102020511B1 (ko) * 2017-12-14 2019-09-10 주식회사 포스코 충격 인성이 우수한 페라이트계 스테인리스강 및 그 제조방법
CN109648064B (zh) * 2019-01-25 2021-04-20 北京科技大学 一种超级奥氏体不锈钢凝固组织σ相变性的方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4889566A (en) * 1987-06-18 1989-12-26 Kawasaki Steel Corporation Method for producing cold rolled steel sheets having improved spot weldability
JP2000144342A (ja) * 1998-01-30 2000-05-26 Sumitomo Metal Ind Ltd 成形性に優れたフェライト系ステンレス鋼及びフェライト系ステンレス鋼鋳片
EP1514949A1 (fr) * 2002-06-17 2005-03-16 JFE Steel Corporation Plaque d'acier inoxydable ferritique avec ti et son procede de production

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3422871B2 (ja) * 1995-04-11 2003-06-30 新日本製鐵株式会社 溶接性に優れたフェライト系ステンレス鋼
JPH09287021A (ja) * 1996-04-19 1997-11-04 Nippon Steel Corp 加工性に優れた高純フェライト系ステンレス熱延鋼帯の製造方法
JP2005307234A (ja) * 2004-04-19 2005-11-04 Nisshin Steel Co Ltd 耐リジング性，表面性状に優れたフェライト系ステンレス鋼板及びその製造方法
JP5219689B2 (ja) * 2008-08-12 2013-06-26 新日鐵住金ステンレス株式会社 加工肌荒れの小さいフェライト系ステンレス鋼板およびその製造方法
JP5560578B2 (ja) * 2009-03-31 2014-07-30 Ｊｆｅスチール株式会社 加工性に優れたフェライト系ステンレス冷延鋼板及びその製造方法
JP5707671B2 (ja) * 2009-03-31 2015-04-30 Ｊｆｅスチール株式会社 加工性と製造性に優れたＮｂ添加フェライト系ステンレス鋼板及びその製造方法
CN102041452A (zh) * 2009-10-23 2011-05-04 宝山钢铁股份有限公司 一种中铬铁素体不锈钢及其制造方法
JP5307170B2 (ja) * 2011-02-25 2013-10-02 新日鐵住金ステンレス株式会社 加工肌荒れの少ない成形性に優れたフェライト系ステンレス鋼板の製造方法
WO2013085005A1 (fr) * 2011-12-09 2013-06-13 新日鐵住金ステンレス株式会社 Feuille d'acier inoxydable férritique laminée à chaud ayant une excellente résistance à la fissuration à froid, et procédé de fabrication s'y rapportant

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4889566A (en) * 1987-06-18 1989-12-26 Kawasaki Steel Corporation Method for producing cold rolled steel sheets having improved spot weldability
JP2000144342A (ja) * 1998-01-30 2000-05-26 Sumitomo Metal Ind Ltd 成形性に優れたフェライト系ステンレス鋼及びフェライト系ステンレス鋼鋳片
EP1514949A1 (fr) * 2002-06-17 2005-03-16 JFE Steel Corporation Plaque d'acier inoxydable ferritique avec ti et son procede de production

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20210371962A1 (en) * 2018-10-23 2021-12-02 Posco High-strength ferritic stainless steel for clamp and method for manufacturing same

Also Published As

Publication number Publication date
EP3239335A1 (fr) 2017-11-01
EP3239335A4 (fr) 2017-11-29
WO2016104883A1 (fr) 2016-06-30
ES2767505T3 (es) 2020-06-17
EP3239335B1 (fr) 2019-11-13
KR101553607B1 (ko) 2015-09-17
CN107109598A (zh) 2017-08-29
JP6605032B2 (ja) 2019-11-13
JP2018505308A (ja) 2018-02-22
WO2016104883A8 (fr) 2017-01-19
CN107109598B (zh) 2018-09-14

Similar Documents

Publication Publication Date Title
JP6844627B2 (ja) 鋼板及びその製造方法
US9410231B2 (en) Steel sheet and method of manufacturing steel sheet
JP6354268B2 (ja) 打抜き穴広げ性と低温靭性に優れた引張最大強度９８０ＭＰａ以上の高強度熱延鋼板及びその製造方法
US10501830B2 (en) High-strength cold-rolled steel sheet, high-strength hot-dip galvanized steel sheet, and high-strength hot-dip galvannealed steel sheet having excellent ductility, stretch-flangeability, and weldability
CN109072371B (zh) 温加工用高强度钢板及其制造方法
JPWO2016136810A1 (ja) 冷延鋼板及びその製造方法
JP2017048412A (ja) 溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板、およびそれらの製造方法
US10570473B2 (en) High-strength cold-rolled steel sheet, high-strength hot-dip galvanized steel sheet, and high-strength hot-dip galvannealed steel sheet having excellent ductility, stretch-flangeability, and weldability
JP6703606B2 (ja) 化成処理性及び曲げ加工性に優れた超高強度鋼板及びその製造方法
JPWO2017115748A1 (ja) 高強度鋼板、高強度亜鉛めっき鋼板及びこれらの製造方法
WO2013150669A1 (fr) Tôle d'acier laminée à chaud recuite après galvanisation et son procédé de fabrication
JPWO2011093319A1 (ja) 高強度冷延鋼板及びその製造方法
JP5363922B2 (ja) 伸びと伸びフランジ性のバランスに優れた高強度冷延鋼板
JP5829977B2 (ja) 降伏強度と成形性に優れた高強度冷延鋼板およびその製造方法
JPWO2018151273A1 (ja) 熱間圧延鋼板及びその製造方法
US20170283894A1 (en) Ferritic stainless steel having excellent ductility and method for manufacturing same
WO2019159771A1 (fr) Tôle d'acier à haute résistance et son procédé de fabrication
JPWO2011065479A1 (ja) 高強度極厚ｈ形鋼及びその製造方法
JP2017201049A (ja) 加工性に優れた高強度ステンレス鋼板およびその製造方法
JP5302840B2 (ja) 伸びと伸びフランジ性のバランスに優れた高強度冷延鋼板
JP7270042B2 (ja) 曲げ加工性に優れた高強度冷延鋼板及びその製造方法
JP7464887B2 (ja) 鋼板およびその製造方法
JP5189959B2 (ja) 伸びおよび伸びフランジ性に優れた高強度冷延鋼板
JP5327301B2 (ja) 延性と深絞り性に優れた高強度鋼板およびその製造方法
JP2008050622A (ja) 延性と深絞り性に優れた高強度鋼板およびその製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: POSCO, KOREA, REPUBLIC OF

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:PARK, SOO-HO;SHIM, JAE-HONG;SIGNING DATES FROM 20170221 TO 20170515;REEL/FRAME:042493/0063

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION