US20160076125A1 - Non-oriented electrical steel sheet having an excellent high-frequency iron loss property - Google Patents

Non-oriented electrical steel sheet having an excellent high-frequency iron loss property Download PDF

Info

Publication number
US20160076125A1
US20160076125A1 US14/767,735 US201414767735A US2016076125A1 US 20160076125 A1 US20160076125 A1 US 20160076125A1 US 201414767735 A US201414767735 A US 201414767735A US 2016076125 A1 US2016076125 A1 US 2016076125A1
Authority
US
United States
Prior art keywords
mass
steel sheet
iron loss
oriented electrical
electrical steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/767,735
Other languages
English (en)
Inventor
Shinji Koseki
Yoshihiko Oda
Hiroaki Toda
Tatsuhiko Hiratani
Tadashi Nakanishi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Original Assignee
JFE Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JFE Steel Corp filed Critical JFE Steel Corp
Assigned to JFE STEEL CORPORATION reassignment JFE STEEL CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KOSEKI, Shinji, TODA, HIROAKI, HIRATANI, TATSUHIKO, NAKANISHI, TADASHI, ODA, YOSHIHIKO
Publication of US20160076125A1 publication Critical patent/US20160076125A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/60—Ferrous alloys, e.g. steel alloys containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/004—Very low carbon steels, i.e. having a carbon content of less than 0,01%
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/008—Ferrous alloys, e.g. steel alloys containing tin
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
    • H01F1/12—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials
    • H01F1/14—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys
    • H01F1/16—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys in the form of sheets
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1216—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the working step(s) being of interest
    • C21D8/1222—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1216—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the working step(s) being of interest
    • C21D8/1233—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
    • C21D8/1255—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest with diffusion of elements, e.g. decarburising, nitriding
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
    • C21D8/1261—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
    • C21D8/1272—Final recrystallisation annealing
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
    • H01F1/12—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials
    • H01F1/14—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys
    • H01F1/147—Alloys characterised by their composition
    • H01F1/14766—Fe-Si based alloys
    • H01F1/14791—Fe-Si-Al based alloys, e.g. Sendust

Definitions

  • This disclosure relates to a non-oriented electrical steel sheet having an excellent high-frequency iron loss property.
  • a motor for a hybrid car or an electric car is driven at a high frequency region of 400-2 kHz from a viewpoint of miniaturization and high efficiency.
  • a non-oriented electrical steel sheet used in a core material for such a high-frequency motor is desired to be low in iron loss at a high frequency.
  • Addition of Si is effective to increase the specific resistance.
  • Si is an element having a large solid-solution strengthening ability so that there is a problem that the material is hardened with the increase in the amount of Si to deteriorate the rolling property.
  • Mn is small in its solid-solution strengthening ability compared to Si, the high-frequency iron loss can be reduced while suppressing deterioration of productivity.
  • JP 2002-47542 A discloses a non-oriented electrical steel sheet containing Si: 0.5-2.5 mass %, Mn: 1.0-3.5 mass % and Al: 1.0-3.0 mass %.
  • JP 2002-30397 A discloses a non-oriented electrical steel sheet containing Si: not more than 3.0 mass %, Mn: 1.0-4.0 mass % and Al: 1.0-3.0 mass %.
  • JP 2002-47542 A and JP 2002-30397 A have a problem that hysteresis loss is increased with the increase of Mn addition amount and, hence, the desired effect of reducing iron loss may not be obtained.
  • non-oriented electrical steel sheet having a chemical composition comprising C: not more than 0.005 mass %, Si: 1.5-4 mass %, Mn: 1.0-5 mass %, P: not more than 0.1 mass %, S: not more than 0.005 mass %, Al: not more than 3 mass %, N: not more than 0.005 mass %, Bi: not more than 0.0030 mass % and the remainder being Fe and inevitable impurities.
  • the non-oriented electrical steel sheet may contain one or two of Ca: 0.0005-0.005 mass % and Mg: 0.0002-0.005 mass % in addition to the above chemical composition.
  • non-oriented electrical steel sheet may further contain one or two of Sb: 0.0005-0.05 mass % and Sn: 0.0005-0.05 mass % in addition to the above chemical composition.
  • non-oriented electrical steel sheet may further contain Mo: 0.0005-0.0030 mass % in addition to the above chemical composition.
  • non-oriented electrical steel sheet may still further contain Ti: not more than 0.002 mass %.
  • FIG. 1 is a graph showing the influence of Bi content upon the relationship between Mn content and high-frequency iron loss W 10/400 .
  • FIG. 2 is a graph showing the relationship between Bi content and high-frequency iron loss W 10/400 .
  • a steel containing C: 0.0016 mass %, Si: 3.35 mass %, P: 0.013 mass %, S: 0.0004 mass %, Al: 1.4 mass % and N: 0.0018 mass % and added with Mn changed within a range of 0.1-5.2 mass % is melted in a laboratory to form a steel ingot, which is hot rolled, subjected to a hot band annealing at 1000° C. in an atmosphere of 100 vol % N 2 for 30 seconds, cold rolled to a cold rolled sheet of 0.30 mm in thickness and subjected to a final annealing at 1000° C. in an atmosphere of 20 vol % H 2 -80 vol % N 2 for 30 seconds.
  • symbol ⁇ shows the above experimental results as the relationship between Mn addition amount and iron loss W 10/400 .
  • Mn is less than 1 mass %
  • the iron loss is decreased with the increase in Mn addition amount, but the decrease of the iron loss becomes gentle at an amount of not less than 1 mass % and, rather, the iron loss is increased at an amount exceeding 4 mass %.
  • the steel sheet containing 2 mass % of Mn is observed by TEM, granular Bi is found in grain boundaries.
  • a steel prepared by adding Mn variously changed within a range of 0.1-5.2 mass % to a high-purity steel containing C: 0.0014 mass %, Si: 3.33 mass %, Al: 1.2 mass %, P: 0.014 mass %, S: 0.0006 mass %, N: 0.0020 mass % and Bi: not more than 0.0010 mass % is melted in a laboratory and shaped into a cold rolled and annealed sheet in the same manner as in the above experiment to measure an iron loss W 10/400 .
  • Bi is an impurity incorporated from scrap so that not only the amount incorporated, but also the deviation thereof becomes gradually large associated with the increased use of scrap in recent years.
  • Such an increase of Bi content is not a big problem in electrical steel sheets having a low Mn content, but the steels having a high Mn content are largely influenced by a slight amount of Bi because the grain growth is lowered by solute drag of Mn.
  • a steel prepared by adding Bi variously changed within a range of tr. to 0.0045 mass % to a steel containing C: 0.0022 mass %, Si: 3.20 mass %, Mn: 1.7 mass %, Al: 1.3 mass %, P: 0.014 mass %, S: 0.0005 mass % and N: 0.0020 mass % is melted in a laboratory and shaped into a cold rolled and annealed sheet of 0.30 mm in thickness in the same manner as in the above experiment to measure an iron loss W 10/400 .
  • FIG. 2 shows the above experimental results as the relationship between Bi content and iron loss W 10/400 .
  • the iron loss largely decreases when the Bi content is not more than 0.0030 mass % (not more than 30 massppm). This is due to the fact that the grain growth is improved by decreasing Bi. From this fact, we confirmed that the Bi content needs to be decreased to not more than 0.0030 mass % to suppress the bad influence of Bi upon grain growth.
  • C is an element forming a carbide with Mn.
  • the amount of Mn-based carbide is increased to block the grain growth, so that an upper limit is 0.005 mass %.
  • it is not more than 0.002 mass %.
  • Si is an element effective to increase the specific resistance of steel and reducing iron loss and is added in an amount of not less than 1.5 mass %. While when it is added in an amount exceeding 4 mass %, the magnetic flux density is lowered, so that an upper limit is 4 mass %.
  • the lower limit of Si is 2.0 mass % and the upper limit thereof is 3.0 mass %.
  • Mn is effective in increasing the specific resistance of steel and reducing an iron loss without largely damaging the workability and is an important ingredient added in an amount of not less than 1.0 mass %. To further obtain the effect of reducing iron loss, it is preferable to be added in an amount of not less than 1.6 mass %. While when it is added in an amount exceeding 5 mass %, the magnetic flux density is lowered, so that an upper limit is 5 mass %.
  • the lower limit of Mn is 2 mass % and the upper limit thereof is 3 mass %.
  • P is an element having a large solid-solution strengthening ability, but when it is added in an amount exceeding 0.1 mass %, the steel sheet is significantly hardened to deteriorate productivity, so that it is limited to not more than 0.1 mass %. Preferably, it is not more than 0.05 mass %.
  • MnS is an inevitable impurity.
  • MnS is precipitated to block the grain growth and increase iron loss, so that an upper limit is 0.005 mass %.
  • it is not more than 0.001 mass %.
  • Al is an element effective to increase the specific resistance of steel and reducing iron loss like Si. When it is added in an amount exceeding 3 mass %, the magnetic flux density is lowered, so that an upper limit is 3 mass %. Preferably, it is not more than 2 mass %. However, when Al content is less than 0.1 mass %, fine AN is precipitated to block grain growth and increase iron loss, so that a lower limit is preferable to be 0.1 mass %.
  • N is an inevitable impurity penetrated from ambient air into steel.
  • the content is large, grain growth is blocked due to the precipitation of AlN to increase the iron loss, so that an upper limit is restricted to 0.005 mass %.
  • it is not more than 0.003 mass %.
  • Bi is an important element to be controlled because it badly affects the high-frequency iron loss property.
  • Bi content exceeds 0.0030 mass % as seen from FIG. 2 , the iron loss violently increases. Therefore, Bi is restricted to not more than 0.0030 mass %. Preferably, it is not more than 0.0010 mass %.
  • the non-oriented electrical steel sheet preferably contains one or two of Ca and Mg in addition to the above chemical composition.
  • Ca is an element effective in forming a sulfide and coarsening by compositely precipitating with Bi to suppress the adverse effect of Bi and reduce iron loss. It is preferable to be added in an amount of not less than 0.0005 mass % to obtain such an effect. However, when it is added in an amount exceeding 0.005 mass %, the amount of CaS precipitated becomes too large and iron loss is adversely increased, so that an upper limit is preferable to be 0.005 mass %. More preferably, the lower limit of Ca is 0.001 mass % and the upper limit thereof is 0.004 mass %.
  • Mg is an element effective in forming an oxide and coarsening by compositely precipitating with Bi to suppress the adverse effect of Bi and reduce iron loss. It is preferable to be added in an amount of not less than 0.0002 mass % to obtain such an effect. However, addition exceeding 0.005 mass % is difficult and brings about an increase in cost, so that an upper limit is preferable to be 0.005 mass %. More preferably, the lower limit of Mg is 0.001 mass % and the upper limit thereof is 0.004 mass %.
  • non-oriented electrical steel sheet preferably further contains the following ingredients in addition to the above chemical composition.
  • Sb and Sn have an effect of improving the texture to increase the magnetic flux density, so that they can be added in an amount of not less than 0.0005 mass % alone or in admixture. More preferably, it is not less than 0.01 mass %. However, addition exceeding 0.05 mass % brings about embrittlement of the steel sheet, so that an upper limit is preferable to be 0.05 mass %. More preferably, the lower limit of each of Sb and Sn is 0.01 mass % and the upper limit thereof is 0.04 mass %.
  • Mo has an effect of coarsening the resulting carbide to reduce iron loss and is preferably added in an amount of not less than 0.0005 mass %. However, when it is added in an amount exceeding 0.0030 mass %, the amount of the carbide becomes too large and the iron loss is rather increased, so that an upper limit is preferable to be 0.0030 mass %. More preferably, the lower limit of Mo is 0.0010 mass % and the upper limit thereof is 0.0020 mass %.
  • Ti is an element forming a carbonitride. When the content is large, the amount of the carbonitride precipitated becomes too large, so that the grain growth is blocked and the iron loss is increased. Therefore, Ti is preferably restricted to not more than 0.002 mass %. More preferably, it is not more than 0.001 mass %.
  • the remainder other than the aforementioned ingredients is Fe and inevitable impurities.
  • other elements may be included within a range not damaging the desired effect.
  • the steel sheet can be produced by a method wherein a steel having a chemical composition is melted, for example, in a converter, a degassing device or the like and shaped into a raw steel material (slab) by a continuous casting method or an ingot making-blooming method, which is hot rolled, subjected to a hot band annealing as required and further to a single cold rolling or two or more cold rollings including an intermediate annealing therebetween to a predetermined sheet thickness and subsequently to a final annealing.
  • a steel having a chemical composition is melted, for example, in a converter, a degassing device or the like and shaped into a raw steel material (slab) by a continuous casting method or an ingot making-blooming method, which is hot rolled, subjected to a hot band annealing as required and further to a single cold rolling or two or more cold rollings including an intermediate annealing therebetween to a predetermined sheet thickness and subsequently to a
  • a steel having a chemical composition shown in Table 1 is melted in a converter, degassed by blowing and continuously cast into a slab, which is heated at 1100° C. for 1 hour, hot rolled at a final rolling temperature of 800° C. and wound into a coil at a temperature of 610° C. to obtain a hot rolled sheet of 1.8 mm in thickness. Thereafter, the hot rolled sheet is subjected to a hot band annealing at 1000° C. in an atmosphere of 100 vol % N 2 for 30 seconds and cold rolled to obtain a cold rolled sheet having a sheet thickness of 0.35 mm, which is subjected to a final annealing at 980° C. in an atmosphere of 20 vol % H 2 -80 vol % N 2 for 15 seconds to form a cold rolled and annealed sheet.
  • Epstein samples with a width: 30 mm ⁇ a length: 280 mm in the rolling direction and in a direction perpendicular to the rolling direction to measure an iron loss W 10/400 and a magnetic flux density B 50 according to JIS C2550, respectively. These results are shown in Table 1.
  • the steel sheets satisfying our chemical composition, particularly the steel sheets decreasing Bi content are excellent in the high-frequency iron loss property irrespective of a high Mn content.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Dispersion Chemistry (AREA)
  • Power Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Soft Magnetic Materials (AREA)
  • Electromagnetism (AREA)
  • Manufacturing & Machinery (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Manufacturing Of Steel Electrode Plates (AREA)
US14/767,735 2013-03-22 2014-03-12 Non-oriented electrical steel sheet having an excellent high-frequency iron loss property Abandoned US20160076125A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2013-060537 2013-03-22
JP2013060537A JP2014185365A (ja) 2013-03-22 2013-03-22 高周波鉄損特性に優れる無方向性電磁鋼板
PCT/JP2014/056430 WO2014148328A1 (ja) 2013-03-22 2014-03-12 高周波鉄損特性に優れる無方向性電磁鋼板

Publications (1)

Publication Number Publication Date
US20160076125A1 true US20160076125A1 (en) 2016-03-17

Family

ID=51580015

Family Applications (1)

Application Number Title Priority Date Filing Date
US14/767,735 Abandoned US20160076125A1 (en) 2013-03-22 2014-03-12 Non-oriented electrical steel sheet having an excellent high-frequency iron loss property

Country Status (8)

Country Link
US (1) US20160076125A1 (zh)
EP (1) EP2977480B1 (zh)
JP (1) JP2014185365A (zh)
KR (1) KR101700694B1 (zh)
CN (1) CN105074032B (zh)
RU (1) RU2650469C2 (zh)
TW (1) TWI551694B (zh)
WO (1) WO2014148328A1 (zh)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3889289A4 (en) * 2018-11-30 2021-10-06 Posco NON-ORIENTED ELECTRIC STEEL SHEET AND ITS PRODUCTION PROCESS
EP3889290A4 (en) * 2018-11-30 2021-10-06 Posco NON-ORIENTED ELECTRIC STEEL SHEET AND METHOD OF MANUFACTURING THEREOF
EP4079889A4 (en) * 2019-12-20 2023-05-24 Posco NON-ORIENTED ELECTRICAL STEEL SHEET AND METHOD OF MANUFACTURING THEREOF

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6738047B2 (ja) 2017-05-31 2020-08-12 Ｊｆｅスチール株式会社 無方向性電磁鋼板とその製造方法
JP7172100B2 (ja) * 2018-04-02 2022-11-16 日本製鉄株式会社 無方向性電磁鋼板
KR102105530B1 (ko) * 2018-09-27 2020-04-28 주식회사 포스코 무방향성 전기강판 및 그 제조방법
JP7328491B2 (ja) * 2018-11-09 2023-08-17 日本製鉄株式会社 無方向性電磁鋼板
KR102348508B1 (ko) 2019-12-19 2022-01-07 주식회사 포스코 무방향성 전기강판 및 그 제조방법

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2540946B2 (ja) * 1989-06-30 1996-10-09 日本鋼管株式会社 磁気特性に優れた無方向性電磁鋼板およびその製造方法
JPH06108149A (ja) * 1992-09-29 1994-04-19 Nippon Steel Corp 需要家焼鈍後の鉄損が極めて優れた無方向性珪素鋼板の製造方法
JP2002030397A (ja) 2000-07-13 2002-01-31 Sumitomo Metal Ind Ltd 無方向性電磁鋼板とその製造方法
JP3835137B2 (ja) * 2000-07-28 2006-10-18 住友金属工業株式会社 無方向性電磁鋼板およびその製造方法
JP3835216B2 (ja) * 2001-08-09 2006-10-18 住友金属工業株式会社 無方向性電磁鋼板およびその製造方法
RU2311479C2 (ru) * 2003-05-06 2007-11-27 Ниппон Стил Корпорейшн Лист из неориентированной электротехнической стали, превосходный по потерям в сердечнике, и способ его изготовления
JP4414727B2 (ja) 2003-10-31 2010-02-10 新日本製鐵株式会社 磁気特性、耐変形性の優れた電磁鋼板とその製造方法
US7662242B2 (en) * 2004-11-04 2010-02-16 Nippon Steel Corporation Non-oriented electrical steel superior in core loss
JP4280224B2 (ja) * 2004-11-04 2009-06-17 新日本製鐵株式会社 鉄損に優れた無方向性電磁鋼板
RU2398894C1 (ru) * 2006-06-16 2010-09-10 Ниппон Стил Корпорейшн Лист высокопрочной электротехнической стали и способ его производства
JP5200376B2 (ja) * 2006-12-26 2013-06-05 Ｊｆｅスチール株式会社 無方向性電磁鋼板およびその製造方法
JP5417689B2 (ja) * 2007-03-20 2014-02-19 Ｊｆｅスチール株式会社 無方向性電磁鋼板
JP4585609B2 (ja) * 2007-12-03 2010-11-24 新日本製鐵株式会社 高周波鉄損の低い無方向性電磁鋼板及びその製造方法
JP4681689B2 (ja) * 2009-06-03 2011-05-11 新日本製鐵株式会社 無方向性電磁鋼板及びその製造方法
JP5338750B2 (ja) * 2010-06-09 2013-11-13 Ｊｆｅスチール株式会社 無方向性電磁鋼板の製造方法
KR101353462B1 (ko) * 2011-12-28 2014-01-24 주식회사 포스코 무방향성 전기강판 및 제조 방법
KR101353463B1 (ko) * 2011-12-28 2014-01-21 주식회사 포스코 무방향성 전기강판 및 그 제조방법
CN102634742B (zh) * 2012-04-01 2013-09-25 首钢总公司 一种无Al的无取向电工钢的制备方法

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3889289A4 (en) * 2018-11-30 2021-10-06 Posco NON-ORIENTED ELECTRIC STEEL SHEET AND ITS PRODUCTION PROCESS
EP3889290A4 (en) * 2018-11-30 2021-10-06 Posco NON-ORIENTED ELECTRIC STEEL SHEET AND METHOD OF MANUFACTURING THEREOF
EP4079889A4 (en) * 2019-12-20 2023-05-24 Posco NON-ORIENTED ELECTRICAL STEEL SHEET AND METHOD OF MANUFACTURING THEREOF

Also Published As

Publication number Publication date
KR101700694B1 (ko) 2017-01-31
CN105074032A (zh) 2015-11-18
RU2015145284A (ru) 2017-04-25
RU2650469C2 (ru) 2018-04-13
JP2014185365A (ja) 2014-10-02
WO2014148328A1 (ja) 2014-09-25
TW201443248A (zh) 2014-11-16
CN105074032B (zh) 2018-01-12
EP2977480A1 (en) 2016-01-27
KR20150109485A (ko) 2015-10-01
EP2977480B1 (en) 2017-07-05
TWI551694B (zh) 2016-10-01
EP2977480A4 (en) 2016-04-13

Similar Documents

Publication Publication Date Title
US20160076125A1 (en) Non-oriented electrical steel sheet having an excellent high-frequency iron loss property
JP5733409B2 (ja) 無方向性電磁鋼板
EP2657355B1 (en) Method of producing non-oriented electrical steel sheet
US10102951B2 (en) Non-oriented electrical steel sheet having excellent magnetic properties
TWI494446B (zh) 無方向性電磁鋼板之製造方法
JP6821055B2 (ja) 無方向性電磁鋼板およびその製造方法
JP2005200756A (ja) 無方向性電磁鋼板の製造方法
EP2975147B1 (en) Non-oriented electrical steel sheet having excellent high-frequency iron loss property
KR100872607B1 (ko) 펀칭 가공성과 왜곡 제거 소둔 후의 자기 특성이 우수한무방향성 전자 강판과 그 제조 방법
JP6123234B2 (ja) 電磁鋼板
CN112430776B (zh) 一种磁各向异性小的无取向电工钢板及其制造方法
US9728332B2 (en) Wire rod and steel wire having superior magnetic characteristics, and method for manufacturing same
JP6852965B2 (ja) 電磁鋼板とその製造方法
JP2003027197A (ja) 高周波特性に優れた無方向性電磁鋼板
JPH1192892A (ja) 鉄損の低い無方向性電磁鋼板
JP2001279396A (ja) 加工性及び高周波磁気特性に優れる無方向性電磁鋼板

Legal Events

Date Code Title Description
AS Assignment

Owner name: JFE STEEL CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KOSEKI, SHINJI;ODA, YOSHIHIKO;TODA, HIROAKI;AND OTHERS;SIGNING DATES FROM 20150714 TO 20150717;REEL/FRAME:036321/0014

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION