US20160021798A1

US20160021798A1 - Emi gasket for shielding electromagnetic wave

Info

Publication number: US20160021798A1
Application number: US14/463,320
Authority: US
Inventors: Young Hun Kim
Original assignee: Ich Co Ltd
Current assignee: Ich Co Ltd
Priority date: 2014-07-18
Filing date: 2014-08-19
Publication date: 2016-01-21
Anticipated expiration: 2034-08-19
Also published as: US9247680B1; KR101541467B1

Abstract

The present invention provides a gasket formed by applying an adhesive on four sides of an elastic body of a closed cell polyurethane material, wrapping a copper film around the elastic body other than a bottom bonding surface, forming a coating layer by depositing or plating nickel on a surface exposing the copper film, forming a resin coating layer on the nickel coating layer, and applying a conductive adhesive on the bottom surface. The present invention may drastically decrease thickness of the gasket by using closed cell polyurethane instead of conventional open cell polyurethane and may completely prevent oxidation and corrosion of copper by depositing or plating nickel on the exposed portions of the copper film and coating resin thereon. Furthermore, since a fiber material is not used, conductive powders are not generated, and thus short circuits or malfunctions can be reduced.

Description

CROSS-REFERENCE TO RELATED APPLICATION

This application is based on and claims priority from Korean Patent Application No. 10-2014-0091109 filed on Jul. 18, 2014 in the Korean Intellectual Property Office, the disclosure of which is incorporated herein in its entirety by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention
The present invention relates to an EMI gasket for shielding electromagnetic waves, and more particularly, to an EMI gasket for shielding electromagnetic waves, which has excellent electromagnetic wave shielding performance.
2. Background of the Related Art
Generally, electromagnetic waves generated by internal circuits of various kinds of electronic devices are radiated to outside through the air or conducted through a power line or the like.
Such electromagnetic waves are known to generate noises and malfunctions in the components or devices in the neighborhood and have a bad effect on human bodies.
As electronic devices are becoming thinner and their circuits are getting complicated recently, possibility of generating electromagnetic waves abruptly increases, and regulations on the electromagnetic waves are strengthened in Korea as well as in developed countries.
Accordingly, conductive sponges are used conventionally so that the electromagnetic waves generated by the circuits of the electronic devices may not be radiated to outside.
However, the conductive sponge is disadvantageous in that since conductive powders are generated, a module risk factor may occur, and its restoring force is low.
In addition, Korean Utility Model Registration No. 20-0208434 discloses a gasket formed by wrapping a copper plate of high conductivity on three sides of an electric conductor, in a general gasket in which four sides of a rectangular elastic body of a polyurethane material are wrapped by a conductor of a PE fiber coated with copper and nickel, and an adhesive tape is attached on the bottom side.
However, since a conductive fabric of a coated fiber is also used in this case and generates conductive powders, a short circuit or a malfunction is worried, and corrosion is also worried since a copper plate is used.

SUMMARY OF THE INVENTION

Accordingly, the present invention has been made in view of the above-mentioned problems occurring in the prior art, and it is an object of the present invention to provide an EMI gasket for shielding electromagnetic waves, which has excellent electromagnetic wave shielding performance without generating a short circuit or a malfunction.
To accomplish the above object, according to the present invention, there is provided an EMI gasket for shielding electromagnetic waves, the EMI gasket formed by applying an adhesive on four sides of an elastic body of a closed cell polyurethane material, wrapping a copper film around the elastic body other than a bottom bonding surface, forming a coating layer on the copper film by depositing or plating nickel, and applying a conductive adhesive on the bottom surface.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects, features and advantages of the present invention will be apparent from the following detailed description of the preferred embodiments of the invention in conjunction with the accompanying drawings, in which:

FIG. 1 is a view showing a cross section of a gasket of the present invention;

FIG. 2 is a view showing a layered structure of the center portion of a gasket of the present invention;

FIG. 3 is a side cross-sectional view showing a layered structure of the side surface of a gasket of the present invention;

FIG. 4 is a picture showing gaskets of the present invention respectively designed and applied to be appropriate to the shape of a component;

FIG. 5 is a view showing a result of a salt water spray test performed on an embodiment of the present invention and a comparative example; and

FIG. 6 a is a picture or photographic view showing a result of a salt water spray test performed on test samples of an embodiment of the present invention, while FIG. 6 b is a picture or photographic view showing comparative examples.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

FIG. 1 is a view showing a cross section of a gasket of the present invention, FIG. 2 is a view showing a layered structure of the center portion of a gasket of the present invention, and FIG. 3 is a side cross-sectional view showing a layered structure of the side surface of a gasket of the present invention. The base layer 10 in the middle uses a closed cell polyurethane material. The base layer has a thickness of 150 to 250 micrometers. Since a closed cell polyurethane material is used, the entire thickness of the currently and commonly used gasket having a thickness of around 400 to 500 micrometers can be reduced by half. An adhesive layer 20 is applied on four sides including side surfaces and top and bottom surfaces. Thickness of the adhesive layer is generally around 10 micrometers. As shown in FIG. 1, a copper film 30 is attached on all areas other than the center portion of the bottom side which is attached to the apparatus. The copper film is manufactured by laminating a thin film copper plate on a polyester film or by plating or depositing copper on the polyester film. The copper film is formed to have a thickness of less than 10 micrometers, preferably less than 5 micrometers, further preferably less than 3 micrometers, and most preferably 2 micrometers. In order to prevent corrosion of the copper layer, it is preferable to form a nickel layer 40 by coating, depositing or sputtering nickel on all sides other than the bottom surface which is attached to the apparatus. The nickel layer is formed to have a thickness of less than one micrometer, preferably less than 0.5 micrometers, and most preferably 0.3 micrometers.
In addition, an extremely thin resin coating layer 60 is formed to completely prevent corrosion of the copper layer. The resin coating layer is formed to have a thickness less than one micrometer so as not to interfere conductivity. Corrosion of the copper layer can be completely prevented by forming the coating layer. The coating layer is preferably formed using silicon or fluorideresin.
A conductive adhesive layer 50 is formed on the bottom surface which is attached to the apparatus. In order to improve adhesiveness, a conductive non-woven fabric layer 30′ may be further formed on the top of the conductive adhesive layer. A conductive material such as nickel, cobalt or the like is coated on the top of the conductive non-woven fabric layer. Damages caused by a short circuit or a malfunction can be reduced compared with a conventional technique using a fabric.
FIG. 4 shows a picture of gasket products of the present invention. The gasket can be freely cut into a shape appropriate to the usage of the product when it is actually used.

Embodiment 1

An adhesive is applied as thick as 10 micrometers on three sides of closed cell polyurethane foam having a thickness of 150 micrometers, and a copper film of 2 micrometers is bonded in the shape as shown in FIG. 1. A gasket having a total thickness of about 200 micrometers is manufactured by applying a nickel coating of 3 micrometers and a fluorideresin coating of 0.5 micrometers on the top and side surfaces and applying a conductive adhesive on the bottom surface as thick as 30 micrometers.
Properties of the product shown in embodiment 1 of the present invention are compared with those of a conventional conductive sponge (comparative example 1), and a result thereof is shown in Table 1. A Toray KP film product is used as the conductive sponge. A restoring force test is performed to measure a restoring force after compressing a test sample by 50%, and the test is performed on a test sample having a size of 25 mm×25 mm at a temperature of 85° C. for 24 hours.

	TABLE 1

		Comparative
	Embodiment 1	example 1

Conductive powder	None	Generated
Restoring force	97%	10%
Minimum thickness	200	400
Surface resistance	0.03/	0.1/

As is understood from the result shown in Table 1, the product of the present invention does not have a module risk factor since conductive powders are not generated, has a superior sealing force as a gasket since its restoring force is excellent, and is manufactured to be thin, and thus it may contribute to making a thinner and lighter electronic device such as a cellular phone or the like. In addition, since surface resistance is low, electromagnetic wave shielding capability and conductivity of the product of the present invention are superior.

Embodiments 2 to 4

In addition, gaskets are manufactured in the same manner as shown in embodiment 1 while changing thickness of the closed cell polyurethane foam to 200 micrometers, 250 micrometers and 300 micrometers, and restoring forces are measured by applying a load of 400 g at a temperature of 70° for 18 hours.

TABLE 2

		Proper
		compression
Total	Foam	rate (based	Compressed	Restored
thickness	thickness	on total	thickness	thickness	Restor-
(T)	(T)	thickness)	(T)	(T)	ing rate

0.20	0.15	25%	0.050	0.046	30%
0.25	0.20	24%	0.060	0.054	28%
0.30	0.25	33%	0.100	0.093	46%
0.35	0.30	34%	0.120	0.111	48%
0.40	0.35	40%	0.160	0.150	62%

TEST EXAMPLE 1

A salt water spray test has been conducted on the product of embodiment 1 of the present invention and the products of comparative example 1 and Korean Utility Model Registration No. 20-0208434 (comparative example 2). The test has been conducted using 5% salt water at a temperature of 35° C. for 24 hours. The product of the embodiment of the present invention does not show any change in appearance after the test, and the surface resistance has not been changed since there is no corrosion. Appearances of both the products of comparative example 1 and comparative example 2 are changed due to corrosion, and values of the surface resistance have been considerably increased after the test.

TEST EXAMPLE 2

One half of a sheet is fabricated to be the same as the product of embodiment 3 of the present invention, and the other half is fabricated to be the same as embodiment 3 without a fluorideresin coating process (comparative example 3), and degrees of corrosion are compared after spraying ten liters of 5% salt water at 35° C. for 48 hours. Pictures compared are shown in FIG. 5.
In addition, pictures of gaskets manufactured as test samples and gone through the salt water spray test are shown in FIG. 6. FIG. 6 a shows a picture of products manufactured in embodiment 3, and FIG. 6 b shows a picture of products of comparative example 3 respectively manufactured as a test sample and gone through a salt water spray test. It is understood that corrosion preventing performance is remarkably improved by the fluorideresin coating of the present invention.
Furthermore, it is confirmed that the product of the embodiment of the present invention does not show a change in the surface resistance after the salt water is sprayed.
The present invention may drastically decrease thickness of a gasket by using closed cell polyurethane instead of conventional open cell polyurethane.
In addition, oxidation and corrosion of copper can be prevented by depositing or plating nickel on three exposed portions of a copper film.
Furthermore, since a fiber material is not used, conductive powders are not generated, and thus short circuits or malfunctions can be reduced.
The product of the present invention can be advantageously used to shield electromagnetic waves of an electronic device such as a cellular phone or the like. Compared with a conventional product, since the product of the present invention does not generate conductive powders, has a superior sealing force and is manufactured to be thin, it may contribute to making a thinner and lighter electronic device such as a cellular phone or the like. In addition, since surface resistance of the product of the present invention is low, its electromagnetic wave shielding capability and conductivity are superior.
While the present invention has been described with reference to the particular illustrative embodiments, it is not to be restricted by the embodiments but only by the appended claims. It is to be appreciated that those skilled in the art can change or modify the embodiments without departing from the scope and spirit of the present invention.

Claims

1. A gasket for shielding electromagnetic waves, the gasket formed by

applying an adhesive on four sides of an elastic body of a closed cell polyurethane material,

wrapping a copper film around the elastic body other than a bottom bonding surface,

forming a nickel coating layer by depositing or plating nickel on a top surface and a side surface where the copper film is exposed,

forming a resin coating layer on the nickel coating layer, and

applying a conductive adhesive on the bottom surface.

2. The gasket according to claim 1, wherein the copper film is formed by plating or depositing copper on a polyester film.

3. The gasket according to claim 1, wherein resin of the resin coating layer is fluoride resin or silicon resin.

4. The gasket according to claim 3, wherein the resin coating layer is formed to have a thickness less than one micro meter.

5. The gasket according to claim 1, wherein a conductive non-woven fabric layer is formed between the conductive adhesive and the adhesive.

6. The gasket according to claim 5, wherein the conductive non-woven fabric layer is formed by coating conductive metal on a non-woven fabric.

7. The gasket according to claim 6, wherein the conductive metal is nickel, cobalt or a mixture of these.

8. The gasket according to claim 2, wherein resin of the resin coating layer is fluoride resin or silicon resin.

9. The gasket according to claim 2, wherein a conductive non-woven fabric layer is formed between the conductive adhesive and the adhesive.