US20150091038A1 - Light emitting diode - Google Patents
Light emitting diode Download PDFInfo
- Publication number
- US20150091038A1 US20150091038A1 US14/561,957 US201414561957A US2015091038A1 US 20150091038 A1 US20150091038 A1 US 20150091038A1 US 201414561957 A US201414561957 A US 201414561957A US 2015091038 A1 US2015091038 A1 US 2015091038A1
- Authority
- US
- United States
- Prior art keywords
- semiconductor layer
- light emitting
- electrode
- layers
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A light emitting diode including a lower semiconductor layer formed on a substrate; an upper semiconductor layer disposed above the lower semiconductor layer, exposing an edge region of the lower semiconductor layer; a first electrode formed on the upper semiconductor layer; an insulation layer interposed between the first electrode and the upper semiconductor layer, to supply electric current to the lower semiconductor layer; a second electrode formed on another region of the upper semiconductor layer, to supply electric current to the upper semiconductor layer. The first electrode includes an electrode pad disposed on the upper semiconductor layer and an extension extending from the electrode pad to the exposed lower semiconductor layer. The insulation layer may have a distributed Bragg reflector structure.
Description
- This application is a divisional of U.S. patent application Ser. No. 12/974,605, filed on Dec. 21, 2010, and claims priority from and the benefit of Korean Patent Application No. 2009-0131693, filed on Dec. 28, 2009, which are hereby incorporated by reference for all purposes as if fully set forth herein.
- 1. Field
- Exemplary embodiments of the invention relate to light emitting diodes.
- 2. Description of the Background
- Gallium nitride (GaN) based light emitting diodes (LEDs) have been under development for about 10 years. GaN-based LEDs represent a significant change in LED technology and are used in a wide range of applications, including natural color LED display devices, LED traffic sign boards, white LEDs, etc. In the future, white LEDs are expected to replace fluorescent lamps, as the efficiency of white LEDs approaches the efficiency of typical fluorescent lamps.
- A GaN-based light emitting diode is generally formed by growing epitaxial layers on a substrate, for example, a sapphire substrate, and includes an N-type semiconductor layer, a P-type semiconductor layer, and an active layer interposed there between. Further, an N electrode is formed on the N-type semiconductor layer, and a P electrode is formed on the P-type semiconductor layer. The light emitting diode is electrically connected to, and operated by, an external power source, through these electrodes. Here, electric current is directed from the P-electrode to the N-electrode, through the semiconductor layers.
- Generally, since the P-type semiconductor layer has a high specific resistance, electric current is not evenly distributed in the P-type semiconductor layer. Instead, the current is concentrated on a portion of the P-type semiconductor layer having the P-electrode formed thereon, causing current concentration at an edge of the P-type semiconductor layer. The current concentration leads to a reduction in light emitting area, thereby reducing luminous efficacy. To solve such problems, a transparent electrode layer having a low specific resistance is formed on the P-type semiconductor layer, so as to enhance current distribution. In this structure, when supplied from the P-electrode, the electric current is dispersed by the transparent electrode layer before entering the P-type semiconductor layer, thereby increasing a light emitting area of the LED.
- However, since the transparency of the transparent electrode layer is dependent upon the thickness thereof, the thickness of the transparent electrode layer is generally limited, thereby limiting the current dispersion. In particular, for a large area LED (having an area of about 1 mm2 or more and a high output), there is a limit to the current dispersion through the transparent electrode layer.
- Meanwhile, the electric current flows into the N electrode through the semiconductor layers. Accordingly, the electric current concentrates on a portion of the N-type semiconductor layer adjacent to the N-electrode. That is, the current flowing in the semiconductor layers is concentrated in a region of the N-type semiconductor layer near the N-electrode is formed. Therefore, there is a need for a light emitting diode solving the problem of current concentration within the N-type semiconductor layer.
- Typically, various types of electrode structures are used in a light emitting diode, to ensure uniform current dispersion.
FIG. 1 illustrates a light emitting diode having a diagonal electrode structure. InFIG. 1 , reference numeral 1 denotes an N electrode, 2 denotes a P electrode, 3 denotes an exposed N-type semiconductor layer, and 4 denotes a transparent electrode layer. Referring toFIG. 1 , the diagonal electrode structure is highly effective for a small LED, but causes an increasing concentration of electric current on a central region of the LED, as the size of the LED increases, such that only the central region of the LED emits light. In addition, an electrode pattern of a simple facing-type structure also suffers from the same problems as the diagonal electrode structure. -
FIG. 2 illustrates a light emitting diode having a combined electrode structure including a facing-type structure and a symmetrical extension-type structure, andFIG. 3 is a cross-sectional view taken along line A-A′ ofFIG. 2 . InFIG. 2 andFIG. 3 ,reference numeral 11 denotes a substrate, 13 denotes an N-type semiconductor layer, 15 denotes an active layer, 17 denotes a P-type semiconductor layer, 19 denotes a transparent electrode layer, 21 denotes an N electrode, 22 and 23 denote extensions of the N electrode, 31 denotes a P electrode, and 32 and 33 denote extensions of the P electrode. - Referring to
FIG. 2 andFIG. 3 , the combined electrode structure is generally used for large LEDs. It can be appreciated that theextension - However, since the N-
type semiconductor layer 13 is exposed by mesa-etching used to form theextensions P electrode 31 and theextension parts N electrode 21, the light emitting area is inevitably decreased. Moreover, in the current state of the art, the number of electrode pads formed on a single chip is more than doubled, for current diffusion, and a mesa-etching area for forming electrodes and extension parts of these electrodes is also expanded. The expansion of the mesa-etching area, caused by the increase in the number of electrode pads, results in a decrease in the light emitting area, based on the same chip area, thereby reducing light emitting efficiency. - It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.
- An exemplary embodiment of the invention provides a light emitting diode configured to prevent a reduction in light emitting area, resulting from the formation of an electrode and/or electrode pad.
- Additional features of the invention will be set forth in the description which follows, and in part will be apparent from the description, or may be learned by practice of the invention. Still other aspects, features, and advantages of the present invention are readily apparent from the following detailed description, simply by illustrating a number of particular embodiments and implementations, including the best mode for carrying out the present invention. The present invention can take the form of a variety of different embodiments, and several details can be modified in various obvious respects, all without departing from the spirit and scope of the present invention. Accordingly, the drawing and description are to be regarded as illustrative in nature, and not as restrictive.
- Exemplary embodiments of the present invention disclose a light emitting diode.
- The light emitting diode includes a lower semiconductor layer formed on a substrate; an upper semiconductor layer disposed above the lower semiconductor layer, to expose a portion of the lower semiconductor layer; a first electrode formed on the upper semiconductor layer and extending onto the exposed portion of the lower semiconductor layer, to supply electric current to the lower semiconductor layer; an insulation layer interposed between the first electrode and the upper semiconductor layer; a second electrode formed the upper semiconductor layer, to supply electric current to the upper semiconductor layer.
- The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate exemplary embodiments of the invention, and together with the description serve to explain the principles of the invention.
-
FIG. 1 illustrates a conventional light emitting diode having a diagonal electrode structure. -
FIG. 2 illustrates a conventional light emitting diode having a combined facing-type and symmetrical extension-type structure. -
FIG. 3 is a cross-sectional view taken along line A-A′ ofFIG. 2 . -
FIG. 4 is a plan view of a light emitting diode, according to one exemplary embodiment of the invention. -
FIG. 5 is a cross-sectional view taken along line A-A ofFIG. 4 . -
FIG. 6 is a cross-sectional view of a light emitting diode, according to another exemplary embodiment of the invention. -
FIG. 7 is a plan view of a light emitting diode, according to a further exemplary embodiment of the invention. -
FIG. 8 is a cross-sectional view taken along line B-B′ ofFIG. 7 . -
FIG. 9 is a cross-sectional view taken along line C-C′ ofFIG. 7 . -
FIG. 10 is a cross-sectional view of a light emitting diode, according to yet another exemplary embodiment of the invention. -
FIG. 11 is a cross-sectional view of a light emitting diode, according to yet another exemplary embodiment of the invention. - The invention is described more fully hereinafter with reference to the accompanying drawings, in which exemplary embodiments of the invention are shown. This invention may, however, be embodied in many different forms and should not be construed as limited to the exemplary embodiments set forth herein. Rather, these exemplary embodiments are provided so that this disclosure is thorough and will fully convey the scope of the invention to those skilled in the art. In the drawings, the size and relative sizes of layers and regions may be exaggerated for clarity. Like reference numerals in the drawings denote like elements.
- It will be understood that when an element such as a layer, film, region or substrate is referred to as being formed or disposed “on” another element, it can be directly on the other element, or intervening elements may also be present. In contrast, when an element is referred to as being formed or disposed “directly on” another element, there are no intervening elements present. In addition, when an element is referred to as being connected to another element, intervening elements may be present there between. In contrast, when an element is referred to as being directly connected to another element, no intervening elements are present.
-
FIG. 4 is a plan view of a light emitting diode, according to one exemplary embodiment, andFIG. 5 is a cross-sectional view taken along line A-A ofFIG. 4 . Referring toFIG. 4 andFIG. 5 , alower semiconductor layer 113 is formed on asubstrate 111. Thesubstrate 111 is not limited to a particular material, and may be, for example, a sapphire substrate. - An
upper semiconductor layer 117 is formed above thelower semiconductor layer 113. Theupper semiconductor layer 117 is positioned within a region surrounded by edges of thelower semiconductor layer 113, so as to expose at least a portion of thelower semiconductor layer 113. Meanwhile, anactive layer 115 is interposed between thelower semiconductor layer 113 and theupper semiconductor layer 117. Theactive layer 115 is positioned under theupper semiconductor layer 117, while exposing edge regions of thelower semiconductor layer 113. - The
lower semiconductor layer 113,active layer 115, andupper semiconductor layer 117 may be formed of, for example, a nitride-based compound semiconductor material, such as (B, Al, In, or Ga)N. Theactive layer 115 includes light-emitting elements, to emit light at desired frequencies, for example, UV or blue light. Thelower semiconductor layer 113 and theupper semiconductor layer 117 include materials having a greater band gap than theactive layer 115. - As shown in the drawings, the
lower semiconductor layer 113 and/or theupper semiconductor layer 117 may have a single layer structure or, in the alternative, may have a multilayer structure. Further, theactive layer 115 may have a single quantum well structure or a multi-quantum well structure. The light emitting diode may further include a buffer layer (not shown) disposed between thesubstrate 111 and thelower semiconductor layer 113. The buffer layer is selected to relieve lattice mismatches between thesubstrate 111 and thelower semiconductor layer 113. - The semiconductor layers 113, 115, 117 may be in the form of a semiconductor stack (light-emitting unit) formed by metal organic chemical vapor deposition (MOCVD) or molecular beam epitaxy (MBE). The semiconductor stack may be subjected to mesa-etching, to expose regions of the
lower semiconductor layer 113, via photolithography and etching processes. As such, the exposed regions of thelower semiconductor layer 113 may have a reduced thickness, as compared to other regions thereof. - Here, mesa-etching may be performed on the semiconductor stack, to form a mesa structure having an inclined side surfaces. The side surfaces may have a degree of inclination in the range of 20˜80 degrees, and preferably in the range of 30˜60 degrees, with respect to the plane of the
substrate 111. The inclined side surfaces may enhance workability and reliability, when forming asecond insulation layer 140 and/or aninclined extension 122 of afirst electrode 120, as described below. In addition, the inclined mesa structure increases a light emitting area. - An insulation layer is formed on mesa. The insulation layer may include a
first insulation layer 119 and asecond insulation layer 140. Thefirst insulation layer 119 covers upper and side surfaces of the mesa structure, and may be formed of, for example, SiO2, Si3N4, Nb2O5, TiO2, etc. - The
second insulation layer 140 may be formed on a selected portion of theupper semiconductor layer 117, where thefirst electrode 120 is to be formed. In particular, thesecond insulation layer 140 may cover a sidewall and a portion of the upper surface of the mesa structure. Thesecond insulation layer 140 may be formed to have, for example, in a distributed Bragg reflector (DBR) structure, by alternately stacking layers having substantially different indices of refraction. For example, thesecond insulation layer 140 may be formed by alternately stacking, multiple layers of SiO2 and TiO2, or multiple layers of SiO2 and Si3N4. The stacked layers may then be etched in a predetermined pattern, using photolithography. - Here, the layers forming the
insulation layer 140 are stacked, such that the outermost layers comprise a Si compound, that is, SiO2. TiO2 may suffer from deformation when subjected to thermal stress. Thus, if a TiO2 layer is used as an outermost layer of thesecond insulation layer 140, by alternately stacking SiO2 and TiO2, thesecond insulation layer 140 may crack after deposition. However, when stacking multiple SiO2 and TiO2 layers, by first forming a SiO2 on thefirst insulation layer 119 and then stacking a TiO2 layer on the SiO2 layer, thesecond insulation layer 140 exhibits good thermal stability, thereby preventing cracking of thesecond insulation layer 140. Likewise, it is desirable that the formation of thesecond insulation layer 140 conclude with the deposition of a SiO2. In other words, top and bottom layers of theinsulation layer 140 are generally formed of layers having good thermal stability, to improve the reliability of thesecond insulation layer 140. Since thesecond insulation layer 140 is formed by alternately stacking layers having different indices of refraction, thesecond insulation layer 140 may operate as a DBR. Accordingly, when light emitted from theactive layer 117 is directed towards thefirst electrode 120, thesecond insulation layer 140 may reflect the light, thereby effectively preventing the light from being absorbed or blocked by thefirst electrode 120. ADBR layer 111 b may be formed on patternedsapphire substrate regions 111 a of thesubstrate 111. - In another embodiment, an insulation layer having a DBR structure is also formed under a
second electrode 130, excluding a portion contacting theupper semiconductor layer 117. In another embodiment, an insulation layer having a DBR structure is also formed on an exposed portion of thelower semiconductor layer 113, in order to improve the extraction of light reflected by thesecond insulation layer 140. In a further embodiment, alower DBR layer 111 c may be formed on a bottom side of thesubstrate 111, as shown inFIG. 6 . - The
first electrode 120 includes afirst electrode pad 121 formed on theupper semiconductor layer 117. Thefirst electrode 120 includes: aninclined extension 122 that extends from thefirst electrode pad 121 to the exposed portion of thelower semiconductor layer 113; and alower extension 123 that extends across the exposed portion of thelower semiconductor layer 113, along a first side of thesubstrate 111. Thefirst electrode pad 121, theinclined extension 122 and thelower extension 123 may be formed of the same material, using the same process. For example, if the lower semiconductor layer is an N-type semiconductor layer, thefirst electrode 120 may be formed of Ti/Al, using a lift-off process. The first and second insulation layers 119, 140 are interposed between thefirst electrode 120 and the mesa structure. - Further, the
second electrode 130 is formed on another portion of theupper semiconductor layer 117. Thesecond electrode 130 includes asecond electrode pad 131 positioned near a corner of thesubstrate 111, on theupper semiconductor layer 117. Thesecond electrode 130 also includes afirst extension 132 and asecond extension 133 that extend in different directions across theupper semiconductor layer 117. The first andsecond extensions second electrode pad 131, along adjacent sides of thesubstrate 111. Thesecond electrode pad 131 and theextensions - A transparent electrode layer (not shown) may be formed on the
upper semiconductor layer 117, under thefirst insulation layer 119. Generally, the transparent electrode layer is formed of indium tin oxide (ITO) or Ni/Au. In addition, the transparent electrode layer may lower contact resistance, through ohmic contact with theupper semiconductor layer 117. On the other hand, thesecond electrode 130 generally is not transparent and does not form substantial ohmic contact with theupper semiconductor layer 117. A portion of thesecond electrode 130 directly contacts theupper semiconductor layer 117, and another portion of thesecond electrode 131 directly contacts the transparent electrode layer. Consequently, thesecond electrode 130 directly contacts theupper semiconductor layer 117, thereby preventing electric current from flowing under thesecond electrode 130. Therefore, the light is not generated in a portion of theactive layer 115 that is covered by thesecond electrode 130. However, light is generated in areas where the active layer is covered by the transparent electrode layer. With this structure, it is possible to minimize the absorption of light emitted from theactive layer 115, by thesecond electrode 131. - An improvement in the light emitting area of the light emitting diode of
FIG. 4 , will be shown by a comparison with the light emitting diode ofFIG. 2 . InFIGS. 2 and 4 , it can be seen that there is a great difference between the conventional light emitting diode and the present embodiment, in terms of the reduction in light emitting area by thelower electrode 21 and thefirst electrode 120. Namely, in the light emitting diode ofFIG. 2 , a portion of theactive layer 15 is removed during the formation of thelower electrode 21, by mesa etching. On the contrary, in the light emitting diode ofFIG. 4 , since thefirst electrode pad 121 is formed above theupper semiconductor layer 117, with the first and second insulation layers 119, 140 interposed there between, theactive layer 115 remains unetched, where covered. Accordingly, the present exemplary light emitting diode provides an effective solution of the problem of the related art, in which the light emitting area is reduced, due to the formation of theelectrode 21. - In addition, as can be seen from
FIG. 4 , thesecond insulation layer 140 is formed under thefirst electrode 120 and reflects light away from thefirst electrode 120. As such, thesecond insulation layer 140 increases light extraction efficiency. -
FIG. 7 is a plan view of a light emitting diode, according to a further exemplary embodiment,FIG. 8 is a cross-sectional view taken along line B-B′ ofFIG. 7 , andFIG. 9 is a cross-sectional view taken along line C-C′ ofFIG. 7 . The embodiment shown inFIGS. 7 , 8, and 9 is different from the embodiment ofFIG. 4 andFIG. 5 , in terms of the number, positions and shapes of first and second electrodes, and the shapes of extensions of the first and second electrodes. - Referring to
FIGS. 7 , 8, and 9, the light emitting diode includes alower semiconductor layer 213, which is formed on asubstrate 211. Thesubstrate 211 is not limited to a particular material, and may be a sapphire substrate, for example. - An
upper semiconductor layer 217 is formed to cover thelower semiconductor layer 213. Theupper semiconductor layer 217 is smaller than thelower semiconductor layer 213, such that edge regions of thelower semiconductor layer 213 are not covered by theupper semiconductor layer 217. Anactive layer 215 is interposed between thelower semiconductor layer 213 and theupper semiconductor layer 217. Theactive layer 215 is larger than theupper semiconductor layer 217, but is smaller than thelower semiconductor layer 213, such that edge regions of thelower semiconductor layer 213 are not covered by theactive layer 215. - The
lower semiconductor layer 213,active layer 215, andupper semiconductor layer 217 may be formed of, for example, a nitride-based compound semiconductor material, such as (B, Al, In, or Ga)N. Theactive layer 215 emits light at desired frequencies, for example, UV or blue light. Thelower semiconductor layer 213 and theupper semiconductor layer 217 are formed of materials having a greater band gap than that of theactive layer 215. - The
lower semiconductor layer 213 and/or theupper semiconductor layer 217 may have a single layer structure or may have a multilayer structure. Further, theactive layer 215 may have a single quantum well structure or a multi-quantum well structure. The light emitting diode may further include a buffer layer (not shown) disposed between thesubstrate 211 and thelower semiconductor layer 213. The buffer layer is selected to relieve lattice mismatches between thesubstrate 211 and thelower semiconductor layer 213. - The semiconductor layers 213, 215, 217 may be in the form of a semiconductor stack formed by MOCVD or MBE. The semiconductor stack may be subjected to mesa-etching, to form a mesa structure, by exposing regions of the
lower semiconductor layer 213, via photolithography and etching processes. Here, the mesa structure may include inclined sidewalls. The sidewalls may have a degree of inclination in the range of 20˜80 degrees, and preferably in the range of 30˜60 degrees, with respect to the plane of thesubstrate 211. The inclined sidewalls may enhance workability and reliability, when forming aDBR layer 240 and aninclined extension part 222 of thefirst electrodes 220, as described below. In addition, the inclined sidewalls provide for a increased light emitting area. - An insulation layer is formed on the
upper semiconductor layer 217. The insulation layer may include afirst insulation layer 219 and asecond insulation layer 240. Thefirst insulation layer 219 covers theupper semiconductor layer 217 and the inclined sidewalls. Thefirst insulation layer 219 may be formed of, for example, SiO2, Si3N4, Nb2O5, TiO2, etc. - The
second insulation layer 240 may be formed on a portion of theupper semiconductor layer 217, where thefirst electrodes 220 will be formed. Thesecond insulation layer 240 may also cover adjacent portions of the sidewalls where thefirst electrodes 220 will be formed. - The
second insulation layer 240 may have, for example, a DBR structure. Thesecond insulation layer 240 is similar to thesecond insulation layer 140. As such, a detailed description of the structure/formation of thesecond insulation layer 240 is omitted. - Since the
second insulation layer 240 operates as a DBR, thesecond insulation layer 240 reflects light emitted from theactive layer 217, away from thefirst electrodes 220. As such, thesecond insulation layer 240 prevents the light from being absorbed or blocked by thefirst electrodes 220. - Further, a
DBR layer 211 b may be formed onPSS regions 211 a of thesubstrate 211. In yet another embodiment, an insulation layer having a DBR structure is also formed under thesecond electrode 230, excluding portions thereof that contact theupper semiconductor layer 217, in addition to thesecond insulation layer 240 formed under thefirst electrodes 220. In yet another embodiment, an insulation layer having a DBR structure is also formed on an exposed portion of thelower semiconductor layer 213, in order to improve the extraction of light reflected by thesecond insulation layer 240. In yet another embodiment, alower insulation layer 211 c including a DBR structure may be formed on a bottom side of thesubstrate 211, as shown inFIG. 10 . - The
first electrodes 220 are formed in a first region, on theupper semiconductor layer 217. The first and second insulation layers 219, 240 are interposed between thefirst electrodes 220 and theupper semiconductor layer 217. Thefirst electrodes 220 each include afirst electrode pad 221 aninclined extension 222 that extends from thefirst electrode pads 221, and anextension 223 that extends from theinclined extension 222, to an exposed portion of thelower semiconductor layer 213. Thefirst electrode pads 221 and theextensions lower semiconductor layer 213 is an N-type semiconductor layer, thefirst electrodes 220 may be formed of Ti/Al, using a lift-off process. - Further, the
second electrode 230 is on theupper semiconductor layer 217. Thesecond electrode 230 includessecond electrode pads 231 positioned near an edge of theupper semiconductor layer 217, opposite to an edge of theupper semiconductor layer 217 where thefirst electrode pads 221 are disposed. Thesecond electrode 230 further includesextensions 233 that extend from thesecond electrode pads 231, to an opposing side of theupper semiconductor layer 217. Thesecond electrode pads 231 and theextensions 233 may be formed of the same material, using the same process. - A
transparent electrode layer 218 may be formed on theupper semiconductor layer 217, before forming thefirst insulation layer 219, as shown inFIG. 11 . Generally, thetransparent electrode layer 218 is formed of indium tin oxide (ITO) or Ni/Au. In addition, thetransparent electrode layer 218 may lower a contact resistance, through ohmic contact with theupper semiconductor layer 217. On the other hand, thesecond electrode 230 is generally not transparent and does not form substantial ohmic contact with theupper semiconductor layer 217. A portion of thesecond electrode 230 contacts theupper semiconductor layer 217, and another portion of thesecond electrode 230 contacts the transparent electrode layer. Consequently, thesecond electrode 230 directly contacts theupper semiconductor layer 217, thereby preventing electric current from flowing under thesecond electrode 230. Therefore, light is not generated in portions of theactive layer 215 that are disposed under thesecond electrode 230, but is generated in portions of theactive layer 215 covered by the transparent electrode layer . With this structure, it is possible to minimize the absorption of light emitted from the active layer, by thesecond electrode 230. - An improvement in the light emitting area of the light emitting diode of
FIG. 7 will be described through a comparison with the light emitting diode ofFIG. 2 . Namely, in the light emitting diode ofFIG. 2 , portions of theactive layer 15 are removed during mesa etching, to form thelower electrode 21. Thus, when thelower electrodes 21 are formed, which correspond to the structure as shown inFIG. 7 , the light emitting area can be further reduced by the mesa etching. On the contrary, in the light emitting diode ofFIG. 7 , thefirst electrodes 220 are formed above theupper semiconductor layer 217. The first and second insulation layers 219, 240 are interposed between thefirst electrodes 220 and theupper semiconductor layer 217. Thus, theactive layer 215 remains unetched. As such, the light emitting diode ofFIG. 7 provides an effective solution to the problem of the related art, in which the light emitting area is reduced, due to the formation of the electrodes. - In addition, as can be seen from
FIG. 7 andFIG. 9 , thesecond insulation layer 240 reflects light that would otherwise be absorbed or blocked by thefirst electrodes 220. As such, according to one embodiment, an electrode including an electrode pad and an extension is formed above an upper semiconductor layer, with an insulation layer interposed between the electrode and the upper semiconductor layer. Consequently, an area of the semiconductor layer removed by mesa-etching used to form the electrode is reduced, thereby preventing a reduction in light emitting area. - Although aspects of the invention have been illustrated with reference to some exemplary embodiments, in conjunction with the drawings, it will be apparent to those skilled in the art that various modifications and changes can be made in the exemplary embodiments, without departing from the spirit and scope of the invention. Therefore, it should be understood that the exemplary embodiments are provided by way of illustration only and are given to provide complete disclosure of the invention and to provide thorough understanding of the invention to those skilled in the art. Thus, it is intended that the invention covers modifications to the disclosed exemplary embodiments that come within the scope of the appended claims and their equivalents.
- For example, in the embodiments of the invention, the insulation layer of the DBR structure is formed by alternately stacking two or more insulation layers having different indices of refraction such that the outermost insulation layers are formed of the Si compound, that is, SiO2, to enhance reliability of the DBR structure. However, it should be understood that this feature may also be applied to all insulation layers set forth herein.
Claims (16)
1. A light emitting diode, comprising:
a substrate;
a lower semiconductor layer disposed on the substrate;
an upper semiconductor layer disposed on the lower semiconductor layer, such than a portion of the lower semiconductor layer is exposed;
a first electrode disposed on the upper semiconductor layer and the exposed portion of the lower semiconductor layer, to supply electric current to the lower semiconductor layer;
a first insulation layer disposed between the first electrode and the upper semiconductor layer; and
a second electrode formed on the upper semiconductor layer, to supply electric current to the upper semiconductor layer.
2. The light emitting diode of claim 1 , wherein the first insulation layer directly contacts surfaces of the upper semiconductor layer.
3. The light emitting diode of claim 1 , further comprising: a second insulation layer having a distributed Bragg reflector (DBR) structure, disposed between the first electrode and the first insulation layer, the second insulation layer contacting the exposed portion of the lower semiconductor layer.
4. The light emitting diode of claim 1 , further comprising: a second insulation layer having a distributed Bragg reflector (DBR) structure, disposed under the second electrode.
5. The light emitting diode of claim 1 , wherein the second electrode comprises:
a second electrode pad disposed on the upper semiconductor layer; and
a second extension that extends from the second electrode pad, across the upper semiconductor layer.
6. The light emitting diode of claim 1 , further comprising a lower insulation layer having a distributed Bragg reflector (DBR) structure, disposed on the substrate.
7. The light emitting diode of claim 6 , wherein the lower insulation layer is disposed on process-induced strain silicon (PSS) regions of the substrate.
8. The light emitting diode of claim 6 , wherein the lower insulation layer is disposed on the bottom surface of the substrate.
9. The light emitting diode of claim 1 , further comprising a transparent electrode layer disposed on the upper semiconductor layer.
10. The light emitting diode of claim 1 , wherein the first insulation layer comprises:
first layers comprising silicon, having a first index of refraction; and
second layers having a second index of refraction that is different from the first index of refraction,
wherein the first layers and the second layers are alternately stacked upon one another, starting and ending with ones of the first layers.
11. The light emitting diode of claim 3 , wherein the second insulation layer comprises:
first layers comprising silicon, having a first index of refraction; and
second layers having a second index of refraction that is different from the first index of refraction, wherein,
the first layers and the second layers are alternately stacked upon one another, starting and ending with ones of the first layers.
12. The light emitting diode of claim 4 , wherein the second insulation layer comprises:
first layers comprising silicon, having a first index of refraction; and
second layers having a second index of refraction that is different from the first index of refraction, wherein,
the first layers and the second layers are alternately stacked upon one another, starting and ending with ones of the first layers.
13. The light emitting diode of claim 6 , wherein the lower insulation layer comprises:
first layers comprising silicon, having a first index of refraction; and
second layers having a second index of refraction that is different from the first index of refraction, wherein,
the first layers and the second layers are alternately stacked upon one another, starting and ending with ones of the first layers.
14. A light emitting diode, comprising:
a substrate;
a light emitting unit disposed on the substrate, comprising:
a lower semiconductor layer disposed on the substrate;
an active layer disposed on the lower semiconductor layer, such than a portion of the lower semiconductor layer is exposed;
an upper semiconductor layer disposed on the active layer;
a first electrode to supply electric current to the lower semiconductor layer, comprising:
a first electrode pad disposed on the upper semiconductor layer;
a lower extension that extends along the exposed portion of the lower semiconductor layer; and
an inclined extension that extends from the first electrode pad to the lower extension, along edges of the upper semiconductor layer, active layer, and lower semiconductor layer;
a first insulation layer disposed between the first electrode pad and the inclined extension, and the light emitting unit;
a reflective second insulation layer disposed between the first insulation layer and the first electrode;
a second electrode formed on the upper semiconductor layer, to supply electric current to the upper semiconductor layer.
15. The light emitting diode of claim 14 , wherein the second insulation comprises layers having different indices of reflection that are stacked on one another, such that the second insulation layer has a distributed Bragg reflector (DBR) structure, wherein top and bottom ones of the stacked layers comprise silicon.
16. The light emitting diode of claim 14 , wherein the exposed portion of the lower semiconductor layer is thinner than portions of the lower semiconductor layer upon which the active layer is disposed.