US20140255646A1 - Forming Composite Features Using Steered Discontinuous Fiber Pre-Preg - Google Patents

Forming Composite Features Using Steered Discontinuous Fiber Pre-Preg Download PDF

Info

Publication number
US20140255646A1
US20140255646A1 US13/789,965 US201313789965A US2014255646A1 US 20140255646 A1 US20140255646 A1 US 20140255646A1 US 201313789965 A US201313789965 A US 201313789965A US 2014255646 A1 US2014255646 A1 US 2014255646A1
Authority
US
United States
Prior art keywords
segments
substrate
preg
resin infused
infused fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/789,965
Other languages
English (en)
Inventor
Kenneth H. Griess
Derek Paul Vetter
Michael Jeffrey Graves
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Boeing Co
Original Assignee
Boeing Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Boeing Co filed Critical Boeing Co
Priority to US13/789,965 priority Critical patent/US20140255646A1/en
Assigned to THE BOEING COMPANY reassignment THE BOEING COMPANY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: GRAVES, MICHAEL JEFFREY, GRIESS, KENNETH H., VETTER, DEREK PAUL
Priority to EP14707580.8A priority patent/EP2964451B1/en
Priority to CA2898224A priority patent/CA2898224C/en
Priority to KR1020157022015A priority patent/KR102119435B1/ko
Priority to CN201911265573.6A priority patent/CN110920093A/zh
Priority to MX2015010813A priority patent/MX388975B/es
Priority to CN201480009859.7A priority patent/CN105073392A/zh
Priority to BR112015019511A priority patent/BR112015019511A2/pt
Priority to CA3004233A priority patent/CA3004233C/en
Priority to JP2015561367A priority patent/JP6453250B2/ja
Priority to PCT/US2014/016533 priority patent/WO2014137568A2/en
Publication of US20140255646A1 publication Critical patent/US20140255646A1/en
Priority to US15/908,793 priority patent/US11007726B2/en
Priority to JP2018230731A priority patent/JP6612958B2/ja
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/28—Shaping operations therefor
    • B29C70/54—Component parts, details or accessories; Auxiliary operations, e.g. feeding or storage of prepregs or SMC after impregnation or during ageing
    • B29C70/545—Perforating, cutting or machining during or after moulding
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/02—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising combinations of reinforcements, e.g. non-specified reinforcements, fibrous reinforcing inserts and fillers, e.g. particulate fillers, incorporated in matrix material, forming one or more layers and with or without non-reinforced or non-filled layers
    • B29C70/021—Combinations of fibrous reinforcement and non-fibrous material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/06—Fibrous reinforcements only
    • B29C70/10—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres
    • B29C70/12—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres using fibres of short length, e.g. in the form of a mat
    • B29C70/14—Fibrous reinforcements only characterised by the structure of fibrous reinforcements, e.g. hollow fibres using fibres of short length, e.g. in the form of a mat oriented
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/22—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed
    • B32B5/32—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed at least two layers being foamed and next to each other
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C2793/00—Shaping techniques involving a cutting or machining operation
    • B29C2793/0072—Shaping techniques involving a cutting or machining operation combined with rearranging and joining the cut parts
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C2793/00—Shaping techniques involving a cutting or machining operation
    • B29C2793/0081—Shaping techniques involving a cutting or machining operation before shaping
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/28—Shaping operations therefor
    • B29C70/30—Shaping by lay-up, i.e. applying fibres, tape or broadsheet on a mould, former or core; Shaping by spray-up, i.e. spraying of fibres on a mould, former or core
    • B29C70/38—Automated lay-up, e.g. using robots, laying filaments according to predetermined patterns
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
    • B29K2105/08—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of continuous length, e.g. cords, rovings, mats, fabrics, strands or yarns
    • B29K2105/0872—Prepregs
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
    • B29K2105/12—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of short lengths, e.g. chopped filaments, staple fibres or bristles
    • B29K2105/14—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of short lengths, e.g. chopped filaments, staple fibres or bristles oriented
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/26—Scrap or recycled material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T156/00—Adhesive bonding and miscellaneous chemical manufacture
    • Y10T156/12—Surface bonding means and/or assembly means with cutting, punching, piercing, severing or tearing
    • Y10T156/1317—Means feeding plural workpieces to be joined
    • Y10T156/1322—Severing before bonding or assembling of parts
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24132—Structurally defined web or sheet [e.g., overall dimension, etc.] including grain, strips, or filamentary elements in different layers or components parallel

Definitions

  • the present disclosure generally relates to fabrication of composite laminate structures using fiber pre-preg, and deals more particularly with a method and apparatus for forming composite structural features by steering discontinuous fiber pre-preg onto a substrate with desired fiber orientations.
  • the strength, stiffness and load transfer characteristics of a composite laminate structure may be optimized through control of fiber orientation during the layup process.
  • Conventional composite laminates may be laid up using pre-preg tapes, tows or broad goods, employing either automated fiber placement equipment or hand placement techniques to layup the material.
  • the resulting composite structure exhibits substantially consistent structural properties throughout. In some cases, however, it may be necessary or desirable to control the thickness and/or fiber orientation in local areas of a composite laminate in order to optimize its structural properties and/or account for higher local stresses.
  • the ability to control local thickness/fiber orientation is limited using current fabrication processes. For example, automated fiber placement equipment may be used to steer continuous tows onto the substrate, but the radius of curvature that can be achieved is limited, thus making control of fiber orientation difficult in local areas having tight contours. Achieving close control over thickness and/or fiber orientation in local areas of laminate may also be costly and time-consuming.
  • the disclosed embodiments provide a method and apparatus for fabricating composite features of laminates which provide increased control over feature thickness and/or fiber orientation in local areas of a laminate structure, such as in tight contours and/or within transitions in laminate thickness.
  • Composite material may be laid up such that fiber orientations are substantially continuously aligned with load vectors in selected local areas of a laminate, thereby optimizing the laminate's structural properties.
  • the amount of composite material required to provide local areas of a laminate structure with desired structural properties may be reduced by forming the composite features using scrap pre-preg derived from other products/processes. Recycling of scrap pre-preg for use in the disclosed method may reduce material costs, thus optimizing the buy-to-fly ratio (the ratio of materials weight procured to the weight of the finished product) for aircraft applications of the embodiments.
  • the embodiments allow composite material in the form of discontinuous fiber pre-preg to be “steered” onto a substrate in order to achieve desired fiber orientations.
  • discontinuous fiber pre-preg allows greater control over laminate thickness variations in local areas of the laminate, while allowing local tailoring of laminate thickness in three dimensions to provide smooth transitions between differing features of a laminate structure. Moreover, the use of discontinuous fiber pre-preg permits the formation of doublers or other pad-ups having tight contours and/or tapered edges to achieve smooth load transitions within a structure. Also, the use of discontinuous fiber pre-preg may result in composite features having a higher fiber content.
  • a method of forming a composite feature having discontinuous reinforcement fibers.
  • the method comprises producing a plurality of resin infused fiber segments each having unidirectional reinforcing fibers, placing the resin infused fiber segments on a substrate, and arranging the resin infused fiber segments such that the reinforcing fibers of resin infused fiber segments placed on the substrate are substantially aligned relative to a desired reference orientation.
  • Producing the resin infused fiber segments includes chopping scrap fiber pre-preg into individual pieces, which may be performed by breaking or splitting fiber pre-preg along and between the reinforcing fibers into individual pieces.
  • Placing the resin infused fiber segments on the substrate includes moving an applicator over the substrate, and dispensing the resin infused fiber segments from the applicator onto the substrate as the applicator moves over the substrate.
  • Arranging the resin infused fiber segments includes aligning the resin infused fiber segments as they are being dispensed from the applicator onto the substrate.
  • Producing the resin infused fiber segments is performed by drawing continuous fiber pre-preg tape from the applicator, and chopping the pre-preg tape into the resin infused fiber segments as the resin infused fiber segments are being dispensed from the applicator onto the substrate.
  • Dispensing the resin infused segments from the applicator includes dispensing a bandwidth of the resin infused fiber segments onto the substrate.
  • Placing the resin infused fiber segments on the substrate is formed of by streaming the resin infused fiber segments from an applicator head onto the substrate. Streaming the resin infused fiber segments is performed by introducing the resin infused fiber segments into an airstream, and using the airstream to project the resin infused fiber segments onto the substrate. The resin infused fiber segments is performed after the resin infused fiber segments have been placed on the substrate.
  • the method may further comprise applying resin to the substrate before the resin infused segments are placed on the substrate.
  • the method may also comprise applying a resin on at least one end of each of the resin infused fiber segments before they are placed on the substrate.
  • a method of laying up composite material on a substrate the method comprises placing individual chopped fiber pre-preg segments on the substrate, and controlling the orientation of the pre-preg segments on the substrate. Placing the pre-preg segments on the substrate is performed by moving an applicator head over the substrate along a desired path, and dispensing the pre-preg segments from the applicator head onto the substrate as the applicator moves over the substrate. Controlling the orientation of the pre-preg segments is performed by aligning the pre-preg segments being dispensed from the applicator head. Controlling the orientation of the pre-preg segments includes changing the orientation of the pre-preg segments after the pre-preg segments have been placed on the substrate.
  • a composite laminate structure layup comprising a plurality of layers of composite material, each of the layers including a plurality individual chopped fiber pre-preg segments having aligned fiber orientations.
  • the fiber orientations of the chopped fiber pre-preg segments are substantially aligned with a non-linear load path through the composite laminate structure.
  • Each of the individual chopped fiber pre-preg segments may have an aspect ratio of approximately 6:1.
  • the plurality of layers of composite material have a tailored cross-sectional shape and is contoured along a length of the layup.
  • apparatus for laying up a composite structure.
  • the apparatus comprises an applicator adapted to move over the surface of a substrate, and dispense at least one stream of substantially aligned chopped, resin infused fiber segments onto the surface of a substrate.
  • the apparatus may also comprise a computer controlled manipulator for moving the applicator along a preselected path over the substrate.
  • the applicator includes a supply of continuous resin infused fiber, and a chopper for chopping the continuous resin infused fiber into individual resin infused fiber segments.
  • Applicator may further include an airstream generator for carrying the resin infused fiber segments from the applicator onto the substrate.
  • the applicator may be adapted to simultaneously dispense multiple streams of substantially aligned chopped, resin infused fiber segments onto the substrate.
  • FIG. 1 is an illustration of a combined block and diagrammatic of discontinuous fiber pre-preg being applied to a substrate along a tight contour.
  • FIG. 1A is an illustration of a plan view showing one shape of the pre-preg segments.
  • FIG. 1B is an illustration of a plan view showing another shape of the pre-preg segments.
  • FIG. 1C is an illustration of a plan view showing a further shape of the pre-preg segments.
  • FIG. 2 is an illustration of a perspective view of a barrel section of an aircraft fuselage showing loads applied to the fuselage.
  • FIG. 3 is an illustration of a diagrammatic view of one of the window openings in the fuselage of FIG. 2 , also showing load vectors around the window opening.
  • FIG. 4 is an illustration of an elevational view of one of the window openings in the fuselage shown in FIG. 2 , also showing a surrounding doubler formed of discontinuous fiber pre-preg.
  • FIG. 5 is an illustration of the area designated as “FIG. 5 ” in FIG. 4 .
  • FIG. 6 is an illustration of a sectional view taken along the line 6 - 6 in FIG. 5 .
  • FIG. 7 is an illustration of a cross-sectional view of a composite structure showing a discontinuous interlaminar fiber filler and transition in a gap within the thickness of a composite laminate structure.
  • FIG. 8 is an illustration of a flow diagram of a method of laying up interlaminar composite features using the disclosed method.
  • FIG. 9 is an illustration of a perspective view of a portion of an aircraft fuselage frame section, broken lines indicating areas where interlaminar structural features may be formed using the disclosed method.
  • FIG. 10 is an illustration of a sectional view taken along the line 10 - 10 in FIG. 9 showing an interlaminar structural feature formed using the disclosed method.
  • FIG. 11 is an illustration of a sectional view taken along the line 11 - 11 in FIG. 9 .
  • FIG. 12 is an illustration of a combined block and diagrammatic view of a system for placing discontinuous fiber pre-preg.
  • FIG. 13 is an illustration of a combined block and diagrammatic view of an alternate embodiment of the system for placing discontinuous fiber pre-preg.
  • FIG. 14 is an illustration of a flow diagram of a method of laying up composite laminates using discontinuous fiber pre-preg derived from pre-preg scrap.
  • FIG. 15 is an illustration of a plan view showing various shapes of pre-preg scrap that may be used in the method shown in FIG. 14 .
  • FIG. 16 is an illustration of a plan view showing randomly oriented, fiber pre-preg segments formed by chopping the scrap shown in FIG. 15 .
  • FIG. 17 is an illustration of a plan view similar to FIG. 16 , but showing the fiber orientations of the fiber pre-preg segments having been aligned in preparation for application to a substrate.
  • FIG. 18 is an illustration of a diagrammatic view of a method of converting fiber pre-preg scrap into segments and readying it for application to a substrate.
  • FIG. 19A is an illustration of a diagrammatic side view of an applicator applying resin onto a substrate.
  • FIG. 19B is an illustration of a plan view of the resin applied to the substrate shown in FIG. 19A .
  • FIG. 20A is an illustration of a diagrammatic side view showing chopped fiber pre-preg segments being applied over the resin shown in FIG. 19B .
  • FIG. 20B is an illustration of a plan view of the substrate in FIG. 20A , showing the random orientation of the chopped fiber pre-preg segments.
  • FIG. 21A is an illustration of a diagrammatic side view showing the fiber segment aligner aligning the chopped fiber pre-preg segments.
  • FIG. 21B is an illustration of a plan view showing the chopped fiber pre-preg segments of FIG. 21A having been aligned by the fiber segment aligner.
  • FIG. 22A is an illustration of a side view of a chopped fiber pre-preg segment with a drop of resin having been placed on one end thereof.
  • FIG. 22B is an illustration of a bottom view of the chopped fiber pre-preg segment shown in FIG. 22A .
  • FIG. 23A is an illustration of a side view of the chopped fiber pre-preg segment of FIG. 22A having been placed on a substrate, but prior to rotation thereof.
  • FIG. 23B is an illustration of a plan view of the chopped fiber pre-preg segment shown in FIG. 23A .
  • FIG. 24A is an illustration of a side view, similar to FIG. 23A , but after the chopped fiber pre-preg segment has been rotated.
  • FIG. 24B is an illustration similar to FIG. 23B , but showing the fiber pre-preg segment having been rotated, the position of the chopped fiber pre-preg segment before rotation being indicated in the phantom.
  • FIG. 25 is an illustration of a flow diagram of aircraft production and service methodology.
  • FIG. 26 is illustration of a block diagram of an aircraft.
  • a composite feature 30 comprises discontinuous, resin infused fibers which may be in the form of chopped fiber pre-preg segments 32 having unidirectional reinforcing fibers 25 .
  • Each of the fiber pre-preg segments 32 is elongate, having a length L that is greater than its width W.
  • Each of the fiber pre-preg segments 32 may have an aspect ratio (L/W) in the range of approximately 6:1, however this particular ratio is merely illustrative.
  • the fiber pre-preg segments 32 may have other aspect ratios that are selected and/or optimized for the application, including structural requirements and the equipment used to position or place the segments 32 .
  • the fiber pre-preg segments 32 may have a length that is equal to or less than its width.
  • the illustrative examples of composite features 30 that will be discussed below utilize unidirectional fiber pre-preg.
  • the principals of the disclosed embodiments may be employed to form composite features 30 using other types of pre-preg segments 32 , including resins that are reinforced with fibers having multiple fiber orientations, such as, for example and without limitation, bidirectional fibers that are woven (cloth pre-preg) or otherwise combined in a manner to suit the particular application.
  • the disclosed embodiments are particularly well-suited for forming any of a variety of interlaminate features 30 , i.e. features 30 that are located between two continuous plies. However, the embodiments may also be employed to form composite features 30 that are partially or fully exposed, such as external features. In some applications, it may be useful or desirable to employ pre-preg segments 32 having fibers of differing lengths. Differing fiber lengths in a segment 32 may be achieved by, for example and without limitation, shaping the segment 32 , such as by chopping, in a manner that results in some of the fibers being longer or shorter than other fibers. Three illustrative examples of pre-preg segments 32 having shapes configured to produce reinforcing fibers of differing lengths are respectively shown in FIGS.
  • the reinforcing fibers 25 may comprise high-strength fibers, such as glass or carbon fibers, graphite, aromatic polyamide fiber, fiberglass, or another suitable reinforcement material.
  • the resin matrix in which the fibers 25 are held may comprise thermoplastic or thermoset polymeric resins.
  • Exemplary thermosetting resins may include allyls, alkyd polyesters, bismaleimides (BMI), epoxies, phenolic resins, polyesters, polyurethanes (PUR), polyurea-formaldehyde, cyanate ester, and vinyl ester resin.
  • thermoplastic resins may include liquid-crystal polymers (LCP); fluoroplastics, including polytetrafluoroethylene (PTFE), fluorinated ethylene propylene (FEP), perfluoroalkoxy resin (PFA), polychlorotrifluoroethylene (PCTFE), and polytetrafluoroethylene-perfluoromethylvinylether (MFA); ketone-based resins, including polyetheretherketone; polyamides such as nylon-6/6, 30% glass fiber; polyethersulfones (PES); polyamideimides (PAIS), polyethylenes (PE); polyester thermoplastics, including polybutylene terephthalate (PBT), polyethylene terephthalate (PET), and poly(phenylene terephthalates); polysulfones (PSU); or poly(phenylene sulfides) (PPS).
  • LCP liquid-crystal polymers
  • fluoroplastics including polytetrafluoroethylene (PTFE), fluorinated
  • pre-preg means fibers that have been impregnated with an uncured or partially cured resin which acts as a matrix to hold the fibers and which is flexible enough to be formed into a desired shape.
  • the resin is then “cured,” e.g., by the application of heat in an oven or an autoclave, to harden the resin into a strong, rigid, fiber-reinforced structure.
  • pre-preg segments 32 having unidirectional fibers the fibers extend substantially parallel to each other and, for purposes of this description, have a 0° axial orientation, referred to hereinafter as the fiber direction or orientation of the pre-preg segments 32 .
  • pre-preg segments 32 are used that have multiple sets of fiber orientations, typically the fiber orientations one or more of these sets will be used in aligning and orienting the segments 32 as they are being placed on a substrate 34 during the layup process.
  • the fiber pre-preg segments 32 may be laid up on a substrate 34 that may comprise a tool or an underlying continuous composite ply, using a suitable applicator system 38 which “steers” the fiber pre-preg segments 32 onto the substrate 34 .
  • the applicator system dispenses, places and aligns the fiber pre-preg segments 32 on the substrate 34 such that the direction of the fibers 25 in each of the fiber pre-preg segments 32 is substantially aligned in a desired orientation. For example, in the example shown in FIG.
  • the fiber orientations of the fiber pre-preg segments 32 are substantially aligned with a curved center axis 36 forming a relatively tight contour 35 , with the fiber orientations of the segments 32 changing in direction along the contour 35 to remain substantially aligned in a desired orientation relative to the center axis 36 .
  • the degree to which a chosen set of the fiber orientations of the pre-preg segments 32 are aligned with respect to a desired orientation, direction, or axis will depend upon the application. In some applications, the orientations of the pre-preg segments 32 may vary to some extent at one or more locations of a composite feature 30 . In fact, in some applications, some degree of variation of pre-preg segment orientation relative to a desired, reference orientation may be useful or desirable within a specified tolerance of variation.
  • the applicator system 38 dispenses a serial stream 40 of pre-aligned fiber pre-preg segments 32 , which are then steered and placed onto substrate 34 by moving an applicator head (not shown) forming part of the applicator system 38 in a desired path over the substrate 34 , which in the illustrated example, is along, or parallel to the center axis 36 . Repeated passes of the applicator head over the substrate result in successive layers or plies being laid up, each comprising aligned fiber pre-preg segments 32 .
  • the composite feature 30 comprises multiple layers or plies of discontinuous fibers infused with resin.
  • the disclosed embodiments may also be employed to fill voids or gaps (not shown) in composite structures as well as to form transitions (not shown) in laminate thicknesses by steering resin infused, discontinuous fibers such as chopped fiber pre-preg onto a substrate.
  • void or gap fillers as well as features such as bulk doubler areas that include transitions in laminate thicknesses will typically be interlaminar features (located between continuous plies), however in some applications as previously mentioned, it is possible that they may be exposed, external features.
  • FIGS. 2-6 illustrate use of the disclosed method and apparatus in connection with the fabrication of an aircraft fuselage ( FIG. 2 ).
  • the fuselage 44 comprises an outer skin 46 supported on internal framework 45 which includes barrel shaped frames 65 and longitudinally extending stringers 47 .
  • the skin 46 may include one or more discontinuities, such as window openings 42 , cargo doors (not shown), etc.
  • Fuselage pressure 49 results in a hoop load 50 being applied to the circumference 55 of the fuselage 44 , passing through the windows 48 or other openings in the skin 46 .
  • the crown 54 of the fuselage 44 is placed under tension 75
  • the belly of the fuselage 44 is placed under compression 77 , resulting in shear loads 52 ( FIG.
  • the disclosed method and apparatus may be employed to layup composite doublers forming an interlaminar pad-up feature 30 around the window openings 42 that stiffens and strengthens the fuselage 44 around the window opening 42 , enabling the skin 46 to transfer the required loads through the corners 58 .
  • the pad-up feature 30 is formed of a discontinuous fiber pre-preg comprising a plurality of steered fiber pre-preg segments 32 similar to the fiber pre-preg segments 32 previously discussed in connection with FIG. 1 .
  • the fiber pre-preg segments 32 are steered as they are being placed on a tool (not shown) or underlying ply (not shown) so that their respective fiber orientations are substantially aligned with structural load paths, which in this example, is along or parallel to a contoured axis 36 at the corners 58 .
  • the number of layers or plies of fiber pre-preg segments 32 that are steered onto the substrate will vary with the application, and the desired thickness of the pad-up feature 30 .
  • the pad-up feature 30 shown in FIGS. 4 and 5 may be laid up on one or more underlying full plies 60 and may be covered by one or more overlying full plies 62 .
  • the pad-up feature 30 comprises a double taper 64 that is formed by laying down layers of the fiber pre-preg segments 32 that are successively narrower in width “W”. Tapering of the pad-up feature 30 allows the resulting doubler to better conform to the full plies 60 , 62 .
  • the fiber pre-preg segments 32 may be steered and layered to form cross-sectional shapes that are suitable for filling gaps or voids 82 in a composite laminate, such as gaps 82 that may be formed in transitions in the thickness of a laminate structure 85 .
  • the composite sandwich laminate structure 85 comprises a core 86 sandwiched between two composite plies 60 , 62 .
  • a gap 82 is formed as the laminate structure 85 as it transitions from the core 86 to a solid laminate 87 .
  • the gap 82 forms a structural discontinuity that may require strengthening and reinforcement in order to carry the required loads.
  • the gap 82 may be filled with layers of the fiber pre-preg segments 32 to form a discontinuous fiber pre-preg filler feature 30 , which in this example, has a single taper 84 .
  • FIG. 8 illustrates the overall steps of a method of making a discontinuous fiber composite feature by steering fiber pre-preg segments 32 onto a substrate 34 .
  • fiber pre-preg segments 32 are produced, as by, for example, chopping the fiber pre-preg to a desired dimensions and a desired aspect ratio.
  • discontinuous fiber plies are laid up by placing the fiber pre-preg segments 32 on a substrate 34 at step 70 , and at 72 , arranging the fiber pre-preg segments 32 such that the fiber orientations of the reinforcing fibers are aligned in a desired direction.
  • the fiber pre-preg segments 32 may be placed on the substrate 34 using an applicator head which may also be used to steer the fiber pre-preg segments 32 and align them along load paths through a structure.
  • FIGS. 9-11 illustrate a portion of a frame section 74 having a generally Z-shaped cross-section.
  • the frame section 74 may form a portion of a barrel shaped frame 65 such that used in the fuselage 44 shown in FIG. 1 .
  • the frame section 74 includes upper and lower, oppositely extending flanges 76 , 78 connected by a web 80 .
  • “Mousehole” openings 82 may be provided in the web 80 and flange 76 in order to provide clearance for longitudinally extending stringers 47 ( FIG. 2 ) in the fuselage 44 .
  • the disclosed method and apparatus may be employed to form discontinuous resin infused fiber features 30 selectively reinforce portions of the frame section 74 , particularly in local areas that may experience higher stresses.
  • one side of a central portion of the web 80 may be provided with a longitudinally extending, contoured, pad-up feature 30 a formed by multiple layers of discontinuous fiber pre-preg comprising fiber pre-preg segments 32 that are steered onto the web 80 as the frame section 74 is being laid up.
  • the pad-up feature 30 a varies in cross-sectional shape along its length, however in other embodiments the cross-sectional shape of the pad-up feature 30 a may be constant along its length.
  • pad-up features 30 b , 30 c comprising layers of fiber pre-preg segments 32 , such as chopped pre-preg, may be steered onto the web 80 in contoured patterns surrounding the mouseholes 82 .
  • the pad-up features 30 a , 30 b , 30 c may have any desired cross-sectional geometry selected to optimize local structural properties of the frame section 74 . Any of the pad-up features 30 b , 30 c may vary in cross-sectional size and/or shape along its length.
  • FIG. 12 illustrates one embodiment of a system 88 that may be employed to form discontinuous, resin infused fiber features 30 of the type previously described, including local features of a structure that may require strengthening, stiffening and/or reinforcement.
  • the system 88 broadly comprises an applicator head 90 that is adapted to place fiber pre-preg segments 32 , such as chopped pre-preg 32 , onto a substrate 34 , forming multiple layers or plies 96 .
  • Applicator head 90 is displaced in X, Y and Z directions over the substrate 34 by an automated manipulator 92 which may comprise, for example and without limitation, a robot.
  • the manipulator 92 as well as the applicator head 90 are operated by a programmed CNC (computer numerically controlled) controller 94 .
  • the applicator head 90 includes a pre-preg tape supply 98 which supplies unidirectional fiber pre-preg tape 100 through guides 102 to a chopper 103 .
  • the chopper 103 may comprise a conventional cutter mechanism (not shown) operated in synchronization with the movement the applicator head 90 to chop the pre-preg fiber tape 100 into fiber pre-preg segments of the desired size and shape.
  • the chopped fiber pre-preg segments 32 are fed 40 into an airstream 104 generated by airstream generators 106 on the applicator head 90 .
  • the airstream 104 propels and places the pre-aligned fiber pre-preg segments 32 through a nozzle 108 onto the substrate 34 as the applicator head 90 over the substrate 34 .
  • the pre-preg segments 32 are applied to the substrate 34 in the desired orientation as they contact and adhere to the substrate 34 . Orienting the segments 32 as they are being placed on the substrate 34 may eliminate the need to subsequently adjust the orientation of the segments 32 .
  • a heater 105 may be provided on the applicator head 90 in order to heat the pre-preg fiber segments 32 and thereby increase their tackiness. This increased tack may assist in adhering and holding the pre-preg fiber segments 32 in a desired orientation on the substrate 34 .
  • the heater 105 may comprise any of a variety of devices suitable for the application, including but not limited to a hot air blower, a conduction rod, a focused infrared heater or a laser, to name only a few.
  • the heater 105 may generally heat the entire area of the segments 32 , or may produce a focused beam (not shown), such as a laser beam, that heats only a portion of a segment 32 until it is “sticky” enough to adhere to the substrate when it is placed.
  • the applicator head 90 may move from side-to-side (in the Y direction) in order to apply a width of the chopped pre-preg segments 32 in a desired orientation, while in other embodiments, the applicator head 90 may be used to make multiple linear passes over the substrate 34 in the X direction, in order to cover a desired width of the substrate 34 with the chopped fiber pre-preg segments 32 for each layer or ply 96 . While the applicator head 90 has been illustrated with airstream generators 106 to place the fiber pre-preg segments 32 , other means such as mechanical mechanisms may be employed to dispense, place and align the fiber pre-preg segments 32 , as the applicator head 90 moves across, and steers the fiber pre-preg segments 32 onto the substrate 34 .
  • system 88 including the applicator head 90 discussed above are merely illustrative of a wide variety of equipment may be used to place and position the pre-preg segments 32 .
  • the particular form of the system 88 that is used will depend upon the application, including specific structural requirements and the layup techniques that are employed.
  • the fabrication of the pre-preg segments 32 and equipment used to place and position the segments 32 on a substrate 34 may be implemented using a single machine, or several different machines.
  • FIG. 13 illustrates an alternate embodiment of the applicator head 90 shown in FIG. 12 , in which multiple rows of individual chopped fiber pre-preg segments 32 may be simultaneously dispensed, aligned in a desired orientation and placed by the applicator head 90 to form a bandwidth 110 of segments 32 with each pass of the applicator head 90 across the substrate 34 .
  • the disclosed embodiments may be employed to layup layers or plies of discontinuous fiber pre-preg using scrap pre-preg 124 ( FIG. 15 ).
  • the scrap pre-preg 124 may be obtained from non-conforming/scrap parts or from scrap pre-preg resulting from other production processes.
  • the scrap pre-preg 124 may have any of various shapes, as shown in FIG. 15 .
  • the scrap pre-preg 124 is chopped into individual fiber pre-preg segments 32 , and following this chopping process, the segments 32 may have a random fiber orientation 126 , as shown in FIG.
  • the chopped fiber pre-preg segments are substantially aligned 128 with a desired fiber orientation as shown in FIG. 17 .
  • the aligned fiber pre-preg segments 32 are fed to an applicator.
  • the applicator is used to dispense, steer and place the fiber pre-preg segments 32 on the substrate 34 , such that fiber orientations of the fiber pre-preg segments 32 are aligned in a desired direction.
  • scrap pre-preg 124 may be introduced into a chopper device 130 which may be similar to a blender, having rotating blades 132 inside an open vessel 135 .
  • the blades 132 chop and break the scrap fiber pre-preg 124 into individual fiber pre-preg segments 32 , breaking or splitting the pre-preg along the lines of, and between the reinforcing fibers, resulting in the fiber pre-preg segments that have a random orientation 126 .
  • the randomly oriented 126 fiber pre-preg segments 32 are aligned, for example by placing them in a shaker tray 134 having a series of parallel channels 136 .
  • the shaker tray 134 is vibrated side-to-side 138 , causing the randomly oriented 126 fiber pre-preg segments 32 that have been loaded onto the tray 134 to fall into and align themselves within the channels 136 , resulting in rows 140 of aligned, fiber pre-preg segments 32 .
  • the aligned rows 140 of the fiber pre-preg segments 32 may be fed to an applicator head 90 which dispenses, places and steers the fiber pre-preg segments 32 on the substrate 34 with desired fiber orientations.
  • FIGS. 19A-21B illustrate another embodiment of a method of steering chopped fiber pre-preg segments 32 onto a substrate 34 .
  • an applicator 140 is used to apply 142 a suitable resin 144 onto the substrate 34 , as the applicator 140 moves 150 across the substrate 34 .
  • the resin 144 may be applied by spraying the resin 144 onto the substrate 34 , rolling the resin 144 onto the substrate 34 or using other application techniques.
  • chopped fiber pre-preg segments 32 are applied to the substrate 34 by a suitable applicator 146 that moves 150 over the substrate 34 .
  • the fiber pre-preg segments 32 may have random orientations, as shown in FIG. 20B .
  • a fiber segment aligner 148 is moved 150 over the substrate 34 to align the fiber pre-preg segments 32 in a desired direction, which in this case, is along axis 36 .
  • the fiber segment aligner 148 may use one or more mechanical devices to contact and realign the fiber pre-preg segments 32 , or alternatively may use noncontact techniques, such as an airstream (not shown) to achieve the desired segment alignment.
  • noncontact techniques such as an airstream (not shown) to achieve the desired segment alignment.
  • orienting the segments 32 as they are being initially placed on the substrate 34 may be desirable in some applications, since this technique may eliminate the need for the additional step of repositioning the segments 32 to the desired fiber orientations.
  • FIGS. 22A-24B illustrate an alternate technique for placing and aligning the fiber pre-preg segments 32 on the substrate 34 .
  • a small quantity, such as a drop, of resin 152 is placed on one end 154 of each of the fiber pre-preg segments 32 .
  • the fiber segment 32 is placed on the substrate 34 .
  • the fibers of the fiber segment 32 may not be aligned with the desired orientation, such as axis 36 .
  • the fiber segment 32 is then rotated 156 so that the fiber orientation of the fiber segment 32 is aligned with the axis 36 .
  • the orientation process may be performed using mechanical devices 49 , or using noncontact techniques such as streaming air over the substrate 34 .
  • Embodiments of the disclosure may find use in a variety of potential applications, particularly in the transportation industry, including for example, aerospace, marine, automotive applications and other application where composite structures may require local features requiring tight contours, thickness control and/or cross-sectional tailoring.
  • embodiments of the disclosure may be used in the context of an aircraft manufacturing and service method 158 as shown in FIG. 25 and an aircraft 160 as shown in FIG. 26 .
  • Aircraft applications of the disclosed embodiments may include, for example, without limitation, various parts of the airframe 176 such as frames, beams, spars, and stringers to name only a few.
  • exemplary method 158 may include specification and design 162 of the aircraft 160 and material procurement 164 .
  • component and subassembly manufacturing 166 and system integration 168 of the aircraft 160 takes place. Thereafter, the aircraft 160 may go through certification and delivery 170 in order to be placed in service 172 . While in service by a customer, the aircraft 160 is scheduled for routine maintenance and service 174 , which may also include modification, reconfiguration, refurbishment, repair and so on.
  • Each of the processes of method 158 may be performed or carried out by a system integrator, a third party, and/or an operator (e.g., a customer).
  • a system integrator may include without limitation any number of aircraft manufacturers and major-system subcontractors
  • a third party may include without limitation any number of vendors, subcontractors, and suppliers
  • an operator may be an airline, leasing company, military entity, service organization, and so on.
  • the aircraft 160 produced by exemplary method 158 may include an airframe 176 with a plurality of systems 178 and an interior 180 .
  • high-level systems 178 include one or more of a propulsion system 182 , an electrical system 184 , a hydraulic system 188 , and an environmental system 190 . Any number of other systems may be included.
  • an aerospace example is shown, the principles of the disclosure may be applied to other industries, such as the marine and automotive industries.
  • Systems and methods embodied herein may be employed during any one or more of the stages of the production and service method 158 .
  • components or subassemblies corresponding to production process 166 may be fabricated or manufactured in a manner similar to components or subassemblies produced while the aircraft 160 is in service.
  • one or more apparatus embodiments, method embodiments, or a combination thereof may be utilized during the production stages 166 and 168 , for example, by substantially expediting assembly of or reducing the cost of an aircraft 160 .
  • apparatus embodiments, method embodiments, or a combination thereof may be utilized while the aircraft 160 is in service, for example and without limitation, to perform maintenance and service 174 , or to carry out repair or refurbishment of structures at any time during the service life of the aircraft 160 .
  • the phrase “at least one of”, when used with a list of items, means different combinations of one or more of the listed items may be used and only one of each item in the list may be needed.
  • “at least one of item A, item B, and item C” may include, without limitation, item A, item A and item B, or item B. This example also may include item A, item B, and item C or item B and item C.
  • the item may be a particular object, thing, or a category. In other words, at least one of means any combination of items and number of items may be used from the list but not all of the items in the list are required.

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Composite Materials (AREA)
  • Mechanical Engineering (AREA)
  • Textile Engineering (AREA)
  • Moulding By Coating Moulds (AREA)
  • Reinforced Plastic Materials (AREA)
  • Robotics (AREA)
  • Manufacture Of Alloys Or Alloy Compounds (AREA)
US13/789,965 2013-03-08 2013-03-08 Forming Composite Features Using Steered Discontinuous Fiber Pre-Preg Abandoned US20140255646A1 (en)

Priority Applications (13)

Application Number Priority Date Filing Date Title
US13/789,965 US20140255646A1 (en) 2013-03-08 2013-03-08 Forming Composite Features Using Steered Discontinuous Fiber Pre-Preg
PCT/US2014/016533 WO2014137568A2 (en) 2013-03-08 2014-02-14 Forming composite features using steered discontinuous fiber pre-preg
CN201480009859.7A CN105073392A (zh) 2013-03-08 2014-02-14 使用转向的不连续纤维预浸件形成复合特征
CA3004233A CA3004233C (en) 2013-03-08 2014-02-14 Forming composite features using steered discontinuous fiber pre-preg
KR1020157022015A KR102119435B1 (ko) 2013-03-08 2014-02-14 조종된 불연속 섬유 수지 함침재를 이용하여 복합재 구조물을 형성하는 방법
CN201911265573.6A CN110920093A (zh) 2013-03-08 2014-02-14 使用转向的不连续纤维预浸件形成复合特征
MX2015010813A MX388975B (es) 2013-03-08 2014-02-14 Formacion de elementos compuestos usando pre-impregnados de fibra discontinua dirigida.
EP14707580.8A EP2964451B1 (en) 2013-03-08 2014-02-14 Forming composite features using steered discontinuous fiber pre-preg
BR112015019511A BR112015019511A2 (pt) 2013-03-08 2014-02-14 método para formar um elemento compósito que tem fibras de reforço descontínuas, deposição de estrutura laminada de compósito, e, aparelho para depositar uma estrutura de compósito
CA2898224A CA2898224C (en) 2013-03-08 2014-02-14 Forming composite features using steered discontinuous fiber pre-preg
JP2015561367A JP6453250B2 (ja) 2013-03-08 2014-02-14 案内された不連続繊維プリプレグを用いる複合特徴部の形成
US15/908,793 US11007726B2 (en) 2013-03-08 2018-02-28 Forming composite features using steered discontinuous fiber pre-preg
JP2018230731A JP6612958B2 (ja) 2013-03-08 2018-12-10 案内された不連続繊維プリプレグを用いる複合特徴部の形成

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US13/789,965 US20140255646A1 (en) 2013-03-08 2013-03-08 Forming Composite Features Using Steered Discontinuous Fiber Pre-Preg

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/908,793 Division US11007726B2 (en) 2013-03-08 2018-02-28 Forming composite features using steered discontinuous fiber pre-preg

Publications (1)

Publication Number Publication Date
US20140255646A1 true US20140255646A1 (en) 2014-09-11

Family

ID=50190809

Family Applications (2)

Application Number Title Priority Date Filing Date
US13/789,965 Abandoned US20140255646A1 (en) 2013-03-08 2013-03-08 Forming Composite Features Using Steered Discontinuous Fiber Pre-Preg
US15/908,793 Active 2033-05-06 US11007726B2 (en) 2013-03-08 2018-02-28 Forming composite features using steered discontinuous fiber pre-preg

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/908,793 Active 2033-05-06 US11007726B2 (en) 2013-03-08 2018-02-28 Forming composite features using steered discontinuous fiber pre-preg

Country Status (9)

Country Link
US (2) US20140255646A1 (enExample)
EP (1) EP2964451B1 (enExample)
JP (2) JP6453250B2 (enExample)
KR (1) KR102119435B1 (enExample)
CN (2) CN105073392A (enExample)
BR (1) BR112015019511A2 (enExample)
CA (2) CA3004233C (enExample)
MX (1) MX388975B (enExample)
WO (1) WO2014137568A2 (enExample)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9486960B2 (en) 2014-12-19 2016-11-08 Palo Alto Research Center Incorporated System for digital fabrication of graded, hierarchical material structures
US20170100910A1 (en) * 2015-10-12 2017-04-13 C&D Zodiac, Inc. Aircraft panel assembly with reinforcement layers
WO2017089460A1 (en) * 2015-11-25 2017-06-01 Hexcel Composites Sas Improvements in or relating to fibre reinforced composites
US9821339B2 (en) 2014-12-19 2017-11-21 Palo Alto Research Center Incorporated System and method for digital fabrication of graded, hierarchical material structures
WO2018091378A1 (en) * 2016-11-16 2018-05-24 Ge Aviation Systems Limited Method for forming stiffened composite parts
US10160004B2 (en) 2015-07-07 2018-12-25 Palo Alto Research Center Incorporated Creating aligned and oriented fiber reinforced polymer composites
CN111016005A (zh) * 2019-12-10 2020-04-17 深圳市飞荣达科技股份有限公司 纤维预浸料制备装置及纤维预浸料制备方法
CN111730877A (zh) * 2019-03-25 2020-10-02 波音公司 自动化纤维铺放系统和方法以及由其生产的物品
US10947419B2 (en) 2018-07-23 2021-03-16 Palo Alto Research Center Incorporated Method for joining dissimilar materials
US11007726B2 (en) 2013-03-08 2021-05-18 The Boeing Company Forming composite features using steered discontinuous fiber pre-preg
US20210276688A1 (en) * 2020-03-06 2021-09-09 Galactic Co., LLC Shaped Composite Vehicle Skins and Method for High Rate Manufacturing of Same
WO2021195714A1 (en) * 2020-04-03 2021-10-07 Darcan Technology Holdings Pty Ltd Fibre material
US11945177B2 (en) 2020-03-31 2024-04-02 Kawasaki Jukogyo Kabushiki Kaisha Method of manufacturing intermediate product of aircraft part and aircraft part

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106113521B (zh) * 2016-06-29 2018-07-17 西安交通大学 贝壳仿生复合材料增韧结构及其设计方法和自动化制造工艺
DE102016213407A1 (de) * 2016-07-22 2018-01-25 Bayerische Motoren Werke Aktiengesellschaft Vorrichtung und Verfahren zur effizienten Herstellung von Bauteilrohlingen aus Verbundwerkstoffen
JP7322588B2 (ja) * 2019-08-19 2023-08-08 株式会社豊田自動織機 繊維構造体及び繊維強化複合材
DE102021131453A1 (de) 2021-11-30 2023-06-01 Cevotec Gmbh Anordnung von Faserbändern

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5380477A (en) * 1993-05-25 1995-01-10 Basf Corporation Process of making fiber reinforced laminates
US20050056362A1 (en) * 2003-08-01 2005-03-17 Benson Vernon M. Apparatus and methods for forming composite stiffeners and reinforcing structures
US20070175572A1 (en) * 2006-02-02 2007-08-02 The Boeing Company Continuous Fabrication of Parts Using In-Feed Spools of Fiber Reinforced Thermoplastic
US20090261199A1 (en) * 2008-04-17 2009-10-22 The Boeing Company Method for producing contoured composite structures and structures produced thereby
US20100178495A1 (en) * 2007-06-04 2010-07-15 Toray Industries, Inc. Chopped fiber bundle, molding material, and fiber reinforced plastic, and process for producing them

Family Cites Families (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3574040A (en) * 1967-06-29 1971-04-06 Gen Dynamics Corp Apparatus for making laminated structural shapes by the controlled detrusive placement and polymerization of tectonic filamentous tapes
US4212216A (en) * 1979-01-22 1980-07-15 Ives Frank E Deflector for attachment to fiber chopper nozzle
JPS58193117A (ja) * 1982-05-07 1983-11-10 Mitsubishi Rayon Co Ltd プリプレグ及びその製造法
US4806298A (en) * 1984-11-21 1989-02-21 The Budd Company A cutter for cutting resin impregnated strands and a method and apparatus for making a charge for molding a fiber reinforced part
MX171501B (es) * 1984-11-21 1993-11-03 Budd Co Metodo y aparato para producir una carga para moldear una pieza reforzada con fibras
US4740346A (en) * 1986-02-26 1988-04-26 The Budd Company Perimeter resin feeding of composite structures
US5272000A (en) 1987-05-22 1993-12-21 Guardian Industries Corp. Non-woven fibrous product containing natural fibers
IL95489A0 (en) * 1989-08-31 1991-06-30 Du Pont Nonwoven preform sheets of fiber reinforced resin
US5164255A (en) 1989-08-31 1992-11-17 E. I. Du Pont De Nemours And Company Nonwoven preform sheets of fiber reinforced resin chips
US6182332B1 (en) * 1999-07-30 2001-02-06 Owens Corning Composites Sprl Method of forming discrete length fibers
US6799081B1 (en) 2000-11-15 2004-09-28 Mcdonnell Douglas Corporation Fiber placement and fiber steering systems and corresponding software for composite structures
US7208220B2 (en) * 2001-12-06 2007-04-24 Toray Industries, Inc. Fiber-reinforced composite material and method for production thereof
JP4292994B2 (ja) 2002-04-23 2009-07-08 東レ株式会社 プリプレグ、その製造方法および成形品
GB0222753D0 (en) * 2002-10-02 2002-11-06 Carbon Fibre Technology Ltd Method of production of advanced composite materials
US7402269B2 (en) * 2005-10-25 2008-07-22 The Boeing Company Environmentally stable hybrid fabric system for exterior protection of an aircraft
ES2291131B1 (es) * 2006-08-08 2008-12-01 Manuel Torres Martinez Cabezal de aplicacion de cintas de fibra de carbono y metodo de aplicacion.
JP2008057849A (ja) 2006-08-31 2008-03-13 Denso Corp 熱交換器の製造方法
EP2067592B1 (en) 2006-09-28 2020-07-15 Toray Industries, Inc. Process for producing composite prepreg base, layered base, and fiber-reinforced plastic
CN101600550B (zh) * 2007-02-02 2013-03-20 东丽株式会社 预浸料坯基材、层合基材、纤维增强塑料、预浸料坯基材的制造方法及纤维增强塑料的制造方法
US8440276B2 (en) 2008-02-11 2013-05-14 Albany Engineered Composites, Inc. Multidirectionally reinforced shape woven preforms for composite structures
JP5253510B2 (ja) * 2008-07-24 2013-07-31 アレニア・アエルマッキ・ソシエタ・ペル・アチオニ プリプレグ材料屑の再利用方法
EP2179838B1 (en) * 2008-10-23 2017-12-06 Campagnolo S.r.l. Sheet moulding compound
US8790566B2 (en) 2009-06-01 2014-07-29 Mitsubishi Heavy Industries, Ltd. Manufacturing method of composite material member and prepreg sheet laminate
ES2645412T3 (es) 2009-10-01 2017-12-05 Albany Engineered Composites, Inc. Preforma tejida, material compuesto y método de elaboración de los mismos
JP5713568B2 (ja) 2010-02-10 2015-05-07 三菱航空機株式会社 構造材の製造方法、構造材
US8668864B2 (en) * 2011-05-31 2014-03-11 MRA Systems Inc. Polymer composite materials and processes therefor
US9463880B2 (en) 2013-02-07 2016-10-11 The Boeing Company Method and system of making composite structures having gap fillers with chopped fiber material
US20140255646A1 (en) 2013-03-08 2014-09-11 The Boeing Company Forming Composite Features Using Steered Discontinuous Fiber Pre-Preg

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5380477A (en) * 1993-05-25 1995-01-10 Basf Corporation Process of making fiber reinforced laminates
US20050056362A1 (en) * 2003-08-01 2005-03-17 Benson Vernon M. Apparatus and methods for forming composite stiffeners and reinforcing structures
US20070175572A1 (en) * 2006-02-02 2007-08-02 The Boeing Company Continuous Fabrication of Parts Using In-Feed Spools of Fiber Reinforced Thermoplastic
US20100178495A1 (en) * 2007-06-04 2010-07-15 Toray Industries, Inc. Chopped fiber bundle, molding material, and fiber reinforced plastic, and process for producing them
US20090261199A1 (en) * 2008-04-17 2009-10-22 The Boeing Company Method for producing contoured composite structures and structures produced thereby

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Dictionary.com definition of "into". Retrieved via an online search. October 5, 2016. *

Cited By (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11007726B2 (en) 2013-03-08 2021-05-18 The Boeing Company Forming composite features using steered discontinuous fiber pre-preg
US9486960B2 (en) 2014-12-19 2016-11-08 Palo Alto Research Center Incorporated System for digital fabrication of graded, hierarchical material structures
US11059216B2 (en) 2014-12-19 2021-07-13 Palo Alto Research Center Incorporated System for digital fabrication of graded, hierarchical material structures
US9713903B2 (en) 2014-12-19 2017-07-25 Palo Alto Research Center Incorporated System for digital fabrication of graded, hierarchical material structures
US9821339B2 (en) 2014-12-19 2017-11-21 Palo Alto Research Center Incorporated System and method for digital fabrication of graded, hierarchical material structures
US10160004B2 (en) 2015-07-07 2018-12-25 Palo Alto Research Center Incorporated Creating aligned and oriented fiber reinforced polymer composites
US11267164B2 (en) 2015-07-07 2022-03-08 Palo Alto Research Center Incorporated Creating aligned and oriented fiber reinforced polymer composites
US20170100910A1 (en) * 2015-10-12 2017-04-13 C&D Zodiac, Inc. Aircraft panel assembly with reinforcement layers
EP3159149A1 (en) * 2015-10-12 2017-04-26 C&D Zodiac, Inc. Aircraft panel assembly with reinforcement layers
US10538050B2 (en) 2015-10-12 2020-01-21 C&D Zodiac, Inc. Aircraft panel assembly with reinforcement layers
JP2019503281A (ja) * 2015-11-25 2019-02-07 ヘクセル コンポズィトゥ エス．ア．エス． 繊維強化複合体における又はこれに関連する改良
WO2017089460A1 (en) * 2015-11-25 2017-06-01 Hexcel Composites Sas Improvements in or relating to fibre reinforced composites
WO2018091378A1 (en) * 2016-11-16 2018-05-24 Ge Aviation Systems Limited Method for forming stiffened composite parts
US10947419B2 (en) 2018-07-23 2021-03-16 Palo Alto Research Center Incorporated Method for joining dissimilar materials
US11834592B2 (en) 2018-07-23 2023-12-05 Xerox Corporation Method for joining dissimilar materials
CN111730877A (zh) * 2019-03-25 2020-10-02 波音公司 自动化纤维铺放系统和方法以及由其生产的物品
CN111016005A (zh) * 2019-12-10 2020-04-17 深圳市飞荣达科技股份有限公司 纤维预浸料制备装置及纤维预浸料制备方法
US20210276688A1 (en) * 2020-03-06 2021-09-09 Galactic Co., LLC Shaped Composite Vehicle Skins and Method for High Rate Manufacturing of Same
US11945177B2 (en) 2020-03-31 2024-04-02 Kawasaki Jukogyo Kabushiki Kaisha Method of manufacturing intermediate product of aircraft part and aircraft part
WO2021195714A1 (en) * 2020-04-03 2021-10-07 Darcan Technology Holdings Pty Ltd Fibre material

Also Published As

Publication number Publication date
CA3004233A1 (en) 2014-09-12
WO2014137568A2 (en) 2014-09-12
US20180186099A1 (en) 2018-07-05
CN105073392A (zh) 2015-11-18
CN110920093A (zh) 2020-03-27
US11007726B2 (en) 2021-05-18
MX2015010813A (es) 2015-11-26
JP2016510701A (ja) 2016-04-11
JP6453250B2 (ja) 2019-01-16
CA2898224C (en) 2018-06-12
CA2898224A1 (en) 2014-09-12
WO2014137568A3 (en) 2014-11-20
JP2019069610A (ja) 2019-05-09
KR20150126346A (ko) 2015-11-11
CA3004233C (en) 2020-03-24
EP2964451B1 (en) 2025-01-15
MX388975B (es) 2025-03-20
BR112015019511A2 (pt) 2017-07-18
KR102119435B1 (ko) 2020-06-08
EP2964451A2 (en) 2016-01-13
JP6612958B2 (ja) 2019-11-27

Similar Documents

Publication Publication Date Title
US11007726B2 (en) Forming composite features using steered discontinuous fiber pre-preg
US9463880B2 (en) Method and system of making composite structures having gap fillers with chopped fiber material
CA2857783C (en) Laminated composite radius filler with geometric shaped filler element and method of forming the same
US9517594B2 (en) Composite structure having a stabilizing element
US20200016796A1 (en) Methods of making hybrid laminate and molded composite structures
US11220069B2 (en) Composite laminate structures

Legal Events

Date Code Title Description
AS Assignment

Owner name: THE BOEING COMPANY, ILLINOIS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:GRIESS, KENNETH H.;VETTER, DEREK PAUL;GRAVES, MICHAEL JEFFREY;REEL/FRAME:029950/0063

Effective date: 20130301

STCB Information on status: application discontinuation

Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION