US20120252223A1 - Method of manufacturing a semiconductor device - Google Patents

Method of manufacturing a semiconductor device Download PDF

Info

Publication number
US20120252223A1
US20120252223A1 US13/494,418 US201213494418A US2012252223A1 US 20120252223 A1 US20120252223 A1 US 20120252223A1 US 201213494418 A US201213494418 A US 201213494418A US 2012252223 A1 US2012252223 A1 US 2012252223A1
Authority
US
United States
Prior art keywords
oxide film
oxidation
gate oxide
sic substrate
semiconductor device
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
US13/494,418
Inventor
Kazuo Kobayashi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Electric Corp
Original Assignee
Mitsubishi Electric Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Electric Corp filed Critical Mitsubishi Electric Corp
Priority to US13/494,418 priority Critical patent/US20120252223A1/en
Publication of US20120252223A1 publication Critical patent/US20120252223A1/en
Granted legal-status Critical Current

Abstract

A method of manufacturing a semiconductor device according to the present invention includes the steps of: (a) introducing hydrogen and oxygen on a SiC substrate; and (b) subjecting the hydrogen and the oxygen to a combustion reaction on the SiC substrate to form a gate oxide film being a silicon oxide film on a surface of the SiC substrate by the combustion reaction.

Description

    CROSS-REFERENCE TO RELATED APPLICATIONS
  • The present divisional application claims the benefit of priority under 35 U.S.C. §120 to application Ser. No. 12/882,746, filed on Sep. 15, 2010, and claims the benefit of priority under 35 U.S.C. 119 from Japanese Application No. 2010-039627, filed on Feb. 25, 2010. The entire contents of application Ser. No. 12/882,746 is hereby incorporated herein by reference.
    • BACKGROUND OF THE INVENTION
  • 1. Field of the Invention
  • The present invention relates to a method of manufacturing a semiconductor device, and more particularly, to a method of providing a highly reliable oxide film whose interface state on an interface between a silicon carbide (SiC) substrate and an oxide film is reduced in an oxidation step on the SiC substrate.
  • 2. Description of the Background Art
  • Silicon carbide (SiC) has a dielectric breakdown field strength higher by approximately one order than that of silicon (Si), which makes it possible to reduce a thickness of a drift layer thereof for keeping a breakdown voltage to one-tenth of a drift layer of Si. This enables a loss reduction in power devices.
  • However, between a silicon surface and a carbon surface of SiC, there are exhibited different physical properties on surfaces and interfaces due to differences in ionicity of crystal and bond sequence, and thus a difference occurs in thermal oxidation rate when oxidation is performed on the SiC substrate. Therefore, when forming a gate oxide film in a SiC-metal oxide semiconductor field-effect transistor (MOSFET), oxidation conditions need to be optimized depending on a crystal plane. This is because a difference in oxidation conditions considerably affects the mobility of an inversion channel and the reliability of an oxide film.
  • Conventional oxidation techniques are classified into two types including the dry oxidation technique of supplying only oxygen to form an oxide film, and the wet oxidation technique of burning oxygen and hydrogen in front of a reactor and supplying a water-vapor atmosphere thereof to the reactor to form an oxide film.
  • In the gate oxide film formed on the SiC substrate by the wet oxidation technique, hydrogen atoms in a water-vapor atmosphere effectively hydrogen-terminate dangling bond on the interface, which produces an effect of reducing an interface state. Accordingly, the inversion channel mobility of the MOSFET is improved. Further, in the wet oxidation technique, strong oxidation power tends to promote desorption of the residual carbon on the interface, to thereby reduce an interface state. For this reason, wet oxidation is desirably employed.
  • When the reliability of an oxide film by the wet oxidation technique is checked, however, the dielectric breakdown field strength is inferior to a gate oxide film formed by the dry oxidation technique due to a large amount of hydroxy groups (OH groups) contained in the gate oxide film.
  • Therefore, in “SiC-MOSFET with High Channel Mobility and High Reliability”, Toshiba Review, Vol. 63, No. 10, 2008, it is devised that in forming a gate oxide film of a SiC-MOSFET, oxidation is performed by the dry oxidation technique, and then oxidation is performed again by the wet oxidation technique so as to achieve high mobility as well as high reliability.
  • However, in the method described in “SiC-MOSFET with High Channel Mobility and High Reliability”, hydroxy groups are inevitably contained due to wet oxidation, which requires the method of forming a gate oxide film capable of achieving higher reliability.
    • SUMMARY OF THE INVENTION
  • An object of the present invention is therefore to provide a method of manufacturing a semiconductor device including a gate oxide film that has high reliability.
  • A method of manufacturing a semiconductor device according to the present invention includes the steps of (a) introducing hydrogen and oxygen on a SiC substrate; and (b) subjecting the hydrogen and the oxygen to a combustion reaction on the SiC substrate to form a silicon oxide film on a surface of the SiC substrate by the combustion reaction.
  • According to the method of manufacturing a semiconductor device of the present invention, it is possible to manufacture a semiconductor device including a gate oxide film that has high reliability.
  • These and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.
    • BRIEF DESCRIPTION OF THE DRAWINGS
  • FIG. 1 is a cross-sectional view of a semiconductor device according to a first preferred embodiment;
  • FIG. 2 shows an outline of a semiconductor manufacturing apparatus used in a method of manufacturing the semiconductor device according to the first preferred embodiment;
  • FIG. 3 shows comparison of reliability of a semiconductor device between immediately-above burning oxidation and wet oxidation;
  • FIG. 4 is a cross-sectional view of another semiconductor device according to the first preferred embodiment; and
  • FIG. 5 shows an outline of a semiconductor manufacturing apparatus used in a method of manufacturing the another semiconductor device according to the first preferred embodiment.
    •  DESCRIPTION OF THE PREFERRED EMBODIMENT A. First Preferred Embodiment
  • A-1. Manufacturing Method
  • FIG. 1 shows a cross-sectional structure of a SiC-MOSFET as a semiconductor device according to a first preferred embodiment. The SiC-MOSFET as shown in FIG. 1 is formed on a substrate in which a SiC epitaxial layer (drift layer) 1 b is formed on a SiC substrate 1 a. Hereinafter, the SiC substrate 1 a and the SiC epitaxial layer 1 b are collectively referred to as a SiC substrate 1. After patterning of a surface of the SiC substrate 1, Al is implanted, whereby p-type diffusion layers 2 are diffused apart from each other. Then, n-type SiC diffusion layers 3 are diffused on the p-type SiC diffusion layers 2 after patterning.
  • After that, a gate oxide film (silicon oxide film) 4 is formed on the SiC substrate 1 after the activation step of the diffusion layers by heat treatment, a poly-Si electrode 5 as a gate electrode is formed at a position sandwiched between the regions in which the p-type SiC diffusion layers 2 and the n-type SiC diffusion layers 3 are diffused.
  • The mobility and reliability of the gate oxide film 4 shown in FIG. 1 are deteriorated if a large number of defect states are created on an interface between the SiC substrate 1 and the gate oxide film 4.
  • There is conventionally employed wet oxidation in which hydrogen and oxygen are burned in advance and a water-vapor atmosphere generated as a result of burning is fed to a reactor for oxidation. Unfortunately, however, a large number of hydroxy groups are contained in the gate oxide film 4 that has been formed by wet oxidation, which deteriorates the mobility and reliability. Therefore, as another oxidation technique, the gate oxide film 4 is formed by immediately-above burning oxidation in the present invention. Herein, immediately-above burning oxidation refers to the oxidation technique in which hydrogen and oxygen are introduced above the substrate as such, and a combustion reaction is caused on the substrate to use an oxidation reaction accompanying the combustion reaction.
  • In order to perform immediately-above burning oxidation, a lamp irradiation single-wafer oxidation apparatus as shown in FIG. 2 (left part thereof) is used. In the lamp irradiation single-wafer oxidation apparatus shown in FIG. 2, halogen lamps 6 are provided in an upper portion of a chamber, the temperature of a back surface of a SiC substrate 8 is checked by radiation thermometers 7 in a lower portion of the chamber, and this temperature is fed back to a lamp power (not shown) to perform heating control.
  • Hydrogen gas and oxygen gas are introduced into a thermal atmosphere of 1,000° C. or higher under reduced pressure (of approximately 133 Pa) through a gas inlet 9. Then, in the state in which hydrogen gas and oxygen gas are introduced (right portion of FIG. 2), a combustion reaction (2H2+O2→2H2O) is caused immediately above the SiC substrate 8 that has been selectively heated by the halogen lamps 6, to thereby perform thermal oxidation of SiC.
  • In the conventional wet oxidation, when hydrogen and oxygen are burned in a processing chamber of atmospheric pressure, quartz chips accompanying burning cause dusts. Therefore, a burning chamber is normally provided in front of a processing chamber, and hydrogen and oxygen are burned in the burning chamber in advance, with the result that a water-vapor atmosphere generated as a result of burning is fed to the processing chamber.
  • On the other hand, in immediately-above burning oxidation, the above-mentioned combustion reaction occurs immediately above the SiC substrate 8. The combustion reaction occurs immediately thereabove, and thus it is conceivable that radicals (such as O radicals) that are intermediate products of combustion reaction may dominantly contribute to oxidation. Therefore, the inventor(s) have found that hydroxy groups contained in a gate oxide film can be reduced, and desorption of carbon in SiC proceeds because radicals (such as O radicals) have higher oxidation power than H2O, which enables the formation of a gate oxide film having higher reliability.
  • Further, as shown in FIG. 2 (left portion thereof), the radiation thermometers 7 are provided at six positions in a radial direction of the SiC substrate 8 on the back surface side of the SiC substrate 8, and thus temperature control is enabled among these 6 zones by rotating the SiC substrate 8. Accordingly, it is possible to keep in-plane uniformity of a film thickness to 1% or less in immediately-above burning oxidation (single-wafer mode), whereas in-plane uniformity of a film thickness is approximately 3% in wet oxidation (batch mode).
  • Note that a partial pressure of H2O is low in immediately-above burning oxidation. Further, the O radicals considered to contribute to oxidation are inactivated along with the growth of a gate oxide film, and accordingly are less likely to be diffused. That is, an oxidation rate decreases in the gate oxide film. As a result, it is possible to suppress thermal stress due to oxidation.
  • A gate oxide film is formed by immediately-above burning oxidation using this lamp irradiation single-wafer oxidation apparatus as described above, which makes it possible to manufacture a SiC-MOSFET having high mobility and reliability.
  • Note that NO gas and N2O gas are introduced into a lamp irradiation single-wafer oxidation apparatus for nitrogenizing an interface of the SiC substrate 8 to reduce interface defects.
  • A-2. Operation
  • FIG. 3 shows evaluation results of constant voltage stress-time dependent dielectric breakdown (CVS-TDDB) in a case of using a Si substrate. In the CVS-TDDB evaluation, changes over time of the number of semiconductor devices that have undergone dielectric breakdown are evaluated at a constant voltage. In FIG. 3, a vertical axis and a horizontal axis represent a failure rate and an elapsed time, respectively.
  • The evaluation results shown in FIG. 3 were obtained using a test element group (TEG) produced by forming two types of oxide films, an oxide film (having a film thickness of 7.2 nm) formed by immediately-above burning oxidation (single-wafer mode) and an oxide film (having a film thickness of 7.2 nm) formed by wet oxidation (batch mode), on an isolation base for shallow trench isolation (STI), further forming a poly-Si electrode, and performing patterning and back surface polishing. Specifically, a failure rate (10-sec failure rate) after application of 11-MV/cm stress (10 mA evaluation) for 10 seconds was evaluated at a temperature of 125° C.
  • As shown in FIG. 3, a 10-sec failure rate is 19.8% in wet oxidation (indicated by triangular dots in FIG. 3) that is conventionally performed, whereas in immediately-above burning oxidation (indicated by dots in FIG. 3), a 10-sec failure rate is 5.2%, which is lower than that of wet oxidation. This means that also in the elapsed time reaching dielectric breakdown, immediately-above burning oxidation outperforms wet oxidation. The above reveals that an oxide film having higher reliability is formed in immediately-above burning oxidation compared with wet oxidation.
  • In immediately-above burning oxidation, O radicals considered to dominantly contribute to oxidation are inactivated in the oxide film as the oxide film grows and are less likely to be diffused in the oxide film, which reduces an oxidation rate. In particular, an oxidation rate of SiC is smaller compared with Si, and thus it is difficult to form a thick gate oxide film (of approximately 100 nm) such as a gate oxide film for a power device. Further, immediately-above burning oxidation in this preferred embodiment is performed by a single-wafer oxidation apparatus, and thus heat is concentrated on the SiC substrate, which causes damage to a SiC substrate as a result of the treatment for a long time. Therefore, it is desired that the gate oxide film be formed on a SiC substrate by immediately-above burning oxidation to be 20 nm or less.
  • As a measure taken against this, a gate oxide film 11 is formed to be 20 nm or less by immediately-above burning oxidation, and then dry oxidation in an atmosphere of only oxygen is performed to further form a gate oxide film 12, whereby a gate oxide film is formed to be thick, 100 nm or more in total (see FIG. 4). In this case, in performing dry oxidation, the gate oxide film 11 has been formed to be approximately 20 nm or less on a SiC substrate 10 by immediately-above burning oxidation. Thus, even in a case where the film formation is performed for a remaining thickness by dry oxidation, interface state density does not increase, which is a drawback of dry oxidation. Note that also in a case where the above-mentioned order is reversed such that a gate oxide film is formed by dry oxidation and then another gate oxide film is formed by immediately-above burning oxidation, the effect of enhancing reliability of a gate oxide film is achieved.
  • Note that in a case where a gate oxide film is additionally formed by the above-mentioned method, an apparatus as shown in FIG. 5 can be used. In this apparatus, an immediately-above burning oxidation processing chamber 13, a dry oxidation processing chamber 14, an HTO furnace 15, loadlock chambers 16 and 17 are connected through a transport chamber 18, and immediately-above burning oxidation and dry oxidation can be performed while keeping insides of the processing chambers vacuum without causing them open to the atmosphere. That is, with the use of an apparatus that has the structure enabling step shift without exposing a SiC substrate to the ambient atmosphere, cleanliness is maintained, whereby it is possible to form a gate oxide film having high reliability in which foreign matters are prevented from being contained and an organic oxide film is not provided.
  • Further, though not shown, it is possible to form a gate oxide film to be thick in total by forming a gate oxide film by immediately-above burning oxidation, and then forming an oxide film by CVD to form another gate oxide film.
  • A-3. Effects
  • According to the first preferred embodiment of the present invention, the method of manufacturing a semiconductor device includes the steps of: (a) introducing hydrogen and oxygen on a SiC substrate 1; and (b) subjecting the hydrogen and the oxygen to a combustion reaction on the SiC substrate 1 to form a gate oxide film 4 being a silicon oxide film on a surface of the SiC substrate 1 by the combustion reaction. Accordingly, it is possible to manufacture a semiconductor device including a gate oxide film having high reliability.
  • Further, according to the first preferred embodiment of the present invention, in the method of manufacturing a semiconductor device, the steps (a) and (b) are performed with a lamp irradiation single-wafer oxidation apparatus forming, on the SiC substrate 1, a high-temperature atmosphere of a higher temperature compared with an ambient temperature by irradiating the SiC substrate 1 with light. Accordingly, it is possible to manufacture a semiconductor device including a highly reliable gate oxide film whose processing time is reduced.
  • Further, according to the first preferred embodiment of the present invention, the method of manufacturing a semiconductor device further includes the step of (c) dry-oxidizing the surface of the SiC substrate 1 to separately form a gate oxide film 12 being a silicon oxide film. Accordingly, it is possible to form a thick gate oxide film of approximately 100 nm, which enables manufacturing of a semiconductor device for a power device that requires a gate oxide film having the above-mentioned thickness. In particular, an oxidation rate of SiC is smaller than that of Si and thus is suitable for a case of forming a gate oxide film for a power device.
  • Further, according to the first preferred embodiment of the present invention, in the method of manufacturing a semiconductor device, the step (c) is performed after the step (b). This prevents an increase in interface state density due to dry oxidation because the gate oxide film 11 has been formed by immediately-above burning oxidation.
  • Further, according to the first preferred embodiment of the present invention, the method of manufacturing a semiconductor device further includes the step of (c) forming an oxide film on the surface of the SiC substrate 1 by CVD to separately form another silicon oxide film after the step (b). Accordingly, it is possible to form a thick gate oxide film of approximately 100 nm, which enables manufacturing of a semiconductor device for a power device that requires a gate oxide film having the above-mentioned thickness.
  • Further, according to the first preferred embodiment of the present invention, in the method of manufacturing a semiconductor device, the steps (a), (b) and (c) are performed with an apparatus having the structure enabling step shift without exposing the SiC substrate to an ambient atmosphere. Accordingly, it is possible to form a highly reliable gate oxide film in which foreign matters are prevented from being contained and an organic oxide film is not provided, which enables manufacturing of a semiconductor device having high mobility and reliability.
  • Further, according to the first preferred embodiment of the present invention, in a method of manufacturing a semiconductor device, when forming a gate oxide film of 100 nm or more on the SiC substrate 1 using the above-mentioned method of manufacturing a semiconductor device: the silicon oxide film of 20 nm or less is formed as the gate oxide film in the step (b); and the silicon oxide film of a remaining film thickness is formed as the gate oxide film in the step (c). Accordingly, it is possible to use the method of forming the gate oxide film of 20 nm or less that is the thickness enabling the formation by immediately-above burning oxidation whose oxidation rate is small, and filling a remaining thickness of 100 nm by forming the gate oxide film by dry oxidation or CVD. This enables manufacturing of a semiconductor device for a power device that requires a gate oxide film having the above-mentioned thickness.
  • While the invention has been shown and described in detail, the foregoing description is in all aspects illustrative and not restrictive. It is therefore understood that numerous modifications and variations can be devised without departing from the scope of the invention.

Claims (1)

1. A method of manufacturing a semiconductor device, comprising the steps of:
(a) introducing hydrogen and oxygen on a SiC substrate;
(b) subjecting said hydrogen and said oxygen to a combustion reaction on said SiC substrate to form a silicon oxide film on a surface of said SiC substrate by said combustion reaction; and
(c) dry-oxidizing said surface of said SiC substrate to separately form another silicon oxide film,
wherein the silicon oxide film formed step (b) is in direct contact with the another silicon oxide film formed in step (c), and
wherein said step (b) is performed after said step (c).
US13/494,418 2010-02-25 2012-06-12 Method of manufacturing a semiconductor device Granted US20120252223A1 (en)