US20120231582A1 - Device including a semiconductor chip - Google Patents
Device including a semiconductor chip Download PDFInfo
- Publication number
- US20120231582A1 US20120231582A1 US13/477,740 US201213477740A US2012231582A1 US 20120231582 A1 US20120231582 A1 US 20120231582A1 US 201213477740 A US201213477740 A US 201213477740A US 2012231582 A1 US2012231582 A1 US 2012231582A1
- Authority
- US
- United States
- Prior art keywords
- face
- layer
- metal layer
- encapsulation material
- semiconductor chip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A device including a semiconductor chip and method. One embodiment provides a method of manufacturing a module, including providing a first device having a first semiconductor chip and a plurality of first external contact elements electrically coupled to the first semiconductor chip. The method further includes providing a second device having a second semiconductor chip, a plurality of second external contact elements and a metal layer including a first face and a second face opposite to the first face, the first face of the metal layer facing the second semiconductor chip and the second face of the metal layer facing the plurality of second external contact elements. The first external contact elements are soldered to the first face of the metal layer.
Description
- This Utility patent application is a divisional application of U.S. application Ser. No. 12/324,420, filed Nov. 26, 2008, which is incorporated herein by reference.
- This invention relates to a device including a semiconductor chip and a method of manufacturing thereof.
- Miniaturization is a continuing trend in integrated circuit packaging technology toward smaller scales for semiconductor devices. Various techniques may be used to produce smaller semiconductor packages, such as chip scale packaging, wafer level packaging or chip stacking.
- For these and other reasons there is a need for the present invention.
- The accompanying drawings are included to provide a further understanding of embodiments and are incorporated in and constitute a part of this specification. The drawings illustrate embodiments and together with the description serve to explain principles of embodiments. Other embodiments and many of the intended advantages of embodiments will be readily appreciated as they become better understood by reference to the following detailed description. The elements of the drawings are not necessarily to scale relative to each other. Like reference numerals designate corresponding similar parts.
-
FIG. 1 schematically illustrates a cross-sectional view of one embodiment of a device including a semiconductor chip, an encapsulation material and a through-hole through the encapsulation material. -
FIG. 2 schematically illustrates a cross-sectional view of one embodiment of a module including two devices stacked on top of each other. -
FIGS. 3A to 3M schematically illustrate a cross-sectional view of one embodiment of a method of manufacturing a device including a carrier, a semiconductor chip, an encapsulation material and a through-hole through the encapsulation material. -
FIGS. 4A to 4K schematically illustrate a cross-sectional view of one embodiment of a method of manufacturing a device including a semiconductor chip, an encapsulation material and a through-hole through the encapsulation material. -
FIGS. 5A to 5C schematically illustrate a cross-sectional view of one embodiment of a method of manufacturing a module including two devices stacked on top of each other and mounting the module on a circuit board. -
FIG. 6 schematically illustrates a cross-sectional view of one embodiment of a device including a semiconductor chip, a laminate material and a through-hole through the laminate material. -
FIG. 7 schematically illustrates a cross-sectional view of one embodiment of a device including a semiconductor chip, a carrier, an encapsulation material and a through-hole through the carrier and the encapsulation material. - In the following Detailed Description, reference is made to the accompanying drawings, which form a part hereof, and in which is shown by way of illustration specific embodiments in which the invention may be practiced. In this regard, directional terminology, such as “top,” “bottom,” “front,” “back,” “leading,” “trailing,” etc., is used with reference to the orientation of the Figure(s) being described. Because components of embodiments can be positioned in a number of different orientations, the directional terminology is used for purposes of illustration and is in no way limiting. It is to be understood that other embodiments may be utilized and structural or logical changes may be made without departing from the scope of the present invention. The following detailed description, therefore, is not to be taken in a limiting sense, and the scope of the present invention is defined by the appended claims.
- It is to be understood that the features of the various exemplary embodiments described herein may be combined with each other, unless specifically noted otherwise.
- As employed in this Specification, the terms “coupled” and/or “electrically coupled” are not meant to mean that the elements must be directly coupled together; intervening elements may be provided between the “coupled” or “electrically coupled” elements.
- Devices containing one or more semiconductor chips are described below. The semiconductor chips may be of different types, may be manufactured by different technologies and may include for example, integrated electrical, electro-optical or electro-mechanical circuits or passives. The integrated circuits may, for example, be designed as logic integrated circuits, analog integrated circuits, mixed signal integrated circuits, power integrated circuits, memory circuits or integrated passives. Furthermore, the semiconductor chips may be configured as MEMS (micro-electro mechanical systems) and may include micro-mechanical structures, such as bridges, membranes or tongue structures. The semiconductor chips may be configured as sensors or actuators, for example, pressure sensors, acceleration sensors, rotation sensors, magnetic field sensors, electro-magnetic field sensors, microphones etc. The semiconductor chips may be configured as antennas and/or discrete passives and/or chip stacks. Semiconductor chips in which such functional elements are embedded generally contain electronic circuits which serve for driving the functional elements or further processing signals generated by the functional elements. The semiconductor chips need not be manufactured from specific semiconductor material, for example, Si, SiC, SiGe, GaAs, and, furthermore, may contain inorganic and/or organic materials that are not semiconductors, such as for example, discrete passives, antennas, insulators, plastics or metals. Moreover, the semiconductor chips may be packaged or unpackaged.
- The semiconductor chips may have contact elements (or contact pads or electrodes) which allow electrical contact to be made with the integrated circuits included in the semiconductor chips. One or more metal layers may be applied to the contact elements of the semiconductor chips. The metal layers may be manufactured with any desired geometric shape and any desired material composition. The metal layers may, for example, be in the form of a layer covering an area. Any desired metal or metal alloy, for example, from aluminum, titanium, gold, silver, copper, palladium, platinum, nickel, chromium or nickel vanadium, may be used as the material. The metal layers need not be homogenous or manufactured from just one material, that is to say various compositions and concentrations of the materials contained in the metal layers are possible.
- The devices may contain one or more metal layers. The metal layers may, for example, be used to produce a redistribution layer. The metal layers may be used as wiring layers to make electrical contact with the semiconductor chips from outside the devices or to make electrical contact with other semiconductor chips and/or components contained in the devices. The metal layers may be manufactured with any desired geometric shape and any desired material composition. The metal layers may, for example, be composed of conductor tracks, but may also be in the form of a layer covering an area. Any desired metals, for example, copper, aluminum, nickel, palladium, silver, tin or gold, metal alloys or metal stacks may be used as the material. The metal layers need not be homogenous or manufactured from just one material, that is to say various compositions and concentrations of the materials contained in the metal layers are possible. Furthermore, the metal layers may be arranged above or below or between electrically insulating layers.
- The semiconductor chips may be placed on carriers. The carriers may be of any shape, size or material. During the fabrication of the devices the carriers may be connected to each other. The carriers may also be made from one piece. The carriers may be connected among each other by connection means with the purpose of separating some of the carriers in the course of the fabrication. Separation of the carriers may be carried out by mechanical sawing, a laser beam, cutting, stamping, milling, etching or any other appropriate method. The carriers may be electrically conductive. They may be fabricated from metals or metal alloys, for example, copper, copper alloys, iron nickel, aluminum, aluminum alloys, or other appropriate materials. The carriers may be, for example, a leadframe or a part of a leadframe. Furthermore, the carriers may be plated with an electrically conductive material, for example, copper, silver, iron nickel or nickel phosphorus. It may also be provided that the carriers are removed from the devices during production of the devices.
- The devices may include an encapsulation material, which may be electrically insulating. The encapsulation material may cover any fraction of any number of surfaces of the components of the device. The encapsulation material may serve various functions. It may be used, for example, to electrically insulate components of the device from each other and/or from external components, but the encapsulation material may also be used as a platform to mount other components, for example, wiring layers. The encapsulation material may be used to produce fan-out type packages. In a fan-out type package at least some of the external contact elements and/or conductor tracks connecting the semiconductor chip to the external contact elements are located laterally outside of the outline of the semiconductor chip or do at least intersect the outline of the semiconductor chip. Thus, in fan-out type packages, a peripherally outer part of the package of the semiconductor chip is typically (additionally) used for electrically bonding the package to external applications, such as application boards etc. This outer part of the package encompassing the semiconductor chip effectively enlarges the contact area of the package in relation to the footprint of the semiconductor chip, thus leading to relaxed constraints in view of package pad size and pitch with regard to later processing, e.g., second level assembly.
- The encapsulation material may be deposited on the components of the device using various techniques. For example, the encapsulation material may be deposited by printing or from a gas phase or a solution or by using any other appropriate method. The encapsulation material may, for example, contain silicone material or may entirely consist of silicone (or polymerized siloxanes or polysiloxanes). The encapsulation material may have an elastic modulus of, for example, less than 100 MPa. The encapsulation material may be thermally conducting so that it can dissipate the heat generated by the semiconductor chips. It may also be provided that the devices contain encapsulation material that is thermally insulating.
- Furthermore, the encapsulation material may be any appropriate duroplastic, thermoplastic or thermosetting material or laminate (prepreg) and may contain filler materials. This kind of encapsulation material may be deposited, for example, by compression molding, injection molding, powder molding, potting, dispensing, jetting or lamination.
- One or more through-holes may be created in the encapsulation material. The through-holes may, for example, expose portions of a metal layer to allow electrical connection to be made to the metal layer from outside the device. The through-holes may be large enough to receive solder balls or solder deposits. This may be used for stacking devices on top of each other. The through-holes may, for example, be produced by laser ablation, etching, photo-lithographic structuring, mechanical drilling or any other suitable process known to a person skilled in the art.
- The devices described below include external contact elements, which may be of any shape, size and material. The external contact elements may be accessible from outside the device and may thus allow electrical contact to be made with the semiconductor chips from outside the device. Furthermore, the external contact elements may be thermally conducting and may serve as heat sinks for dissipating the heat generated by the semiconductor chips. The external contact elements may be composed of any desired electrically conducting material. The external contact elements may include external contact pads. Solder material may be deposited on the external contact pads. The solder material may have the shape of solder balls and may, for example, be composed of SnPb, SnAg, SnAgCu, SnAgCuNi, SnAu, SnCu and/or SnBi.
-
FIG. 1 schematically illustrates a cross-sectional view of adevice 100. Thedevice 100 includes ametal layer 10, asemiconductor chip 11 and anencapsulation material 12. Themetal layer 10 has afirst face 13 and asecond face 14 opposite to the first 13. Thesemiconductor chip 11 has afirst face 15 and asecond face 16 opposite to thefirst face 15. Thesemiconductor chip 11 is placed over themetal layer 10 with itsfirst face 15 facing thefirst face 13 of themetal layer 10. Furthermore, thesemiconductor chip 11 is electrically coupled to themetal layer 10. Theencapsulation material 12 covers thefirst face 13 of themetal layer 10 and thesemiconductor chip 11. At least one through-hole 17 extends from thefirst face 13 of themetal layer 10 through theencapsulation material 12. The through-hole 17 is unfilled or at least not completely filled with a material so that the through-hole 17 is accessible from outside thedevice 100. Furthermore, the portion of thefirst face 13 of themetal layer 10, which is exposed by the through-hole 17, is accessible from outside thedevice 100. -
FIG. 2 schematically illustrates a cross-sectional view of amodule 200. Themodule 200 consists of afirst device 20 and asecond device 21. Thefirst device 20 includes afirst semiconductor chip 22 and a plurality of firstexternal contact pads 23 electrically coupled to thefirst semiconductor chip 22. Thesecond device 21 includes ametal layer 10 having afirst face 13 and asecond semiconductor chip 11 having afirst face 15. Thesecond semiconductor chip 11 is attached to themetal layer 10 with itsfirst face 15 facing thefirst face 13 of themetal layer 10. Thesecond device 21 further includes anencapsulation material 12 covering thefirst face 13 of themetal layer 10 and thesemiconductor chip 11. A plurality of through-holes 17 extend from thefirst face 13 of themetal layer 10 through theencapsulation material 12. Themodule 200 further contains a plurality of solder bumps 24 electrically coupling themetal layer 10 to the firstexternal contact pads 23, wherein each of the solder bumps 24 is placed at least partially in a respective one of the through-holes 17. -
FIGS. 3A to 3M schematically illustrate a cross-sectional view of one embodiment of a method of manufacturing adevice 300, which is illustrated inFIG. 3M . Thedevice 300 is an implementation of thedevice 100 illustrated inFIG. 1 . The details of thedevice 300 that are described below can therefore be likewise applied to thedevice 100. Similar or identical components of thedevices - As illustrated in
FIG. 3A , acarrier 30 is provided. Thecarrier 30 may be a plate or a foil made of a rigid material, for example, a metal or a metal alloy, such as copper, aluminum, nickel, CuFeP, steel or stainless steel. Thecarrier 30 may have a flat upper surface on which the semiconductor chips 11 are placed later on. The shape of thecarrier 30 is not limited to any geometric shape, and thecarrier 30 may have any appropriate size. For example, the thickness of thecarrier 30 may be in the range from 50 μm to 1 mm. Furthermore, thecarrier 30 may be structured. Thecarrier 30 may be, for example, a leadframe or a part of a leadframe. Moreover, thecarrier 30 may be plated with an electrically conductive material, for example, copper, silver, iron nickel or nickel phosphorus. - A
material 31, for example, an adhesive material, may be deposited on the upper surface of thecarrier 30 as illustrated inFIG. 3B . Theadhesive material 31 may be made of a polymer or any other suitable material. Theadhesive material 31 may contain silicone, i.e. polymerized siloxanes or polysiloxanes, or fluorinated silicone or may be entirely made of silicone. Theadhesive material 31 may further be a mixture of silicone and epoxy resin or a mixture of silicone and polyimide. After hardening, theadhesive material 31 may have an elastic modulus of less than 100 MPa, less than 50 MPa or 20 MPa or 10 MPa or 5 MPa or 2 MPa or 1 MPa or 500 kPa or 200 kPa or 100 kPa or 50 kPa or 20 kPa. The elastic modulus is also known as the Young's modulus, modulus of elasticity or tensile modulus. The elastic modulus may be defined as the ratio of stress, which has units of pressure, to strain, which is dimensionless; therefore the elastic modulus itself has units of pressure. - The elastic modulus of the
adhesive material 31 as described above may allow a floating mounting of the semiconductor chips 11. Due to the different thermal expansion coefficients of thecarrier 30 and the semiconductor chips 11, floating mounting of thesemiconductor chip 11 is desired to reduce the mechanical stress induced during temperature cycles. As an example, copper of which thecarrier 30 may be manufactured has a thermal expansion coefficient of about 17×10−6/K and silicon of which the semiconductor chips 11 may be manufactured has a thermal expansion coefficient of about 3×10−6/K. - The
adhesive material 31 may have a thermal conductivity, for example, in the range between 0.1 W/mK and 5 W/mK or higher. Alternatively, theadhesive material 31 may be thermally insulating. Theadhesive material 31 may exhibit low outgassing during cure and high thixotropy. Elastosil may be used for theadhesive material 31, for example, Elastosil RT705, which is commercially available. - The
adhesive material 31 may be deposited at those places of the upper surface of thecarrier 30 where the semiconductor chips 11 are placed later on. When deposited theadhesive material 31 may be fluid, viscous or waxy. The deposition of theadhesive material 31 may, for example, be performed by stencil printing, screen printing, dispensing or any other appropriate method. - As illustrated in
FIG. 3C , twosemiconductor chips 11 as well as possibly further semiconductor chips are placed over the islands of theadhesive material 31 deposited on thecarrier 30. Although the islands of theadhesive material 31 and the semiconductor chips 11 have the same surface areas inFIG. 3C , their surface areas may be different. The semiconductor chips 11 may be arranged in an array. Furthermore, any suitable array ofsemiconductor chips 11 may be placed on the carrier 30 (only two of the semiconductor chips 11 are illustrated inFIG. 3C ). For example, more than 50 or 500 or 1000semiconductor chips 11 may be placed on thecarrier 30. The semiconductor chips 11 are relocated on thecarrier 30 in larger spacing as they have been in the wafer bond. The semiconductor chips 11 may have been manufactured on the same semiconductor wafer, but may alternatively have been manufactured on different wafers. Furthermore, the semiconductor chips 11 may be physically identical, but may also contain different integrated circuits and/or represent other components and/or may have different outer dimensions and/or geometries. The semiconductor chips 11 may have a thickness in the range between 50 μm and several hundred micrometers. The semiconductor chips 11 may be placed on thecarrier 30 with theirfirst faces 15 facing away from thecarrier 30 and theirsecond faces 16 opposite to the first faces 15 facing thecarrier 30. The first and second faces 15, 16 may be main faces of the semiconductor chips 11. The first faces 15 may be activemain faces 15 of the semiconductor chips 11, on whichcontact pads 32 may be located. The integrated circuits embedded in the semiconductor chips 11 can be electrically accessed via thecontact pads 32, which may be made of a metal, for example, aluminum or copper. - A pick-and-place tool may be used capable of picking the semiconductor chips 11 and placing them on the
adhesive material 31. The semiconductor chips 11 may be pressed in theadhesive material 31. - After the placement of the semiconductor chips 11, the
adhesive material 31 may be cured (hardened) by a heat treatment at moderate temperatures, for example, temperatures of less than 200° C. or 140° C. or 100° C. for several minutes. The heat treatment may be performed by using a hot plate or an oven. - Photo imaging may be performed to store the positions and angles of the semiconductor chips 11 placed on the
carrier 30. Depending on the accuracy of the positioning system used to place the semiconductor chips 11, photo imaging may not be necessary. - Before the deposition of the encapsulation material 12 a leveling process may be performed to align the first faces 15 of the semiconductor chips 11. For that, a further carrier, for example, a wafer, may be pressed onto the semiconductor chips 11. The leveling process may be performed before or after the
adhesive material 31 is hardened. - As illustrated in
FIG. 3D , theencapsulation material 12 is deposited on the semiconductor chips 11 and the exposed surfaces of thecarrier 30. The gaps between the semiconductor chips 11 are also filled with theencapsulation material 12. The height d1 of theencapsulation material 12 above the first faces 15 of the semiconductor chips 11 may be at least 10 μm and around 30 μm. After its deposition theencapsulation material 12 may provide planar sections on its upper surface, which are coplanar to the upper surface of thecarrier 30. These planar surfaces may be used to mount other components, such as a redistribution layer. - The
encapsulation material 12 used for covering the semiconductor chips 11 may be electrically insulating and made of a polymer or any other suitable material. Theencapsulation material 12 may contain silicone or fluorinated silicone or may be entirely made of silicone. Theencapsulation material 12 may further be a mixture of silicone and epoxy resin or a mixture of silicone and polyimide. After hardening, theencapsulation material 12 may have an elastic modulus of less than 100 MPa, less than 50 MPa or 20 MPa or 10 MPa or 5 MPa or 2 MPa or 1 MPa or 500 kPa or 200 kPa or 100 kPa or 50 kPa or 20 kPa. Its elastic modulus may be around 3 MPa. Theencapsulation material 12 may have a thermal conductivity, for example, in the range between 0.1 W/mK and 5 W/mK or higher. Theencapsulation material 12 may exhibit low outgassing during cure and low thixotropy. Elastosil may be used for theencapsulation material 12 though being highly thixotropic, for example, Elastosil RT705, which is commercially available. - The elastic modulus of the
encapsulation material 12 as described above may allow a floating mounting of the semiconductor chips 11 with respect to themetal foil 10 which is placed over the semiconductor chips 11 later on. Due to the different thermal expansion coefficients of the semiconductor chips 11 and themetal foil 10, floating mounting of thesemiconductor chip 11 is desired to reduce the mechanical stress induced during temperature cycles. - During its deposition the
encapsulation material 12 may be fluid, viscous or waxy. The deposition of theencapsulation material 12 may, for example, be performed by stencil printing, screen printing, dispensing or any other appropriate method. - After its deposition, the
encapsulation material 12 may be semi-cured (partially hardened) by a heat treatment at moderate temperatures, for example, temperatures of less than 120° C. or 100° C. or 80° C. for several minutes. The heat treatment may be performed by using a hot plate or an oven. - The
encapsulation material 12 may be structured to create cut-outs or through-holes 33 reaching from the upper surface of theencapsulation material 12 down to thecontact pads 32 of the semiconductor chips 11 as illustrated inFIG. 3E . The aspect ratio of the through-holes 33, which is the ratio of the height to the width of the through-holes 33, may depend on the method used to fill the through-holes 33 with electrically conductive material. Theencapsulation material 12 may, for example, be structured by laser ablation. It may be provided that the diameter of the through-holes 33 is not larger than 50 μm if laser structuring is employed. Laser structuring may be used in one embodiment if the accuracy of the positioning system used to place the semiconductor chips 11 is low, and photo imaging has been performed to store the positions and angles of the semiconductor chips 11 placed on thecarrier 30. Other techniques to create the through-holes 33 are chemical etching or photo-lithographic structuring if theencapsulation material 12 contains a photo-sensitive component. A further alternative is to use a printing technology for the deposition of theencapsulation material 12, such as stencil printing or screen printing, and to leave at least portions of thecontact pads 32 exposed when printing theencapsulation material 12 on thecarrier 30 and the semiconductor chips 11. -
Solder material 34 may be placed in the through-holes 33 as illustrated inFIG. 3F . Thesolder material 34 may be applied by using stencil printing or other suitable printing methods. In another embodiment, pre-shaped solder balls having diameters not larger than the diameters of the through-holes 33 may be inserted into the through-holes 33 by brushing or rolling. Furthermore, thesolder material 34 or any other electrically conductive material may be filled into the through-holes 33 by using pressure to fill the material in liquid state into the through-holes 33. It may be provided that thesolder material 34 protrudes from the upper surface of theencapsulation material 12 meaning that thesolder material 34 deposited in the through-holes 33 has a height larger than the height d1. Thesolder material 34 may be made of metal alloys which are composed, for example, from the following materials: SnPb, SnAg, SnAgCu, SnAgCuNi, SnAu, SnCu and SnBi. Thesolder material 34 may contain flux material which exhibits low outgassing. Thecontact pads 32 of the semiconductor chips 11 may have a solderable surface. - As an alternative to the
solder material 34, other electrically conductive materials, such as electrically conductive glue or metal (nano-)particles, may be deposited in the through-holes 33. The metal particles may, for example, be made of a metal, such as silver, gold, copper, tin or nickel. The extensions (average diameter) of the metal particles may be smaller than 100 nm and, in one embodiment, smaller than 50 nm or 10 nm. It may also be provided that only a fraction of the metal particles has such dimensions. For example, at least 10% or 20% or 30% or 40% or 50% or 60% or 70% of the metal particles may have dimensions smaller than 100 nm or 50 nm or 10 nm. The other metal particles may have larger dimensions. - On top of the encapsulation material 12 a redistribution layer may be produced. One possibility to produce the redistribution layer is to use a standard PCB (printed circuit board) industry process flow. As illustrated in
FIG. 3G , ametal layer 10, for example, a metal foil, may be applied with itsfirst face 13 to the upper surface of theencapsulation layer 12. Themetal foil 10 may be made of copper, aluminum or any other metal, metal alloy or metal stack. Themetal foil 10 may be solderable so that it does not completely dissolve at locations where a solder process is performed. The thickness of themetal foil 10, for example, a copper foil, may be in the range between 6 and 500 μm and in the range between 8 and 200 μm. Themetal layer 10 may also consists of stacked metal layers. For example, a copper layer, a nickel layer and another copper layer may be stacked on top of each other. Each of the three layers may have a thickness of at least 1 μm. The reduced thickness of the stacked metal layers when compared to a foil made of, for example, pure copper may be due to the lower solubility of nickel by solder material. Instead of the nickel layer other metal layers may be used that have a lower solubility in solder material than copper. - The
metal foil 10 may be laminated onto the underlying structures by applying vacuum and pressure for a time suitable to adhere themetal foil 10 to theencapsulation material 12. Furthermore, heat may be applied during the lamination of themetal foil 10. After the lamination of themetal foil 10 heat and pressure may be applied to melt thesolder material 34 embedded in theencapsulation material 12. The temperature may be in the range between 200 and 400° C. By melting thesolder material 34, a soldering process is initiated which produces soldered joints between thecontact pads 32 of the semiconductor chips 11 and themetal foil 10. Due to the heat applied during the soldering process, theencapsulation material 12 may be cured and may connect firmly with themetal foil 10. Themetal foil 10 may be perforated to allow outgassing of theencapsulation material 12 and thesolder material 34 during cure. - If electrically conductive glue is deposited in the through-
holes 33 instead of thesolder material 34, a temperature higher than, for example, 150° C. may be applied in order to cure the glue. If metal (nano-)particles are deposited in the through-holes 33, a temperature high enough to sinter the metal particles may be applied. The temperature may, for example, be higher than 150 or 200° C. and depends on the diameter of the metal particles. - On top of the
metal foil 10, a dry resist film may be laminated, which is photostructurable. Recesses may be formed in the resist film by exposure to light having a suitable wave-length. For that, a laser beam and the data recorded during the photo imaging may be used. If the accuracy of the positioning system used to place the semiconductor chips 11 is high enough, the resist film may be selectively exposed to the light of the suitable wave-length emitted through a mask. Subsequently, the resist film is developed and the thereby exposed portions of themetal foil 10 are etched. Afterwards the resist film is stripped off, and only the structuredmetal foil 10 remains on theencapsulation material 12 as illustrated inFIG. 3H . - A
layer 35, which may consist of a silicone material and a ductile electrically insulating material, may be applied to the structuredmetal foil 10 and the exposed portions of theencapsulation material 12 as illustrated inFIG. 3I . Thelayer 35 may be electrically insulating and thermally conductive. For example, thelayer 35 may have a thickness of about 20 μm. Thelayer 35 may, for example, be stencil printed or screen printed leavingexternal contact pads 36 open at appropriate locations. Thelayer 35 may be cured and cleaned afterwards. Moreover, prior to the deposition of the layer 35 a further layer may be deposited from the gas phase, for example, by sputtering. The further layer may consist of amorphous carbon, for example, HDMC, or ceramic material. Thelayer 35 may prevent solder material from bridging between conductor tracks and creating short circuits. Thelayer 35 also provides protection from the environment. - The
layer 35 may be photostructurable. By exposure to light having a suitable wave-length and subsequent development, recesses may be formed in thelayer 35 to expose theexternal contact pads 36. -
Solder material 37 may be applied onto the surfaces of theexternal contact pads 36 exposed from thelayer 35 as illustrated inFIG. 3J . Thesolder material 37 may be applied by printing, for example, stencil printing, followed by a heat-treatment process to melt thesolder material 37. The solder material may, for example, be composed of SnPb, SnAg, SnAgCu, SnAgCuNi, SnAu, SnCu and/or SnBi. Theexternal contact pads 36 and thesolder material 37 may be used as external contact elements later on to electrically couple thedevices 300 to other components, for example, a PCB. Theexternal contact pads 36 may be laterally shifted from thecontact pads 32 of the semiconductor chips 11. Prior to the application of thesolder material 37, theexternal contact pads 36 may be cleaned, for example, by RIE (reactive ion etching) or chemical cleaning, in order to remove solder stop material and/or embedded material remained on theexternal contact pads 36. Instead of thesolder material 37, other materials, for example, NiAu, may be applied onto the surfaces of theexternal contact pads 36, which prevent oxidation of theexternal contact pads 36. - Before or after the application of the
solder material 37, through-holes 38 extending through thecarrier 30 may be created as illustrated inFIG. 3K . The through-holes 38 may be essentially orthogonal to thefirst face 13 of themetal foil 10. The through-holes 38 expose portions of theencapsulation material 12. The diameter d2 of the through-holes 38 is not necessarily uniform and may be in the range from 200 to 800 μm, the diameter d2 may be larger than 210 or 220 or 230 or 240 or 250 or 260 or 270 or 280 or 290 or 300 μm. The cross section of the through-holes 38 (parallel to thefirst face 13 of the metal foil 10) may have any appropriate shape, for example, it may be circular-, rectangular- or square-shaped. The cross section of each of the through-holes 38 may have an area of at least 3.0×104 or 3.2×104 or 3.4×104 or 3.6×104 or 3.8×104 or 4.0×104 or 4.5×104 or 5.0×104 or 5.5×104 or 6.0×104 or 6.5×104 or 7.0×104 μm2. The cross sections of the through-holes 38 may be large enough to receive solder bumps, for example, solder balls, later on. - The
carrier 30 may be structured by any appropriate method in order to produce the through-holes 38, for example, by etching, a stamping process, laser ablation, mechanical drilling. For example, a dry photostructurable resist film may be laminated on top of thecarrier 30. Recesses may be formed in the resist film by exposure to light having a suitable wave-length. For that, a laser beam may be used, or the resist film may be selectively exposed to the light of the suitable wave-length emitted through a mask. Subsequently, the resist film is developed and the thereby exposed portions of thecarrier 30 are etched. Afterwards the resist film is stripped off, and only thestructured carrier 30 remains as illustrated inFIG. 3K . The redistribution layer may be protected during the etching process, for example, by performing the etching process only on one side of thedevice 300. - Through-
holes 39 may be produced in theencapsulation material 12 at places where theencapsulation material 12 has been exposed by the through-holes 38 as illustrated inFIG. 3L . The through-holes 39 may be, for example, essentially orthogonal to thefirst face 13 of themetal foil 10 and may expose portions of thefirst face 13 of themetal foil 10. The diameter d3 of the through-holes 39 is not necessarily uniform and may be in the range from 200 to 800 μm, the diameter d3 may be larger than 210 or 220 or 230 or 240 or 250 or 260 or 270 or 280 or 290 or 300 μm. The cross section of the through-holes 39 (parallel to thefirst face 13 of the metal foil 10) may have any appropriate shape, for example, it may be circular-, rectangular- or square-shaped. The cross section of each of the through-holes 39 may have an area of at least 3.0×104 or 3.2×104 or 3.4×104 or 3.6×104 or 3.8×104 or 4.0×104 or 4.5×104 or 5.0×104 or 5.5×104 or 6.0×104 or 6.5×104 or 7.0×104 μm2. The cross sections of the through-holes 39 may be large enough to receive solder bumps, for example, solder balls, later on. - The through-
holes 39 may be produced by a laser beam or any other appropriate method. In case of laser ablation, the laser ablation process may be stopped by themetal foil 10. After the production of the through-holes first face 13 of themetal foil 10 may be cleaned, for example, by using RIE or chemical cleaning, in order to remove embedded material remained on the exposed portions of themetal foil 10. - The diameter d2 of the through-
holes 38 may be equal to the diameter d3 of the through-holes 39, or the diameter d2 may be larger than the diameter d3. In the latter case, each of the through-holes 39 may be centered with respect to the respective through-hole 38. The larger diameter d2 of the through-holes 38 may prevent solder material to come into contact with the electricallyconductive carrier 30 once solder bumps are placed in the through-holes holes 38 and/or 39 with an electrically insulating solder stop layer. In general, the through-holes first face 13 of themetal foil 10 are accessible from outside thedevice 300. - As illustrated in
FIG. 3M , thedevices 300 are separated from one another by separation of thecarrier 30, theencapsulation material 12 and the redistribution layer, for example, by sawing, cutting, laser ablation or etching. - The
devices 300 manufactured by the method described above are fan-out type packages. Theencapsulation material 12 allows the redistribution layer to extend beyond the outline of thesemiconductor chip 11. Theexternal contact elements semiconductor chip 11 but can be distributed over a larger area. The increased area which is available for arrangement of theexternal contact elements encapsulation material 12 means that theexternal contact elements external contact elements external contact elements semiconductor chip 11. - It is obvious to a person skilled in the art that the
devices 300 illustrated inFIG. 3M and the manufacturing thereof as described above are only intended to be an exemplary embodiment, and many variations are possible. For example, further semiconductor chips or passives of different types may be included in thesame device 300. The semiconductor chips and passives may differ in function, size, manufacturing technology etc. Moreover, the redistribution layer may include more than one metal layer. - In the embodiment described above and illustrated in
FIGS. 3A to 3M , thesolder material 34 deposited in the through-holes 33 is melted after the lamination of themetal foil 10. Thesolder material 34 may be melted when thesolder material 37 deposited on theexternal contact pads 36 is melted, i.e. after the deposition of thesolder material 34 its melting temperature is not reached until thesolder material 37 is melted. If electrically conductive glue or metal particles are used instead of thesolder material 34, the electrically conductive glue is cured or the metal particles are sintered when thesolder material 37 is melted. - According to one embodiment, the
encapsulation material 12 deposited on top of the semiconductor chips 11 may be different from theencapsulation material 12 deposited on the exposed portions of thecarrier 30 and covering the side faces of the semiconductor chips 11. The twoencapsulation materials 12 may, for example, differ in terms of their elastic modulus and/or thermal conductivity and/or thixotropy. - According to one embodiment, the
encapsulation material 12 may be deposited using two deposition processes. In a first process, theencapsulation material 12 is deposited on the exposed parts of thecarrier 30 such that the upper surface of theencapsulation material 12 and the first faces 15 of the semiconductor chips 11 form an essentially common plane. In a second process, a layer of theencapsulation material 12 having a thickness d1 is deposited on the previously depositedencapsulation material 12 and the semiconductor chips 11. In another embodiment, in the first process, theencapsulation material 12 is deposited on the exposed parts of thecarrier 30 such that theencapsulation material 12 is higher than the semiconductor chips 11 for about the height d1. In the second process, theencapsulation material 12 is only deposited on the first faces 15 of the semiconductor chips 11. - According to one embodiment, after the deposition of the
encapsulation material 12, no through-holes 33 are created in theencapsulation material 12 as illustrated inFIG. 3E , but themetal foil 10 is laminated on the upper surface of theencapsulation material 12 and is structured. After the structuring of themetal foil 10, theencapsulation material 12 may be structured to create the through-holes 33. Afterwards, thesolder material 34 may be placed in the through-holes 33 and may be melted in order to create an electrical connection between thecontact pads 32 of the semiconductor chips 11 and themetal foil 10. As an alternative to thesolder material 34, electrically conductive adhesive material may be placed in the through-holes 33. Furthermore, nanopastes, which consist of metal particles, such as copper or silver, having dimensions in the nanometer range, may be used instead of thesolder material 34. During application the metal particles may be dispersed in a solvent which evaporates later on. The metal particles are sintered to create electrically conductive connections. - According to one embodiment, after the manufacturing of the through-
holes 33 as illustrated inFIG. 3E an electrically conductive material is deposited in the through-holes 33 and on the upper surface of theencapsulation material 12 thereby forming a redistribution layer. The electrically conductive material may not completely fill the through-holes 33, but only coat the walls of the through-holes 33. The electrically conductive material may be produced by electroless and/or galvanic plating processes. Thereby a seed layer is first electroless deposited onto the upper surface of theencapsulation material 12 and the exposed regions of thecontact elements 32. Materials such as palladium or titanium may be used for the seed layer which usually has a thickness of less than 1 μm. The thickness of the seed layer may be increased by depositing a further layer of an electrically conductive material onto the seed layer. For example, a layer of copper may be electroless deposited onto the seed layer. This copper layer may have a thickness of less than 1 μm. Afterwards another layer of copper may be galvanically deposited, which may have a thickness of more than 5 μm. The electroless copper deposition may also be omitted. - According to one embodiment, the
encapsulation material 12 is applied to thecarrier 30 before the semiconductor chips 11 are placed over thecarrier 30. In this case, the semiconductor chips 11 are pressed into theencapsulation material 12. -
FIGS. 4A to 4K schematically illustrate a cross-sectional view of one embodiment of a method of manufacturing adevice 400, which is illustrated inFIG. 4K . Thedevice 400 is an implementation of thedevice 100 illustrated inFIG. 1 . The details of thedevice 400 that are described below can therefore be likewise applied to thedevice 100. Similar or identical components of thedevices - In order to manufacture the
device 400, acarrier 40 is provided as illustrated inFIG. 4A . Thecarrier 40 may be a plate made of a rigid material, for example, a metal, such as nickel, steel or stainless steel, laminate, film or a material stack. Thecarrier 40 may have at least one flat surface on which components of thedevice 400 can be placed. The shape of thecarrier 40 is not limited to any geometric shape, for example, thecarrier 40 may be round or square-shaped. Thecarrier 40 may have any appropriate size. Anadhesive tape 41, for example, a double sided sticky tape, may be laminated onto thecarrier 40 as illustrated inFIG. 4B . - As illustrated in
FIG. 4C , two ormore semiconductor chips 11 are placed over thecarrier 40. The semiconductor chips 11 can be fixed on theadhesive tape 41 with the first faces 15 of the semiconductor chips 11 facing thecarrier 40. Contactpads 32 may be arranged on the first faces 15 of the semiconductor chips 11. - The semiconductor chips 11 are relocated on the
carrier 40 in larger spacing as they have been in the wafer bond. The semiconductor chips 11 may be physically identical, but may also contain different integrated circuits and/or represent other components. - After the semiconductor chips 11 have been mounted on the
carrier 40, the semiconductor chips 11 are covered with anencapsulation material 12 as illustrated inFIG. 4D . For example, theencapsulation material 12 may be a duroplastic or thermosetting mold material. The gaps between the semiconductor chips 11 are also filled with theencapsulation material 12. Theencapsulation material 12 may be based on an epoxy material and may contain a filling material consisting of small particles of glass (SiO2) or other electrically insulating mineral filler materials like Al2O3 or organic filler materials. Compression molding, injection molding, powder molding or other appropriate molding techniques or other casting techniques may be employed to apply theencapsulation material 12. - As an alternative to the mold material, another polymer material may be used as the
encapsulation material 12 to cover the semiconductor chips 11. Thepolymer material 12 may have the shape of an electrically insulating foil or sheet, which is laminated on top of the semiconductor chips 11 and thecarrier 40. Heat and pressure may be applied for a time suitable to attach the polymer foil orsheet 12 to the underlying structure. The gaps between the semiconductor chips 11 are also filled with thepolymer material 12. Thepolymer material 12 may, for example, be a prepreg (short for preimpregnated fibers) that is a combination of a fiber mat, for example, glass or carbon fibers, and a resin, for example, a duroplastic material. Prepreg materials are usually used to manufacture PCBs (printed circuit boards). Well known prepreg materials that are used in PCB industry and that can be used here as thepolymer material 12 are: FR-2, FR-3, FR-4, FR-5, FR-6, G-10, CEM-1, CEM-2, CEM-3, CEM-4 and CEM-5. Prepreg materials are bi-stage materials, which are flexible when applied over the semiconductor chips 11 and hardened during a heat-treatment. For the lamination of the prepreg the same or similar processes can be used as in PCB manufacturing. - The semiconductor chips 11 covered with the
encapsulation material 12 are released from thecarrier 40, and theadhesive tape 41 is pealed from the semiconductor chips 11 and theencapsulation material 12 as illustrated inFIG. 4E . Theadhesive tape 41 may feature thermo-release properties, which allow the removal of theadhesive tape 41 during a heat-treatment. The removal of theadhesive tape 41 from thecarrier 40 is carried out at an appropriate temperature, which depends on the thermo-release properties of theadhesive tape 41 and is usually higher than 150° C. - After the release of the
carrier 40 and theadhesive tape 41 the first faces 15 of the semiconductor chips 11, which were previously attached to thecarrier 40, as well as the bottom surface of theencapsulation material 12 form a commonplanar surface 42. As illustrated inFIGS. 4F to 4H , a redistribution layer may be applied to thesurface 42. - In the present embodiment, the redistribution layer includes a
metal layer 10 anddielectric layers dielectric layer 43 is deposited on theplanar surface 42 as illustrated inFIG. 4F . Themetal layer 10 is applied to thedielectric layer 43, with itsfirst face 13 facing thedielectric layer 43 and electrical contacts being produced to thecontact pads 32 of the semiconductor chips 11 as illustrated inFIG. 4G . Thedielectric layer 43 has openings in order to produce these electrical contacts. Thedielectric layer 44 is subsequently applied to thedielectric layer 43 and thesecond face 14 of themetal layer 10 as illustrated inFIG. 4H . Thedielectric layer 44 is opened in areas whereexternal contact pads 36 are arranged. - The dielectric layers 43, 44 may be fabricated in various ways. For example, the
dielectric layers dielectric layers dielectric layers dielectric layers - The
metal layer 10 may, for example, be fabricated by metallization followed by structuring of the metallization layer in order to form the conductor tracks of the wiring layer. Any desired metal, for example, aluminum, nickel, palladium, silver, tin, gold or copper, or metal alloy may be used as the material. - The
metal layer 10 may also be generated galvanically. For that, usually a seed layer, for example, a palladium layer, is deposited first, which may be carried out electroless or by using an ink jet printing technique. The seed layer can then be used as an electrode for the galvanic deposition of a further electrically conductive layer, for example, a copper layer. - Another technique that may be employed to generate the
metal layer 10 is laser direct structuring. In case of laser direct structuring an electrically insulating polymer foil is attached on the desired surface. The circuit definition is done by using a laser beam, which activates special additives in the polymer foil in order to allow subsequent selective plating. - Solder bumps 37, for example, solder balls or solder half-spheres, may be placed onto the
external contact pads 36 as illustrated inFIG. 4I . The solder bumps 37 may be applied by ball placement or any other appropriate technique. Thedielectric layer 44 may be a solder stop layer that prevents solder from bridging between the conductor tracks and creating short circuits. Thedielectric layer 44 also provides protection from the environment. - Before or after the placement of the solder bumps 37, through-
holes 45 extending through theencapsulation layer 12 and thedielectric layer 43 may be created as illustrated inFIG. 4J . The through-holes 45 expose portions of thefirst face 13 of themetal layer 10. The diameter d4 of the through-holes 45 may be in the range from 200 to 800 μm, in one or more embodiments the diameter d4 may be larger than 210 or 220 or 230 or 240 or 250 or 260 or 270 or 280 or 290 or 300 μm. The cross section of the through-holes 45 (parallel to thefirst face 13 of the metal layer 10) may have any appropriate shape, for example, it may be circular-, rectangular- or square-shaped. The cross section of each of the through-holes 45 may have an area of at least 3.0×104 or 3.2×104 or 3.4×104 or 3.6×104 or 3.8×104 or 4.0×104 or 4.5×104 or 5.0×104 or 5.5×104 or 6.0×104 or 6.5×104 or 7.0×104 μm2. The cross sections of the through-holes 45 may be large enough to receive solder bumps, for example, solder balls, later on. The through-holes 45 may be produced by any appropriate technique, for example, by etching, a stamping process, laser ablation, photo-structuring or mechanical drilling. The exposed portions of thefirst face 13 of themetal layer 10 may be cleaned, for example, by RIE or chemical cleaning, in order to remove any embedded material remained on these surfaces. - As illustrated in
FIG. 4K , thedevices 400 are separated from one another by separation of theencapsulation material 12 and the redistribution layer, for example, by sawing, cutting, milling, etching or a laser beam. -
FIGS. 5A to 5C schematically illustrate a cross-sectional view of one embodiment of a method ofmanufacturing modules FIGS. 5B and 5C , respectively. Themodules module 200 illustrated inFIG. 2 . The details of themodules module 200. Similar or identical components of themodules - As illustrated in
FIG. 5A , adevice 20 and adevice 21 are provided. Thedevice 20 includes asemiconductor chip 22 and a plurality ofexternal contact pads 23 electrically coupled to thesemiconductor chip 22 via awiring layer 50. Solder bumps 24 are attached to theexternal contact pads 23. Furthermore, thesemiconductor chip 22 and other components of thedevice 20 may be embedded in a packaging orhousing 51, which may be electrically insulating. Thedevice 20 may be manufactured using one of the manufacturing technologies described above in connection with the manufacturing of thedevices device 20 may, for example, be a BGA (ball grid array) device or any other device with contains solder bumps on the bottom side used for external electrical connection of the device. Instead of solder bumps any other external contact elements may be attached to the bottom face of thedevice 20 that allow thedevice 20 to stand off from the component on that thedevice 20 is mounted. Such external contact elements may, for example, be copper posts which may be connected to theexternal contact pads 23 and have solder deposits on their bottom sides. - The
device 21 may, for example, be thedevice FIG. 5A , thedevice 21 is embodied as thedevice 400. Thedevice 21 includes ametal layer 10, asemiconductor chip 11 and anencapsulation material 12. In theencapsulation material 12 through-holes 17 are formed in order to expose portions of thefirst face 13 of themetal layer 10. - As illustrated in
FIG. 5B , thedevice 20 is stacked on top of thedevice 21 such that the through-holes 17 receive the solder bumps 24. The solder bumps 24 are placed on the exposed portions of thefirst face 13 of themetal layer 10. For example, the height h2 of the through-holes 17 may be at least 40% or 50% or 60% or 80% or 90% of the height h1 of the solder bumps 24. Furthermore, the diameter d5 of the solder bumps 24 may equal to or smaller than the diameter d6 of the through-holes 17. In case thedevice 21 is implemented as thedevice 300 illustrated inFIG. 3M , each through-hole 17 corresponds to one of the through-holes 38 and the respective through-hole 39. In case thedevice 21 is implemented as thedevice 400 illustrated inFIG. 4K , each through-hole 17 corresponds to one of the through-holes 45. - The solder bumps 24 are melted in order to initiate a soldering process which produces soldered joints between the
external contact pads 23 of thedevice 20 and themetal layer 10 of thedevice 21 so that thedevices holes 17 allow to produce amodule 500 consisting of thestacked devices module 500. - The
module 500 may be mounted on acircuit board 52, for example, a PCB as schematically illustrated inFIG. 5C . The solder bumps 37 of thedevice 21 may face thecircuit board 52. Thecircuit board 52 may havecontact pads 53, and themodule 500 may be soldered to thecontact pads 53 using the solder bumps 37. It may be provided that melting the solder bumps 24 and melting the solder bumps 37 is performed at the same time. -
FIGS. 6 and 7 schematically illustrate cross-sectional views of adevice devices device 100 illustrated inFIG. 1 . Similar or identical components of thedevices devices device 21 illustrated inFIGS. 5A to 5C . - In the
device 600 theencapsulation material 12 is alaminate material 12, in which thesemiconductor chip 11 is embedded. Thelaminate material 12 covers thefirst face 15 and thesecond face 16 of thesemiconductor chip 11. Thecontact pads 32 of thesemiconductor chip 11 are electrically coupled to the structuredmetal layer 10 via through-connections 34. A structuredmetal layer 60 is arranged on the other side of thelaminate material 12. Both structuredmetal layers connections 61 through thelaminate material 12. The structuredmetal layer 60 is covered with an electrically insulatinglayer 62, which may be thermally conductive. The metal layers 10, 60 and the through-connections holes 17 extend through thelaminate material 12 and expose portions of themetal layer 10. Thelaminate material 12 may, for example, be a prepreg material, such as FR-2, FR-3, FR-4, FR-5, FR-6, G-10, CEM-1, CEM-2, CEM-3, CEM-4 and CEM-5. - According to one embodiment, the
metal layer 60, the through-connections 61 and the electrically insulatinglayer 62 of thedevice 600 may also be omitted. - In the
device 700 thesemiconductor chip 11 is mounted on acarrier 30 using anadhesive material 31, wherein thesecond face 16 of thesemiconductor chip 11 faces thecarrier 30. The side faces of thesemiconductor chip 11 and thecarrier 30 are covered with anencapsulation material 12, which may be thesame encapsulation material 12 as used for thedevice 300 described above. Furthermore, bumps 65 may be formed on thefirst face 15 of thesemiconductor chip 11 by theencapsulation material 12. The structuredmetal layer 10 may be deposited on theencapsulation material 12 and in one embodiment thebumps 65. An electrically insulatinglayer 35 is deposited on the structuredmetal layer 10. The electrically insulatinglayer 35 leavesexternal contact elements 36 open at appropriate locations.Solder balls 37 may be placed on theexternal contact elements 36 located on thecarrier 30. Furthermore, through-holes 17 may extend through thecarrier 30 and theencapsulation material 12 in order to expose portions of themetal layer 10. - The through-
holes 17 may not be arranged directly over thesolder balls 37. It may be provided that the through-holes 17 and thesolder balls 37 are laterally shifted away from each other. In case the through-holes 17 and thesolder balls 37 are positioned on top of each other as illustrated inFIG. 7 , themetal layer 10 may have a sufficient thickness in order to be solderable from both sides or may consist of several metal layers. - In addition, while a particular feature or aspect of an embodiment of the invention may have been disclosed with respect to only one of several implementations, such feature or aspect may be combined with one or more other features or aspects of the other implementations as may be desired and advantageous for any given or particular application. Furthermore, to the extent that the terms “include”, “have”, “with”, or other variants thereof are used in either the detailed description or the claims, such terms are intended to be inclusive in a manner similar to the term “comprise”. Furthermore, it should be understood that embodiments of the invention may be implemented in discrete circuits, partially integrated circuits or fully integrated circuits or programming means. Also, the term “exemplary” is merely meant as an example, rather than the best or optimal. It is also to be appreciated that features and/or elements depicted herein are illustrated with particular dimensions relative to one another for purposes of simplicity and ease of understanding, and that actual dimensions may differ substantially from that illustrated herein.
- Although specific embodiments have been illustrated and described herein, it will be appreciated by those of ordinary skill in the art that a variety of alternate and/or equivalent implementations may be substituted for the specific embodiments shown and described without departing from the scope of the present invention. This application is intended to cover any adaptations or variations of the specific embodiments discussed herein. Therefore, it is intended that this invention be limited only by the claims and the equivalents thereof.
Claims (18)
1. A method of manufacturing a module, comprising:
providing a first device comprising a first semiconductor chip and a plurality of first external contact elements electrically coupled to the first semiconductor chip;
providing a second device comprising a second semiconductor chip, a plurality of second external contact elements and a metal layer comprising a first face and a second face opposite to the first face, the first face of the metal layer facing the second semiconductor chip and the second face of the metal layer facing the plurality of second external contact elements; and
soldering the first external contact elements to the first face of the metal layer.
2. The method of claim 1 , wherein the second device further comprises an encapsulation material covering the first face of the metal layer and the second semiconductor chip.
3. The method of claim 2 , wherein the encapsulation material comprises openings exposing the first face of the metal layer and configured to receive the first external contact elements.
4. The method of claim 1 , comprising wherein the first external contact elements are solder bumps.
5. A method of making a device, comprising:
providing a metal layer having a first layer face;
electrically coupling and placing at least one semiconductor chip over the metal layer with the first layer face facing a first chip face of the semiconductor chip;
covering the first layer face and the semiconductor chip with an encapsulation material; and
extending at least one through-hole through the encapsulation material, the at least one through-hole being open and unfilled and exposing a portion of the first layer face, and wherein the at least one through-hole and the portion of the metal layer exposed therein are physically accessible from outside the device.
6. The method of claim 5 , comprising defining the at least one through-hole to have a cross section of at least 3×104 μm2.
7. The method of claim 5 , further comprising:
electrically coupling an array of solder bumps to a second layer face of the metal layer, the second layer face being opposite to the first layer face.
8. The method of claim 7 , comprising wherein a second layer face layer faces the solder bumps, the second layer face being opposite to the first layer face.
9. The method of claim 5 , further comprising:
a second metal layer covering a second chip face of the semiconductor chip with a second metal layer; and covering the first layer face of the metal layer with a surface of the encapsulation material opposite a surface of the encapsulation material, the second chip face being opposite to the first chip face.
10. The method of claim 9 , comprising extending the at least one through-hole through the second metal layer as well as through the encapsulation material.
11. The method of claim 9 , comprising wherein a cross section of the at least one through-hole where it passes through the second metal layer is larger than a cross section of the through-hole where it passes through the encapsulation material.
12. The method of claim 9 , comprising arranging a first material between the second chip face and the second metal layer, the first material comprising silicone.
13. The method of claim 5 , comprising wherein the encapsulation material has an elastic modulus of less than 100 MPa.
14. The method of claim 5 , wherein the encapsulation material comprises silicone.
15. The method of claim 5 , comprising wherein the at least one through-hole has a cross section of at least 6×104 μm2.
16. The method of claim 5 , comprising extending the at least one through-hole in a direction orthogonal to the first layer face.
17. The method of claim 5 , comprising wherein the at least one through-hole has a length of at least 150 μm.
18. The method of claim 5 , including defining the semiconductor chip to include an array of contact elements arranged on the first chip face.