US20110294388A1 - Water-disintegrable nonwoven fabric - Google Patents
Water-disintegrable nonwoven fabric Download PDFInfo
- Publication number
- US20110294388A1 US20110294388A1 US13/147,895 US201013147895A US2011294388A1 US 20110294388 A1 US20110294388 A1 US 20110294388A1 US 201013147895 A US201013147895 A US 201013147895A US 2011294388 A1 US2011294388 A1 US 2011294388A1
- Authority
- US
- United States
- Prior art keywords
- water
- nonwoven fabric
- fibers
- disintegrable
- disintegrable nonwoven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The present invention provides a water-disintegrable nonwoven fabric having a high strength and flexibility. The water-disintegrable nonwoven fabric includes fibers mechanically entangled with one another and adapted to be disentangled from one another when it is stirred in water. 10 to 50% by mass of the fibers is occupied by ultrafine thermoplastic synthetic fibers each having a fineness of 0.01 to 0.5 dtex and a fiber length of 3 to 10 mm. 90 to 50% by mass of the fibers is occupied by at least one of chemical fibers each having a fineness of 1 to 2 dtex and a fiber length of 5 to 20 mm and pulp fibers having a freeness of 600 to 770 cc.
Description
- The present invention relates to water-disintegrable nonwoven fabrics adapted to be disintegrated to fragments (small pieces) and/or individual fibers or masses of several fibers when stirred in water.
- Water-disintegrable nonwoven fabrics adapted to be disintegrated to fragments (small pieces) and/or individual fibers or masses of several fibers when stirred in water are known. For example, JP1997-78919A (PTL 1) discloses a nonwoven fabric of this kind as a water decaying nonwoven fabric. The nonwoven fabric disclosed therein is obtained by taking the following steps; making a web which is composed of 70 to 97% regenerated cellulose fibers or synthetic fibers by mass each having a fiber length of 5 to 20 mm and 3 to 30% ultrafine pulp fibers by mass each having water retention capacity of 210 to 450% by papermaking treatment, subjecting the web to high pressure water jets treatment so that the fibers may be mechanically entangled with one another, and then drying it. The nonwoven fabric obtained in this manner is suitable to be used as a material for wet tissues, sweeping wipers, diapers, sanitary napkins or the like. Such nonwoven fabric may be easily disintegrated in a large amount of water flow.
-
- {PTL 1} JP 1997-78419 A
- The nonwoven fabric disclosed in PTL 1 uses ultrafine pulp fibers finely beaten in a wetted condition. While such ultrafine fibers have their surface areas enlarged and a hydrogen bonding strength between each of the ultrafine pulp fibers is significantly increased as they are drying compared to that of pulp fibers before being beaten finely and consequently the nonwoven fabric being made of such ultrafine pulp fibers increases in strength, there is a possibility that the nonwoven fabric may become stiff and have a poor flexibility and be deteriorated in texture. In addition, though this nonwoven fabric is made by following the steps of a paper making process and an injection process of high pressure water jets, in these steps, the ultrafine pulp fibers easily fall off from the web and/or it is difficult for the ultrafine pulp fibers to be entangled with other types of fibers. In these respects, manufacturing of the nonwoven fabric disclosed in the cited invention is not necessarily easy.
- An object of the present invention is to provide a water-disintegrable nonwoven fabric adapted to be easily made and having a desirable degree of strength and flexibility.
- According to the present invention, there is provided a water-disintegrable nonwoven fabric including fibers mechanically entangled with one another and being adapted to be disintegrated from one another when the nonwoven fabric is stirred in water.
- The present invention is characterized as follows: 10 to 50% by mass of the above-mentioned fibers is occupied by ultrafine thermoplastic synthetic fibers each having a fineness of 0.01 to 0.5 dtex and a fiber length of 3 to 10 mm, and 90 to 50% by mass of the above-mentioned fibers is occupied by at least one of chemical fibers each having a fineness of 1 to 2 dtex and a fiber length of 5 to 20 mm and pulp fibers having a freeness of 600 to 770 cc.
- According to one embodiment of the invention, the ultrafine thermoplastic synthetic fibers are formed by splitting split fibers.
- According to another embodiment of the invention, the water-disintegrable nonwoven fabric contains 3 to 10% water-soluble binder by mass.
- According to still another embodiment of the invention, the water-disintegrable nonwoven fabric is obtained by taking the following steps of mixing the ultrafine thermoplastic synthetic fibers with at least one of the chemical fibers and the pulp fibers to prepare a slurry, injecting high pressure water jets to a web formed from the slurry, and thereafter drying the web.
- According to yet another embodiment of the invention, the slurry contains a water-soluble binder.
- The water-disintegrable nonwoven fabric according to the present invention uses the ultrafine thermoplastic synthetic fibers each having a fineness of 0.01 to 0.5 dtex and a fiber length of 3 to 10 mm and the fibers are mechanically entangled with one another in the nonwoven fabric. Such unique arrangement allows the water-disintegrable nonwoven fabric to be easily manufactured and, in addition, improves a flexibility and a tensile strength of the nonwoven fabric.
-
FIG. 1 Diagram exemplarily illustrating a part of a process for making a water-disintegrable nonwoven fabric. - A water-disintegrable nonwoven fabric according to the present invention is suitable to be used, for example, as a topsheet adapted to be come in contact with a wearer's skin, a backsheet adapted to be come in contact with a wearer's garment, dry wipes and wet wipes. This nonwoven fabric can be advantageously disintegrated to fragments (small pieces) and/or individual fibers or masses of several fibers (hereinafter referred to as “fragments”) when the nonwoven fabric is thrown in a large amount of water and stirred. Such water-disintegrable nonwoven fabric has a thickness of 0.15 to 0.4 mm and a basis mass of 25 to 60 g/m2 and contains 10 to 50% ultrafine thermoplastic synthetic fibers by mass each having a fineness of 0.01 to 0.5 dtex and a fiber length of 3 to 10 mm. 90 to 50% by mass of the nonwoven fabric is occupied by at least one of chemical fibers having a fineness of 1 to 2 dtex and a fiber length of 5 to 20 mm and pulp fibers having a freeness of 600 to 770 cc. The term “thermoplastic synthetic fibers” used herein means the fibers formed from the thermoplastic synthetic resin adapted for melt spinning by means of an extruder. The term “chemical fibers” used herein includes synthetic fibers inclusive of the thermoplastic synthetic fibers, semisynthetic fibers and regenerated fibers. One example of the semisynthetic fibers is acetate fibers and one example of the regenerated fibers is rayon. These fibers included in the water-disintegrable nonwoven fabric according to the invention are entangled with one another under the effect of high pressure water jets. The water-disintegrable nonwoven fabric may contain a water-soluble binder in order to restrain its liquid-perviousness or to enhance its tensile strength depending on the intended purposes. In contrast, the water-disintegrable nonwoven fabric may contain a hydrophilizing agent in order to improve its liquid-perviousness or liquid retention capacity.
-
FIG. 1 is a schematic diagram exemplarily illustrating a process for making a water-disintegrable nonwoven fabric according to the invention wherein the water-disintegrable nonwoven fabric is denoted by reference numeral 1. The process illustrated inFIG. 1 utilizes the known process of paper making and includes afirst wire part 11, asecond wire part 12, athird wire part 13, adryer drum 14 and areeler 15. Aslurry feeder 16 and awater jets injector 17 are provided so as to cooperate with thefirst wire part 11. Theslurry feeder 16 feeds aslurry 21 containing a fibrous mixture to form the water-disintegrable nonwoven fabric and an appropriate amount of water onto thefirst wire part 11 so that the fibrous mixture may form aweb 22 on thefirst wire part 11. Thewater jets injector 17 includes two ormore nozzle rows 18 each having a plurality of nozzles arranged intermittently in a cross direction (CD) being orthogonal to a machine direction (MD). High pressure water jets are injected to theweb 22 and the fibers forming theweb 22 are mechanically entangled with one another under the effect of predetermined injection energy. Thewater jets injector 17 is provided with asuction box 19 so as to suck the high pressure water jets after working thereof. The high pressure water jets treatedweb 22 is transported by thesecond wire part 12 and then thethird wire part 13 onto a peripheral surface of thedryer drum 14. Theweb 22 is dried by thedryer drum 14 to become the water-disintegrable nonwoven fabric 1 and rolled up by thereeler 15. - When the water-disintegrable nonwoven fabric 1 obtained in this manner is thrown into a large amount of water and stirred, the fibers being mechanically entangled with one another can be disintegrated from one another to fragments.
- Referring to
FIG. 1 , the fibrous mixture to form the water-disintegrable nonwoven fabric and the amount of water are mixed in an appropriate proportion so that, for example, the fibrous mixture may occupy 0.5 to 1.5% by mass of the quantity of theslurry 21. In the fibrous mixture, two or more types of fibers are mixed at the same ratio as that in the water-disintegrable nonwoven fabric 1. More specifically, the fibrous mixture in both the water-disintegrable nonwoven fabric 1 and theslurry 21 contain the ultrafine thermoplastic synthetic fibers having a fineness of 0.01 to 0.5 dtex and a fiber length of 3 to 10 mm at a rate of 10 to 50% by mass. In addition, the fibrous mixture in both the water-disintegrable nonwoven fabric 1 and theslurry 21 contain at least one of (a) the chemical fibers having a fineness of 1 to 2 dtex and a fiber length of 5 to 20 mm and (b) the pulp fibers having a freeness as an indication of the degree of beating, at a rate of 90 to 50% by mass. - As the ultrafine thermoplastic synthetic fibers being contained in the water-disintegrable nonwoven fabric 1 and the
slurry 21, it is possible to use, for example, fibers which are obtained by splitting a commercially available polyester/nylon conjugate fiber having a fineness of 3.3 dtex and being formed to be splittable into 11 fibers. This conjugate fiber may be mechanically treated, for example, by a grinder to split this fiber into 11 ultrafine thermoplastic synthetic fibers having a fineness of about 0.3 dtex. It is also possible to use ultrafine thermoplastic synthetic fibers which are obtained by splitting a commercially available polypropylene/polyester conjugate fiber having a fineness of 3.3 dtex and being formed to be splittable into 16 fibers having a fineness of about 0.21 dtex. In addition to the above-mentioned fibers, ultrafine thermoplastic synthetic fibers which are obtained by splitting a commercially available polyester/nylon conjugate fiber having a fineness of 3.3 dtex and being formed to be splittable into 16 fibers each having a fineness of about 0.21 dtex, ultrafine thermoplastic synthetic fibers which are obtained by splitting a commercially available polypropylene/polyethylene conjugate fiber having a fineness of 2.0 dtex and being formed to be splittable into 16 fibers each having a fineness of about 0.13 dtex, ultrafine thermoplastic synthetic fibers which are obtained by splitting a commercially available polyester/polyethylene conjugate fiber having a fineness of 2.2 dtex and being formed to be splittable into 8 fibers each having a fineness of about 0.28 dtex are possible to be used. Furthermore, it is also possible to use ultrafine thermoplastic synthetic fibers such as melt blown fibers each having a fineness of 0.01 to 0.51 dtex and a fiber length of 3 to 10 mm. - The ultrafine thermoplastic synthetic fibers each having a fiber length of 3 to 10 mm assure that the water-disintegrable nonwoven fabric 1 has a low stiffness, a high flexibility and a high tensile strength in a dry state as well as in a wet state. The term “stiffness” used herein is based on the value measured by Bending Resistance A Method according to JIS L 1096. It is preferable that an average bending resistance of water-disintegrable nonwoven fabric 1 should be 80 mm or less, and the average bending resistance is determined by measuring the stiffness of two or more test pieces of water-disintegrable nonwoven fabric 1 in the length direction corresponding to the machine direction as well as to the cross direction in the process of making the water-disintegrable nonwoven fabric. Assumed that the nonwoven fabric of which the stiffness exceeds 80 mm is used as a sheet in the bodily fluid absorbent article to be put in contact with the wearer's skin, it will be rather difficult to put this sheet in contact with the wearer's skin with a desired fit. A tensile strength of the water-disintegrable nonwoven fabric 1 means a breaking strength value which is obtained when a test piece of 25 mm in width and 150 mm in length is stretched at a tension rate of 100 mm/min with a chuck distance of a tensile tester set at 100 mm. The test pieces of which length direction were corresponding to the machine direction and the test pieces of which length direction were corresponding to the cross direction were prepared and strength of the respective test pieces measured after they had been conditioned at a temperature of 20° C. and R. H. 60% for 24 hours was measured as DRY strength. Strength after the respective test pieces had been impregnated with ion exchanged water corresponding to 200% by mass of the respective test pieces was measured as WET strength. DRY strength of the water-disintegrable nonwoven fabric 1 is 3.0 N or higher per width dimension of 25 mm in MD as well as in CD. WET strength thereof is 2.0 N or higher per width dimension of 25 mm in MD as well as in CD.
- According to the invention, the water-disintegrable property is evaluated in a manner as follows. The evaluation is conducted on the basis of visual observation and measurement of dispersive power. In the visual observation, a test piece of 100×100 mm is dried at a temperature of 100° C. for 2 hours and a dry mass (W1) is determined. Then this test piece is thrown together with 800 ml of distilled water into a vertical liquid separatory funnel shaker (SHKV-200 manufactured by IWKI) and shaken at a shaking speed of 240 rpm for 60 minutes and then the interior of the separatory funnel is visually observed. The water-disintegrable nonwoven fabric 1 according to the invention is disintegrated beyond recognition of the original shape or at least to three fractions. In the dispersive power measurement, the test piece remaining within the liquid separatory funnel after having been visually observed was transferred together with distilled water into a basket made of 2-mesh woven metal wire (mesh size of 11.2 mm, void of 77.8% and adapted for grain diameter of 1.5 mm) and having a longitudinal dimension×transverse dimension×height dimension=100×100×120 mm. Then, the quantity of the test piece remaining in the basket was dried at a temperature of 100° C. for 2 hours and dry mass (W2) was determined. From this dry mass W2 and the dry mass W1 having been determined in the step of visual observation, the dispersive power was obtained by a following equation:
-
{(W 1 −W 2)/W 1}×100=Dispersive power(%) - The water-disintegrable nonwoven fabric 1 according to the invention has a dispersive power of 50% or higher.
- The ultrafine thermoplastic synthetic fibers having a fiber length of 3 to 10 mm are rarely oriented in one direction and not intricately entangled with the fibers of the web when the
web 22 is formed from theslurry 21 in the process ofFIG. 1 . In consequence, theweb 22 in which the fibers are uniformly distributed and the water-disintegrable nonwoven fabric 1 obtained from such web is easily disintegrated in water. The ultrafine thermoplastic synthetic fiber having a fiber length exceeding 10 mm will often prevent theweb 22 being smoothly disintegrable in water, consequently, the water-disintegrable nonwoven fabric 1 from being obtained. The ultrafine thermoplastic synthetic fiber having a fiber length less than 3 mm will make it difficult for the fibers to be entangled with one another and will be apt to fall off from thefirst wire part 11. - Assumed that the content of the ultrafine thermoplastic synthetic fibers in the water-disintegrable nonwoven fabric 1 exceeds 50% by mass, it will be difficult of the
web 22 to assure a desired freeness in the process ofFIG. 1 . Consequently, the productivity of the water-disintegrable nonwoven fabric 1 will be deteriorated. - The pulp fibers being used in the invention may be used for making the water-disintegrable nonwoven fabric 1 liquid-pervious, and the pulp fibers are preferably not beaten in order to make the water-disintegrable nonwoven fabric 1 as flexible as possible or to prevent the pulp fibers from falling off from the
first wire part 11 from theweb 22 in the process ofFIG. 1 . More specifically, the freeness is preferably measured as indication of a degree of beating by Canadian Standard Freeness Tester in accordance with JIS P 2181 and the pulp fibers having the freeness of 600 to 770 cc are preferably used. Even when the pulp fibers meet such requirement, there is a possibility that the water-disintegrable nonwoven fabric 1 might have a high density leading to a high stiffness. The water-disintegrable nonwoven fabric 1 containing the pulp fibers and having a relatively high density is suitable to be used as wipes. - In the process illustrated in
FIG. 1 , the composition of the fibrous mixture contained in theslurry 21 and the injection working conditions for theinjector 17 were appropriately varied to obtain water-disintegrable nonwoven fabrics as the working examples and nonwoven fabrics as the comparative examples, each having a basis mass of 35 g/m2. Compositions, evaluation items, evaluation methods and evaluation results will be indicated in TABLE 1 and described later in details. -
TABLE 1 Composition, evaluation Working Working Working Working Working Working Working Working Working items, etc. Spec, unit, etc. Example 1 Example 2 Example 3 Example 4 Example 5 Example 6 Example 7 Example 8 Example 9 NBKP CSF 720 cc 30% 50% NBKP CSF 400 cc Rayon 1.1 dtex × 7 mm 80% 50% 50% 90% 50% 80% 74% PET 1.45 dtex × 10 mm 30% 50% Split fiber-1 3.3 dtex × 5 mm 20% 20% 20% 10% 50% 50% 50% 18% Split fiber-2 3.3 dtex × 5 mm 20% Water-soluble AQ55S 8% binder Injection working kW/m2 0.0063 0.0063 0.0063 0.0063 0.0063 0.0063 0.0063 0.0063 0.0063 condition Basis mass g/m2 35 35 35 35 35 35 35 35 38 Thickness mm 0.24 0.22 0.34 0.26 0.20 0.30 0.32 0.25 0.30 Density g/cm3 0.146 0.159 0.103 0.135 0.175 0.117 0.109 0.140 0.127 DRY strength MD 9.39 8.42 7.85 4.35 14.01 13.56 9.86 4.14 26.24 (N) CD 5.66 4.35 4.01 3.27 4.85 5.06 4.32 3.11 11.53 DRY extension MD 31.02 20.85 19.54 21.34 11.34 30.15 28.15 21.60 12.27 (%) CD 37.51 30.32 28.64 15.98 12.10 21.39 27.55 14.27 19.97 WET strength MD 6.75 5.46 5.04 4.26 6.47 7.99 5.52 4.73 7.72 (N) CD 4.09 2.26 2.11 2.42 2.69 3.32 2.07 2.94 4.43 WET extension MD 39.45 38.26 38.41 41.68 34.51 34.01 42.59 31.40 29.55 (%) CD 40.89 46.03 44.25 29.60 40.34 32.22 27.90 27.70 51.56 Cantilever bending mm 34 48 40 30 46 50 54 35 78 resistance Water disintegrable Visual ◯ ◯ ◯ ◯ ◯ Δ Δ ◯ Δ property observation Dispersive 78 79 74 87 72 58 63 76 53 power (%) Liquid retention % 24.7% 27.0% 19.1% 26.9% 22.3% 16.1% 7.0% 10.7% 8.1% Liquid absorbing sec 1 sec 1 sec 1 sec 1 sec 1 sec 1 sec 3 sec 1 sec 7 sec time Dispersion area mm2 2256 2585 1974 2500 2116 1680 1260 1520 306 Composition, evaluation Comparative Comparative Comparative Comparative Comparative Comparative items, etc. Spec, unit, etc. Example 1 Example 2 Example 3 Example 4 Example 5 Example 6 NBKP CSF 720 cc NBKP CSF 400 cc 20% Rayon 1.1 dtex × 7 mm 100% 40% 80% 80% 80% PET 1.45 dtex × 10 mm Split fiber-1 3.3 dtex × 5 mm 60% 100% 20% 20% Split fiber-2 3.3 dtex × 5 mm Water-soluble AQ55S binder Injection working kW/m2 0.0063 0.0063 0.0063 0.0063 0.0012 0.0131 condition Basis mass g/m2 35 35 35 35 35 35 Thickness mm 0.36 0.25 0.23 0.24 0.22 0.25 Density g/cm3 0.097 0.140 0.152 0.146 0.159 0.140 DRY strength MD 2.15 14.16 19.52 20.33 2.74 14.23 (N) CD 1.68 2.55 3.66 12.29 1.20 8.58 DRY extension MD 10.40 39.37 38.35 7.30 17.57 35.11 (%) CD 8.30 14.95 18.89 4.30 16.03 38.93 WET strength MD 3.00 5.72 5.52 6.57 2.55 8.24 (N) CD 1.92 2.76 2.16 3.66 1.59 5.10 WET extension MD 29.60 33.91 30.17 27.90 29.82 42.77 (%) CD 18.40 34.65 30.22 25.80 39.08 44.29 Cantilever bending mm 38 52 33 86 resistance Water disintegrable Visual ◯ X X ◯ ◯ X property observation Dispersive 97 14 3 99 91 34 power (%) Liquid retention % 30.8% 18.6% 10.0% 31.3% Liquid absorbing sec 1 sec 1 sec 12 sec 1 sec time Dispersion area mm2 2736 1764 304 3021 - 1. NBKP is abbreviated name of Nadelholz Bleached Kraft Pulp (bleached softwood kraft pulp). This type of pulp having a freeness of 720 cc as measured by Canadian Freeness Standard Filter was used in the working examples and the same type of pulp having a freeness of 400 cc was used in the comparative examples.
2. PET is abbreviated name of polyethylene terephthalate fiber.
3. An ultrafine fiber, which has a fineness of about 0.3 dtex and is obtained by splitting a PET/nylon conjugate fiber having a fineness of 3.3 dtex and a fiber length of 5 mm and being formed to be splittable into 11 fibers, was used as a split fiber-1.
4. An ultrafine fiber, which has a fineness of about 0.21 dtex and is obtained by splitting a polypropylene/PET conjugate fiber having a fineness of 3.3 dtex and a fiber length of 5 mm and being formed to be splittable into 16 fibers, was used as a split fiber-2.
5. Sulfopolyester resin (AQ5SS of Eastman Chemical Company) was used as a water-soluble binder. - 1. The
injector 17 shown inFIG. 1 includes fournozzle rows 18 which have injection nozzles each having an orifice diameter of 95μ and lining up in the cross direction at a pitch of 0.5 mm are arranged in the machine direction.
2. The conditions for injection working being set on therespective nozzle rows 18 were adjusted by varying a working energy quantity in accordance with an equation below: -
Working energy quantity(kW/m2)=1.63×injection pressure(kg/cm2)×injection flow rate (m3/min)/working speed(m/min)/60 -
Injection flow rate(m3/min)=750×total orifice area(m2)×injection pressure(kg/cm2)0.495 - Injection nozzles: having an orifice diameter of 95μ and arranged at a pitch of 0.5 mm
- First, second and third wire parts: LL-70E manufactured by Nippon Filcon Co., Ltd.
- A basis mass indicates an average value of each basis mass of three test pieces each dimensioned in 100×100 mm.
- A thickness indicates an average value of each thickness of three test pieces under measuring pressure of 3 g/cm2 by a dial thickness gauge.
- A density was calculated from the basis mass and the thickness.
- After leaving each test piece having a width dimension of 25 mm and a length dimension of 150 mm in a humidity controlled condition for 24 hours at a temperature of 20° C. and R.H. of 60%, a tensile test was conducted at an inter-chuck distance of 100 mm and a tension rate of 100 m/min to determine a tensile strength at break. Three test pieces being dimensioned to be coincident with one another in the machine direction (MD) and in the cross direction (CD) were prepared, and the tensile strength was determined on these test pieces, respectively, in both directions. Then an average value thereof was calculated as the DRY strength. The water-disintegrable nonwoven fabric according to the present invention preferably has DRY strength of 3 kg or higher in both directions MD, CD.
- A DRY extension percentage is an average value of each extension percentage of the test pieces of when DRY strength at break is measured. The water-disintegrable nonwoven fabric according to the present invention preferably has DRY extension percentage of 10% or higher in both directions MD, CD.
- A WET strength was determined under the same conditions as those of DRY strength except that an amount of ion-exchanged water corresponding to 200% of the mass of the test piece was sprayed onto the test piece and thereby the test piece was impregnated with the ion-exchanged water. The water-disintegrable nonwoven fabric according to the present invention preferably has WET strength of 2 kg or higher in both directions MD, CD.
- A WET extension percentage is an average value of each extension percentage of the test pieces of when WET tensile strength at break is measured. The water-disintegrable nonwoven fabric according to the present invention preferably has WET extension percentage of 20% or higher in both directions MD, CD.
- A stiffness was measured in accordance with Bending Resistance A Method (45° cantilever method) specified by Section 8.19.1 of JIS L 1096. Test results are indicated by average values of measured values which are obtained from three test pieces each having the longitudinal direction thereof aligned in the MD and other three test pieces each having the longitudinal direction thereof aligned in the CD.
- A single test piece of 100×100 mm was dried at a temperature of 100° C. for 2 hours to measure a dry mass (W1). The dried test piece was introduced together with 800 ml of distilled water into a vertical separatory funnel shaking apparatus (SHKV-200 manufactured by IWKI) and shaken at a shaking speed of 240 rpm for 60 minutes. Thereafter the inside of the separatory funnel was visually observed. The water-disintegrable property was ranked as highly disintegrable (circle-mark) if the test piece was observed to be disintegrated beyond recognition, ranked as moderately disintegrable (triangle-mark) if the test piece was observed to be disintegrated to at least three fractions or to visually countable number of fibers, and ranked as poorly disintegrable (x-mark) if disintegration of the test piece was observed to come short of the moderately disintegrable property. The water-disintegrable nonwoven fabric according to the present invention has the highly or moderately water-disintegrable properties.
- The test piece remaining within the liquid separatory funnel after having been visually observed was transferred together with distilled water into a basket made of 2-mesh woven metal wire (mesh size of 11.2 mm, void of 77.8% and adapted for grain diameter of 1.5 mm) and having longitudinal dimension×transverse dimension×height dimension=100×100×120 mm. Then, the quantity of the test piece remaining in the basket was dried at a temperature of 100° C. for 2 hours and dry mass (W2) was determined. With this dry mass W2 and the dry mass W1 having been determined in the step of visual observation, the dispersive power was obtained by a following equation:
-
Dispersive power(%)={(W 1 −W 2)/W 1}×100 - Five 100×100 mm dimensioned paper filters in accordance with JIS P 3801 were layered one on another and a 100×100 mm dimensioned test piece (having a mass W0) was placed on the layer. A burette was used to drop 1 cc of physiologic saline water from a height of 10 mm onto the test piece at a rate of 1 cc/2 sec. After 30 seconds had elapsed from dropping, a mass of the test piece (W1) was determined and the liquid retention percentage was calculated according to a following equation:
-
Liquid retention(%)={(W 1 −W 0)/W 0}×100 - The water-disintegrable nonwoven fabric 1 according to the present invention tends to have a high liquid retention percentage by containing pulp fibers and/or rayon fibers. The disintegrable nonwoven fabric 1 having a liquid retention percentage of 20% or higher is suitable to be used as dry wipes or wet wipes.
- In the step of measuring the liquid retention percentage, a time length from completion of dropping of physiologic saline water to a moment at which all drops of physiologic saline water disappeared from the surface of the test piece was measured. In TABLE 1, a record “measuring time length: 1 sec” means that the time length until all drops of physiologic saline water disappear was 1 second or shorter.
- The water-disintegrable nonwoven fabric 1 according to the present invention may be used in a bodily fluid-absorbent article as a liquid-pervious water-disintegrable nonwoven fabric if the liquid absorption time length is 3 seconds or shorter. If the liquid absorption time length is a range of 6 to 8 seconds due to water-soluble binder contained therein, the water-disintegrable nonwoven fabric 1 according to the present invention may be used in the bodily fluid-absorbent article as a poorly liquid-pervious water-disintegrable nonwoven fabric.
- In the step of measuring the liquid retention percentage, a dimension ML (mm) over which the physiologic saline water dispersed on the surface of the test piece in MD direction and a dimension CL (mm) over which the physiologic saline water dispersed on the surface of the test piece in CD direction were measured and the dispersion area was determined according to a following equation:
-
Dispersion area=ML×CL - The water-disintegrable nonwoven fabric 1 according to the present invention contains rayon and/or pulp fibers both of which are hydrophilic and apt to enlarge the dispersion area. The water-disintegrable nonwoven fabric 1 assuring the dispersion area larger than 2000 mm2 is suitable to be used as dry wipes or wet wipes. In contrast, the water-disintegrable nonwoven fabric 1 of which the dispersion area is smaller than 1800 mm2 is suitable to enhance a spot absorption property of the bodily fluid-absorbent article.
- In the process illustrated in
FIG. 1 , a fibrous mixture including the split fibers-1 of ultrafine thermoplastic synthetic fibers in 20% by mass and chemical fibers in 80% by mass, specifically, rayon fibers each having a fineness of 1.1 dtex was used in a slurry. The injection working was carried out under the conditions that four rows of nozzles each having an injection energy of 0.0063 kW/m2 may be used to obtain a water-disintegrable nonwoven fabric having the same composition as that of the fibrous mixture, a basis mass of 35 g/m2 and a thickness of 0.24 mm. Evaluation results of the water-disintegrable nonwoven fabric are indicated in TABLE 1. - In the working examples 2 through 8, water-disintegrable nonwoven fabrics were obtained by the same process as in the working example 1 except that the composition of the fibrous mixture in a slurry and the composition of the fibrous mixture in the water-disintegrable nonwoven fabrics were differentiated from those in the working example 1 as indicated in TABLE 1. Evaluation results of these water-disintegrable nonwoven fabrics according to the working examples 2 through 8 are indicated in TABLE 1. The water-disintegrable nonwoven fabrics according to the working examples 2 and 5 have a relatively high density and stiffness and are suitable to be used particularly as liquid-absorbent wipes.
- In the working example 9, a water-disintegrable nonwoven fabric having a composition similar to that of the water-disintegrable nonwoven fabric according to the working example 1 except that the slurry being used in the working example 1 contains a water-soluble binder so that the water-disintegrable nonwoven fabric contains the water-soluble binder in 8% by mass is obtained. Evaluation results of the water-disintegrable nonwoven fabric are indicated in TABLE 1. Specifically, being high in DRY strength as well as in WET strength and assuring significant long liquid-absorption time, the water-disintegrable nonwoven fabric according to this working example is suitable to be used as a water-disintegrable backsheet material for bodily fluid-absorbent articles.
- The nonwoven fabrics according to these comparative examples were made under the same working conditions as those for the working example 1 except that the composition of the fibrous mixture in the slurry used in the process of
FIG. 1 was different from the composition of the fibrous mixture in the working example 1. Evaluation results of the nonwoven fabrics according to these comparative examples are indicated in TABLE 1. - The nonwoven fabrics according to these comparative examples were made under the same working conditions as those for the working example 1 except the injection working condition. Evaluation results of the nonwoven fabrics according to the comparative examples 5, 6 are indicated in TABLE 1.
-
- 1 water-disintegrable nonwoven fabric
- 21 slurry
- 22 web
Claims (5)
1. A water-disintegrable nonwoven fabric comprising fibers mechanically entangled with one another and adapted to be disintegrated from one another when the water-disintegrable nonwoven fabric is stirred in water, the water-disintegrable nonwoven fabric being characterized in that:
10 to 50% by mass of the above-mentioned fibers is occupied by ultrafine thermoplastic synthetic fibers each having a fineness of 0.01 to 0.5 dtex and a fiber length of 3 to 10 mm; and
90 to 50% by mass of the above-mentioned fibers is occupied by at least one of chemical fibers each having a fineness of 1 to 2 dtex and a fiber length of 5 to 20 mm and pulp fibers having a freeness of 600 to 770 cc.
2. The water-disintegrable nonwoven fabric defined by claim 1 , wherein the ultrafine thermoplastic synthetic fibers are formed by splitting split fibers.
3. The water-disintegrable nonwoven fabric defined by claim 1 , wherein the water-disintegrable nonwoven fabric contains a water-soluble binder in 3 to 10% by mass.
4. The water-disintegrable nonwoven fabric defined by claim 1 , wherein the water-disintegrable nonwoven fabric is obtained by taking the following steps of mixing the ultrafine thermoplastic synthetic fibers with at least one of the chemical fibers and the pulp fibers to prepare a slurry, injecting high pressure water jets to a web formed from a slurry and thereafter drying the web.
5. The water-disintegrable nonwoven fabric defined by claim 4 , wherein the slurry contains therein a water-soluble binder.