US20090274664A1 - Method of culturing vascular smooth muscle cells, culture device and medical material obtained by the culture - Google Patents

Method of culturing vascular smooth muscle cells, culture device and medical material obtained by the culture Download PDF

Info

Publication number
US20090274664A1
US20090274664A1 US12/227,688 US22768807A US2009274664A1 US 20090274664 A1 US20090274664 A1 US 20090274664A1 US 22768807 A US22768807 A US 22768807A US 2009274664 A1 US2009274664 A1 US 2009274664A1
Authority
US
United States
Prior art keywords
elastin
smooth muscle
muscle cells
vascular smooth
culturing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/227,688
Other languages
English (en)
Inventor
Keiichi Miyamoto
Takashi Horiuchi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JNC Corp
Original Assignee
Chisso Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chisso Corp filed Critical Chisso Corp
Assigned to CHISSO CORPORATION reassignment CHISSO CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HORIUCHI, TAKASHI, MIYAMOTO, KEIICHI
Publication of US20090274664A1 publication Critical patent/US20090274664A1/en
Assigned to JNC CORPORATION reassignment JNC CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CHISSO CORPORATION
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C12—BIOCHEMISTRY; BEER; SPIRITS; WINE; VINEGAR; MICROBIOLOGY; ENZYMOLOGY; MUTATION OR GENETIC ENGINEERING
    • C12N—MICROORGANISMS OR ENZYMES; COMPOSITIONS THEREOF; PROPAGATING, PRESERVING, OR MAINTAINING MICROORGANISMS; MUTATION OR GENETIC ENGINEERING; CULTURE MEDIA
    • C12N5/00—Undifferentiated human, animal or plant cells, e.g. cell lines; Tissues; Cultivation or maintenance thereof; Culture media therefor
    • C12N5/06—Animal cells or tissues; Human cells or tissues
    • C12N5/0602—Vertebrate cells
    • C12N5/069—Vascular Endothelial cells
    • C12N5/0691—Vascular smooth muscle cells; 3D culture thereof, e.g. models of blood vessels
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
    • A61L27/14—Macromolecular materials
    • A61L27/22—Polypeptides or derivatives thereof, e.g. degradation products
    • A61L27/227—Other specific proteins or polypeptides not covered by A61L27/222, A61L27/225 or A61L27/24
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
    • A61L27/36—Materials for grafts or prostheses or for coating grafts or prostheses containing ingredients of undetermined constitution or reaction products thereof, e.g. transplant tissue, natural bone, extracellular matrix
    • A61L27/38—Materials for grafts or prostheses or for coating grafts or prostheses containing ingredients of undetermined constitution or reaction products thereof, e.g. transplant tissue, natural bone, extracellular matrix containing added animal cells
    • A61L27/3804—Materials for grafts or prostheses or for coating grafts or prostheses containing ingredients of undetermined constitution or reaction products thereof, e.g. transplant tissue, natural bone, extracellular matrix containing added animal cells characterised by specific cells or progenitors thereof, e.g. fibroblasts, connective tissue cells, kidney cells
    • A61L27/3826—Muscle cells, e.g. smooth muscle cells
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
    • A61L27/36—Materials for grafts or prostheses or for coating grafts or prostheses containing ingredients of undetermined constitution or reaction products thereof, e.g. transplant tissue, natural bone, extracellular matrix
    • A61L27/38—Materials for grafts or prostheses or for coating grafts or prostheses containing ingredients of undetermined constitution or reaction products thereof, e.g. transplant tissue, natural bone, extracellular matrix containing added animal cells
    • A61L27/3804—Materials for grafts or prostheses or for coating grafts or prostheses containing ingredients of undetermined constitution or reaction products thereof, e.g. transplant tissue, natural bone, extracellular matrix containing added animal cells characterised by specific cells or progenitors thereof, e.g. fibroblasts, connective tissue cells, kidney cells
    • A61L27/383—Nerve cells, e.g. dendritic cells, Schwann cells
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
    • A61L27/36—Materials for grafts or prostheses or for coating grafts or prostheses containing ingredients of undetermined constitution or reaction products thereof, e.g. transplant tissue, natural bone, extracellular matrix
    • A61L27/38—Materials for grafts or prostheses or for coating grafts or prostheses containing ingredients of undetermined constitution or reaction products thereof, e.g. transplant tissue, natural bone, extracellular matrix containing added animal cells
    • A61L27/3895—Materials for grafts or prostheses or for coating grafts or prostheses containing ingredients of undetermined constitution or reaction products thereof, e.g. transplant tissue, natural bone, extracellular matrix containing added animal cells using specific culture conditions, e.g. stimulating differentiation of stem cells, pulsatile flow conditions
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
    • A61L27/50—Materials characterised by their function or physical properties, e.g. injectable or lubricating compositions, shape-memory materials, surface modified materials
    • A61L27/507—Materials characterised by their function or physical properties, e.g. injectable or lubricating compositions, shape-memory materials, surface modified materials for artificial blood vessels
    • C—CHEMISTRY; METALLURGY
    • C12—BIOCHEMISTRY; BEER; SPIRITS; WINE; VINEGAR; MICROBIOLOGY; ENZYMOLOGY; MUTATION OR GENETIC ENGINEERING
    • C12M—APPARATUS FOR ENZYMOLOGY OR MICROBIOLOGY; APPARATUS FOR CULTURING MICROORGANISMS FOR PRODUCING BIOMASS, FOR GROWING CELLS OR FOR OBTAINING FERMENTATION OR METABOLIC PRODUCTS, i.e. BIOREACTORS OR FERMENTERS
    • C12M25/00—Means for supporting, enclosing or fixing the microorganisms, e.g. immunocoatings
    • C12M25/02—Membranes; Filters
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
    • A61K35/00—Medicinal preparations containing materials or reaction products thereof with undetermined constitution
    • A61K35/12—Materials from mammals; Compositions comprising non-specified tissues or cells; Compositions comprising non-embryonic stem cells; Genetically modified cells
    • C—CHEMISTRY; METALLURGY
    • C12—BIOCHEMISTRY; BEER; SPIRITS; WINE; VINEGAR; MICROBIOLOGY; ENZYMOLOGY; MUTATION OR GENETIC ENGINEERING
    • C12N—MICROORGANISMS OR ENZYMES; COMPOSITIONS THEREOF; PROPAGATING, PRESERVING, OR MAINTAINING MICROORGANISMS; MUTATION OR GENETIC ENGINEERING; CULTURE MEDIA
    • C12N2533/00—Supports or coatings for cell culture, characterised by material
    • C12N2533/50—Proteins

Definitions

  • the present invention relates to a method of culturing vascular smooth muscle cells, to a culture device therefor and to a medical material obtained by the culture.
  • Vascular graft replacement has come to be performed in recent years as surgical treatment for trauma and vascular diseases such as atherosclerosis, but artificial blood vessels have not been realized for small blood vessels with diameters of 5 mm and less. The reason is that obstruction due to thickening of the tunica intima of vascular grafts or thrombus formation cannot be prevented, because of the poor biocompatibility of artificial materials.
  • the major bypass or vascular replacement technique currently used for elastic arteries such as coronary artery and lower leg peripheral arteries is autologous vein grafting. However, approximately 20-30% of all patients requiring vascular replacement do not have suitable blood vessels and are not candidates for autologous vein grafting.
  • extracellular matrixes such as collagen
  • extracellular matrixes such as collagen
  • the lumen surfaces of artificial vessels made of synthetic fibers worked into small diameters Dacron/polyurethane/drawn polytetrafluoroethylene
  • bioabsorbable synthetic polymers for example, polyglycolic acid, polylactic acid, poly ⁇ -caprolactam and the like
  • small-diameter artificial vessels have not been realized because the endothelial cells do not become stably anchored to the extracellular matrix, or the artificial vessels undergo intimal thickening.
  • the blood vessel wall damage that occurs due to endothelial thickening causes smooth muscle cells near the endothelium to undergo a phenotypic change from the normal contractile to synthetic type, thus promoting growth and organization and extending the lesion.
  • Numerous methods of culturing vascular smooth muscle cells have been investigated, as basic research on vascular smooth muscle. Examples thereof include a method of culturing solution containing insulin-like growth factor-I on a laminin-coated culture dish (for example, Patent document 1), and a method of fixing smooth muscle cells onto fibronectin-coated glass and applying shear flow stress for culturing, as a method that takes into account the orientation of the smooth muscle cells (for example, Patent document 2).
  • the present inventors have also developed a crosslinked elastin article having water-soluble elastin crosslinked with a water-soluble crosslinking agent, which can be applied as a biomaterial for regenerative medicine (Patent document 3).
  • the crosslinked elastin article is utilized as a culture substrate for regenerative medicine, and embryonic stem (ES) cells, somatic stem cells, mesenchymal stem cells or the like are cultured on a film surface or tube interior made therefrom, to form organs having desired shapes.
  • ES embryonic stem
  • Culturing of neuroblastoma cells has been carried out using elastin films produced from crosslinked elastin articles, but no biomaterial has been disclosed with special affinity between elastin and vascular smooth muscle cells.
  • Non-patent document 1 Since most cells in the body are present at sites that are subject to mechanical forces, dynamic culturing methods are also known whereby the cell-growing surface is expanded and contracted in order to accomplish cell culturing with growth under conditions similar to in vivo conditions.
  • Patent document 1 Japanese Unexamined Patent Publication No. 2002-335955
  • Patent document 2 Japanese Patent Public Inspection No. 2002-531118
  • Patent document 3 WO 02/096978
  • the present invention is an application of the knowledge that vascular smooth muscle cells grow on elastin as a scaffold.
  • the invention therefore relates to a method of culturing vascular smooth muscle cells characterized by culturing vascular smooth muscle cells on elastin.
  • Vascular smooth muscle cells are subjected to mechanical stress in the body.
  • the vascular smooth muscle cells are cultured under static conditions in which the elastin neither expands nor contracts, until the vascular smooth muscle cells have become bound to the elastin, and then the vascular smooth muscle cells are cultured under dynamic conditions in which the elastin expands and contracts.
  • the invention also incorporates the knowledge that vascular smooth muscle cells grow more specifically on elastin, compared to other vascular cells.
  • the invention therefore further relates to a method of culturing vascular smooth muscle cells by selective growth of the vascular smooth muscle cells, characterized by culturing a mixture of vascular smooth muscle cells and other vascular cells on elastin.
  • the invention still further relates to a culture device for vascular smooth muscle cells, having elastin anchored on a cell-growing surface.
  • a culture device for vascular smooth muscle cells wherein the elastin is anchored on a non-elastic material surface.
  • Another mode thereof is a culture device for vascular smooth muscle cells wherein the elastin is anchored on an elastic material surface.
  • Preferred is a culture device for vascular smooth muscle cells wherein the elastin is anchored onto a silicon rubber sheet. Since such culture devices are usually placed under microscope observation, the transmittance of the cell-growing surface for visible light or ultraviolet light is preferably 50-100%.
  • the invention still further relates to a culture device for vascular smooth muscle cells, wherein the cell-growing surface is composed of a molded crosslinked elastin article.
  • the transmittance of the cell-growing surface of the culture device for visible light or ultraviolet light is preferably 50-100%.
  • the invention yet further relates to a medical material obtained by culturing vascular smooth muscle cells using a culture device for vascular smooth muscle cells that has elastin anchored on a cell-growing surface, and to a medical material obtained by culturing vascular smooth muscle cells on a molded crosslinked elastin article obtained by crosslinking water-soluble elastin.
  • vascular smooth muscle cells on elastin By culturing vascular smooth muscle cells on elastin, and especially by using a culture device having elastin anchored on the cell growth surface for the culturing, it is possible to accomplish selective culturing of vascular smooth muscle cells, and to accomplish the cell culturing while maintaining the normal type (differentiated type) of the vascular smooth muscle cells.
  • a medical material by culturing the vascular smooth muscle cells on the elastin-anchored culture device or molded crosslinked elastin article.
  • FIG. 1 is a bar graph showing the cytotoxicity test results for water-soluble elastin using MTT. The water-soluble elastin was judged to have no cytotoxicity.
  • FIG. 2 is a bar graph showing the cytotoxicity test results for a crosslinking agent (DODE-DSP) using MTT.
  • the crosslinking agent (DODE-DSP) was judged to have no cytotoxicity.
  • FIG. 3 is a bar graph showing the cytotoxicity test results for active ester group (DSP) using MTT.
  • the active ester group (DSP) was judged to have no cytotoxicity.
  • FIG. 4 is a graph showing the results of measuring the coacervation temperature (elastin concentration: 0.1-70 wt %). No coacervation temperature is exhibited at 60% and greater because of the non-agglutinating liquid.
  • FIG. 5 is a bar graph showing the results of measuring the water droplet contact angle on the surface of a sample subjected only to corona discharge (Control), a sample subjected to corona discharge and then elastin treatment (Elastin) and a sample subjected to corona discharge and then collagen treatment (Collagen), in a polystyrene culturing dish. (**P ⁇ 0.0001 vs. control)
  • FIG. 6 is a bar graph showing the results of measuring the water droplet contact angle on the surface of a sample subjected only to corona discharge (Control), a sample subjected to corona discharge and then elastin treatment (Elastin) and a sample subjected to corona discharge and then collagen treatment (Collagen), in a culturing dish with a silicon sheet bottom.
  • FIG. 7 is a set of graphs showing the results of measuring the adhesion and distensibility of vascular cells on a surface-treated polystyrene culturing dish. It shows the a) adhesion and b) distensibility of vascular smooth muscle cells, the c) adhesion and d) distensibility of fibroblasts and the e) adhesion and f) distensibility of vascular arterial endothelial cells.
  • ⁇ represents samples subjected to corona discharge and then collagen treatment
  • ⁇ represents samples subjected to corona discharge and then elastin treatment
  • X represents samples subjected only to corona discharge.
  • FIG. 8 is a bar graph showing the results of measuring the change in orientation angle (0-4 hour) during static culturing.
  • FIG. 9 is a bar graph showing the results of measuring the change in orientation angle (0-4 hour) during dynamic culturing.
  • the stretch conditions were a cycle of 0.5 Hz and a distensibility of 10%.
  • FIG. 10 is a bar graph showing the results of assaying ⁇ -actin and ⁇ -actin in smooth muscle cells cultured on an elastin-coated dish.
  • Arterial vascular walls have a three-layer structure comprising an intima, media and adventitia, and it is a muscular tissue structure with smooth muscle cells as the major components.
  • the intima which directly contacts with the blood has a monolayer squamous epithelium of endothelial cells and, directly under it, a subendothelial layer consisting of a basement membrane, loose connective tissue and a small number of longitudinal smooth muscle cells.
  • the endothelial cell layer covers the vascular lumen, and is oriented in such a manner the cell long axes are parallel to the direction of blood flow.
  • the media is the blood vessel wall and the thickest layer, and the concentric cell layers composing it are made of smooth muscle cells oriented parallel to the pulsating direction.
  • the smooth muscle cells perform the important function of maintaining blood pressure and controlling the distribution of blood flow.
  • elastin fibers type III collagen and proteoglycans
  • the intima and media lies a structure composed of a fenestrated homogeneous elastin layer, known as the internal elastic lamina.
  • the adventitia is composed mainly of fibroblasts, collagen fibers and longitudinal elastic fibers, and a fenestrated homogeneous elastin layer known as the external elastic lamina is likewise present between the media and adventitia.
  • the vascular smooth muscle is in an intimate relationship with elastin layers, and therefore when vascular smooth muscle cells are cultured with a culture device comprising an elastin layer, the elastin acts as a scaffold for the vascular smooth muscle cells.
  • elastin forms tissue that surrounds vascular smooth muscle cells in the body, it is conjectured that the binding of the vascular smooth muscle cells to elastin in the vascular wall media structure and their presence in the elastin matrix while being subjected to mechanical stimulation in the body, are the factors responsible for the normal type of smooth muscle cells. Consequently, culturing of vascular smooth muscle cells on elastin can be accomplished under conditions similar to in vivo tissue, thus suitably maintaining the normal type (differentiated type).
  • the first aspect of the invention relates to a method of culturing vascular smooth muscle cells, characterized by culturing vascular smooth muscle cells on elastin.
  • One mode thereof comprises culturing vascular smooth muscle cells with a culture device having elastin anchored on a cell-growing surface.
  • Another mode employs a molded crosslinked elastin article as the cell-growing surface.
  • any elastin may be used for the invention, including water-soluble elastin, water-insoluble elastin and crosslinked elastin obtained by crosslinking water-soluble elastin with a crosslinking agent.
  • water-soluble elastin and crosslinked elastin according to the invention are preferable for ease of use.
  • Cell culturing methods include dynamic culturing and static culturing.
  • Dynamic culturing involves culturing while contracting and expanding the surface on which the cells grow.
  • Dynamic culturing according to the invention is therefore a method of culturing wherein elastin is anchored onto the cell-growing surface, i.e. the surface on which the culture solution is placed, and the surface is repeatedly contracted and expanded.
  • Most cells in the body are located in areas subject to dynamic forces, and function while being exposed to dynamic environmental changes.
  • shear flow stress is produced in the endothelial cells composing the vascular wall, and periodic tensile load is exerted on the vascular smooth muscle cells and fibroblasts that do not contact with the blood flow.
  • Culturing under conditions similar to vascular smooth muscle cells in the body is dynamic culturing.
  • Dynamic culturing with vascular smooth muscle cells placed under mechanical stress is effective for observing whether dedifferentiation occurs, or for observing the phenomenon of cellular orientation.
  • Static culturing is a common culturing method with the cell-growing surface in a static state, i.e. without expansion or contraction. This culturing method is carried out under conditions that are different from the in vivo environment, but it is still useful as a method for examining the basic properties of vascular smooth muscle cells.
  • ordinary static culturing is known to cause vascular smooth muscle cells to dedifferentiate to the synthetic form, and to promote proliferation. Since cells in this state are not the normal in vivo type, it must be kept in mind that false conclusions can be drawn when they are utilized for drug screening or as a cell culture model for tissue regeneration.
  • the most advantageous culturing method for vascular smooth muscle cells is a method in which the vascular smooth muscle cells are statically cultured until they bind to elastin, and then dynamically cultured by expanding and contracting the cell-growing surface to which the elastin is anchored.
  • the culturing temperature and carbon dioxide gas concentration for static culturing and dynamic culturing may be according to ordinary conditions, preferably with a temperature of approximately 37° C. and a carbon dioxide gas concentration of approximately 5%.
  • a standard frequency for expansion and contraction for dynamic culturing is 0.5 Hz, i.e. one cycle every 2 seconds, but this frequency may be higher or lower.
  • the expansion and contraction may be unaxial stretch in a single direction or biaxial stretch in two directions.
  • the degree of expansion and contraction is generally about 5-50% of the length of the cell-growing surface, but this may be varied depending on the needs of the study. The degree of expansion and contraction is determined in relation to its frequency.
  • the second aspect of the invention is to provide a method of selectively culturing vascular smooth muscle cells, characterized by culturing a mixture of vascular smooth muscle cells and other vascular cells (vascular endothelial cells, vascular smooth muscle cells, fibroblasts, hemocytes, macrophages or the like) on elastin.
  • vascular smooth muscle cells vascular endothelial cells, vascular smooth muscle cells, fibroblasts, hemocytes, macrophages or the like
  • elastin as the surface substance allows specific growth of vascular smooth muscle cells, as opposed to most of the major extracellular matrix substances such as collagen, fibronectin and laminin. It is believed that only the smooth muscle cells recognize elastin among the vascular cells. On the other hand, all cell types bind and distend on collagen without specificity.
  • vascular smooth muscle cells a mixture of vascular smooth muscle cells with other vascular cells on elastin can accomplish growth of the vascular smooth muscle cells alone.
  • elastin-recognizing receptors on the vascular smooth muscle cell surfaces play an important role in this growth.
  • the third aspect of the invention is to provide a culture device for vascular smooth muscle cells by the culturing method described above.
  • elastin is used on the surface on which the vascular smooth muscle cells are to be grown (the surface on which the culture solution is placed).
  • the elastin anchored to the cell-growing surface acts through cell surface receptors to participate in extracellular matrix recognition in signal transduction of vascular smooth muscle cell activity, thus providing a very favorable environment for growth of the vascular smooth muscle cells.
  • the material of the cell-growing surface on the culture device may be elastin anchored on a plastic or silicon rubber sheet, or an elastin molded article produced by crosslinking of water-soluble elastin.
  • a non-elastic plastic material such as polystyrene, polycarbonate, polypropylene or polyacrylonitrile may be employed.
  • any material that can withstand repeated expansion and contraction may be employed, such as silicon rubber, natural rubber, acrylic rubber, polyurethane rubber or the like.
  • An elastin molded article produced by crosslinking water-soluble elastin is elastic and can therefore be used for dynamic culturing. Materials that can be used for dynamic culturing can, of course, also be used for static culturing.
  • the material of the cell-growing surface is transparent.
  • the transmittance of the cell-growing surface for visible light or ultraviolet light is most preferably 50-100%. In some cases, however, the material will not need to be transparent, and the material may therefore be selected without regard to transparency.
  • the water-soluble elastin used for the invention can be obtained by hydrolysis of elastin, and specifically, it may be one or more types of elastin such as a-elastin or ⁇ -elastin obtained by hot oxalic acid treatment of animal cervical ligaments, K-elastin obtained by alkali ethanol treatment of elastin, water-soluble elastin obtained by enzyme treatment with elastase, or tropoelastin as a precursor of the elastin biosynthetic pathway.
  • Water-insoluble elastin is commercially available, and it may be subjected to hot oxalic acid treatment to obtain water-soluble elastin.
  • the cell-growing surface i.e. the surface on which the culture solution is to be placed
  • the cell-growing surface may be chemically or physically activated, a water-soluble elastin solution placed thereover and the activated surface allowed to react with the water-soluble elastin for a fixed period of time, and then the excess elastin solution discarded and the surface dried.
  • the anchoring reaction may be based on a commonly known chemical reaction (hydrogen bonding, ionic bonding, covalent bonding), or a radical bonding reaction.
  • the method of activating the surface of the culture device may be any method that generates highly reactive functional groups (amino, aldehyde, epoxy, carboxyl, hydroxyl, thiol groups, etc.) or radicals.
  • the inactive surface may be treated by carbonylation or carboxyl group introduction with a chemical agent such as chromic acid, sulfuric acid or hypochlorous acid, or by coating with a silane coupling agent containing functional groups, for activation of the culture substrate surface.
  • silane coupling agents there may be mentioned ⁇ -aminopropyltriethoxysilane, N- ⁇ -(aminoethyl)- ⁇ -aminopropyltrimethoxysilane and N- ⁇ -(aminoethyl)- ⁇ -aminopropylmethyldimethoxysilane.
  • a method of polymer coating such as the method of covering the inactive surface with, for example, polyacrylic acid containing added azide groups to introduce active groups, as described in Japanese Unexamined Patent Publication No. 2003-189843. This allows anchoring by photoreaction to be accomplished by pre-azidation of the elastin to be anchored.
  • the water-soluble elastin is preferably reacted immediately after activation of the inactive surface by corona discharge treatment.
  • corona discharge treatment the material with the inactive surface is placed on a glass base, and the tip of the corona flame blow-out point is brought to a position about 5-10 mm distant, and the corona flame is discharged onto the material surface (approximately 9 kV) for about 10-40 seconds.
  • active radicals disappear from the surface that has been activated by corona discharge at the activation sites other than the locations where the water-soluble elastin has been anchored, thus restoring the inactive surface. This prevents anchoring of other substances present in the culture solution during growth of the cells, in order to facilitate a continuous effect of the elastin-anchored surface.
  • the water-soluble elastin is anchored by reaction with the surface-treated material as described above, it does not elute into the culture solution when subsequently contacted with the culture solution.
  • Another preferred mode of the culture device of the invention is a culture device for vascular smooth muscle cells employing a molded crosslinked elastin article having water-soluble elastin crosslinked on the cell-growing surface (bottom).
  • a crosslinked elastin article having water-soluble elastin crosslinked with a crosslinking agent can be produced by the method described in WO 02/096978.
  • the molded crosslinked elastin article produced by this process is contractile and porous (spongy).
  • the crosslinked elastin article can then be shaped into a transparent sheet.
  • the culture device having such a material as the cell-growing surface is suitable for static culturing and dynamic culturing of vascular smooth muscle cells.
  • the elastin molded article is porous, the three-dimensional culturing condition of the vascular smooth muscle cells can be observed under a microscope.
  • a preferred crosslinking agent for the water-soluble elastin is one represented by the following general formula.
  • R 1 and R 3 are ⁇ A> or ⁇ B> represented by the following structural formula, and R 1 and R 3 may be either the same or different,
  • R 4 and R 5 are H, CH 3 or C 2 H 5 , and R 4 and R 5 may be either the same or different
  • R 2 is a compound ⁇ C> or ⁇ D> represented by the following structural formula
  • n is an integer of 1-20
  • m and 1 are integers of 0-15, X and Y are CH 2 or 0, X and Y being either the same or different, Z is C or N, and R 6 , R 7 , R 8 and R 9 are H, CH 3 or C 2 H 5 , and may be either the same or different).
  • the apparatus used for dynamic culturing is made of an elastic material capable of expanding and contracting the entire culture device containing the culture solution. It employs an elastic material having elastin attached to the cell-growing surface, or an elastic elastin molded article composed of crosslinked elastin. Any desired shape may be used. When expansion and contraction are applied uniaxially, a quadrilateral shape is most advantageous. A hexagonal shape may be employed to obtain non-uniformity for the directions of expansion and contraction.
  • a quadrilateral culture device is produced by forming a rectangular box-like enclosure using a relatively thick material that can withstand repeated expansion and contraction, such as a thick natural rubber or silicon rubber sheet.
  • a thin silicon rubber sheet is attached to the enclosure with an adhesive, and then the cell-growing surface is activated by corona discharge or the like to anchor the elastin.
  • a crosslinked elastin sheet is attached to the bottom of the enclosure. For expansion and contraction of the entire culture device, a tensile tool is loaded at the opposing enclosure sections.
  • the apparatus for dynamic culturing may be cylindrical with stopped ends. A hole is formed at one of the stopped ends, a tool that applies expansive force and contractive force is fitted near the opening, and the culture solution is added through the opening for rotated culturing, to allow growth of the vascular smooth muscle cells only inside the cylindrical section.
  • a tool that applies expansive force and contractive force is fitted near the opening, and the culture solution is added through the opening for rotated culturing, to allow growth of the vascular smooth muscle cells only inside the cylindrical section.
  • a cylinder may be formed with crosslinked elastin and the vascular smooth muscle cells grown on the inner surface.
  • a commercially available apparatus such as one by Strex, Inc., may be used as a dynamic culturing apparatus that expands and contracts the cell-growing surface.
  • the fourth aspect of the invention is a medical material obtained by culturing vascular smooth muscle cells on elastin.
  • One mode thereof is obtained by culturing vascular smooth muscle cells using a culture device having elastin anchored on a cell-growing surface. For example, only the inner surface of a silicon rubber tube is activated by a chemical method and elastin is anchored thereto, and the tube is rotated in the culture solution while repeating expansion and contraction, so that only the inner surface becomes coated with vascular smooth muscle cells and can be used as a vascular graft.
  • Another mode is a medical material obtained by culturing vascular smooth muscle cells on a molded crosslinked elastin article obtained by crosslinking water-soluble elastin.
  • a sheet is formed of elastin gel comprising crosslinked water-soluble elastin, and is attached to the bottom of a rectangular box-like enclosure formed of, for example, natural rubber or silicon rubber, to construct box-shaped culture device.
  • the section on which the vascular smooth muscle cells have grown may be cut out and directly applied as a material for in vivo implantation.
  • a tube of approximately the size of a small-diameter artery may be formed of crosslinked elastin, and vascular smooth muscular tissue uniformly cultured and grown on the inner surface thereof, to produce a tissue engineering graft as a substitute small-diameter artery.
  • vascular smooth muscular tissue uniformly cultured and grown on the inner surface thereof.
  • a wide variety of uses are possible for biomedical materials obtained by culturing and growing vascular smooth muscle cells on elastin.
  • a material obtained by a method of culturing vascular smooth muscle cells using crosslinked elastin according to the invention can be utilized for treatment of patients that are normally not candidates for vascular replacement techniques.
  • Defatted porcine aorta was washed with water and then immersed in 5-10 wt % aqueous sodium chloride and allowed to stand for 24 hours in a refrigerator, for dissolution and removal of the collagen. After washing, water was added and the mixture was boiled for 1 hour with a pressure cooker, after which the vascular accretions were removed and the mixture was placed in a mixer for crushing to a tissue fragment size of 1-5 mm. It was then heated for 1 hour in the pressure cooker and washed with water. After transfer to a meshed bag and washing with an electric washer, ethanol was added to a final concentration of 50 vol % and the mixture was allowed to stand for 30 minutes.
  • Ethanol was then added to a final concentration of 70 vol % and the mixture was allowed to stand for 90 minutes. Ethanol was then further added to a final concentration of 90 vol % and the mixture was allowed to stand for 10 hours. Finally, the ethanol was removed and the product was dried under reduced pressure in a desiccator to obtain insoluble elastin (yield: approximately 330 g by dry weight from 2 kg of blood vessels). After adding 45 mL of 0.25 M oxalic acid to 10 g of the insoluble elastin, the mixture was heated at 100° C. for 1 hour.
  • a chemical crosslinking agent was prepared by the method described in WO 02/096978, for production of an elastin structure using water-soluble elastin.
  • the method involves active esterification of the carboxyl groups of dodecanedicarboxylic acid with 4-hydroxyphenyldimethyl-sulfonium methyl sulfate (hereunder, DSP). Specifically, 1 mol of dodecanedicarboxylic acid, 2 mol of DSP and 2 mol of dicyclohexylcarbodiimide (hereunder, DCCD) are dissolved in acetonitrile and the mixture is stirred at 25° C. for 5 hours for reaction. The dicyclohexylurea produced during the reaction process was removed with a glass filter. The reaction mixture (filtrate) was then solidified by dropwise addition into ether. The solid product was dried under reduced pressure to obtain the target crosslinking agent. The chemical structure and purity was confirmed by 1 H-NMR.
  • the MTT method which is based on the principle that viable cells convert 3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyl-2H-tetrazolium bromide (hereunder, MTT) to a formazan product, was used as a toxicity test for the water-soluble elastin and crosslinking agent with respect to vascular smooth muscle cells. Since tetrazolium salts of MTT and the like can serve as substrates of dehydrogenase in the TCA cycle, which is an oxidative phosphorylation reaction in mitochondria, they allow measurement of the inhibition of sample substances on cell activity. A Cell Proliferation Kit I (Roche) was used for the measurement.
  • CSC culture medium vascular smooth muscle cell culturing medium: product of Dainippon Pharmaceutical Co., Ltd.
  • a smooth muscle cell suspension (cell density: 1.5 ⁇ 10 5 cells/mL) was seeded at 10 ⁇ L/well and culturing was carried out at 37° C. in a 5 vol % CO 2 incubator.
  • the medium was aspirated, 100 ⁇ L of CSC medium containing 0.1 vol % fetal bovine serum was added, and culturing was continued for 24 hours in the incubator until cell growth ceased.
  • the water-soluble elastin aqueous solution (concentration: 0.1-5 wt %) produced in Production Example 1
  • the DSP activated dodecanedicarboxylic acid crosslinking agent 50-500 ⁇ M
  • the DSP 0.05-20 mM
  • the sample solution was then aspirated and rinsed with PBS, CSC medium containing 10 vol % fetal bovine serum was added to 100 ⁇ L/well, a specified amount of MTT solution was added prior to stationing overnight in the incubator, and a microplate reader was used for measurement of the absorbance at a measuring wavelength of 550 nm and a reference wavelength of 655 nm.
  • a control was prepared without addition of sample and compared with the measured values. The results are shown in FIG. 1 , FIG. 2 and FIG. 3 .
  • the water-soluble elastin, crosslinking agent and activeester group portion (DSP) were all essentially unchanged with respect to the control within the measured concentration range, or in other words, they had no effect on cell activation and exhibited no toxicity.
  • Water-soluble elastin exhibited a heat-sensitive phenomenon of hydrophobic interaction and aggregation within the molecules or between molecules with increasing solution temperature. This is referred to as “coacervation”, and is known as an important phenomenon in water-soluble elastin.
  • the coacervation temperature can be determined by measuring the solution turbidity. Specifically, a spectrophotometer with a temperature-variable device was used for irradiation of the sample solution with a specific wavelength (640 nm), and the proportion of transmitted light intensity with respect to incident light intensity was calculated as the transmittance. The transmittance was measured while varying the temperature from 10-80° C., and the temperature at which the transmittance reduction was 50% of the total was defined as the coacervation temperature.
  • the coacervation temperature was measured while varying the elastin concentration from 0.1-70 wt %. The results are shown in FIG. 4 . It was confirmed that the coacervation temperature increased with increasing water-soluble elastin concentration, with no aggregation at 60 wt % and higher. These results demonstrated that with a water-soluble elastin concentration of 60 wt % or greater, the water-soluble elastin crosslinked at a temperature of 100° C. or above to obtain a transparent molded article.
  • This treatment results in reaction and anchoring of elastin onto the dish surface that has been activated by the corona discharge, so that it becomes coated with elastin.
  • a collagen-coated dish As a control experiment there was also prepared a collagen-coated dish. The coated state was evaluated by measuring the water droplet contact angle on the surface. Specifically, a 35 ⁇ suspension culture dish was placed on slide glass situated on the placement stage of a contact angle measuring instrument (by ERMA Corp.), 20 ⁇ L of deionized water was added with a microburet, and the contact angle was measured after allowing it to stand for several seconds. The average value of 5 contact angle measurements was recorded as the measured value.
  • Elastin and collagen were anchored onto the surface by activating the hydrophobic surface by corona discharge and reacting it with protein in water. Restoration to the original hydrophobicity in air was observed at approximately 8 hours after discharge (contact angle: approximately 80°). When water alone was added immediately after discharge (control), a portion of the water molecules slowly reacted during restoration to the original hydrophobicity producing a hydrophilic state, and surface change was stabilized at about 8 hours, with a contact angle of about 42°. With immersion in an elastin aqueous solution or collagen aqueous solution immediately after discharge, the contact angles were 25° and 34° respectively after 8 hours, and thus a stabilized surface had been formed in a more hydrophilic state than the control ( FIG. 5 ). These results confirmed that elastin and collagen had been coated onto the corona discharge treated dish surface.
  • a 10 mm-thick silicon rubber sheet was prepared and used to form a box-like enclosure for a culture dish with dimensions of 3 cm length ⁇ 3 cm width ⁇ 1 cm height.
  • a 50 ⁇ m-thick silicon rubber sheet was attached to the bottom using Bathcoke (HJ-132 by Cemedine Co., Ltd.), and this was allowed to stand for a day for complete attachment. After thorough washing with deionized water, autoclave treatment was carried out at 121° C. for 30 minutes for sterilization. The same corona discharge apparatus of Example 1 was used for 45 seconds of surface treatment, and after adding 1 mL of a 100 ⁇ g/mL water-soluble elastin solution and collagen solution, the dish was allowed to stand for 8 hours.
  • An enclosure for a culture dish with dimensions of 3 cm length ⁇ 3 cm width ⁇ 1 cm height was produced using a 10 mm-thick silicon rubber sheet, similar to the one prepared in Example 2, and the elastin gel sheet was attached thereto with an adhesive. After thorough washing with deionized water, autoclave treatment was carried out at 121° C. for 30 minutes for sterilization.
  • the adhesion was judged in the following manner.
  • the cells immediately after seeding are spherical, but generate desmosomes at the first change.
  • integrin aggregates to form desmosomes at the high density region points.
  • the shapes of the cells are essentially spherical. This was defined as the attached state.
  • desmosomes form over the entire cell membrane such that the cells undergo a change in shape to a non-spherical shape. This is the distended state.
  • the adhesion and stretch is evaluated based on these two changes.
  • FIG. 7 The results of determining the adhesion and stretch of each cell type for the elastin- (or collagen)-coated dish are shown in FIG. 7 .
  • the vascular smooth muscle cells were observed to exhibit high adhesion ( ⁇ 63% after 1 hour) and stretch ( ⁇ 62% after 4 hours) for the elastin surface and collagen surface. In particular, it was found that adhesion and stretch were essentially complete with about 1 hour and within 4 hours, respectively.
  • Vascular smooth Fibro- Vascular muscle cells blasts endothelial cells Discharge only X X X Elastin ⁇ X X Collagen ⁇ ⁇ ⁇
  • a dynamic culture device employing the elastin-coated silicon sheet prepared in Example 2, with CSC medium (vascular smooth muscle cell medium: product of Dainippon Pharmaceutical Co., Ltd.), there was seeded 1 mL of a vascular smooth muscle cell suspension prepared to a cell density of 1.0 ⁇ 10 5 (cells/mL).
  • CSC medium vascular smooth muscle cell medium: product of Dainippon Pharmaceutical Co., Ltd.
  • static culturing was carried out at 37° C. in a 5% CO 2 culturing apparatus (OLYMPUS MI-IBC).
  • OLEDUS MI-IBC 5% CO 2 culturing apparatus
  • the static-cultured dynamic culture device was set in a dynamic cell culturing apparatus fixed to a microscope stage, and dynamic cell culturing (uniaxial stretch culturing) was carried out for 4 hours with stretching conditions of 1 cycle every 2 seconds (0.5 Hz) at 10% stretch, with repeated photographing of the same location.
  • Analysis of the photographed images allowed measurement of the orientation angle of the vascular smooth muscle cells in the direction of tension application at each time point during dynamic culturing.
  • FIG. 8 shows the change in orientation angle during static culturing (0-4 hour)
  • FIG. 9 shows the change in orientation angle during dynamic culturing (0-4 hour).
  • ⁇ -actin is characterized by differentiation while ⁇ -actin is mostly dedifferentiated.
  • the amounts of both actins expressed in vascular smooth muscle cells cultured on an elastin-coated dish prepared by the method of Example 1 were divided by the amounts of both actins expressed in vascular smooth muscle cells cultured in a common adhesive cell dish (product of Sumitomo Bakelite Co., Ltd., hydrophilic treated polystyrene) as a control, and the ratios were as shown in FIG. 10 .
  • the smooth muscle cells cultured on elastin had increased ⁇ -actin and reduced ⁇ -actin compared with the actin in the untreated culture dish, thus indicating that differentiation had been induced.
  • Vascular smooth muscle cells were cultured in the same manner as Example 5, using a dynamic culture device employing the elastin gel sheet prepared in Example 3. It was possible to perform three-dimensional microscope observation of the cells growing on the elastin gel sheet.
US12/227,688 2006-05-25 2007-05-24 Method of culturing vascular smooth muscle cells, culture device and medical material obtained by the culture Abandoned US20090274664A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2006-144909 2006-05-25
JP2006144909A JP4989108B2 (ja) 2006-05-25 2006-05-25 血管平滑筋細胞の培養方法、培養器材および培養によって得られる医療用材料
PCT/JP2007/060604 WO2007138973A1 (ja) 2006-05-25 2007-05-24 血管平滑筋細胞の培養方法、培養器材および培養によって得られる医療用材料

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2007/060604 A-371-Of-International WO2007138973A1 (ja) 2006-05-25 2007-05-24 血管平滑筋細胞の培養方法、培養器材および培養によって得られる医療用材料

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US13/613,206 Division US9085758B2 (en) 2006-05-25 2012-09-13 Method of culturing vascular smooth muscle cells, culture device and medical material obtained by the culture

Publications (1)

Publication Number Publication Date
US20090274664A1 true US20090274664A1 (en) 2009-11-05

Family

ID=38778493

Family Applications (2)

Application Number Title Priority Date Filing Date
US12/227,688 Abandoned US20090274664A1 (en) 2006-05-25 2007-05-24 Method of culturing vascular smooth muscle cells, culture device and medical material obtained by the culture
US13/613,206 Active 2027-09-30 US9085758B2 (en) 2006-05-25 2012-09-13 Method of culturing vascular smooth muscle cells, culture device and medical material obtained by the culture

Family Applications After (1)

Application Number Title Priority Date Filing Date
US13/613,206 Active 2027-09-30 US9085758B2 (en) 2006-05-25 2012-09-13 Method of culturing vascular smooth muscle cells, culture device and medical material obtained by the culture

Country Status (5)

Country Link
US (2) US20090274664A1 (ja)
EP (1) EP2020435B1 (ja)
JP (1) JP4989108B2 (ja)
AU (1) AU2007268748A1 (ja)
WO (1) WO2007138973A1 (ja)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108866147A (zh) * 2018-07-06 2018-11-23 宁波美晶医疗技术有限公司 一种细胞形变和细胞活性的动态光学检测方法

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6041294B2 (ja) * 2012-07-26 2016-12-07 公立大学法人秋田県立大学 細胞培養基材、培養容器、及び細胞培養基材の製造方法
JP6143163B2 (ja) * 2013-03-22 2017-06-07 国立大学法人三重大学 弾性組織様構造体の製造方法
CN110694101A (zh) * 2019-11-25 2020-01-17 高敏楠 医用伤口组织止血修复细胞胶水与胶带组合及方法

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040136977A1 (en) * 2001-05-30 2004-07-15 Keiichi Miyamoto Crosslinked elastin and process for producing the same

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU2171900A (en) 1998-12-11 2000-06-26 Advance Tissue Sciences, Inc. Application of shear flow stress to smooth muscle cells for the production of implantable structures
ATE292939T1 (de) * 2000-10-30 2005-04-15 Childrens Medical Center Aus gewebe hergestellte gefässstrukturen
JP2002335955A (ja) 2001-05-23 2002-11-26 Kenji Sofue 血管平滑筋細胞の培養方法
JP2003189843A (ja) 2001-10-17 2003-07-08 Taiko Denki Co Ltd 細胞培養器材

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040136977A1 (en) * 2001-05-30 2004-07-15 Keiichi Miyamoto Crosslinked elastin and process for producing the same

Non-Patent Citations (4)

* Cited by examiner, † Cited by third party
Title
Kitazono et al., 2004, J. Synthetic Organic Chemistry, Vol. 62(5), pgs. 514-519. *
Teng et al., J. Phys. Chem. B 2011, 115, 1608-1615. *
Wilson et al., 1995, JCI, Vol. 96, pgs. 2364-2372. *
Yamamoto et al., 1994, Connective Tissue, Vol. 26, pgs. 245-254. *

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108866147A (zh) * 2018-07-06 2018-11-23 宁波美晶医疗技术有限公司 一种细胞形变和细胞活性的动态光学检测方法

Also Published As

Publication number Publication date
WO2007138973A1 (ja) 2007-12-06
EP2020435B1 (en) 2017-08-30
US9085758B2 (en) 2015-07-21
EP2020435A4 (en) 2010-04-28
EP2020435A1 (en) 2009-02-04
JP4989108B2 (ja) 2012-08-01
AU2007268748A1 (en) 2007-12-06
US20130029420A1 (en) 2013-01-31
JP2007312663A (ja) 2007-12-06

Similar Documents

Publication Publication Date Title
Kikuchi et al. Nanostructured designs of biomedical materials: applications of cell sheet engineering to functional regenerative tissues and organs
EP0494216B1 (en) Surfaces having desirable cell adhesive effects
CN101395267B (zh) 在聚合膜上的工程细胞生产及其在生物工程方面的应用
JP2741378B2 (ja) 固体表面の生物適合性の改良
JP5086398B2 (ja) 心筋様細胞シート、３次元構造体、心筋様組織及びそれらの製造法
CA2454807C (en) Cultured cell construct which contains spheroids of cultured animal cells and the use thereof
Raphel et al. Photoreactive elastin-like proteins for use as versatile bioactive materials and surface coatings
US20050053642A1 (en) Biocompatible materials
US20100196432A1 (en) Biopolymer structures
JPS6339583A (ja) 細胞・組織の基体への付着方法
CA2467836A1 (en) Interfacial biomaterials
US9085758B2 (en) Method of culturing vascular smooth muscle cells, culture device and medical material obtained by the culture
WO2004085606A1 (ja) 細胞培養基質および細胞接着蛋白質またはペプチドの固相化標品
US20110151564A1 (en) Method for proliferation of cells on polyelectrolyte multilayer films and use thereof, particularly for the preparation of cellular biomaterials
Bettini et al. Physicochemical and cell adhesion properties of chitosan films prepared from sugar and phosphate-containing solutions
JPH02502246A (ja) 粘着性細胞成長のための過弗化硫化物
Akiyama et al. Temperature-responsive polymers for cell culture and tissue engineering applications
US20180127700A1 (en) Cell Culture Substrate for Rapid Release and Re-Plating
US11253626B2 (en) Use for peptide uniquely binding to vascular endothelial cells, and peptide
Dee et al. Cell function on substrates containing immobilized bioactive peptides
Giannoulis et al. Characterization of proteins and fibroblasts on thin inorganic films
Dhyani et al. Self-Patterning Silk Films for Cellular Coculture
JP4336756B2 (ja) 動物細胞の培養構築物
JP2006055157A (ja) 細胞培養器具及びその製造方法
JPH02181628A (ja) 生物活性部分の基質への固定方法、生きた細胞の基質への固定方法および細胞培養方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: CHISSO CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MIYAMOTO, KEIICHI;HORIUCHI, TAKASHI;REEL/FRAME:021917/0888

Effective date: 20081028

AS Assignment

Owner name: JNC CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:CHISSO CORPORATION;REEL/FRAME:026187/0940

Effective date: 20110412

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION