US20090104733A1 - Microcrystalline silicon deposition for thin film solar applications - Google Patents

Microcrystalline silicon deposition for thin film solar applications Download PDF

Info

Publication number
US20090104733A1
US20090104733A1 US11/876,173 US87617307A US2009104733A1 US 20090104733 A1 US20090104733 A1 US 20090104733A1 US 87617307 A US87617307 A US 87617307A US 2009104733 A1 US2009104733 A1 US 2009104733A1
Authority
US
United States
Prior art keywords
silicon layer
type
layer
microcrystalline silicon
junction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/876,173
Other languages
English (en)
Inventor
Yong Kee Chae
Soo Young Choi
Shuran Sheng
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Applied Materials Inc
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US11/876,173 priority Critical patent/US20090104733A1/en
Assigned to APPLIED MATERIALS, INC. reassignment APPLIED MATERIALS, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CHAE, YONG KEE, CHOI, SOO YOUNG, SHENG, SHURAN
Priority to CN2008801127040A priority patent/CN101836299B/zh
Priority to JP2010530192A priority patent/JP2011501445A/ja
Priority to PCT/US2008/080834 priority patent/WO2009055502A1/en
Priority to EP08843208A priority patent/EP2206156A1/en
Priority to KR1020107011266A priority patent/KR20100089856A/ko
Publication of US20090104733A1 publication Critical patent/US20090104733A1/en
Priority to US12/493,020 priority patent/US7919398B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/04—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices
    • H01L31/06—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices characterised by potential barriers
    • H01L31/075—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices characterised by potential barriers the potential barriers being only of the PIN type, e.g. amorphous silicon PIN solar cells
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/0248—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies
    • H01L31/036—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by their crystalline structure or particular orientation of the crystalline planes
    • H01L31/0368—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by their crystalline structure or particular orientation of the crystalline planes including polycrystalline semiconductors
    • H01L31/03682—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by their crystalline structure or particular orientation of the crystalline planes including polycrystalline semiconductors including only elements of Group IV of the Periodic Table
    • H01L31/03685—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by their crystalline structure or particular orientation of the crystalline planes including polycrystalline semiconductors including only elements of Group IV of the Periodic Table including microcrystalline silicon, uc-Si
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/04—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices
    • H01L31/06—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices characterised by potential barriers
    • H01L31/075—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices characterised by potential barriers the potential barriers being only of the PIN type, e.g. amorphous silicon PIN solar cells
    • H01L31/076—Multiple junction or tandem solar cells
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/18—Processes or apparatus specially adapted for the manufacture or treatment of these devices or of parts thereof
    • H01L31/1804—Processes or apparatus specially adapted for the manufacture or treatment of these devices or of parts thereof comprising only elements of Group IV of the Periodic Table
    • H01L31/182—Special manufacturing methods for polycrystalline Si, e.g. Si ribbon, poly Si ingots, thin films of polycrystalline Si
    • H01L31/1824—Special manufacturing methods for microcrystalline Si, uc-Si
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02367—Substrates
    • H01L21/0237—Materials
    • H01L21/02373—Group 14 semiconducting materials
    • H01L21/02381—Silicon, silicon germanium, germanium
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02436—Intermediate layers between substrates and deposited layers
    • H01L21/02439—Materials
    • H01L21/02441—Group 14 semiconducting materials
    • H01L21/0245—Silicon, silicon germanium, germanium
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02518—Deposited layers
    • H01L21/02521—Materials
    • H01L21/02524—Group 14 semiconducting materials
    • H01L21/02532—Silicon, silicon germanium, germanium
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02518—Deposited layers
    • H01L21/0257—Doping during depositing
    • H01L21/02573—Conductivity type
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02612—Formation types
    • H01L21/02617—Deposition types
    • H01L21/0262—Reduction or decomposition of gaseous compounds, e.g. CVD
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E10/00—Energy generation through renewable energy sources
    • Y02E10/50—Photovoltaic [PV] energy
    • Y02E10/545—Microcrystalline silicon PV cells
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E10/00—Energy generation through renewable energy sources
    • Y02E10/50—Photovoltaic [PV] energy
    • Y02E10/548—Amorphous silicon PV cells
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
    • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product

Definitions

  • Embodiments of the present invention generally relate to solar cells and methods and apparatuses for forming the same. More particularly, embodiments of the present invention relate to thin film multi-junction solar cells and methods and apparatuses for forming the same.
  • Crystalline silicon solar cells and thin film solar cells are two types of solar cells.
  • Crystalline silicon solar cells typically use either mono-crystalline substrates (i.e., single-crystal substrates of pure silicon) or a multi-crystalline silicon substrates (i.e., poly-crystalline or polysilicon). Additional film layers are deposited onto the silicon substrates to improve light capture, form the electrical circuits, and protect the devices.
  • Thin-film solar cells use thin layers of materials deposited on suitable substrates to form one or more p-i-n junctions. Suitable substrates include glass, metal, and polymer substrates.
  • Microcrystalline silicon film ( ⁇ C-Si) is one type of film being used to form solar cells.
  • Conventional deposition processes of microcrystalline silicon films have slow deposition rates, which disadvantageously reduce manufacturing throughput and increase production costs.
  • a method of forming a thin film multi-junction solar cell over a substrate comprises positioning a substrate in a reaction zone, providing a gas mixture to the reaction zone, wherein the gas mixture comprises a silicon containing compound and hydrogen gas (H 2 ), forming a first region of an intrinsic type microcrystalline silicon layer on the substrate at a first deposition rate, forming a second region of the intrinsic type microcrystalline silicon layer on the substrate at a second deposition rate higher than the first deposition rate, and forming a third region of the intrinsic type microcrystalline silicon layer on the substrate at a third deposition rate lower than the second deposition rate.
  • the gas mixture comprises a silicon containing compound and hydrogen gas (H 2 )
  • a method of forming a thin film multi-junction solar cell over a substrate comprises forming a first p-i-n junction and forming a second p-i-n junction over the first p-i-n junction.
  • the first p-i-n junction is formed by forming a p-type amorphous silicon layer, forming an intrinsic type amorphous silicon layer over the p-type amorphous silicon layer, and forming a first n-type silicon layer over the intrinsic type amorphous silicon layer.
  • the second p-i-n junction is formed by forming a p-type microcrystalline silicon layer, forming an intrinsic type microcrystalline silicon layer over the p-type microcrystalline silicon layer, and forming a second n-type silicon layer over the intrinsic type microcrystalline silicon layer.
  • the intrinsic type microcrystalline silicon layer is formed by forming a first region of the intrinsic type microcrystalline silicon layer at a first deposition rate, forming a second region of the intrinsic type microcrystalline silicon layer at a second deposition rate higher than the first deposition rate, and forming a third region of the intrinsic type microcrystalline silicon layer at a third deposition rate lower than the second deposition rate.
  • the first n-type silicon layer is an n-type amorphous/microcrystalline silicon layer.
  • the first n-type silicon layer is a microcrystalline silicon layer.
  • the second n-type silicon layer is either an amorphous silicon layer or a microcrystalline silicon layer.
  • FIG. 1 is a schematic diagram of a microcrystalline silicon based thin film solar cell oriented toward the light or solar radiation;
  • FIG. 2 is a flow chart illustrating the processing steps for forming an intrinsic microcrystalline silicon layer according to one embodiment of the invention
  • FIG. 3 is a schematic diagram of a multi-junction solar cell oriented toward the light or solar radiation
  • FIG. 4 is a schematic diagram of the multi-junction solar cell of FIG. 3 further comprising a seed layer;
  • FIG. 5 is a schematic diagram of the multi-junction solar cell of FIG. 3 further comprising a seed layer and an amorphous silicon barrier layer;
  • FIG. 6 is a schematic cross-section view of one embodiment of a plasma enhanced chemical vapor deposition (PECVD) chamber in which one or more solar films of a solar cell may be deposited;
  • PECVD plasma enhanced chemical vapor deposition
  • FIG. 7 is a top schematic view of one embodiment of a process system having a plurality of process chambers.
  • FIG. 8 depicts properties of an intrinsic microcrystalline silicon layer deposited according to one embodiment of the invention.
  • Thin film solar cells generally comprise one or more p-i-n junctions.
  • the p-i-n junction generally comprises a p-doped silicon layer or p-type layer and an n-doped silicon layer or n-type layer with an intrinsic layer sandwiched in between the p-type layer and the n-type layer.
  • the intrinsic layer generally comprises an undoped semiconductor layer.
  • the intrinsic layer comprises a microcrystalline silicon layer which is between about 10,000 ⁇ and 30,000 ⁇ thick. Using current methods, a microcrystalline silicon layer of this size takes about one hour to deposit. However, using the methods in the present disclosure, the deposition time for an intrinsic type microcrystalline silicon layer may be reduced by up to 20-30 minutes without significantly damaging the underlying layers.
  • FIG. 1 is a schematic diagram of a microcrystalline silicon based thin film solar cell oriented toward the light or solar radiation.
  • the solar cell 100 comprises an intrinsic type microcrystalline silicon layer 124 formed using the methods described herein.
  • Solar cell 100 comprises a substrate 102 , such as a glass substrate, polymer substrate, metal substrate, or other suitable substrate with thin films formed thereover.
  • the solar cell 100 further comprises a first transparent conducting oxide (TCO) layer 110 formed over the substrate 102 , a p-i-n junction 120 formed over the first TCO layer 110 , a second TCO layer 140 formed over the p-i-n junction 120 , and a metal back layer 150 formed over the second TCO layer 140 .
  • TCO transparent conducting oxide
  • the substrate and/or one or more of thin films formed thereover may be optionally textured by wet, plasma, ion, and/or mechanical processes.
  • the first TCO layer 110 may be textured and the subsequent thin films deposited thereover will generally follow the topography of the surface below it.
  • the first TCO layer 110 and the second TCO layer 140 may each comprise tin oxide, zinc oxide, indium tin oxide, cadmium stannate, combinations thereof, or other suitable materials. It is understood that the TCO materials may also include additional dopants and components.
  • zinc oxide may further include dopants, such as aluminum, gallium, boron, and other suitable dopants. Zinc oxide preferably comprises 5 atomic % or less of dopants, and more preferably comprises 2.5 atomic % or less aluminum.
  • the p-i-n junction 120 may comprise a p-type microcrystalline silicon layer 122 , an intrinsic type microcrystalline silicon layer 124 formed over the p-type microcrystalline silicon layer 122 , and an n-type silicon layer 126 formed over the intrinsic type microcrystalline silicon layer 124 .
  • the p-type microcrystalline silicon layer 122 may be formed to a thickness between about 100 ⁇ and about 400 ⁇ .
  • the intrinsic type microcrystalline silicon layer 124 may be formed to a thickness between about 10,000 ⁇ and about 30,000 ⁇ , for example between about 16,000 ⁇ and about 20,000 ⁇ .
  • the n-type silicon layer 126 may be formed to a thickness between about 100 ⁇ and about 500 ⁇ .
  • the n-type silicon layer 126 is either an n-type amorphous silicon layer or an n-type microcrystalline silicon layer.
  • the metal back layer 150 may include, but is not limited to a material selected from the group consisting of Al, Ag, Ti, Cr, Au, Cu, Pt, alloys thereof, or combinations thereof. Other processes may be performed to form the solar cell 100 , such a laser scribing processes. Other films, materials, substrates, and/or packaging may be provided over metal back layer 150 to complete the solar cell.
  • the solar cells may be interconnected to form modules, which in turn can be connected to form arrays.
  • FIG. 2 is a flow chart 200 illustrating the processing steps according to one embodiment of the invention that may be used to deposit an intrinsic type microcrystalline silicon layer.
  • a substrate is positioned in a reaction zone.
  • a gas mixture comprising a silicon containing gas and hydrogen gas is supplied to the reaction zone.
  • a first region of the intrinsic type microcrystalline silicon layer is formed on the substrate at a first deposition rate.
  • a second region of the intrinsic type microcrystalline silicon layer is formed on the substrate at a second deposition rate greater than the first deposition rate.
  • a third region of the intrinsic type microcrystalline silicon layer is formed on the substrate at a third deposition rate lower than the second deposition rate.
  • a substrate 102 is positioned in a reaction zone.
  • the substrate may comprise a glass substrate, polymer substrate, metal substrate, or other suitable substrate with thin films formed thereover.
  • the substrate 102 may be provided by the glass manufacturers with the first TCO layer 110 already provided.
  • a p-type microcrystalline silicon layer 122 may also be formed on the substrate 102 .
  • a gas mixture comprising a silicon containing gas and hydrogen gas is supplied to the reaction zone.
  • Suitable silicon based gases include, but are not limited to silane (SiH 4 ), disilane (Si 2 H 6 ), silicon tetrafluoride (SiF 4 ), silicon tetrachloride (SiCl 4 ), dichlorosilane (SiH 2 Cl 2 ), and combinations thereof.
  • inert gases such as argon and helium may also be supplied to the reaction zone.
  • inert gases such as argon and helium may be supplied to the reaction zone in lieu of helium.
  • a first region of the intrinsic type microcrystalline silicon layer 124 is formed on the substrate 102 at a first deposition rate.
  • the first region of the intrinsic type microcrystalline silicon layer is between about 0 and about 500 ⁇ thick, such as between about 50 ⁇ and about 400 ⁇ thick, for example between about 200 ⁇ and about 300 ⁇ thick.
  • the first region may be deposited at a low deposition rate between about 100 ⁇ /minute and 350 ⁇ /minute, for example, between about 150 ⁇ /minute and about 300 ⁇ /minute.
  • the first region of the intrinsic type microcrystalline silicon layer 124 functions as a buffer layer for the previously deposited p-type microcrystalline silicon layer 122 .
  • the first region which is deposited at a low deposition rate, protects the PI interface during the high RF power deposition which occurs in step 240 . It has been found that deposition of the i-type microcrystalline silicon layer directly on the p-type layer using a high deposition rate (e.g. >400 ⁇ /minute) damages the underlying p-type layer.
  • a high deposition rate e.g. >400 ⁇ /minute
  • the first region may be formed by providing a silicon containing gas at a flow rate between about 1000 sccm and about 3000 sccm, for example, about 1500 sccm, hydrogen gas at a flow rate between about 100,000 sccm and about 300,000 sccm, for example, about 150,000 sccm, and supplying an RF power between about 0.2 Watts/cm 2 and about 0.6 Watts/cm 2 , for example, about 0.45 Watts/cm 2 .
  • a second region of the i-type microcrystalline silicon layer is formed on the substrate 102 at a second deposition rate greater than the first deposition rate.
  • the second region of the intrinsic type microcrystalline silicon layer is between about 10,000 ⁇ and about 30,000 ⁇ thick, preferably between about 16,000 and about 20,000 ⁇ thick.
  • the second region may be deposited at a deposition rate greater than about 400 ⁇ /minute, for example, between about 400 ⁇ /minute and about 1500 ⁇ /minute or between about 500 ⁇ /minute and about 600 ⁇ /minute.
  • the presence of the first region which functions as a buffer layer allows for the second region to be deposited using a higher RF power and a higher deposition rate.
  • the second region may be formed by providing a silicon containing gas at a flow rate between about 1,000 sccm and about 6,000 sccm, for example, about 3,000 sccm, hydrogen gas at a flow rate between about 200,000 sccm and about 600,000 sccm, for example, about 300,000 sccm, and RF power between 0.6 Watts/cm 2 and about 1.3 Watts/cm 2 , for example, about 0.9 Watts/cm 2 .
  • a third region of the intrinsic type microcrystalline silicon layer 124 is formed on the substrate at a third deposition rate lower than the second deposition rate.
  • the third region of the intrinsic type microcrystalline silicon layer 124 is between about 0 and about 500 ⁇ thick, such as between about 50 ⁇ and about 400 ⁇ thick, for example between about 200 ⁇ and about 300 ⁇ thick.
  • the third region may be deposited at a deposition rate between about 100 ⁇ /minute and 350 ⁇ /minute, for example, between about 150 ⁇ /minute and about 300 ⁇ /minute.
  • the third region functions as a passivation layer for the previously deposited second region of the intrinsic type microcrystalline silicon layer 124 .
  • the second region which is deposited at a high deposition rate is composed of large microcrystalline silicon crystals which form an uneven surface. Deposition of the n-type silicon layer 126 directly onto the uneven surface of the second region would yield an uneven n-type silicon layer 126 thus making uniform deposition of subsequent layers very difficult. Thus deposition of the third region of the intrinsic type microcrystalline silicon layer at a low deposition rate yields an intrinsic type microcrystalline layer with a more even surface making uniform deposition of subsequent layers possible.
  • the third region may be formed by providing silane gas at a flow rate between about 1,000 sccm and about 3,000 sccm, for example about 1500 sccm, hydrogen gas at a flow rate between about 100,000 sccm and about 300,000 sccm, for example about 150,000 sccm, and RF power between 0.2 Watts/cm 2 and about 0.6 Watts/cm 2 , for example about 0.45 Watts/cm 2 .
  • One embodiment of the intrinsic microcrystalline silicon layer has the following properties set forth in FIG. 8 .
  • FIG. 3 is a schematic diagram of a multi-junction solar cell oriented toward the light or solar radiation.
  • the solar cell 300 comprises an intrinsic type microcrystalline silicon layer (i-type ⁇ c-Si layer) 334 formed using the methods described herein.
  • Solar cell 300 comprises a substrate 302 , such as a glass substrate, polymer substrate, metal substrate, or other suitable substrate with thin films formed thereover.
  • the solar cell 300 further comprises a first transparent conducting oxide (TCO) layer 310 formed over the substrate 302 , a first p-i-n junction 320 formed over the first TCO layer 310 , a second p-i-n junction 330 formed over the first p-i-n junction 320 , a second TCO layer 340 formed over the second p-i-n junction 330 , and a metal back layer 350 formed over the second TCO layer 340 .
  • TCO transparent conducting oxide
  • the substrate and/or one or more of thin films formed thereover may be optionally textured by wet, plasma, ion, and/or mechanical processes.
  • the first TCO layer 310 and the second TCO layer 340 may each comprise tin oxide, zinc oxide, indium tin oxide, cadmium stannate, combinations thereof, or other suitable materials. It is understood that the TCO materials may also include additional dopants and components.
  • zinc oxide may further include dopants, such as aluminum, gallium, boron, and other suitable dopants. Zinc oxide preferably comprises 5 atomic % or less of dopants, and more preferably comprises 2.5 atomic % or less aluminum.
  • the substrate 302 may be provided by the glass manufacturers with the first TCO layer 310 already provided.
  • the first p-i-n junction 320 may comprise a p-type amorphous silicon layer 322 , an intrinsic type amorphous silicon layer 324 formed over the p-type amorphous silicon layer 322 , and a first n-type silicon layer 326 formed over the intrinsic type amorphous silicon layer 324 .
  • the p-type amorphous silicon layer 322 may be formed to a thickness between about 60 ⁇ and about 300 ⁇ .
  • the intrinsic type amorphous silicon layer 324 may be formed to a thickness between about 1,500 ⁇ and about 3,500 ⁇ .
  • the first n-type silicon layer 326 may be formed to a thickness between about 100 ⁇ and about 400 ⁇ .
  • the first n-type silicon layer 326 is a dual layer structure comprising n-type amorphous silicon and n-type microcrystalline silicon with the n-type amorphous silicon deposited on the intrinsic type amorphous silicon layer 324 .
  • the first n-type silicon layer 326 comprises microcrystalline silicon.
  • the second p-i-n junction 330 may comprise a p-type microcrystalline silicon layer 332 , an intrinsic type microcrystalline silicon layer 334 formed over the p-type microcrystalline silicon layer 332 , and a second n-type silicon layer 336 formed over the intrinsic type microcrystalline silicon layer 334 , wherein the second n-type silicon layer is either microcrystalline silicon or amorphous silicon.
  • the p-type microcrystalline silicon layer 332 may be formed to a thickness between about 100 ⁇ and about 400 ⁇ .
  • the intrinsic type microcrystalline silicon layer 334 may be formed using the methods described herein to a thickness between about 10,000 ⁇ and about 30,000 ⁇ , for example, between about 16,000 ⁇ and about 20,000 ⁇ .
  • the second n-type silicon layer 336 may be formed to a thickness between about 100 ⁇ and about 500 ⁇ . In certain embodiments, the second n-type silicon layer 336 is an amorphous silicon layer. In certain embodiments, the second n-type silicon layer 336 is a microcrystalline silicon layer.
  • the metal back layer 350 may include, but is not limited to a material selected from the group consisting of Al, Ag, Ti, Cr, Au, Cu, Pt, alloys thereof, or combinations thereof.
  • Other processes may be performed to form the solar cell 300 , such as a laser scribing processes.
  • Other films, materials, substrates, and/or packaging may be provided over metal back layer 350 to complete the solar cell.
  • the solar cells may be interconnected to form modules, which in turn can be connected to form arrays.
  • the first p-i-n junction 320 comprises an intrinsic type amorphous silicon layer 324 and the second p-i-n junction 330 comprises an intrinsic type microcrystalline silicon layer 334 because amorphous silicon and microcrystalline silicon absorb different wavelengths of solar radiation. Therefore, the solar cell 300 is more efficient since it captures a larger portion of the solar radiation spectrum.
  • the intrinsic layer of amorphous silicon and the intrinsic layer of microcrystalline are stacked in such a way that solar radiation first strikes the intrinsic type amorphous silicon layer 324 and then strikes the intrinsic type microcrystalline silicon layer 334 since amorphous silicon has a larger bandgap than microcrystalline silicon. Solar radiation not absorbed by the first p-i-n junction 320 continues on to the second p-i-n junction 330 .
  • the solar cell 300 does not need to utilize a metal tunnel layer between the first p-i-n junction 320 and the second p-i-n junction 330 .
  • the first n-type silicon layer 326 of the first p-i-n junction 320 and the p-type microcrystalline silicon layer 332 has sufficient conductivity to provide a tunnel junction to allow electrons to flow from the first p-i-n junction 320 to the second p-i-n junction 330 .
  • FIG. 4 is a schematic diagram of the multi-junction solar cell of FIG. 3 further comprising a seed layer 360 formed between the p-type microcrystalline silicon layer 332 and the intrinsic type microcrystalline silicon layer 334 .
  • the seed layer 360 may be formed to a thickness between about 20 ⁇ and about 500 ⁇ , such as between about 50 ⁇ and about 300 ⁇ , for example, between about 100 ⁇ and about 200 ⁇ . It is believed that the seed layer 360 helps provide better contact adhesion and interfacial qualities between the p-type microcrystalline layer and the intrinsic type microcrystalline silicon layer 334 .
  • the low deposition rate of the seed layer may be controlled by a gas mixture having a ratio of silane-based gas to H 2 between about 1:100 and about 1:20,000, such as between 1:200 and 1:1,500, for example 1:1,000 with other process parameters substantially similar to the i-type ⁇ c-Si layer 334 deposition.
  • the i-type ⁇ c-Si layer 334 deposition may include a four step deposition process having a first step depositing the seed layer and a second, third, and fourth step as described herein for depositing the bulk i-type ⁇ c-Si layer 334 .
  • the first step seed layer deposition process has a relatively lower deposition rate, such as less than 100 ⁇ /minute, controlled by a gas mixture having a ratio of silane-based gas to H 2 between about 1:100 and about 1:2,000, such as between 1:200 and 1:1,500, for example 1:1,000.
  • FIG. 5 is a schematic diagram of the multi-junction solar cell of FIG. 3 further comprising an amorphous silicon barrier layer 370 formed between the p-type microcrystalline silicon layer 332 and the seed layer 360 .
  • the amorphous silicon barrier layer 370 may be formed to a thickness between about 20 ⁇ and about 100 ⁇ , such as between about 30 ⁇ and about 90 ⁇ . It is believed that the amorphous silicon barrier layer 370 acts as a dopant diffusion barrier layer thus preventing contamination of the intrinsic type microcrystalline silicon layer 334 with dopants such as boron.
  • the amorphous silicon barrier layer 370 may be used in structures without the seed layer 360 .
  • FIG. 6 is a schematic cross-section view of one embodiment of a plasma enhanced chemical vapor deposition (PECVD) chamber in which one or more solar films of a solar cell, such as the solar cell 100 of FIG. 1 and solar cell 300 of FIG. 3 , FIG. 4 , and FIG. 5 , may be deposited.
  • PECVD plasma enhanced chemical vapor deposition
  • Suitable plasma enhanced chemical vapor deposition chambers include the AKT 4300 PECVD and the AKT 60K both of which are available from AKT America, Inc., of Santa Clara, Calif.
  • the chamber 600 generally includes walls 602 , a bottom 604 , and a showerhead 610 , and substrate support 630 which define a reaction zone 606 .
  • the reaction zone 606 is accessed through a valve 608 such that the substrate, such as substrate 601 , may be transferred in and out of the chamber 600 .
  • the substrate support 630 includes a substrate receiving surface 632 for supporting a substrate and stem 634 coupled to a lift system 636 to raise and lower the substrate support 630 .
  • a shadow from 633 may be optionally placed over periphery of the substrate 601 .
  • Lift pins 638 are moveably disposed through the substrate support 630 to move a substrate to and from the substrate receiving surface 632 .
  • the substrate support 630 may also include heating and/or cooling elements 639 to maintain the substrate support 630 at a desired temperature.
  • the substrate support 630 may also include grounding straps 631 to provide RF grounding at the periphery of the substrate support 630 . Examples of grounding straps are disclosed in U.S. Pat. No. 6,024,044 issued on Feb. 15, 2000 to Law et al. and U.S. patent application Ser. No. 11/613,934 filed on Dec. 20, 2006 to Park et al., which are both incorporated by reference in their entirety to the extent not inconsistent with the present disclosure.
  • the showerhead 610 is coupled to a backing plate 612 at its periphery by a suspension 614 .
  • the showerhead 610 may also be coupled to the backing plate by one or more center supports 616 to help prevent sag and/or control the straightness/curvature of the showerhead 610 .
  • a gas source 620 is coupled to the backing plate 612 to provide gas through the backing plate 612 and through the showerhead 610 to the substrate receiving surface 632 .
  • a vacuum pump 609 is coupled to the chamber 600 to control the reaction zone 606 at a desired pressure.
  • An RF power source 622 is coupled to the backing plate 612 and/or to the showerhead 610 to provide a RF power to the showerhead 610 so that an electric field is created between the showerhead and the substrate support so that a plasma may be generated from the gases between the showerhead 610 and the substrate support 630 .
  • Various RF frequencies may be used, such as a frequency between about 0.3 MHz and about 200 MHz.
  • the RF power source is provided at a frequency of 13.56 MHz.
  • Examples of showerheads are disclosed in U.S. Pat. No. 6,477,980 issued on Nov. 12, 2002 to White et al., U.S. Publication 20050251990 published on Nov. 17, 2006 to Choi et al., and U.S. Publication 2006/0060138 published on Mar. 23, 2006 to Keller et al., which are all incorporated by reference in their entirety to the extent not inconsistent with the present disclosure.
  • a remote plasma source 624 such as an inductively coupled remote plasma source, may also be coupled between the gas source and the backing plate.
  • a cleaning gas may be provided to the remote plasma source 624 so that a remote plasma is generated and provided to clean chamber components.
  • the cleaning gas may be further excited by the RF power source 622 provided to the showerhead.
  • Suitable cleaning gases include but are not limited to NF 3 , F 2 , and SF 6 . Examples of remote plasma sources are disclosed in U.S. Pat. No. 5,788,778 issued Aug. 4, 1998 to Shang et al., which is incorporated by reference to the extent not inconsistent with the present disclosure.
  • the deposition methods for one or more silicon layers may include the following deposition parameters in the process chamber of FIG. 6 or other suitable chamber.
  • a substrate having a surface area of 10,000 cm 2 or more, preferably 40,000 cm 2 or more, and more preferably 55,000 cm 2 or more is provided to the chamber. It is understood that after processing the substrate may be cut to form smaller solar cells.
  • the heating and/or cooling elements 639 may be set to provide a substrate support temperature during deposition of about 400° C. or less, preferably between about 100° C. and about 400° C., more preferably between about 150° C. and about 300° C., such as about 200° C.
  • the spacing during deposition between the top surface of a substrate disposed on the substrate receiving surface 632 and the showerhead 610 may be between 400 mil and about 1,200 mil, preferably between 400 mil and about 800 mil.
  • a silicon-based gas and hydrogen gas are provided.
  • Suitable silicon based gases include, but are not limited to silane (SiH 4 ), disilane (Si 2 H 6 ), silicon tetrafluoride (SiF 4 ), silicon tetrachloride (SiCl 4 ), dichlorosilane (SiH 2 Cl 2 ), and combinations thereof.
  • the p-type dopants of the p-type silicon layers may each comprise a group III element, such as boron or aluminum.
  • boron is used as the p-type dopant.
  • boron-containing sources include trimethylboron (TMB (or B(CH 3 ) 3 )), diborane (B 2 H 6 ), BF 3 , B(C 2 H 5 ) 3 , and similar compounds.
  • TMB trimethylboron
  • B 2 H 6 diborane
  • BF 3 B(C 2 H 5 ) 3
  • phosphorus-containing sources include phosphine and similar compounds.
  • the dopants are typically provided with a carrier gas, such as hydrogen, argon, helium, and other suitable compounds.
  • a total flow rate of hydrogen gas is provided. Therefore, if hydrogen gas is provided as the carrier gas, such as for the dopant, the carrier gas flow rate should be subtracted from the total flow rate of hydrogen to determine how much additional hydrogen gas should be provided to the chamber.
  • Certain embodiments of depositing a p-type amorphous silicon layer may comprise providing a gas mixture of hydrogen gas to silicon containing gas in a ratio of about 20:1 or less.
  • Silane gas may be provided at a flow rate between about 10 sccm/L and about 200 sccm/L.
  • Hydrogen gas may be provided at a flow rate between about 100 sccm/L and 1000 sccm/L.
  • Trimethylboron may be provided at a flow rate between about 0.5 sccm/L and about 1 sccm/L.
  • the dopant/carrier gas mixture may be provided at a flow rate between about 100 sccm/L and about 200 sccm/L.
  • Methane may be provided at a flow rate between about 100 sccm/L and 200 sccm/L.
  • the flow rates in the present disclosure are expressed as sccm per interior chamber volume.
  • the interior chamber volume is defined as the volume of the interior of the chamber in which a gas can occupy.
  • the interior chamber volume of chamber 600 is the volume defined by the backing plate 612 and by the walls 602 and bottom 604 of the chamber minus the volume occupied therein by the showerhead assembly (i.e., including the showerhead 610 , suspension 614 , center support 615 ) and by the substrate support assembly (i.e., substrate support 630 , grounding straps 631 ).
  • An RF power between about 15 milliWatts/cm 2 and about 200 milliWatts/cm 2 may be provided to the showerhead.
  • the RF powers in the present disclosure are expressed as Watts supplied to an electrode per substrate area.
  • the pressure of the chamber is maintained between about 0.1 Torr and 20 Torr, preferably between about 1 Torr and about 4 Torr.
  • the deposition rate of the p-type amorphous silicon layer may be about 100 ⁇ /min or more.
  • Methane or other carbon containing compounds, such C 3 H 8 , C 4 H 10 , C 2 H 2 can be used to improve the window properties (e.g. to lower absorption of solar radiation) of p-type amorphous silicon layer.
  • an increased amount of solar radiation may be absorbed through the intrinsic layers and thus cell efficiency is improved.
  • Certain embodiments of depositing an intrinsic type amorphous silicon layer comprises providing a gas mixture of hydrogen gas to silicon containing gas in a ratio of about 20:1 or less.
  • Silane gas may be provided at a flow rate between about 100 sccm/L and about 200 sccm/L.
  • Hydrogen gas may be provided at a flow rate between about 100 sccm/L and 3000 sccm/L.
  • An RF power between 15 milliWatts/cm 2 and about 250 milliWatts/cm 2 may be provided to the showerhead.
  • the pressure of the chamber may be maintained between about 0.1 Torr and 20 Torr, preferably between about 0.5 Torr and about 5 Torr.
  • the deposition rate of the intrinsic type amorphous silicon layer may be about 100 ⁇ /min or more.
  • Certain embodiments of depositing an n-type silicon layer comprise providing hydrogen gas to silicon gas in a ratio of about 1000:1 or less.
  • Silane gas may be provided at a flow rate between about 1 sccm/L and about 250 sccm/L.
  • Hydrogen gas may be provided at a flow rate between about 100 sccm/L and about 5000 sccm/L.
  • Phosphine may be provided at a flow rate between about 0.005 sccm/L and about 0.15 sccm/L.
  • the dopant/carrier gas mixture may be provided at a flow rate between about 1 sccm/L and about 30 sccm/L.
  • An RF power between about 15 milliWatts/cm 2 and about 1000 milliWatts/cm 2 may be provided to the showerhead.
  • the pressure of the chamber may be maintained between about 0.1 Torr and 20 Torr, preferably between about 0.5 Torr and about 12 Torr.
  • the deposition rate of the first n-type silicon layer 326 may be about 200 ⁇ /min or more.
  • Certain embodiments of depositing a p-type microcrystalline silicon layer may comprise providing a gas mixture of hydrogen gas to silicon containing gas in ratio of about 200:1 or greater.
  • Silane gas may be provided at a flow rate between about 1 sccm/L and about 20 sccm/L.
  • Hydrogen gas may be provided at a flow rate between about 100 sccm/L and about 6,000 sccm/L.
  • Trimethylboron may be provided at a flow rate between about 0.005 sccm/L and about 0.05 sccm/L.
  • the dopant/carrier gas mixture may be provided at a flow rate between about 1 sccm/L and about 10 sccm/L.
  • An RF power between about 50 milliWatts/cm 2 and about 1000 milliWatts/cm 2 may be provided to the showerhead.
  • the pressure of the chamber may be maintained between about 1 Torr and about 100 Torr, preferably between about 3 Torr and about 20 Torr, more preferably between 4 Torr and about 12 Torr.
  • the deposition rate of the p-type microcrystalline silicon contact layer may be about 10 ⁇ /min or more.
  • the p-type microcrystalline silicon contact layer has a crystalline fraction between about 20 percent and about 80 percent, preferably between 50 percent and about 70 percent.
  • an intrinsic type microcrystalline silicon layer such as silicon layer 334 of FIGS. 3-5
  • silicon layer 334 of FIGS. 3-5 may be deposited as described above in relation to the intrinsic type microcrystalline silicon layer 124 .
  • Certain embodiments of depositing an n-type amorphous or microcrystalline silicon layer may comprise providing a gas mixture of hydrogen gas to silicon containing gas in a ratio of about 5:1 or more.
  • Silane gas may be provided at a flow rate between about 100 sccm/L and about 300 sccm/L.
  • Hydrogen gas may be provided at a flow rate between about 100 sccm/L and about 2,000 sccm/L.
  • Phosphine may be provided at a flow rate between about 0.05 sccm/L and about 1.5 sccm/L.
  • the dopant/carrier gas may be provided at a flow rate between about 10 sccm/L and about 300 sccm/L.
  • An RF power between about 100 milliWatts/cm 2 and about 900 milliWatts/cm 2 may be provided to the showerhead.
  • the pressure of the chamber may be maintained between about 1 Torr and about 100 Torr, preferably between about 3 Torr and about 20 Torr, more preferably between 3 Torr and about 12 Torr.
  • the deposition rate of the n-type microcrystalline or amorphous silicon layer may be about 50 ⁇ /min or more. In certain embodiments the n-type microcrystalline silicon layer has a crystalline fraction between about 20 percent and about 80 percent, preferably between 50 percent and about 70 percent.
  • FIG. 7 is a top schematic view of one embodiment of a process system 700 having a plurality of process chambers 731 - 737 , such as PECVD chambers chamber 600 of FIG. 6 or other suitable chambers capable of depositing silicon films.
  • the process system 700 includes a transfer chamber 720 coupled to a load lock chamber 710 and the process chambers 731 - 737 .
  • the load lock chamber 710 allows substrates to be transferred between the ambient environment outside the system and vacuum environment within the transfer chamber 720 and process chambers 731 - 737 .
  • the load lock chamber 710 includes one or more evacuatable regions holding one or more substrate. The evacuatable regions are pumped down during input of substrates into the system 700 and are vented during output of the substrates from the system 700 .
  • the transfer chamber 720 has at least one vacuum robot 722 disposed therein that is adapted to transfer substrates between the load lock chamber 710 and the process chambers 731 - 737 . Seven process chambers are shown in FIG. 7 ; however, the system may have any suitable number of process chambers.
  • one system 700 is configured to deposit the first p-i-n junction comprising an intrinsic type amorphous silicon layer(s) of a multi-junction solar cell, such as the first p-i-n junction 320 of FIGS. 3-5 .
  • One of the process chambers 731 - 737 is configured to deposit the p-type silicon layer(s) of the first p-i-n junction while the remaining process chambers 731 - 737 are each configured to deposit both the intrinsic type amorphous silicon layer(s) and the n-type silicon layer(s).
  • the intrinsic type amorphous silicon layer(s) and the n-type silicon layer(s) of the first p-i-n junction may be deposited in the same chamber without any passivation process in between the deposition steps.
  • a substrate enters the system through the load lock chamber 710 , is transferred by the vacuum robot into the dedicated process chamber configured to deposit the p-type silicon layer(s), is transferred by the vacuum robot into one of the remaining process chamber configured to deposited both the intrinsic type silicon layer(s) and the n-type silicon layer(s), and is transferred by the vacuum robot back to the load lock chamber 710 .
  • the time to process a substrate with the process chamber to form the p-type silicon layer(s) is approximately 4 or more times faster, preferably 15 or more times faster, than the time to form the intrinsic type amorphous silicon layer(s) and the n-type silicon layer(s) in a single chamber. Therefore, in certain embodiments of the system to deposit the first p-i-n junction, the ratio of p-chambers to i/n-chambers is 1:4 or more, preferably 1:6 or more.
  • the throughput of the system including the time to provide plasma cleaning of the process chambers may be about 20 substrates/hr or more.
  • one system 700 is configured to deposit the second p-i-n junction comprising an intrinsic type microcrystalline silicon layer(s) of a multi-junction solar cell, such as the second p-i-n junction 330 of FIGS. 3-5 .
  • One of the process chambers 731 - 737 is configured to deposit the p-type silicon layer(s) of the first p-i-n junction while the remaining process chambers 731 - 737 are each configured to deposit both the intrinsic type microcrystalline silicon layer(s) and the n-type silicon layer(s).
  • the intrinsic type microcrystalline silicon layer(s) and the n-type silicon layer(s) of the second p-i-n junction may be deposited in the same chamber without any passivation process in between the deposition steps.
  • the method advantageously increases the deposition rate of the microcrystalline silicon layer in a solar cell without significantly damaging the underlying layers.
  • the increased deposition rate reduces the processing time for solar cells comprising microcrystalline silicon layers and increases manufacturing throughput while reducing production costs.
  • the process chamber of FIG. 4 has been shown in a horizontal position. It is understood that in other embodiments of the invention the process chamber may be in any non-horizontal position, such as vertical.
  • embodiments of the invention have been described in reference to the multi-process chamber cluster tool in FIG. 7 . It is understood that embodiments of the invention may also be practiced in on in-line systems and hybrid in-line/cluster systems.
  • embodiments of the invention have been described in reference to a first system configured to form a first p-i-n junction and a second p-i-n junction. It is understood that in other embodiments of the invention, the first p-i-n junction and a second p-i-n junction may be formed in a single system.
  • embodiments of the invention have been described in reference to a process chamber adapted to deposit both an intrinsic type layer and an n-type layer. It is understood that in other embodiments of the invention, separate chambers may be adapted to deposit the intrinsic type layer and the n-type layer. It is understood that in other embodiments of the invention, a process chamber may be adapted to deposit both a p-type layer and an intrinsic type layer.

Landscapes

  • Engineering & Computer Science (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Computer Hardware Design (AREA)
  • Power Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • Electromagnetism (AREA)
  • General Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical & Material Sciences (AREA)
  • Manufacturing & Machinery (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Sustainable Development (AREA)
  • Sustainable Energy (AREA)
  • Photovoltaic Devices (AREA)
US11/876,173 2007-10-22 2007-10-22 Microcrystalline silicon deposition for thin film solar applications Abandoned US20090104733A1 (en)

Priority Applications (7)

Application Number Priority Date Filing Date Title
US11/876,173 US20090104733A1 (en) 2007-10-22 2007-10-22 Microcrystalline silicon deposition for thin film solar applications
CN2008801127040A CN101836299B (zh) 2007-10-22 2008-10-22 用于薄膜太阳能应用的微晶硅沉积
JP2010530192A JP2011501445A (ja) 2007-10-22 2008-10-22 薄膜太陽電池用途のための微結晶シリコン堆積
PCT/US2008/080834 WO2009055502A1 (en) 2007-10-22 2008-10-22 Microcrystalline silicon deposition for thin film solar applications
EP08843208A EP2206156A1 (en) 2007-10-22 2008-10-22 Microcrystalline silicon deposition for thin film solar applications
KR1020107011266A KR20100089856A (ko) 2007-10-22 2008-10-22 박막 태양열 이용제품을 위한 미정질 실리콘 증착
US12/493,020 US7919398B2 (en) 2007-10-22 2009-06-26 Microcrystalline silicon deposition for thin film solar applications

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US11/876,173 US20090104733A1 (en) 2007-10-22 2007-10-22 Microcrystalline silicon deposition for thin film solar applications

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US12/493,020 Continuation US7919398B2 (en) 2007-10-22 2009-06-26 Microcrystalline silicon deposition for thin film solar applications

Publications (1)

Publication Number Publication Date
US20090104733A1 true US20090104733A1 (en) 2009-04-23

Family

ID=40563883

Family Applications (2)

Application Number Title Priority Date Filing Date
US11/876,173 Abandoned US20090104733A1 (en) 2007-10-22 2007-10-22 Microcrystalline silicon deposition for thin film solar applications
US12/493,020 Expired - Fee Related US7919398B2 (en) 2007-10-22 2009-06-26 Microcrystalline silicon deposition for thin film solar applications

Family Applications After (1)

Application Number Title Priority Date Filing Date
US12/493,020 Expired - Fee Related US7919398B2 (en) 2007-10-22 2009-06-26 Microcrystalline silicon deposition for thin film solar applications

Country Status (6)

Country Link
US (2) US20090104733A1 (ja)
EP (1) EP2206156A1 (ja)
JP (1) JP2011501445A (ja)
KR (1) KR20100089856A (ja)
CN (1) CN101836299B (ja)
WO (1) WO2009055502A1 (ja)

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090130827A1 (en) * 2007-11-02 2009-05-21 Soo Young Choi Intrinsic amorphous silicon layer
US20090142878A1 (en) * 2007-11-02 2009-06-04 Applied Materials, Inc. Plasma treatment between deposition processes
US20090263930A1 (en) * 2007-10-22 2009-10-22 Yong Kee Chae Microcrystalline silicon deposition for thin film solar applications
US20100132774A1 (en) * 2008-12-11 2010-06-03 Applied Materials, Inc. Thin Film Silicon Solar Cell Device With Amorphous Window Layer
US20110088760A1 (en) * 2009-10-20 2011-04-21 Applied Materials, Inc. Methods of forming an amorphous silicon layer for thin film solar cell application
US20110174362A1 (en) * 2010-01-18 2011-07-21 Applied Materials, Inc. Manufacture of thin film solar cells with high conversion efficiency
US20110198640A1 (en) * 2008-02-29 2011-08-18 Osram Opto Semiconductor Gmbh Semiconductor Light-Emitting Diode and Method for Producing a Semiconductor Light-Emitting Diode
US20110275200A1 (en) * 2010-05-06 2011-11-10 Applied Materials, Inc. Methods of dynamically controlling film microstructure formed in a microcrystalline layer
US20110303289A1 (en) * 2008-11-07 2011-12-15 Mitsubishi Heavy Industries, Ltd. Process for producing photovoltaic device and photovoltaic device
US8203071B2 (en) 2007-01-18 2012-06-19 Applied Materials, Inc. Multi-junction solar cells and methods and apparatuses for forming the same
WO2012027857A3 (en) * 2010-09-02 2012-06-28 Oerlikon Solar Ag, Trübbach Method for manufacturing a tandem solar cell with microcrystalline absorber layer
WO2012065957A3 (en) * 2010-11-16 2012-10-18 Oerlikon Solar Ag, Trübbach Improved a-si:h absorber layer for a-si single- and multijunction thin film silicon solar cell
TWI401812B (zh) * 2009-12-31 2013-07-11 Metal Ind Res Anddevelopment Ct Solar battery
TWI488322B (zh) * 2010-12-27 2015-06-11 Nexpower Technology Corp 薄膜太陽能電池堆疊製造方法及其薄膜太陽能電池
US9236523B2 (en) 2012-03-05 2016-01-12 First Solar, Inc Method and apparatus for forming a transparent conductive oxide using hydrogen

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
IN2012DN05898A (ja) * 2009-12-18 2015-09-18 First Solar Inc
KR101037124B1 (ko) 2010-01-29 2011-05-26 주식회사 티지솔라 태양전지 및 그 제조방법
JP4967066B2 (ja) * 2010-04-27 2012-07-04 東京エレクトロン株式会社 アモルファスシリコン膜の成膜方法および成膜装置
US20120318335A1 (en) * 2011-06-15 2012-12-20 International Business Machines Corporation Tandem solar cell with improved tunnel junction
TWI455343B (zh) 2012-04-20 2014-10-01 Ind Tech Res Inst 一種薄膜太陽能電池之ｐ－ｉ－ｎ微晶矽結構及其製法
TWI474499B (zh) * 2012-10-12 2015-02-21 Iner Aec Executive Yuan Microcrystalline silicon thin film solar cell element and its manufacturing method
KR101879363B1 (ko) 2017-01-17 2018-08-16 엘지전자 주식회사 태양 전지 제조 방법

Citations (99)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4271328A (en) * 1979-03-20 1981-06-02 Yoshihiro Hamakawa Photovoltaic device
US4272641A (en) * 1979-04-19 1981-06-09 Rca Corporation Tandem junction amorphous silicon solar cells
US4400577A (en) * 1981-07-16 1983-08-23 Spear Reginald G Thin solar cells
US4471155A (en) * 1983-04-15 1984-09-11 Energy Conversion Devices, Inc. Narrow band gap photovoltaic devices with enhanced open circuit voltage
US4476346A (en) * 1982-12-14 1984-10-09 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Photovoltaic device
US4728370A (en) * 1985-08-29 1988-03-01 Sumitomo Electric Industries, Inc. Amorphous photovoltaic elements
US4737196A (en) * 1984-10-29 1988-04-12 Mitsubishi Denki Kabushiki Kaisha Amorphous solar cell
US4755475A (en) * 1986-02-18 1988-07-05 Sanyo Electric Co., Ltd. Method of manufacturing photovoltaic device
US4776894A (en) * 1986-08-18 1988-10-11 Sanyo Electric Co., Ltd. Photovoltaic device
US4781765A (en) * 1986-09-26 1988-11-01 Sanyo Electric Co., Ltd. Photovoltaic device
US4841908A (en) * 1986-06-23 1989-06-27 Minnesota Mining And Manufacturing Company Multi-chamber deposition system
US4878097A (en) * 1984-05-15 1989-10-31 Eastman Kodak Company Semiconductor photoelectric conversion device and method for making same
US4907052A (en) * 1984-10-11 1990-03-06 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Semiconductor tandem solar cells with metal silicide barrier
US5015838A (en) * 1987-03-31 1991-05-14 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Color sensor having laminated semiconductor layers
US5021100A (en) * 1989-03-10 1991-06-04 Mitsubishi Denki Kabushiki Kaisha Tandem solar cell
US5032884A (en) * 1985-11-05 1991-07-16 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Semiconductor pin device with interlayer or dopant gradient
US5256887A (en) * 1991-07-19 1993-10-26 Solarex Corporation Photovoltaic device including a boron doping profile in an i-type layer
US5403404A (en) * 1991-07-16 1995-04-04 Amoco Corporation Multijunction photovoltaic device and method of manufacture
US5677236A (en) * 1995-02-24 1997-10-14 Mitsui Toatsu Chemicals, Inc. Process for forming a thin microcrystalline silicon semiconductor film
US5720826A (en) * 1995-05-30 1998-02-24 Canon Kabushiki Kaisha Photovoltaic element and fabrication process thereof
US5730808A (en) * 1996-06-27 1998-03-24 Amoco/Enron Solar Producing solar cells by surface preparation for accelerated nucleation of microcrystalline silicon on heterogeneous substrates
US5738732A (en) * 1995-06-05 1998-04-14 Sharp Kabushiki Kaisha Solar cell and manufacturing method thereof
US5797998A (en) * 1994-03-31 1998-08-25 Pacific Solar Pty. Limited Multiple layer thin film solar cells with buried contacts
US5913986A (en) * 1996-09-19 1999-06-22 Canon Kabushiki Kaisha Photovoltaic element having a specific doped layer
US5923049A (en) * 1995-08-31 1999-07-13 Cohausz & Florack Trichromatic sensor
US5927994A (en) * 1996-01-17 1999-07-27 Canon Kabushiki Kaisha Method for manufacturing thin film
US5942050A (en) * 1994-12-02 1999-08-24 Pacific Solar Pty Ltd. Method of manufacturing a multilayer solar cell
US5977476A (en) * 1996-10-16 1999-11-02 United Solar Systems Corporation High efficiency photovoltaic device
US6100466A (en) * 1997-11-27 2000-08-08 Canon Kabushiki Kaisha Method of forming microcrystalline silicon film, photovoltaic element, and method of producing same
US6121541A (en) * 1997-07-28 2000-09-19 Bp Solarex Monolithic multi-junction solar cells with amorphous silicon and CIS and their alloys
US6190932B1 (en) * 1999-02-26 2001-02-20 Kaneka Corporation Method of manufacturing tandem type thin film photoelectric conversion device
US6200825B1 (en) * 1999-02-26 2001-03-13 Kaneka Corporation Method of manufacturing silicon based thin film photoelectric conversion device
US6222115B1 (en) * 1999-11-19 2001-04-24 Kaneka Corporation Photovoltaic module
US6242686B1 (en) * 1998-06-12 2001-06-05 Sharp Kabushiki Kaisha Photovoltaic device and process for producing the same
US6265288B1 (en) * 1998-10-12 2001-07-24 Kaneka Corporation Method of manufacturing silicon-based thin-film photoelectric conversion device
US6281561B1 (en) * 1997-08-28 2001-08-28 Forschungszentrum Julich Gmbh Multicolor-color sensor
US6288325B1 (en) * 1998-07-14 2001-09-11 Bp Corporation North America Inc. Producing thin film photovoltaic modules with high integrity interconnects and dual layer contacts
US6297443B1 (en) * 1997-08-21 2001-10-02 Kaneka Corporation Thin film photoelectric transducer
US6307146B1 (en) * 1999-01-18 2001-10-23 Mitsubishi Heavy Industries, Ltd. Amorphous silicon solar cell
US6309906B1 (en) * 1996-01-02 2001-10-30 Universite De Neuchatel-Institut De Microtechnique Photovoltaic cell and method of producing that cell
US20010035206A1 (en) * 2000-01-13 2001-11-01 Takashi Inamasu Thin film solar cell and method of manufacturing the same
US6337224B1 (en) * 1997-11-10 2002-01-08 Kaneka Corporation Method of producing silicon thin-film photoelectric transducer and plasma CVD apparatus used for the method
US20020033191A1 (en) * 2000-05-31 2002-03-21 Takaharu Kondo Silicon-type thin-film formation process, silicon-type thin film, and photovoltaic device
US6380480B1 (en) * 1999-05-18 2002-04-30 Nippon Sheet Glass Co., Ltd Photoelectric conversion device and substrate for photoelectric conversion device
US6395973B2 (en) * 1998-08-26 2002-05-28 Nippon Sheet Glass Co., Ltd. Photovoltaic device
US6459034B2 (en) * 2000-06-01 2002-10-01 Sharp Kabushiki Kaisha Multi-junction solar cell
US6506622B1 (en) * 1998-01-05 2003-01-14 Canon Kabushiki Kaisha Method of manufacturing a photovoltaic device
US20030013280A1 (en) * 2000-12-08 2003-01-16 Hideo Yamanaka Semiconductor thin film forming method, production methods for semiconductor device and electrooptical device, devices used for these methods, and semiconductor device and electrooptical device
US20030044539A1 (en) * 2001-02-06 2003-03-06 Oswald Robert S. Process for producing photovoltaic devices
US20030041894A1 (en) * 2000-12-12 2003-03-06 Solarflex Technologies, Inc. Thin film flexible solar cell
US6566159B2 (en) * 2000-10-04 2003-05-20 Kaneka Corporation Method of manufacturing tandem thin-film solar cell
US20030104664A1 (en) * 2001-04-03 2003-06-05 Takaharu Kondo Silicon film, semiconductor device, and process for forming silicon films
US6602606B1 (en) * 1999-05-18 2003-08-05 Nippon Sheet Glass Co., Ltd. Glass sheet with conductive film, method of manufacturing the same, and photoelectric conversion device using the same
US6632993B2 (en) * 2000-10-05 2003-10-14 Kaneka Corporation Photovoltaic module
US6645573B2 (en) * 1998-03-03 2003-11-11 Canon Kabushiki Kaisha Process for forming a microcrystalline silicon series thin film and apparatus suitable for practicing said process
US20040082097A1 (en) * 1999-07-26 2004-04-29 Schott Glas Thin-film solar cells and method of making
US6750394B2 (en) * 2001-01-12 2004-06-15 Sharp Kabushiki Kaisha Thin-film solar cell and its manufacturing method
US6777610B2 (en) * 1998-10-13 2004-08-17 Dai Nippon Printing Co., Ltd. Protective sheet for solar battery module, method of fabricating the same and solar battery module
US20040187914A1 (en) * 2003-03-26 2004-09-30 Canon Kabushiki Kaisha Stacked photovoltaic element and method for producing the same
US20040231590A1 (en) * 2003-05-19 2004-11-25 Ovshinsky Stanford R. Deposition apparatus for the formation of polycrystalline materials on mobile substrates
US6825104B2 (en) * 1996-12-24 2004-11-30 Interuniversitair Micro-Elektronica Centrum (Imec) Semiconductor device with selectively diffused regions
US6825408B2 (en) * 2001-08-24 2004-11-30 Sharp Kabushiki Kaisha Stacked photoelectric conversion device
US6887728B2 (en) * 2002-08-26 2005-05-03 University Of Hawaii Hybrid solid state/electrochemical photoelectrode for hydrogen production
US20050115504A1 (en) * 2002-05-31 2005-06-02 Ishikawajima-Harima Heavy Industries Co., Ltd. Method and apparatus for forming thin films, method for manufacturing solar cell, and solar cell
US20050173704A1 (en) * 1998-03-16 2005-08-11 Canon Kabushiki Kaisha Semiconductor element and its manufacturing method
US20050189012A1 (en) * 2002-10-30 2005-09-01 Canon Kabushiki Kaisha Zinc oxide film, photovoltaic device making use of the same, and zinc oxide film formation process
US6963120B2 (en) * 2002-11-13 2005-11-08 Canon Kabushiki Kaisha Photovoltaic element
US20050251990A1 (en) * 2004-05-12 2005-11-17 Applied Materials, Inc. Plasma uniformity control by gas diffuser hole design
US6989553B2 (en) * 2000-03-03 2006-01-24 Matsushita Electric Industrial Co., Ltd. Semiconductor device having an active region of alternating layers
US20060060138A1 (en) * 2004-09-20 2006-03-23 Applied Materials, Inc. Diffuser gravity support
US7064263B2 (en) * 1998-02-26 2006-06-20 Canon Kabushiki Kaisha Stacked photovoltaic device
US7071018B2 (en) * 2001-06-19 2006-07-04 Bp Solar Limited Process for manufacturing a solar cell
US7074641B2 (en) * 2001-03-22 2006-07-11 Canon Kabushiki Kaisha Method of forming silicon-based thin film, silicon-based thin film, and photovoltaic element
US20060169317A1 (en) * 2001-10-19 2006-08-03 Asahi Glass Company Limited Substrate with transparent conductive oxide film, process for its production and photoelectric conversion element
US20060249196A1 (en) * 2005-04-28 2006-11-09 Sanyo Electric Co., Ltd. Stacked photovoltaic device
US20070000538A1 (en) * 2005-06-30 2007-01-04 Sanyo Electric Co., Ltd. Stacked photovoltaic device
US20070039942A1 (en) * 2005-08-16 2007-02-22 Applied Materials, Inc. Active cooling substrate support
US20070137698A1 (en) * 2002-02-27 2007-06-21 Wanlass Mark W Monolithic photovoltaic energy conversion device
US7235810B1 (en) * 1998-12-03 2007-06-26 Semiconductor Energy Laboratory Co., Ltd. Semiconductor device and method of fabricating the same
US7238545B2 (en) * 2002-04-09 2007-07-03 Kaneka Corporation Method for fabricating tandem thin film photoelectric converter
US7256140B2 (en) * 2005-09-20 2007-08-14 United Solar Ovonic Llc Higher selectivity, method for passivating short circuit current paths in semiconductor devices
US20070209699A1 (en) * 2006-03-08 2007-09-13 National Science And Technology Development Agency Thin film solar cell and its fabrication process
US20070227579A1 (en) * 2006-03-30 2007-10-04 Benyamin Buller Assemblies of cylindrical solar units with internal spacing
US20070249898A1 (en) * 2004-07-02 2007-10-25 Olympus Corporation Endoscope
US7301215B2 (en) * 2005-08-22 2007-11-27 Canon Kabushiki Kaisha Photovoltaic device
US7332226B2 (en) * 2000-11-21 2008-02-19 Nippon Sheet Glass Company, Limited Transparent conductive film and its manufacturing method, and photoelectric conversion device comprising it
US20080047599A1 (en) * 2006-03-18 2008-02-28 Benyamin Buller Monolithic integration of nonplanar solar cells
US20080047603A1 (en) * 2006-08-24 2008-02-28 Guardian Industries Corp. Front contact with intermediate layer(s) adjacent thereto for use in photovoltaic device and method of making same
US20080057220A1 (en) * 2006-01-31 2008-03-06 Robert Bachrach Silicon photovoltaic cell junction formed from thin film doping source
US7351993B2 (en) * 2000-08-08 2008-04-01 Translucent Photonics, Inc. Rare earth-oxides, rare earth-nitrides, rare earth-phosphides and ternary alloys with silicon
US20080110491A1 (en) * 2006-03-18 2008-05-15 Solyndra, Inc., Monolithic integration of non-planar solar cells
US7375378B2 (en) * 2005-05-12 2008-05-20 General Electric Company Surface passivated photovoltaic devices
US20080153280A1 (en) * 2006-12-21 2008-06-26 Applied Materials, Inc. Reactive sputter deposition of a transparent conductive film
US20080160661A1 (en) * 2006-04-05 2008-07-03 Silicon Genesis Corporation Method and structure for fabricating solar cells using a layer transfer process
US20080156370A1 (en) * 2005-04-20 2008-07-03 Hahn-Meitner-Institut Berlin Gmbh Heterocontact Solar Cell with Inverted Geometry of its Layer Structure
US7402747B2 (en) * 2003-02-18 2008-07-22 Kyocera Corporation Photoelectric conversion device and method of manufacturing the device
US20080196761A1 (en) * 2007-02-16 2008-08-21 Mitsubishi Heavy Industries, Ltd Photovoltaic device and process for producing same
US20080223440A1 (en) * 2007-01-18 2008-09-18 Shuran Sheng Multi-junction solar cells and methods and apparatuses for forming the same
US7560750B2 (en) * 2003-06-26 2009-07-14 Kyocera Corporation Solar cell device

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2719230B2 (ja) * 1990-11-22 1998-02-25 キヤノン株式会社 光起電力素子
US5507881A (en) * 1991-09-30 1996-04-16 Fuji Electric Co., Ltd. Thin-film solar cell and method of manufacturing same
JPH08264815A (ja) * 1995-03-23 1996-10-11 Sanyo Electric Co Ltd 非晶質シリコンカーバイド膜及びこれを用いた光起電力素子
EP0886325A1 (en) * 1997-06-18 1998-12-23 Rijksuniversiteit Utrecht Amorphous silicon photovoltaic devices and method of making thereof
JPH1187742A (ja) 1997-09-01 1999-03-30 Kanegafuchi Chem Ind Co Ltd シリコン系薄膜光電変換装置
JP3046965B1 (ja) * 1999-02-26 2000-05-29 鐘淵化学工業株式会社 非晶質シリコン系薄膜光電変換装置の製造方法
ES2405597T3 (es) * 2003-07-24 2013-05-31 Kaneka Corporation Convertidor fotoeléctrico apilado
JP2005050905A (ja) * 2003-07-30 2005-02-24 Sharp Corp シリコン薄膜太陽電池の製造方法
US20050059186A1 (en) * 2003-09-15 2005-03-17 Kelly Nelson A. Photoelectrochemical device and method of making
JP2005123466A (ja) * 2003-10-17 2005-05-12 Sharp Corp シリコン系薄膜光電変換装置の製造方法およびその方法により製造されたシリコン系薄膜光電変換装置
AU2004222793B2 (en) * 2003-10-27 2007-07-26 Mitsubishi Heavy Industries, Ltd. Solar cell and process for producing solar cell
US7655542B2 (en) * 2006-06-23 2010-02-02 Applied Materials, Inc. Methods and apparatus for depositing a microcrystalline silicon film for photovoltaic device
US7501305B2 (en) * 2006-10-23 2009-03-10 Canon Kabushiki Kaisha Method for forming deposited film and photovoltaic element
US7582515B2 (en) * 2007-01-18 2009-09-01 Applied Materials, Inc. Multi-junction solar cells and methods and apparatuses for forming the same
US20080173350A1 (en) * 2007-01-18 2008-07-24 Applied Materials, Inc. Multi-junction solar cells and methods and apparatuses for forming the same
US20090104733A1 (en) * 2007-10-22 2009-04-23 Yong Kee Chae Microcrystalline silicon deposition for thin film solar applications

Patent Citations (99)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4271328A (en) * 1979-03-20 1981-06-02 Yoshihiro Hamakawa Photovoltaic device
US4272641A (en) * 1979-04-19 1981-06-09 Rca Corporation Tandem junction amorphous silicon solar cells
US4400577A (en) * 1981-07-16 1983-08-23 Spear Reginald G Thin solar cells
US4476346A (en) * 1982-12-14 1984-10-09 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Photovoltaic device
US4471155A (en) * 1983-04-15 1984-09-11 Energy Conversion Devices, Inc. Narrow band gap photovoltaic devices with enhanced open circuit voltage
US4878097A (en) * 1984-05-15 1989-10-31 Eastman Kodak Company Semiconductor photoelectric conversion device and method for making same
US4907052A (en) * 1984-10-11 1990-03-06 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Semiconductor tandem solar cells with metal silicide barrier
US4737196A (en) * 1984-10-29 1988-04-12 Mitsubishi Denki Kabushiki Kaisha Amorphous solar cell
US4728370A (en) * 1985-08-29 1988-03-01 Sumitomo Electric Industries, Inc. Amorphous photovoltaic elements
US5032884A (en) * 1985-11-05 1991-07-16 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Semiconductor pin device with interlayer or dopant gradient
US4755475A (en) * 1986-02-18 1988-07-05 Sanyo Electric Co., Ltd. Method of manufacturing photovoltaic device
US4841908A (en) * 1986-06-23 1989-06-27 Minnesota Mining And Manufacturing Company Multi-chamber deposition system
US4776894A (en) * 1986-08-18 1988-10-11 Sanyo Electric Co., Ltd. Photovoltaic device
US4781765A (en) * 1986-09-26 1988-11-01 Sanyo Electric Co., Ltd. Photovoltaic device
US5015838A (en) * 1987-03-31 1991-05-14 Kanegafuchi Kagaku Kogyo Kabushiki Kaisha Color sensor having laminated semiconductor layers
US5021100A (en) * 1989-03-10 1991-06-04 Mitsubishi Denki Kabushiki Kaisha Tandem solar cell
US5403404A (en) * 1991-07-16 1995-04-04 Amoco Corporation Multijunction photovoltaic device and method of manufacture
US5256887A (en) * 1991-07-19 1993-10-26 Solarex Corporation Photovoltaic device including a boron doping profile in an i-type layer
US5797998A (en) * 1994-03-31 1998-08-25 Pacific Solar Pty. Limited Multiple layer thin film solar cells with buried contacts
US5942050A (en) * 1994-12-02 1999-08-24 Pacific Solar Pty Ltd. Method of manufacturing a multilayer solar cell
US5677236A (en) * 1995-02-24 1997-10-14 Mitsui Toatsu Chemicals, Inc. Process for forming a thin microcrystalline silicon semiconductor film
US5720826A (en) * 1995-05-30 1998-02-24 Canon Kabushiki Kaisha Photovoltaic element and fabrication process thereof
US5738732A (en) * 1995-06-05 1998-04-14 Sharp Kabushiki Kaisha Solar cell and manufacturing method thereof
US5923049A (en) * 1995-08-31 1999-07-13 Cohausz & Florack Trichromatic sensor
US6309906B1 (en) * 1996-01-02 2001-10-30 Universite De Neuchatel-Institut De Microtechnique Photovoltaic cell and method of producing that cell
US5927994A (en) * 1996-01-17 1999-07-27 Canon Kabushiki Kaisha Method for manufacturing thin film
US5730808A (en) * 1996-06-27 1998-03-24 Amoco/Enron Solar Producing solar cells by surface preparation for accelerated nucleation of microcrystalline silicon on heterogeneous substrates
US5913986A (en) * 1996-09-19 1999-06-22 Canon Kabushiki Kaisha Photovoltaic element having a specific doped layer
US5977476A (en) * 1996-10-16 1999-11-02 United Solar Systems Corporation High efficiency photovoltaic device
US6825104B2 (en) * 1996-12-24 2004-11-30 Interuniversitair Micro-Elektronica Centrum (Imec) Semiconductor device with selectively diffused regions
US6121541A (en) * 1997-07-28 2000-09-19 Bp Solarex Monolithic multi-junction solar cells with amorphous silicon and CIS and their alloys
US6297443B1 (en) * 1997-08-21 2001-10-02 Kaneka Corporation Thin film photoelectric transducer
US6281561B1 (en) * 1997-08-28 2001-08-28 Forschungszentrum Julich Gmbh Multicolor-color sensor
US6337224B1 (en) * 1997-11-10 2002-01-08 Kaneka Corporation Method of producing silicon thin-film photoelectric transducer and plasma CVD apparatus used for the method
US6100466A (en) * 1997-11-27 2000-08-08 Canon Kabushiki Kaisha Method of forming microcrystalline silicon film, photovoltaic element, and method of producing same
US6506622B1 (en) * 1998-01-05 2003-01-14 Canon Kabushiki Kaisha Method of manufacturing a photovoltaic device
US7064263B2 (en) * 1998-02-26 2006-06-20 Canon Kabushiki Kaisha Stacked photovoltaic device
US6645573B2 (en) * 1998-03-03 2003-11-11 Canon Kabushiki Kaisha Process for forming a microcrystalline silicon series thin film and apparatus suitable for practicing said process
US20050173704A1 (en) * 1998-03-16 2005-08-11 Canon Kabushiki Kaisha Semiconductor element and its manufacturing method
US6242686B1 (en) * 1998-06-12 2001-06-05 Sharp Kabushiki Kaisha Photovoltaic device and process for producing the same
US6288325B1 (en) * 1998-07-14 2001-09-11 Bp Corporation North America Inc. Producing thin film photovoltaic modules with high integrity interconnects and dual layer contacts
US6395973B2 (en) * 1998-08-26 2002-05-28 Nippon Sheet Glass Co., Ltd. Photovoltaic device
US6265288B1 (en) * 1998-10-12 2001-07-24 Kaneka Corporation Method of manufacturing silicon-based thin-film photoelectric conversion device
US6777610B2 (en) * 1998-10-13 2004-08-17 Dai Nippon Printing Co., Ltd. Protective sheet for solar battery module, method of fabricating the same and solar battery module
US7235810B1 (en) * 1998-12-03 2007-06-26 Semiconductor Energy Laboratory Co., Ltd. Semiconductor device and method of fabricating the same
US6307146B1 (en) * 1999-01-18 2001-10-23 Mitsubishi Heavy Industries, Ltd. Amorphous silicon solar cell
US6190932B1 (en) * 1999-02-26 2001-02-20 Kaneka Corporation Method of manufacturing tandem type thin film photoelectric conversion device
US6200825B1 (en) * 1999-02-26 2001-03-13 Kaneka Corporation Method of manufacturing silicon based thin film photoelectric conversion device
US6602606B1 (en) * 1999-05-18 2003-08-05 Nippon Sheet Glass Co., Ltd. Glass sheet with conductive film, method of manufacturing the same, and photoelectric conversion device using the same
US6380480B1 (en) * 1999-05-18 2002-04-30 Nippon Sheet Glass Co., Ltd Photoelectric conversion device and substrate for photoelectric conversion device
US20040082097A1 (en) * 1999-07-26 2004-04-29 Schott Glas Thin-film solar cells and method of making
US6222115B1 (en) * 1999-11-19 2001-04-24 Kaneka Corporation Photovoltaic module
US20010035206A1 (en) * 2000-01-13 2001-11-01 Takashi Inamasu Thin film solar cell and method of manufacturing the same
US6989553B2 (en) * 2000-03-03 2006-01-24 Matsushita Electric Industrial Co., Ltd. Semiconductor device having an active region of alternating layers
US20020033191A1 (en) * 2000-05-31 2002-03-21 Takaharu Kondo Silicon-type thin-film formation process, silicon-type thin film, and photovoltaic device
US6459034B2 (en) * 2000-06-01 2002-10-01 Sharp Kabushiki Kaisha Multi-junction solar cell
US7351993B2 (en) * 2000-08-08 2008-04-01 Translucent Photonics, Inc. Rare earth-oxides, rare earth-nitrides, rare earth-phosphides and ternary alloys with silicon
US6566159B2 (en) * 2000-10-04 2003-05-20 Kaneka Corporation Method of manufacturing tandem thin-film solar cell
US6632993B2 (en) * 2000-10-05 2003-10-14 Kaneka Corporation Photovoltaic module
US7332226B2 (en) * 2000-11-21 2008-02-19 Nippon Sheet Glass Company, Limited Transparent conductive film and its manufacturing method, and photoelectric conversion device comprising it
US20030013280A1 (en) * 2000-12-08 2003-01-16 Hideo Yamanaka Semiconductor thin film forming method, production methods for semiconductor device and electrooptical device, devices used for these methods, and semiconductor device and electrooptical device
US20030041894A1 (en) * 2000-12-12 2003-03-06 Solarflex Technologies, Inc. Thin film flexible solar cell
US6750394B2 (en) * 2001-01-12 2004-06-15 Sharp Kabushiki Kaisha Thin-film solar cell and its manufacturing method
US20030044539A1 (en) * 2001-02-06 2003-03-06 Oswald Robert S. Process for producing photovoltaic devices
US7074641B2 (en) * 2001-03-22 2006-07-11 Canon Kabushiki Kaisha Method of forming silicon-based thin film, silicon-based thin film, and photovoltaic element
US20030104664A1 (en) * 2001-04-03 2003-06-05 Takaharu Kondo Silicon film, semiconductor device, and process for forming silicon films
US7071018B2 (en) * 2001-06-19 2006-07-04 Bp Solar Limited Process for manufacturing a solar cell
US6825408B2 (en) * 2001-08-24 2004-11-30 Sharp Kabushiki Kaisha Stacked photoelectric conversion device
US20060169317A1 (en) * 2001-10-19 2006-08-03 Asahi Glass Company Limited Substrate with transparent conductive oxide film, process for its production and photoelectric conversion element
US20070137698A1 (en) * 2002-02-27 2007-06-21 Wanlass Mark W Monolithic photovoltaic energy conversion device
US7238545B2 (en) * 2002-04-09 2007-07-03 Kaneka Corporation Method for fabricating tandem thin film photoelectric converter
US20050115504A1 (en) * 2002-05-31 2005-06-02 Ishikawajima-Harima Heavy Industries Co., Ltd. Method and apparatus for forming thin films, method for manufacturing solar cell, and solar cell
US6887728B2 (en) * 2002-08-26 2005-05-03 University Of Hawaii Hybrid solid state/electrochemical photoelectrode for hydrogen production
US20050189012A1 (en) * 2002-10-30 2005-09-01 Canon Kabushiki Kaisha Zinc oxide film, photovoltaic device making use of the same, and zinc oxide film formation process
US6963120B2 (en) * 2002-11-13 2005-11-08 Canon Kabushiki Kaisha Photovoltaic element
US7402747B2 (en) * 2003-02-18 2008-07-22 Kyocera Corporation Photoelectric conversion device and method of manufacturing the device
US20040187914A1 (en) * 2003-03-26 2004-09-30 Canon Kabushiki Kaisha Stacked photovoltaic element and method for producing the same
US20040231590A1 (en) * 2003-05-19 2004-11-25 Ovshinsky Stanford R. Deposition apparatus for the formation of polycrystalline materials on mobile substrates
US7560750B2 (en) * 2003-06-26 2009-07-14 Kyocera Corporation Solar cell device
US20050251990A1 (en) * 2004-05-12 2005-11-17 Applied Materials, Inc. Plasma uniformity control by gas diffuser hole design
US20070249898A1 (en) * 2004-07-02 2007-10-25 Olympus Corporation Endoscope
US20060060138A1 (en) * 2004-09-20 2006-03-23 Applied Materials, Inc. Diffuser gravity support
US20080156370A1 (en) * 2005-04-20 2008-07-03 Hahn-Meitner-Institut Berlin Gmbh Heterocontact Solar Cell with Inverted Geometry of its Layer Structure
US20060249196A1 (en) * 2005-04-28 2006-11-09 Sanyo Electric Co., Ltd. Stacked photovoltaic device
US7375378B2 (en) * 2005-05-12 2008-05-20 General Electric Company Surface passivated photovoltaic devices
US20070000538A1 (en) * 2005-06-30 2007-01-04 Sanyo Electric Co., Ltd. Stacked photovoltaic device
US20070039942A1 (en) * 2005-08-16 2007-02-22 Applied Materials, Inc. Active cooling substrate support
US7301215B2 (en) * 2005-08-22 2007-11-27 Canon Kabushiki Kaisha Photovoltaic device
US7256140B2 (en) * 2005-09-20 2007-08-14 United Solar Ovonic Llc Higher selectivity, method for passivating short circuit current paths in semiconductor devices
US20080057220A1 (en) * 2006-01-31 2008-03-06 Robert Bachrach Silicon photovoltaic cell junction formed from thin film doping source
US20070209699A1 (en) * 2006-03-08 2007-09-13 National Science And Technology Development Agency Thin film solar cell and its fabrication process
US20080110491A1 (en) * 2006-03-18 2008-05-15 Solyndra, Inc., Monolithic integration of non-planar solar cells
US20080047599A1 (en) * 2006-03-18 2008-02-28 Benyamin Buller Monolithic integration of nonplanar solar cells
US20070227579A1 (en) * 2006-03-30 2007-10-04 Benyamin Buller Assemblies of cylindrical solar units with internal spacing
US20080160661A1 (en) * 2006-04-05 2008-07-03 Silicon Genesis Corporation Method and structure for fabricating solar cells using a layer transfer process
US20080047603A1 (en) * 2006-08-24 2008-02-28 Guardian Industries Corp. Front contact with intermediate layer(s) adjacent thereto for use in photovoltaic device and method of making same
US20080153280A1 (en) * 2006-12-21 2008-06-26 Applied Materials, Inc. Reactive sputter deposition of a transparent conductive film
US20080223440A1 (en) * 2007-01-18 2008-09-18 Shuran Sheng Multi-junction solar cells and methods and apparatuses for forming the same
US20080196761A1 (en) * 2007-02-16 2008-08-21 Mitsubishi Heavy Industries, Ltd Photovoltaic device and process for producing same

Cited By (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8203071B2 (en) 2007-01-18 2012-06-19 Applied Materials, Inc. Multi-junction solar cells and methods and apparatuses for forming the same
US20090263930A1 (en) * 2007-10-22 2009-10-22 Yong Kee Chae Microcrystalline silicon deposition for thin film solar applications
US7919398B2 (en) 2007-10-22 2011-04-05 Applied Materials, Inc. Microcrystalline silicon deposition for thin film solar applications
US20090142878A1 (en) * 2007-11-02 2009-06-04 Applied Materials, Inc. Plasma treatment between deposition processes
US7741144B2 (en) 2007-11-02 2010-06-22 Applied Materials, Inc. Plasma treatment between deposition processes
US20090130827A1 (en) * 2007-11-02 2009-05-21 Soo Young Choi Intrinsic amorphous silicon layer
US20110198640A1 (en) * 2008-02-29 2011-08-18 Osram Opto Semiconductor Gmbh Semiconductor Light-Emitting Diode and Method for Producing a Semiconductor Light-Emitting Diode
US8772804B2 (en) * 2008-02-29 2014-07-08 Osram Opto Semiconductors Gmbh Semiconductor light-emitting diode and method for producing a semiconductor light-emitting diode
US20110303289A1 (en) * 2008-11-07 2011-12-15 Mitsubishi Heavy Industries, Ltd. Process for producing photovoltaic device and photovoltaic device
US20100132774A1 (en) * 2008-12-11 2010-06-03 Applied Materials, Inc. Thin Film Silicon Solar Cell Device With Amorphous Window Layer
US20110088760A1 (en) * 2009-10-20 2011-04-21 Applied Materials, Inc. Methods of forming an amorphous silicon layer for thin film solar cell application
TWI401812B (zh) * 2009-12-31 2013-07-11 Metal Ind Res Anddevelopment Ct Solar battery
US20110177648A1 (en) * 2010-01-18 2011-07-21 Applied Materials, Inc. Method of manufacturing thin film solar cells having a high conversion efficiency
US20110174362A1 (en) * 2010-01-18 2011-07-21 Applied Materials, Inc. Manufacture of thin film solar cells with high conversion efficiency
US8252624B2 (en) * 2010-01-18 2012-08-28 Applied Materials, Inc. Method of manufacturing thin film solar cells having a high conversion efficiency
US20110275200A1 (en) * 2010-05-06 2011-11-10 Applied Materials, Inc. Methods of dynamically controlling film microstructure formed in a microcrystalline layer
WO2012027857A3 (en) * 2010-09-02 2012-06-28 Oerlikon Solar Ag, Trübbach Method for manufacturing a tandem solar cell with microcrystalline absorber layer
WO2012065957A3 (en) * 2010-11-16 2012-10-18 Oerlikon Solar Ag, Trübbach Improved a-si:h absorber layer for a-si single- and multijunction thin film silicon solar cell
TWI488322B (zh) * 2010-12-27 2015-06-11 Nexpower Technology Corp 薄膜太陽能電池堆疊製造方法及其薄膜太陽能電池
US9236523B2 (en) 2012-03-05 2016-01-12 First Solar, Inc Method and apparatus for forming a transparent conductive oxide using hydrogen

Also Published As

Publication number Publication date
CN101836299A (zh) 2010-09-15
EP2206156A1 (en) 2010-07-14
KR20100089856A (ko) 2010-08-12
CN101836299B (zh) 2012-06-27
JP2011501445A (ja) 2011-01-06
WO2009055502A1 (en) 2009-04-30
US7919398B2 (en) 2011-04-05
US20090263930A1 (en) 2009-10-22

Similar Documents

Publication Publication Date Title
US7919398B2 (en) Microcrystalline silicon deposition for thin film solar applications
US7582515B2 (en) Multi-junction solar cells and methods and apparatuses for forming the same
US7741144B2 (en) Plasma treatment between deposition processes
US20080173350A1 (en) Multi-junction solar cells and methods and apparatuses for forming the same
US7875486B2 (en) Solar cells and methods and apparatuses for forming the same including I-layer and N-layer chamber cleaning
US8203071B2 (en) Multi-junction solar cells and methods and apparatuses for forming the same
US20120171852A1 (en) Remote hydrogen plasma source of silicon containing film deposition
US20080223440A1 (en) Multi-junction solar cells and methods and apparatuses for forming the same
US20080271675A1 (en) Method of forming thin film solar cells
US20080245414A1 (en) Methods for forming a photovoltaic device with low contact resistance
US20110088760A1 (en) Methods of forming an amorphous silicon layer for thin film solar cell application
US20100258169A1 (en) Pulsed plasma deposition for forming microcrystalline silicon layer for solar applications
US20130112264A1 (en) Methods for forming a doped amorphous silicon oxide layer for solar cell devices
JP2010067973A (ja) 薄膜の微結晶シリコン合金及びウエハベースのソーラー用途
US20090130827A1 (en) Intrinsic amorphous silicon layer
US20090101201A1 (en) Nip-nip thin-film photovoltaic structure
US20110171774A1 (en) Cleaning optimization of pecvd solar films
US20110275200A1 (en) Methods of dynamically controlling film microstructure formed in a microcrystalline layer
EP2304072A1 (en) Solar cells and methods and apparatuses for forming the same
WO2012113441A1 (en) Thin-film solar fabrication process, deposition method for a layer stack of a solar cell, and solar cell precursor

Legal Events

Date Code Title Description
AS Assignment

Owner name: APPLIED MATERIALS, INC., CALIFORNIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:CHAE, YONG KEE;CHOI, SOO YOUNG;SHENG, SHURAN;REEL/FRAME:019993/0340

Effective date: 20071017

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO PAY ISSUE FEE